A Fast and Cost-Effective Detection of Melamine by Surface Enhanced Raman Spectroscopy Using a Novel Hydrogen Bonding-Assisted Supramolecular Matrix and Gold-Coated Magnetic Nanoparticles

A fast and cost-effective melamine detection approach has been developed based on surface enhanced Raman spectroscopy (SERS) using a novel hydrogen bonding-assisted supramolecular matrix. The detection utilizes Fe3O4/Au magnetic nanoparticles coated with 5-aminoorotic acid (AOA) as a SERS active substrate (Fe3O4/Au–AOA), and Rhodamine B (RhB) conjugated AOA as a Raman reporter (AOA–RhB). Upon mixing the reagents with melamine, a supramolecular complex [Fe3O4/Au–AOA•••melamine•••AOA–RhB] was formed due to the strong multiple hydrogen bonding interactions between AOA and melamine. The complex was separated and concentrated to a pellet by an external magnet and used as a supramolecular matrix for the melamine detection. Laser excitation of the complex pellet produced a strong SERS signal diagnostic for RhB. The logarithmic intensity of the characteristic RhB peaks was found to be proportional to the concentration of melamine with a limit of detection of 2.5 μg/mL and a detection linearity range of 2.5~15.0 μg/mL in milk. As Fe3O4 nanoparticles and AOA are thousands of times less expensive than the monoclonal antibody used in a traditional sandwich immunoassay, the current assay drastically cut down the cost of melamine detection. The current approach affords promise as a biosensor platform that cuts down sample pre-treatment steps and measurement expense.


Introduction
Melamine is a common industrial chemical and has been widely used to manufacture thermoset plastics, coating materials, flame retardants, wood adhesives, glues, and many other applications.The chemical became a global concern in 2008 because a high amount of melamine had been illegally added to pet food and even infant milk formula in China [1,2].The long-term ingestion of melamine may cause severe damages like kidney stones [3], bladder stones [4,5], and even bladder cancer [6,7].Under the effect of gastric juice, part of melamine may transfer into cyanuric acid and react with the remaining melamine to produce insoluble crystals of melamine cyanurate, which induce renal malfunction, metabolic problems of the urinary system [8], or even death in infants.For both health and social reasons, there remains an urgent need for a rapid, on-site, sensitive, and cost-effective analysis of melamine.
The current detection methods for melamine analysis primarily include high performance liquid chromatography (HPLC), liquid chromatography-mass spectrometry (LC-MS), gas chromatography-mass spectrometry (GC-MS), enzyme-linked immunosorbent assay (ELISA), infrared Appl.Sci.2017, 7, 475 2 of 13 spectrometry (IR), and surface enhanced Raman spectroscopy (SERS) [9][10][11].Though HPLC is a powerful method of high sensitivity and selectivity to determine melamine, its complicated and time-consuming pretreatment of samples brings much inconvenience for on-site rapid detection [12].LC-MS or GC-MS requires expensive equipment, complicated operations, professional skills, and high test costs, and thus is suitable for laboratory testing only [13].IR has a fast detection speed, less sample consumption, and high operability, but it is less sensitive and less accurate in quantitative analysis.ELISA is easy to carry out and its short analysis time makes it possible for mass screening, but ELISA often gives false positive results and thus is difficult to achieve a rapid onsite determination of melamine [14].
The phenomenon of SERS was first observed by Fleischmann and coworkers in 1974 [15].Van Duyne and Jeanmaire [16] later found that the Raman scattering signal of pyridine on the rough surface of silver electrodes was about 10 6 times higher than the same amount of pyridine in solution.Under ideal conditions, SERS is able to detect a single molecule of the detected analytes [17].Rough gold or silver surfaces as well as gold or silver nanoparticles are generally used as Raman active substrates due to their high surface enhanced Raman scattering effect [18].With the help of a portable spectrometer, SERS can provide simple, rapid, and on-site analysis due to its inherent simplicity and high sensitivity and thus has been developed as a fast detection platform for biothreat investigation [19], DNA and RNA identification [20][21][22], cancer-diagnostics [23], protein immunoassay [24][25][26][27][28], and food safety analysis [29][30][31][32][33][34][35][36][37].For example, SERS has been explored to detect melamine in milk using hollow gold chips or other SERS active substrates fabricated on glass or silicon wafers [32][33][34] and using melamine-induced aggregation of gold nanoparticles as an enhanced substrate [35].Printed SERS substrates combined with paper chromatograph have been successfully applied in the direct detection of melamine in proteinaceous samples [38].Melamine has been directly detected in infant formula with a limit of detection of 100 ppb using commercial gold nanofinger SERS sensor chips [10] and has also been detected in pure water with a limit of detection of 1 ppb using ultrasensitive Ag nanoparticles over Au film coated on PS colloid monolayer as a substrate [39].However, these direct detections of melamine by SERS may not be applicable to other complex samples in practice such as blood, urine, pet foods, and fertilizers.For example, the serum amino acid (e.g., methionine) [40] and serum vitamins (e.g., folic acid) [41] show Raman characteristic peaks around 690 cm −1 , which overlap the signature peak of melamine at 695 cm −1 [38] and thus may cause severe interference in the detection of melamine in blood samples.
Herein, in this work, we propose an indirect detection approach based on a novel, magnetic, supramolecular hydrogen bonding-assisted SERS-active matrix and use it for the rapid onsite detection of melamine.Melamine has been found to form stable complexes with cyanuric acid, orotic acid, and their derivatives via strong supramolecular multiple hydrogen bonds [42][43][44].Accordingly, gold nanoparticles (Au NPs) were first assembled on the surface of Fe 3 O 4 nanoparticles to form Fe 3 O 4 /Au magnetic nanoparticles and then coated with 5-aminoorotic acid (AOA) to produce a magnetic gold nanoparticle substrate (Fe 3 O 4 /Au-AOA), while Rhodamine B (RhB) was conjugated with AOA to generate a highly sensitive Raman reporter (AOA-RhB), as illustrated in Figure 1.The substrate combined the high SERS effects of gold nanoparticles and the magnetic properties of Fe 3 O 4 nanoparticles.Upon mixing the reagents with melamine, a magnetic supramolecular complex [Fe 3 O 4 /Au-AOA•••melamine•••AOA-RhB] was formed due to the strong multiple hydrogen bonding interaction between AOA and melamine.The complex was subsequently separated and concentrated to a pellet point by an external magnet, followed by a laser excitation of the pellet to provide strong SERS signals of RhB.The concentration of melamine was quantitatively determined by the intensity of RhB signals.The synthesis and characterization of gold magnetic nanoparticles Fe 3 O 4 /Au, as well as the RhB-conjugated Raman reporter, the limit of detection of melamine, and the detection linear range, were investigated in this work.

Instruments and Reagents
The morphology of prepared Fe3O4/Au nanoparticles was observed on a transmission electron microscope (TEM, Tecnai G2 F30 S-Twin, FEI Company, Hillsboro, OR, USA) equipped with an energy dispersive X-ray (EDX) analyzer (JEOL 4000FX), operating at an acceleration voltage of 300 keV.SERS spectra were recorded on a DeltaNu Advantage 785 Raman spectrometer equipped with a microscope and a stage-sample holder.The spectrometer has a laser power of 120 mW with an excitation wavelength at 785 nm and a spectral range of 200-2000 cm −1 .Fourier transform infrared spectroscopy (FTIR) analysis was conducted on a Shimadzu IRaffinity-1S spectrometer equipped with a Specac ATR attachment containing a ZnSe crystal (refractive index n = 2.43).The transmission and reflectance spectra were recorded in the range from 4000 to 600 cm −1 with a resolution of 2 cm −1 .

Instruments and Reagents
The morphology of prepared Fe 3 O 4 /Au nanoparticles was observed on a transmission electron microscope (TEM, Tecnai G2 F30 S-Twin, FEI Company, Hillsboro, OR, USA) equipped with an energy dispersive X-ray (EDX) analyzer (JEOL 4000FX), operating at an acceleration voltage of 300 keV.SERS spectra were recorded on a DeltaNu Advantage 785 Raman spectrometer equipped with a microscope and a stage-sample holder.The spectrometer has a laser power of 120 mW with an excitation wavelength at 785 nm and a spectral range of 200-2000 cm −1 .Fourier transform infrared spectroscopy (FTIR) analysis was conducted on a Shimadzu IRaffinity-1S spectrometer equipped with a Specac ATR attachment containing a ZnSe crystal (refractive index n = 2.43).The transmission and reflectance spectra were recorded in the range from 4000 to 600 cm −1 with a resolution of 2 cm −1 .

Synthesis of Fe 3 O 4 /Au Gold Magnetic Nanoparticles
The modification of Fe 3 O 4 nanoparticles was based on a literature method [45].Briefly, 25.0 mg of Fe 3 O 4 nanoparticles were dispersed in a mixture of 10.0 mL of distilled water, 50 mL of ethanol, and 0.5 mL of ammonia.After the mixture was ultrasonicated for 5 min, 40.0 µL of TEOS was added and the mixture was subjected to ultrasonic oscillation at room temperature for 6 h.Then, the nanoparticles were separated and collected with a magnet, washed with distilled water and ethanol respectively, and redispersed in 50.0 mL of ethanol.Exactly 20 µL of APTES and 20.0 µL of MPTES were added to the ethanol solution, and the solution was treated with ultrasonic oscillation at room temperature for 18 h.Magnetic Fe 3 O 4 nanoparticles coated with -NH 2 and -SH groups were collected with a magnet, washed with distilled water and ethanol retrospectively, and finally redispersed in 10.0 mL distilled water for later use.
According to the method of Frens [46], sodium citrate was used as a reducing agent to synthesize gold nanoparticles.Fifty milliliters of distilled water was heated to boiling, and 10.0 mg of chloroauric acid hydrate was added to the water under stirring.Then, 50.0 µL of sodium citrate solution (5%) was added to the water solution, and the solution was kept boiling and stirring for 1 min.After the solution cooled down to room temperature, Au nanoparticles were obtained and stored in a fridge at 4 • C for later use.
Exactly 10.0 mL of the modified Fe 3 O 4 nanoparticle solution above was mixed with 10.0 mL of gold nanoparticle solution, and the mixture was mechanically stirred at room temperature for 4 h.Then, the Fe 3 O 4 /Au gold magnetic nanoparticles were separated by a magnet, washed with distilled water, and finally redispersed in 10.0 mL of distilled water.

Synthesis of AOA-Coated Gold Magnetic Nanoparticles (Fe 3 O 4 /Au-AOA)
Exactly 50.0 mg of 5-aminoorotic acid (AOA) was dissolved in 10.0 mL of phosphate buffer solution (PBS, pH = 7.4) and 100.0 mg of NHS-PEG-SH was added to the PBS solution.The solution was stirred at room temperature for 6 h and then dialyzed against fresh PBS solution to remove the excess of AOA, followed by the addition of 10.0 mL of the above-mentioned Fe 3 O 4 /Au gold magnetic nanoparticle solution.After the mixture was stirred at room temperature for 24 h, the gold magnetic nanoparticles (Fe 3 O 4 /Au-AOA) were separated and concentrated by a magnet, washed with distilled water, and finally redispersed in 10.0 mL of distilled water.

Synthesis of RhB-Conjugated AOA (AOA-RhB)
Exactly 10.0 mg of Rhodamine B isothiocyanate and 2.9 mg 5-aminoorotic acid were dissolved in 1.0 mL of N,N-dimethylformamide (DMF).The solution was stirred at room temperature for 24 h and then dialyzed against water to remove the excess of Rhodamine B and finally obtain AOA-RhB.

as a Matrix
A melamine stock solution was prepared by accurately dissolving 1.0 mg of melamine in 10.0 mL of water.The gold magnetic nanoparticle (Fe 3 O 4 /Au-AOA) and the RhB-conjugated AOA (AOA-RhB) solution were prepared at concentrations of 2.5 and 0.1 mg/mL, respectively.Aliquots of the melamine stock solution above were added to the mixture of 0.1 mL of Fe 3 O 4 /Au-AOA and 0.1 mL of AOA-RhB solution to make a series of solutions, respectively containing 1.0 µg/mL, 2.5 µg/mL, 5.0 µg/mL, 10.0 µg/mL, and 15.0 µg/mL of melamine.These solutions were oscillated at room temperature for 30 min and then transferred to concave glass slides with pipettes.A strong NdFeB cylinder magnet (10 mm in diameter, 3 mm in thickness, Jiangdong Magnetic Industry of Ningbo Co. Ltd., Ningbo, China) was placed under each slide to separate and concentrate the gold magnetic nanoparticles to a pellet point.The laser irradiation of the pellets produced Raman spectra of RhB and its characteristic peak at 1510 cm −1 was analyzed to build the calibration curve for melamine since the peaks between 1200 and 1400 cm −1 were prone to interference with the glass background of slides [47].Each recorded spectrum is an average of five independent readings taken at an integration time of 1 s.The total analysis time can be less than 1 h.

Detection of Melamine in Milk Using
The gold magnetic nanoparticle (Fe 3 O 4 /Au-AOA) and the RhB-conjugated AOA (AOA-RhB) solution were prepared at a concentration of 4.0 and 0.5 mg/mL, respectively.A melamine stock solution was prepared by accurately dissolving 10.0 mg of melamine in 10.0 mL of ethanol/H 2 O 50:50 (v/v).Aliquots of the melamine stock solution above were added into 0.2 mL of milk.Then, the milk solution was mixed with 0.1 mL of Fe 3 O 4 /Au-AOA and 0.1 mL of AOA-RhB solution to make a series of solutions, respectively containing 2.0, 2.5, 5.0, 10.0, and 15.0 µg/mL of melamine.These solutions were oscillated at room temperature for 30 min and then transferred to concave glass slides with pipettes.A strong NdFeB cylinder magnet (10 mm in diameter, 3 mm in thickness, Jiangdong Magnetic Industry of Ningbo Co. Ltd, Ningbo, China) was placed under each slide to separate and concentrate the gold magnetic nanoparticles into a pellet point.The supernatant was removed by a filter paper.The laser irradiation of the pellets produced Raman spectra of RhB, and its characteristic peak at 1510 cm −1 was analyzed to build the calibration curve of melamine.Each recorded spectrum is an average of five independent readings taken at an integration time of 1 s.The total analysis time can be less than 1 h.The gold magnetic nanoparticle (Fe3O4/Au-AOA) and the RhB-conjugated AOA (AOA-RhB) solution were prepared at a concentration of 4.0 and 0.5 mg/mL, respectively.A melamine stock solution was prepared by accurately dissolving 10.0 mg of melamine in 10.0 mL of ethanol/H2O 50:50 (v/v).Aliquots of the melamine stock solution above were added into 0.2 mL of milk.Then, the milk solution was mixed with 0.1 mL of Fe3O4/Au-AOA and 0.1 mL of AOA-RhB solution to make a series of solutions, respectively containing 2.0, 2.5, 5.0, 10.0, and 15.0 µ g/mL of melamine.These solutions were oscillated at room temperature for 30 min and then transferred to concave glass slides with pipettes.A strong NdFeB cylinder magnet (10 mm in diameter, 3 mm in thickness, Jiangdong Magnetic Industry of Ningbo Co. Ltd, Ningbo, China) was placed under each slide to separate and concentrate the gold magnetic nanoparticles into a pellet point.The supernatant was removed by a filter paper.The laser irradiation of the pellets produced Raman spectra of RhB, and its characteristic peak at 1510 cm −1 was analyzed to build the calibration curve of melamine.Each recorded spectrum is an average of five independent readings taken at an integration time of 1 s.The total analysis time can be less than 1 h.

Characteristics of Fe3O4/Au Gold Magnetic Nanoparticles by TEM and EDX
TEM images of Fe3O4 nanoparticles, Au nanoparticles and Fe3O4/Au gold magnetic nanoparticles at various resolutions are shown in Figure 2 and the corresponding EDX spectrum of Fe3O4/Au is presented in Figure 3.The Fe3O4 nanoparticles were in cubic shape and the particle size was in the range of 100-200 nm (Figure 2a) and the spherical or oval Au nanoparticles had a relatively narrow size distribution with a diameter ranging from 10 to 20 nm (Figure 2b). Figure 2c demonstrates the structure of Fe3O4/Au gold magnetic nanoparticles.Obviously, the cubic Fe3O4 nanoparticles were densely covered by a layer of spherical Au nanoparticles.At higher resolutions, the Au nanoparticles were found to closely attach on the surface of Fe3O4 nanoparticle (Figure 2d,e).Figure 2f clearly shows the crystal lattice fringes of Au nanoparticles and Fe3O4 nanoparticles.The EDX spectrum (Figure 3) of the gold magnetic nanoparticles shows Au signal peaks and Fe signal peaks from Au nanoparticles and Fe3O4 nanoparticles, respectively, as well as C peaks and Cu peaks from the ultrathin carbon-coated copper grids.These results indicated the formation of Fe3O4/Au gold magnetic nanoparticles.

Characterization of AOA-Coated Gold Magnetic Nanoparticles (Fe3O4/Au-AOA) by FTIR
Figure 4a presents the FTIR spectrum of Fe3O4/Au.The broad double peaks at 1110 cm −1 and 1014 cm −1 are due to the stretching vibration of Si-O-Si.Au, as a simple metal substance, has no obvious absorption peaks.Figure 4b clearly shows characteristic double peaks of the amino group of 5-aminoorotic acid (AOA) at 3470 cm −1 and 3343 cm −1 , as well as a strong carbonyl C=O stretching vibration at 1696 cm −1 , respectively.Figure 4c indicates the spectrum of AOA-coated gold magnetic

Characterization of AOA-Coated Gold Magnetic Nanoparticles (Fe3O4/Au-AOA) by FTIR
Figure 4a presents the FTIR spectrum of Fe3O4/Au.The broad double peaks at 1110 cm −1 and 1014 cm −1 are due to the stretching vibration of Si-O-Si.Au, as a simple metal substance, has no obvious absorption peaks.Figure 4b clearly shows characteristic double peaks of the amino group of 5-aminoorotic acid (AOA) at 3470 cm −1 and 3343 cm −1 , as well as a strong carbonyl C=O stretching vibration at 1696 cm −1 , respectively.Figure 4c indicates the spectrum of AOA-coated gold magnetic  a stable Au-S bond, the -NHS reacted with the amino group of AOA to form an amide bond by amidation reaction.As can be seen from Figure 4c, the disappearance of the amino double peaks and the appearance of a broad amide peaks between 3100 cm −1 and 3200 cm −1 in addition to the carbonyl C=O peak at 1696 cm −1 unambiguously proved that the AOA had been coated on the surface of Fe 3 O 4 /Au via the polyethylene glycolthiol linkage.
Appl.Sci.2017, 7, 475 7 of 13 nanoparticles synthesized by the connection of AOA to Fe3O4/Au nanoparticles through polyethylene glycolthiol (NHS-PEG-SH).As the -SH group was firmly attached to the surface of Fe3O4/Au via a stable Au-S bond, the -NHS reacted with the amino group of AOA to form an amide bond by amidation reaction.As can be seen from Figure 4c, the disappearance of the amino double peaks and the appearance of a broad amide peaks between 3100 cm −1 and 3200 cm −1 in addition to the carbonyl C=O peak at 1696 cm −1 unambiguously proved that the AOA had been coated on the surface of Fe3O4/Au via the polyethylene glycolthiol linkage.

Characterization of RhB-Conjugated AOA (AOA-RhB) by FTIR
The infrared spectrum of Rhodamine B isothiocyanate (RhB) is shown in Figure 5a.RhB has a strong and broad IR adsorption of -OH stretching vibration between 3100 cm −1 and 3600 cm −1 and a characteristic adsorption of -N=C=S group at 2025 cm −1 .The peaks at 2977 cm −1 and 2926 cm −1 were ascribed to the anti-symmetric and symmetric stretching vibrations of -CH3 of RhB.After the conjugation of RhB to AOA, the -N=C=S characteristic peak at 2025 cm −1 completely disappeared while a strong peak at 1694 cm −1 corresponding to the carboxyl group of AOA appeared (Figure 5b), indicating that the RhB had been connected to AOA through the reaction of -N=C=S with the amino group of AOA.

Characterization of RhB-Conjugated AOA (AOA-RhB) by FTIR
The infrared spectrum of Rhodamine B isothiocyanate (RhB) is shown in Figure 5a.RhB has a strong and broad IR adsorption of -OH stretching vibration between 3100 cm −1 and 3600 cm −1 and a characteristic adsorption of -N=C=S group at 2025 cm −1 .The peaks at 2977 cm −1 and 2926 cm −1 were ascribed to the anti-symmetric and symmetric stretching vibrations of -CH 3 of RhB.After the conjugation of RhB to AOA, the -N=C=S characteristic peak at 2025 cm −1 completely disappeared while a strong peak at 1694 cm −1 corresponding to the carboxyl group of AOA appeared (Figure 5b), indicating that the RhB had been connected to AOA through the reaction of -N=C=S with the amino group of AOA.nanoparticles synthesized by the connection of AOA to Fe3O4/Au nanoparticles through polyethylene glycolthiol (NHS-PEG-SH).As the -SH group was firmly attached to the surface of Fe3O4/Au via a stable Au-S bond, the -NHS reacted with the amino group of AOA to form an amide bond by amidation reaction.As can be seen from Figure 4c, the disappearance of the amino double peaks and the appearance of a broad amide peaks between 3100 cm −1 and 3200 cm −1 in addition to the carbonyl C=O peak at 1696 cm −1 unambiguously proved that the AOA had been coated on the surface of Fe3O4/Au via the polyethylene glycolthiol linkage.

Characterization of RhB-Conjugated AOA (AOA-RhB) by FTIR
The infrared spectrum of Rhodamine B isothiocyanate (RhB) is shown in Figure 5a.RhB has a strong and broad IR adsorption of -OH stretching vibration between 3100 cm −1 and 3600 cm −1 and a characteristic adsorption of -N=C=S group at 2025 cm −1 .The peaks at 2977 cm −1 and 2926 cm −1 were ascribed to the anti-symmetric and symmetric stretching vibrations of -CH3 of RhB.After the conjugation of RhB to AOA, the -N=C=S characteristic peak at 2025 cm −1 completely disappeared while a strong peak at 1694 cm −1 corresponding to the carboxyl group of AOA appeared (Figure 5b), indicating that the RhB had been connected to AOA through the reaction of -N=C=S with the amino group of AOA.Melamine had characteristic double peaks of amino group at 3466 cm −1 and 3415 cm −1 (Figure 6c), while Fe 3 O 4 /Au-AOA and AOA-RhB presented characteristic peak of carbonyl groups at 1696 cm −1 and 1694 cm −1 , respectively (Figure 6a,b).The FTIR spectrum of the 6d) clearly showed that the double peaks of amino group of melamine disappeared, and the carbonyl group stretching vibration of AOA simultaneously shifted from 1696 cm −1 to 1694 cm −1 to a lower wavenumber at 1681 cm −1 , indicating the formation of a strong hydrogen bonding between melamine and AOA in the complex, as illustrated in Figure 1.
Appl.Sci.2017, 7, 475 8 of 13 Figure 6 demonstrates the changes in FTIR spectra of Fe3O4/Au-AOA and AOA-RhB when melamine was added to form the [Fe3O4/Au-AOA•••melamine•••AOA-RhB] complex.Melamine had characteristic double peaks of amino group at 3466 cm −1 and 3415 cm −1 (Figure 6c), while Fe3O4/Au-AOA and AOA-RhB presented characteristic peak of carbonyl groups at 1696 cm −1 and 1694 cm −1 , respectively (Figure 6a,b).The FTIR spectrum of the [Fe3O4/Au-AOA•••melamine•••AOA-RhB] complex (Figure 6d) clearly showed that the double peaks of amino group of melamine disappeared, and the carbonyl group stretching vibration of AOA simultaneously shifted from 1696 cm −1 to 1694 cm −1 to a lower wavenumber at 1681 cm −1 , indicating the formation of a strong hydrogen bonding between melamine and AOA in the complex, as illustrated in Figure 1.

Detection of Melamine in Water Using [Fe3O4/Au-AOA•••Melamine•••AOA-RhB] as a Matrix
The detection assay of melamine was assembled by the addition of aliquots of melamine solution to the mixture of 0.1 mL of Fe3O4/Au-AOA and 0.1 mL of AOA-RhB solution to make a series of mixture solutions respectively containing 1.0 µ g/mL, 2.5 µ g/mL, 5.0 µ g/mL, 10.0 µ g/mL, and 15.0 µ g/mL of melamine.Figure 7 shows the difference in Raman spectra for the samples containing no melamine (Spectrum a) and 1.0 µ g/mL of melamine (Spectrum b).There are no apparent diagnostic signal peaks for RhB in Spectrum a because the RhB molecules were far from the surface of the gold magnetic nanoparticles due to the lack of strong interactions between Fe3O4/Au-AOA and AOA-RhB in the absence of melamine.In contrast, several characteristic peaks (between 1100 and 1700 cm −1 ) of RhB appeared in Spectrum b since the addition of melamine caused the formation of the supramolecular complex of [Fe3O4/Au-AOA•••melamine•••AOA-RhB] via strong multiple hydrogen bonding between melamine and AOA, and consequently brought the RhB molecules close enough to the surface of Fe3O4/Au nanoparticles for the generation of SERS signal of RhB.
Figure 8 demonstrates a progressive increment in peak intensity at 1510 cm −1 of RhB when melamine concentration was increased from 0 to 15.0 µ g/mL.A linear plot of the logarithm of the peak intensity at 1510 cm −1 versus the melamine concentration indicates that the detection is linear within the concentration between 1.0 and 15.0 µ g/mL with the detection limit of melamine at 1.0 µg/mL in water.The linear equation is lgI = 2.07546 + 0.06641 × C (lgI refers to the logarithmic  The detection assay of melamine was assembled by the addition of aliquots of melamine solution to the mixture of 0.1 mL of Fe 3 O 4 /Au-AOA and 0.1 mL of AOA-RhB solution to make a series of mixture solutions respectively containing 1.0 µg/mL, 2.5 µg/mL, 5.0 µg/mL, 10.0 µg/mL, and 15.0 µg/mL of melamine.Figure 7 shows the difference in Raman spectra for the samples containing no melamine (Spectrum a) and 1.0 µg/mL of melamine (Spectrum b).There are no apparent diagnostic signal peaks for RhB in Spectrum a because the RhB molecules were far from the surface of the gold magnetic nanoparticles due to the lack of strong interactions between Fe 3 O 4 /Au-AOA and AOA-RhB in the absence of melamine.In contrast, several characteristic peaks (between 1100 and 1700 cm Figure 8 demonstrates a progressive increment in peak intensity at 1510 cm −1 of RhB when melamine concentration was increased from 0 to 15.0 µg/mL.A linear plot of the logarithm of the peak intensity at 1510 cm −1 versus the melamine concentration indicates that the detection is linear within the concentration between 1.0 and 15.0 µg/mL with the detection limit of melamine at 1.0 µg/mL in water.The linear equation is lgI = 2.07546 + 0.06641 × C (lgI refers to the logarithmic peak intensity at 1510 cm −1 , C refers to melamine concentrations) and the linear regression coefficient was determined to be R 2 = 0.9840.peak intensity at 1510 cm −1 , C refers to melamine concentrations) and the linear regression coefficient was determined to be R 2 = 0.9840.

Detection of Melamine in Milk Using [Fe3O4/Au-AOA•••Melamine•••AOA-RhB] as a Matrix
Similar results were found in the detection assay of melamine in milk as shown in Figure 9. Due to the interference of protein, lipid, and other materials in milk, a conservative detection limit of melamine was set at 2.5 µ g/mL in milk.The regression of the logarithmic peak intensity at 1510 cm −1 versus the melamine concentration produced a linear plot with linear equation as lgI = 2.02148 + 0.05852 × C (lgI represents the logarithms of the peak intensity at 1510 cm −1 , C is the melamine concentrations) and R 2 = 0.9852 in the melamine concentration ranging from 2.5 to 15.0 µ g/mL.peak intensity at 1510 cm −1 , C refers to melamine concentrations) and the linear regression coefficient was determined to be R 2 = 0.9840.

Detection of Melamine in Milk Using [Fe3O4/Au-AOA•••Melamine•••AOA-RhB] as a Matrix
Similar results were found in the detection assay of melamine in milk as shown in Figure 9. Due to the interference of protein, lipid, and other materials in milk, a conservative detection limit of melamine was set at 2.5 µ g/mL in milk.The regression of the logarithmic peak intensity at 1510 cm −1 versus the melamine concentration produced a linear plot with linear equation as lgI = 2.02148 + 0.05852 × C (lgI represents the logarithms of the peak intensity at 1510 cm −1 , C is the melamine concentrations) and R 2 = 0.9852 in the melamine concentration ranging from 2.5 to 15.0 µ g/mL.

Detection of Melamine in Milk Using
Similar results were found in the detection assay of melamine in milk as shown in Figure 9. Due to the interference of protein, lipid, and other materials in milk, a conservative detection limit of melamine was set at 2.5 µg/mL in milk.The regression of the logarithmic peak intensity at 1510 cm −1 versus the melamine concentration produced a linear plot with linear equation as lgI = 2.02148 + 0.05852 × C (lgI represents the logarithms of the peak intensity at 1510 cm −1 , C is the melamine concentrations) and R 2 = 0.9852 in the melamine concentration ranging from 2.5 to 15.0 µg/mL.In a traditional enzyme-linked immunosorbent assay (ELISA) or the immuno-based SERS detection of melamine, monoclonal or polyclonal antibodies are inevitably used to establish the assay [14,27,28].In comparison with commercial Fe3O4 nanoparticles, 5-aminoorotic acid, and Au nanoparticles, these antibodies are often tens of thousands of times more expensive and require careful handling and disposal because they are sensitive to temperature and pH value.The current assay drastically cut down the cost of detection by replacing monoclonal and polyclonal antibodies with Fe3O4/Au nanoparticles and 5-aminoorotic acid and simplified the detection procedure by employing magnetic separation with external magnets.With the help of a portable spectrometer, the current method provided a simple, rapid, on-site, and low cost analysis of melamine.

Conclusions
This work presents a fast and cost-effective detection approach of melamine based on surface enhanced Raman spectroscopy (SERS) using a novel hydrogen bonding-assisted supramolecular matrix and gold-coated magnetic nanoparticles.The detection utilizes Fe3O4/Au magnetic nanoparticles coated with 5-aminoorotic acid (AOA) as a SERS active substrate (Fe3O4/Au-AOA), and Rhodamine B (RhB) conjugated AOA as a Raman reporter (AOA-RhB).The formation of the [Fe3O4/Au-AOA•••melamine•••AOA-RhB] complex due to the strong multiple hydrogen bonding between AOA and melamine, followed by the laser excitation of the complex, produced strong SERS signals diagnostic for RhB.The logarithmic intensity of the characteristic peak at 1510 cm −1 of RhB was found to be proportional to the concentration of melamine with a limit of detection of 1.0 µ g/mL and a detection linearity range of 1.0~15.0µ g/mL in water, and a limit of detection of 2.5 µ g/mL and a detection linearity range of 2.5~15.0µ g/mL in milk.As Fe3O4 nanoparticle and AOA are tens of thousands of times less expensive than monoclonal antibodies used in traditional sandwich immunoassays, and the total analysis time of the assay was less than 1 h, the current method affords promise as a biosensor platform that can be adapted for portable and cost-effective detection applications.In a traditional enzyme-linked immunosorbent assay (ELISA) or the immuno-based SERS detection of melamine, monoclonal or polyclonal antibodies are inevitably used to establish the assay [14,27,28].In comparison with commercial Fe 3 O 4 nanoparticles, 5-aminoorotic acid, and Au nanoparticles, these antibodies are often tens of thousands of times more expensive and require careful handling and disposal because they are sensitive to temperature and pH value.The current assay drastically cut down the cost of detection by replacing monoclonal and polyclonal antibodies with Fe 3 O 4 /Au nanoparticles and 5-aminoorotic acid and simplified the detection procedure by employing magnetic separation with external magnets.With the help of a portable spectrometer, the current method provided a simple, rapid, on-site, and low cost analysis of melamine.

Conclusions
This work presents a fast and cost-effective detection approach of melamine based on surface enhanced Raman spectroscopy (SERS) using a novel hydrogen bonding-assisted supramolecular matrix and gold-coated magnetic nanoparticles.The detection utilizes Fe 3 O 4 /Au magnetic nanoparticles coated with 5-aminoorotic acid (AOA) as a SERS active substrate (Fe 3 O 4 /Au-AOA), and Rhodamine B (RhB) conjugated AOA as a Raman reporter (AOA-RhB).The formation of the [Fe 3 O 4 /Au-AOA•••melamine•••AOA-RhB] complex due to the strong multiple hydrogen bonding between AOA and melamine, followed by the laser excitation of the complex, produced strong SERS signals diagnostic for RhB.The logarithmic intensity of the characteristic peak at 1510 cm −1 of RhB was found to be proportional to the concentration of melamine with a limit of detection of 1.0 µg/mL and a detection linearity range of 1.0~15.0µg/mL in water, and a limit of detection of 2.5 µg/mL and a detection linearity range of 2.5~15.0µg/mL in milk.As Fe 3 O 4 nanoparticle and AOA are tens of thousands of times less expensive than monoclonal antibodies used in traditional sandwich immunoassays, and the total analysis time of the assay was less than 1 h, the current method affords promise as a biosensor platform that can be adapted for portable and cost-effective detection applications.
Fe 3 O 4 /Au Gold Magnetic Nanoparticles by TEM and EDX TEM images of Fe 3 O 4 nanoparticles, Au nanoparticles and Fe 3 O 4 /Au gold magnetic nanoparticles at various resolutions are shown in Figure 2 and the corresponding EDX spectrum of Fe 3 O 4 /Au is presented in Figure 3.The Fe 3 O 4 nanoparticles were in cubic shape and the particle size was in the range of 100-200 nm (Figure2a) and the spherical or oval Au nanoparticles had a relatively narrow size distribution with a diameter ranging from 10 to 20 nm (Figure2b).

13 2. 6 .
Figure 2c demonstrates the structure of Fe 3 O 4 /Au gold magnetic nanoparticles.Obviously, the cubic Fe 3 O 4 nanoparticles were densely covered by a layer of spherical Au nanoparticles.At higher resolutions, the Au nanoparticles were found to closely attach on the surface of Fe 3 O 4 nanoparticle (Figure 2d,e).Figure 2f clearly shows the crystal lattice fringes of Au nanoparticles and Fe 3 O 4 nanoparticles.The EDX spectrum (Figure 3) of the gold magnetic nanoparticles shows Au signal peaks and Fe signal peaks from Au nanoparticles and Fe 3 O 4 nanoparticles, respectively, as well as C peaks and Cu peaks from the ultrathin carbon-coated copper grids.These results indicated the formation of Fe 3 O 4 /Au gold magnetic nanoparticles.Appl.Sci.2017, 7, 475 5 of Detection of Melamine in Milk Using [Fe3O4/Au-AOA•••Melamine•••AOA-RhB] as a Matrix

3. 2 .
Figure 4a presents the FTIR spectrum of Fe 3 O 4 /Au.The broad double peaks at 1110 cm −1 and 1014 cm −1 are due to the stretching vibration of Si-O-Si.Au, as a simple metal substance, has no obvious absorption peaks.Figure 4b clearly shows characteristic double peaks of the amino group of 5-aminoorotic acid (AOA) at 3470 cm −1 and 3343 cm −1 , as well as a strong carbonyl C=O stretching vibration at 1696 cm −1 , respectively.Figure 4c indicates the spectrum of AOA-coated gold magnetic nanoparticles synthesized by the connection of AOA to Fe 3 O 4 /Au nanoparticles through polyethylene glycolthiol (NHS-PEG-SH).As the -SH group was firmly attached to the surface of Fe 3 O 4 /Au via

3. 5 .
Detection of Melamine in Water Using [Fe 3 O 4 /Au-AOA•••Melamine•••AOA-RhB] as a Matrix −1 ) of RhB appeared in Spectrum b since the addition of melamine caused the formation of the supramolecular complex of [Fe 3 O 4 /Au-AOA•••melamine•••AOA-RhB] via strong multiple hydrogen bonding between melamine and AOA, and consequently brought the RhB molecules close enough to the surface of Fe 3 O 4 /Au nanoparticles for the generation of SERS signal of RhB.

Figure 7 .
Figure 7. Raman spectra of the mixture of Fe3O4/Au-AOA and AOA-RhB (a) in the absence of melamine and (b) in the presence of 1.0 µ g/mL of melamine.

Figure 7 .
Figure 7. Raman spectra of the mixture of Fe 3 O 4 /Au-AOA and AOA-RhB (a) in the absence of melamine and (b) in the presence of 1.0 µg/mL of melamine.

Figure 7 .
Figure 7. Raman spectra of the mixture of Fe3O4/Au-AOA and AOA-RhB (a) in the absence of melamine and (b) in the presence of 1.0 µ g/mL of melamine.

Acknowledgments:
The authors wish to acknowledge the financial support of the National Natural Science Foundation of China (Grant No. 31301483), the Zhejiang Provincial Natural Science Foundation of China (Grant No. LY17C200016), the Scientific Research Fund of Zhejiang Provincial Education Department (Grant No. Y201329221), and the Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry.The received funds will cover the costs to publish in open access.