Thermal Sensitive Shape Memory Behavior of Epoxy Composites Reinforced with Silicon Carbide Whiskers

A novel shape memory polymer composite was fabricated by introducing various amounts of silicon carbide whiskers (SiCws) into a shape memory epoxy. The relationship between the thermomechanical properties of the system and structural changes were investigated via dynamic mechanical analysis, scanning electron microscopy, and bending tests. The results show that the bend strength of composites can improve by 64.1% when SiCw content reaches 12 wt %. The shape transition temperatures of SiCw/epoxy composites decreased slightly with the increase in SiCw content, but it was noted that all of the composites showed excellent shape memory properties. The shape fixity ratio increased as SiCw content increased (>99%), and the shape recovery ratio slightly decreased as SiCw content increased (>95%). All of the composites nearly recovered to their original shape within 2 min (not 100%), and the shape recovery speed significantly improved at a higher temperature. It is anticipated that tagging products will be used in the aerospace industry.

Though outstanding in some aspects compared with shape memory alloys and shape memory ceremics, SMPs have obvious shortcomings: low mechanical strength and shape recovery stress.The recovery stress of shape memory alloys can reach as high as 800 megapascals, but the recovery stress of SMPs is usually from a few tenths of a megapascal to a few tens of megapascals.In order to solve this problem, considerable efforts have been made.However, until today, the immediate method has been using high modulus inorganic or organic fillers to reinforce the pristine SMPs.In the past few years, carbon materials, including carbon black, carbon fiber, carbon nanotubes, and graphene, have been widely applied in polymer composites.Ma et al. [22] filled shape memory polyethylene with carbon black to prepare two-way reversible shape memory polymer composites.In the composites, the additional of carbon black nanoparticles has had a beneficial effect on performance in the two-way shape memory effect, and carbon black increased the tensile modulus in the rubbery.Park et al. [23] reinforced shape memory polyurethane with graphene and found that graphene effectively reinforced polyurethane and improved the shape recovery of an SMP composite.
In general, there are two types of SMPs: thermoplastic and thermoset SMPs.Compared with thermoplastic SMPs, thermoset SMPs exhibit a much higher stiffness and dimensional stability, and have better environmental durability.Therefore, thermosetting SMPs have received much of the attention among researchers and are commonly used as matrix materials in structural composites for their high stiffness and shape recovery force.However, the studies have been mostly conducted in tension mode.In the current work, silicon carbide whiskers (SiCws) were used to fill a hydro-epoxy resin to prepare a shape memory polymer composite.SiCws usually act as reinforcement phases to improve the property of a polymer-matrix due to their exceptional mechanical properties, low weight, high aspect ratio, high elastic modulus, chemical stability, and high thermal shock resistance [24][25][26].Moreover, epoxy resins have been associated with a high modulus and strength, and have been widely studied and used in many kinds of structural composites [27].Therefore, SiCws were chosen as the reinforcing phase to fill the shape memory epoxy resin.The effect of the SiCws on the mechanical properties, thermal properties, and shape memory performance of SiCw/hydro-epoxy composites were investigated.

Preparation of Shape Memory SiCw/Hydro-Epoxy Composites
The samples were fabricated by incorporating different contents of high purity SiCws (4, 8, 12, and 16 wt %) into hydro-epoxy resin.Firstly, the SiCws were treated with a silane coupling agent KH-560 for surface treatment.Secondly, a certain proportion of hydro-epoxy and SiCws was stirred evenly at 80 • C, MeTHPA and DMP-30 (the weight ratio of hydro-epoxy/MeTHPA/DMP-30 = 100:80:0.8)were mixed in, and the mixture was then stirred with a magnetic stirrer until the mixture was evenly mixed.After that, the mixtures were sonicated by an ultrasonic dispersion instrument for 20 min.Finally, the mixture was poured into a glass mold for curing, and the curing temperature process was 80

Experimental Methods
In order to investigate the influence of SiCw content on the mechanical properties of SiCw/hydro-epoxy composites, blend tests at room temperature were performed with a SANS tester (Shenzhen SANS Material Test Instrument Co. Ltd., Shenzhen, China) according to ASTM D7264.
The SiCw/hydro-epoxy composites were cut into pieces of 4 × 20 × 20 mm 3 and tested with a thermal constant analyzer (Hot-Disk, AB Company, Bern, Switzerland).
The SiCw/hydro-epoxy composites were cut into 5 × 10 × 30 mm 3 , and the samples were sanded with 800 grit sandpaper (Shandong Lianjie Engineering Materials Co., Ltd., Jinan, China).DMA was performed in a single cantilever clamping fixture and carried out using a Q800 (TA instruments The specimens were frozen in liquid nitrogen and then brittle-fractured.The broken surfaces were sputter-coated with gold and observed with a SEM (INCA X-ACT, Tescan, Brno, Czech Republic).
Rectangular samples (100 × 10 × 3 mm 3 ) were cut to investigate the thermo-active shape memory effect of the SiCw/hydro-epoxy composites.Shape memory performance of the composites were tested as follows: (i) in an oven, the samples were heated to the glass transition temperature (T g ) and held for 5 min; (ii) the samples were bent into a "U" shape and then quickly dipped into ice water, the angle recovery of the "U" shape was measured, and the shape fixity ratio (R f ) was tested; (iii) the "U"-shaped samples were placed into the oven, and the temperature of the oven was set to T g , T g + 10 • C, and T g + 20 • C of the composites; (iv) the shape recovery process of the composites was observed, and, when the shape of the samples did not change, the recovery time was recorded.Figure 1 shows the shape memory model.The shape memory recovery speed is defined as θ i /t, and the shape recovery ratio (R r ) is defined as (θ i − θ f )/θ i × 100% [28], where θ i is the deformation angle ( • ), t is the recovery time, and θ f is the angle of recovery after deformation.The specimens were frozen in liquid nitrogen and then brittle-fractured.The broken surfaces were sputter-coated with gold and observed with a SEM (INCA X-ACT, Tescan, Brno, Czech Republic).
Rectangular samples (100 × 10 × 3 mm 3 ) were cut to investigate the thermo-active shape memory effect of the SiCw/hydro-epoxy composites.Shape memory performance of the composites were tested as follows: (i) in an oven, the samples were heated to the glass transition temperature (Tg) and held for 5 min; (ii) the samples were bent into a "U" shape and then quickly dipped into ice water, the angle recovery of the "U" shape was measured, and the shape fixity ratio (Rf) was tested; (iii) the "U"-shaped samples were placed into the oven, and the temperature of the oven was set to Tg, Tg + 10 °C, and Tg + 20 °C of the composites; (iv) the shape recovery process of the composites was observed, and, when the shape of the samples did not change, the recovery time was recorded.Figure 1 shows the shape memory model.The shape memory recovery speed is defined as θi/t, and the shape recovery ratio (Rr) is defined as (θi − θf)/θi × 100% [28], where θi is the deformation angle (°), t is the recovery time, and θf is the angle of recovery after deformation.

Mechanical Properties
The bending strength and tensile strength are the most important indicators revealing the mechanical property of SiCw/hydro-epoxy composites.The relationship between mechanical properties and SiCw content is shown in Figures 2 and 3. From Figure 2, it can be found that, with the increase in SiCw content, the bending strength of the SiCw/hydro-epoxy composites increases when the SiCw content is less than 12 wt %.The bending strength of the bulk specimen is 72.2 MPa, and the bending strength of sample with 12 wt % SiCw increases by 64.1% compared to the 0 wt %. Figure 3 reveals that the tensile strength of SiCw /hydro-epoxy composites increases first and then decreases with the increase in SiCw content.When the content of the SiCw content is less than 8 wt %, the tensile strength of the SiCw/hydro-epoxy composites increases linearly with the increase in SiCw content.However, the tensile strength increases significantly when the SiCw content rises to 12 wt %, and the tensile strength increases about 77.16% compared with the bulk specimen.However, the tensile strength decreases when the SiCw content increases to 16 wt %.This shows that the SiCw content should be such that the mechanical properties of the SiCw/hydro-epoxy composites are improved.
Considering the effect of SiCw reinforment, the bending strength of the composites will increase [29].However, it was noted that the bending strength of the sample with 16 wt % SiCw decreased significantly; this is due to the proper amount of SiCw can not only strengthen the matrix but also make up the micro defects present in the pure epoxy resin, which can effectively transfer the stress, prevent the crack growth, and improve the mechanical properties of the pure epoxy resin.However, too many SiCws will increase the viscosity of epoxy resin.It is easy to produce bubbles and other defects and destroy the continuous structure of epoxy resin matrix.

Mechanical Properties
The bending strength and tensile strength are the most important indicators revealing the mechanical property of SiCw/hydro-epoxy composites.The relationship between mechanical properties and SiCw content is shown in Figures 2 and 3. From Figure 2, it can be found that, with the increase in SiCw content, the bending strength of the SiCw/hydro-epoxy composites increases when the SiCw content is less than 12 wt %.The bending strength of the bulk specimen is 72.2 MPa, and the bending strength of sample with 12 wt % SiCw increases by 64.1% compared to the 0 wt %. Figure 3 reveals that the tensile strength of SiCw /hydro-epoxy composites increases first and then decreases with the increase in SiCw content.When the content of the SiCw content is less than 8 wt %, the tensile strength of the SiCw/hydro-epoxy composites increases linearly with the increase in SiCw content.However, the tensile strength increases significantly when the SiCw content rises to 12 wt %, and the tensile strength increases about 77.16% compared with the bulk specimen.However, the tensile strength decreases when the SiCw content increases to 16 wt %.This shows that the SiCw content should be such that the mechanical properties of the SiCw/hydro-epoxy composites are improved.
Considering the effect of SiCw reinforment, the bending strength of the composites will increase [29].However, it was noted that the bending strength of the sample with 16 wt % SiCw decreased significantly; this is due to the proper amount of SiCw can not only strengthen the matrix but also make up the micro defects present in the pure epoxy resin, which can effectively transfer the stress, prevent the crack growth, and improve the mechanical properties of the pure epoxy resin.However, too many SiCws will increase the viscosity of epoxy resin.It is easy to produce bubbles and other defects and destroy the continuous structure of epoxy resin matrix.

Thermal Properties Analyses and SEM
Thermal conductivity is one of the key factors for shape memory composites, and the high thermal conductivity favors a reduction in the shape recovery time of the SiCw/hydro-epoxy composites.Figure 4 reveals that the thermal conductivity of the composites was improved with the addition of SiCw filler, and the thermal conductivity increased with increasing SiCw content.This is because, when SiCw content is low, few SiCws are in contact with each other, and thermal conductivity is slightly improved [30].However, with an increase in SiCw content (>12 wt %), the probability of the thermal conductivity chain and thermal conductivity network increased.Thus, the thermal conductivity increased significantly.

Thermal Properties Analyses and SEM
Thermal conductivity is one of the key factors for shape memory composites, and the high thermal conductivity favors a reduction in the shape recovery time of the SiCw/hydro-epoxy composites.Figure 4 reveals that the thermal conductivity of the composites was improved with the addition of SiCw filler, and the thermal conductivity increased with increasing SiCw content.This is because, when SiCw content is low, few SiCws are in contact with each other, and thermal conductivity is slightly improved [30].However, with an increase in SiCw content (>12 wt %), the probability of the thermal conductivity chain and thermal conductivity network increased.Thus, the thermal conductivity increased significantly.

Thermal Properties Analyses and SEM
Thermal conductivity is one of the key factors for shape memory composites, and the high thermal conductivity favors a reduction in the shape recovery time of the SiCw/hydro-epoxy composites.Figure 4 reveals that the thermal conductivity of the composites was improved with the addition of SiCw filler, and the thermal conductivity increased with increasing SiCw content.This is because, when SiCw content is low, few SiCws are in contact with each other, and thermal conductivity is slightly improved [30].However, with an increase in SiCw content (>12 wt %), the probability of the thermal conductivity chain and thermal conductivity network increased.Thus, the thermal conductivity increased significantly.
Dynamic mechanical analysis (DMA) is can not only be used to characterize the mechanical properties of polymers in different temperature fields, but also characterize the glass transition temperature of T g .The T g s of the SiCw/hydro-epoxy composites are the peaks of the tan δ curves, as shown in Figure 5.The storage modulus of the SiCw/hydro-epoxy composites are shown in Figure 6.T g is an important parameter of the themomechanical properties and the shape memory effect of shape memory polymer composites.In this work, the shape memory transition temperature is glass transition temperature (T g ).From Figure 5, it can be found that the T g values of the SiCw/hydro-epoxy Appl.Sci.2017, 7, 108 5 of 10 composites slightly decrease with increasing SiCw content.This phenomenon is due to the addition of the whiskers, reducing the crosslinking density of the epoxy resin, and increasing the peristalsis ability of the molecular chain in the curing network, which leads to the decrease in the T g values of the SiCw/hydro-epoxy composite.Dynamic mechanical analysis (DMA) is can not only be used to characterize the mechanical properties of polymers in different temperature fields, but also characterize the glass transition temperature of Tg.The Tgs of the SiCw/hydro-epoxy composites are the peaks of the tan δ curves, as shown in Figure 5.The storage modulus of the SiCw/hydro-epoxy composites are shown in Figure 6.Tg is an important parameter of the themomechanical properties and the shape memory effect of shape memory polymer composites.In this work, the shape memory transition temperature is glass transition temperature (Tg).From Figure 5, it can be found that the Tg values of the SiCw/hydro-epoxy composites slightly decrease with increasing SiCw content.This phenomenon is due to the addition of the whiskers, reducing the crosslinking density of the epoxy resin, and increasing the peristalsis ability of the molecular chain in the curing network, which leads to the decrease in the Tg values of the SiCw/hydro-epoxy composite.
The storage modulus below the shape memory transition temperature is related to the shape fixity ratio of the composites, and the storage modulus above the shape memory transition temperature is related to the shape recovery ratio [31].It also can be found in Figure 6 that the storage modulus increases with the increase in SiCw content but decreases when SiCw content rises to 16 wt %.For further analysis, the SEM images of the samples were observed.Figure 7 indicates that, when SiCw content is lower than 12 wt %, the whiskers are dispersed in the matrix, and the whiskers cannot contact each other.The interface between the SiCws and the hydro-epoxy resin is smooth, and the fracture surface is ductile fracture.Therefore, the mechanical properties and thermal conductivity of the composites insignificantly improved.When the whisker content increased to 12 wt %, the SiCw network structure was formed in the composites, which can be useful in improving the mechanical properties and thermal conductivity of composites; however, higher SiCw content (w ≥ 16 wt %) caused a serious aggregation that resulted in bubbles in the matrix, which destroy the continuous structure of the resin.Thus, the mechanical properites of the composites decreased.Dynamic mechanical analysis (DMA) is can not only be used to characterize the mechanical properties of polymers in different temperature fields, but also characterize the glass transition temperature of Tg.The Tgs of the SiCw/hydro-epoxy composites are the peaks of the tan δ curves, as shown in Figure 5.The storage modulus of the SiCw/hydro-epoxy composites are shown in Figure 6.
Tg is an important parameter of the themomechanical properties and the shape memory effect of shape memory polymer composites.In this work, the shape memory transition temperature is glass transition temperature (Tg).From Figure 5, it can be found that the Tg values of the SiCw/hydro-epoxy composites slightly decrease with increasing SiCw content.This phenomenon is due to the addition of the whiskers, reducing the crosslinking density of the epoxy resin, and increasing the peristalsis ability of the molecular chain in the curing network, which leads to the decrease in the Tg values of the SiCw/hydro-epoxy composite.
The storage modulus below the shape memory transition temperature is related to the shape fixity ratio of the composites, and the storage modulus above the shape memory transition temperature is related to the shape recovery ratio [31].It also can be found in Figure 6 that the storage modulus increases with the increase in SiCw content but decreases when SiCw content rises to 16 wt %.For further analysis, the SEM images of the samples were observed.Figure 7 indicates that, when SiCw content is lower than 12 wt %, the whiskers are dispersed in the matrix, and the whiskers cannot contact each other.The interface between the SiCws and the hydro-epoxy resin is smooth, and the fracture surface is ductile fracture.Therefore, the mechanical properties and thermal conductivity of the composites insignificantly improved.When the whisker content increased to 12 wt %, the SiCw network structure was formed in the composites, which can be useful in improving the mechanical properties and thermal conductivity of composites; however, higher SiCw content (w ≥ 16 wt %) caused a serious aggregation that resulted in bubbles in the matrix, which destroy the continuous structure of the resin.Thus, the mechanical properites of the composites decreased.The storage modulus below the shape memory transition temperature is related to the shape fixity ratio of the composites, and the storage modulus above the shape memory transition temperature is related to the shape recovery ratio [31].It also can be found in Figure 6 that the storage modulus increases with the increase in SiCw content but decreases when SiCw content rises to 16 wt %.For further analysis, the SEM images of the samples were observed.Figure 7 indicates that, when SiCw content is lower than 12 wt %, the whiskers are dispersed in the matrix, and the whiskers cannot contact each other.The interface between the SiCws and the hydro-epoxy resin is smooth, and the fracture surface is ductile fracture.Therefore, the mechanical properties and thermal conductivity of the composites insignificantly improved.When the whisker content increased to 12 wt %, the SiCw network structure was formed in the composites, which can be useful in improving the mechanical properties and thermal conductivity of composites; however, higher SiCw content (w ≥ 16 wt %) caused a serious aggregation that resulted in bubbles in the matrix, which destroy the continuous structure of the resin.Thus, the mechanical properites of the composites decreased.

Shape Memory Property Analysis
Through the DMA analysis, it can found that the SiCw has a passive effect on the shape fixity ratio.However, because the SiCw does not have shape memory behavior, there is no doubt that the SiCw has a negative effect on the shape recovery ratio of the SiCw/hydro-epoxy composite.In order to analyze the effect of SiCw content on the shape memory properties of the hydro-epoxy system, we tested the shape memory performance of the SiCw/hydro-epoxy composite.The results are shown in Table 1, revealing that, with the increase in SiCw content in the shape memory composites, the shape recovery speed slightly decreased, the shape fixity ratio improved, and the shape recovery ratio significantly decreased.However, the shape recovery ratio of all samples was more than 95%, which indicates that the SiCw/hydro-epoxy composite is an excellent shape memory polymer composite.Figure 8 shows the shape memory process of a specimen with 8 wt % SiCw.Starting from the original shape, the specimen is deformed into a U shape in the oven.Upon cooling under load, the deformed temporary shape is fixed.Then, placing the specimen in the 56 °C oven, full recovery was observed after only 75 s.

Shape Memory Property Analysis
Through the DMA analysis, it can found that the SiCw has a passive effect on the shape fixity ratio.However, because the SiCw does not have shape memory behavior, there is no doubt that the SiCw has a negative effect on the shape recovery ratio of the SiCw/hydro-epoxy composite.In order to analyze the effect of SiCw content on the shape memory properties of the hydro-epoxy system, we tested the shape memory performance of the SiCw/hydro-epoxy composite.The results are shown in Table 1, revealing that, with the increase in SiCw content in the shape memory composites, the shape recovery speed slightly decreased, the shape fixity ratio improved, and the shape recovery ratio significantly decreased.However, the shape recovery ratio of all samples was more than 95%, which indicates that the SiCw/hydro-epoxy composite is an excellent shape memory polymer composite.Figure 8 shows the shape memory process of a specimen with 8 wt % SiCw.Starting from the original shape, the specimen is deformed into a U shape in the oven.Upon cooling under load, the deformed temporary shape is fixed.Then, placing the specimen in the 56 • C oven, full recovery was observed after only 75 s.In fact, the shape memory effect of the polymer composite is determined by two factors.One is the external condition [32].These external conditions include the deformation amplitude, the velocity of deformation, deformation temperature, temporary fixed time, cooling rate, and deformation response times.Different conditions cause different shape memory effects.The other is the structure of the polymer composite [33].Therefore, it is very important to control the external conditions of the shape memory polymer composites when the polymer has the same structures.In this work, we mainly analyzed the effect of the deformation temperature and cycle times on the shape memory performance of the SiCw/hydro-epoxy composites.
The sample with 12 wt % SiCw was used to investigate the effect of the deformation temperature on the shape memory effect of the SiCw/hydro-epoxy composite, as shown in Figure 9.According to the results, the slope of the curves is generally larger from 60° to 120°.This indicates that the shape recovery rate is high.However, the specimens have a relative low recovery rate at the initial and final stages.This increase is because, during the initial stage, the specimen needs time to increase temperature to that of the shape memory transition.The molecular chain slowly begins to creep, and the frozen stress begins to release gradually.After that, the frozen stress releases rapidly, and the shape recovery speed significantly increases.However, during the final stage, there is little frozen stress in the specimen, and the recovery rate thus becomes slow again.In fact, the shape memory effect of the polymer composite is determined by two factors.One is the external condition [32].These external conditions include the deformation amplitude, the velocity of deformation, deformation temperature, temporary fixed time, cooling rate, and deformation response times.Different conditions cause different shape memory effects.The other is the structure of the polymer composite [33].Therefore, it is very important to control the external conditions of the shape memory polymer composites when the polymer has the same structures.In this work, we mainly analyzed the effect of the deformation temperature and cycle times on the shape memory performance of the SiCw/hydro-epoxy composites.
The sample with 12 wt % SiCw was used to investigate the effect of the deformation temperature on the shape memory effect of the SiCw/hydro-epoxy composite, as shown in Figure 9.According to the results, the slope of the curves is generally larger from 60 • to 120 • .This indicates that the shape recovery rate is high.However, the specimens have a relative low recovery rate at the initial and final stages.This increase is because, during the initial stage, the specimen needs time to increase temperature to that of the shape memory transition.The molecular chain slowly begins to creep, and the frozen stress begins to release gradually.After that, the frozen stress releases rapidly, and the shape recovery speed significantly increases.However, during the final stage, there is little frozen stress in the specimen, and the recovery rate thus becomes slow again.
Figure 10 shows the effect of the cycling number on the recovery ratio of SiCw/hydro-epoxy composites.It can be found that the shape recovery ratio of composites slightly decreases with increasing cycling number.However, the shape recovery ratio was gradually balanced when the cycling number was higher than 5.This phenomenon is attributed to the accumulation of plastic deformations in the composites, which inevitably occurs during the recovery process.Moreover, when the deformation occurs more than 5 times, the change in the shape recovery ratio is small, which is due to the stability of the molecular chain and plastic deformations.
stages.This increase is because, during the initial stage, the specimen needs time to increase temperature to that of the shape memory transition.The molecular chain slowly begins to creep, and the frozen stress begins to release gradually.After that, the frozen stress releases rapidly, and the shape recovery speed significantly increases.However, during the final stage, there is little frozen stress in the specimen, and the recovery rate thus becomes slow again.Figure 10 shows the effect of the cycling number on the recovery ratio of SiCw/hydro-epoxy composites.It can be found that the shape recovery ratio of composites slightly decreases with increasing cycling number.However, the shape recovery ratio was gradually balanced when the cycling number was higher than 5.This phenomenon is attributed to the accumulation of plastic deformations in the composites, which inevitably occurs during the recovery process.Moreover, when the deformation occurs more than 5 times, the change in the shape recovery ratio is small, which is due to the stability of the molecular chain and plastic deformations.

Conclusions
A series of thermo-induced shape memory SiCw/hydro-epoxy composites were fabricated.Due to the reinforcement of the SiCws, the mechanical properties of the SiCw/hydro-epoxy composites were improved by 64.1% when SiCw content was 12 wt %.With increasing SiCw content, the shape memory transition temperatures of the SiCw/hydro-epoxy composites slightly decreased, but thermal conductivity increased.The additional SiCws improved the shape fixity ratio of SiCw/hydroepoxy composites, but the shape recovery ratio significantly decreased because the SiCws do not have shape memory effect.The shape recovery speed increased with the increase in test temperature.Though the cycling times have a disadvantageous effect on shape memory behavior, the shape recovery ratio of the composites is higher than 90%.
Castle, DE, USA).The temperature was increased to 180 • C from 20 • C at a rate of 5 • C/min, and the amplitude and dynamic load were 10 um and 1 Hz, respectively.

Figure 8 .
Figure 8. Shape memory process of the hydro-epoxy composites with 8 wt % SiCw at 56 °C.

Figure 9 .
Figure 9. Relationship between recovering angle and recovering time of 12 wt % SiCw/hydro-epoxy composite at different temperatures.

Figure 8 .
Figure 8. Shape memory process of the hydro-epoxy composites with 8 wt % SiCw at 56 • C.

Figure 9 .
Figure 9. Relationship between recovering angle and recovering time of 12 wt % SiCw/hydro-epoxy composite at different temperatures.

Figure 9 .
Figure 9. Relationship between recovering angle and recovering time of 12 wt % SiCw/hydro-epoxy composite at different temperatures.

Figure 10 .
Figure 10.Effects of cycling number on recovery ratio of SiCw/hydro-epoxy composites.

Table 1 .
Effect of SiCw content on the shape memory properties of the hydro-epoxy system.

Table 1 .
Effect of SiCw content on the shape memory properties of the hydro-epoxy system.