Biosynthesis and Biomedical Applications of Gold Nanoparticles Using Eclipta prostrata Leaf Extract

This study reports the biological synthesis of gold nanoparticles (AuNPs) by the reduction of HAuCl4 by using of Eclipta prostrata leaf extract as the reducing and stabilizing agent. AuNPs were characterized using Ultraviolet–visible (UV-vis) spectroscopy, X-ray diffraction (XRD), Fourier Transform-Infrared (FTIR) spectroscopy, Scanning Electron Microscopy (SEM), High Resolution-Transmission Electron Microscopy (HRTEM), and Energy Dispersive X-ray analysis (EDAX). The UV-visible spectrum of the synthesized AuNPs showed surface plasmon resonance (SPR) around 534 nm. The face-centered cubic (FCC) structure of the AuNPs was confirmed by XRD peaks at 38.10 ̋, 44.13 ̋, 64.43 ̋, and 77.32 ̋, which correspond to (111), (200), (220), and (311) miller indices, respectively, with clear circular spots in the selected area electron diffraction (SAED). FTIR measurements showed the AuNPs having a coating of phenolic compounds, indicating a possible role of biomolecules responsible for capping and efficient stabilization of the AuNPs. The HRTEM images determined the particles are spherical, hexagonal, and triangular in shape, with an average size of 31  ̆ 1.6 nm. The synthesized AuNPs show good antibacterial, antioxidant, and cytotoxic activity. The outcomes of this study indicate that these nanoparticles could be effectively utilized in pharmaceutical, biotechnological, and biomedical applications.


Introduction
Metal nanoparticles are utilized not only in research but in many fields of applications, especially in the pharmaceutical and biomedical fields, owing to their improved physical and chemical properties upon size reduction.These particles have a broad range of applications, such as catalysis, biosensing, optoelectronics, chemical sensing, and medical diagnosis [1].Out of various nano-structured materials under research, gold nanoparticles (AuNPs) are of particular interest to scientific community owing to their stability, inertness, and potential applications in biotechnology [2].Additionally, AuNPs can efficiently bind to thiol and amine groups, which help with surface modification and increase their effectiveness in biomedical applications.Various physical and chemical processes have been involved in the synthesis of AuNPs.However, these processes generate a large amount of hazardous byproducts [3].Hence, there has been a growing interest to make a remarkable improvement in the ability to synthesize AuNPs to overcome the disadvantages of the physical and chemical process.It is suggested that the use of plant materials for the synthesis of AuNPs could be more advantageous than the physical and chemical method.Several studies have shown that biomolecules like amino acids, organic acids, phenols, and flavonoids present in plants play a vital role in reducing the metal ions to their respective nanomaterials as well as aid in the capping of the metal NPs, which keeps them stable for a longer period.In addition to this, plant extracts are secure to handle, readily available, and have a wide variety of metabolites that may aid in the reduction of metal salts to NPs [4].
Application of nanotechnology to herbal drugs may lead to the development of nano herbal products possessing high bioavailability and less toxicity, which consequently will open a new era of herbal drug discovery [5].Several plants were productively used for efficient and rapid extracellular production of stable dispersions of AuNPs.Apart from this, plant extracts used for the biosynthesis of gold nanoparticles have gained much more importance due to their simplicity, eco-friendliness, and non-toxic nature [6].Recently, AuNPs were used for cancer cell detection, encapsulation of drugs, nerve cell signaling stimulator, luminescent biomarker, drug delivery, sensor analysis, and membrane filtration, and as nano barcodes, and antimicrobial agents [7].Cancer is one of the most challenging diseases to cure and the second leading cause of death in developed countries.Over the past few decades, it continues to be a worldwide health problem despite the rising number of nanoscaled technologies [8].The synthesis of AuNPs was mediated by an extract of Allium cepa and it was internalized by MCF-7 breast cancer cells via endocytosis [9].AuNPs have recently been investigated for biocompatibility according to their interactions with human breast epithelial MCF-7 cells, which were assessed by cytotoxicity by MTT assay and caspase 3, 9, Bax, and Bcl expression by real-time PCR assays [10].
Eclipta prostrata (Asteraceae) is a perennial herb distributed in the tropical and sub-tropical regions of the world.It is a common weed in moist regions throughout India.There is a potential for medicinal use of this plant as an antiseptic, stringent, depurative, emetic, febrifuge, ophthalmic, purgative, styptic, and tonic, for use against hepatitis, jaundice, liver cirrhosis, aching and weakness of the knees and loins, hematuria and diarrhea with bloody stools, and abnormal uterine bleeding [19].Also, previous phytochemical studies on E. prostrata revealed the presence of thiophene-derivatives, steroids, triterpenes [20,21], flavonoids, polyacetylenes, polypeptides, coumestons, alkaloids, and so on, which are responsible for all its significant traditional medicine properties [22][23][24].
Since the plant extracts may act both as reducing agents and stabilizing agents in the synthesis of nanoparticles [25,26], in the present study, we report the synthesis of AuNPs by reduction of gold ions using E. prostrata extract.AuNPs were characterized with Ultraviolet-visible (UV-vis) spectroscopy, X-ray diffraction (XRD), Fourier Transform-Infrared (FTIR) spectroscopy, Scanning Electron Microscopy (SEM), and High Resolution-Transmission Electron Microscopy (HRTEM).Moreover, Au-NPs were screened for antibacterial, antioxidant (total antioxidant activity, determination of total phenolic contents, and determination of DPPH radical scavenging activity), and anticancer activities (MTT assay, Caspase-3, 8, 9 assays) against Hep-G2 cell lines.In the present study, we report the novel synthesis of AuNPs by reduction of gold ions using E. prostrata aqueous leaf extract.The biotechnological method, capable of producing AuNPs at room temperature and involving assisted template synthesis of AuNPs, is a green, high-yield, fast, and low-cost approach.In addition, the sizes of the particles produced by the one-step synthesis are large enough for the particles to be used in biological applications.

Materials
Fresh and healthy E. prostrata leaves were collected, washed with deionized water, shade dried, and powdered.The HAuCl 4 (99.9%) was obtained from Sigma-Aldrich (Bangalore, India), and all of the other chemicals were also purchased from Sigma-Aldrich and Hi-Media (Mumbai, India).Reagents were purely analytical grade and used without any further purification.

Preparation of Plant Extract
About 10 g of finely cut leaves were weighed and transferred into a 250-mL beaker containing 100 mL distilled water, mixed well, and boiled for 15 min.The extract obtained was filtered through Whatman No.1 filter paper and the filtrate was collected in a 250-mL Erlenmeyer flask and stored in the refrigerator for further use [27].

Biosynthesis of Gold Nanoparticles (AuNPs)
An aqueous solution of HAuCl4 (1.0 mM) was prepared for the synthesis of AuNPs.In particular, a solution of the E. prostrata leaves extract (40 mL) was added to a solution of HAuCl4 (60 mL, 1.0 mM).The stirred solution was incubated at room temperature.The resulting solution showed a color change from light brown to dark brown within 30 min [28].

Characterization of Synthesized AuNPs
The formation and stability of AuNPs in aqueous solutions were initially characterized by UV-visible (Shimadzu UV-1650, Shimadzu, Kyoto, Japan) spectrophotometer in a wavelength range from 200-800 nm.FTIR spectra were recorded at room temperature on a spectrophotometer (PerkinElmer, Waltham, MA, USA).The AuNPs were dried at 60 ˝C for 4 h and mixed with KBr to form a round disk suitable for FTIR measurements.The structural characterization and the crystalline nature of AuNPs were determined by X-ray diffractometer (diffractometer with Philips ® PW 1830 X-ray generator, Philips, Amsterdam, The Netherlands) operating at a voltage of 40 kV and current of 20 mA with Cu Ka radiation (λ 1  4 0.1542 nm) for the freeze-dried AuNPs.The surface morphology of AuNPs was investigated by Scanning Electron Microscopy (SEM), and the samples were prepared by placing a drop over a carbon coated grid and allowing drying before measurement on a Model JFC-1600 (JEOL USA, INC., Peabody, MA, USA).SEM instruments were operated at an accelerated voltage at 20 kV.The morphology of the nanoparticles was analyzed using the images obtained with a JEOL 3010 HRTEM with an accelerating voltage of 100 kV.A thin film of the sample was prepared on a carbon-coated copper grid by dropping a tiny amount of the sample on the grid and drying it under a lamp.A Malvern Zetasizer Nano ZS (Malvern Instruments Ltd., London, UK) Merck 2423 instrument was used to measure the zeta potential.

Antibacterial Activity
The bactericidal activity of AuNPs was tested by the well diffusion method against the pathogenic bacteria Escherichia coli (MTCC 1665), Staphylococcus aureus (MTCC 3160), and Bacilus subtilis (MTCC 441).Briefly, the individual bacterial strain was swabbed on three axes with a sterile cotton-tipped swab that was first dipped in the freshly prepared diluted culture.Approximately the same amount of bacterial cultures of both the strains was spread over Petri plate to create a confluent lawn of bacterial growth.A 7 mm diameter well was made on the MHA plate.The cultures were swabbed on test media with a sterile cotton swab.About 25 µL of synthesized particles were inoculated to the well, and then the plates were incubated at 37 ˝C for 24 h.Tetracycline was used as a positive control (30 mcg/µL).All experiments were conducted in triplicate, and the results were concurrent [29].

Evaluation of Total Antioxidant Activity
The total antioxidant activities of the synthesized AuNPs and aqueous leaves extract were analyzed.First 0.1 gm of the synthesized AuNPs and aqueous leaves extract were taken into a reaction vial at different concentrations (100-500 µg/mL) and mixed with 0.05% DMSO.Then 0.1 mL aliquot of the sample was mixed with 1 mL of the reagent solution (0.6 M sulfuric acid, 28 mM sodium phosphate, and 4 mM ammonium molybdate).The tubes were capped and then incubated at 95 ˝C for 90 min.The samples were cooled to 25 ˝C, and the absorbance was measured at 695 nm against a blank.The blank contained 1 mL of the reagent solution without the samples.The total antioxidant activity was expressed as the absorbance of samples.The higher the absorbance value, the higher the antioxidant activity.Ascorbic acid was also assayed for comparison [30].

Determination of DPPH Radical Scavenging Activity
AuNPs were screened for DPPH free radical scavenging activity by the method described by Chang et al. [31] with little modification.Briefly, 0.5 mL of 1.5m MDPPH was mixed with different concentrations (31-1000 mg/mL) of gold nanoparticles and incubated in dark for 30 min.After incubation, the absorbance of the samples was determined by UV spectrophotometer (Shimadzu UV-1650, Shimadzu, Kyoto, Japan) at 517 nm.DPPH methanol reagent without sample was used as a control, and Vitamin C was used as a standard.

Cytotoxicity Study of Hep-G2 Cell Line
To evaluate the cytotoxicity of aqueous leaf extract of E. prostrata and AuNPs, Hep-G2 cells were collected in the exponential phase of growth, seeded into 96-well tissue culture plates (15,000 per well), and allowed to adhere for 24 h.Then, 1, 10, 100, 250, and 500 µg/mL concentrations of aqueous leaf extract of E. prostrata and AuNPs were added to the desired wells and incubated for 48 h.After incubation, 20 µL of an EMEM medium containing MTT (3-[4,5-dimethylthiazol-2-yl]-2,5diphenyltetrazolium bromide) (5 mg/mL) was added to each well and incubated at 37 ˝C for 4 h.Subsequently, the medium was changed with 100 µL of DMSO, and optical densities were measured at 570 nm.All the measurements were made in triplicate and expressed as the mean ˘standard error (Mosmann [32] and Kang et al. [33]).

Statistical Analysis
All experiments were carried out in triplicate and data were analyzed.For the experiments of antimicrobial activity, arithmetic mean values were considered for data analysis.All the statistical analysis was done by SPSS Statistics 18 Release Version 18.0.0,2009 (BM Corporation, Armonk, NY, USA).

Visual Observations and UV-Vis Spectroscopy
The UV-visible spectral analysis confirmed the formation and stability of the biosynthesized AuNPs using the leaves extract of E. prostrata.At 534 nm wavelength, the optimum AuNPs production was determined at 60 ˝C, pH 7 with 1 mM HAuCl 4 , and 45 min incubation period (Figure 1).Reduction of AuCl 4 ´was visually evident from the color change and the synthesis process completed within 90 min, with a stable ruby-red color indicating the formation of AuNPs.A peak observed in the UV-visible spectrum corresponding to the SPR occurs at 534 nm and clearly showed the formation of AuNPs in solution as the exact position of absorbance depends on some factors such as the dielectric constants of the medium and size of the particle.It was observed that the crystalline shape of the biosynthesized AuNPs was dependent on the quantity of Au + ions in solution and the biomolecules or factors from the leaf extract of E. prostrata.

X-Ray Diffraction (XRD) Analysis
XRD performed the structural analysis of AuNPs prepared from the alkaline-treated sample.The XRD pattern of synthesized AuNPs showed pure crystalline gold nature (Figure 2).Reflection peaks appeared at 38.10°, 44.13°, 64.43°, and 77.32° which correspond to (111), ( 200), (220), and (311) Miller indices, respectively.Taking into account the angular positions of the Bragg peaks, the facecentered cubic (FCC) structure was assigned to the gold nanostructures.The majority of the gold nanostructured samples were preferentially oriented along the (111) plane.Another less intense, board peak was observed, oriented along the (200) plane.The observed ′d-values′ of the samples (from XRD patterns) correlate well with the standard ′d-values′ from the JCPDS data card 04-0784 for Au and confirming the formation of AuNPs.The characteristic of FCC structure and the broadening of peaks confirmed the formation of NPs.The Scherrer equation was used to calculate average particle size and the size was found to be 28 ± 1.5 nm.Similar results were observed by Noruzi et al. [34], who reported that the XRD pattern was crystalline in nature and noted reflection peaks indicating the high purity of AuNPs synthesized by an aqueous extract of cypress leaves.

X-Ray Diffraction (XRD) Analysis
XRD performed the structural analysis of AuNPs prepared from the alkaline-treated sample.The XRD pattern of synthesized AuNPs showed pure crystalline gold nature (Figure 2).Reflection peaks appeared at 38.10 ˝, 44.13 ˝, 64.43 ˝, and 77.32 ˝which correspond to (111), ( 200), (220), and (311) Miller indices, respectively.Taking into account the angular positions of the Bragg peaks, the face-centered cubic (FCC) structure was assigned to the gold nanostructures.The majority of the gold nanostructured samples were preferentially oriented along the (111) plane.Another less intense, board peak was observed, oriented along the (200) plane.The observed 1 d-values 1 of the samples (from XRD patterns) correlate well with the standard 1 d-values 1 from the JCPDS data card 04-0784 for Au and confirming the formation of AuNPs.The characteristic of FCC structure and the broadening of peaks confirmed the formation of NPs.The Scherrer equation was used to calculate average particle size and the size was found to be 28 ˘1.5 nm.Similar results were observed by Noruzi et al. [34], who reported that the XRD pattern was crystalline in nature and noted reflection peaks indicating the high purity of AuNPs synthesized by an aqueous extract of cypress leaves.

X-Ray Diffraction (XRD) Analysis
XRD performed the structural analysis of AuNPs prepared from the alkaline-treated sample.The XRD pattern of synthesized AuNPs showed pure crystalline gold nature (Figure 2).Reflection peaks appeared at 38.10°, 44.13°, 64.43°, and 77.32° which correspond to (111), ( 200), (220), and (311) Miller indices, respectively.Taking into account the angular positions of the Bragg peaks, the facecentered cubic (FCC) structure was assigned to the gold nanostructures.The majority of the gold nanostructured samples were preferentially oriented along the (111) plane.Another less intense, board peak was observed, oriented along the (200) plane.The observed ′d-values′ of the samples (from XRD patterns) correlate well with the standard ′d-values′ from the JCPDS data card 04-0784 for Au and confirming the formation of AuNPs.The characteristic of FCC structure and the broadening of peaks confirmed the formation of NPs.The Scherrer equation was used to calculate average particle size and the size was found to be 28 ± 1.5 nm.Similar results were observed by Noruzi et al. [34], who reported that the XRD pattern was crystalline in nature and noted reflection peaks indicating the high purity of AuNPs synthesized by an aqueous extract of cypress leaves.

FTIR Spectroscopy
FTIR analysis showed the absorption peaks at 3351, 1671, 1405, 1038, and 597 cm ´1 (Figure 3) for the synthesis of AuNPs.The absorption band at 3351 cm ´1 for Hydroxy group, H-bonded OH stretch, 1671 cm ´1 for Amide [35], 1405 cm ´1 which expose symmetric stretching of COO ´from an amino group, 1038 cm ´1 for Phosphate ion, and 597 cm ´1 for Alcohol, OH out-of-plane bend.

FTIR Spectroscopy
FTIR analysis showed the absorption peaks at 3351, 1671, 1405, 1038, and 597 cm −1 (Figure 3) for the synthesis of AuNPs.The absorption band at 3351 cm −1 for Hydroxy group, H-bonded OH stretch, 1671 cm −1 for Amide [35], 1405 cm −1 which expose symmetric stretching of COO − from an amino group, 1038 cm −1 for Phosphate ion, and 597 cm −1 for Alcohol, OH out-of-plane bend.The proposed reaction was Au + ions' reduction into metallic Au nanoparticles in the presence of metabolites and redox enzymes [36].The significant reduction in reaction time with Eclipta leaf is an important result and will enable nanoparticle biosynthesis methods to compete with other plantassisted biosynthesis routes for the formation of nanoparticles that are currently much more rapid and reproducible [37].The IR band proved the presence of amines, alcohols, phenols, and aromatic groups and strongly suggested the presence of certain proteins in Eclipta prostrata that act as reducing/capping agents and may be responsible for the synthesis of AuNPs using leaves of E. prostrata.

SEM-EDX Analysis
The SEM analysis clearly showed the presence of the synthesized AuNPs.NPs ranging from 25 to 40 nm with an average size of 32 ± 1.1 were observed in the surface morphology of AuNPs.It was noted that smaller sized particles were almost spherical in shape, and some of them were aggregated (Figure 4a).Similar results were found in Kumar et al. [38]: the SEM micrographs showed aggregates of Zingiber officinale synthesized AuNPs, and the particles were in the range of 15-25 nm and are not in direct contact even within the aggregates, indicating the stabilization of NPs by the capping agents.The EDX analysis shown in Figure 4b revealed that a strong signal of Au peak was observed at approximately 3.6 keV, which is typical for the absorption of metallic gold nanocrystallites due to SPR.The proposed reaction was Au + ions' reduction into metallic Au nanoparticles in the presence of metabolites and redox enzymes [36].The significant reduction in reaction time with Eclipta leaf is an important result and will enable nanoparticle biosynthesis methods to compete with other plant-assisted biosynthesis routes for the formation of nanoparticles that are currently much more rapid and reproducible [37].The IR band proved the presence of amines, alcohols, phenols, and aromatic groups and strongly suggested the presence of certain proteins in Eclipta prostrata that act as reducing/capping agents and may be responsible for the synthesis of AuNPs using leaves of E. prostrata.

SEM-EDX Analysis
The SEM analysis clearly showed the presence of the synthesized AuNPs.NPs ranging from 25 to 40 nm with an average size of 32 ˘1.1 were observed in the surface morphology of AuNPs.It was noted that smaller sized particles were almost spherical in shape, and some of them were aggregated (Figure 4a).Similar results were found in Kumar et al. [38]: the SEM micrographs showed aggregates of Zingiber officinale synthesized AuNPs, and the particles were in the range of 15-25 nm and are not in direct contact even within the aggregates, indicating the stabilization of NPs by the capping agents.The EDX analysis shown in Figure 4b revealed that a strong signal of Au peak was observed at approximately 3.6 keV, which is typical for the absorption of metallic gold nanocrystallites due to SPR.

FTIR Spectroscopy
FTIR analysis showed the absorption peaks at 3351, 1671, 1405, 1038, and 597 cm −1 (Figure 3) for the synthesis of AuNPs.The absorption band at 3351 cm −1 for Hydroxy group, H-bonded OH stretch, 1671 cm −1 for Amide [35], 1405 cm −1 which expose symmetric stretching of COO − from an amino group, 1038 cm −1 for Phosphate ion, and 597 cm −1 for Alcohol, OH out-of-plane bend.The proposed reaction was Au + ions' reduction into metallic Au nanoparticles in the presence of metabolites and redox enzymes [36].The significant reduction in reaction time with Eclipta leaf is an important result and will enable nanoparticle biosynthesis methods to compete with other plantassisted biosynthesis routes for the formation of nanoparticles that are currently much more rapid and reproducible [37].The IR band proved the presence of amines, alcohols, phenols, and aromatic groups and strongly suggested the presence of certain proteins in Eclipta prostrata that act as reducing/capping agents and may be responsible for the synthesis of AuNPs using leaves of E. prostrata.

SEM-EDX Analysis
The SEM analysis clearly showed the presence of the synthesized AuNPs.NPs ranging from 25 to 40 nm with an average size of 32 ± 1.1 were observed in the surface morphology of AuNPs.It was noted that smaller sized particles were almost spherical in shape, and some of them were aggregated (Figure 4a).Similar results were found in Kumar et al. [38]: the SEM micrographs showed aggregates of Zingiber officinale synthesized AuNPs, and the particles were in the range of 15-25 nm and are not in direct contact even within the aggregates, indicating the stabilization of NPs by the capping agents.The EDX analysis shown in Figure 4b revealed that a strong signal of Au peak was observed at approximately 3.6 keV, which is typical for the absorption of metallic gold nanocrystallites due to SPR.

HRTEM Analysis and SAED Pattern
The morphology and size of the particles were determined by the HRTEM images shown in Figure 5a.The particles formed were spherical, hexagonal, and triangular in shape.The NPs formed were in the range of 23 to 46 nm with an average size of 31 ˘1.6 nm.The SAED of a single spherical particle confirmed the crystalline nature of AuNPs and the rings corresponding to (111), ( 200) and ( 220) planes of FCC crystalline lattices of gold (Figure 5b).The reflection patterns indicated that the surfaces of the gold plates were flat and crystalline in nature.Similar results were found in AuNPs synthesized using ethonolic leaf extract of Bacopa monnieri: they were predominantly spherical in shape with a size distribution range of 3-45 nm [39].

HRTEM Analysis and SAED Pattern
The morphology and size of the particles were determined by the HRTEM images shown in Figure 5a.The particles formed were spherical, hexagonal, and triangular in shape.The NPs formed were in the range of 23 to 46 nm with an average size of 31 ± 1.6 nm.The SAED of a single spherical particle confirmed the crystalline nature of AuNPs and the rings corresponding to (111), ( 200) and (220) planes of FCC crystalline lattices of gold (Figure 5b).The reflection patterns indicated that the surfaces of the gold plates were flat and crystalline in nature.Similar results were found in AuNPs synthesized using ethonolic leaf extract of Bacopa monnieri: they were predominantly spherical in shape with a size distribution range of 3-45 nm [39].

Zeta Potential Analysis
Zeta potential (ZP) values reveal information regarding the surface charge and stability of biosynthesized AuNPs.As can be seen from Figure 6, the average ZP value of −17.4 mV indicated that the capping molecules present on the surface of AuNPs are mainly comprised of negatively charged groups and also responsible for moderate stability of the nanoparticles.The sample did not precipitate for a period of one month, indicating that the AuNPs are stable for a reasonable period of time.Many reports have proposed that surface-active molecules can stabilize the nanoparticles and a reaction of the metal ions is possibly facilitated by reducing sugars and/or terpenoids.

Zeta Potential Analysis
Zeta potential (ZP) values reveal information regarding the surface charge and stability of biosynthesized AuNPs.As can be seen from Figure 6, the average ZP value of ´17.4 mV indicated that the capping molecules present on the surface of AuNPs are mainly comprised of negatively charged groups and also responsible for moderate stability of the nanoparticles.The sample did not precipitate for a period of one month, indicating that the AuNPs are stable for a reasonable period of time.Many reports have proposed that surface-active molecules can stabilize the nanoparticles and a reaction of the metal ions is possibly facilitated by reducing sugars and/or terpenoids.

HRTEM Analysis and SAED Pattern
The morphology and size of the particles were determined by the HRTEM images shown in Figure 5a.The particles formed were spherical, hexagonal, and triangular in shape.The NPs formed were in the range of 23 to 46 nm with an average size of 31 ± 1.6 nm.The SAED of a single spherical particle confirmed the crystalline nature of AuNPs and the rings corresponding to (111), ( 200) and (220) planes of FCC crystalline lattices of gold (Figure 5b).The reflection patterns indicated that the surfaces of the gold plates were flat and crystalline in nature.Similar results were found in AuNPs synthesized using ethonolic leaf extract of Bacopa monnieri: they were predominantly spherical in shape with a size distribution range of 3-45 nm [39].

Zeta Potential Analysis
Zeta potential (ZP) values reveal information regarding the surface charge and stability of biosynthesized AuNPs.As can be seen from Figure 6, the average ZP value of −17.4 mV indicated that the capping molecules present on the surface of AuNPs are mainly comprised of negatively charged groups and also responsible for moderate stability of the nanoparticles.The sample did not precipitate for a period of one month, indicating that the AuNPs are stable for a reasonable period of time.Many reports have proposed that surface-active molecules can stabilize the nanoparticles and a reaction of the metal ions is possibly facilitated by reducing sugars and/or terpenoids.

Calculation of Average Number of Gold Atoms per Nanoparticle
The average number of gold atoms per nanoparticle may be calculated from high-resolution TEM analysis [40].The HRTEM images of the synthesized gold nanoparticles shows the average particle size of about 31 ˘1.6 nm (D, nm).Assuming a spherical shape and a uniform FCC structure [41], the average number of gold atoms (N) for each type of nanosphere was calculated by the following equation, where ρ is the density for FCC gold (19.3 g/cm 3 ) [42,43] and M stands for atomic weight of gold (197 g/mol): On applying the above equation, the average number of gold atoms per synthesized nanoparticle was found to be in the range from 885,251.797 to 1,070,422.767atoms.

Antibacterial Activity
The antibacterial activity of the AuNPs was studied against gram-positive (B.substilis and S. aureus) and gram-negative (E.coli) using the well diffusion method (Figure 7).The highest antibacterial activity was observed against E. coli (24 ˘0.67 nm), followed in order by S. aureus (16 ˘0.91 nm) and B. substilis (12 ˘0.13 nm).However, a leaf extract of E. prostrata did not show any significant antibacterial activity, whereas the AuNPs showed maximum bactericidal activity.AuNPs possess well-developed surface chemistry, chemical stability, and a large surface-to-volume ratio, due to which more drug molecules get adsorbed on their surfaces via electrostatic attraction between the amino group of drugs and nanoparticles.The gold nanoparticles surrounded by some drug moieties now act as a single group against the microbial organisms, thereby increasing the microbial activity [44].AuNPs may initially get anchored to bacterial cell wall and interact with the peptidoglycan layer, thereby causing the breakage of bonds and entering inside the cell to cause perforations at the exterior [45].This result reveals that the AuNPs synthesized here have effective antibacterial activity, and they contribute the most to the antibacterial capability of AuNPs.

Calculation of Average Number of Gold Atoms per Nanoparticle
The average number of gold atoms per nanoparticle may be calculated from high-resolution TEM analysis [40].The HRTEM images of the synthesized gold nanoparticles shows the average particle size of about 31 ± 1.6 nm (D, nm).Assuming a spherical shape and a uniform FCC structure [41], the average number of gold atoms (N) for each type of nanosphere was calculated by the following equation, where ρ is the density for FCC gold (19.3 g/cm 3 ) [42,43] and M stands for atomic weight of gold (197 g/mol): On applying the above equation, the average number of gold atoms per synthesized nanoparticle was found to be in the range from 885,251.797 to 1,070,422.767atoms.

Antibacterial Activity
The antibacterial activity of the AuNPs was studied against gram-positive (B.substilis and S. aureus) and gram-negative (E.coli) using the well diffusion method (Figure 7).The highest antibacterial activity was observed against E. coli (24 ± 0.67 nm), followed in order by S. aureus (16 ± 0.91 nm) and B. substilis (12 ± 0.13 nm).However, a leaf extract of E. prostrata did not show any significant antibacterial activity, whereas the AuNPs showed maximum bactericidal activity.AuNPs possess well-developed surface chemistry, chemical stability, and a large surface-to-volume ratio, due to which more drug molecules get adsorbed on their surfaces via electrostatic attraction between the amino group of drugs and nanoparticles.The gold nanoparticles surrounded by some drug moieties now act as a single group against the microbial organisms, thereby increasing the microbial activity [44].AuNPs may initially get anchored to bacterial cell wall and interact with the peptidoglycan layer, thereby causing the breakage of bonds and entering inside the cell to cause perforations at the exterior [45].This result reveals that the AuNPs synthesized here have effective antibacterial activity, and they contribute the most to the antibacterial capability of AuNPs.

Evaluation of Total Antioxidant Activity
Using an aqueous leaf extract of E. prostrata, the total antioxidant activity was found to be high in synthesized NPs at different concentrations between 100 and 500 μg/mL.The aqueous leaf extract of E. prostrata showed 0.67 ± 0.78 mg gallic acid equivalent/g (mg GAE/g) and for standard ascorbic acid 0.75 ± 0.84 mg GAE/g followed by AuNPs 0.91 ± 0.24 mg GAE/g, at the concentration of 500 μg/mL respectively (Figure 8a).

Evaluation of Total Antioxidant Activity
Using an aqueous leaf extract of E. prostrata, the total antioxidant activity was found to be high in synthesized NPs at different concentrations between 100 and 500 µg/mL.The aqueous leaf extract of E. prostrata showed 0.67 ˘0.78 mg gallic acid equivalent/g (mg GAE/g) and for standard ascorbic acid 0.75 ˘0.84 mg GAE/g followed by AuNPs 0.91 ˘0.24 mg GAE/g, at the concentration of 500 µg/mL respectively (Figure 8a).

Determination of DPPH Radical Scavenging Activity
To assess the antioxidant activity of E. prostrata extract and as synthesized AuNPs, DPPH was used as a free radical model and treated with varying concentrations (100-500 µg/mL) of E. prostrata extract and AuNPs.The percentage of inhibition of DPPH radical scavenging activity is presented in Figure 8b.The average percentage inhibition of synthesized AuNPs (63%) and powdered leaves of E. prostrata was 48%, and control of ascorbic acid showed 95% in 500 µg/mL concentration.The AuNPs coated with torolex and chitosan enhance the DPPH radical scavenging activity [46].

Determination of DPPH Radical Scavenging Activity
To assess the antioxidant activity of E. prostrata extract and as synthesized AuNPs, DPPH was used as a free radical model and treated with varying concentrations (100-500 μg/mL) of E. prostrata extract and AuNPs.The percentage of inhibition of DPPH radical scavenging activity is presented in Figure 8b.The average percentage inhibition of synthesized AuNPs (63%) and powdered leaves of E. prostrata was 48%, and control of ascorbic acid showed 95% in 500 μg/mL concentration.The AuNPs coated with torolex and chitosan enhance the DPPH radical scavenging activity [46]

Cytotoxicity Study of Hep-G2 Cell Line
The aqueous leaf extract of E. prostrata and synthesized AuNPs were tested at 1-500 μg/mL, which provided cellular toxicity of 7.5%, 12%, 22%, 32%, and 39% for the aqueous leaf extract of E. prostrata and for synthesized AuNPs 16%, 28%, 40%, 57%, and 69%, respectively.The plaque formations of the Hep-G2 cell lines were found to induce cytopathic effects and necrosis formation.The viability was in inverse proportion to the cellular regeneration of Hep-G2 (Figure 9a-f).The results of this study suggest that the cytotoxicity of biologically synthesized AuNPs increased with the increasing concentration of nanoparticles.AuNPs of certain non-irregular shapes can be adsorbed readily to the surface of the biomolecules, which show higher surface plasmon resonance and will have a greater contrast effect than those of photothermal dyes that are used regularly in the detection of cancer cell lines [47,48].In Figure 10, it is also quite clear that the test samples showed concentration-dependent cytotoxic effect on cancerous cells.This observation is comparable with the report published by Milovanovic et al. on gold(III)-monoethylenediamine complexes on chronic lymphocytic leukemia (CLL) cells [49].From the results of biological analysis, it is established that our AuNPs are possible candidates for use in nanotherapy.AuNPs possess good cytotoxicity properties and biocompatibility.

Cytotoxicity Study of Hep-G2 Cell Line
The aqueous leaf extract of E. prostrata and synthesized AuNPs were tested at 1-500 µg/mL, which provided cellular toxicity of 7.5%, 12%, 22%, 32%, and 39% for the aqueous leaf extract of E. prostrata and for synthesized AuNPs 16%, 28%, 40%, 57%, and 69%, respectively.The plaque formations of the Hep-G2 cell lines were found to induce cytopathic effects and necrosis formation.The viability was in inverse proportion to the cellular regeneration of Hep-G2 (Figure 9a-f).The results of this study suggest that the cytotoxicity of biologically synthesized AuNPs increased with the increasing concentration of nanoparticles.AuNPs of certain non-irregular shapes can be adsorbed readily to the surface of the biomolecules, which show higher surface plasmon resonance and will have a greater contrast effect than those of photothermal dyes that are used regularly in the detection of cancer cell lines [47,48].In Figure 10, it is also quite clear that the test samples showed concentration-dependent cytotoxic effect on cancerous cells.This observation is comparable with the report published by Milovanovic et al. on gold(III)-monoethylenediamine complexes on chronic lymphocytic leukemia (CLL) cells [49].From the results of biological analysis, it is established that our AuNPs are possible candidates for use in nanotherapy.AuNPs possess good cytotoxicity properties and biocompatibility.

Conclusion
In the present study, a green synthesis approach using the leaf extract of E. prostrata was successful for preparing functionally stable and crystalline AuNPs.This method is easy, efficient, and eco-friendly, and is the best option for metal.
Nanoparticles synthesis was compared to other methods.The prepared nanoparticles were characterized to confirm their formation using UV-vis, XRD, FTIR, SEM, HRTEM, and EDAX

Conclusion
In the present study, a green synthesis approach using the leaf extract of E. prostrata was successful for preparing functionally stable and crystalline AuNPs.This method is easy, efficient, and eco-friendly, and is the best option for metal.
Nanoparticles synthesis was compared to other methods.The prepared nanoparticles were characterized to confirm their formation using UV-vis, XRD, FTIR, SEM, HRTEM, and EDAX

Conclusions
In the present study, a green synthesis approach using the leaf extract of E. prostrata was successful for preparing functionally stable and crystalline AuNPs.This method is easy, efficient, and eco-friendly, and is the best option for metal.
Nanoparticles synthesis was compared to other methods.The prepared nanoparticles were characterized to confirm their formation using UV-vis, XRD, FTIR, SEM, HRTEM, and EDAX analysis.From the UV-visible spectrum, the absorbance at 534 nm confirms the presence of AuNPs.The XRD pattern reveals that the prepared AuNPs have a face-centered cubic structure with 2θ values at 38.10 ˝, 44.13 ˝, 64.43 ˝, and 77.32 ˝.FTIR spectrum results confirmed the presence of AuNPs with the phytochemicals that are responsible for their conversion.Zeta potential (ZP) values (´17.4 mV) showed a negative charge density with moderate stability of the synthesized nanoparticles.The HRTEM images showed spherical, hexagonal, and triangular morphology with an average size of 31 ˘1.6 nm, and the biomedical evaluation proved that the synthesized AuNPs are biocompatible.

Figure 1 .
Figure 1.UV-vis spectral analysis and color intensity of biosynthesized NPs at various time intervals of AuNPs (gold nanoparticles) at 45 min.The inset shows the color change from ruby-red to dark black color.

Figure 1 .
Figure 1.UV-vis spectral analysis and color intensity of biosynthesized NPs at various time intervals of AuNPs (gold nanoparticles) at 45 min.The inset shows the color change from ruby-red to dark black color.

Figure 4 .
Figure 4. (a) Scanning electron microscope (SEM) micrograph showed the synthesized of AuNPs using E. prostrata leaf aqueous extract (× 40,000) and (b) EDX analysis showing the chemical composition of synthesized AuNPs.

Figure 5 .
Figure 5. (a) High-resolution transmission electron microscopy (HRTEM) micrograph of synthesized AuNPs; (b) selected area of electron diffraction pattern (SAED) of the synthesized AuNPs showing the rings.

Figure 5 .
Figure 5. (a) High-resolution transmission electron microscopy (HRTEM) micrograph of synthesized AuNPs; (b) selected area of electron diffraction pattern (SAED) of the synthesized AuNPs showing the rings.

Figure 5 .
Figure 5. (a) High-resolution transmission electron microscopy (HRTEM) micrograph of synthesized AuNPs; (b) selected area of electron diffraction pattern (SAED) of the synthesized AuNPs showing the rings.

Figure 6 .
Figure 6.Stability of AuNPs at ´17.4 mV in zeta potential analysis.

Figure 6 .
Figure 6.Stability of AuNPs at −17.4 mV in zeta potential analysis.

Figure 10 .
Figure 10.Anticancer activity of aqueous leaf extract of E. prostrata and AuNPs on a Hep-G2 cancer cell line.

Figure 10 .
Figure 10.Anticancer activity of aqueous leaf extract of E. prostrata and AuNPs on a Hep-G2 cancer cell line.

Figure 10 .
Figure 10.Anticancer activity of aqueous leaf extract of E. prostrata and AuNPs on a Hep-G2 cancer cell line.