MoSe 2 with Ultra-Fine Pt Decoration for Efficient Photodegradation

: Transition metal dichalcogenides are widely studied for their photocatalytic ability due to the adjustable bandgap, high carrier mobility and possibility of foreign-element doping. In this work, multilayer molybdenum diselenide (MoSe 2 ) was decorated with ultra-fine Pt nanoparticles through the mild hydrothermal method. MoSe 2 -Pt nanocomposites were synthesized and showed good structural and chemical stabilities. The incorporation of Pt nanoparticles provides plenty of active sites for MoSe 2 . The dominant Pt particle sizes are 1.8 nm, 1.8 nm, and 1.9 nm for the three synthesized samples, respectively. The mean crystal sizes of Pt (111) were calculated from X-ray diffraction patterns and we found that they were in accordance with the particle sizes. Both the particle sizes and mean crystal sizes are related to the synthesis conditions. X-ray photoelectron spectroscopy (XPS) characterizations revealed the formation of Se–Pt bonding. The relative contents of Pt–Se bonding were also calculated from XPS results, and they show the same trends as the optical absorption properties. Combining the XPS and optical absorption results, the effects of Se–Pt bonding during the photo-related process could be further confirmed. By degrading methylene blue (MB) under visible light, the synthesized nanocomposites proved promising for application in real-case degradation of organic pollutants. The sample synthesized with a moderate content of MoSe 2 exhibited the best photodegradation efficiency, which could be explained by the maximum Pt-Se contents. Based on the experimental findings, we proposed a possible photodegradation mechanism.


Introduction
Photodegradation of organic pollutants in natural water has been studied for several decades [1,2].By employing sunlight and semiconducting materials, redox reactions could be taking place to degrade and remove those dissolved pollutants, especially organic dyes [3] such as methylene blue, methyl orange, bisphenol A (BPA), etc.It provides a green and sustainable route for natural water purification.Among so many semiconducting candidates, transition metal dichalcogenides (TMDs) are known for their suitable bandgaps for visible light absorption and utilization [4,5].As layered two-dimensional materials, TMDs are formed by covalence bonds in layers and van der Waals forces between layers [6].Such a layered structure also brings an adjustable bandgap which can be easily manipulated by controlling the layer numbers [7].They usually have active edge sites due to various types of defects but a relatively inert basal surface [8,9].Thanks to their host ability for incorporating dopants, especially noble metal nanoparticles, the light-matter interaction as well as the photocatalytic performance could be improved.In this case, members of the TMD group are currently featured as photocatalysts for hydrogen evolution and organicpollutant decomposition in water [10].It is believed that the TMDs would hopefully provide a solution towards current fossil fuel deficiency and natural water pollution problems.
As a typical member of the TMD family, molybdenum diselenide (MoSe 2 ) has similar atomic arrangements to molybdenum disulfide (MoS 2 ) [11], and has been widely investigated for applications such as transistors, gas sensors, photodetectors and photocatalysts [12,13].For example, n-MoSe 2 transistors perform well in detecting the streptavidin molecule, due to the controllable high reverse current [14].As for photocatalytic ability, researchers proposed the hydrothermal synthesis method to prepare MoSe 2 for hydrogen evolution reactions and organic dye degradations [15].MoSe 2 is stacked into layers of Se-Mo-Se sandwich planes through the van der Waals force.The typically tunable bandgap also exists in MoSe 2 , making it suitable for light absorption among a wide range of wavelengths.It should be mentioned that MoSe 2 has relatively smaller band gap than MoS 2 , which brings more efficient photoexcitation [16].In the photocatalytic applications, researchers proposed several routes to improve its total activities.For instance, the typical core-shell structures are beneficial for strong chemical activities which could be achieved by incorporating carbon nanotubes, MoS 2 nanoflakes, and transition metals, especially noble metals [17][18][19][20][21].The optical absorption of MoSe 2 has been successfully adjusted by phase engineering, providing another choice for obtaining efficient photocatalytic performance [22].Moreover, it is also possible to form Z-scheme nanocomposites by introducing other semiconducting materials [23,24].Among the above methods, noble-metal doping is an effective and controllable way.Noble metal nanoparticles could be easily anchored to MoSe 2 edges due to the commonly existing Se defects.However, it usually requires sophisticated synthesis to activate the inert MoSe 2 basal planes [8].For instance, there should be a pre-synthesis to prepare MoSe 2 @mesoporous hollow carbon spheres, and the following step to obtain the incorporation of Pt nanoparticles [25].
Herein, we report a feasible and straightforward synthetic method to introduce Pt nanoparticles onto MoSe 2 .The Pt nanoparticles are well formed and their sizes are controlled within 2.3 nm, which could be called ultra-fine Pt nanoparticles.The synthesized MoSe 2 -Pt nanocomposites exhibit great structural and chemical stabilities.The introduced Pt nanoparticles provide plenty of active sites for light absorption and photocatalysis.We performed the photodegradation of MB under visible light irradiation.It has been found that the synthesized materials could decompose MB efficiently compared to pristine MoSe 2 .Such improved photocatalytic performance has been explained by the enhanced light absorption and photoelectron transportation.Using X-ray photoelectron spectroscopy (XPS), the chemical bonding between Se and Pt was confirmed.It explains not only the great stabilities of the compounds but also the efficient channels for charge transfer during photocatalytic reactions.The Pt-Se bonding also contributes to the enhanced visible light absorption.Considering the excellent photocatalytic properties of the MoSe 2 -Pt nanocompounds, we believe that the reported synthetic method might be suitable for further investigation and mass production.

Materials and Sample Preparations
The materials were purchased from Sigma-Aldrich (St. Louis, MA, USA) with analytical grade, and deionized water was produced at our own lab.The MoSe 2 -Pt samples were synthesized with the following steps: (a) multilayer MoSe 2 nanopowders were dispersed into deionized water with various ratios.The concentration of MoSe 2 suspension was 0.1 mg/mL, 0.2 mg/mL and 0.3 mg/mL, respectively.(b) In order to obtain Pt nanoparticles with an extremely small size, K 2 PtCl 4 and trisodium citrate were used as precursors to obtain Pt nanoparticles [26,27].K 2 PtCl 4 and trisodium citrate were added into the MoSe 2 suspension by mechanically stirring.(3) The mixed solution was set under an ultrasonic bath at 50 • C for 150 min or 200 min.(4) Pt 0 can be reduced from PtCl 4 2− , and Pt nanoparticles would finally grow onto MoSe 2 nanoflakes.After synthesis, three samples with different mass ratios were obtained, as shown in Table 1.These samples are labelled according to their contents, which were M1Pt, M2Pt and M3Pt, respectively.

Characterizations
The sample morphologies were studied through a transmission electron microscope (TEM, JEOL 2200FS (JEOL, Tokyo, Japan)).The crystal structures of MoSe 2 and the synthesized complexes were measured through X-ray diffraction (XRD, Bruker (Billerica, MA, USA)).Cu Kα emission (λ = 1.5406Å) was employed as the X-ray source.The optical properties were measured through a Lambda 950 UV-Vis spectrophotometer (Spectralab Scientific Inc., Markham, ON, Canada) with BaSO 4 as reference.The synthesized powder was dissolved in deionized water for UV-vis absorption tests.The chemical states were analyzed by Thermo Fisher (Waltham, MA, USA) K-Alpha X-ray photoelectron spectroscopy.

Photodegradation Measurements
The photocatalytic properties of the synthesized MoSe 2 -Pt catalysts were studied by degrading Methylene blue (MB).During each photocatalytic reaction, 50 mg of the catalyst was put in 50 mL of MB solution (10 mg/L).Reactions were carried out under a 300 W Xe lamp.We used a cutoff filter (#84-689, TECHSPEC, Co., Ltd., Gauteng, South Africa) to block the light under the wavelength of 400 nm.Before degradation tests, MB solutions with catalysts inside were stirred under a dark environment for half an hour to dispose of the adsorption/desorption effects.During photocatalytic degradations, 2 mL of the solution was taken every 30 min and was centrifuged to remove the MoSe 2 -Pt powder.Visible-light absorption spectra ranging from 400 nm to 800 nm were measured through a Lambda 950 UV-Vis spectrophotometer.During measurements, the absorption peak of MB was set at 664 nm and the concentration of residual MB could be determined by the integration of the MB absorption peaks.The photocatalytic reactions were therefore presented by time-course decrease in MB concertation.

MoSe 2 -Pt Morphologies and Crystal Structures
After synthesis, a drop of the solution containing MoSe 2 -Pt was placed onto a holey carbon grid and dried in air.Then the samples were observed under TEM.The morphologies of MoSe 2 flakes among the three samples were similar in shape and size.Therefore, we chose sample M1Pt as an example whose morphologies are shown in Figure 1.In Figure 1a, MoSe 2 nanoflakes are of a round shape with a typical size of 40 nm.There are tiny Pt dots on the edge of the MoSe 2 .The Pt dots are clearer in the zoomed-in image in Figure 1b.Due to the mild synthetic conditions and low concentration of K 2 PtCl 4 in solution 1, PtCl 4 2− was reduced to ultrafine particles.There are more Pt nanoparticles formed on the edge sites compared to the surfaces of the MoSe 2 because the edge sites are more reactive than the basal planes [28].Although very small in size, the Pt particles were well crystallized in (111) phase with a lattice spacing of 2.29 Å, as shown in Figure 1c.Such crystalline structure is compatible with the MoSe 2 (100) facet.It suggests the Pt particles are well grown on MoSe 2 .Figure 1d-f show the distribution of Pt nanoparticles for the samples of M1Pt, M2Pt, and M3Pt, respectively.It can be seen that the samples of M1Pt and M2Pt have the same dominant Pt size of 1.8 nm, while M3Pt has a slightly larger Pt size of 1.9 nm.
have the same dominant Pt size of 1.8 nm, while M3Pt has a slightly larger Pt size of 1.9 nm.In Figure 2, the XRD spectra show the crystal structure of the three samples of MoSe2-Pt nanocomposites and pristine MoSe2 nanopowder.The crystal planes of MoSe2 and Pt were marked with diamonds and stars, respectively.The MoSe2 (100), ( 103), (105), ( 110) and (200) planes were identified from both samples, which was in good agreement with previous reports [29].Compared to the pristine MoSe2, Figure 2 shows that MoSe2 is stable and keeps its crystal structure after synthesis.In Figure 2, the XRD spectra show the crystal structure of the three samples of MoSe 2 -Pt nanocomposites and pristine MoSe 2 nanopowder.The crystal planes of MoSe 2 and Pt were marked with diamonds and stars, respectively.The MoSe 2 (100), ( 103), (105), ( 110) and (200) planes were identified from both samples, which was in good agreement with previous reports [29].Compared to the pristine MoSe 2 , Figure 2 shows that MoSe 2 is stable and keeps its crystal structure after synthesis.
have the same dominant Pt size of 1.8 nm, while M3Pt has a slightly larger Pt size of 1.9 nm.In Figure 2, the XRD spectra show the crystal structure of the three samples of MoSe2-Pt nanocomposites and pristine MoSe2 nanopowder.The crystal planes of MoSe2 and Pt were marked with diamonds and stars, respectively.The MoSe2 (100), ( 103), (105), ( 110) and (200) planes were identified from both samples, which was in good agreement with previous reports [29].Compared to the pristine MoSe2, Figure 2 shows that MoSe2 is stable and keeps its crystal structure after synthesis.Pt (111) and (200) planes were identified in the synthesized MoSe 2 -Pt samples.The Pt (111) lattice spacings are shown in Table 2.We can see that Pt (111) peak positions were slightly varied among the three samples.The lattice spacings are calculated as 0.2285, 0.2291, and 0.2274 nm, respectively.Moreover, the mean crystal sizes (D (111) in Table 2) were also calculated through Scherrer's equation [30].They are very close for the M1Pt and M2Pt samples, while slightly larger for the M2Pt sample.It should be noted that the calculated mean crystal sizes are not the particle sizes which could be directly measured under TEM; however, the D (111) values show the same trends with the particle sizes shown in Figure 1d-f.

Chemical States, Mechanism of Efficient Photocatalytic Reactions
The chemical electronic states of the MoSe 2 -Pt samples were evaluated through XPS.The high-resolution XPS spectra of Pt 4f and Se 3d are shown in Figure 3.In Figure 3a-c, there are two Pt species which were identified by fitting the original Pt 4f spectra.Pt 0 peaks are the reduced Pt nanoparticles in metal form, and Pt-Se peaks are attributed to the Pt-Se bonding.The binding energies of these Pt peaks are slightly shifted among the three samples which may be caused by partial electron transfer between MoSe 2 and Pt [31].In Figure 3d-f, two main contents are found in the Se 3d spectra, which are the Se-Mo peaks and Se-Pt peaks.Such results are typical for MoSe 2 and PtSe 2 characteristics [32], and further confirm the formation of Se-Pt bonding.Therefore, it is obvious that chemical bonding of Pt-Se formed after the synthesis.Such chemical bonding can provide an effective pathway for charge transportation during photocatalytic reactions [9].The Se-Mo 3d 5/2 peaks at 54.56 eV are barely shifted among the three samples, suggesting that MoSe 2 takes a dominant content compared to the Se-Pt species.
Based on the XPS results, it is noticed that the relative contents of Pt-Se varies among the samples, which may have influence on electron transportation.The relative contents of Pt-Se can be calculated from Pt 4f spectra, which are 34.78%,40.02%, and 19.79%, respectively.It suggests that too much MoSe 2 involved in the synthesis (the M3Pt sample) may limit the formation of Pt-Se bonding.
In this case, there may be two ways that the photocatalytic abilities could be affected.Firstly, Pt-Se bonding provides an efficient pathway for charge transfer, so more contents of Pt-Se would be beneficial to the photocatalytic reactions.Secondly, the existence of Pt nanoparticles (Pt 0 ) can be confirmed by TEM results in Figure 1.Such ultra-fine Pt nanoparticles offer active sites for photocatalytic reactions where degradation could take place [33].Introducing noble metal nanoparticles on edge sites of MoSe 2 is a typical method for enhancing the photocatalytic properties.

Optical Properties of the Catalysts
In order to evaluate the optical performance of the synthesized samples, they were prepared in aqua solution for UV-visible absorption measurements.Figure 4 shows the absorption spectra of MoSe 2 and the three samples.In the visible wavelength range, there are obvious absorption peaks at around 475 nm and 710 nm, respectively.Such optical behavior is typical for multilayer MoSe 2 on a nanometer scale [34].It can be seen that the pristine MoSe 2 has a weak response to visible light, while the MoSe 2 -Pt samples strongly absorb the short wavelength of visible light, mainly between 450 and 550 nm.Among the three synthesized samples, M2Pt shows the best absorption ability for visible light while M3Pt shows the worst.Moreover, there is slight red-shift between the pristine MoSe 2 and the catalysts.Such feature enhances the absorption of light in a longer wavelength, making it suitable for the utilization of the solar spectrum.

Optical Properties of the Catalysts
In order to evaluate the optical performance of the synthesized samples, they were prepared in aqua solution for UV-visible absorption measurements.Figure 4 shows the absorption spectra of MoSe2 and the three samples.In the visible wavelength range, there are obvious absorption peaks at around 475 nm and 710 nm, respectively.Such optical behavior is typical for multilayer MoSe2 on a nanometer scale [34].It can be seen that the pristine MoSe2 has a weak response to visible light, while the MoSe2-Pt samples strongly absorb the short wavelength of visible light, mainly between 450 and 550 nm.Among the three synthesized samples, M2Pt shows the best absorption ability for visible light while M3Pt shows the worst.Moreover, there is slight red-shift between the pristine MoSe2 and the catalysts.Such feature enhances the absorption of light in a longer wavelength, making it suitable for the utilization of the solar spectrum.

Photodegradation
The aforementioned characterizations provide chemical and optical insights into the synthesized materials.Their photocatalytic performance is evaluated by MB degradation, as shown in Figure 5.The time-course photodegradation results are shown in Figure 5a.Here, C/C0 is used to represent the decrease of MB concentration, where C0 and C are the original MB concentration and the MB concentration at a certain time, respectively.The dark process suggests that the synthesized materials show obvious adsorption of MB, while the pristine MoSe2 can hardly adsorb MB.Such adsorption abilities are usually re-

Photodegradation
The aforementioned characterizations provide chemical and optical insights into the synthesized materials.Their photocatalytic performance is evaluated by MB degradation, as shown in Figure 5.The time-course photodegradation results are shown in Figure 5a.Here, C/C 0 is used to represent the decrease of MB concentration, where C 0 and C are the original MB concentration and the MB concentration at a certain time, respectively.The dark process suggests that the synthesized materials show obvious adsorption of MB, while the pristine MoSe 2 can hardly adsorb MB.Such adsorption abilities are usually related to the photocatalytic process.We can see that pristine MoSe 2 can hardly degrade MB and the samples are all reactive with MB.Within around 60 min, MB is nearly removed by the samples of M1Pt and M2Pt.However, the M3Pt sample performs slightly less efficiently, but it can still degrade more than 90% of MB after 120 min.Such photocatalytic results are in accordance with the optical absorption properties shown in Figure 4. Considering the catalyst amount used in the degradation process, the above photocatalytic performance is comparable to other popular photocatalysts, such as Bi 2 WO 6 /BiOCl [35].As a comparison, pristine MoSe 2 removes only 5.4% of the MB in 120 min with the same irradiation condition.It suggests that the introduction of Pt to MoSe 2 edges greatly improves the photocatalytic property.

Photodegradation
The aforementioned characterizations provide chemical and optical insights into the synthesized materials.Their photocatalytic performance is evaluated by MB degradation, as shown in Figure 5.The time-course photodegradation results are shown in Figure 5a.Here, C/C0 is used to represent the decrease of MB concentration, where C0 and C are the original MB concentration and the MB concentration at a certain time, respectively.The dark process suggests that the synthesized materials show obvious adsorption of MB, while the pristine MoSe2 can hardly adsorb MB.Such adsorption abilities are usually related to the photocatalytic process.We can see that pristine MoSe2 can hardly degrade MB and the samples are all reactive with MB.Within around 60 min, MB is nearly removed by the samples of M1Pt and M2Pt.However, the M3Pt sample performs slightly less efficiently, but it can still degrade more than 90% of MB after 120 min.Such photocatalytic results are in accordance with the optical absorption properties shown in Figure 4. Considering the catalyst amount used in the degradation process, the above photocatalytic performance is comparable to other popular photocatalysts, such as Bi2WO6/BiOCl [35].As a comparison, pristine MoSe2 removes only 5.4% of the MB in 120 min with the same irradiation condition.It suggests that the introduction of Pt to MoSe2 edges greatly improves the photocatalytic property.The photodegradation kinetics was evaluated by the pseudo-first-order model.With this model, the pseudo-first-order constant k could be expressed as The results of ln(C 0 /C) are shown in Figure 5b.The constants were calculated as 0.0361 min −1 , 0.0379 min −1 , and 0.0185 min −1 for the three samples, respectively.It is obvious that the M2Pt sample has the best photocatalytic kinetics.The constant values have the same trends as the Pt-Se contents.This indicates the correlation between Se-Pt bonding and photocatalytic performance.On the other hand, k values are not lineally affected by either the Pt amount used in the synthesis nor the relative contents of Pt-Se bonding.This may indicate that the surface segregation occurred during synthesis [36].
The possible photocatalytic mechanism can therefore be discussed.During the degradation process, photo-generated electrons from valence bands of MoSe 2 reach the conduction bands, and finally migrate to the active sites provided by Pt nanoparticles.The electron-hole pairs participate in redox reactions, where the holes oxidize water to H + and •OH.The hydroxyl radicals then react with MB [9].Meanwhile, the electrons reduce H + to •H.The Pt-Se bonding offers stable and efficient routes for charge transfer during the whole process.

Conclusions
In conclusion, we synthesized MoSe 2 -Pt complexes with a facile method, where Pt is reduced to ultra-fine nanoparticles.The synthetic method is simple and straightforward, making it suitable for mass production.The synthesized samples show a greatly enhanced photocatalytic performance for degrading the organic pollutant of MB under visible-light irradiation.Such properties show the excellent ability of visible-light utilization.The photodegradation mechanism could be explained through XPS analysis.Effective Pt-Se bonding provides pathways for charge transportation and ultra-fine Pt nanoparticles offer active sites for photocatalytic reactions.This work may be helpful for further photocatalyst design and applications in real cases.

Figure 1 .
Figure 1.Morphologies of MoSe2-Pt samples.(a) TEM image of MoSe2-Pt; (b) zoomed-in image of the squared region in (a); (c) HR-TEM image shows the crystal structure of Pt; (d-f) Pt size distributions of the samples of M1Pt, M2Pt, and M3Pt, respectively.

Figure 1 .
Figure 1.Morphologies of MoSe 2 -Pt samples.(a) TEM image of MoSe 2 -Pt; (b) zoomed-in image of the squared region in (a); (c) HR-TEM image shows the crystal structure of Pt; (d-f) Pt size distributions of the samples of M1Pt, M2Pt, and M3Pt, respectively.

Figure 1 .
Figure 1.Morphologies of MoSe2-Pt samples.(a) TEM image of MoSe2-Pt; (b) zoomed-in image of the squared region in (a); (c) HR-TEM image shows the crystal structure of Pt; (d-f) Pt size distributions of the samples of M1Pt, M2Pt, and M3Pt, respectively.

Figure 4 .
Figure 4. UV-vis absorption spectra of MoSe 2 and the synthesized samples.

Figure 4 .
Figure 4. UV-vis absorption spectra of MoSe2 and the synthesized samples.

Figure 5 .
Figure 5.The time-course photocatalytic MB degradation under visible light irradiation.(a) Photodegradation of the synthesized samples and pristine MoSe2.(b) Photodegradation kinetics of ln(C0/C).

Figure 5 .
Figure 5.The time-course photocatalytic MB degradation under visible light irradiation.(a) Photodegradation of the synthesized samples and pristine MoSe 2 .(b) Photodegradation kinetics of ln(C 0 /C).

Table 1 .
The synthetic details of the samples.