Austenitic Stainless Steel as a Catalyst Material for Photo-Fenton Degradation of Organic Dyes

Featured Application: The advanced degradation of organic pollutants aided by visible light could be carried out through the use of austenitic stainless steel (X5CrNi18-10, a source for iron ions at pH values close to neutral. Abstract: In this paper, a typical austenitic stainless steel was used as a catalyst in the visible photo-Fenton degradation process of two model dyes, methylene blue and methylorange, in the presence of hydrogen peroxide and potassium persulfate as free radical-generating species. The concentration intervals for both peroxide and persulfate were in the range of 333–1667 µ g/L. Very high photodecoloration efﬁciencies have been achieved using peroxide (>93%), while moderate ones have been achieved using persulfate (>75%) at a pH value of 6.5. For methylene blue, the maximum mineralization yield of 74.5% was achieved using 1665 µ g/L of hydrogen peroxide, while methylorange was better mineralized using 999 µ g/L of persulfate. The photodegradation of the dye occurred in two distinct steps, which were successfully modeled by the Langmuir–Hinshelwood pseudo-ﬁrst-order kinetic model. Reaction rate constants k between 0.1 and 4.05 h − 1 were observed, comparable to those presented in the reference literature at lower pH values and higher concentrations of total iron from the aqueous media.


Introduction
The continuous growth of industry-related activities has led to the discharge of persistent and potentially toxic organic compounds into the environment. Organic compounds with aromatic structures, such as most dyes used in the textile and food industry, phenolic compounds, and pesticides, are relatively challenging to remove through conventional adsorption, precipitation, and chemical/biochemical oxidation processes. Most of these "conventional" processes have several drawbacks, such as poor cost efficiencies or mineralization efficiencies [1,2]. They often fail to completely remove organic pollutants, leaving trace amounts that still pose environmental and/or aesthetic concerns.
Advanced oxidation processes (AOPs) such as the Fenton process have been known to have a much more economically efficient upscaling potential and a relatively low environmental impact compared with heterogeneous semiconductor photocatalysis-based AOPs [3,4].
The Fenton process involves the formation of highly reactive nonspecific oxidant radicals, such as hydroxyl, perhydroxyl, superoxide, or sulfate, based on electron transfer between iron ions and a chemical species capable of generating such radicals, among which hydrogen peroxide, peroxide ion-generating substances (percarbonates, perborates), and persulfates are the most widely used. Traditionally, Fe 2+ ions catalyze AOPs more efficiently, but Fe 3+ ions can be used as well in combination with a chelating agent [5]. Usually, the electron transfer process works better in relatively acidic conditions (pH values between 2 and 4) due to the complex electrochemistry of iron, which can precipitate from solution as hydroxides with a low solubility, thus limiting the ability of iron ion to react with the oxidant [6]. The generation of oxidant radicals in the Fenton process could be efficiently conducted through chemical means alone, by light from the UV and visible domain (the so-called photo-Fenton process variant) [7], by ultrasonic longitudinal waves [8], or through electrochemical means [6].
The formation of the free hydroxyl radical in the homogeneous Fenton variant occurs in a one-step mechanism variant with a water-soluble Fe 2+ source and a two-step mechanism with the addition of Fe 3+ ions. Heterogeneous Fenton processes, which use zero-valent iron (ZVI) in the metallic form, are very promising due to the iron source's high accessibility and low cost, the high organic pollutant mineralization rates, and facile separation of the iron source from the treated wastewater. Zero-valent iron is a strong reducing agent and has been used in particulate form for the removal of different organic (aromatic compounds) for groundwater remediation in the form of permeable reaction barriers [9] or as a slurry [10]. ZVI in the form of micropowders with diameters in the range of 50 to 200 µm [11] or in the form of nanopowders [12] shows a good reactivity in the presence of H 2 O 2 , meaning it could react with the surface iron to produce Fe 2+ and Fe 3+ and initiate the Fenton process [13][14][15]. Several studies have demonstrated that the optimal pH in the case of ZVI shifts to higher values (4 to 6), allowing outstanding degradation efficiencies for organic aromatic compounds [16,17]. However, zero-valent iron in particulate form has a strong tendency to aggregate, limiting its efficiency over time [12]. Additionally, uncontrolled iron leaching can occur, and the recovery and reusability of ZVI particles lead to the overall process having a higher cost [18]. Several supports for ZVI in particulate form, such as activated carbon cloths or zeolites. have been employed [19,20].
Comparatively, considerably fewer approaches have used metallic iron in pure form (i.e., higher than 99.5%) in sheets or meshes as catalyst supports for photo-Fenton processes. Solid iron supports generate iron ions in the presence of hydrogen peroxide without the usual drawbacks of particle aggregation [21]. However, the use of these supports poses problems of its own, such as the rapid passivation of the surface, decrease in the mineralization reaction rate, and inactivation of the surface.
This work aims to study the feasibility of the use of a commonly encountered austenitic stainless steel (X5CrNi18-10, AISI 304) as a zero-valent iron source in the photo-Fenton degradation of methylene blue and methylorange dyes in the presence of peroxide and persulfate ions. Austenitic stainless steel has several advantages compared to pure iron, such as a good corrosion resistance, allowing for a low amount of Fe 2+ ions being generated (which reduces sludge formation); constant photodegradation rate; and better overall control of the process. Using an iron-rich support, such as stainless steel, could mitigate the issue of ZVI surface passivation, but the use of stainless steel in photo-Fenton processes is not as widely researched compared to the use of ZVI particles [22,23]. Using persulfate ions to degrade oxidant sulfate radicals for the degradation of the two model dyes in the presence of stainless steel as ZVI at pH values close to 7 has been identified as a gap in the literature [24,25]. pH values close to neutral while generating a lower amount of iron ions in the presence of oxidant species could ensure the reuse and prolonged maintenance of the mechanical properties of the substrate. Under these conditions, the photo-Fenton catalyst can be structural steel from the lining or manufacture of a wastewater storage or treatment tank, without adding supplementary particulate or mesh catalysts.
To possibly contribute to future applications of the photo-Fenton process, a comparison between the degradation efficiency and kinetics of the two model dyes was performed for the two source oxidant species, hydrogen peroxide and potassium persulfate. The persulfate-initiated photo-Fenton process has been addressed less often in the reference literature. Additionally, the photo-Fenton process under nearly neutral pH conditions is a less well-addressed issue associated with solid iron-based catalysts. The novelty of this study, as previously stated, is not related to using custom-made catalysts or "unconventional" oxidant sources, but to documenting the feasibility of the use of stainless steel as a photo-Fenton catalyst for various oxidant concentrations. This type of catalyst has been insufficiently well-studied in the reference literature with photo-Fenton processes. Although stainless steel could be considered rather mundane, its wide use, known behaviour in different environments, and the fact that it is a structural material could constitute an advantage over custom-made ZVI sources for upscaling wastewater treatment installations. This upscaling is not possible without knowing the material's behaviour (performance, compositional stability) under different reaction conditions, and it is the aim of this study to contribute to this.

Materials and Methods
The methylene blue (MB) cationic dye (C 16 H 18 ClN 3 S, M w = 319.85) and methylorange (MO) anionic dye (C 14 H 14 N 3 NaO 3 S, M w = 327.33) were purchased from Sigma-Aldrich. The austenitic stainless steel (1.4301; X5CrNi18-10, AISI 304) had a nominal weight percent chemical composition of 0.07% C, 1% Si, 1.5% Mn, 18% Cr, 9% Ni, Fe balance, determined by atomic emission spectroscopy. The microstructure of the steel, as seen in reflexion microscopy mode (200×, aqua regia etchant), consists of equiaxed austenite grains with a small amount of d-ferrite at the austenite grain boundaries (Figure 1a). The reagents used in the spectrophotometric determination of the total Fe content-namely, 1,10-phenanthroline (Phen), hydroxylamine, and trisodium citrate-were purchased from Sigma-Aldrich and were of analytical grade. The hydrogen peroxide was used as a 30% wt. aqueous solution (Chemical Company SA, Iasi, Romania). The potassium persulfate (K 2 S 2 O 8 ) oxidant of 99.5% purity was purchased from Sigma-Aldrich and used as a 4% vol. aqueous solution. conditions is a less well-addressed issue associated with solid iron-based catalysts. The novelty of this study, as previously stated, is not related to using custom-made catalysts or "unconventional" oxidant sources, but to documenting the feasibility of the use of stainless steel as a photo-Fenton catalyst for various oxidant concentrations. This type of catalyst has been insufficiently well-studied in the reference literature with photo-Fenton processes. Although stainless steel could be considered rather mundane, its wide use, known behaviour in different environments, and the fact that it is a structural material could constitute an advantage over custom-made ZVI sources for upscaling wastewater treatment installations. This upscaling is not possible without knowing the material's behaviour (performance, compositional stability) under different reaction conditions, and it is the aim of this study to contribute to this.

Materials and Methods
The methylene blue (MB) cationic dye (C16H18ClN3S, Mw = 319.85) and methylorange (MO) anionic dye (C14H14N3NaO3S, Mw = 327.33) were purchased from Sigma-Aldrich. The austenitic stainless steel (1.4301; X5CrNi18-10, AISI 304) had a nominal weight percent chemical composition of 0.07% C, 1% Si, 1.5% Mn, 18% Cr, 9% Ni, Fe balance, determined by atomic emission spectroscopy. The microstructure of the steel, as seen in reflexion microscopy mode (200×, aqua regia etchant), consists of equiaxed austenite grains with a small amount of d-ferrite at the austenite grain boundaries (Figure 1a). The reagents used in the spectrophotometric determination of the total Fe content-namely, 1,10phenanthroline (Phen), hydroxylamine, and trisodium citrate-were purchased from Sigma-Aldrich and were of analytical grade. The hydrogen peroxide was used as a 30% wt. aqueous solution (Chemical Company SA, Iasi, Romania). The potassium persulfate (K2S2O8) oxidant of 99.5% purity was purchased from Sigma-Aldrich and used as a 4% vol. aqueous solution.  Each experiment was performed at ambient temperature (22 • C) in triplicate; the average values are presented in this paper.
A Spekol 11 mono-channel spectrophotometer (Carl Zeiss Jena, Germany) was used for monitoring the MB and MO dye solutions decolorization at various time intervals (c t ), based on their absorbance values at wavelength maxima of λ = 665 nm (MB) and λ = 465 nm (MO). The photodegradation efficiencies (η) were calculated with Equation (1): In addition, to elucidate the type of radicals responsible for the photodegradation, the photo-Fenton experiments were performed with each of the dye solutions spiked with 50 µL tert-butanol (99.8%, Scharlau), which is an efficient quencher of hydroxyl (HO•) or sulphate (SO 4 · 2− •) radicals [25].
To provide a complete picture of the advanced decomposition of MB and MO, not only based on the degradation of chromophore groups, which determines the VIS absorbance decrease, the chemical oxygen demand (COD) values of the irradiated solutions containing the two dyes were determined using the spectrophotometric method [26]. The COD, expressed in mg/L, is proportional to the amount of oxidizable organic substances in water [27].
Mineralization was assessed through calculating the COD-based efficiency η COD , according to Equation (2): where COD 0 represents the chemical oxygen demand of the initial dye solutions and COD eq represents the equilibrium chemical oxygen demand after reaching the photodegradation equilibrium. This work aimed to study the performance of the photo-Fenton process under the leastfavorable electrochemical conditions (to preserve the chemical composition of the aqueous environment and the steel as much as possible), with a minimum of added reagents. The average surface roughness (R a ) of the steel was kept as purchased (1.75 µm). The monitoring of the total iron content (Fe 2+ and Fe 3+ ), according to the spectrophotometric method with Phen, was performed at λ = 510 nm according to the procedure described in the reference literature [28].
The surface chemistry of the stainless steel photo-Fenton catalysts after their withdrawal from the irradiated MB dye solutions containing 1665 µg/L hydrogen peroxide and potassium persulfate was assessed through X-ray photoelectron spectrometry (XPS). A Perkin-Elmer (Waltham, MA, USA) XPS PHI 550 spectrometer was used with an Al Kα line (1486.6 eV) X-ray source. Both survey spectra and narrow-scans of Fe2p were acquired using a 20 eV pass energy.

Results and Discussion
The decolorization of both methylene blue and methylorange dyes was successfully achieved through the use of the stainless steel photocatalyst in the presence of both types of oxidant species-namely, peroxide and persulfate ions.
High photodecoloration efficiencies (>99.1%) were registered in the case of MB for all hydrogen peroxide concentrations, indicating that the disruption of the chromophore groups for this dye occurs in a more facile manner than for methylorange, for which efficiencies of 91-93.5% were registered (Figure 2a,b). As far as photodecoloration is concerned, for the hydrogen peroxide concentration range reported in this paper and under close to neutral pH conditions, there seems to be a less marked influence of peroxide ion concentration on the photo-Fenton process efficiency for both dyes.
Photodecoloration in the presence of persulfate ions also occurs with a high efficiency in the case of MB (88.4% at a 999 mg/L persulfate concentration, Figure 2a), although in this case, after the aforementioned concentration, there is a sharp efficiency decrease. This could be due to the fact that the higher amount of iron ions generated from stainless steel through persulfate-aided oxidation hinders the efficient harvesting of visible light [29,30]. In the experiments where the photodecoloration occurs in the presence of the sulfate and hydroxyl radicals scavenger tert-butanol (TBu), a decrease of up to 55% (for MB, Figure 2a) and up to 62% (for MO, Figure 2b) in the photo-Fenton efficiencies was registered for both oxidants, indicating the critical role that these species play in the degradation of organic matter. A more significant drop in photodecoloration efficiency was registered for persulfate due to tert-butanol inhibiting the generation of both sulfate and hydroxyl radicals.
When mineralization comes into discussion, hydrogen peroxide presents the highest photodegradation efficiency for MB (74.5% vs. 69.9% for persulfate, at 1666 μg/L, Figure  2c), while for MO, persulfate is more efficient at 999 μg/L (57%, Figure 2c). Photodecoloration in the presence of persulfate ions also occurs with a high efficiency in the case of MB (88.4% at a 999 mg/L persulfate concentration, Figure 2a), although in this case, after the aforementioned concentration, there is a sharp efficiency decrease. This could be due to the fact that the higher amount of iron ions generated from stainless steel through persulfate-aided oxidation hinders the efficient harvesting of visible light [29,30].
In the experiments where the photodecoloration occurs in the presence of the sulfate and hydroxyl radicals scavenger tert-butanol (TBu), a decrease of up to 55% (for MB, Figure 2a) and up to 62% (for MO, Figure 2b) in the photo-Fenton efficiencies was registered for both oxidants, indicating the critical role that these species play in the degradation of organic matter. A more significant drop in photodecoloration efficiency was registered for persulfate due to tert-butanol inhibiting the generation of both sulfate and hydroxyl radicals.
The decolorization kinetic was fitted with the pseudo-first-order kinetic model (Langmuir-Hinshelwood) from Equation (3) In Equation (3), k represents the pseudo-first-order rate constant. The fitting parameters for this model (including the correlation coefficients, R 2 ) are depicted in Tables 1 and 2. Figure 3a-d indicate that the photo-Fenton degradation mechanism of both dyes occurs in two steps. The first part of the kinetic (rate constant, k1) is characterized by a slower overall degradation of the dyes for both H2O2 and S2O8 2− , because in this step the oxidation of metallic iron Fe 0 to Fe 2+ and the generation of hydroxyl and sulfate radicals take place; thus, initially there is a low amount of oxidant species to initiate the photodegradation. The generation of reactive HO• radicals in the presence of H2O2 and Fe 2+ ions from the catalyst is depicted by the following Mechanism (4)   In Equation (3), k represents the pseudo-first-order rate constant. The fitting parameters for this model (including the correlation coefficients, R 2 ) are depicted in Tables 1 and 2.   Figure 3a-d indicate that the photo-Fenton degradation mechanism of both dyes occurs in two steps. The first part of the kinetic (rate constant, k 1 ) is characterized by a slower overall degradation of the dyes for both H 2 O 2 and S 2 O 8 2− , because in this step the oxidation of metallic iron Fe 0 to Fe 2+ and the generation of hydroxyl and sulfate radicals take place; thus, initially there is a low amount of oxidant species to initiate the photodegradation. The generation of reactive HO• radicals in the presence of H 2 O 2 and Fe 2+ ions from the catalyst is depicted by the following Mechanism (4) [32,33]: The persulfate ions can decompose in a first slow, ongoing step to highly reactive sulfate radicals (SO 4 − •), which oxidize the metallic iron to produce Fe 2+ ions (i.e., the iron is "activated"), which can further initiate the production of sulfate radicals on their own. Avoiding surface passivation in this step is crucial for achieving a high photodegradation yield [32]. The sulfate radicals can react with water to generate hydroxyl radicals, so for the persulfate oxidant, the dyes can be oxidized by both type of radicals [29,34,35], according to the following Mechanism (5): Regarding the dye photodegradation in this step, these could be oxidized to higher molecular mass intermediates (possibly hydroxylated compounds or carboxylic acids) according to Mechanism (6), where DyeH denotes the methylene blue/methylorange dyes in their non-oxidized form. The dyes can also be directly oxidized by Fe 3+ ions [35,36].
In the second step, these organic intermediates can be degraded at a higher rate to smaller molecular compounds with a rate constant of k 2 . The values of k 1 and k 2 for each amount of H 2 O 2 and S 2 O 8 2added are presented in Tables 1 and 2 (the R 2 correlation coefficients are given in parentheses after the actual values of k 1 and k 2 ).
For both dyes, the results indicate that the initial peroxide or persulfate ion concentrations play a crucial role in the kinetic of photodecoloration. For hydrogen peroxide (Table 1), there is a linear increase in the reaction rates for both steps until 999 µg/L (29.38 µmol/L), which seems to represent the optimal concentration for the setup presented in the paper. After this optimal hydrogen peroxide concentration value, there is a leveling off in the reaction rate. Excess amounts of H 2 O 2 could determine the trapping of the generated hydroxyl radicals to form hydroperoxyl radicals (with lower oxidation potential) and water, according to the Mechanism (7). Additionally, a higher amount of generated Fe 2+ with the increase in H 2 O 2 addition could determine the decrease in the concentration of the hydroxyl radicals [33,37].
For persulfate (Table 2), the optimum concentration for photodecoloration is maintained at 999 µg/L (5.20 µmol/L), after which the generated iron ions can similarly quench both sulfate and hydroxyl radicals through the following Mechanism (7) In general, the methylorange-related rate constants are up to 42% lower than those corresponding to methylene blue due to the higher molecular mass of the former. A similar trend was also observed for semiconductor-aided photocatalysis [38]. Tables 1 and 2 also indicate that the total amount of iron generated in the solution during the photo-Fenton process is below the recommended values for groundwater (0.3 mg/L, as recommended by the World Health Organization) in the case of using hydrogen peroxide. A higher total iron amount is generated for potassium persulfate, which may need additional precipitation and filtering steps for the wastewater.
A comparison of the overall efficiency of photo-Fenton over the widely available systems reported in the reference literature must be viewed with some caution, due to the different experimental conditions, reagent concentrations, model pollutant concentrations, and catalyst specific surfaces used, but it is widely agreed that fast degradation rate constants (k), coupled with high decoloration and mineralization rates, constitute important candidate parameters. Additionally, the use of the smallest amount of catalyst, iron ions, and oxidant possible is desired for economic efficiency reasons and to limit additional wastewater purification steps and avoid the excessive degradation of the catalyst [7,39,40]. In some studies, the importance of the photo-Fenton reaction medium's pH value being as close to neutral as possible is also stressed [7,41]. For the sake of comparison, to highlight the benefits of using the proposed system with other photo-Fenton setups, Table 3 lists the photo-Fenton process parameters and efficiencies in other studies extracted from the reference literature. Table 3. Parameters of selected photo-Fenton processes from the reference literature compared to those of the present study.  By analysing the data presented in Table 3, it can be seen that using austenitic stainless steel as a photo-Fenton catalyst determines good mineralization and discoloration efficiencies at near-neutral pH values. Compared with the literature data, attained using hydrogen peroxide or persulfate and Fe 2+ salts or ZVI nanoparticles as an iron source, at the same pH values as used in this study (6)(7), the mineralization efficiency can be considered practically nil [33,42,48,49]. Comparable degradation efficiencies of already-reported photo-Fenton systems are reported to be achieved only under acidic pH values (3)(4), which generate total iron concentrations in solution ranging from 0.6 to 150 mg/L. Compared to this study, these values are up to 38 times higher, necessitating further separation steps in a real-life wastewater treatment pilot installation. Also, photo-Fenton on solid stainless steel supports, as reported herein, can operate at oxidant concentrations of 20 to 460 times lower than those reported in the reference literature [44,46], reducing the costs and the oxidative degradation of the installation. The reaction rates obtained are similar to those reported in the reference literature for ZVI nanoparticles or iron salts (except when using UV irradiation) but under nearly-neutral pH conditions. A comparison of this study's reaction rates with those from the reference literature under neutral pH conditions was not possible due to the lack of such data for MB and MO.

Photo-Fenton with Hydrogen
Regarding the surface chemistry of the catalyst, the relative wt.% of the elements of interest (Fe, Cr, Ni, C, O) before and after the photo-Fenton degradation process for both hydrogen peroxide and potassium persulfate ions at their highest concentration (1667 µg/L) used in this study was determined through XPS spectroscopy (Figure 4a, Table 4). It can be seen that the most notable modification in the surface chemistry of stainless steel is the increase in oxygen content with 107% in the case of hydrogen peroxide and with 159% in the case of potassium persulfate.

Conclusions
Efficient methods for the degradation of persistent organic compound should make use of commonly available materials, be upscalable, be energy-efficient, and alter the chemical composition of the aqueous environment as little as possible. This work aimed to determine the suitability of using a photo-Fenton process triggered by irradiation with light from the visible spectrum to degrade two model dyes (methylene blue and methylorange) with hydrogen peroxide and potassium persulfate at ambient temperature, without any pH correction and without stirring. Good photodegradation efficiencies (photodecoloration and mineralization) were achieved by using the operational parameters described in this paper. The photodegradation of the model dyes was achieved at pH values close to neutral and with considerably lower amounts of peroxide or persulfate than those used in other related studies. Further studies will be performed to assess the photodegradation efficiency of stainless steel in the presence of various interfering anions and cations and for real industrial wastewater effluents.   Furthermore, there is a decrease up to a maximum of 4.5% in the iron content of the material. An increase in the oxygen content on the steel surface and iron dissolution has also been observed in the case of electro-Fenton processes [22,50]. The dissolved iron provides the ions necessary to initiate and sustain the photo-Fenton photodegradation process. As mentioned in Tables 1 and 2, the iron concentration in solution ranges from 0.13 to 3.95 mg/L. In water, iron concentrations below 0.3 mg/L can be characterized as unnoticeable, whereas levels of 0.3-3 mg/L are generally acceptable [26]. As previously stated, using stainless steel at near-neutral pH generates much less iron in solution than "traditional" processes using ZVI iron (Table 3).
Regarding Ni and Cr, the other major constituents of stainless steel responsible for its characteristic corrosion resistance in aqueous environments, Table 4 reveals that there is a 0.05% reduction in the weight percentage of Ni on the surface of the stainless steel catalyst submitted to the photo-Fenton process (H 2 O 2 oxidant), while for Cr, a reduction of 0.01% is registered for both oxidants. In solution, at the experimental pH values used in this study, nickel should exist as NiO and/or Ni(OH) 2 , as these species are stable at pH 5−15. Consequently, these species tend to separate from aqueous solution and precipitate [51], posing a low cause for environmental concern. Cr oxidation products such as Cr 3+ and/or Cr(VI) ions are rarely present at pH values over 6 because hydrated chromium oxide (Cr(OH) 3 ) is hardly water-soluble, and Cr(VI) can be reduced to Cr 3+ (thus precipitating it out of the solution) by the Fe 2+ ions [52,53]. More probably, since Ni and Cr are known to form a thin oxide layer on the surface of stainless steel in the presence of atmospheric oxygen (oxygen is present in the surface chemistry of the steel material, as in Table 4), the reduction in the surface Ni and Cr in steel could be more likely due to the microabrasion of this oxide layer than metallic Ni and Cr oxidation to water-soluble species [54].
Regarding the chemical states of iron (high-resolution Fe2p envelopes, Figure 4b), all samples present a high-intensity broad signal ascribed to metallic Fe 0 2p 3/2 at about 706 eV, representing the dominating contribution [55]. Fe in higher oxidation states, such as Fe 2+ 2p 3/2 at~710 eV [56] is present on the surface of the steel samples submitted to photo-Fenton. Iron at its maximally oxidized state-i.e., Fe 3+ -can be detected at~715 eV [57] in very low amounts on the surface of the initial stainless steel sample, but most notably on the surface of the samples submitted to photo-Fenton. Fe 2+ seems to represent the highest oxidized-state iron contribution. Since the ferrous ions are the main species responsible for electron transfer to the peroxide and persulfate oxidants, their presence on the material's surface confirms the depicted photogeneration of radicals and dye photodegradation mechanism schemes.

Conclusions
Efficient methods for the degradation of persistent organic compound should make use of commonly available materials, be upscalable, be energy-efficient, and alter the chemical composition of the aqueous environment as little as possible. This work aimed to determine the suitability of using a photo-Fenton process triggered by irradiation with light from the visible spectrum to degrade two model dyes (methylene blue and methylorange) with hydrogen peroxide and potassium persulfate at ambient temperature, without any pH correction and without stirring. Good photodegradation efficiencies (photodecoloration and mineralization) were achieved by using the operational parameters described in this paper. The photodegradation of the model dyes was achieved at pH values close to neutral and with considerably lower amounts of peroxide or persulfate than those used in other related studies. Further studies will be performed to assess the photodegradation efficiency of stainless steel in the presence of various interfering anions and cations and for real industrial wastewater effluents.