Geochemical Assessment and Mobility of Undesired Elements in the Sludge of the Phosphate Industry of Gafsa-Metlaoui Basin, (Southern Tunisia)

The raw phosphates in the Gafsa-Metlaoui phosphate basin are valorized by wet processes that are performed in the laundries of the Gafsa Phosphates Company (CPG, Gafsa, Tunisia) to reach market grades (>28% P2O5). This enrichment process allows the increase of P2O5 content by the elimination of the coarse (>2 mm) and fine (<71 µm) fractions. Mineralogical analysis has shown that all the investigated materials (raw phosphate, marketable phosphate, coarse waste, and fine waste) from the laundries of M’Dhilla-Zone L and Redeyef are both composed of carbonate fluorapatite, carbonates, quartz, gypsum, clays, and clinoptilolite. Chemical analysis shows that Cr, Cd, Zn, Pb, and U are concentrated in the fine wastes and associated with the clay–phosphate fraction. The rare earth elements are more concentrated in both raw and marketable phosphates. Drilling and sludge-water analysis, along with leaching tests conducted on the fine wastes, showed that, due to phosphate industry, cadmium, fluorine, and sulfate contributing to the pollution of water resources in the region, pollution is more conspicuous at M’Dhilla.


Introduction
The Gafsa-Metlaoui phosphate basin that is managed by the Compagnie des Phosphates de Gafsa (CPG, Gafsa, Tunisia) is the most important mining area in Tunisia. It includes large-scale phosphate-extraction industry activities, with an annual production rate of around 3.34 million tons in 2018 [1]. Most of the phosphate ores are not suitable for immediate use in the processing industry, due to their relatively low P 2 O 5 content and generally their content of a series of gangue minerals. Thus, they shall undergo prior enrichment before being employed in the acidulation process [2]. Upgrading processes of sedimentary-type phosphate ores to reach marketable grades (P 2 O 5 > 28%) consist of separating the gangue minerals (silicates and carbonates) from the valuable phosphate material [3]. The CPG in the Gafsa-Metlaoui Basin is equipped with ten laundries, in which phosphates are enriched by wet processing according to the following steps: phosphate ore is extracted from quarries, then transported by trucks and conveyors to laundries, then scalped to 120 mm. At a later stage, the fraction >120 mm is considered sterile and evacuated to the rock dumps, while the fraction <120 mm is crushed and screened at 40 mm to feed the scrubbers. In the present work, the ore with a grain size <40 mm, resulting from these last operations (scalping, crushing, and screening), is considered as raw phosphate (RP).
The scrubbing consists of shaking the raw ore with water for 2 min to 3 min, followed by washing on a 2 mm mesh-vibrating screen. This first operation of particle-size grading consists of paring the high cut; the particles >2 mm in diameter make the coarse waste (CW) at the factory. The fraction <2 mm is meant for the supply of hydrocyclones, in order to eliminate fine wastes (FW) in the form of mud with a particle size <71 µm. The final product matches the marketable phosphates (MP) with a particle size ranging from 2 mm to 71 µm [4].
The water that is required to wash the phosphate ore is provided by deep boreholes often located nearby the laundries. Due to the excessive consumption of drilling water (DW), the CPG has opted, for many years now, for another strategy that consists of recycling water from the washing circuit. This process is conducted by recovering water from the settling pond and mixing it with new drilling water. In this work, the discharge filtrates are sludge water (SW), which is recovered from the natural decantation of the sludge collected from the laundries.
At the laundries, the process water is recycled after recovery from the sludge by flocculation in settling ponds. Once settled, the resulting thick mud is discharged either to tailings disposal impoundments or into the hydrographic network. However, these fine wastes (FW) may contain mineral fractions carrying undesired elements such as Cd, U, Zn, F − , NO 3 − , PO 4 3− , etc. Several scholars have focused on both mineralogical and geochemical studies of solid discharges from laundries [5][6][7][8], but without establishing a geochemical assessment between the input and output products of the phosphate laundries.
Other scholars have focused on the impact generated by heavy metals from these discharges at the soil-plant interface [7][8][9][10], but they did not highlight the influence of mineralogy and geochemistry of the solid effluents on the mobility of metallic trace elements (MTE).
In this study, we have tried, firstly, to determine the mineralogical and geochemical characterization of the input and output products of the two laundries of Zone L (ZL) of M'Dhilla and Redeyef, which are installed east and west of the Gafsa-Metlaoui Basin, respectively. Second, this work is innovative in terms of mobility assessment of MTE (Cd and U) contained in the sludge being discharged by the aforementioned laundries, with reference to batch tests.

Study Area
Covering an area of approximately 5.000 km 2 to 6.000 km 2 , the Gafsa phosphate basin (Figure 1) is located in the southern Tunisian Atlas region. It is bounded, to the north, by the Gafsa fault, to the east by the north Chotts chain, to the west by the Algerian territory, and to the south by the Saharan platform.
Weather data (temperature, rainfall, wind, humidity, and evaporation) prevailing in the region are coterminous with pre-desert climatic characteristics, whereas the M'Dhilla and Redeyef zones are characterized by a cool lower -arid bioclimatic belt.
Only the exploitable phosphate ore from the Metlaoui formation of Upper Paleocene-Lower Eocene age, which contains the main phosphate series of the mining basin, will be taken into consideration in this study.

Phosphates Deposits
Sedimentary phosphate deposits result from the long-term active sedimentation in the sea and account for more than 80% of phosphate ore production in the world.
Natural phosphates include more than 200 mineralogical species. The most abundant belong to the apatite group, which make a family of solid isomorphic fluorapatite compounds with the formula Ca 10 (PO 4 ) 6 F 2 .
Fluorapatite is the most common phosphate mineral in igneous rocks. In this mineral, fluorine can be partially replaced by OH or Cl.
In the phosphate minerals of sedimentary deposits, the corresponding phosphate minerals are related to fluorapatite. They differ from this mineral by a set of partial isomorphic substitutions. The most marked substitution in sedimentary apatites is that of PO 4 3− by CO 3

Phosphates Deposits
Sedimentary phosphate deposits result from the long-term active sedimentation in the sea and account for more than 80% of phosphate ore production in the world.
Natural phosphates include more than 200 mineralogical species. The most abundant belong to the apatite group, which make a family of solid isomorphic fluorapatite compounds with the formula Ca10(PO4)6F2.
Fluorapatite is the most common phosphate mineral in igneous rocks. In this mineral, fluorine can be partially replaced by OH or Cl.
In the phosphate minerals of sedimentary deposits, the corresponding phosphate minerals are related to fluorapatite. They differ from this mineral by a set of partial isomorphic substitutions. The most marked substitution in sedimentary apatites is that of PO4 3-by CO3 2-, accompanied by the introduction of additional Fions to preserve electrical neutrality. The mineral obtained is carbonate fluorapatite (CFA) with a simplified structural formula Ca10((PO4)6−x(CO3F)x)F2.
Other substitutions may also occur, consisting essentially in the partial replacement of Ca by Na, Mg, or Sr; of F by OH; and of PO4 by SO4, VO4, SiO4, AsO4, etc.

Sampling and Preparation
A series of samples of the input and output products were taken in the laundries. The samples selected from the same washing circuit are raw phosphate (RP), marketable phosphate (MP), coarse waste (CW), fine waste (FW), drilling water (DW), recycled water (RW), and sludge water (SW). The sampling procedure was the same for both laundries (Redeyef and M'Dhilla-Zone L). A total of 14 samples were collected from the two laundries-six water samples (DW, RW, and SW) and eight solid samples (RP, MP, CW, and

Sampling and Preparation
A series of samples of the input and output products were taken in the laundries. The samples selected from the same washing circuit are raw phosphate (RP), marketable phosphate (MP), coarse waste (CW), fine waste (FW), drilling water (DW), recycled water (RW), and sludge water (SW). The sampling procedure was the same for both laundries (Redeyef and M'Dhilla-Zone L). A total of 14 samples were collected from the two laundries-six water samples (DW, RW, and SW) and eight solid samples (RP, MP, CW, and FW). About two kilograms of each solid sample were collected and kept in plastic bags. Sludge samples were decanted naturally for 24 h in order to separate water from the solid residue.
In the laboratory, all the water samples were filtered to 0.45 µm with a cellulose acetate filter. The filtered water was acidified to pH 2.0 with nitric acid to be analyzed by inductively coupled plasma-atomic emission spectroscopy (ICP-AES). The solid samples (RP, MP, CW, and FW) were dried at 60 • C for 24 h. Because the size distribution of the sludge was determined by the wet method, the rest of the samples were sieved to 2 mm to be used for the characterization of the main physicochemical properties of input and output products-(i) particle size determination, (ii) mineralogical analysis, (iii) geochemical analysis, and (iv) leaching tests.

Methods
The collected samples were submitted to particle size, mineralogical, and chemical analyses. The grain-size distribution was performed using a laser analyzer (Malvern Mas-Appl. Sci. 2021, 11, 1075 4 of 16 tersizer 2000, Malvern Panalytical, Malvern, UK). The total calcium carbonate content (%CaCO 3 ) was carried out by means of a Bernard calcimeter (Gabbrielli Technology, Calenzano, Italy). The organic carbon (C org ) and nitrogen (N) rates were successively determined by an elementary micro analyzer carbon/sulfur (Horiba-Jobin, Yvon, Edison, NJ, USA), and the nitrogen was assessed by means of a UDK 132 semi-automatic distillation unit, VELP SCIENTIFICA, Usmate velate (MB), Italy. The organic matter (OM) content was determined by multiplying Corg by 1.72 (Van Bemmelen factor, [11]). The mineralogical analyzes were carried out by a PANalyticalX'Pert Pro X-ray diffractometer (XRD, PANalytical, Almelo, The Netherland).
In most cases, mobility designates the ability of an element to migrate in space, to shift from one chemical form to another, or to undergo a phase change (mainly from a solid phase to a liquid one) [13]. The transfer processes between the two phases (solid and liquid) are multiple; they strongly depend on the nature of the link between the elements being considered, in addition to the solid phase, which is also known as the carrier or retention phase, and the physico-chemical conditions prevalent in the environment. Several physical and chemical processes at the solid-liquid interface generally allow the trapping of metals, such as (physical and chemical) adsorption [14,15], precipitation [16][17][18], substitution in the crystal lattice, and mechanical trapping.
Leaching is a method for removing soluble components from a solid matrix [19,20]. The batch extraction procedure is a short-term leaching test intended to estimate the release potential of constituents from waste materials over a range of environmental conditions [21], and to evaluate potential risks to human and/or groundwater [22]. It takes into account the nature and particle size of the solid sample, the nature and the pH of the solution, as well as operating conditions such as the liquid/solid ratio (L/S), temperature, contact time, number of extractions, or even the stirring mode [21][22][23][24][25].
In order to assess the mobility of MTE in the fine wastes from the two laundries, batch extraction tests were performed on dried and sieved (2 mm) solid fractions of the sludges, according to the protocols of Kosson et al. [21] and Garrabrants et al. [25], which were adapted to genuine conditions of this study (particle size < 2 mm, sludge water as extractant, liquid to solid (L/S) ratio of 2/1, natural pH). The procedure consists of mixing 10 g of dried sludge with 20 mL of fresh sludge water in a 50 mL polyethylene tube, and then the suspension was subjected to rotary (20 rpm) agitation (end-over-end) for 48 h. Thereafter, the suspension was centrifuged at 2500× g rpm for 20 min. Following the recovery of the supernatant by filtration using 0.45 µm cellulosic acetate membrane, the pH and Electrical Conductivity (EC) measurement were taken with a multi-parameter (WTW, Xylem analytics, Beverly, MA, USA), and cadmium and uranium concentrations were determined with an inductive plasma coupled with a mass spectrometer (ICP-MS) (Thermo Scientific X-series 2, Thermo fisher scientific, Waltham, Massachusetts, United States). The DL for these elements was 0.001 µg/L. The solid residue was mixed again with 20 mL of fresh sludge water to perform a new leaching cycle. The whole batch experience was carried out over seven extraction cycles. All preparations and analyses were performed in the laboratories of the National Institute of Research and Physico-Chemical Analysis (INRAP, Technopole of Sidi Thabet, Ariana, Tunisia).

Characterization of the Inputs and Output Products of the Phosphate Laundries
The samples collected from the laundries (RP, MP, CW, and FW), were submitted to a particle-size, mineralogical, and geochemical analyses.

Particle-Size Analysis
The results of particle-size analyses of the different phosphate samples from the two laundries are shown in Table 1, taking into account only the fractions of less than 2 mm. The raw (RP) and marketable (MP) phosphates of the two laundries are dominated by fine to very fine sandy texture with percentages ranging from 65% to 66% and from 69% to 78%, respectively. They are also characterized by average contents of medium to coarse sand-sized, ranging from 23.6% to 24.7% and from 21.7% to 30.6%, respectively. It should be noted that the fine waste that was recovered at the outlet of the hydrocyclones has displayed large percentages (58.87% for M'Dhilla-Zone L and 82.84% for Redeyef) of fine fraction (<63 µm). However, due to occasional problems, the particle size of wastes at the outlet of hydrocyclones, which is supposed to be lower than 71 µm, can go up to 400 µm.  (Figure 2). The similarity in the mineralogical composition between the input and the output products indicates that the processes of ore treatment in the washing units do not alter the mineralogy. Other silicates, such as smectite ((Si 3+x Al 1−x )O 10 (Al 2−y Mg y )(OH) 2 M+I 1−(x−y) (H2O) n ) and palygorskite ((Mg,Al) 2 Si 4 O 10 (OH)·4(H 2 O)), are present in the fine wastes from the two laundries. However, regarding clinoptilolite, it was revealed that this mineral is more abundant in the fine waste of the Redeyef laundry (Table 2).
ing according to the samples being employed (Figure 2). The similarity in the mineralogical composition between the input and the output products indicates that the processes of ore treatment in the washing units do not alter the mineralogy. Other silicates, such as smectite ((Si3+xAl1−x)O10(Al2−yMgy)(OH)2M+I1−(x−y)(H2O)n) and palygorskite ((Mg,Al)2Si4O10(OH)·4(H2O)), are present in the fine wastes from the two laundries. However, regarding clinoptilolite, it was revealed that this mineral is more abundant in the fine waste of the Redeyef laundry (Table 2).

Geochemistry
Results of the geochemical analysis of the input and output products from the two laundries are summarized in Table 3.
These results show considerable amounts of OM in the samples in particular those of the Redeyef (1.22-3.89%). This is one of the characteristics of the phosphorites of the Gafsa-Metlaoui Basin. It should be also noted that the raw phosphates and the fine wastes from the two laundries contain the highest OM contents (1.22% to 1.36% and 1.51% to 3.89%, respectively). According to Belayouni [26], this OM makes an absorption/adsorption surface for some metals such as zinc. Table 3. Whole-rock chemical composition of the input and output products of M'Dhilla-Zone L (ZL) and Redeyef laundries (references of samples are as in Tables 1 and 2). Concerning the total nitrogen, all the samples contain low contents 0.003% to 0.01%; the highest content (0.01%) characterizes the sample FW-R. Likewise, the highest CaCO 3 contents (27.16% to 24.19%) characterize the coarse wastes from the two laundries, thus substantiating the carbonated nature of these wastes.

RP-ZL
In terms of major elements, results show that CaO and P 2 O 5 have the highest concentrations as major elements for all samples. The highest levels of CaO characterized the marketable phosphate with a maximum of around 49.51% for the Redeyef laundry, and 47.93% for the ZL laundry, whereas the lowest levels are recorded with the fine wastes (Table 3).
Considering the P 2 O 5 contents, it is worth noting that the washing process at M'Dhilla-Zone L and Redeyef results in the enrichment of the marketable ore (29.37% and 28.45%, respectively), consequently eliminating the coarse and fine wastes, which are low in phosphate (18.81% and 8.45% P 2 O 5 , respectively).
With regards to samples extracted from both laundries, the CaO/P 2 O 5 ratios show that the values for raw and market phosphates range from 1.63 to 1.94, the lowest values (1.63-1.74) characterize the marketable phosphates. The latter are slightly higher than the corresponding ratio in pure CFA, which is estimated at 1.57 [27]-1.62 [28], indicating that the apatite dealt with is chemically identifiable to CFA [8,[29][30][31][32][33][34][35][36]. The higher values obtained for the coarse and fine wastes (2.03-2.54) are indicative of high contents of carbonates as gangue minerals.
The oxides SiO 2 , Al 2 O 3 , and Fe 2 O 3 characterize mainly the fine wastes (Table 3), which is indicative of the abundance of alumino-silicates in the sludge in both laundries and in particular those of Redeyef (32.29%, 7.34%, and 5.97%, respectively).
Likewise, MgO (1.96% for ZL and 2.25% for Redeyef) is generally known as a component deriving from magnesian clay and dolomite.
Zinc contents ranged between 151.6 mg/kg and 292 mg/kg, with the highest levels detected in fine wastes (271.6 mg/kg for FW-ZL and 292 mg/kg for FW-R), whereas in all other fractions, the contents ranged between 151.6 mg/kg and 220 mg/kg. Although Zn may easily permeate the apatite structure, the high contents observed in the fine wastes, especially in Redeyef, may be attributed to the high content in OM.
The distribution of Cd was different, with the highest concentrations being recorded in both fine wastes (30.6 mg/kg for FW-R and 25.9 mg/kg for FW-ZL) and raw phosphates (19.7 mg/kg for RP-ZL and 28.8 mg/kg for RP-R) ( Table 3). With its bivalent state and the ionic radius of 0.97A • [42] being close to that of Ca (0.99A • ), Cd can replace Ca in the apatite structure. Therefore, cadmium has been associated with the apatite structure, even though in very small quantities [29,32,34,43]. Equally, cadmium can be also adsorbed by apatite crystals [44].
Chromium content ranged between 122.2 mg/kg and 466.5 mg/kg (Table 3). Fine wastes from the two laundries contained the highest amounts (302.3 mg/kg for FW-ZL and 466.5 mg/kg for FW-R), making up to three times the Cr contents in the other fractions (182 mg/kg to 187 mg/kg). This result shows, firstly, that Cr is essentially associated both to the clay-phosphate fraction and organic matter [29], especially at Redeyef, and secondly, as stipulated by Galfati et al. [8], this result shows that most of this element recorded in fine wastes derives from the corrosion of the process installations (chrome steel-made hydrocyclones).
Uranium distribution shows small fluctuations between the raw phosphates (31 mg/kg for RP-ZL and 28.7 mg/kg for RP-R) and the marketable phosphates (28.87 mg/kg for MP-ZL and 35.1 mg/kg for MP-R). With regards to wastes, U concentrations revealed a small decrease in terms of coarse wastes at M'Dhilla (22.87 mg/kg). Yet, this decrease was noticed with both cases, coarse and fine wastes, at Redeyef (19.35 mg/kg and 23 mg/kg, respectively). These findings indicate that U is evenly distributed between the phosphatic phase and the exogangue at M'Dhilla but is closer to the phosphatic phase at Redeyef.
In terms of raw phosphates, Pb displayed the lowest concentration rate among trace elements (3.9 mg/kg for RP-R and 5.15 mg/kg for RP-ZL). The levels recorded in the output products are slightly variable but more significant in the fine wastes (4.37 mg/kg for FW-ZL and 8.9 mg/kg for FW-R) ( Table 3).
In another respect, and compared to other sedimentary rocks, it is generally known that REEs are enriched in marine phosphorites [37,40,41,[45][46][47]. In our samples, and even though characterized by patterns similar in shape, the REEs show variable concentration rates (Table 3), all of which display a slight enrichment in light REEs (LREEs), compared to heavy REEs (HREEs), along with negative Ce and Tb anomalies and a positive Eu anomaly (Figure 3). The cerium anomaly indicates that phosphate has formed in a suboxic to oxic marine environment that is deficient in this element [48]. However, the Tb anomaly, which was previously reported for phosphates in the Gafsa-Métlaoui Basin [8,33,40,49,50], should be relevant in terms of analytical problems only [12,51,52]. According to Fryer [53], the variations in the Eu contents result from the reduction of this element to the valence 2+, deriving from the modifications observed in the redox conditions. In another respect, the input products (RP) from the two laundries bear almost similar total concentrations (∑REE of around 204.39 mg/kg for M'Dhilla and 218.66 mg/kg for Redeyef). Similarly, and although the marketable phosphates from both laundries bear more significant total contents in REEs (248.68 mg/kg for MP-ZL and 251.29 mg/kg for MP-R), the coarse and fine wastes still carry considerable quantities of REEs at M'Dhilla-Zone L (184.3 mg/kg and 210.32 mg/kg, respectively) but much lower total contents at Redeyef (114.42 mg/kg and 125.27 mg/kg, respectively). The high contents of REEs in the fine wastes of M'Dhilla are strongly related to their P 2 O 5 content (16.87%). As indicated by Slansky [30], it can be stated that REEs have an affinity for phosphates because of their substitution for Ca 2+ in the apatite structure, on the one hand, and their correlation with the organic matter present in pellets, on the other.
to heavy REEs (HREEs), along with negative Ce and Tb anomalies and a positive Eu anomaly (Figure 3). The cerium anomaly indicates that phosphate has formed in a suboxic to oxic marine environment that is deficient in this element [48]. However, the Tb anomaly, which was previously reported for phosphates in the Gafsa-Métlaoui Basin [8,33,40,49,50], should be relevant in terms of analytical problems only [12,51,52]. According to Fryer [53], the variations in the Eu contents result from the reduction of this element to the valence 2+, deriving from the modifications observed in the redox conditions. In another respect, the input products (RP) from the two laundries bear almost similar total concentrations (∑REE of around 204.39 mg/kg for M'Dhilla and 218.66 mg/kg for Redeyef). Similarly, and although the marketable phosphates from both laundries bear more significant total contents in REEs (248.68 mg/kg for MP-ZL and 251.29 mg/kg for MP-R), the coarse and fine wastes still carry considerable quantities of REEs at M'Dhilla-Zone L (184.3 mg/kg and 210.32 mg/kg, respectively) but much lower total contents at Redeyef (114.42 mg/kg and 125.27 mg/kg, respectively). The high contents of REEs in the fine wastes of M'Dhilla are strongly related to their P2O5 content (16.87%). As indicated by Slansky [30], it can be stated that REEs have an affinity for phosphates because of their substitution for Ca 2+ in the apatite structure, on the one hand, and their correlation with the organic matter present in pellets, on the other.

Water Quality
The water samples collected from drilling water (DW), recycled water (RW), and sludge water (SW) and recovered from the laundries after natural decantation and filtration, were submitted to chemical analysis in order to determine the anion (F -, NO2 -, NO3 -,

Water Quality
The water samples collected from drilling water (DW), recycled water (RW), and sludge water (SW) and recovered from the laundries after natural decantation and filtration, were submitted to chemical analysis in order to determine the anion (F − , NO 2 − , NO 3 − , PO 4 3− , and SO 4 2− ) and trace element (Cd, Fe, Pb, Zn, and U) contents. Table 4 presents the results.
The pH values of the discharge water, which were measured in situ, at the exit of the laundries were 7.87 at M'Dhilla-ZL and 7.07 at Redeyef, reflecting the slight alkaline nature of the wastewater. The feedwater used in the phosphate washing units comes from the various aquifers in the region. At M'Dhilla, the wash (drilling) water shows high loads, exceeding the World Health Organization (WHO) standards, in sulfates (1979 mg/L), fluorine (23.75 mg/L), and nitrites (15.3 mg/L), while the sludge water is heavily loaded with sulfates (2570 mg/L), fluorine (47 mg/L), and cadmium (14.14 µg/L). At Redeyef, the wash water is rich in fluorine (1.9 mg/L), while the sludge water is contaminated with Cd (6.12 µg/L).

Evaluation of Fine Waste-Iron Mobility: Batch Experiments
In this study, batch tests were carried out to assess the potential mobility and hydro solubility of MTE contained in the fine wastes of the laundries of the study area.

pH and Conductivity
The pH variations of the leachate representative of the whole cycles of the test are provided in Figure 4. The pH values recorded for the leachate of the sample FW-ZL show a gradual increase from a minimum of 7.07 to a maximum of 7.73 during the second cycle, followed by a decrease until stabilization during the last three cycles at a value close to 7.55. The increased portion in pH could be explained by the dissolution of CaCO 3 , the content of which is higher in these wastes (Table 3). However, pH values of the sample FW-R gradually decrease from 7.87, before they stabilize again during the last three cycles at 7.45.
Results of the EC measured on the leachates in both samples FW-ZL and FW-R are displayed by the two curves provided in Figure 4. This phenomenon shows an increase during the first cycle, then the conductivity decreases during the second cycle, and stabilizes during the subsequent cycles. It is shown, however, that the EC values are high for both samples, but those measured for FW-ZL (10.97 ms/cm to 20 ms/cm) are much larger compared to those of FW-R (3.85 ms/cm to 7.85 ms/cm), indicating a greater ionic charge in the solution for FW-ZL.
The high values of EC can be explained by the dissolution of the more soluble minerals, such as gypsum and calcite ( Table 2). The highest values characterizing the first cycle for the leachates of both samples can be explained by the solubilization of the gypsum contained in the fine wastes [54]. Subsequently, the stable conductivity values during the last four cycles may be attributed to the stability of the leached ion fluxes.

Mobilisation of Cd and U
The concentrations of Cd and U, as measured in the leachate from batch tests, are displayed in Figure 5. First, we shall underscore the similarity in the behavior of the two elements throughout the seven cycles for both waste samples; both show a general tendency to increase during the first four cycles to a maximum (17.53 µg/L and 4.41 µg/L, respectively, for M'Dhilla, and 8.68 µg/L and 3.78 µg/L, respectively, for Redeyef), and with a stabilization (plateau) over the last three cycles, indicating the stability of the fluxes of both elements that go into solution during each cycle at this stage of the experiment. These results show that cadmium is more mobile than uranium because its mobility is more pronounced for the sample FW-ZL. However, the cadmium contents in the leachate, recovered during both batch experiments (11.9 µg/L-17 µg/L for FW-ZL and 5.4 µg/L-8.7 µg/L for FW-R), exceed the WHO standards required for potable water (3 µg/L).
The high values of EC can be explained by the dissolution of the more soluble minerals, such as gypsum and calcite ( Table 2). The highest values characterizing the first cycle for the leachates of both samples can be explained by the solubilization of the gypsum contained in the fine wastes [54]. Subsequently, the stable conductivity values during the last four cycles may be attributed to the stability of the leached ion fluxes.

Mobilisation of Cd and U
The concentrations of Cd and U, as measured in the leachate from batch tests, are displayed in Figure 5. First, we shall underscore the similarity in the behavior of the two elements throughout the seven cycles for both waste samples; both show a general tendency to increase during the first four cycles to a maximum (17.53 µg/L and 4.41 µg/L, respectively, for M'Dhilla, and 8.68 µg/L and 3.78 µg/L, respectively, for Redeyef), and with a stabilization (plateau) over the last three cycles, indicating the stability of the fluxes of both elements that go into solution during each cycle at this stage of the experiment. These results show that cadmium is more mobile than uranium because its mobility is more pronounced for the sample FW-ZL. However, the cadmium contents in the leachate, recovered during both batch experiments (11.9 µg/L-17 µg/L for FW-ZL and 5.4 µg/L-8.7 µg/L for FW-R), exceed the WHO standards required for potable water (3 µg/L).
The percentages of Cd and U mobility in the solid fraction of the sludge, which are calculated from the ratio between the concentrations mobilized by the extractant (sludge water) to the total concentration of MTE, show that the mobility of both elements is low, with percentages not exceeding 0.067% and 0.014%, respectively, for M'Dhilla, and 0.028% and 0.016% for Redeyef.

Discussion
The fine petrographic, mineralogical, and geochemical characterization showed significant differences between the two sludge samples analyzed.
Equally, the particle-size distribution showed that the sludge from the Redeyef laundry is enriched in fine fraction (82.84%) compared to that from M'Dhilla-ZL (58.87%). The percentages of Cd and U mobility in the solid fraction of the sludge, which are calculated from the ratio between the concentrations mobilized by the extractant (sludge water) to the total concentration of MTE, show that the mobility of both elements is low, with percentages not exceeding 0.067% and 0.014%, respectively, for M'Dhilla, and 0.028% and 0.016% for Redeyef.

Discussion
The fine petrographic, mineralogical, and geochemical characterization showed significant differences between the two sludge samples analyzed.
Equally, the particle-size distribution showed that the sludge from the Redeyef laundry is enriched in fine fraction (82.84%) compared to that from M'Dhilla-ZL (58.87%).
The mineralogical study showed the presence of the following minerals in the two fine wastes: CFA, clinoptilolite, calcite, dolomite, gypsum, ankerite, quartz, and other silicates, such as smectite and palygorskite. We also deduced that the latter are more abundant in the fine wastes of the Redeyef laundry.
The wet processing of raw phosphate is a simple physical process of granulometric classification resulting in the separation of the merchant ore (71 µm-2000 µm) enriched in CFA, from the fine (−71 µm) and coarse (+2000 µm) fractions enriched in gangue minerals (carbonates, silicates, etc.).
Chemical analysis showed that carbonates, P 2 O 5 , U, and REEs are more abundant in the fine wastes from M'Dhilla-ZL (17.47%, 18.81%, 30.2 mg/kg, and 210.3 mg/kg, respectively), whereas higher contents in organic matter, Fe 2 O 3 , and Al 2 O 3 characterize the sludge from Redeyef (3.89%, 5.97%, and 7.34%, respectively). It should be noted, however, that Cd, Cr, and Zn are more concentrated in the fine wastes of both laundries, as compared to their content in the raw phosphate.
Batch experiments showed that, although the two fine waste samples of M'Dhilla-ZL and Redeyef laundries contain close total contents in Cd (26 mg/kg and 30.6 mg/kg, respectively); and U (30.2 mg/kg and 23 mg/kg, respectively), they behaved quite differently during the tests.
With regards to pH conditions, the slightly alkaline conditions prevailed during the whole test. As a result, heavy metals are characterized by low mobility due to precipitation reactions, and the increase of adsorption sites is linked to OM (carboxyl groups), oxyhydroxides, and clay minerals [55,56], as well as the decrease of H + ions competition for adsorption [57]. Furthermore, the higher content in clay-phosphate fraction, clinoptilolite, and OM in the fine wastes of Redeyef (FW-R) seemed to have played a role in the retention of Cd, consequently, its low mobility with respect to Cd in the case of the equivalent sample from M'Dhilla-ZL (FW-ZL).
Considering the sample FW-R, Cd could be associated with the phosphatic phase and adsorbed on the surface of silicate minerals (clays and clinoptilolite), which are plentiful in fine fractions. Besides aluminosilicates, these fine wastes contain also high amounts of OM ( Table 3). Both of them are capable of adsorbing cadmium, consequently reducing its mobility [58], which makes it difficult to be released by leaching. Indeed, thanks to their very large specific surfaces (up to 800 m 2 /g) and their great cation-exchange capacities, organic matter and silicate minerals are believed to be excellent absorbents [59][60][61]. Clinoptilolite, with its cavernous structure, has a very high selective retention capacity for certain heavy metals, in particular Cd [62].
With regards to the sample FW-ZL, the significant mobility of Cd is attributed to its high content of phosphate and low content of silicate minerals, with high metal adsorption capacity. In freshwater, aqueous species of cadmium consist of Cd 2+ , Cd(OH) 2 0, and CdHCO 3 − [63], among which Cd 2+ is the dominant ionic species up to pH 8 [64][65][66][67], which is a free and very reactive (bioavailable) form [58,[68][69][70].
Likewise, the adsorption phenomenon by aluminosilicates and the carbonated nature of the two fine wastes may account for the small quantities of released uranium. As postulated by Altschuler et al. [71], Sassi [29], Baturin et al. [72], Giresse et al. [73], and Chaabani [32], an important part of uranium is adsorbed onto apatite in an oxidized form. According to Sassi [29] and Favas et al. [74], uranium can also be adsorbed on clays and other organic matter.
In natural water, uranium can exist mainly as U 4+ and U 6+ ions, the abundance of which is influenced by the presence and the profusion of complexing agents, as well as the prevailing pH and Eh conditions [75][76][77][78]. U (IV) is the most dominant form in reducing environments, while U (VI) is prevalent in oxidizing environments [79,80]. Furthermore, tetravalent U is extremely resistant to leaching, whereas hexavalent U is highly mobile. At pH > 5, U mobility is due to the complexation of uranyl ions (UO 2 2+ ) by carbonate, phosphate, and hydroxyl species [74][75][76]78,[80][81][82][83][84]. Besides pH and Eh, uranyl speciation may also be influenced by organic ligand concentration [81], as long as the two fine wastes being considered bear high amounts of organic matter (Table 3).

Conclusions
This study, dealing with the input and output products of the laundries of Redeyef and M'Dhilla-ZL in the Gafsa-Metlaoui Basin, has shown that these products bear the same mineral assemblages (CFA, calcite, dolomite, ankerite, quartz, gypsum, and clinoptilolite), with varying proportions from fraction to fraction. Also, geochemical analyses have revealed that the majority of metallic elements (Cr, Zn, Cd, and Pb) are most often concentrated in the fine wastes (<71 µm) and associated with the clay-phosphate fraction, whereas the contents of rare earth elements and U are higher in the marketable and raw phosphate fractions.
The geochemical study of the water shows that, at M'Dhilla, the feed (drilling) water, which is used for washing, is loaded with sulfates (1979 mg/L), fluorine (2.37 mg/L), and nitrites (15.3 mg/L), while the sludge water is loaded with even more sulfates (2570 mg/L) and fluorine (4.7 mg/L), besides Cd (14.14 µg/L). At Redeyef, the feedwater is slightly loaded with fluorine (1.9 mg/L), while the sludge water is loaded with Cd (6.12 µg/L). Equally, the leaching tests that were conducted on fine wastes from both laundries have revealed that only small proportions of Cd and U are mobilized (≤0.07% and ≤0.02%, respectively).
These results show that, in both localities, feed (drilling) and process (sludge) water, which are loaded with fluorine and cadmium, along with sulfate at M'Dhilla, exceed the WHO standards for potable water for fluoride (M'Dhilla and Redeyef), cadmium (M'Dhilla and Redeyef), and sulfate (M'Dhilla), indicating that these elements account for the water resource pollution in the region. This pollution rate is even more conspicuous in M'Dhilla than in Redeyef.
These results should prompt the CPG to review its strategy for managing discharges from the phosphate industry, especially to safeguard both surface and underground water resources in the region.