Inﬂuence of Operating Parameters on Photocatalytic Oxidation of 2,4-Dichlorofenol in Aqueous Solution by TiO 2 /Stainless Steel Photocatalytic Membrane

: The inﬂuence of some operating parameters of an UV photocatalytic reactor with TiO 2 / stainless steel photocatalytic membrane on the photocatalytic oxidation of 2,4-dichlorophenol from aqueous solutions was studied in this paper. It was shown that the pH of the working solution substantially inﬂuences the photocatalytic degradation of the organic substrate, with the degradation efﬁciency increasing with decreasing the pH of the working solution by a maximum corresponding to pH 3. The rate constant of the photocatalytic oxidation process is about twice as high at pH 3 comparative with pH 7 for the same initial concentration of the organic substrate. The molar ratio of hydrogen peroxide/organic substrate also inﬂuences the photocatalytic oxidation process of the organic substrate. The results obtained in this paper highlight the fact that a stoichiometric molar ratio is favorable for the photocatalytic degradation of 2,4-dichlorophenol. It has also been shown that the initial concentration of the organic substrate inﬂuences the rate of photocatalytic degradation. It appears that the rate of photocatalytic degradation decreases with the increasing of initial concentration of 2,4-dichlorophenol.


Introduction
The rapid development of various industrial sectors around the world has recently led to an increase in the diversity of pollutants that reach natural water bodies. Many of these pollutants cannot be removed naturally from these waters. Therefore, they have a long residence time and can have a serious long-term negative effect on these natural systems [1,2]. A significant category of these persistent pollutants is represented by refractory organic compounds, which include chlorophenols. They end up in wastewater resulting from the manufacture of pesticides, paints, polymers, cosmetics, etc., and because they cannot be removed by conventional methods in wastewater treatment plants, they arrive in natural water bodies [3,4].
2,4-dichlorophenol is one of the most toxic chlorophenols with a major negative impact on aquatic life and human health and, therefore, is classified as a priority pollutant in the United States of America (USA) and European Union (EU) [5]. It is also persistent and bioaccumulative in the environment, being suspected of producing carcinogenic and mutagenic effects on living organisms [6]. The World Health Organization (WHO) has set a maximum allowable concentration of 0.1 µg/L in drinking water and 1 mg/L in treated wastewater discharged into natural water bodies [7].
Photochemical advanced oxidation processes are the most widely used methods for wastewater treatment containing refractory organic compounds. Of these, the most popular seems to be the photocatalytic oxidation [8,9]. Titanium dioxide is the most used photocatalyst due to its advantages such as high stability, low toxicity, availability, low cost, and low environmental adversity [10]. The photocatalyst can be immobilized in the photocatalytic reactor (either by depositing it on a membrane, by adding it to a membrane, or by making a stand-alone photocatalyst membrane), or it can be dispersed in the aqueous solution to be treated. It has been shown that each option to configure the photocatalytic reactor has both advantages and disadvantages depending on the specific application [11]. For example, photocatalytic reactors with dispersed photocatalysts usually have the main advantage of a larger active surface area which generally gives them a higher substrate degradation efficiency than photocatalytic reactors with immobilized photocatalysts. Instead, this type of photocatalytic reactor has the major disadvantage of the need to separate the photocatalyst from the suspension and reuse it [12][13][14][15]. At the same time, photocatalytic reactors with immobilized photocatalyst have, among other things, the great advantage of the possibility of being operated continuously, at least for the time interval in which the membrane has sufficient photocatalytic activity. Regeneration of photocatalytic membranes is usually much easier to achieve compared to dispersed photocatalysts [16][17][18][19].
However, regardless of the reactor configuration, the photocatalytic activity of the system largely depends on its operating parameters, such as the initial organic substrate concentration, photocatalyst loading, photocatalytic reactor and photocatalytic membrane geometry, the physico-chemical characteristics of the aqueous solution subjected to the treatment, light wavelength and its intensity, etc. Despite the many studies conducted in this field that have led to significant achievements, there are still many problems that need to be solved, especially for specific applications and photocatalytic systems designed to work on an industrial scale [20].
Usually, the efficiency of removing the refractory organic material from aqueous solutions depends on the particularities of the photocatalytic system used [21]. For example, studies on TiO 2 -based UV photocatalytic degradation of 2,4-dichlorophenol have shown that the efficiency of removing refractory organic material from aqueous solutions as a function of its initial pH differs from one photocatalytic system to another. Thus, it was found that for a photocatalytic system with dispersed TiO 2 , the photocatalytic degradation efficiency is maximum at a pH of the aqueous solution of 5 [22]. For a photocatalytic system with dispersed TiO 2 intercalated talc nanocomposite, the best results were recorded for neutral conditions of the aqueous solution of 2,4-dichlorophenol [23]. In the case of a photocatalytic system with dispersed Fe/TiO 2 , the maximum degradation efficiency of 2,4-dichlorophenol in aqueous solution was recorded at a pH of 4 [24]. For a photocatalytic system with a Fe 0 /TiO 2 /ACF (activated carbon fiber) composite photocatalytic membrane, it has been established that the optimum pH of the aqueous 2,4-dichlorophenol solution subjected to the photocatalytic treatment is 6 [25]. Thus, it becomes clear that for each new photocatalytic system, it is necessary to optimize the operating parameters in order to obtain the highest possible photocatalytic degradation efficiency of specific refractory organic compounds.
Therefore, the influence of some operating conditions on the performances of an UV photocatalytic reactor with an immobilized photocatalyst (new photocatalytic membrane -titanium dioxide deposited on the stainless-steel grid support, TiO 2 /stainless steel) for removing 2,4-dichlorophenol from aqueous solutions was studied in this work. The paper aims to identify the optimal pH of the working solution and to establish the need for hydrogen peroxide to be added to the system so that the efficiency of photocatalytic degradation is as high as possible. The influence of the initial concentration of the organic substrate is also investigated.

Materials and Reagents
2,4-dichlorophenol (C 6 H 4 Cl 2 O) used in experiments as an organic substrate was of analytical grade and was purchased from Fluka Chemicals. In the text of the paper, the acronym 2,4-DCF will be used for this reagent. Hydrogen peroxide (H 2 O 2 ) solution 30% Appl. Sci. 2021, 11, 11664 3 of 17 by mass was purchased from Sigma-Aldrich, and it was used as a source of hydroxyl radical species. A solution of 1 N (normality) sulfuric acid (H 2 SO 4 ) purchased from Sigma-Aldrich was used to adjust the pH of the working solutions to the default values. Chemical oxygen demand (COD) analysis was performed by using potassium dichromate (K 2 Cr 2 O 7 ), mercuric sulfate (HgSO 4 ), silver sulfate (Ag 2 SO 4 ), potassium acid phthalate (C 8 H 5 KO 4 ), as well as sulfuric acid 95-97% by mass, all of them of analytical grade purchased from Sigma-Aldrich. Distilled water was used to prepare all reagent and working solutions. The photocatalytic membrane is made from a stainless-steel grid support (cylindrical shape, 10 cm × 30 cm) on which TiO 2 (P25 from Degussa, Essen, Germany) was deposited by electrophoretic deposition.

Dark Adsorption Experiments
Dark adsorption experiments were performed under same conditions with photocatalytic degradation experiments but without putting into operation the UV lamp of the photocatalytic reactor (without UV radiation) and without addition of hydrogen peroxide. In this respect, a UV photocatalytic reactor with photocatalytic membrane was used in which the working solution was continually recirculated through a recirculation vessel by means of an external centrifugal pump. The photocatalytic reactor is designed so that the UV lamp, the photocatalytic membrane, and the water-cooling jacket are coaxially positioned inside it. The characteristics and operating parameters of the photocatalytic reactor are presented in Table 1. In the case of experiments on adsorption isotherms, working solutions were prepared with the initial COD equivalent concentration of 2,4-DCF ranging from 50 to 300 mg O 2 /L. It should be mentioned that because in photocatalytic experiments it is more useful to report the content in organic substrate in terms of organic carbon (OC), throughout this work the content in organic substrate is expressed exclusively in terms of organic carbon. Thus, for adsorption isotherms experiments the organic carbon equivalent initial concentrations of 2,4-DCF solutions ranged from 18.75 to 112.50 mg OC/L. After the solutions were prepared, their pH was adjusted to the default values (pH of 2, 3, 5, and 7). Next, each working solution was introduced in the photocatalytic reactor, and by means of the external centrifugal pump these were recirculated at room temperature until the equilibrium concentration was reached. The samples by which the adsorption equilibrium was checked were taken from the photocatalytic reactor by means of its special sampling holes without the need to turn it off. Next, the samples were prepared and measured for their organic content by COD analysis following the APHA 5220 D standard method [26]. Both LT 200 thermostat and DR 3800 spectrophotometer (Hach Lange GmbH, Weinheim, Germany) were used to carry out the analysis. Regeneration of the photocatalytic membrane was accomplished by operating the reactor charged with distilled water to which oxygen peroxide was added for two hours in the presence of UV radiation. The regeneration procedure was applied where q eq is the amount of 2,4-DCF adsorbed on the photocatalytic membrane at equilibrium (mg/g), V is the volume of the working solution (L), C 0 and C eq are the initial and equilibrium concentration of 2,4-DCF (mg/L), and m is the mass of the photocatalytic membrane (g). The adsorption isotherms were plotted in terms of the amount of 2,4-DCF adsorbed (expressed as organic carbon) on the photocatalytic membrane q eq (mg/g) against of equilibrium concentration of 2,4-DCF C eq (mg/L). The experiments on adsorption kinetics were performed in the same way as those on adsorption isotherms. For these experiments, working solutions were prepared with initial COD equivalent concentration of 2,4-DCF of 100, 200, and 300 mg O 2 /L. Thus, the organic carbon equivalent initial concentrations of 2,4-DCF solutions were 37.50, 75.00, and 112.50 mg OC/L. The amount of 2,4-DCF adsorbed on the photocatalytic membrane was determined was established based on Equation (2).
where q t is the amount of 2,4-DCF adsorbed on the photocatalytic membrane at time t (mg/g), V is the volume of the working solution (L), C 0 and C t are the initial and residual concentration of 2,4-DCF at time t (mg/L), and m is the mass of the photocatalytic membrane (g). A pseudo-second-order kinetic model was used to evaluate the experimental data for adsorption kinetics.

Photocatalytic Oxidation Experiments
The photocatalytic degradation was conducted by monitoring the evolution of the organic content of the working solution as a function of irradiation time. Thus, samples of about 10 mL were taken from reactor at predetermined irradiation times. After the solutions were prepared, their pH was adjusted to the default value and the calculated amount of hydrogen peroxide was added. Further, the experiments were performed similar to the previous ones, except that the UV lamp was turned on. The experimental conditions are presented in Table 1.

Adsorption Isotherms
The adsorption isotherms obtained for 2,4-DCF-TiO 2 /stainless steel system for the four pH values of the working solution are presented in Figure 1. To describe the types of interactions between the adsorbate (2,4-DCF) and the adsorbent (TiO 2 /stainless steel membrane), and to determine the maximum adsorption capacity of the adsorbent, Langmuir (Equation (3)) and Freundlich (Equation (4)) isotherm models were used [27]. The parameters of the adsorption process are presented in Table 2. As can be seen, the pH value of the working solution influences the adsorption process, the adsorption capacity at pH 3 being about 13% higher than at pH 7. The slight decrease of the adsorption capacity at pH 2 could be attributed to the increase of the instability of the photocatalytic membrane in strong acidic conditions (i.e., formation of titanium hydroxo complexes with hydroxyl ions release) which leads to the modification of the properties of the aqueous environment in which the adsorption takes place.
where q e is the adsorption capacity at equilibrium (mg 2,4-DCF/g of adsorbent), K L is the Langmuir adsorption constant (L/mg), K F is the Freundlich adsorption constant (mg 1−n ·L n /g) related to the energy of adsorption, C e is the equilibrium concentration of 2,4-DCF in the aqueous solution (mg/L), q m is the maximum adsorption capacity (mg 2,4-DCF/g of adsorbent) and 1/n is the heterogeneity factor (dimensionless).
DCF in the aqueous solution (mg/L), qm is the maximum adsorption capacity (mg 2,4-DCF/g of adsorbent) and 1/n is the heterogeneity factor (dimensionless). The value of parameter n in the Freundlich model provides information on the average adsorption energy. If n has values less than 1, the interactions between adsorbent and adsorbate are weak, and if n is greater than 1 the interactions are strong. At values of n equal to 1 it is assumed that all active centers are similar in terms of energy, and the experimental data fit better on the theoretical curves obtained with the Langmuir model. In this respect, as can be seen for all working conditions, the parameter n has values above 1 which suggests that there is a strong interaction between 2,4-DCF and the adsorbent, but the number of heterogeneous active centers is limited. Therefore, this is also the reason why the experimental data fit better on the Langmuir isotherm. It can also be seen that the value of parameter n increases with the decrease of the pH of the working solution which indicates that the interactions between the adsorbent and chlorophenol are stronger in acidic medium.    The value of parameter n in the Freundlich model provides information on the average adsorption energy. If n has values less than 1, the interactions between adsorbent and adsorbate are weak, and if n is greater than 1 the interactions are strong. At values of n equal to 1 it is assumed that all active centers are similar in terms of energy, and the experimental data fit better on the theoretical curves obtained with the Langmuir model. In this respect, as can be seen for all working conditions, the parameter n has values above 1 which suggests that there is a strong interaction between 2,4-DCF and the adsorbent, but the number of heterogeneous active centers is limited. Therefore, this is also the reason why the experimental data fit better on the Langmuir isotherm. It can also be seen that the value of parameter n increases with the decrease of the pH of the working solution which indicates that the interactions between the adsorbent and chlorophenol are stronger in acidic medium.
The analysis of the adsorption parameters obtained with Langmuir model provides a similar image to the one outlined in the analysis of the adsorption parameters obtained with the Freundlich model. Thus, the values of the maximum adsorption capacity q mmax and of the Langmuir adsorption constant (K L ) increase with the decrease of the pH values of the working solution with a maximum corresponding to pH 3. Because the Langmuir adsorption constant provides information on the binding energy between the adsorbent and the adsorbate, increasing its values as the pH of the working solution decreases indicates that the binding energy between chlorophenol and the adsorbent is higher in acidic aqueous solutions.

Adsorption Kinetics
The adsorption kinetics for 2,4-DCF-TiO 2 /stainless steel system for the four pH values of the working solution is presented in Figure 2 (non-linear fitting) and Figure 3 (linear fitting). It is observed that the adsorption process proceeds rapidly, the adsorption equilibrium being reached after about 30 min regardless of the initial concentration of 2,4-DCF. The pH of the working solution influences the adsorption capacity of the photocatalytic membrane in the sense that for the same initial concentration of 2,4-DCF there is an increase in the adsorption capacity of the catalyst as the pH of the working solution decreases with a maximum corresponding to pH 3. Thus, for an initial concentration of 2,4-DCF of 84.9 mg/L the adsorption capacity of the catalyst increases from 5.311 mg 2,4-DCF/g adsorbent at pH 7 to 8.413 mg 2,4-DCF/g adsorbent at pH 3, for an initial concentration of 169.79 mg/L the adsorption capacity of the catalyst increases from 10.739 mg 2,4-DCF/g adsorbent at pH 7 to 14.803 mg 2,4-DCF/g adsorbent at pH 3, and for an initial concentration of 254.69 mg/L the adsorption capacity of the catalyst increases from 12.190 mg 2,4-DCF/g adsorbent at pH 7 to 19.156 mg 2,4-DCF /g adsorbent at pH 3.
Appl. Sci. 2021, 11, x FOR PEER REVIEW 6 of 16 The analysis of the adsorption parameters obtained with Langmuir model provides a similar image to the one outlined in the analysis of the adsorption parameters obtained with the Freundlich model. Thus, the values of the maximum adsorption capacity qmmax and of the Langmuir adsorption constant (KL) increase with the decrease of the pH values of the working solution with a maximum corresponding to pH 3. Because the Langmuir adsorption constant provides information on the binding energy between the adsorbent and the adsorbate, increasing its values as the pH of the working solution decreases indicates that the binding energy between chlorophenol and the adsorbent is higher in acidic aqueous solutions.

Adsorption Kinetics
The adsorption kinetics for 2,4-DCF-TiO2/stainless steel system for the four pH values of the working solution is presented in Figure 2 (non-linear fitting) and Figure 3 (linear fitting). It is observed that the adsorption process proceeds rapidly, the adsorption equilibrium being reached after about 30 min regardless of the initial concentration of 2,4-DCF. The pH of the working solution influences the adsorption capacity of the photocatalytic membrane in the sense that for the same initial concentration of 2,4-DCF there is an increase in the adsorption capacity of the catalyst as the pH of the working solution decreases with a maximum corresponding to pH 3. Thus, for an initial concentration of 2,4-DCF of 84.9 mg/L the adsorption capacity of the catalyst increases from 5.311 mg 2,4-DCF/g adsorbent at pH 7 to 8.413 mg 2,4-DCF/g adsorbent at pH 3, for an initial concentration of 169.79 mg/L the adsorption capacity of the catalyst increases from 10.739 mg 2,4-DCF/g adsorbent at pH 7 to 14.803 mg 2,4-DCF/g adsorbent at pH 3, and for an initial concentration of 254.69 mg/L the adsorption capacity of the catalyst increases from 12.190 mg 2,4-DCF/g adsorbent at pH 7 to 19.156 mg 2,4-DCF /g adsorbent at pH 3.   Second-order kinetics described by the equations presented below were used to estimate the kinetic parameters of the 2,4-DCF adsorption process [28]. The kinetic parameters and the correlation coefficients are presented in Table 3.
where qt is the adsorption capacity of the adsorbent at time t, qe represents the adsorption capacity of the adsorbent at equilibrium, and k represents the second order kinetic constant of the adsorption process, g·mg −1 ·min −1 . The integrated form of the above equation (considering the boundary conditions t = 0, t = t and qt = 0 qt = qe) is as follows: Rearranging the above equation, its linearized form is obtained: where h is the initial adsorption rate, mg·g −1 ·min −1 , and t1/2 represents the half-life, min.
Representing graphically t/qm as a function of t, a line is obtained from which qe, k, h, and t1/2 can be calculated from the slope, respectively, the line at its origin. Regarding the Second-order kinetics described by the equations presented below were used to estimate the kinetic parameters of the 2,4-DCF adsorption process [28]. The kinetic parameters and the correlation coefficients are presented in Table 3.
where q t is the adsorption capacity of the adsorbent at time t, q e represents the adsorption capacity of the adsorbent at equilibrium, and k represents the second order kinetic constant of the adsorption process, g·mg −1 ·min −1 . The integrated form of the above equation (considering the boundary conditions t = 0, t = t and q t = 0 q t = q e ) is as follows: Rearranging the above equation, its linearized form is obtained: where h is the initial adsorption rate, mg·g −1 ·min −1 , and t 1/2 represents the half-life, min. Representing graphically t/q m as a function of t, a line is obtained from which q e , k, h, and t 1/2 can be calculated from the slope, respectively, the line at its origin. Regarding the kinetic parameters of the adsorption process, namely the initial adsorption rate and the half-life, their values vary depending on the pH value of the working solution. Thus, the initial adsorption rate increases as the pH of the working solution decreases, and the half-life decreases as the pH of the working solution decreases. These results suggest that in addition to increasing the adsorption capacity of the catalyst as the pH of the working solution decreases, the rate of the adsorption process and therefore its overall efficiency also increases. It should be noted that this trend is maintained until a pH of the working solution of 3. At lower pH values, this trend appears to change slightly, most likely due to decreased photocatalytic membrane stability in a strongly acidic environment. The kinetic and thermodynamic results regarding the adsorption of 2,4-DCF on the TiO 2 /stainless steel photocatalytic membrane show that the efficiency of the adsorption process increases with the increase of the acidity of the working solution with a maximum corresponding to pH 3. This result is highlighted in Figure 4. As can be seen, simultaneously with the decrease of the adsorption process efficiency with the decrease of the acidity of the working solution there is also a decrease of the adsorption process efficiency with the increase of the initial chlorophenol concentration. The low efficiency recorded in all cases can be attributed to the fact that the adsorbent (TiO 2 catalyst) is deposited on a stainless-steel support in the form of a grid and is not suspended, with the specific surface in this case being smaller. kinetic parameters of the adsorption process, namely the initial adsorption rate and the half-life, their values vary depending on the pH value of the working solution. Thus, the initial adsorption rate increases as the pH of the working solution decreases, and the halflife decreases as the pH of the working solution decreases. These results suggest that in addition to increasing the adsorption capacity of the catalyst as the pH of the working solution decreases, the rate of the adsorption process and therefore its overall efficiency also increases. It should be noted that this trend is maintained until a pH of the working solution of 3. At lower pH values, this trend appears to change slightly, most likely due to decreased photocatalytic membrane stability in a strongly acidic environment. The kinetic and thermodynamic results regarding the adsorption of 2,4-DCF on the TiO2/stainless steel photocatalytic membrane show that the efficiency of the adsorption process increases with the increase of the acidity of the working solution with a maximum corresponding to pH 3. This result is highlighted in Figure 4. As can be seen, simultaneously with the decrease of the adsorption process efficiency with the decrease of the acidity of the working solution there is also a decrease of the adsorption process efficiency with the increase of the initial chlorophenol concentration. The low efficiency recorded in all cases can be attributed to the fact that the adsorbent (TiO2 catalyst) is deposited on a stainless-steel support in the form of a grid and is not suspended, with the specific surface in this case being smaller.

Kinetics of Photocatalytic Oxidation
Because the photocatalytic oxidation process mainly involves two stages, one of adsorption of the organic compound on the catalyst surface and another of photocatalytic oxidation itself, the experimental results were interpreted based on the Langmuir-Hinshelwood (L-H) model which takes into account these two main stages. The Langmuir-

Kinetics of Photocatalytic Oxidation
Because the photocatalytic oxidation process mainly involves two stages, one of adsorption of the organic compound on the catalyst surface and another of photocatalytic oxidation itself, the experimental results were interpreted based on the Langmuir-Hinshelwood (L-H) model which takes into account these two main stages. The Langmuir-Appl. Sci. 2021, 11, 11664 9 of 17 Hinshelwood (L-H) model was initially used to quantitatively describe solid-gas reactions. Currently the Langmuir-Hinshelwood model is also used to describe the kinetics of reactions that take place in the solid-liquid system by a rate law in which the reaction rate (r) is directly proportional to the fraction of surface area occupied by the substrate (θ) [29,30]: Considering the form of the Langmuir equation: and substituting in the above equation obtains: where k represents the rate constant, which is influenced by several parameters including catalyst mass, photon flux, etc. K represents the Langmuir-Hinshelwood equilibrium adsorption constant. Usually, the value of K is obtained from the Langmuir equation from kinetic studies performed in the presence of light, the results being much better than those obtained from studies in the dark. C represents the concentration of the organic substrate at time t. By integration, the above equation becomes: where C 0 represents the initial concentration of the organic substrate, and t represents the irradiation time. Equation (13) is considered to be of pseudo-zero order (Equation (14)) when the substrate concentration is high (>5 × 10 −3 mol/L), and the reaction rate will be maximum. In the case of diluted solutions, the substrate concentration is low (<10 −3 mol/L), and the reaction becomes apparently of pseudo-first order (Equation (15)).
The linearized form of the above equation is described by the equation: By graphically representing the term ln (C 0 /C) as a function of the irradiation time t, a line is obtained whose slope represents the apparent rate constant, k ap . Its value can be used to calculate the half-life t 1/2 . By the graphical representation of the term ln (C 0 -C) as a function of short irradiation times, it is possible to identify the area in which the reaction takes place after a kinetics of pseudo-zero order. By multiplying the apparent rate constant k ap obtained from the slope of the graph ln (C 0 /C) as a function of the irradiation time with the initial concentration of organic substrate C 0 , the value of the initial reaction rate r 0 is obtained for pseudo-first-order kinetics. This value can be used for comparison with other values of reaction rates obtained under various experimental conditions. After finding the value of the initial reaction rate, the values of the rate constant k and the adsorption constant K can be calculated using the model L-H described by an equation of the form: 1/r 0 = 1/kK · 1/C 0 + 1/k

Influence of pH of the Working Solution
The initial rate values were calculated according to the methodology described above and were plotted as a function to the initial concentration of 2,4-DCF expressed in terms of organic carbon (Figure 5a) for the four pH values of the working solution. To determine the kinetic parameters, the linearized form of the Langmuir-Hinshelwood model was used (Figure 5b). Figure 5b shows that for all pH values in the chosen concentration range (18.5-112.5 mg OC/L), there is a linear dependence characterized by regression coefficients with values close to unity. Table 4 shows the values of the kinetic parameters obtained for the three pH values of the working solution at a hydrogen peroxide/chlorophenol molar ratio (N) of 1.

Influence of pH of the Working Solution
The initial rate values were calculated according to the methodology described above and were plotted as a function to the initial concentration of 2,4-DCF expressed in terms of organic carbon (Figure 5a) for the four pH values of the working solution. To determine the kinetic parameters, the linearized form of the Langmuir-Hinshelwood model was used (Figure 5b). Figure 5b shows that for all pH values in the chosen concentration range (18.5-112.5 mg OC/L), there is a linear dependence characterized by regression coefficients with values close to unity. Table 4 shows the values of the kinetic parameters obtained for the three pH values of the working solution at a hydrogen peroxide/chlorophenol molar ratio (N) of 1.  From the data presented in Table 4 it is observed that the photocatalytic oxidation of 2,4-DCF takes place at a faster rate with the increasing of acidity of the working solution with a maximum corresponding to pH 3. The rate constant of the photocatalytic oxidation process (k) is about twice as high at pH 3 comparative with pH 7, and the adsorption constant (K) is about 1.4 times higher at pH 3 compared to that corresponding to pH 7. These results are consistent with the results obtained in the adsorption study in the absence of UV radiation (dark adsorption experiments), which confirms that at low pH values of the working solution the adsorption capacity of the catalyst is higher. Figure 6 shows that complete mineralization of 2,4-dichlorophenol at an initial concentration of 34. 6    From the data presented in Table 4 it is observed that the photocatalytic oxidation of 2,4-DCF takes place at a faster rate with the increasing of acidity of the working solution with a maximum corresponding to pH 3. The rate constant of the photocatalytic oxidation process (k) is about twice as high at pH 3 comparative with pH 7, and the adsorption constant (K) is about 1.4 times higher at pH 3 compared to that corresponding to pH 7. These results are consistent with the results obtained in the adsorption study in the absence of UV radiation (dark adsorption experiments), which confirms that at low pH values of the working solution the adsorption capacity of the catalyst is higher. Figure 6 shows that complete mineralization of 2,4-dichlorophenol at an initial concentration of 34.

Influence of Hydrogen Peroxide/Organic Carbon Molar Ratio
The initial rates were plotted as a function to the initial concentration of the organic carbon (Figure 7a) for the three hydrogen peroxide/organic carbon molar ratios used (N 0.5, N 1, and N 2) and at a pH of working solution of 3. The values of the kinetic parameters are presented in Table 5. As can be seen, the rate constant of the photocatalytic oxidation process (k) is about 1.2 higher at the molar ratio N 1 compared to the molar ratio N 2, and about 1.4 higher compared to the molar ratio N 0.5. The adsorption constant (K) has a value about 1.7 higher at the molar ratio N 1 compared to the molar ratio N 2, and about 2.7 higher compared to the molar ratio N 0.5.

Influence of Hydrogen Peroxide/Organic Carbon Molar Ratio
The initial rates were plotted as a function to the initial concentration of the organic carbon (Figure 7a) for the three hydrogen peroxide/organic carbon molar ratios used (N 0.5, N 1, and N 2) and at a pH of working solution of 3. The values of the kinetic parameters are presented in Table 5. As can be seen, the rate constant of the photocatalytic oxidation process (k) is about 1.2 higher at the molar ratio N 1 compared to the molar ratio N 2, and about 1.4 higher compared to the molar ratio N 0.5. The adsorption constant (K) has a value about 1.7 higher at the molar ratio N 1 compared to the molar ratio N 2, and about 2.7 higher compared to the molar ratio N 0.5.

Influence of Hydrogen Peroxide/Organic Carbon Molar Ratio
The initial rates were plotted as a function to the initial concentration of the organic carbon (Figure 7a) for the three hydrogen peroxide/organic carbon molar ratios used (N 0.5, N 1, and N 2) and at a pH of working solution of 3. The values of the kinetic parameters are presented in Table 5. As can be seen, the rate constant of the photocatalytic oxidation process (k) is about 1.2 higher at the molar ratio N 1 compared to the molar ratio N 2, and about 1.4 higher compared to the molar ratio N 0.5. The adsorption constant (K) has a value about 1.7 higher at the molar ratio N 1 compared to the molar ratio N 2, and about 2.7 higher compared to the molar ratio N 0.5.

Influence of Initial Concentration of the Organic Carbon
As expected, the initial concentration of the organic substrate influences the rate of photocatalytic degradation. In this respect, it seems that the photocatalytic degradation rate decreases with the increases of initial concentration of the organic substrate ( Figure  9a,b). From Figure 9c,d it can be observed that the evolution of photocatalytic degradation in time fits on a pseudo-first-order kinetics (the values of the correlation coefficient R 2 are between 0.9950 and 0.9995) and it is strong depending on the values of the initial concentration of the organic substrate. The apparent rate constant corresponding to the lowest initial organic carbon content is about 3.2 times higher than that corresponding to the highest initial organic carbon content.

Influence of Initial Concentration of the Organic Carbon
As expected, the initial concentration of the organic substrate influences the rate of photocatalytic degradation. In this respect, it seems that the photocatalytic degradation rate decreases with the increases of initial concentration of the organic substrate (Figure 9a,b). From Figure 9c,d it can be observed that the evolution of photocatalytic degradation in time fits on a pseudo-first-order kinetics (the values of the correlation coefficient R 2 are between 0.9950 and 0.9995) and it is strong depending on the values of the initial concentration of the organic substrate. The apparent rate constant corresponding to the lowest initial organic carbon content is about 3.2 times higher than that corresponding to the highest initial organic carbon content.

Influence of Initial Concentration of the Organic Carbon
As expected, the initial concentration of the organic substrate influences the rate of photocatalytic degradation. In this respect, it seems that the photocatalytic degradation rate decreases with the increases of initial concentration of the organic substrate ( Figure  9a,b). From Figure 9c,d it can be observed that the evolution of photocatalytic degradation in time fits on a pseudo-first-order kinetics (the values of the correlation coefficient R 2 are between 0.9950 and 0.9995) and it is strong depending on the values of the initial concentration of the organic substrate. The apparent rate constant corresponding to the lowest initial organic carbon content is about 3.2 times higher than that corresponding to the highest initial organic carbon content.

Influence of pH of the Working Solution
The pH of the aqueous solution containing the organic substrate to be degraded has an important effect on the degradation efficiency, both by modifying the activity of the TiO2 photocatalyst and by favoring the hydroxyl radical formation reactions. It is considered that the pH value influences the position of the transition band between the conduction band and the valence band of TiO2 which determines its amphoteric character. It has been determined that around a pH of 7, the catalyst surface is electrically neutral. Below and above this value, the surface of the TiO2 photocatalyst is charged positively and negatively according to the following equilibria [21]: TiOH ⇄ TiO + H Chlorophenols and their intermediates formed during the photocatalytic degradation process are electronegatively charged compounds or are electrically neutral. This results in better adsorption of organic molecules on the catalyst surface and higher degradation efficiencies at acidic pH values of the solution. The overall photocatalytic reaction can be described by a reaction of the following form [31]: The equilibrium constant (Ke) for the above reaction has the following form: Considering the ionic product of water: Equation (23) can be written as follows: From the relation presented above, it is observed that between the concentration of hydrogen ions [H + ] and the concentration of hydroxyl radicals [·OH] there is a direct

Influence of pH of the Working Solution
The pH of the aqueous solution containing the organic substrate to be degraded has an important effect on the degradation efficiency, both by modifying the activity of the TiO 2 photocatalyst and by favoring the hydroxyl radical formation reactions. It is considered that the pH value influences the position of the transition band between the conduction band and the valence band of TiO 2 which determines its amphoteric character. It has been determined that around a pH of 7, the catalyst surface is electrically neutral. Below and above this value, the surface of the TiO 2 photocatalyst is charged positively and negatively according to the following equilibria [21]: TiOH Chlorophenols and their intermediates formed during the photocatalytic degradation process are electronegatively charged compounds or are electrically neutral. This results in better adsorption of organic molecules on the catalyst surface and higher degradation efficiencies at acidic pH values of the solution. The overall photocatalytic reaction can be described by a reaction of the following form [31]: The equilibrium constant (K e ) for the above reaction has the following form: Considering the ionic product of water: Equation (23) can be written as follows: From the relation presented above, it is observed that between the concentration of hydrogen ions [H + ] and the concentration of hydroxyl radicals [·OH] there is a direct dependence. Thus, the more acidic the conditions under which the experiment takes place, the more hydroxyl radicals are produced that will degrade the organic substrate faster. This can be highlighted by comparing the kinetic parameters obtained for various pH values of the working solution. However, at pH less than 3, the efficiency of the process decreases due to the protonation effect of hydrogen peroxide with the formation of the oxonium ion (H 3 O 2 + ), which prevents the decomposition of H 2 O 2 and thus the formation of ·OH radicals.
The aspects presented above are the basis for the identification of the mechanisms of photocatalytic degradation of 2,4-dichlorophenol. At least two of them could be confirmed by the results obtained in this work. The first one involves the formation of nascent hydrogen (·H) from protons (H + ) adsorbed on the surface of the photocatalyst, which can successively displace chlorine from the benzene ring. Subsequently, the formed phenols can be attacked by hydroxyl radicals (·OH) which can open the benzene ring with the formation of aliphatic compounds. The second one involves a direct attack of the hydroxyl radicals which would lead to the displacement of chlorine from the para position with the formation of 2-chloro-4-hydroxyphenol. Next, there may be a successive attack of the hydroxyl radicals until the benzene ring is open, or there may be a first attack of the nascent hydrogen on the chlorine from the ortho position with the formation of hydroxyquinone followed by the successive attack of hydroxyl radicals until the opening of the benzene ring [9,32]. However, it appears that both degradation mechanisms are strongly influenced by the pH of the aqueous solution, and therefore these are in good agreement with the results found in this work.

Influence of Hydrogen Peroxide/Organic Carbon Molar Ratio
It is known that the addition of H 2 O 2 leads to an improvement in the rate of oxidation of organic compounds due to the formation on the surface of the TiO 2 photocatalyst of HO· radicals, according to the following reaction.
TiO 2 e − + H 2 O 2 −→ TiO 2 + OH − + ·OH (26) The rate of degradation of the organic compound increases with increasing concentration of H 2 O 2 due to the generation of an increasing number of HO· radicals, the reaction being favored by an acidic pH of the working solution. It has been found that this direct dependence is only valid up to a certain concentration of H 2 O 2 , after which the reaction rate begins to decrease. This decrease is due to side reactions that occur at the surface of the TiO 2 catalyst, such as the following [33].
Given that there is a high concentration of H 2 O 2 in the system, it will participate in a competition with the organic compound in the reaction with HO· radicals, according to the reaction (28). To avoid these side reactions, the addition of H 2 O 2 must be optimized to obtain the maximum rate of degradation of the organic compound. The optimum H 2 O 2 concentration depends on the nature and concentration of the organic compound to be degraded. Resulting from the data obtained in this work, a stoichiometric hydrogen peroxide/organic carbon molar ratio is favorable for the degradation of the initial organic compound, namely 2,4-DCF.

Influence of Initial Concentration of the Organic Carbon
There is an inversely proportional dependence between the initial concentration of organic substrate and the degradation rate. Thus, the higher the initial concentration of organic carbon, the lower the overall degradation rate. This is due to the increasingly intense adsorption of organic substrate molecules on the surface of the photocatalyst as its concentration increases, while the number of hydroxyl radicals formed at constant radiation and constant irradiation time remains constant. Decreasing the ratio between the concentration of the substrate and the concentration of hydroxyl radicals in the solution subjected to irradiation leads to a decrease in the degradation efficiency of the substrate [25]. In the case of this work, this effect is even more visible because the specific surface of the photocatalyst deposited on titanium support is much smaller than if it had been dispersed in the volume of liquid.

Conclusions
The results obtained in this paper highlight the importance of operating parameters on the efficiency of removing 2,4-dichlorophenol from aqueous solutions by photocatalytic oxidation in an UV photocatalytic reactor equipped with a TiO 2 /stainless-steel photocatalytic membrane. In this respect, it was demonstrated that the photocatalytic degradation rate increases in acidic conditions with a maximum corresponding to pH 3, which leads to an increase in the removal efficiency of 2,4-dichlorophenol. A stoichiometric molar ratio of hydrogen peroxide/organic substrate is favorable for the photocatalytic degradation of 2,4-dichlorofenol. Decreasing or increasing it above the stoichiometric value leads to a significant decrease in the efficiency of photocatalytic degradation of the organic substrate. The rate of photocatalytic degradation decreases with the increasing of initial concentration of 2,4-dichlorophenol. The results obtained showed that there is an inversely proportional dependence between the initial concentration of the organic substrate and the photocatalytic degradation rate.