Simultaneous Measurement of Refractive Index and Flow Rate Using a Co 2+ -Doped Microﬁber

: This paper has proposed and experimentally demonstrated an integrated Co 2+ -doped microﬁber Bragg grating sensor (Co-MFBGS) that can measure the surrounding liquid refractive index (LRI) and liquid ﬂow rate (LFR) simultaneously. The Co-MFBGS provides well-deﬁned resonant modes of core and cladding in the reﬂection spectrum. By monitoring the wavelength of the cladding mode, the LRI can be measured; meanwhile, by monitoring the wavelength of the core mode caused by the heat exchange, the LFR can be measured. The LRI and LFR can be distinguished by the wavelength separation between cladding mode and core mode. The experimental results show that in aqueous glycerin solution, the maximum measurement sensitivity for LRI detection is − 7.85 nm/RIU (refractive index unit), and the LFR sensitivity is − 1.93 nm/( µ L/s) at a ﬂow rate of 0.21 µ L/s.

The liquid flow rate (LFR) measurement is also a paramount index for many applications, such as medical and biological analysis [20]. In the application of optical fiber biosensors, due to the herringbone microfluidic chip's capture efficiency being highly dependent on the flow rate, its accuracy and efficiency can be significantly improved by the measurement of flow rate [21,22].
"Hot-wire" is the most famous microfiber flowmeter [23][24][25]. For many applications, not only is the LFR needed, but also other parameters, such as LRI and temperature [19]. Sometimes simultaneous measurements may be necessary, and the measurement parameters should not be cross-impacted.
In this paper, based on the Co 2+ -doped microfiber Bragg grating sensor (Co-MFBGS), an integrated LRI and LFR sensing sensor has been presented and experimentally demon-strated, which can measure both parameters simultaneously. The Co-MFBGS reflection spectrum provides a well-defined core mode resonance as well as two cladding mode resonances; the wavelength shifts of two kinds of resonances have quadratic non-linear relationship to LRI and LFR. The temperature cross-impact to the LRI measurement can be eliminated by monitoring the wavelength interval change between the core mode and cladding mode. Additionally, due to the non-radiation effect of Co 2+ -doped fiber, the Co-MFBGS can be heated by a pump laser; by interrogating the core mode's wavelength shift caused by the heat exchange effect, the LFR can be measured. The proposed integrated optical fiber sensor has potential value in chemical, medical and environmental applications.

Fabrication of the Co-MFBGS
In the proposed Co-MFBGS, the sensing device is a section of Co 2+ -doped optical fiber (CDOF) with 8.4/125 µm core diameter and cladding diameter, and the length is 20 mm. At a laser wavelength of 1480 nm, the section of CDOF absorption coefficient is approximately equal to 31.3 dB/m. The CDOF with a length of 20 mm was spliced to two sections of 1m length single-mode optical fibers, one at each end.
The fabrication of the proposed Co-MFBGS has two steps. First, an FBG with a length of 15 mm was written in the section of CDOF using a KrF excimer laser (248 nm) with a phase mask. Second, the CDOF with an FBG was immersed into a 20% aqueous hydrofluoric acid solution for 105 min, then removed and rinsed with ultrapure water to clean off the acid solution. Thus, a Co-MFBGS with a diameter of 16.7 µm (Figure 1a) was fabricated. With the same process, a Co-MFBGS with a diameter of 6.4 µm (Figure 1b) was also fabricated. linear relationship to LRI and LFR. The temperature cross-impact to th can be eliminated by monitoring the wavelength interval change betw and cladding mode. Additionally, due to the non-radiation effect of C Co-MFBGS can be heated by a pump laser; by interrogating the core shift caused by the heat exchange effect, the LFR can be measu integrated optical fiber sensor has potential value in chemical, medical applications.

Fabrication of the Co-MFBGS
In the proposed Co-MFBGS, the sensing device is a section of Co 2+ (CDOF) with 8.4/125 μm core diameter and cladding diameter, and t At a laser wavelength of 1480 nm, the section of CDOF absor approximately equal to 31.3 dB/m. The CDOF with a length of 20 mm sections of 1m length single-mode optical fibers, one at each end.
The fabrication of the proposed Co-MFBGS has two steps. First, a of 15 mm was written in the section of CDOF using a KrF excimer la phase mask. Second, the CDOF with an FBG was immersed in hydrofluoric acid solution for 105 min, then removed and rinsed with clean off the acid solution. Thus, a Co-MFBGS with a diameter of 16.7 fabricated. With the same process, a Co-MFBGS with a diameter of 6.4 also fabricated. The reflection spectra of the Co-MFBGS with diameters of 16. investigated, as shown in Figure 1c. It is clear that the Co-MFBGS wit μm has a core mode and two cladding modes, but the Co-MFBGS wit has only a core mode, the wavelength range from 1525 to 1565 nm. A μm Co-MFBGS was selected as the test sensor for the rest of the expe in Figure 1c, the wavelength separation of λa (core mode) and λb (cla The reflection spectra of the Co-MFBGS with diameters of 16.7 and 6.4 µm were investigated, as shown in Figure 1c. It is clear that the Co-MFBGS with a diameter of 16.7 µm has a core mode and two cladding modes, but the Co-MFBGS with a 6.4 µm diameter has only a core mode, the wavelength range from 1525 to 1565 nm. Accordingly, the 16.7 µm Co-MFBGS was selected as the test sensor for the rest of the experiments. As shown in Figure 1c, the wavelength separation of λ a (core mode) and λ b (cladding mode) is 7.1 nm. The spectral characteristics of the Co-MFBGS were analyzed by using the numerical mode simulation software COMSOL, and the reflection spectrum compositions of the core mode and one cladding mode, and amplitude distributions of the transverse electric field, are as shown in the bottom of Figure 1. This indicates that on the Co-MFBGS surface, the evanescent field of the cladding mode is stronger than that of the core mode.

Principle of the Proposed Sensor
It is well known that the FBG center wavelength λ B and the resonant wavelength λ cl,k of the kth cladding mode can be shown as [18,26] where n eff,co and n eff,cl,k are the effective index of the core mode and the kth cladding mode in the Co-MFBGS, respectively; Λ is the Bragg grating period. As the core mode was confined in the core of the Co-MFBGS, it was insensitive to the surrounding LRI. Meanwhile, the cladding modes of the Co-MFBGS due to the evanescent field are very sensitive to the LRI. So, the Co-MFBGS can be used for LRI sensing, and from Equation (2) the wavelength drift of the cladding mode caused by LRI change is rewritten as where ∆n eff,cl,k (RI) is the kth cladding mode LRI change.
The wavelength interval λ int is defined as It is the wavelength difference between core mode and kth cladding mode. Combining Equations (3) and (4), the wavelength interval shift ∆λ int (RI) caused by the change of LRI can be written as ∆λ int (RI) = ∆λ cl,k (RI) = ∆n e f f ,cl,k (RI)·Λ (5) The wavelength drift of FBG caused by temperature change is well known as [27] ∆λ B (T) = 2n e f f ,co ·Λ( 1 n e f f ,co dn e f f ,co dT where ∆λ B (T) and ∆λ cl,k (T) are the wavelength changes of the core mode and k th cladding Cobalt is a kind of light absorption material and is easy to get, and the CDOF can be heated by the pump laser as a result of the non-radiation effect; meanwhile, the temperature of the Co-MFBGS increases and the wavelengths of the core mode and cladding modes have a redshift. When the Co-MFBGS was used as an LFR sensor, parts of the sensor heat can be carried away by the fluidic sample [28], which would lead to a decrease in the sensor's temperature and a blue shift in the wavelengths of the core mode and cladding modes. So, the LFR can be measured by detecting the wavelength shift of the Co-MFBGS.
Depending on the theory of hot-wire, the relationship between the LFR of the fluidic sample and heat loss is shown as [29] Q = ∆T(A + Bν i ) (8) where Q is the power absorbed by the CDOF, ν is the LFR, and A, B and i are empirical coefficients. So, Equations (6) and (7) can be rewritten as Additionally, the wavelength interval shift ∆λ int (T) caused by the change of temperature can be deduced as As the difference of α and γ is very small (<0.00324 K −1 ) [20], Equation (11) can be rewritten as According to Reference [20], when the LFR changes from 0 to 1 µL/s, ∆λ int (T) is quite small (~0.017 nm)-that is, the wavelength interval shift caused by the effect of LFR can almost be neglected. Consequently, the LRI and LFR can be measured simultaneously using the cladding mode wavelength and core mode wavelength of the Co-MFBGS, respectively, and the crosstalk can be distinguished using the wavelength interval shift.

Experimental Setup
As shown in Figure 2, the experimental setup includes an amplified spontaneous emission (ASE) laser (wavelength: 1525-1565 nm, output power: 20 mW) and a tunable pump laser (1480 nm), and both the lasers are launched into the Co-MFBGS from the opposite ends. The reflective spectrum of the Co-MFBGS was interrogated by an optical spectrum analyzer (OSA, YOKOGAWA AQ6370D). At the beginning of the experiments of LRI and LFR measurement, a specially designed PDMS-based microfluidic channel was used to place the proposed Co-MFBGS, in order to impart a slight pre-stretch; then, in order to avoid the effects of other forces, a UV-sensitive adhesive was used to fix the two ends of the Co-MFBGS fiber, as shown in Figure 2. During the experiments of LRI and LFR measurement, aqueous glycerin solutions were injected into the microfluidic channel via a pressure controller whose pressure stability is as high as 10 µbar.
The temperature characteristics of the Co-MFBGS were tested first by putting the
The temperature characteristics of the Co-MFBGS were tested first by putting the sensor into a chamber whose temperature could be adjusted in the range of 20-140 • C in steps of 10 • C and a resolution of 0.1 • C. The temperature experimental result of the wavelength interval (λ a-b ) change between λ a and λ b of the Co-MFBGS is shown in Figure 3a, which is clearly showing that λ a-b is almost free from temperature perturbations. So, the temperature cross-sensitivity of LRI measurements can be neglected. Before beginning the LFR measurement experiment, the Co-M using pumped laser powers of 250, 350 and 450 mW at a waveleng Co-MFBGS can be heated by pump laser due to the light absorptio shows the wavelength shift of the core mode (λa) at different pumpe clearly shows that λa has a redshift while increasing pumped sensitivity increases significantly with increasing heating pow temperature of Co-MFBGS is increased, so, when the Co-MFBGS is the heat of Co-MFBGS will be carried away by the flowing liquid, t MFBGS will be decreased, and λa will has a blueshift.
During the LFR measurement experiment of the proposed Covaried in 0-0.98 μL/s by using a commercial electronic-controlled s an aqueous glycerin solution with a constant concentration into the meanwhile, the pumped laser power was set to 450 mW. A PZT flo The LRI measurement experiment of the Co-MFBGS was conducted at room temperature (25 • C). In each measurement, the aqueous glycerin solutions, with concentrations whose RI changed from 1.32 to 1.44 RIU in steps of 0.02 RIU, were injected into the microfluidic channel. After the aqueous glycerin solution had flowed to surround the entire Co-MFBGS, the reflection spectrum was interrogated several times by the OSA until almost no change was observed, and then the spectrum was recorded, so the reliable measuring values can be obtained.
The experimental results of the proposed Co-MFBGS wavelength shift with different LRIs are shown in Figure 3b-d. Figure 3b-d shows the value change of λ a , λ b and λ a-b with different LRIs, respectively. It is clear that the core mode wavelength of the proposed Co-MFBGS does not shift, which means it is insensitive to the LRI. Meanwhile, the cladding mode is exceedingly sensitive to the LRI; its wavelength shift decreases by 0.69 nm with the LRI changes from 1.32 to 1.44 RIU. So, the value change of λ a-b is almost the same with the value change of λ b , and it can be fit to a quadratic non-linear equation with LRI change (1.32-1.44 RIU). The equation indicates that the maximum LRI sensitivity of the proposed Co-MFBGS wavelength interval is about −7.85 nm/RIU, Figure 3d.
Before beginning the LFR measurement experiment, the Co-MFBGS was heated by using pumped laser powers of 250, 350 and 450 mW at a wavelength of 1480 nm, as the Co-MFBGS can be heated by pump laser due to the light absorption of cobalt. Figure 4f shows the wavelength shift of the core mode (λ a ) at different pumped laser powers, which clearly shows that λ a has a redshift while increasing pumped laser power, and the sensitivity increases significantly with increasing heating power. That means the temperature of Co-MFBGS is increased, so, when the Co-MFBGS is used for LFR sensing, the heat of Co-MFBGS will be carried away by the flowing liquid, the temperature of Co-MFBGS will be decreased, and λ a will has a blueshift.
l. Sci. 2021, 11, x FOR PEER REVIEW With increasing LFR, both λa and λb experience a blueshift temperature of the Co-MFBGS; reflection spectra corresponding to d shown in Figure 4a. Figure 4b shows the value change of λb and rates; it can be seen that their wavelengths shift to shorter wavele but in Figure 4c it is shown that λa-b exhibited almost no change. Th the LRI can be discriminated by wavelength interval. Figure 4b als quadratic non-linear relationship between the value change of λa an During the LFR measurement experiment of the proposed Co-MFBGS, the LFR was varied in 0-0.98 µL/s by using a commercial electronic-controlled syringe pump to inject an aqueous glycerin solution with a constant concentration into the microfluidic channel; meanwhile, the pumped laser power was set to 450 mW. A PZT flow sensor was used to calibrate the LFR. The experimental results are shown in Figure 4.
With increasing LFR, both λ a and λ b experience a blueshift due to the decreasing temperature of the Co-MFBGS; reflection spectra corresponding to different flow rates are shown in Figure 4a. Figure 4b shows the value change of λ b and λ a with different flow rates; it can be seen that their wavelengths shift to shorter wavelengths simultaneously, but in Figure 4c it is shown that λ a-b exhibited almost no change. That means the LFR and the LRI can be discriminated by wavelength interval. Figure 4b also shows that there is a quadratic non-linear relationship between the value change of λ a and the LFR; a flow rate of 0.21 µL/s can lead to a sensitivity of −1.93 nm/(µL/s). From Figure 4e, it can be seen that it takes about 10 s for the reading to stabilize when the LFR increases from 0 to 0.39 µL/s; therefore, the response time of the LFR measurement of the proposed Co-MFBGS is 10 s.

Conclusions
This paper has presented an integrated Co-MFBGS, which can measure the LRI and LFR simultaneously. A single straight Bragg grating was written in a section of Co 2+ -doped fiber and then immersed into aqueous hydrofluoric acid solution to fabricate a Co-MFBGS with a diameter of 16.7 µm. The Co-MFBGS of the proposed sensor provides well-defined resonances in reflection; by detecting the wavelength of the cladding mode and core mode, the LRI and LFR can be measured, respectively, and they can be distinguished by the change of wavelength separation between cladding mode and core mode, and the temperature cross-impact of LRI measurements is also eliminated. The experimental results show that in aqueous glycerin solution the maximum measurement sensitivity for LRI detection is −7.85 nm/RIU, and the LFR sensitivity is −1.93 nm/(µL/s) at a flow rate 0.21 µL/s. The proposed Co-MFBGS can potentially be used in bioengineering, medicine, environmental protection, etc.