A Practice for the Application of Waste in Road Asphalt Pavements in an Eco-Friendly Way

: The integration of circular economy principles in the design of road pavements raises the problem of obtaining high-performance asphalt mixtures for reduction of waste and environmental pollution compared to traditional solutions. In this study, the base and binder layers of road asphalt pavements were prepared by using reclaimed asphalt pavement and construction and demolition waste as coarse aggregates, while jet grouting waste and ﬂy ash served as ﬁllers. A leaching test was performed for the marginal materials, after which the engineering performances of the designed asphalt mixtures were investigated through laboratory tests. A life cycle assessment methodology was applied to determine the life cycle impacts of one cubic meter of each asphalt solution. Next, a multi-criteria decision analysis (MCDA) was performed for the solutions suggested for the binder and base layers. Finally, a sensitivity analysis was conducted to identify the most suitable MCDA solutions by varying the weights for a total of 24 different weight conﬁgurations. The results of this work revealed that the solutions utilizing jet grouting waste (in particular, the hot asphalt mixture for the binder layer and cold asphalt mixture for the base layer) were preferred to other traditional and alternative solutions in most decision-making scenarios.


Introduction
One of the seventeen objectives of the 2030 Agenda for Sustainable Development refers to grow quality, reliable, sustainable and resilient infrastructure, strengthening economic development and social well-being [1].
Some of these materials are usually used as bitumen modifiers, whose beneficial performance effects are highlighted in comparison with traditional bitumen and commercial modified bitumen [25,26].
For example, Ren et al. [27] adopted the lignin, the major waste from biofuel and paper industries, as a modifier to enhance the performance of 70/100 penetration grade bitumen. Three different dosages of lignin of 10, 20 and 30% by the weight of binder were analysed. The results showed that the lignin enhances the complex modulus and rutting factor of bitumen; in fact, for a lignin dosage of 30%, the recovery percentage resulted to be contribution of CO 2 , CH 4 and N 2 O gases to the warming of Earth's climate due to human activities. The obtained results showed that the CC indicator of the CIRM solution was 81% lower than that of HMA.
Other research works focused on developing a methodology that could identify the best alternative treatment by performing a multi-criteria decision analysis (MCDA) [57,58]. This strategy has been widely adopted to (a) determine the most suitable technology for reusing RAP in central plant hot recycling, hot in-place recycling, central plant cold recycling and cold in-place recycling applications [59]; (b) compare various asphalt mixtures based on their engineering performance and life cycle cost indicators [60], cost, environmental and social indicators of the life cycle [61] or engineering performance and service life [62].
On the basis of the above, a new methodological tool was developed in this study for the selection of the most appropriate asphalt mixture solution containing waste materials in substitution of natural aggregates. The sensitivity analysis based on the results of a multicriteria decision analysis has been performed with the aim to bring together the goals of maximizing asphalt materials' engineering performance and minimizing both the use of natural resources and the overall environmental impacts of the life cycle evaluated through LCA methodology.
A total of four marginal materials were investigated and reused, such as CDW (waste produced during construction and demolition of houses, building or other structures, made up of concrete, bricks, gypsum and other debris), RAP, JGW (waste produced during soil consolidation works) and fly ashes (FA).
A summary of the research phases is reported in Figure 1.

Materials
In this study, for the preparation of asphalt mixtures, four marginal materials were employed replacing both natural aggregates and fillers. The wastes were as follows: • Jet grouting waste (JGW) obtained from the consolidation works of an underground highway tunnel; • Construction and demolition waste (CDW) derived from the demolition of buildings; • Reclaimed asphalt pavement (RAP) originated from the milling of deteriorated asphalt pavements; • Fly ashes (FA) generated by the coal combustion process to produce electricity; JGW and CDW required a grinding process of 120 min (after that, no variation in the grading curve arose) to obtain their final size, during which the materials were examined every 30 min. On the contrary, FA and RAP were adopted as replacement of filler and coarse aggregates, respectively, without a grinding transformation.
The environmental compatibility of the four waste materials was assessed by the leaching test in compliance with the EN 12457-2 standard [63] (see Figure S1 in Supplementary Materials). The results of the analysis, as shown in Table S1a in Supplementary Materials, demonstrated the environmental applicability of the four wastes (JGW, CDW, RAP and FA) since the concentration of the pollutant resulted lower than the limits set by the Italian Ministerial Decree of 5 February 1998 [64].
The physical properties in terms of equivalent sand and Rigden voids and the mechanical properties expressed in terms of Los Angeles value of the limestone aggregates and waste materials are reported in Table S1b. The results of these properties allowed to made observations regarding the collocation of the waste into road pavement stratigraphy. Since the RAP exhibited poor Los Angeles value that represents the abrasion resistance of the aggregate, it was decided to use it into the base layer; on the contrary CDW was reemployed for making the binder course. In the case of JGW and FA, their mechanical properties allowed to re-use them in both binder and base layer.
A total of nine asphalt mixtures were designed comprising the four wastes mentioned whose grading curve followed the requirements of the EN 13108-1 standard [65].
Three different binders were adopted; in detail, a 50/70 penetration grade bitumen was used for making hot asphalt mixtures while for the cold one, a cationic bitumen emulsion and a Portland cement 325R were used.
The mechanical investigation of the four asphalt mixtures (see Figure S2 in Supplementary Materials) were evaluated by investigating the engineering performance reported in Table 1 in compliance with the EN standards. The optimum bitumen content (OBC) was identified in correspondence to the maximum S value [65] (see Tables 2-4) for the hot asphalt mixtures of the binder (see Table 2a) and base (see Table 2b) layer, while for the cold asphalt mixtures, designed only for the base layer (see Table 2b), the optimum solution was identified by considering those with the specific gravity and ITS value, assessed at the 28th curing day [72], close to those of HMA base (see Table 4). Therefore, the optimum cement, water and bituminous emulsion content were 1.5, 5 and 3.75% by the weight of the grading curve for CMRA RAP solution, respectively, and 0.5, 5 and 5% for CMRA RAPJGW , respectively.

LCA of Asphalt Road Pavement Mixtures
LCA methodology [73] was employed (using a commercial licensed software for LCA assessments [74]) to assess the environmental impacts of the nine asphalt road pavement mixtures during their life cycles. In this process, one cubic meter of each solution (functional unit) was examined. The LCA procedure consisted of two main parts: life cycle inventory (LCI) and life cycle impact assessment (LCIA).
For the designed binder course and base layer mixtures, LCI was performed to investigate the input flows of different components (including the raw materials used for the construction/maintenance of facilities and machinery) as well as water and fossil fuels, and the output flows of pollutants emitted into the air (CO 2 , CO, CH 4 , NO x , SO 2 , non-methane volatile organic compounds (NMVOCs) and particulate matter) and water (chemical oxygen demand (COD), biological oxygen demand (BOD), nitrogen, sulphur and phosphorus compounds).
Let M be a set of the analysed functional units with M = {1, . . . p, . . . o}, o = 9 (the total number of asphalt mixtures). In this case, LCI is evaluated using Equation (1) for each functional unit.
where: • p belongs to the range [1; 9] and represents the asphalt mixture solutions.
After that, the LCIA procedure was performed using ReCiPe methodology [75] which converts the 19 flows of the specified components into 18 midpoint category indicators, where the flow of each component can affect one or more impact categories: global warming (GWP); stratospheric ozone depletion (ODP); ionizing radiation (IR); the negative effects of ozone formation on terrestrial ecosystems (OFT) and human health (OFH); fine particulate matter formation (PM); terrestrial acidification (A); freshwater eutrophication (FE); marine eutrophication (ME); terrestrial, freshwater and marine ecotoxicities (T-ECO, F-ECO and M-ECO); human carcinogenic and non-carcinogenic toxicities (CT and NCT); land use (LU); mineral and fossil resource scarcity (MR and FR); and water consumption (W).
The component flows were converted into the impact category indicators using different characterization (weighing) factors to aggregate heterogeneous inventory flows (e.g., CO 2 , CO and CH 4 ) into homogeneous impact category indicators (e.g., GWP) expressed by specific measurement units (e.g., kg CO 2 equivalent for GWP) and determine the cumulative effect of different components on the environment. Therefore, each impact assessment matrix IC p of the p-th asphalt solution was calculated from the inventory matrix F p according to Equation (2).
where CF is the matrix of the characterization factors whose generic entry cf t,r converts the r-th component of each process of the inventory matrix into the t-th impact category indicator of the impact assessment matrix.
Finally, the impact assessment matrixes of the nine asphalt mixtures were combined into a single txp global impact assessment matrix IC, whose generic entry ic t,p for MCDA is expressed by Equation (3).
where ic t,p is the indicator of the t-th impact category for the p-th asphalt mixture, which is obtained by summing up the t-th impact indicators of each of the v mentioned macroprocesses of the life cycle (namely, each row of the impact assessment matrix ICp).

MCDA Procedure
As mentioned above, the four asphalt solutions prepared for the binder course and five asphalt solutions prepared for the base layer were compared using 18 environmental and 9 engineering performance indicators (see Tables 2 and 3 By calculating all indicators for each asphalt mixture, two distinct decision matrixes A 1 and A 2 were obtained, as shown in Equation (4) and Tables 2 and 3 (see also the flow diagram depicted in Figure 2).
The generic entry a 1,ij of A 1 represents the value of the i-th indicator related to the j-th asphalt mixture for the binder layer, while a 2,ik is the value of i-th indicator related to the k-th asphalt mixture for the base layer matrix (A 2 ).
Afterwards, the decision matrixes (A 1 and A 2 ) were normalized according to Equations (5) and (6) depending on the indicator type to obtain the normalized decision matrixes N 1 and N 2 , respectively (see Table S2 and Equation (7)). Specifically, Equation (5) was used to normalize the S, MS, ITSM, ITS, ITSR and N f indicators (here, 0 represents the worst performance, and 1 denotes the best performance), while Equation (6) was used for RD and all indicators from the environmental impact category (in this case, 0 and 1 have the opposite meanings). where: • n 1,ij and n 2,ik are the normalized i-th indicators belonging to the range [1; 27] of the j-th binder solution and k-th base solution, respectively (j belongs to [1; 5], and k belongs to [1; 4]); • maxa 1,i and mina 1,i are the maximum and minimum values of the i-th indicator, respectively, among all solutions suggested for the binder course; • maxa 2,i and mina 2,i are the maximum and minimum values of the i-th indicator, respectively, among all solutions suggested for the base layer.
Workflow diagrams describing the MCDA and sensitivity analysis procedures.

ELECTRE I Application
All the utilized 27 indicators were categorized into four groups (four for the solutions suggested for the base layer and four for the solutions belonging to the binder layer) as follows: • Environmental and human health performance of the asphalt mixtures (EHP) that involves 18 indicators from the midpoint impact LCA category described in Section 2.2.
The weight vector was determined by assigning equal weights to the four groups of indicators, namely, HP (25%), LP (25%), EHP (25%) and MP (25%). The weight assigned to each group was equally divided among all indicators in this group.
ELECTRE I represented an MCDA method, which considered the interactions between different pairs of alternatives. To compare all such pairs, a concordance index (c 1,jj for the binder layer, and c 2,kk for the base layer) and a discordance index (d 1,jj for the binder layer, and d 2,kk for the base layer) were determined. In particular, the concordance and discordance indexes were calculated for each pair (j-th; j'-th) of alternatives for the binder layer by Equations (8) and (9), respectively. where: • c 1,jj is the concordance index of the (j-th; j'-th) pair of alternatives of the binder layer with j and j' belonging to the range [1; 5]; • n * 1,ij and n * 1,ij are the normalized i-th indicators belonging to the range [1; 27], which are calculated via Equations (6) and (7), respectively, for the j-th and j'-th binder solutions with n * 1,ij > n * 1,ij ; • w * i is the weight of the i-th indicator with n * 1,ij > n * 1,ij where: • d 1,jj is the discordance index of the (j-th; j'-th) pair of alternatives for the binder layer with j and j' belonging to the range [1; 5]; • n * 1,ij and n * 1,ij are the normalized i-th indicators belonging to the range [1; 27], which are calculated via Equations (5) and (6), respectively, for the j-th and j'-th binder layer solutions with n * 1,ij < n * 1,ij . Note that the same concordance and discordance indices were also computed for each pairwise comparison between the k-th and k'-th alternatives of the base layer solutions with k and k' belonging to the range [1; 4] to obtain the c 2,kk and d 2,kk values.
The concordance and discordance thresholds were initially set to the mean values of all concordance and discordance indices assessed for each layer, respectively. As a result, c * 1 and d * 1 were obtained for the binder layer and c * 2 and d * 2 for the base layer, and alternative j was preferred to alternative j' if c jj > c * 1 and d jj ≤ d * 1 for the binder layer and c kk > c * 2 and d kk ≤ d * 2 for the base layer. If more than one asphalt mixture satisfied the conditions specified above, the concordance threshold was progressively lowered, and the discordance threshold increased until only one optimal solution was obtained.
The next steps involved the sensitivity analysis that played an important role in verifying the MCDA results. In total, 24 different weight configurations were applied to the decision matrices of the binder and base layer in addition to that used for ELECTRE I methodology. Specifically, relative weights of 0, 20, 40, 60, 80 and 100% were assigned to each of the four groups of indicators (HP, LP, MP and EHP), and the remaining weights (100, 80, 60, 40, 20 and 0%, respectively) were divided equally among the other groups. Inside each group, the assigned weight was divided equally among all indicators (see Figure 2). Table S3 lists the 24 weight configurations applied.
Therefore, MCDA was conducted for each of the 24 weight configurations, and the most suitable alternative was selected for the binder and base layers. Subsequently, the frequency of occurrence of the best alternatives was calculated according to ELECTRE I methodology and compared with the value obtained without the sensitivity analysis.

Mechanical Performance
The obtained results (see Table 3) show that the asphalt mixtures prepared for the binder layer exhibit better mechanical performance than that of the traditional HMA solutions. In particular, the mechanical properties of HMA binderJGW are superior to those of HMA binder (S (+144%), MS (+86%), ITS (+23%), ITSR (+10%), ITSM (+23% on average), RD (−7%) and N f (+80%)) and the remaining solutions (average 26% improvement of all engineering performance characteristics as compared with those of HMA binderCDW and HMA binderFA ). Similar results in terms of fracture resistance were found by Fakhri an Ahmadi [76] using a different waste material, namely the steel slag aggregates, added in similar percentage to the asphalt mixture.
For the base layer, the CMRAs exhibited lower RD values than that of the traditional HMA base . In addition, the other engineering performance indicators were significantly improved after JGW addition (CMRA RAPJGW ), leading to higher MS, ITS and ITSM (+27%, +10% and +68%, respectively) as compared with HMA base . These results are easily comparable with those obtained by Gómez-Meijide et al. [77], who used CDW in substitution of natural aggregates; they found that the asphalt mixture with CDW had a significantly lower permanent deformation than that of the traditional one.

Natural Aggregate, Sand and Filler Production
Considering the amounts of the coarse aggregates and sand required for preparing the asphalt mixtures solutions (Table 1), the highest savings were obtained by increasing the marginal material contents as follows: HMA binderCDW saved 7.8 kgCO 2 /m 3 compared to HMA binder , while CMRA RAP and CMRA RAPJGW saved 13.7 and 14.9 kgCO 2 /m 3 compared to HMA base , respectively.

Recycled Aggregate Supplies
JGW, FA, CDW and RAP were added to the binder and base layers in a functional unit (1 m 3 ) of the studied asphalt mixtures (Table 1). First, JGW was produced at the construction site; therefore, it was milled by a mobile ball mill (CMRA RAPJGW solution) or directly transported to the asphalt plant located 20 km away followed by milling (HMA binderJGW and HMA baseJGW solutions). Meanwhile, CDW was supplied to the asphalt plant from a distance of 20 km and then milled to a desired aggregate size. FA was stored in a dedicated local plant and then transported to the asphalt plant located 100 km away without size reduction actions. RAP was produced by milling the existing asphalt pavement at the construction site without any crushing actions.
Notably, all the waste-containing asphalt mixtures exhibited lower CO 2 emissions than those of the traditional mixtures by 7% on average. This advantage was maximized for the cold mixtures, among which CMRA RAP decreased the CO 2 emissions by 10% as compared with that of HMA base , and CMRA RAPJGW demonstrated a further 13% CO 2 emission reduction with respect to that of CMRA RAP .

Binder Production
For the asphalt binder production (see Figure S3i for the hot asphalt mixtures and Figure S3i for the cold recycled mixtures), the required parameters were obtained from Eurobitume [78] by considering the binder contents determined in the previous sections (Table 1); the Ecoinvent database [79] was used for the Portland cement production and transportation, while the transportation distances were known in this study. Note that the cement was purchased by the asphalt producer and then transported to the construction site for the cold in-place recycling at a distance of 20 km.
Considering the production of bitumen, bitumen emulsion and cement, CMRA RAP lowered the overall CO 2 emissions by 16% with respect to that of HMA base , while CMRA RAPJGW with a 1% lower optimum cement content accounted for the further 15% reduction of CO 2 emissions.

Production, Laying and Compaction of Asphalt Mixtures
The section describes the inventory flows of 1 m 3 of the produced, laid and compacted road asphalt pavement mixtures.
Different processes were considered for the hot asphalt mixtures and cold in-place recycled asphalt mixtures, as described below: During the hot in-plant production (see Figure S3i), the input and output flows of all HMA solutions were assumed to be the same. The unit processes included the following operations and parameters mainly provided by local contractors: (a) the transportation of coarse aggregates and sand from stockpiles to the mixing equipment using a wheel loader with a productivity of 60 m 3 /h powered by diesel fuel; (b) the natural gas consumption for drying aggregates in the drum dryer of the production plant was equal to 8.79 m 3 /t; (c) the electricity consumption during the bitumen storage at 180 • C and mixing the aggregates, fillers and bitumen was equal to 4.37 kWh/t; and (d) the NMVOC emission to air for each ton of the produced hot asphalt mixture was 0.19 g according to the United States Environmental Protection Agency (2004) [80]. The hot asphalt mixtures were hauled over a distance of 20 km to the construction site by trucks. Afterwards, 1 m 3 of an asphalt mixture was laid by a paver and compacted by a roller machine (both pieces of equipment had a productivity of 45 t/h). The production and transportation of the hot asphalt mixtures account for the global emission of 15.8 kg CO 2 /m 3 , while the laying and compacting operations produce 6.2 kg CO 2 /m 3 .
For the cold in-place recycled mixtures (see Figure S3i), the natural raw materials were hauled from the asphalt plant to the construction site by different trucks. The milled RAP was placed over the surface by a motor grader with a productivity of 1815 m 2 /h. A pulvimixer was utilized to mix and bind together the natural aggregates, marginal materials (RAP or RAP and JGW), cement, water and bitumen emulsion (see Table 2b) supplied at the construction site and then lay the resulting mixture on the pavement surface at a productivity of 750 m 2 /h. Subsequently, the cold mixture was compacted to a desired bulk density (Section 2.1) using a large pneumatic tire roller and a large vibratory steel wheel roller with productivities of 45 t/h. In synthesis, the lower heating temperature (60 • C) of the cold in-place recycling operations as compared with that of HMA production (180 • C) required a lower amount of fuel and thus reduced the CO 2 emissions by 20 kg CO 2 /m 3 during the laying and compaction operations.

End of Life
The CO 2 emissions in the end of life phase that involved the demolition and disposal of the old milled asphalt pavements ( Figure S3i,ii) were equal for all the analysed asphalt mixtures (48.4 kg CO 2 /m 3 ) and, therefore, were not considered further in this study.

LCA Indicators
The LCIA midpoint indicators of the life cycles of the nine road asphalt pavement solutions are presented in Table 3 for binder layer and Table 4 for base layer. They show that HMA binderJGW is not significantly different from HMA binder (−1.5% on average for all impact category indicators) due to the higher optimum bitumen content (+0.75%) that is required to achieve satisfactory engineering performance. However, HMA binderJGW has on average 8% lower GWP, A, OFT, OFH and FR values than those of HMA binderCDW .
HMA binderFA exhibits the best performance among the mixtures for the binder layer characterized by the average 2% reduction of all impact indicators as compared with those of HMA binder , HMA binderCDW and HMA binderJGW due to the lower OBC and absence of the FA crushing phase.
The corresponding hot asphalt solutions for the base layer (HMA baseJGW and HMA baseFA ) demonstrated better environmental performance as compared with that of the traditional HMA base (−6% on average for all impact indicators) as well as HMA binderJGW and HMA binderFA due to the lower natural filler amount and OBC (−0.7% on average).
Reusing FA produced the HMA baseFA mixture, which was most suitable among the hot asphalt solutions for the base layer (−2% on average for all impact category indicators) and binder layer (−4% on average for all impact category indicators).
Comparing CMRA RAP to HMA base , the most remarkable reduction of the impact indicators was observed for FE, which decreased by 87% for the first solution due to the lower amount of nitrogen and phosphorus compounds released in water during aggregate production. In addition, OFT decreased by 36% because of the elimination of the hot in-plant mixing phase and related NMVOC emissions.
Finally, CMRA RAPJGW was found to be the most environmentally friendly alternative among the prepared hot and cold asphalt mixtures for the base layer (−35% and −4% on average for all impact indicators, respectively). In particular, the impact indicators IR, OFT and MR of CMRA RAPJGW are on average 12% lower than those of CMRA RAP due to the lower gaseous and particulate air emissions and minerals consumption required to produce the aggregates and cement (see Table 2b). The same results have been demonstrated by Bonoli et al. [81], who showed that the recycling of RAP combined with steel slag aggregates provides benefits by reducing the consumption of virgin bitumen and aggregates and, at the same time, by reducing the CO 2 equivalent emissions.

Performance Evaluation Based on MCDA and Sensitivity Analysis
In this section, ELECTRE I methodology was applied to the normalized matrixes of the analysed alternatives (see Table S2). The obtained results revealed that HMA binderJGW was the optimal solution for the binder layer, while CMRA RAPJGW was the optimal solution for the base layer in terms of the four defined groups (HP, LP, EHP and MP) with constant weights of 25%.
As indicated by the concordance and discordance values determined for the binder layer (Figure 3(a1,a2)) and base layer (Figure 3(b1,b2)), HMAs exhibited the lowest concordance and highest discordance indices as compared to thresholds c* and d*, respectively. Consequently, the HMA solutions were outperformed by the other solutions in all pairwise comparisons.
In terms of the engineering performance evaluated both at high and low temperatures, HMA binderJGW was often preferred to the other hot asphalt mixtures designed for the binder layer because its concordance and discordance indices were higher than the c* threshold (see Figure 3(a1)) and lower than the d* threshold (see Figure 3(a2)). However, the HMA binderFA performance was better than that of HMA binder and worse than the performances of the other mixtures fabricated from the marginal materials. On the contrary, HMA binderCDW was never preferred to the other hot asphalt mixtures (see Figure 3(a1)), except for HMA binder due to its higher S value at 40 • C.
Considering the base layer alternatives, the hot asphalt mixtures were less favourable than CMRAs because they reached the highest average values of the discordance indices for the environmental indicators (see Figure 3(b2)). CMRA RAPJGW was always preferred to HMA base , HMA baseJGW and HMA baseFA (−34% for all impact indicators on average) as well as to CMRA RAP in terms of HP, MP and EHP, as indicated by the concordance indices presented in Figure 3(b1). Meanwhile, the discordance indices of the CMRAs were slightly below or little above the discordance threshold d* as compared to the hot asphalt mixtures in terms of LP (see Figure 3(b2)) and especially ITSM at 20 • C and N f . Although the hot asphalt mixtures are outranked by the CMRAs, HMA baseJGW exhibits the lowest discordance index among the base layer alternatives compared with that of the HMA baseFA solution, indicating that even its worst indicator (FR) was not very different from the best value obtained for the hot asphalt mixtures.
In general, as opposed to JGW and FA, CDW addition resulted in small environmental benefits and worsened the LP characteristics as compared with that of HMA binder .
A sensitivity analysis was conducted to corroborate the MCDA results by varying the weights of the four groups of indicators (see Figure 2) to obtain 24 different scenarios, as described in Section 2.3. Figure 4a,b shows the solutions selected for the binder and base layers, respectively, at least one time as the best alternatives (their concordance indices were above the concordance threshold, while the discordance indices were below the discordance threshold) with weight configurations that made them preferable to the other solutions. The selection frequency of the best solutions for the p-th alternative (f p ) was calculated via Equation (10).
where: n p is the number of times the p-th alternative of the binder layer or the base layer is selected as the best solution; and n is the total number of analyses (24) performed in different weight configurations.
According to the results obtained for the binder layer (see Figure 4a), HMA binderJGW was the best alternative for 18 out of 24 weight configurations (75% of all cases); HMA binderFA was selected in the remaining 25% cases, while HMA binder and HMA binderCDW were never preferred. The results obtained for the base layer (see Figure 4b) revealed that CMRA RAPJGW was selected as the best alternative for 10 out of 24 weight configurations (42%), HMA baseJGW for 8 out of 24 configurations (33%) and HMA baseFA for 6 out of 24 configurations (25%), while HMA base and CMRA RAP were never selected as the preferable solutions.
The data presented in Figure 4a for the binder asphalt mixtures can be summarized as follows: • HMA binderJGW was the solution that produced the highest concordance and low discordance values; it also represented the best alternative regardless of the weight assigned to the LP group of indicators (the blue shades in Figure 4a) and was selected either when LP was the only criterium of the analysis procedure or when LP was excluded. Because HMA binderJGW had the best HP group among the binder solutions, it also outranked all other solutions when the weight of this group exceeded 20% (see the dark shades of red in Figure 4a). Hence, HMA binderJGW can be used at various pavement service temperatures in the range of 10-60 • C. Similar conclusions may be drawn from the yellow shades in Figure 4a, which represent the configurations with MP weights varying between 20% and 100%. • When the weight assigned to the EHP group is equal to or higher than 60% (the dark shades of green in Figure 4a), HMA binderFA outranks the other binder alternatives in all pairwise comparisons mainly due to the low values of ecotoxicity (M-ECO and F-ECO) and human toxicity (NCT), which were primarily derived from the limestone filler production; thus, HMA binderFA stands out when the mitigation of environmental and human health impacts is the main decision criterium. Instead, HMA binderFA does not produce a good HP group, making it mainly suitable for cold climate regions. The last weight configuration that makes HMA binderFA the best solution for the binder layer does not take into account the MP group (0% MP); this scenario can arise in dry climates or when the groundwater has little effect on the deterioration of pavement materials. The results presented in Figure 4b for the base asphalt mixtures can be summarized as follows: • CMRA RAPJGW is preferred to the other base layer alternatives regardless of the weight assigned to the EHP indicators (from 0% to 100%; see the dark shades of green in Figure 4b). In particular, the preference of CMRA RAPJGW over the other alternatives for the base layer increases when the weight of these indicators grows in the decision-making scenario (−34% on average for all environmental impact indicators as compared to those of HMA base , HMA baseJGW and HMA baseFA ). In addition, CMRA RAPJGW is also preferred to the four remaining base layer solutions with HP indicator weights exceeding 40%, especially in terms of the S, ITSM and RD values, which increased by 13% and 26% and decreased by 17%, respectively.

•
The hot asphalt solutions containing JGW and FA were always preferred to HMA base regardless of the weight configuration; at the same time, HMA baseJGW and HMA baseFA often failed to outrank the cold solutions due to the high discordance indices (equal to 0.82 for the EHP group on average) and in particular due to the OFH, T-ECO, PM, MR and W impact category indicators whose values determined for both CMRA RAP and CMRA RAPJGW were much lower than those of HMA base (−50%), HMA baseJGW (−48%) and HMA baseFA (−46%). • HMA baseJGW is the preferred alternative when a weight of 40% or more is assigned to the LP group (see the dark shades of blue in Figure 4b), which includes such indicators as ITS, ITSM at 10 and 20 • C and N f . Moreover, HMA baseJGW also produces the second best ITSR among the base layer solutions (1% lower than HMA binderFA ); therefore, it is selected as the best alternative when a weight up to 60% is assigned to the MP group. • HMA baseFA generally fails to outrank HMA binderJGW and CMRA RAPJGW from the mechanical viewpoint; hence, it is selected as the best alternative only when the engineering performance groups (LP and HP) are not the main decision criteria and have weights of less than 20%. Meanwhile, the highest moisture resistance makes it preferable to other solutions when the weight assigned to the MP group is equal or higher than 80%, which indicates its suitability for extremely wet areas with low traffic volumes.
In conclusion, the best solutions (HMA binderJGW and CMRA RAPJGW ) provided by ELECTRE I methodology that applied the weight configuration (0) (see Table S3) to various asphalt solutions were partially confirmed by the results of sensitivity analysis for most weight configurations (see Figure 4).

Conclusions
In conclusion, base and binder layers of road asphalt pavements were designed by introducing reclaimed asphalt Pavement and Construction and Demolition Waste as coarse aggregates, while Jet Grouting Waste and Fly Ashes as a filler. A total of four hot asphalt mixtures were investigated for the binder layer and five asphalt mixtures for the base layer, of which two are hot asphalt mixtures and two are cold recycled mixtures. First, a leaching test of the marginal materials was carried out, and their physical properties were assessed to ascertain compliance for reuse in asphalt mixtures.

•
The cold asphalt mixtures for the base layer returned higher resistance to the permanent deformations (lower RD) compared to the traditional HMA base ; in particular, CMRA RAPJGW showed the best engineering performance indicators, returning higher stiffness at 40 • C, MS, ITS and ITSM (+27%, +10% and +68%, respectively) than HMA base .

•
In terms of environmental and human health performance of the life cycle, HMA binderFA has the best performance between the mixtures for the binder layer, bringing on average a 2% reduction of all impact category indicators compared to HMA binder , HMA binderCDW and HMA binderJGW , above all due to lower OBC and the absence of the crushing phase of FA; instead, HMA binderJGW brings on average 1.5% reduction of all impact category indicators compared to HMA binder but reaches 8% lower GWP, A, OFT, OFH and FR than HMA binderCDW . • CMRA RAPJGW is the most environmentally performing alternative compared to all the other hot (−35% on average for all impact indicators) and cold asphalt mixtures (−4% on average for all impact indicators) for the base layer. Specifically, the impact indicators IR, OFT, and MR of CMRA RAPJGW are on average 12% lower than CMRA RAP due to lower gaseous and particulate emissions in air and minerals consumption to produce the aggregates and cement. • MCDA and sensitivity analysis made it possible to identify which of the alternatives envisaged represents the most favourable solution in view of the indicators which are taken into account in a decision-making process for the construction and maintenance of a road pavement, such as high and low-temperature engineering performance, moisture resistance and environmental and human health performance. With a view to reducing raw materials consumption, decreasing greenhouse gas emissions and increasing the service life of asphalt pavements, it was possible to state that, when the operative conditions require the best mechanical performance independently from the average service temperature and humidity, HMA binderJGW results the best alternative. Instead, when decision-makers look for a solution that not only produces the lowest environmental impacts during its useful life but at the same time returns the best resistance to high temperature conditions, the preference is the adoption of the CMRA RAPJGW solution.
Supplementary Materials: The following are available online at https://www.mdpi.com/article/10 .3390/app11199268/s1. Figure S1: Leaching test: (a) sample mineralisation, (b) stirring samples, (c) making samples for COD investigation, (d) titration for COD investigation and (e) plasma optical emission spectrometry for the detection of metals. Figure S2: Testing equipment for (a) Marshall test, (b) ITS, (c) ITSM, (d) Fatigue test and (e) wheel tracking test. Figure S3: Flowchart: unit processes of the life cycle of (i) hot asphalt solutions and (ii) cold in-place recycled asphalt mixtures.