Experimental Study on Two PCM Macro-Encapsulation Designs in a Thermal Energy Storage Tank

: The use of latent heat thermal energy storage is an effective way to increase the efﬁciency of energy systems due to its high energy density compared with sensible heat storage systems. The design of the storage material encapsulation is one of the key parameters that critically affect the heat transfer in charging/discharging of the storage system. To ﬁll the gap found in the literature, this paper experimentally investigates the effect of the macro-encapsulation design on the performance of a lab-scale thermal energy storage tank. Two rectangular slabs with the same length and width but different thickness (35 mm and 17 mm) ﬁlled with commercial phase change material were used. The results show that using thinner slabs achieved a higher power, leading to a reduction in the charging and discharging time of 14% and 30%, respectively, compared with the thicker slabs. Moreover, the variation of the heat transfer ﬂuid ﬂow rate has a deeper impact on the temperature distribution and the energy charged/released when thicker slabs were used. The macro-encapsulation design did not have a signiﬁcant impact on the discharging efﬁciency of the tank, which was around 85% for the operating thresholds considered in this study. designs of macro-encapsulation of rectangular PCM slabs. The behavior of a thermal energy storage tank was analyzed using commercial PCM slabs with different thicknesses. The comparison of the two designs was done in terms of temperature proﬁle, heat transfer rate, and energy obtained during the discharging process. Contributions: Conceptualization, D.V., E.B., L.F.C.; methodology, E.B., G.Z.; formal analysis, D.V., E.B., L.F.C.; investigation, E.B.; resources, L.F.C.; data curation, L.F.C.; writing—original writing—


Introduction
The use of thermal energy storage (TES) has been proved as an effective way to enhance the penetration of renewable energy into energy systems. Amongst all thermal storage technologies, latent heat thermal energy storage (LHTES) received the attention of several researchers over the last decade due to its high energy density and the wide range of applications [1]. Buildings, for example, represent one of the most common applications of the integration of LTHES as an active or passive system [2][3][4]. For the active systems, TES can be used in HVAC components or systems to balance the supply of domestic hot water and heating/cooling demand when renewables are used [5,6], or to reduce the energy consumption through peak load shifting [7], or free cooling techniques [8]. On the other hand, passive systems are directly integrated into the building envelope to reduce the energy demand [9,10]. Other common applications where LTHES can be integrated include solar thermal power plants, such as concentrated solar power (CSP) [11], solar cooling applications [12], district heating or cooling [13], waste heat recovery [14], solar process heat [15], or cryogenic applications [16].
The principle behind LHTES is the use of phase change materials (PCM) as the storage medium, allowing to store thermal energy at a nearly constant temperature exploiting the latent heat during the phase transition, for which the most common one is from solid to liquid to minimize the impact of volume expansions [17]. One of the weaknesses of PCM is its low thermal conductivity that negatively affects the thermal power involved in the charging and discharging processes of the energy storage system. Indeed, this represents The PCM selected in this experimentation was PlusICE S15 (hydrated salt), supplied by PCM products, United Kingdom [35]. The main thermophysical properties of this material are shown in Table 1. Moreover, water was used as the heat transfer fluid (HTF). Table 1. Thermophysical properties of PlusICE S15 [35].

Properties Value
Melting

Experimental Set-Up
The experiments presented in this paper were carried out at the laboratory of the GREiA research group at the University of Lleida in Spain, in a set-up designed to test and characterize latent heat TES systems for mid-low temperature applications (−20 • C < T < 100 • C). Figure 1 shows a detailed schematic diagram of the experimental set-up composed by a 25 L inertia water tank, whose temperature is controlled by a vapor compression cooling unit (Zanotti model GCU2030ED01B [36]) of 5 kW cooling power, two immersion thermostats (OVAN TH100E-2kW [37], and JP SELECTA-1kW [38]). The set-up also integrates: two variable speed pumps, used to control the flow and inlet temperature at the TES system; and a flow meter Badger meter type ModMAG M1000 [39] with an accuracy of ±0.25 % of the actual value, and the latent heat TES storage. The connections between components were joined using 0.5" diameter copper pipes insulated with 18 × 0.9 mm polyurethane tubes. The data acquisition system used consisted of 3 STEP DL-01 data logger [40] connected to a computer that integrates a system control and data acquisition software (SCADA) developed in InduSoft Web Studio [41]. The data recording interval was set to 10 s. terms of temperature profile, heat transfer rate, and energy obtained during the discharging process. The main results obtained from the experimental tests reported in this paper can be used as a reference for institutions and manufacturers to optimize future designs of PCM tanks.

Materials
The PCM selected in this experimentation was PlusICE S15 (hydrated salt), supplied by PCM products, United Kingdom [35]. The main thermophysical properties of this material are shown in Table 1. Moreover, water was used as the heat transfer fluid (HTF).

Experimental Set-Up
The experiments presented in this paper were carried out at the laboratory of the GREiA research group at the University of Lleida in Spain, in a set-up designed to test and characterize latent heat TES systems for mid-low temperature applications (−20 °C < T < 100 °C). Figure 1 shows a detailed schematic diagram of the experimental set-up composed by a 25 L inertia water tank, whose temperature is controlled by a vapor compression cooling unit (Zanotti model GCU2030ED01B [36]) of 5 kW cooling power, two immersion thermostats (OVAN TH100E-2kW [37], and JP SELECTA-1kW [38]). The set-up also integrates: two variable speed pumps, used to control the flow and inlet temperature at the TES system; and a flow meter Badger meter type ModMAG M1000 [39] with an accuracy of ±0.25 % of the actual value, and the latent heat TES storage. The connections between components were joined using 0.5" diameter copper pipes insulated with 18 × 0.9 mm polyurethane tubes. The data acquisition system used consisted of 3 STEP DL-01 data logger [40] connected to a computer that integrates a system control and data acquisition software (SCADA) developed in InduSoft Web Studio [41]. The data recording interval was set to 10 s.    Figure 3, characterized by presenting similar length and width (A and B), but different thickness, with FlatICE dimensions being double that of ThinICE (C). Furthermore, the (D) dimension reveals that the use of thin macro-encapsulation enabled a larger distance between the slabs, increasing the space that allows circulating the HTF through the TES tank. Considering the aforementioned dimensions shown in Figure 3, the use of ThinICE encapsulation allowed fitting a larger number of slabs inside the tank, but less amount of latent storage material compared with the FlatICE, as shown in Table 2.
Appl. Sci. 2021, 11, x FOR PEER REVIEW 4 of 14 Figure 2 shows the PCM storage tank connected to the experimental set-up. The tests were carried out with two different PCM macro-encapsulation designs, namely, ThinICE and FlatICE ( Figure 3). The containers were made in HDPE. The external dimensions of each design are reported in Figure 3, characterized by presenting similar length and width (A and B), but different thickness, with FlatICE dimensions being double that of ThinICE (C). Furthermore, the (D) dimension reveals that the use of thin macro-encapsulation enabled a larger distance between the slabs, increasing the space that allows circulating the HTF through the TES tank. Considering the aforementioned dimensions shown in Figure  3, the use of ThinICE encapsulation allowed fitting a larger number of slabs inside the tank, but less amount of latent storage material compared with the FlatICE, as shown in Table 2.      Figure 2 shows the PCM storage tank connected to the experimental set-up. The test were carried out with two different PCM macro-encapsulation designs, namely, ThinIC and FlatICE ( Figure 3). The containers were made in HDPE. The external dimensions o each design are reported in Figure 3, characterized by presenting similar length and widt (A and B), but different thickness, with FlatICE dimensions being double that of ThinIC (C). Furthermore, the (D) dimension reveals that the use of thin macro-encapsulation en abled a larger distance between the slabs, increasing the space that allows circulating th HTF through the TES tank. Considering the aforementioned dimensions shown in Figur 3, the use of ThinICE encapsulation allowed fitting a larger number of slabs inside th tank, but less amount of latent storage material compared with the FlatICE, as shown i Table 2.     The temperature inside the PCM storage was measured using nine Pt-100 class B, IEC 60751 standard type, with an accuracy of (0.3 + 0.005 · T). The sensors were fixed as shown in Figure 4 to the external surface of three different PCM slabs placed at the bottom, middle, and top of the tank, respectively. Moreover, two additional Pt-100 class A IEC 60751 standard type with an accuracy of (0.15 + 0.002 · T) sensors were placed at the inlets and outlets of the storage tank.
Appl. Sci. 2021, 11, x FOR PEER REVIEW 5 of 14 The temperature inside the PCM storage was measured using nine Pt-100 class B, IEC 60751 standard type, with an accuracy of (0.3+0.005·T). The sensors were fixed as shown in Figure 4 to the external surface of three different PCM slabs placed at the bottom, middle, and top of the tank, respectively. Moreover, two additional Pt-100 class A IEC 60751 standard type with an accuracy of (0.15+0.002·T) sensors were placed at the inlets and outlets of the storage tank.

Methodology
The experimental tests consisted of performing four different charging and discharging processes to evaluate the effect of the PCM macro-encapsulation design and the flow rate on the temperature distribution, heat transfer rate, and energy stored/released. At least three repetitions of each process were performed to ensure repeatability. A summary of the flow rates and temperatures used in the experimentation is shown in Table 3. Furthermore, the heat losses in the worst-case scenario analyzed represent 4% of the charging/discharging energy, therefore the analysis of heat losses was not included in the paper.
To perform a charging process, HTF was first circulated through the PCM tank until all sensors inside the tank reached a temperature of 5 ± 1 °C. Then, the HTF inlet temperature was set at 25 ± 1 °C and the flow rate was set to the corresponding value of the experiment shown in Table 3. The charging process was considered complete when the HTF temperature at the outlet of the tank reached 25 °C. To perform a discharging process, HTF was first circulated through the PCM tank until all sensors inside the tank reached a temperature of 25 ± 1 °C. Then, the HTF inlet temperature was set at 5 ± 1 °C and the flow rate was set to the corresponding value of the experiment in Table 3. The discharging process was considered complete when the HTF at the outlet of the tank reached 7 °C. This value was used instead of 5 °C because a minimum temperature difference of 2 °C was assumed between inlet and outlet of the storage tank as a constraint from the demand side.

Methodology
The experimental tests consisted of performing four different charging and discharging processes to evaluate the effect of the PCM macro-encapsulation design and the flow rate on the temperature distribution, heat transfer rate, and energy stored/released. At least three repetitions of each process were performed to ensure repeatability. A summary of the flow rates and temperatures used in the experimentation is shown in Table 3. Furthermore, the heat losses in the worst-case scenario analyzed represent 4% of the charging/discharging energy, therefore the analysis of heat losses was not included in the paper. To perform a charging process, HTF was first circulated through the PCM tank until all sensors inside the tank reached a temperature of 5 ± 1 • C. Then, the HTF inlet temperature was set at 25 ± 1 • C and the flow rate was set to the corresponding value of the experiment shown in Table 3. The charging process was considered complete when the HTF temperature at the outlet of the tank reached 25 • C. To perform a discharging process, HTF was first circulated through the PCM tank until all sensors inside the tank reached a temperature of 25 ± 1 • C. Then, the HTF inlet temperature was set at 5 ± 1 • C and the flow rate was set to the corresponding value of the experiment in Table 3. The discharging process was considered complete when the HTF at the outlet of the tank reached 7 • C. This value was used instead of 5 • C because a minimum temperature difference of 2 • C was assumed between inlet and outlet of the storage tank as a constraint from the demand side.

Uncertainties Analysis
The impact of the uncertainties in the calculated parameters from the different measurements was evaluated by performing an uncertainty analysis using the Kline McClintock method. The uncertainties of the different monitored parameters are shown in Table 4. HTF specific heat capacity and density were calculated following the correlations presented in Equations (1) and (2) [42]: (2) By applying Equation (3) to the different parameters [43], the uncertainties of the HTF thermophysical properties (density and specific heat) as well as of the heat transfer rates and total stored/released energy were estimated. The uncertainty of the HTF thermophysical properties and heat transfer rates was estimated at each registered time step, and then the mean value was used. Table 5 shows the average uncertainties of the HTF density, specific heat, heat transfer rate, and stored/released energy during the different processes carried out: where W R is the estimated uncertainty in the final result, R the function which depends on the measured parameters, x n is the different independent monitored parameters, and w x is the uncertainties associated to those independent parameters.  Figure 5 shows the charging temperature profile of all sensors placed at the surface of the slabs for the two PCM encapsulation design at different flow rates. To analyze the effect of the encapsulation design in the charging duration, both slabs types were compared at the same flow rate. Due to the higher heat transfer surface and the reduced amount of PCM (30% less according to Table 3) when using ThinICE slabs, at both flow rates, the experiment with the ThinICE slabs reached full charge (T_out = 25 • C) 14% faster than with FlatICE. Furthermore, when analyzing the impact of the flow rate, in both slab designs the experiments show that at 4 L/min the full charge is reached 60% faster than at 2 L/min. rates, the experiment with the ThinICE slabs reached full charge (T_out = 25 °C) 14% faster than with FlatICE. Furthermore, when analyzing the impact of the flow rate, in both slab designs the experiments show that at 4 L/min the full charge is reached 60% faster than at 2 L/min. When comparing temperature distribution inside the tank ( Figure 5), a constant stratification profile between the top, middle, and bottom slabs was observed in all the experiments. This effect was more pronounced in the tests performed with FlatICE slabs in which the lower part of the tank takes longer to charge, obtaining a temperature gradient up to 15 K between the coldest and hottest regions of the tank. This can be explained by the fact that the tank with FlatICE fits a lower number of slabs, as well as presenting smaller HTF channels compared with the tank with the ThinICE design ( Figure 3, Table  2). Therefore, in this tank, the opposition to the HTF flow is higher, enhancing the distribution of the latter towards the regions of the tank where the density is more similar to the HTF inlet one (i.e., upper and middle region of the tank).    When comparing temperature distribution inside the tank ( Figure 5), a constant stratification profile between the top, middle, and bottom slabs was observed in all the experiments. This effect was more pronounced in the tests performed with FlatICE slabs in which the lower part of the tank takes longer to charge, obtaining a temperature gradient up to 15 K between the coldest and hottest regions of the tank. This can be explained by the fact that the tank with FlatICE fits a lower number of slabs, as well as presenting smaller HTF channels compared with the tank with the ThinICE design ( Figure 3, Table 2). Therefore, in this tank, the opposition to the HTF flow is higher, enhancing the distribution of the latter towards the regions of the tank where the density is more similar to the HTF inlet one (i.e., upper and middle region of the tank). Figure 6 presents the evolution of the heat transfer rate (HTR) during the charging process of the four studied cases. Due to the characteristics of the experimental set-up, at the beginning of the experiment, the inlet temperature of the tank oscillated ±2 • C with respect to the desired temperature, affecting the initial peak of the heat transfer rate. However, the inlet temperature stabilized (with Tin standard deviation lower than 0.3) before the temperature inside the tank reaches the latent range of the PCM. The HTR profiles showed an exponential behavior with significantly higher values during the first 20 min of the process when the heat is mainly transferred to the HTF inside the tank and, therefore, rapidly increases its temperature. Afterwards, while the PCM temperature increases, the values of the heat transfer exponentially decrease until minimum values.

Heat Transfer Rate Evolution and Total Energy Stored in the Charging Process
When analyzing the effect of the flows in each slab type, the influence is greater in the tank with ThinICE slabs obtaining, after the initial peak, up to 0.4 kW more in Thin-ICE_4L than in ThinICE_2L. In the case of the tank with FlatICE, this increase drops to 0.1 kW when comparing FlatICE_4L vs FlatICE_2L. The latter results corroborate the statement above; the increase in heat transfer by convection, as the flow rate increases, is more pronounced in the tank with ThinICE slabs due to the larger heat transfer surface and the lower thickness of the PCM layer using this type of slab.   Figure 6. Evolution of the HTF heat transfer rate during the charging processes of the four study cases presented in this study. Figure 7 reports the total energy stored for each experiment condition. The results with ThinICE slabs show that the flow variation did not affect the total stored energy, suggesting the correct utilization of the energy storage capacity of the PCM. Conversely, when analyzing the tank with FlatICE slabs, the charging experiments at 4 L/min stored 10% less energy than the same experiment at 2 L/min. This is due to changes in the flow rate distribution between the slab channels inside the tank when increasing the flow rate. At the end of the experiment, (T_out 25 °C) with FlatICE at 4 L/min, the PCM in the bottom Figure 6. Evolution of the HTF heat transfer rate during the charging processes of the four study cases presented in this study.
During the first 1.5 h of operation, ThinICE_2L and FlatICE_2L showed similar HTR values, which indicates that, due to the low flow rate, the heat transfer by convection is low. Therefore, the higher heat transfer surface area existing with ThinICE slabs is not fully exploited. Moreover, after 1.5 h the HTR delivered to the ThinICE_2L decreases faster than the one delivered to the FlatICE_2L due to the higher amount of PCM introduced into the tank with FlatICE slabs. At a higher flow rate, heat transfer by convection increases. Therefore, during the first 1.5 h of operation, the bigger heat transfer surface area present with ThinICE_4L slabs increases its HTR over FlatICE_4L. After this period, and similar to the results at 2 L/min, the power delivered to the ThinICE_4L decreased faster than the one delivered to the FlatICE_4L.
When analyzing the effect of the flows in each slab type, the influence is greater in the tank with ThinICE slabs obtaining, after the initial peak, up to 0.4 kW more in ThinICE_4L than in ThinICE_2L. In the case of the tank with FlatICE, this increase drops to 0.1 kW when comparing FlatICE_4L vs FlatICE_2L. The latter results corroborate the statement above; the increase in heat transfer by convection, as the flow rate increases, is more pronounced in the tank with ThinICE slabs due to the larger heat transfer surface and the lower thickness of the PCM layer using this type of slab. Figure 7 reports the total energy stored for each experiment condition. The results with ThinICE slabs show that the flow variation did not affect the total stored energy, suggesting the correct utilization of the energy storage capacity of the PCM. Conversely, when analyzing the tank with FlatICE slabs, the charging experiments at 4 L/min stored 10% less energy than the same experiment at 2 L/min. This is due to changes in the flow rate distribution between the slab channels inside the tank when increasing the flow rate. At the end of the experiment, (T_out 25 • C) with FlatICE at 4 L/min, the PCM in the bottom slabs of the tank had not completed the phase change ( Figure 5) and therefore stored 8% less energy.
Appl. Sci. 2021, 11, x FOR PEER REVIEW 9 of 14 slabs of the tank had not completed the phase change ( Figure 5) and therefore stored 8% less energy.  Figure 8 shows the discharging temperature profile of all sensors placed at the surface of the slabs at two different mass flow rates. Analyzing the influence of the PCM encapsulation design on both flow rates, the tank with ThinICE slabs finished the discharging process 30% faster than with FlatICE slabs. This can be explained by the higher heat transfer surface and the lower amount of PCM (30% less according to Table 3) when using ThinICE. Moreover, when analyzing the influence of the flow rate, Figure 8 shows that for both slab types at 4 L/min the experiments were completed 50% faster than at 2 L/min.

Temperature Evolution during the Discharging Process
When comparing temperature distribution inside the tank (Figure 8), a similar temperature profile between the top, middle, and bottom slabs was observed in all the experiments performed with ThinICE slabs. Moreover, this behavior changed with the use of the FlatICE, where the stratification and the profile temperature inside the tank depends on the mass flow rate.  Figure 8 shows the discharging temperature profile of all sensors placed at the surface of the slabs at two different mass flow rates. Analyzing the influence of the PCM encapsulation design on both flow rates, the tank with ThinICE slabs finished the discharging process 30% faster than with FlatICE slabs. This can be explained by the higher heat transfer surface and the lower amount of PCM (30% less according to Table 3) when using ThinICE. Moreover, when analyzing the influence of the flow rate, Figure 8 shows that for both slab types at 4 L/min the experiments were completed 50% faster than at 2 L/min.

Heat Transfer Rate Evolution and Total Energy Released in the Discharging Process
The HTR evolution during the discharging process for all the experimental cases is shown in Figure 9. In all the experiments the profiles showed a similar trend. Significantly higher values were obtained during the first 20 min of the process when the heat is mainly transferred from the HTF inside the tank followed by an exponential decrease while the PCM decreases its temperature until minimum values are reached. Furthermore, in this case, due to the characteristics of the experimental facility, at the beginning of the experimentation the inlet temperature of the tank oscillates ±2 °C around the desired temperature, affecting the initial peak of power. However, the inlet temperature stabilizes (T_in standard deviation lower than 0.3 °C) before the temperature inside the tank reaches the latent range of the PCM. After the initial peak and during the first 1.5 h of operation, ThinICE_2L shows slightly better performance getting up to 0.1 kW more HTR than FlatICE_2L. Moreover, due to the lower amount of PCM in the storage tank with ThinICE slabs, after 1.5 h the HTR delivered by ThinICE_2L decreases faster than the one delivered   When comparing temperature distribution inside the tank (Figure 8), a similar temperature profile between the top, middle, and bottom slabs was observed in all the experiments performed with ThinICE slabs. Moreover, this behavior changed with the use of the Flat-ICE, where the stratification and the profile temperature inside the tank depends on the mass flow rate.

Heat Transfer Rate Evolution and Total Energy Released in the Discharging Process
The HTR evolution during the discharging process for all the experimental cases is shown in Figure 9. In all the experiments the profiles showed a similar trend. Significantly higher values were obtained during the first 20 min of the process when the heat is mainly transferred from the HTF inside the tank followed by an exponential decrease while the PCM decreases its temperature until minimum values are reached. Furthermore, in this case, due to the characteristics of the experimental facility, at the beginning of the experimentation the inlet temperature of the tank oscillates ±2 • C around the desired temperature, affecting the initial peak of power. However, the inlet temperature stabilizes (T_in standard deviation lower than 0.3 • C) before the temperature inside the tank reaches the latent range of the PCM. After the initial peak and during the first 1.5 h of operation, ThinICE_2L shows slightly better performance getting up to 0.1 kW more HTR than FlatICE_2L. Moreover, due to the lower amount of PCM in the storage tank with ThinICE slabs, after 1.5 h the HTR delivered by ThinICE_2L decreases faster than the one delivered by FlatICE_2L. At 4 L/min, after the initial peak and during the first 1.5 h, similar results to 2 L/min are obtained. Moreover, after 1.5 h the HTR of ThinICE_4L drastically decreases, therefore for the next 2 h (from 1.5-3.5 h) FlatICE_4L maintains an HTR up to 0.4 kW higher than ThinICE_2L.
Appl. Sci. 2021, 11, x FOR PEER REVIEW 11 of 14 Figure 9. Evolution of the HTF heat transfer rate during the discharging processes of the four study cases presented in this study. Figure 10 reports the total energy released for each experiment conditions, and the percentage it represents with respect to the energy stored in the charging process ( Figure  7) in each case. Analyzing the effects of flow rate, similar to the charging, both experiments with ThinICE slabs showed a comparable energy release, suggesting a correct utilization of the energy stored in the PCM. In the case of FlatICE slabs, experiments at 2 L/min released 10% more energy compared with 4 L/min. This is supported by the fact that in the charging process the tank at 2 L/min manages to store 10% more energy than at 4 L/min ( Figure 5). In addition, it is interesting to note that in all cases of the selected operating threshold approximately 85% of the energy stored in the tank was discharged.   Figure 9. Evolution of the HTF heat transfer rate during the discharging processes of the four study cases presented in this study. Figure 10 reports the total energy released for each experiment conditions, and the percentage it represents with respect to the energy stored in the charging process (Figure 7) in each case. Analyzing the effects of flow rate, similar to the charging, both experiments with ThinICE slabs showed a comparable energy release, suggesting a correct utilization of the energy stored in the PCM. In the case of FlatICE slabs, experiments at 2 L/min released 10% more energy compared with 4 L/min. This is supported by the fact that in the charging process the tank at 2 L/min manages to store 10% more energy than at 4 L/min ( Figure 5). In addition, it is interesting to note that in all cases of the selected operating threshold approximately 85% of the energy stored in the tank was discharged.
with ThinICE slabs showed a comparable energy release, suggesting a correct utilization of the energy stored in the PCM. In the case of FlatICE slabs, experiments at 2 L/min released 10% more energy compared with 4 L/min. This is supported by the fact that in the charging process the tank at 2 L/min manages to store 10% more energy than at 4 L/min ( Figure 5). In addition, it is interesting to note that in all cases of the selected operating threshold approximately 85% of the energy stored in the tank was discharged.

Conclusions
Macro-encapsulation of phase change materials (PCM) represents one of the most widely used techniques for the implementation of latent heat thermal energy storage systems. The design of the macro-encapsulation is fundamental to archive the best compromise between optimal heat transfer performance and energy stored. However, current literature lacks experimental data on the effect of macro-encapsulation in the performance of latent heat thermal energy storage.

Conclusions
Macro-encapsulation of phase change materials (PCM) represents one of the most widely used techniques for the implementation of latent heat thermal energy storage systems. The design of the macro-encapsulation is fundamental to archive the best compromise between optimal heat transfer performance and energy stored. However, current literature lacks experimental data on the effect of macro-encapsulation in the performance of latent heat thermal energy storage. This paper analyzed, through an experimental study, the effect of the design of macroencapsulated PCM on the thermal behavior of a latent heat thermal energy storage tank during both the charging and discharging processes. In this study, external dimensions of the energy storage tank were fixed and two different types of commercial slabs with different thickness filled with the same PCM were tested. The results could be particularly useful to evaluate the best configuration of storage medium when the storage tank is limited with a fixed volume.
The results were compared in terms of temperature profile, heat transfer rate, and energy stored/released. The results and the conclusions obtained from this study can be applied to similar configuration of the PCM storage that aim to use rectangular macroencapsulated slabs as storage medium. The lesson learnt from this study suggests that macro-encapsulation design has a relevant impact on the heat transfer during both charging and discharging processes, so the design of the TES unit should be done and analyzed according to the requirements of the application.
The use of a thinner macro-encapsulation design (ThinICE) allowed fitting a larger number of slabs inside the tank. However, the higher amount of encapsulation material and the larger distance between the slabs (i.e., higher HTF channels height) resulted in a 30% less amount of PCM introduced inside the tank with this encapsulation design.
With ThinICE slabs, the temperature profiles were less affected by the influence of the mass flow rate, promoting a stratified temperature profile inside the tank in both the charging and discharging processes. Using FlatICE, this effect is more pronounced at low flow rates due to the smaller height of the channels that obstructed the flow at the bottom of the tank during charging and at the top of the tank during discharging. However, at high flow rates, the stratification is reduced with the use of thicker slabs, especially during the discharging process.
In all the discharging tests, when the outlet temperature of the tank reached 7 • C, approximately 85% of the energy previously stored in the tank was discharged.
The effect of increasing the heat transfer surface using ThinICE slabs on the power delivered by the storage tank is mostly appreciated at a higher flow rate where the heat transferred by convection is higher. Furthermore, using thinner slabs, the higher heat transfer surface area achieves a higher discharging power but is delivered for a shorter period of time. Therefore, for longer discharging periods and for higher storage capacity given a fixed volume of storage tank, the use of FlatICE should be preferred.