Inﬂuence of Process Parameters on Cutting Width in CO 2 Laser Processing of Hardox 400 Steel

: This paper presents an experimental research that proposes to determine the inﬂuence of process parameters on CO 2 laser cutting of 8 mm thick Hardox 400 steel, for which Kerf has a minimum value. The experimental research was conducted according to a complete factorial plan with laser power, assistant gas pressure and cutting speed as the input parameters, and cutting width as the dependable variable. The Design of Experiment (DOE) consisted of 27 references and was completed with four replicas to determine the variation of the Kerf average. Functional, linear and quadratic relations were determined, which describe the Kerf dependence on the cutting parameters in order to establish the most inﬂuential parameter. The results show that the independent parameter with the most signiﬁcant inﬂuence was the laser power, with minimum Kerf obtained if the laser power and the assistant gas pressure were adjusted to average values. The interaction between laser power and auxiliary gas pressure at constant cutting speed was investigated to improve Kerf and reduce the laser processing cost. The study offers the right combination of process parameters that leads to a minimum value of the cutting width.


Introduction
The extension of laser beam cutting (LBC) as a cutting process in industrial processes is due to the advantages it generates. Laser beam processing allows for cutting a wide range of materials with different mechanical properties. The optimization of the cutting parameters, which results from the concentration of the laser beam in a very small point, on the surface of the material to be processed, will lead to faster processing of various materials with lower processing costs.
The use of laser in cutting and processing metallic materials has been researched in many specialized works. Tatzel et al. showed the effect of the focusing position on the induced heat affecting the laser-cut edges of 3-mm-thick stainless steel. The process parameters observed during cutting were speed, assistant gas pressure and focusing position. The latter has proven to be an important parameter if a high processing quality is to be achieved [1]. Levichev et al. shows that continuous heating of the semifinished part during oxygen-assisted cutting decreases the quality and generates material losses to thick metal plates, where the cutting speed is low. The cutting experiments took place on a soft steel with a thickness of 15 mm using a 4 KW power laser. Three methods were used to obtain high quality of the cut surface: optimizing the input parameters for preheated areas, using active cooling to eliminate heat excess and using active cooling was statistically analyzed with ANOVA dispersion technique. The obtained results show that any increase of the values of the cutting parameters generates a larger cutting width and the increase of the laser speed and power leads to the increase of the Kerf taper [13]. Hajad et al. indicated a method of optimizing the laser cutting path to accumulate minimal heat by using a genetic algorithm with neighborhood search. This technique is useful for hardening the surface in the welding process where the working distance and heat accumulation must be optimized to obtain quality parts [14]. Seong et al. highlighted the behavior of the gas flow in the subsonic and supersonic nozzle by analysis with the Nomarsk interferometer. The process of cutting 60 mm thick stainless steel sheets took place with the help of a 6 KW laser. The experiments were performed to observe the effect of the geometric configuration of the nozzles. By varying the stand-off distance, the ability to eliminate the formed melt was determined. The results show that the supersonic nozzle has a capacity to remove the melt at a greater distance [15].
Anghel et al. conducted CO 2 laser cutting research on 304 stainless steel to obtain miniatural gears. The cutting experiments were designed according to the Box-Behnken design and performed based on the response technique, with 29 references evaluated by the RSM (response surface) model. The varied parameters were laser power, cutting speed, focal position and cutting gas pressure, while the output parameter measured and calculated the surface roughness R a . With the help of ANOVA it was established that the focal position is the most influential parameter [16]. Chen et al. presented the optimization of the hardness of the carbon steel material AISI 1045 under the influence of the input parameters: laser power, scanning speed and focusing distance. They found that the hardness of the hardened surface after laser cutting improved from 200 HV to 660 HV. RSM models are able to interpret hardened width (HW), hardened hardness (MH) and hardness gradient (HG) [17]. Li et al. showed that when laser cutting thin sapphire sheets with the help of a Bessel beam, a zero taper and a higher roughness were obtained [18]. Subasi et al. used a laser beam guided by a water jet to process the nickel alloys used in the aerospace industry, in the technological process of micro-drilling. The improvement consisted of eliminating the burrs of the cut surfaces, reducing the taper and reducing the area affected by the laser heat [19]. Das Partha et al. optimized the cutting parameters (cutting speed, gas pressure, pulse width, pulse frequency) of two laser sources, solid Nd-YAG and gas CO 2 in pulsed mode. The optimization method is based on several criteria, superiority and inferiority, to identify the most suitable combination, which ensures low R a value, reduced cutting width and slope [20]. Cheng et al. presented a low-cost method of manufacturing PMMA (polymethyl methacrylate) nozzles, based on laser cutting and PDMS (polydimethylsiloxane) bonding [21]. Powell et al. experimentally investigated the CO 2 laser cutting of soft steel sheets with a thickness of 15-20 mm. There is a decrease in the quality of the cut edge to thicknesses between 15 and 20 mm [22]. Dontu [23], Savii [24] and Draganescu [25] contributed to the expansion of the CO 2 and Nd-YAG laser application in industrial engineering activities, as well as applications in the production processes of laser cutting, drilling and welding in the manufacture of industrial products. Genna et al. studied the interaction between the cutting parameters and the part parameters depending on the type of chosen material-AlMg3, St37-2 and AlSI 304-in order to vary the kerf width. The auxiliary gases used were N 2 and O 2 . The results show that the Kerf width increases as the cutting speed decreases, due to the higher accumulated energy [26]. Son et al. presented the influence of laser parameters on Kerf in the case of SS41 and SUS 304 metal sheets used in engineering applications. The ANOVA method established the most significant parameters used in the experiments: laser power and cutting speed [27]. Tahir et al. researched UHSS ultrahard steel in nitrogen and oxygen-assisted laser processing. The results observed after cutting and analysis indicate a better cutting width for nitrogen, and better hardness and perpendicularity of the cut edge when using oxygen as an assistant gas [28]. El Aoud et al. demonstrated that CO 2 laser technology is advantageous for cutting sheets of Ti-6Al-4V titanium alloys and pure titanium. For both types of material, the most influential cutting parameter is the laser power in case of cutting width disturbance. In this study, Kerf is inversely proportional to the cutting speed [29]. Chatterjee et al. showed laser piercing for Ti6Al4V alloy in order to obtain quality holes. The analysis of variance indicates that the most influential input parameter is the laser power on the area affected by HAZ heat and the conicity of the processing [30]. Gvozdev et al. presented a mathematical model that describes the influence of laser cutting parameters on the surface roughness, HAZ and the deviation from the rectilinearity of the cut surface. Nomograms are constructed indicating the selection of cutting regimes in case of minimizing the responses for carbon steel sheets with thicknesses of 6, 10 and 14 mm [31]. Patel et al. studied the effect of the input parameters (laser power, gas pressure, cutting speed, nozzle diameter) on the cutting quality for H400 materials. They concluded that the minimum Kerf was obtained at a pulse frequency of 25 Hz, while maximum Kerf was obtained at a laser pulse frequency of 20 Hz [32]. Patel et al. showed the influence of the cutting parameters (cutting speed, laser power, frequency, pressure) to identify the responses due to laser cutting (taper, Ra and HAZ) of En-31 molded steel. Mathematical models were developed using the method of response surfaces and it was identified that the best roughness is obtained when selecting process parameters at average values [33]. Prajapati et al. investigated the effect of laser installation parameters such as laser power, gas pressure, cutting speed and thickness in the case of cutting experiments designed after the Taguchi L27 model on roughness. The statistical analysis was performed using the ANOVA variant. The sensitive parameters identified are the cutting speed and the thickness of the part [34]. El Aoud et al. used 3-mm-thick Ti sheets to investigate laser cutting. The cutting parameters, laser power, cutting speed and gas pressure ran according to an experimental plan given by Taguchi's method in order to analyze the microstructure of the cut edge and optimize the roughness. The conclusion indicated the optimal cutting condition was obtained at laser power P = 3 KW, cutting speed v = 2.400 mm/min and gas pressure p = 8 bar [35]. Boujelbene et al. studied CO 2 laser cutting on Ti sheet with thickness g = 2 mm. Taguchi's method was implemented to minimize roughness and identify optimal cutting parameters. It turned out that the roughness increases when the thermal energy is increased by the laser and decreases at the high cutting speed [36]. Zhou et al. studied the laser polishing of S136D die-cast steel using an L16 orthogonal experimental plane. Experiments have shown a tendency for surface roughness to vary with laser energy density using a moving laser heat source [37]. From the above literature it appears that numerous investigations were performed to identify the effects of process parameters on Kerf responses, hardness, roughness and taper . In addition, other research included the focusing position, nozzle geometry, stand-off distance on the gas jet, temperature of the cutting area, melting depth, thermal stresses, HAZ [6,15,21], and laser fusion deposition technique [11]. Further, some studies methods used modern design and optimization, genetic algorithm, iterative, artificial neural network model, superiority and inferiority criteria [3,10,14,20].
Most research focuses on various metallic materials, alloys, groups of materials with different physical, chemical and thermal properties. The presented studies conducted numerous experimental investigations in order to identify the effects of laser cutting parameters on process responses. At present, there is a diversity of research aimed at finding a suitable combination of the main parameters that affect the quality of cutting. In the previous approaches the most common use of materials in the case of laser heating is found on stainless steel, Ti, mild steel, alloys and reduced on hard and ultra-hard steel. In this study we selected the H400 steel material in the laser manufacturing process due to its extensive capacity for use and exploitation over time, surface conditions and absorbability. H400 is an insufficiently used steel from a technical point of view, and is little used in the laser processing process, which is why it was chosen as a study material. Linear (L) and quadric (Q) prediction models, and regression (L) and (Q) models, respectively, were developed using the response surfaces, which were then compared for adequacy and in the ranking of the cutting factors. A number of physical quantities were calculated that accompany the interaction between radiation and substance as a result of the transformation of light energy into caloric energy.
H400 steel can be heat-processed with laser, needs minimal subsequent post-laser processing, and is often used after cutting mechanical machining operations can be performed. The selection criterion is based on the fact that the material is suitable for mechanical processing for different types of parts that must meet wear resistance in operation; it is a a high-quality material used in the machine building industry and is superior to ordinary hot rolled steels. It behaves very well in operation, and the processed parts are very well manifested in the coal mining industry. Due to its wear resistance properties, the material is used in the oil shale industry, stone quarries, civil engineering and road construction. H400 is an economical, high-quality material that is durable and resistant to abrasion and corrosion. It is superior to OL, Dillidur and Weldox rolled steel. The main destination of H400 steel is for the production of mechanical parts whose strength is very high; in the machine building industry it is used to make crushing machines, metal waste compactors and sandblasting machines. CO 2 laser cutting is a manufacturing process based on focusing light energy in a spot with a diameter of 0.2 mm. Laser beam melts the material due to the incident intensity in a range of 105-106 W/cm 2 . The characteristics of the laser beam and the projection on the part have been set in order to reduce the local heat and stress. From the laser spot starts a beam of rays with very small divergence (<2 • ) which cuts the material by heat processing, resulting in a conical surface. The light generated by the laser attacks the material and crosses it through a stationary piercing, after which the cut is made in a straight profile until it enters the contour of the piece. The H400 steel plate is heated with the laser light beam until the initialization of the oxidation and melting reaction. There is a surplus of heat due to the thermochemical reaction that accompanies the laser thermal cutting. The manufacture of parts by laser cutting is done with the help of the computer based on the execution drawing. Laser cutting is improved with the help of spotlights, which generate melts of different sizes, depending on the laser power. The energy from the laser is transferred and absorbed by the metal increasing the temperature of the cutting area and forming the melt.
The thermal laser cutting process is assisted by the oxygen jet that coaxially accompanies the laser light from the cutting head, through the nozzle, until it enters the material. The role of the gas jet is to protect the laser beam from dust particles; it is used to meet the material and cause the iron to burn. The gas flows through the nozzle, removing the molten mass of material from the slit. Due to the heat distribution, there is a thermal stress in the material of the cut surfaces. When laser light interacts with the substance, a collision process takes place between the incident photons and the electrons of the steel. In this process, part of the photon energy is taken up by free electrons from the metal, in the form of kinetic energy, and the other part is taken up by the ions of the network that vibrate with higher amplitude, which leads to increased internal energy and its transformation into heat.
Depending on the laser parameters and the physical and chemical properties of the material, the position of spot f can be chosen after several tests. The technological process of cutting can be explained based on the interaction between energy-carrying radiation and matter. The cutting of allied and non-allied steels takes place when the preheating temperature is reached (1200 • C). The laser spot advances with speed v, and the part is cut as it moves. The spot moves on the established trajectory from the execution drawing, electronically transmitted from ByVision software to the cutting head. The shorter the stand-off distance, the higher the pressure of the gas jet on the part. Temperature is a status parameter that influences the cut. Laser melting gives rise to an oxidation reaction between iron and oxygen. Slot dimensions are influenced by pressure and temperature due to heat flow. The size of the 0.2 mm laser spot produces a larger slit due to the working pressure and temperature of the thermal energy reaction. Oxygen produces a crack as a result of the combustion reaction. High pressure removes the molten material and creates Appl. Sci. 2021, 11, 5998 6 of 29 a slit. The increase in temperature due to laser energy and chemical reaction influences the cut. The cut edges are burned, oxidized and corroded, so oxygen pressure causes the cutting of edges. The temperature also rises due to friction between the gas and the contact surface. The intensity of the chemical reaction in the material is influenced by the laser power and the pressure of the assistant gas. The melting mass is determined by the power and pressure of the cutting gas. The gas jet has more energy than the energy of the melt, so destruction of the surface is achieved. As a result of chemical reactions, oxides appear on the cutting surface, material and in the atmosphere [38].
When heating a metal target with a circular spot of diameter d, the working temperature is given by the relation: where A is the absorbsion coefficient, dimensionless; p is the laser power (W); k is the thermal conductivity of the material (W/m·K); d is the spot diameter (mm). The novelty of this research consists in the fact that for the studied material no recommendations regarding the working regime were found in the literature. In order to understand the processes that take place inside the material, the authors considered it necessary to mathematically model aspects related to the cutting width. The obtained results allowed the determination of the optimal variant of the input parameters which leads to obtaining a minimum cutting width. The cost of processing H400 steel by CO 2 laser cutting was also established.

Materials and Methods
The material used in cutting experiments was high-hardness steel H400. There are few studies to discover the qualities and uses of steel, which is why it was chosen as a study material in CO 2 laser cutting experiments. Prior to processing, the material was carefully studied to ensure it was not damaged nor oxidized, because this would inhibit its ability to absorb laser light. The chemical composition of the processed material is specified in Table 1. The alloying element silicon has a melting point of 1414 • C, which burns more than manganese, which has a melting point of 1244 • C. In addition, carbon helps to increase the hardness of the material to a certain concentration. Laser treatment changes the chemical composition of the material in the cutting area. Manganese increases the tendency to overheat while carbon reduces the intensity of the oxidation reaction. The laser-treated surface contains MnC and SiC carbides. The chromium and nickel content make the material corrosion-resistant. Laser treatment of this material increases the hardness on the cut surface. The parts made of this steel are intended for the industrial, extractive, and automotive fields.
The problem of identifying the sensitive parameters that reduce the cut has been solved experimentally using RSM (model of response surfaces). The intelligent production in the manufacture of H400 parts considers the design potential of the experiment and its directing from the computer of the laser installation that has the capacity of self-positioning, self-adjustment, self-determination, and self-measurement. Two steel plates were prepared in the laboratory, which were subjected to a robust factorial plan complete with 27 independent experiments that were conducted four times. The design of the complete factorial plan is robust and respects the recommendations of the cutting technology, the distance from the edges and the distance between the parts equal to the thickness of the material. For the experimental design, a model was chosen with all the interactions between the three influencing factors that provide relevant information about the cutting process. The project has two constant parameters at a time and a variable parameter to determine the effect, the correlation coefficient and the estimated average of Kerf. The way in which the cutting process varies is ensured by performing four subsequent identical experiments. Dimensional accuracy is ensured when we select cutting parameters within the tolerances. DOE renders an execution of the experimental project that changes a factor at each step. In designing the experiment each factor must be run at the maximum and minimum level to calculate the effect as accurately as possible. The experimental design is suitable for the H400 experiment for the following reasons: the design of the experiment consists of 27 different experiments that lead us to look for the most appropriate parameters to minimize Kerf. The input values of the important parameters result from the criteria imposed on the experiment and the Kerf taxonomy. The set of the optimum point chosen can subsequently save time and reduce the processing cost in the manufacture of approximately identical parts by setting the laser machine to execute a certain number of products using the operation of multiplication and copying, ensuring production. Moreover, under laser cutting conditions, the cutting speed is used at the maximum level to have a low heat flux and reduced interaction time, resulting in a reduced melt mass so that the gas flux eliminates drops in smaller numbers. The DOE generates an orthogonal matrix that can be discussed and evaluated mathematically and theoretically based on data obtained for Kerf.
The dimensions of the semi-finished product used in the experiment are 300 mm, 220 mm and 8 mm for length, width and thickness, respectively. The 5.181 kg plate was cut, as shown in Figure 1, to perform a complete factorial experiment, based on an experimental plan, to determine the optimal value of the input parameters that influence the cutting width. and a variable parameter to determine the effect, the correlation coe estimated average of Kerf. The way in which the cutting process vari performing four subsequent identical experiments. Dimensional accu when we select cutting parameters within the tolerances. DOE renders an experimental project that changes a factor at each step. In designing the factor must be run at the maximum and minimum level to calculate the ef as possible. The experimental design is suitable for the H400 experiment reasons: the design of the experiment consists of 27 different experimen look for the most appropriate parameters to minimize Kerf. The inp important parameters result from the criteria imposed on the experim taxonomy. The set of the optimum point chosen can subsequently save the processing cost in the manufacture of approximately identical parts by machine to execute a certain number of products using the operation o and copying, ensuring production. Moreover, under laser cutting condit speed is used at the maximum level to have a low heat flux and reduced resulting in a reduced melt mass so that the gas flux eliminates drops in s The DOE generates an orthogonal matrix that can be discussed mathematically and theoretically based on data obtained for Kerf.
The dimensions of the semi-finished product used in the experiment mm and 8 mm for length, width and thickness, respectively. The 5.181 k as shown in Figure 1, to perform a complete factorial experimen experimental plan, to determine the optimal value of the input paramete the cutting width. The factorial design consists of 27 tests, followed by four replicas. semi-finished products containing 135 pieces. Test processing was done combinations of parameters that provide the least satisfactory results, es ensure cutting. The extreme combinations were tested, and the averag power, gas pressure and cutting speed were chosen. Following the expe design 33 was built which offers all possible combinations of the valu parameters. The complete factorial plan allows the study of the common input parameters on the variation of the cutting width. The comple independent test block was established with respect to the single ce maintaining a balance of increase and decrease in the values of t parameters, resulting in an orthogonal matrix.
The piece with a contour consisting of three straight segments and a was designed to be cut to the dimensions: length 20 mm, width 20 m The factorial design consists of 27 tests, followed by four replicas. There were two semi-finished products containing 135 pieces. Test processing was done to determine the combinations of parameters that provide the least satisfactory results, especially that still ensure cutting. The extreme combinations were tested, and the average values of laser power, gas pressure and cutting speed were chosen. Following the experimental design, design 33 was built which offers all possible combinations of the values of the cutting parameters. The complete factorial plan allows the study of the common influence of the input parameters on the variation of the cutting width. The complete design of the independent test block was established with respect to the single central test point, maintaining a balance of increase and decrease in the values of the independent parameters, resulting in an orthogonal matrix.
The piece with a contour consisting of three straight segments and a circular profile, was designed to be cut to the dimensions: length 20 mm, width 20 mm, with a semi-circular side, from a 20 mm side square, effective area 0.00036 m 2 and mass 0.02803 kg. The sketch of the resulting piece is shown in Figure 1. A complete factorial experiment was performed to determine the most suitable combinations that decrease the cutting width and improve the production cost. The ByAutonom 4020/6000 W laser cutting equipment, manufacturer: Bystronic Switzerland, was used to cut H400 sheets ( Figure 2).
Appl. Sci. 2021, 11, x FOR PEER REVIEW circular side, from a 20 mm side square, effective area 0.00036 m 2 and m The sketch of the resulting piece is shown in Figure 1.
A complete factorial experiment was performed to determine the combinations that decrease the cutting width and improve the produc ByAutonom 4020/6000 W laser cutting equipment, manufacturer: Bystron was used to cut H400 sheets ( Figure 2). The wavelength of the CO2 laser beam is 10.6 µm. The diameter of th at the entrance to the lens is 20 mm, and the diameter of the spot is 0.2 m nozzle through which the gas is directed has a diameter of 1.5 mm. Sta source, the laser beam reaches the lens with focal length of 190.5 mm, and in the focus of the lens, where the incident intensity on the piece increases compared to the value recorded before entering the lens, approximate W/cm 2 . The focusing position of the laser spot was kept constant at +1 mm a level of the blank, taking into account that the assistant gas is O2.
The research of the influencing factors on the dependent variable, the was based on performing preliminary tests to identify the central point, th experiments were run, the selection of parameters being a condition to results. After these tests, the reference values were established: laser pow auxiliary gas pressure p = 0.50 bar and cutting speed v = 1800 mm/min experiment has three influencing factors, and each factor has three levels the central values, the experiment predicted the variation of the input follows: laser power ± 100 W, auxiliary gas pressure ± 0.05 bar, cuttin mm/min, so that the levels for laser power reached the values of 4900 W, 50 W; the auxiliary gas pressure was 0.45, 0.50 and 0.55 bar; the cutting speed and 1900 mm/min. The process parameters of the laser installation are sho A mixed experimental design with independently run experiments with three input levels for laser power, auxiliary gas pressure and cutting of the experiment is a block containing 27 independent experiments. You how the input parameters have been changed. The 27 parts were divided in For each series, a value of the laser power (4900, 5000 and 5100 W) was ma the values of the gas pressure (0.45, 0.50 and 0.55 bar), respectively of the (1700, 1800 and 1900 mm/min) were modified.  The wavelength of the CO 2 laser beam is 10.6 µm. The diameter of the laser beam D at the entrance to the lens is 20 mm, and the diameter of the spot is 0.2 mm. The conical nozzle through which the gas is directed has a diameter of 1.5 mm. Starting from the source, the laser beam reaches the lens with focal length of 190.5 mm, and is concentrated in the focus of the lens, where the incident intensity on the piece increases 103-104 times, compared to the value recorded before entering the lens, approximately 162.5 × 105 W/cm 2 . The focusing position of the laser spot was kept constant at +1 mm above the upper level of the blank, taking into account that the assistant gas is O 2 .
The research of the influencing factors on the dependent variable, the cutting width, was based on performing preliminary tests to identify the central point, then the cutting experiments were run, the selection of parameters being a condition to obtain correct results. After these tests, the reference values were established: laser power p = 5000 W, auxiliary gas pressure p = 0.50 bar and cutting speed v = 1800 mm/min. The factorial experiment has three influencing factors, and each factor has three levels. Compared to the central values, the experiment predicted the variation of the input parameters as follows: laser power ± 100 W, auxiliary gas pressure ± 0.05 bar, cutting speed ± 100 mm/min, so that the levels for laser power reached the values of 4900 W, 5000 W and 5100 W; the auxiliary gas pressure was 0.45, 0.50 and 0.55 bar; the cutting speed was 1700, 1800 and 1900 mm/min. The process parameters of the laser installation are shown in Table 2. A mixed experimental design with independently run experiments was prepared with three input levels for laser power, auxiliary gas pressure and cutting speed. The size of the experiment is a block containing 27 independent experiments. You can easily see how the input parameters have been changed. The 27 parts were divided into three series. For each series, a value of the laser power (4900, 5000 and 5100 W) was maintained, while the values of the gas pressure (0.45, 0.50 and 0.55 bar), respectively of the cutting speed (1700, 1800 and 1900 mm/min) were modified.
In the stationary piercing stage (initial piercing of the laser material in pulsed regime) the working parameters are different, compared to those used in the actual experiment, in which dynamic piercing is used. The cutting gas pressure is 0.7 bar, higher than the maximum pressure used in the cutting experiments, and the focusing position f = 0 mm, which means that the laser spot is positioned on the surface of the material. In addition, through a stationary piercing, a conical channel with a diameter larger than the cutting width was drilled. After drilling, the laser entered the straight profile at a distance of about 10 mm until it reached the contour of the part.
In addition to process factors (laser power, auxiliary gas pressure and cutting speed), the cutting width is also influenced by uncontrollable factors: material condition, chemical composition, heat propagated in the material and temperature. The laser beam interacts with the part determining the geometry of the cutting slot. One aspect to consider in the laser beam at the top is that it does not have the same intensity at all points, the distribution being given by the Gaussian curve. The intensity of the oxidation reaction can ensure an improved cutting width. To improve laser cutting, the light rays refracted by the lens meet above the steel material and form the laser spot by interference.
The front inclination of the cut determines the taper in the processing of the parts. The first test piece was 1P, processed as follows: At first a perforated channel with a diameter of 1.07 mm outside the part was created, and after, the laser entered a straight line with a length of 10 mm for processing the first part. Four sample pieces were cut, and subsequently 27 pieces for which the cutting width was measured. An important role in establishing the geometry of the slot and the conical have the cutting fronts created by the laser spot. As the rays leave at an angle of divergence, it follows that the vertical section through the material has the shape of a trapezoid with bases K s and K i , whose height is 8 mm. How each process parameter influences the cutting width is analysed using the statistical model of prediction and regression calculation. The laser beam exposed to the material for a long time heats the cutting area, achieving larger cutting widths than usual. The state of sudden heating and cooling of the part determines the appearance of a temperature gradient in the plate.
UNIOR 701 caliber (from Unior Tools manufacturer) was used to measure the slit at the straight side. In the experiment it was used to measure the cut through the material by probing, based on the pass-by-pass principle. Laser piercing is the first contact between radiation and material. A conical channel is produced, because the geometry of the laser beam has a conical appearance, while around it the cut edges are burnt by the oxidation reaction. With the help of a Celestron digital microscope, the plate channel was studied for parts 1 and 28 (replica of part 1), in which minimum values of the input parameters were used (Figure 3a,b).
The shape at the entrance of the channel is a circular surface, surrounded by melt. As the laser penetrates the material, the diameter of the bore decreases. The melt around the channel was removed from the slit at first on the top edge. There is melting on the bottom edge of the metal sheet due to the removal of hot drops on the bottom edge. The material is melted locally and cut due to the focused laser energy. radiation and material. A conical channel is produced, because the geometry o beam has a conical appearance, while around it the cut edges are burnt by the reaction. With the help of a Celestron digital microscope, the plate channel wa for parts 1 and 28 (replica of part 1), in which minimum values of the input p were used (Figure 3a,b). The spot of the laser beam produces in the material a liquid portion (melt) which is removed with the help of the assistant gas, thus forming the gap between the piece and the waste plate. The melt acquires an approximate spherical shape. Centrifugal, superficial and inertia forces act on the melt. Centrifugal force (Fcf) occurs due to heating and increased thermal agitation of the liquid melt. Surface forces (Fs) act to reduce the potential energy in the surface layer, keeping the melt to a minimum volume. The force of inertia (Fi) occurs as a result of the tendency to increase the liquid volume and the tendency of detachment of small droplets from the melt [33].
Heat accumulation helps to process the material by laser cutting. H400 steel has increased thermal resistance, reducing heat dissipation, which shows us a giant energy available in the processing area. The high energy density required by laser cutting of Hardox steels means increased energy consumption and thus reduced cutting efficiency and increased processing costs. Mainly the research methods include: CO 2 laser is suitable for cutting H400 steels, because the laser beam has a power of over 4 KW with an average and maximum level, good quality and high cutting efficiency; DOE is used in robust experiments of laser cutting; metal sheets and parts are researched to set Kerf to the right profile; the experimental design was run at three levels of cutting parameters resulting in 27 references; the measurement of Kerf responses was done with the slit by probing the slot based on the passing principle/does not pass; and the experimental data were mathematically and statistically processed using the RSM response surfaces given by the linear (L) and quadratic (Q) model.

Results
During the study, the cut parts and steel scrap plates were carefully analysed. The followed parameters were cutting width, dimensional accuracy and surface quality. The sequence consisted of checking the plates and the cut parts (surface, thickness and dimensions). The following conclusions were drawn:

•
The parts have unevenness at the entrance and exit of the laser, places where a portion with wrinkles affected by heat is formed at a distance of up to 3.22 mm, measured from the exit of the contour; • The quality of the cut surface is higher on the semi-circular profile compared to the linear profile. The cut surface has a concave appearance in the middle of the piece; • The surface of the part is damaged at the corners where the laser changes its cutting direction in the area of 90 • angles. On the side surfaces, the pieces have unevenness, more accentuated towards the corners. The position of the ridges on the cut surface is vertical and coincides with the direction of the laser beam. Some ridges/striations show bends due to slipping of the melt and resolidification of the surface. On the rectilinear sections of the linear contour of the parts, the surfaces are smooth with small irregularities. The upper part of the cut part has no molten material, which means a good setting of the cutting parameters, except for the area where the laser comes out of the worksheet (the lower part of the piece). This is due to the lower piercing speed of the laser at the exit of the material, which explains the formation of melt on the lower edge of the sheet. For the same reason, another cutting defect was observed on the cut surfaces, in the form of a notch, located between two ridges; • Analysing the stationary piercing on the upper face of the sheet, it results that the largest diameter of the perforation is at piece 8 (3.54 mm), for which the laser power was 4900 W, the assist gas pressure 0.55 bar and the cutting speed 1800 mm/min, while for the rest of the parts the penetration is very small (maximum 1 mm). Table 3 shows the cutting defects found on the cut parts, the values of the input parameters, and the value of the response of the cutting width, for the 27 pieces of the experimental plan. Parts 9 and 18 are largely affected by steeper and thicker unevenness and penetrations towards the bottom. In all cases, the parts have a small penetration at the lower level, about 0.75 mm. The metal sheet of Hardox expanded in thickness, where the laser acted, due to the heat flow that passes through the material. It has no melt deposited on the bottom edge, which means that the selection of the cutting parameters was correct. Dimensional measurements show differences, from part to part, due to heating, burning and deformation of the plate. The laser attacks the surface, and there is surface damage to the lower corners of the part. Due to the melting of the material, the surface of the part is not perfectly smooth. In the laser input and output areas there are high values of Ra roughness.
In order to obtain finished products with a smooth surface, free of unevenness and roughness, the parts must undergo further mechanical processing to remove the solidified melt. Setting the cutting parameters (laser power, gas pressure, cutting speed) to average values results in a minimum cutting width; 37% of the parts have a minimum cutting width of 0.30 mm. The parts in the third series were made at a temperature of over 100 • C, which led to an increase in cutting width. The evaluation of the cutting width was performed with the Statistics 7.0 program by analysing and interpreting the predictability model and determining the cutting width by the regression analysis method.
The experiment results are: 1. The parts were processed by laser cutting following the complete experimental factorial design (DOE); 2.
Series 1 of the experiment conducted at minimum laser power, with maximum cutting speed, has a higher cutting width, under the conditions of using the auxiliary gas at average to maximum values; 3.
Series 2 which uses an average power of 5000 W achieves a good cut with a qualitative aspect, without structural defect of the parts. The cutting width reaches the lowest value in six experimental cases. The combination of medium power, low pressure and medium speed indicates the best result of the cutting width. In addition, the average power combined with the average pressure and any value of the cutting speed, indicates a cutting width of 0.30 mm; 4.
If the laser power increases, it causes an increased energy density of the laser beam. The heat absorption in the steel sheet increases and the melt increases its volume, which determines a large cutting width; 5.
Series 3 indicates a generally increased cutting width involving high consumption and costs. The cutting width increases with the evolution of laser power up to 5100 W; 6.
The cutting width decreases if a laser spot with moderate energy is used. This causes a local heat that melts a very small volume of material and after a very short time it dissipates quickly through the material;

7.
If the cutting speed decreases, the time of interaction between the spot and the material increases, having as an effect a longer irradiation of the material, high heat absorption, increased melted volume and finally, the cutting width deteriorates; 8.
If the cutting speed is increased, the spot-part interaction time decreases, resulting in reduced heat absorption of the H400 plate and a decrease in the cutting width; 9.
If low assist gas pressure values are used, the cutting width is affected.
From the calculations, a cutting width of 0.37 mm is obtained, a good result that falls within the limits of the experimental data. Next, the individual influence of laser power and gas pressure on Kerf was studied. The graphs are built to find the dependence of the cutting width on the laser power. Series 1 was run at 4900 W in three references, 5000 W in three experiments and 5100 W in three cases, at the same time with the low pressure of 0.45 bar kept constant. Nine values for the cutting width resulted. The coefficient of determination R 2 = 0.33 is low. For series 2, the procedure was similar, slightly increasing the gas pressure to 0.50 bar (Figure 4).  The Pearson coefficient R 2 = 0.66 shows that the cutting width depends on 66% laser power. The functional relationship between the cutting width and the laser power is approximated by the polynomial: Kerf=5.0·E-0.6·x 2 -0.0498·x+124.4667. ( The best dimensions of the slot width are obtained at average values of laser power equal to 5000 W and cutting gas pressure of 0.50 bar. The speed between values of 1800 and 1900 mm/min ensures a better quality of the cut surface, smaller cutting width, if we consider an average laser power level 5000 W, and an average pressure of 0.50 bar. If the pressure is increased to 0.55 bar the results become unsatisfactory. Series 1 was chosen for all minimum levels of the independent parameters (4900 W; 0.45 bar; 1700 mm/min), at the average levels of the cutting parameters (5000 W; 0.50 bar; 1800 mm/min) and at the level of maximum input parameters (5100 W; 0.55 bar; 1900 mm/min). With the help of the Graph 4 program, the dependence of the cutting width was obtained depending on the assistant gas pressure and the functional relationship between them ( Figure 5). The minimum pressure is obtained using Fermat's theorem and is equal to 0.508 bar. The Karl-Pearson coefficient is equal to 1 which indicates that there is a strong link between the cutting width and the assist gas pressure. The parts manufactured by laser processing are geometrically characterized by a minimum width of 0.30, under the conditions of setting the input parameters at 5000 W, 0.50 bar and 1800 mm/min. The Pearson coefficient R 2 = 0.66 shows that the cutting width depends on 66% laser power. The functional relationship between the cutting width and the laser power is approximated by the polynomial: The best dimensions of the slot width are obtained at average values of laser power equal to 5000 W and cutting gas pressure of 0.50 bar. The speed between values of 1800 and 1900 mm/min ensures a better quality of the cut surface, smaller cutting width, if we consider an average laser power level 5000 W, and an average pressure of 0.50 bar. If the pressure is increased to 0.55 bar the results become unsatisfactory. Series 1 was chosen for all minimum levels of the independent parameters (4900 W; 0.45 bar; 1700 mm/min), at the average levels of the cutting parameters (5000 W; 0.50 bar; 1800 mm/min) and at the level of maximum input parameters (5100 W; 0.55 bar; 1900 mm/min). With the help of the Graph 4 program, the dependence of the cutting width was obtained depending on the assistant gas pressure and the functional relationship between them ( Figure 5). The minimum pressure is obtained using Fermat's theorem and is equal to 0.508 bar. The Karl-Pearson coefficient is equal to 1 which indicates that there is a strong link between the cutting width and the assist gas pressure. The parts manufactured by laser processing are geometrically characterized by a minimum width of 0.30, under the conditions of setting the input parameters at 5000 W, 0.50 bar and 1800 mm/min. The optimal cutting conditions are described by the variation of the cutting width as a function of the auxiliary gas pressure for H400 using the polynomial: For series 1 (laser power 4900 W), the measurements made on the cutting width highlighted three pieces with 0.30 mm, three pieces with 0.35 mm and three pieces with 0.40 mm. It is observed that under conditions of minimum gas pressure, laser power and speed, a maximum cutting width is obtained, and for the combination of minimum power, maximum pressure and speed a minimum cutting width (0.30 mm) results. Series 2 with pieces numbered from 10 to 18, has six pieces with minimum values of cutting width (0.30 mm), due to preheating of the sheet. Series 3 with parts 19 to 27 has a single piece with a cutting width equal to 0.30 mm (piece 25), because the sheet was heated during previous processing.
We therefore conclude that the parameters used in series 1 and 2 are indicated as a priority in the technological process of cutting in order to have a minimum cutting width, material savings, low energy consumption and implicitly low processing costs.
The input data needed to determine the cost of the laser manufacturing process were centralized in Table 4, with the prices being of the manufacturers. The study aims to determine the cost of the manufacturing process, which is of interest to manufacturers of such facilities, but especially to users. The first column of the table contains the cost elements identified in the processing. The second column indicates the calculation relationship. All costs were expressed in Euro/hour.  The optimal cutting conditions are described by the variation of the cutting width as a function of the auxiliary gas pressure for H400 using the polynomial: For series 1 (laser power 4900 W), the measurements made on the cutting width highlighted three pieces with 0.30 mm, three pieces with 0.35 mm and three pieces with 0.40 mm. It is observed that under conditions of minimum gas pressure, laser power and speed, a maximum cutting width is obtained, and for the combination of minimum power, maximum pressure and speed a minimum cutting width (0.30 mm) results. Series 2 with pieces numbered from 10 to 18, has six pieces with minimum values of cutting width (0.30 mm), due to preheating of the sheet. Series 3 with parts 19 to 27 has a single piece with a cutting width equal to 0.30 mm (piece 25), because the sheet was heated during previous processing.
We therefore conclude that the parameters used in series 1 and 2 are indicated as a priority in the technological process of cutting in order to have a minimum cutting width, material savings, low energy consumption and implicitly low processing costs.
The input data needed to determine the cost of the laser manufacturing process were centralized in Table 4, with the prices being of the manufacturers. The study aims to determine the cost of the manufacturing process, which is of interest to manufacturers of such facilities, but especially to users. The first column of the table contains the cost elements identified in the processing. The second column indicates the calculation relationship. All costs were expressed in Euro/hour. The range of variation of the cutting width allows the evolution of the processing cost between certain limits. The consumptions in the table are specific to the installation used for laser processing.
The analysis of the experiment shows a good arrangement of the block of parts. An important parameter used in cutting is the assist gas pressure. For this reason, an important result is the identification of the function of approximating the cutting width in relation to the oxygen gas pressure. In this case, the dependent variable is the cutting width. The initial function depends on the set of x i points, according to Table 5. The values considered were: (4900 W; 0.45 bar; 1700 mm/min), (5000 W; 0.50 bar; 1800 mm/min) and (5100 W; 0.55 bar; 1900 mm/min).  The Lagrange interpolation polynomial that corresponds to a functional relation f in nodes x 0 , x 1 , x 2 is given by the relation: The polynomial passes through the points (0.45; 0.40), (0.50; 0.30), (0.55; 0.35) being described by a parabola. The Lagrange interpolation polynomial is obtained from the basic Lagrange polynomials and the value of the function f at points x i . The mathematical expression has the following form: The interpolation approximation criterion presents the best possible approximation of the function f(x) by the interpolation polynomial L(x). The interpolation method establishes a functional link between the interpolation support consisting of the assisting gas pressure data set and the cutting width. The estimation error calculated as the difference between the actual function and the Lagrange function is 4.25%.
To calculate the external parameters of the laser beam, it is important to know the radiation strength, spot diameter and optical properties of the material. The physical phenomena that take place following the laser-material interaction are based on the transformation of laser energy into thermal energy. The increase in local temperature and the distribution of laser-induced heat change the thermal state of the metal by heating-meltingvaporization. The intensity of the incident radiation at the moment of penetration in the material is given by the relation: The intensity of incident radiation entering the material at depth x follows the relation [35]: where R is the coefficient of reflexion; A is the absorption coefficient. The temperature inside the material developed by the absorption of laser radiation is a parameter that indicates the heat input required for heating with phase transformations of the target until melting. The absorption coefficient for metals is 10-15% for the CO 2 laser wavelength of 10.6 µm [32]. The reflection coefficient depends on the wavelength; in the case of the CO 2 laser it is 0.9. Draganescu et al. indicated that at 0.2% C, the thermal conductivity is 39 W/m*K [33]. Thus, we obtain the values of the physical quantities studied given in Table 6. The dimensions of the target are larger in relation to the radius of the laser spot which generates a constant flow of energy while creating cuts of material, delimiting the slot. The cutting width dependence on the temperature and the incident intensity, under conditions of maximizing oxygen gas pressure and cutting speed, for the three levels of laser power used in the experiment are shown in Figures 6 and 7.
The quadratic regression model of the cutting width as a function of the incident intensity produced by the laser radiation at the entrance to the material has the expression: The second-order model of quadratic regression was developed for the cutting width by accessing data from independent experiments. The coefficient of determination R 2 was calculated to verify that the data anticipated by the regression model are appropriate.  The quadratic regression model of the cutting width as a function of the temperature produced by the laser in the material has the form: The quadratic regression model of the cutting width as a function of the incident intensity produced by the laser radiation at the entrance to the material has the expression: The second-order model of quadratic regression was developed for the cutting width by accessing data from independent experiments. The coefficient of determination R 2 was calculated to verify that the data anticipated by the regression model are appropriate. When using the Graph program, the coefficient of determination is 1, which means that The quadratic regression model of the cutting width as a function of the temperature produced by the laser in the material has the form: The quadratic regression model of the cutting width as a function of the incident intensity produced by the laser radiation at the entrance to the material has the expression: The second-order model of quadratic regression was developed for the cutting width by accessing data from independent experiments. The coefficient of determination R 2 was calculated to verify that the data anticipated by the regression model are appropriate. When using the Graph program, the coefficient of determination is 1, which means that the mathematical accuracy of the regression is the most appropriate. When the temperature and power density increase, an increase in the cutting width is observed. The cutting width decreases as the temperature in the material and the incident intensity decrease.
If the laser power increases, the cutting width is disturbed due to the energy density. The situation leads to a longer interaction time between the laser radiation and the substance, and the slit increases due to thermal erosion. Specifically, the cutting efficiency of the laser beam decreases with the increase of energy received from the laser, due to losses through thermal conduction. Kerf was evaluated, and the results show a section of the slit as a V-profile, almost straight edges, parallel or A-shaped. In most cases, the top width is larger compared to its size at the bottom edge. Moreover, a sufficient amount of laser energy is absorbed more intensely at the upper edge of the Kerf profile. This energy is transformed into heat, thermal energy that melts a very small portion of the material locally, strongly heats the cut surfaces by changing the metallographic structure of the surfaces, the local change of the material characteristics. The local heat generated in the material, in the area affected by the laser, can trigger chemical reactions very quickly. As a result of the thermal action of the laser and the chemical reaction under the influence of an oxygen jet, changes in the size of the cutting width occur, so that at the lower edge of the material, an increased Kerf results due to burning and melting of cut material. In the process of interaction of laser radiation with the substance there is a temperature gradient through the cut that determines the heat in the slot.
The diffusion of heat through the sheet is based on the fact that, under the influence of the laser pulse, the optical energy is instantly transformed into heat. The incident intensity of the laser beam decreases as it enters the material. The gradient of laser radiation intensity can be explained by the fact that the material is resistant, the layers of molten material have different temperatures and the accumulated heat is removed from the slit more difficultly. The temperature difference between the two surfaces of the plate explains that the melt loses mass as it discharges to the bottom edge. The range of variation of the radiation intensity has a higher temperature of the molten area on the surface of the material, and a lower temperature on the lower surface of the steel plate, resulting in a smaller melting area.
In this study, the cutting width was determined as a function of laser power, gas pressure, material temperature and the incident intensity of laser radiation. The measured results are represented graphically in Figures 3 and 4 showing a low Kerf at values close to 5000 W and gas pressures in the range of 0.47-0.48 bar. As can be seen from Figures 5 and 6, in the case of the assisting gas pressure of 0.55 bar and a speed of 1900 mm/min, Kerf is the lowest. The same result happens at a temperature of 6.25 × 10 4 K and a minimum incident intensity of 15.931 × 10 6 W/cm 2 . The Kerf cutting width compared to the laser power, the assisting gas pressure, the working temperature and the incident intensity for the H400 sheet with a thickness of 8 mm has a square shape. These curves have a maximum for Kerf processing at oxygen gas pressures and cutting speed under maximizing conditions and a minimum that was reached at selected cutting pressures and inputs at average values. The average cost is for the CO 2 laser installation applied to the 8 mm sheet for H400 at the value of 13.245 Euro/h. The function of approximating the cutting width according to the important cutting parameter, the low pressure of the assistant gas, run at three levels used in the experiment (0.45, 0.50, 0.55) bar is a Lagrange polynomial of quadratic order. The channel/cut is well formed during the O 2 laser cutting of the steel when the input parameters are set to medium values and low power densities that cause lower surface and material temperatures, the important role being played by the minimum thermal energy that forms melt of minimal geometric dimensions and moving on the side walls along the cutting front. The evaluation of the influence of the input factors, laser power and gas pressure, but also of the physical quantities detached from the laser melting on the slit showed that under laser processing conditions, the distribution of these inlets in the slot have different parabolic shapes. The interaction between the input factors can create a minimal melt that removed from the slot will ensure a small cutting width between the piece and the sheet. There is a good agreement between the experimental model and the calculated one of the assistant gas pressure.

Linear Predictive Model
The linear predictive model shown in Figure 8a shows that, during the cutting of the parts, the laser power was progressively changed to the values of 4900 W, 5000 W and 5100 W. A set value of the laser power outside the range of 4900-5100 W, indicates an increase in cutting width. The simultaneous variation of two parameters of influence (laser power, auxiliary gas pressure) on the cutting width, determines the most appropriate influence of the predictive factors if the level of the cutting speed is maintained at a constant value. The linear prediction graph rendered by the RSM method shows a 2D surface with the interaction between the laser power and the assistant gas pressure. The cutting width can be evaluated, following the interaction between two influencing factors, as follows:

Linear Predictive Model
The linear predictive model shown in Figure 8a shows that, during the cutting of the parts, the laser power was progressively changed to the values of 4900 W, 5000 W and 5100 W. A set value of the laser power outside the range of 4900-5100 W, indicates an increase in cutting width. The simultaneous variation of two parameters of influence (laser power, auxiliary gas pressure) on the cutting width, determines the mos appropriate influence of the predictive factors if the level of the cutting speed i maintained at a constant value. The linear prediction graph rendered by the RSM method shows a 2D surface with the interaction between the laser power and the assistant gas pressure. The cutting width can be evaluated, following the interaction between two influencing factors, as follows: The linear prediction graph anticipates that the best results of the cutting width are obtained at low values of the assist gas pressure (0.45-0.48 bar) with values of the laser power in the range (4980-5040 W). The average value of the laser power leads to a better absorbability of the laser energy by the material, small amount of molten material, optimal heat distribution efficiency and low processing cost. A low value of the laser power negatively influences the melting process.
The linear mathematical model (Figure 8b) for the cutting width is given by the regression calculation in case of the interaction between the laser power (P) and the assistant gas pressure (p) by the relation: In the ANOVA linear regression function, the interaction effect of the laser power term is higher than that of the assisting gas pressure (0.1111). It means that the most significant factor in determining the cutting width is the laser power. The positive sign indicates in the linear equation that the laser power is an influencing factor that determines the increase of the cutting width and the minus sign shows that the gas pressure acts in the direction of decreasing Kerf. The interaction of laser power and cutting gas pressure will change the geometry produced in the slit; the two independent factors optimized validate the quality of Kerf. Regression analysis studies the effect of each controllable factor on the Kerf response during laser cutting. This demonstrates that the laser parameters used in cutting have an influential effect on the results of the experiment. The line graph in Figure 8b shows the following: The cutting width increases to values close to 0.34 mm when the gas pressure is maximum 0.55 bar and the laser power increases to a maximum value of 5100 W. Increasing the density of the energy flow contributes to the increase of the melting mass, the heat entering the material increases, which is why the width of Kerf increases; • There is a similarity between the prediction and the linear regression model at gas pressure values of 0.52 bar at the same time as the laser power of 5000 W. The response surface graph for the linear regression model is a flat surface describing the cutting width perturbation. There are differences for average values of laser power and low pressure between the anticipated and the calculated model. Such differences occur due to the deviation of the values from the measurements compared to the average value. A possible cause may be the degree of heating of the steel plate. Another cause may be the low speed level, which causes a longer irradiation time of the steel plate, having the effect of increasing the cutting width. Increasing the cutting speed to the maximum level causes a short irradiation time and a lower heat absorption, and finally a minimum cutting width.
There is a similarity between the prediction and the linear regression model at gas pressure values of 0.52 bar and laser power of 5000 W. The regression model is different from the anticipated one due to the estimation of the cutting width. Possible causes would be technical, standard error, standard deviation, plate temperature gradient, pressure gradient and melt mass. The mathematical model more accurately estimates the width cut by its small variations and errors to an average value. The predictive model indicates lower values of the cut width due to the correlation between the laser energy and the heat flow distribution through the material at high values of the cutting speed. The disturbed values of the cutting width are obtained when the values of the laser power are antagonistic to those of the assist gas pressure. The two investigated models lead to the same value of the cutting width <0.34 mm, a good agreement due to the influence factors set at values close to the environment.

Quadratic Predictive Model
The 3D diagram in Figure 9 provides a clear picture of how the prediction factors, laser power and gas pressure affect the cutting width of Hardox 400 steel parts. It is observed that the smallest values of cutting width are obtained when the laser power is 5000 W, and the assist gas pressure has a low value located in the range 0. flow distribution through the material at high values of the cutting sp values of the cutting width are obtained when the values of th antagonistic to those of the assist gas pressure. The two investigated same value of the cutting width <0.34 mm, a good agreement due to t set at values close to the environment.

Quadratic Predictive Model
The 3D diagram in Figure 9 provides a clear picture of how the laser power and gas pressure affect the cutting width of Hardox 4 observed that the smallest values of cutting width are obtained whe 5000 W, and the assist gas pressure has a low value located in the rang values increase with the distance (somewhat circular, semi-ellipt characterized by average power values and low pressure values. The h cutting width (over 0.38 mm) are obtained, on the one hand, for sma power, 4900 W, at the same time with increased values of the cutting g 0.55 bar, and on the other hand, at high laser power values 5100 W and of 0.50 bar. Specifically, the best cutting width (0.30 mm) is obtained for lase auxiliary gas pressure 0.46 bar. For the response confidence interval 0.26-0.28 mm), the graph shows values of the laser power between 4 the same time as the gas pressure between 0.45 and 0.48 bar. Th combines the shape of a classical paraboloid (in the centre) with a hy (at the extremes) and shows that the cutting width has a variation Gaussian bell, with the tip on the average axis of laser power. If maintained at average values and the gas pressure increases, the bell that the cutting width increases. The predicted graph indicates a sign the input parameters (power and pressure) on the cutting width usin The estimated square model of the cutting width, depending on and the assist gas pressure, using the regression technique is represen polynomial in Figure 10  Specifically, the best cutting width (0.30 mm) is obtained for laser power 5000 W and auxiliary gas pressure 0.46 bar. For the response confidence interval of ±1 mm (width = 0.26-0.28 mm), the graph shows values of the laser power between 4980 and 5020 W, at the same time as the gas pressure between 0.45 and 0.48 bar. The response surface combines the shape of a classical paraboloid (in the centre) with a hyperbolic paraboloid (at the extremes) and shows that the cutting width has a variation of the shape of the Gaussian bell, with the tip on the average axis of laser power. If the laser power is maintained at average values and the gas pressure increases, the bell rises, which means that the cutting width increases. The predicted graph indicates a significant influence of the input parameters (power and pressure) on the cutting width using the RSM model. The estimated square model of the cutting width, depending on the laser power and the assist gas pressure, using the regression technique is represented by the polynomial in Figure 10 Kerf = 89.5315 − 0.0357·x − 0.03889·y + 3.6111·E − 6·x·x − 0.0008·x·y + 4.4444·y·y, (11) The term of the square laser power effect is greater than the term pressure effect with the experimentally used data. It results that the the laser power. The term containing the square of the laser powe means that the dominant effect of the laser power is to increase th response, while the positive sign of the term containing the square of that the dominant effect of the second influencing factor, gas p increasing. Furthermore, it can be seen that the important factors tha other affect Kerf. From this identification it is found that the most infl kerf is the laser power, and the second significant factor is the assis coefficient of the model is 89.5315, the correlation coefficient of the laser power and pressure is 0.0008, which indicates an effect conj reduction influence, and the linear correlation coefficients of laser pow are low which shows a decrease Kerf take together with the level of in By analysing Figure 9 the following aspects were deduced: • The cutting width is a quadratic surface, resulting from the intera power and auxiliary gas pressure; • The low value of the cutting width, below 0.32 mm, is obtained w pressure is 0.50 bar, and the gas pressure 5000 W; • The shape of the Kerf variation in the RSM model is a parabo quadratic surface that indicates a more pronounced influence of t the gas pressure. The Kerf graph depending on the laser power is compared to the graph representing Kerf depending on the c which is less deformed, that is a curve less pronounced; Figure 10. Graph of the quadric dependence of the cutting width on the laser power and the assist gas pressure.
The term of the square laser power effect is greater than the term of the assistant gas pressure effect with the experimentally used data. It results that the significant factor is the laser power. The term containing the square of the laser power is positive, which means that the dominant effect of the laser power is to increase the value of the Kerf response, while the positive sign of the term containing the square of the pressure shows that the dominant effect of the second influencing factor, gas pressure, is of Kerf increasing. Furthermore, it can be seen that the important factors that interact with each other affect Kerf. From this identification it is found that the most influential factor on the kerf is the laser power, and the second significant factor is the assist gas pressure. The coefficient of the model is 89.5315, the correlation coefficient of the interaction between laser power and pressure is 0.0008, which indicates an effect conjugated with a Kerf reduction influence, and the linear correlation coefficients of laser power and gas pressure are low which shows a decrease Kerf take together with the level of independent factors. By analysing Figure 9 the following aspects were deduced: • The cutting width is a quadratic surface, resulting from the interaction between laser power and auxiliary gas pressure; • The low value of the cutting width, below 0.32 mm, is obtained when the cutting gas pressure is 0.50 bar, and the gas pressure 5000 W; • The shape of the Kerf variation in the RSM model is a paraboloid representing a quadratic surface that indicates a more pronounced influence of the laser power than the gas pressure. The Kerf graph depending on the laser power is steeper and longer compared to the graph representing Kerf depending on the cutting gas pressure which is less deformed, that is a curve less pronounced; • The damaged values of the cutting width, over 0.38 mm, are obtained at 5100 W laser power and 0.45 bar gas pressure; • From the spectral analysis of the colors (green to red) corresponding to the cutting width, there is an increase from the set values (average power and pressure) to the extremities; • Comparing the quadratic model with the prediction given in Figure 9, we find that the minimum cutting width moves from minimum values of gas pressure to average values. The agreement between predictability and the statistical mathematical model for laser power is good, but there are significant differences in gas pressure. The explanation can be attributed to the increase in gas flow that increases the contact surface so that the cutting width increases. As the cutting gas pressure decreases, the area affected by the gas decreases and the cutting width is minimized. The gas jet is high (length at the outlet of the nozzle) when the pressure increases, the material melts in larger quantities, which leads to an increase in the cutting width, while an average jet of gas affects the steel plate less.
The variation of the laser power has as effect the change of temperature and implicitly of the viscosity of the melt. In the case of very narrow cuts, the operation of removing the melt is more difficult. The cutting gas pressure is influenced by the length of the gas flow, which determines a cutting force exerted on the cut surface. Changing the assistant gas flow has effects on Kerf geometry. The low cutting speed causes a significant accumulation of laser energy in the cutting area, which implies a larger cutting width. The cutting width on the top side is larger than the one on the bottom side as it is closer to the laser spot and captures a larger amount of energy. The heat is transmitted inwards with a negative heat gradient. The cutting width on the lower side is larger than on the upper side due to changes in the cutting parameters. There is a pressure gradient towards the outlet, as the amount of heat absorbed increases. Cylindrical cases are rare and depend on the structure of the material. The geometry of the beam changes in the material due to the section variation. The cut in the material is U-shaped due to the decrease of the transmitted energy, so that, at the bottom, the molten material is stationary. As the beam advances in the material it loses energy, so at certain depths the melting time is different.The cutting surface is parabolic, concave and test-tube-bottom shaped. Laser power is a physical quantity that influences the density of energy absorbed by the material. Energy density is closely related to power density and interaction time. If the laser power remains constant, the laser intensity in the material varies with the change of section. Oxygen gas pressure can influence the cutting width due to gas flow, gas flow length and nozzle diameter. The combination of laser power-gas pressure assistant can improve the cutting width.
The surface methodology of the Kerf response was developed and influenced by the laser power and the assist gas pressure. Graphs with response areas were obtained for the linear (L) and quadric (Q) models to predict and calculate the global Kerf. Laser power and gas pressure were chosen on the X and Y axes. The Kerf response for the straight profile is made on the Z axis. The prediction graph (L) due to the effects of the interaction between laser power and gas pressure is a curved flat surface. The linear shape of the Kerf answer is given by Equation (10). The graph (L) resulting from the mathematical modeling of the answer is a linear surface indicating the Kerf force. In conditions of average power and average pressure Kerf reaches the value of 0.34 mm. There is a good agreement between the prediction and the linear mathematical model for average values of laser power and gas pressure. The Kerf prediction graph contains the interaction effects of the laser power and the assist gas pressure. Kerf decreases sharply at average values of 5000 W of laser power compared to the average values of gas pressure, but also at minimum laser power with maximum gas pressure. The Kerf response surface contains several interaction effects due to input factors, and the surface area reaches the Kerf value. The prediction graph (Q) is a curved area at maximum values of laser power and gas pressure. The Kerf minimum is achieved at sensible variations compared to the average level of laser power and low gas pressure. The developed mathematical RSM (Q) model shows that the average gas pressure and the average laser power have a Kerf size reduction effect. The curve due to the effects of laser power is steeper than due to the effect of working gas pressure, which means that laser power had a greater effect in reducing Kerf, being the most significant parameter. The gas pressure had a lower effect in terms of Kerf size compared to laser power. These quadratic models of predictability and regression can reduce the cost of the experiment and the working time. The minimum Kerf < 0.32 mm is obtained at p = 5000 W and the pressure of 0.45 bar, and the maximum Kerf > 0.38 mm results at the maximum power of 5100 W and the cutting gas pressure equal to 0.45 bar. The quadratic model is more complete than the linear model because it contains quadratic interactions of process parameters, linear interactions, and interactions of each type, so it is possible to obtain a better cutting width for Kerf in the case of the straight cut profile. Square RSM (Q) graphs predict and estimate Kerf for average values of laser power and are significantly different for cutting gas pressure due to instability of cutting flow. In any case, maximised laser power and gas pressure damage Kerf due to the accumulation of caloric energy, and the increased gas flow maximises Kerf at minimum values of the energy received from the laser. Kerf is optimized when the technical characteristics chosen are the gas pressure in the range (0.44-0.52 bar) at the same time with the laser power around (4920-5080 W). The quadric model is a restricted mathematical analysis model that requires that the parameters of studied cutting, laser power and gas pressure tend to the average values used in the experiment. As there is relatively good comparative agreement between prediction (Q) and regression (Q), it is possible that other external factors influence the process: temperature in the material, heat gradient, state of the material and chemical composition.
Statistical models were developed to validate the Kerf regression equations (linear and quadratic). The effect of each input parameter, the interaction between the parameters, the standard deviation, the Student's t-test and the probability of error are presented in Table 7. From Table 7 provided by the Statistics 7.0 program results: the coefficient of determination R 2 = 0.74211, the adjustment coefficient Adj = 0.16184 and the standard deviation STD = 0.01122. The average cutting width is 0.348 mm resulting from a complete factorial experiment with 27 trials. There is a 7421% chance that the influencing factors and their interactions will determine the cutting width. The adjustment coefficient helps to detail the process and the influence of the independent parameters. The normal distribution of the cutting width is within a maximum of two standard deviations from the central mean (media): cnf. limit (-95%) = µ-2σ = 0.322 mm and cnf. limit (+95%) = µ + 2σ = 0.374 mm. The Student's t-test (t) equal to 31.01196 and the probability p < 0.05 (corresponding to the average, on the first line of the table) show that the relationship between the influencing factors and the cutting width is appreciable. The value distribution of the cutting width is normal, the distribution graph is plotted by the Gaussian curve, and the maximum height is the arithmetic mean µ = 0.348 mm.
For verification, the initial experiment was replicated four times, at equal intervals. The average cutting width for each replica was calculated. The following values were obtained: µ 1 = 0.335 mm, µ 2 = 0.338 mm, µ 3 = 0.317 mm, µ 4 = 0.348 mm. Notice that replica 3 has the best average. For the 3rd replica we have: ∑(X i −µ 3 ) 2 = 0.045883, standard deviation: σ 3 = 0.0420, and t calc = µ 3 −µ The t-test parameter of the Student distribution belongs to the critical region, and the H 0 hypothesis is rejected, so that the average cutting width of the initial design differs significantly from the average of three replicates. In conclusion, there is a statistically significant difference between the two averages. In the case of reply 4, an uncontrolled disturbing factor intervened, which altered to some extent the experimental results. Table 7 uses the significance of the indices: (1) laser power, (2) gas pressure, (3) cutting speed. Q and L also refer to the term square and linear. 1L by 2Q means the influence of linear power combined with square gas pressure. The effect determines the correlation coefficient of the shear parameters in determining the polynomial that describes the Kerf answer. The parameter of the Student's t-test distribution belongs to the critical region, and the H 0 hypothesis is rejected, so that the average cutting width of the initial design differs significantly from the average of three replicates. In conclusion, there is a statistically significant difference between the two averages. In the case of reply 4, an uncontrolled disturbing factor intervened, which altered to some extent the experimental results. Table 8 uses the significance of the indices (1) laser power, (2) gas pressure, (3) cutting speed. In addition, Q and L refer to the square and linear term. 1L by 2Q means the influence of linear power combined with square gas pressure. The effect determines the correlation coefficient of the cutting parameters in determining the polynomial that describes the Kerf answer. Table 8. Influence of laser power and assisting gas pressure at CO 2 laser cutting. The developed regression models have acceptable values of standard deviation. Due to the high standard error, the probability of error is high. The probability p > 0.05 shows that the terms of the model are not significant ( Table 8). The statistical table reduced after the comparison p > t, to establish the significance of each influencing factor and the interactions between them, shows that the input parameters randomly influence the cutting process. In Table 8 the project has no interaction with significant influence on the Kerf response. The experimental data are adequate for the regression model. The correlation model was used to determine the most influential input parameter on Kerf. In this study the linear and quadratic regression model is the most appropriate. The graphs show the effect of the interaction between the influencing factors, the laser power and the cutting gas pressure in establishing the Kerf variation.

3.
The incident laser intensity, the working temperature and the laser intensity at the output of the material are physical quantities analytically determined; 4.
The quadratic prediction shows that a cutting width of 0.3 mm is obtained at the laser power inlet level in the range (4980-5020 W) and the cutting gas pressure in the range (0.47-0.51 bar); 5.
Contrary to prediction, the square regression response surface model indicates a cutting width <0.32 mm, if the laser power is 5000 W and the assisting gas pressure is 0.5 bar. A relatively good agreement was obtained between the predictive model and the regression mathematical model; 6.
The regression graph, indicated by the RSM response area, shows a Kerf value affected as the laser power is 5100 W and the gas pressure in the range (0.46-0.48 bar), but also in the case of laser power of 4900 W and low gas pressure of 0.45 bar, resulting in a Kerf >0.40 mm. It is observed that the edges of the laser power adjustment range at the same time with low gas pressure indicate a negatively affected Kerf; 7.
Opposite extreme values, laser power and gas pressure, increase the width of the Kerf; 8.
The plane projection shows at quadratic prediction an increase of Kerf according to the Gaussian curve in Figure 9, and in the quadratic regression model after a disk as in Figure 10; 9.
The term laser power, in the linear (Equation (10)) and quadric (Equation (11)) polynomials, has the higher effect showing that laser power is the most influential input factor; 10. The prediction linear model of the cutting width is in relative agreement with the calculated polynomial model, the laser power being the most significant parameter in determining the cutting width. The calculated linear model indicates a Kerf of 0.33 mm for the power of 4900 W and the gas pressure of 0.45 bar. The differences between the linear and quadric result are due to the heating of the material during processing; 11. The quadric model is more accurate because it takes into account the interactions between laser power and auxiliary gas pressure, at a constant level at the cutting speed. It also takes into account the combined action of the parameters on Kerf, while the linear model takes into account the independent action of one factor or the other; 12. Pressure is the second significant factor in relations (Equations (10) and (11)). This influences the cutting process through the pressure gradient that eliminates the melt, hot drops and heat transfer through the slot; 13. High power causes an increased power density, which induces a higher amount of heat in the material, resulting in increased Kerf.
Response surface models for the evaluation of the Kerf cutting width at the straight profile using the full factorial design L27 were considered appropriate. The empirical data developed are used to predict and calculate the global mean of the Kerf response using the linear (L) and quadric (Q) response area model. From the response graph (Q) it could be seen that the laser power had a more pronounced effect in reducing the Kerf size compared to the pressure. To obtain a small Kerf it is necessary to select an average value of the gas pressure observed using the regression model (Q). In the case of the calculated linear model (L) it is observed that a low Kerf is obtained at the low value of the laser power and the increased gas pressure. These models can be used successfully to anticipate Kerf at the right profile in the case of CO 2 laser cutting of the H400 sheet. The RSM model can be used to predict Kerf under the influence of other cutting parameters to optimize Kerf at the right profile. A minimum straight profile Kerf of 0.33 mm is obtained when cutting parameters such as gas pressure and laser power are maintained at 0.55 bar and 4900 W, as indicated by model (L). A minimum kerf of 0.30 mm can be obtained when we maintain the laser power at 5000 W and the cutting gas pressure at 0.50 bar. As a result, we propose to use the combination of values: laser power p = 5000 W, auxiliary gas pressure p = 0.50 bar at constant cutting speed v = 1900 mm/min to obtain a fine cut.