Study on the Basic Performance Deterioration Law and the Application of Lead Rubber Bearings under the Alternation of Aging and Seawater Erosion

: Lead rubber isolation bearings are well-recognized as a common and effective means to mitigate the seismic responses of bridges. However, rubber isolation bearings used in offshore bridges are extremely vulnerable to the action of the alternation of aging and seawater erosion caused by weather conditions, wind, waves, and other factors. Meanwhile, the deterioration law and application of lead rubber bearings subject to the effect of aging and seawater erosion cycles are not clear. Thus, aging and seawater erosion cycles testing on both lead rubber isolation bearings (LRB) and rubber materials were carried out. The parameters for the Mooney–Rivlin model of the rubber material used in LRBs were determined and the time-varying law of basic performance of LRBs was obtained based on test results of LRBs and their rubber material. Then, the determined rubber material parameters were applied into the ﬁnite-element model of LRBs to verify the basic performance degradation law of the LRBs. Finally, the obtained basic performance degradation law of LRBs was substituted into the ﬁnite model of offshore bridges to investigate the impact of the property degradation of LRBs on their seismic performance. The time-varying law of seismic performance of offshore bridge structures was also studied based on ﬁnite element analysis. The results show that both the horizontal and vertical stiffness of LRBs increase with the alternating of aging and seawater erosion time, and the horizontal and vertical stiffness increase by 16.1% and 24.3%, respectively, during the 120-year service period. Additionally, the Mooney–Rivlin model parameters of the LRB rubber material are also signiﬁcantly affected by the alternating of aging and seawater erosion. Additionally, the results also indicate the deterioration of LRBs has a great inﬂuence on the anti-seismic performance of offshore bridge structures. After 120 years of service of offshore bridge isolation bearings under the alternating of aging and seawater erosion, the maximum displacement of the pier top of the offshore bridges, the maximum bending moment at the pier bottom, and the maximum displacement of the rubber bearing increased by 14.2%, 6.6%, and 9.1%, respectively. The ﬁndings of this paper play an important role in the seismic behavior study and the life-cycle performance analysis of offshore trafﬁc projects such as sea-crossing bridges in marine environments. At the same time, they also lay a theoretical foundation for the performance analysis of rubber isolation bearings and offshore bridge structures under the alternation of aging and seawater erosion cycles.


Introduction
In recent years, the construction of offshore transportation engineering such as seacrossing bridges has become increasingly prosperous. More and more sea-crossing bridges have adopted the relatively mature rubber isolation technology, such as the Hong Kong Zhuhai Macao Bridge opened in 2019. Natural rubber isolation bearings (LNR), high damping rubber isolation bearings (HDR) and lead rubber isolation bearings (LRB) are the most commonly used rubber bearings in bridge isolation. Among them, lead rubber bearings are the most widely used. In view of the long coastline of China, and because rubber isolation bearings for sea-crossing bridges will remain in challenging ocean environment for the long term, they are easily subjected to the aging and seawater erosion cycles caused by factors such as weather, rain, waves, tides, wind, and so on. This effect mentioned above may lead to the deterioration or even failure of rubber isolation bearings, which may threaten the seismic safety of offshore bridges or sea-crossing bridge structures. Therefore, exploring degradation laws and the application of lead rubber isolation bearings under the aging and seawater erosion cycles plays an important role in the decision making and performance evaluating of the isolation scheme for offshore bridges.
At present, there are many reports on the basic performance and aging performance of rubber bearings at home and abroad, but there are few reports on the basic performance and application of lead rubber isolation bearings under the alternating action of aging and seawater erosion. Both systematic experimental research on the mechanical properties of bridge high damping bearings and comparative tests on the mechanical properties of the rubber bearings of different bridges have been conducted by Shen Chaoyong et al. [1,2], and the fitting empirical formulas for the mechanical properties of HDRs and LRBs were given in the two papers. Akihiro [3] studied the mechanical behavior of rubber bearings through finite element analysis and put forward an evaluation method for natural rubber bearings' mechanical performance. A comparative test on the accelerated deterioration of laminated rubber isolation bearings and rubber sheets has been conducted by Xu Bin et al. [4], and the change law of horizontal stiffness was obtained after 80 years of service at 20 • C ambient temperature. Y Itoh et al. [5][6][7][8][9] carried out a series of experiments on natural rubber bearings, high damping rubber bearings, and rubber materials; they also predicted the performance degradation model of high damping rubber bearings and analyzed the internal aging law of natural rubber bearings. Wang Jianqiang et al. [10,11] studied the impact of compression stress and shear strains on the shear properties of HDRs and LRBs at room temperature, and then put forward the empirical formula for the correlation between the shear performance of HDRs and LRBs and shear strain and compressive stress. In order to reduce the seismic excitations of bridge structures, Li et al. [12] designed and processed a high damping rubber bearing and studied its mechanical properties. The research results provide a basis for the shaking table test of a continuous beam bridge with high damping rubber isolation bearings. Accelerated-aging tests and finite element simulation on lead rubber bearings were conducted by J. Park et al. [13], and the aging performance coefficient of lead rubber bearings was also studied. Kalpakidis V. I. et al. [14,15] proposed a theoretical method to predict the characteristic strength and dissipation capacity of lead rubber bearing over time. Takenaka Y. et al. [16] studied the thermo-mechanical interaction effect of the laminated rubber bearings under larger and more cyclic lateral movement, and then conducted dynamic tests on full-size and scaled rubber bearing specimens under sinusoidal and seismic response displacement input to verify their damping characteristics when affected by temperature rise.
In addition, the present research on the seismic behavior of offshore bridges is mostly concentrated on the seismic performance of bridge structures or main components under the condition of pier deterioration and material deterioration. The probabilistic timevarying nonlinear static analysis method of structural systems was used by Biondini [17] to investigate the seismic performance of bridge structures based on the randomness of erosion processes and the uncertainty of material and geometry. Alipour et al. [18] studied the probability of seismic risk considering chloride ion corrosion and the degree of structural degradation during the service period for reinforced concrete highway bridges. Kobayashi et al. [19] studied the seismic performance degradation of reinforced concrete beams under chloride ion erosion environment. Choe et al. [20] investigated the impact of performance degradation of reinforcement materials on the seismic performance of bridges. The results showed that the corrosion of reinforcement materials reduces the seismic performance of bridge structures. Gosh J. et al. [21] conducted a vulnerability study of bridge structures under the condition of corrosion of the bearings and pier reinforcement materials. Zhao Guifeng et al. [22] studied the seismic performance of Hong Kong Zhuhai Macao Bridge in the whole service life under the condition of deterioration of the friction pendulum bearings. Chen Jiajia et al. [23] carried out the research on the time-varying vulnerability of offshore isolated bridges based on the aging time-varying law of natural rubber bearings. Farhangi and Karakouzian [24] studied the structural responses of glass-fiber-reinforced polymer (GFRP) tubes filled with regenerated concrete material to develop compound piles, and which can be used as a substitute for traditional steel reinforced piles in bridge foundations. They additionally indicated that, according to the curve interaction diagram, the combination of pipe wall thickness and GFRP fiber content can meet the required axial and flexural bearing capacity of piles in different eccentricity ranges. Additionally, a new anti-seismic abutment with high-capacity wing walls was presented and analytically studied by Mitoulis et al. [25], and the earthquake-resistant behavior of the proposed anti-seismic abutment was evaluated by utilizing a benchmark bridge. The results showed that the proposed unconventional design is reliable. Nutt et al. [26] used AASHTO division I-A to compare the typical bridge columns with and without abutment in seismic design and raised AASHTO LRFD provisions.
To sum up, most of the comparative studies on bearing performance do not consider the influence of the marine environment, and most of the durability studies focus on aging performance. There are few studies on the time-varying law of the performance degradation of rubber isolation bearings and few reports on the influence of the marine environment such as the effect of aging and seawater erosion cycles or marine erosion on the performance of bridge rubber bearings. Comparative study on the degradation of lead rubber isolation bearings is rarer. Now, the influence of performance degradation of lead rubber bearings on the seismic performance of bridge structure is not clear. In order to study the influence of the alternating of aging and seawater erosion on the performance degradation law of lead rubber isolation bearings and the time-dependent law of seismic performance of offshore isolation bridges under the condition of bearing degradation, the research group carried out a seawater dry-wet cycle test and an aging and seawater erosion test of bridge natural rubber bearings, high damping rubber isolation bearings, and their rubber materials [27][28][29][30], and the change law of rubber material and bearing performance was also revealed in references [27][28][29][30]. In this paper, an age and seawater corrosion alternating test on LRBs and their rubber materials was carried out, and the time-dependent law of LRB rubber material parameters was fitted and calculated according to the relevant data. Then, this was verified by the finite-element analytical method, and the time-variable law of the horizontal and vertical stiffness ratio of lead rubber isolation bearings under aging and seawater erosion cycles is summarized. Finally, the time-varying rule of seismic performance of an offshore isolation bridge was analyzed based on the performance degradation law of lead rubber bearings. The research results provide a good theoretical basis for seismic isolation design, life-cycle seismic performance evaluation, and the usage and maintenance of cross-sea bridges and other ocean engineering in future, and can also provide a theoretical basis for exploring the impact of bridge support performance degradation on the full life-cycle seismic behavior of marine engineering structures such as cross-sea bridges. It is of great significance for us to better understand the performance degradation of rubber isolation bearings and the deterioration law of the structural performance of isolated bridges in marine environments.

Overview of the Age and Seawater Alternating Corrosion Test on Lead Rubber Bearings
Considering the weather ratio of the top ten coastal cities in China and the possibility of the alternation of aging and seawater corrosion caused by sea breeze, sea wave, sea tide, and so on [27,29], the research group carried out an aging and seawater corrosion cycles test on natural rubber isolation bearings, high damping rubber bearings, and their rubber materials. The aging and seawater corrosion cycles test was carried out on the lead rubber bearing and its rubber material in this paper, to investigate the performance deterioration law of LRBs and their rubber material and to also explore its influence on the seismic performance of offshore bridge structures. This can lay a foundation for a more systematic understanding of the deterioration law of the performance of different bridge isolation bearings under the alternation of aging and seawater corrosion. The parameters of LRBs, test parameters, and working conditions are shown in Tables 1 and 2. The layout of test samples is shown in Figure 1. The sketch of the bearing and the photograph of the location in the actual structure are shown in Figures 2 and 3.

Overview of the Age and Seawater Alternating Corrosion Test on Lead Rubber Bearings
Considering the weather ratio of the top ten coastal cities in China and the possibility of the alternation of aging and seawater corrosion caused by sea breeze, sea wave, sea tide, and so on [27,29], the research group carried out an aging and seawater corrosion cycles test on natural rubber isolation bearings, high damping rubber bearings, and their rubber materials. The aging and seawater corrosion cycles test was carried out on the lead rubber bearing and its rubber material in this paper, to investigate the performance deterioration law of LRBs and their rubber material and to also explore its influence on the seismic performance of offshore bridge structures. This can lay a foundation for a more systematic understanding of the deterioration law of the performance of different bridge isolation bearings under the alternation of aging and seawater corrosion. The parameters of LRBs, test parameters, and working conditions are shown in Tables 1 and 2. The layout of test samples is shown in Figure 1. The sketch of the bearing and the photograph of the location in the actual structure are shown in Figures 2 and 3.

Overview of the Age and Seawater Alternating Corrosion Test on Lead Rubber Bearings
Considering the weather ratio of the top ten coastal cities in China and the possibility of the alternation of aging and seawater corrosion caused by sea breeze, sea wave, sea tide, and so on [27,29], the research group carried out an aging and seawater corrosion cycles test on natural rubber isolation bearings, high damping rubber bearings, and their rubber materials. The aging and seawater corrosion cycles test was carried out on the lead rubber bearing and its rubber material in this paper, to investigate the performance deterioration law of LRBs and their rubber material and to also explore its influence on the seismic performance of offshore bridge structures. This can lay a foundation for a more systematic understanding of the deterioration law of the performance of different bridge isolation bearings under the alternation of aging and seawater corrosion. The parameters of LRBs, test parameters, and working conditions are shown in Tables 1 and 2. The layout of test samples is shown in Figure 1. The sketch of the bearing and the photograph of the location in the actual structure are shown in Figures 2 and 3.      (1) Horizontal stiffness; (2) Vertical stiffness.
Buildings 2023, 13, 360 6 of 21 It can be seen from Table 2 that one test day on an LRB is approximately equivalent to its service in the actual environment for one year. Therefore, test time (days) in this paper can be directly converted into the actual environment service time (years).

Basic Performance Test Results of Lead Rubber Bearings under the Alternation of Aging and Seawater Corrosion
A 120-day alternating test of aging and seawater corrosion for LRBs and their rubber materials were conducted in this paper. The performance of LRBs and their rubber materials were tested termly in the test process, to investigate the time-varying rule of their mechanical properties. The test method and contents of bearing performance are referred to in [31][32][33], and the horizontal and vertical stiffness of LRBs were tested on a 500-ton tensile-compression-shear comprehensive testing machine; see Figure 4. This laid the foundation for the application of the deterioration law of LRBs. The appearance changes of the LRBs before and after the test are shown in Figure 5. According to the rest results, the variation law of horizontal equivalent stiffness and vertical stiffness is shown in Figure 6.

Basic Performance Test Results of Lead Rubber Bearings under the Alternation of Aging and Seawater Corrosion
A 120-day alternating test of aging and seawater corrosion for LRBs and their rubber materials were conducted in this paper. The performance of LRBs and their rubber materials were tested termly in the test process, to investigate the time-varying rule of their mechanical properties. The test method and contents of bearing performance are referred to in [31][32][33], and the horizontal and vertical stiffness of LRBs were tested on a 500-ton tensile-compression-shear comprehensive testing machine; see Figure 4. This laid the foundation for the application of the deterioration law of LRBs. The appearance changes of the LRBs before and after the test are shown in Figure 5. According to the rest results, the variation law of horizontal equivalent stiffness and vertical stiffness is shown in Figure  6.

Basic Performance Test Results of Lead Rubber Bearings under the Alternation of Aging and Seawater Corrosion
A 120-day alternating test of aging and seawater corrosion for LRBs and their rubber materials were conducted in this paper. The performance of LRBs and their rubber materials were tested termly in the test process, to investigate the time-varying rule of their mechanical properties. The test method and contents of bearing performance are referred to in [31][32][33], and the horizontal and vertical stiffness of LRBs were tested on a 500-ton tensile-compression-shear comprehensive testing machine; see Figure 4. This laid the foundation for the application of the deterioration law of LRBs. The appearance changes of the LRBs before and after the test are shown in Figure 5. According to the rest results, the variation law of horizontal equivalent stiffness and vertical stiffness is shown in Figure  6.  Figure 5 shows that, after testing for 120 days, there was obvious brick red rust and white salt attached to the appearance of the LRBs, and the surface gloss was obviously faded. This indicates that the alternation of aging and seawater corrosion has an important impact on the appearance of LRBs. Figure 6a shows that the horizontal equivalent stiffness of LRBs increases exponentially with the time of the aging and seawater corrosion alternation test. Figure 6a also indicates that the fitting and test values of the LRBs' horizontal equivalent stiffness coincide with each other well, and the deviation between them both is shown in Table 3. The fitting results state that the horizontal stiffness of LRBs increases exponentially with test time (see Formula (1)). After testing for 60 days (equivalent to an LRB service for 60 years in an actual environment) and 120 days, the growth rates were 14.3% and 16.3%, respectively. Figure 6b indicates that the vertical stiffness of LRBs increases slowly with test time, and the fitting results are in good agreement with the experimental results; deviations between them both are also shown in Table 3. The fitting results also state that the growth amplitudes of vertical stiffness are 18% and 24.3%, respectively, after the LRB testing for 60 days and 120 days.
To sum up, the alternation of aging and seawater corrosion plays an important role in the basic horizontal and vertical stiffness of LRBs. The time-varying law of LRBs' basic performance with test time is shown in Formulas (1) and (2). The results state that the growth of the horizontal and vertical stiffness of LRB is 16.3% and 24.3%, respectively, after years of service in the actual environment where aging and seawater corrosion alternate. Additionally, the increase of the horizontal and vertical stiffness of LRBs is mainly concentrated in 0 to 60 years of its service life.  Figure 5 shows that, after testing for 120 days, there was obvious brick red rust and white salt attached to the appearance of the LRBs, and the surface gloss was obviously faded. This indicates that the alternation of aging and seawater corrosion has an important impact on the appearance of LRBs. Figure 6a shows that the horizontal equivalent stiffness of LRBs increases exponentially with the time of the aging and seawater corrosion alternation test. Figure 6a also indicates that the fitting and test values of the LRBs' horizontal equivalent stiffness coincide with each other well, and the deviation between them both is shown in Table 3. The fitting results state that the horizontal stiffness of LRBs increases exponentially with test time (see Formula (1)). After testing for 60 days (equivalent to an LRB service for 60 years in an actual environment) and 120 days, the growth rates were 14.3% and 16.3%, respectively. Figure 6b indicates that the vertical stiffness of LRBs increases slowly with test time, and the fitting results are in good agreement with the experimental results; deviations between them both are also shown in Table 3. The fitting results also state that the growth amplitudes of vertical stiffness are 18% and 24.3%, respectively, after the LRB testing for 60 days and 120 days.
To sum up, the alternation of aging and seawater corrosion plays an important role in the basic horizontal and vertical stiffness of LRBs. The time-varying law of LRBs' basic performance with test time is shown in Formulas (1) and (2). The results state that the growth of the horizontal and vertical stiffness of LRB is 16.3% and 24.3%, respectively, after years of service in the actual environment where aging and seawater corrosion alternate. Additionally, the increase of the horizontal and vertical stiffness of LRBs is mainly concentrated in 0 to 60 years of its service life.

Determination of the Constitutive Parameters of the LRB Rubber Material
We had carried out the aging and seawater corrosion alternate test on LNRs and rubber material in an earlier stage and the variation law of the rubber material stress-strain and the Mooney-Rivlin constitutive parameters with test time was obtained [27,[33][34][35]. Similar research methods as above were used to investigate the time-dependent law of the Mooney-Rivlin model parameters C 10 and C 01 of LRB rubber material. As we all know, the Mooney-Rivlin model is commonly applied to simulate the mechanical property of most rubber materials with small and medium deformation. The typical strain energy density function is shown in Equation (3) [36]. The time = variable law of the model parameters of LRB rubber material with the time of aging and seawater corrosion alternation is shown in Figure 7 and Formulas (4) and (5). Then, the time-dependent law of the rubber material parameters was applied in a finite model (see Figure 8) to simulate the horizontal and vertical stiffness of LRBs. The finite-element model of LRBs is shown in Figure 6. The finite element analysis of performance of lead rubber isolation bearings did not consider the rotational freedom of the bearings. In addition, because the friction cloth is used to replace the connecting plate in the mechanical behavior test of the rubber bearing, the three degrees of freedom of X, Y and Z of the bottom surface of the bearing are restrained in this study, which can better reflect the real boundary conditions. Finally, the calculated values by Formulas (1) and (2) for horizontal stiffness and vertical stiffness were compared with their simulation results, to verify that the time-varying rule of the LRB's basic performance is true and fair.
where W represents the strain potential energy; I 1 , I 2 are invariants of the deviatoric strain tensor; C 10 , C 01 , and D 1 are material parameters, which can be decided through material tests of the rubber; and J is the elastic volume ratio.

26.84
(5) Figure 7 shows that the constitutive parameter C 10 increases exponentially with the time of the aging and seawater corrosion alternation test, while parameter C 01 decreases exponentially with test time. It also states that both the fitting values and calculated values for the material parameters are in good agreement with each other; deviations between them both are shown in Table 4.
where W represents the strain potential energy; 1 I , 2 I are invariants of the deviatoric strain tensor; 10 C , 01 C , and 1 D are material parameters, which can be decided through material tests of the rubber; and J is the elastic volume ratio.

Comparative Analysis of the Simulation and Experimental Results of LRB Basic Performance
This paper used ABAQUS to establish the finite model of LRBs [27], and the LRBs' shape parameters are given in Table 1. The LRB rubber material parameters calculated by Formulas (4) and (5) are applied into the finite model of LRBs to simulate the horizontal and vertical stiffness of LRBs at different test time points. Comparison between the fitting values based on the experimental result in part 2 and the simulation results is shown in Figure 9. Deviation between the above two is shown in Table 5. values based on the experimental result in part 2 and the simulation results is shown in Figure 9. Deviation between the above two is shown in Table 5.   Table 5. This also confirmed that the deterioration law of LRBs' horizontal stiffness and vertical stiffness with the test time, shown in Formulas (1) and (2), is basically accurate.

Overview of Isolated Bridges
Sap2000 was used to model an offshore isolated bridge and the seismic response of an offshore bridge considering LRB deterioration alone was analyzed to investigate the influence of LRB deterioration on the time-varying law of seismic performance of offshore bridges. The isolation bridge had a total length of 510 m and was arranged in equal span. Its layout is shown in Figure 10. The main beam of the isolated bridge adopted a steelconcrete composite single-box three-chamber equal section, in which the bridge deck adopted C60 concrete and the box girder adopted a steel truss with a yield strength of about 384 MPa (namely, Q384). The pier was 19 m high and adopted a single-box doublechamber equal-section hollow rectangular section reinforced concrete independent pier, in which the concrete model was C50, and the longitudinal and stirrups used were secondary-thread hot rolled ribbed bars with a yield strength of 335 MPa (namely, HRB335). LRBs were adopted between the main beam and the secondary beam, respectively. Four bearing were arranged on each pier column in parallel. See Table 6 for the relevant parameters of the isolation bearings. The anti-seismic intensity of the isolated bridge was 8   Figure 9 shows that the finite element simulation values of LRB horizontal and vertical stiffness are in good agreement with the fitting values of its test results, and the deviations between the simulation and fitting values are shown in Table 5. This also confirmed that the deterioration law of LRBs' horizontal stiffness and vertical stiffness with the test time, shown in Formulas (1) and (2), is basically accurate.

Overview of Isolated Bridges
Sap2000 was used to model an offshore isolated bridge and the seismic response of an offshore bridge considering LRB deterioration alone was analyzed to investigate the influence of LRB deterioration on the time-varying law of seismic performance of offshore bridges. The isolation bridge had a total length of 510 m and was arranged in equal span. Its layout is shown in Figure 10. The main beam of the isolated bridge adopted a steel-concrete composite single-box three-chamber equal section, in which the bridge deck adopted C60 concrete and the box girder adopted a steel truss with a yield strength of about 384 MPa (namely, Q384). The pier was 19 m high and adopted a single-box double-chamber equal-section hollow rectangular section reinforced concrete independent pier, in which the concrete model was C50, and the longitudinal and stirrups used were secondary-thread hot rolled ribbed bars with a yield strength of 335 MPa (namely, HRB335). LRBs were adopted between the main beam and the secondary beam, respectively. Four bearing were arranged on each pier column in parallel. See Table 6 for the relevant parameters of the isolation bearings. The anti-seismic intensity of the isolated bridge was 8 degrees, the site category was grade III, the site characteristic period was 0.65 s, and the design service life was 120 years. degrees, the site category was grade Ⅲ, the site characteristic period was 0.65 s, and the design service life was 120 years.

Material Constitutive Model
The Scott-Kent-Park model is adopted for concrete in this study, as shown in Figure   11. is the hardening ratio, with a value of 0.01. LRBs are used as the isolation bearings of the bridge, and the modified bilinear model is used for both; see Figure 13. In Figure 13

Material Constitutive Model
The Scott-Kent-Park model is adopted for concrete in this study, as shown in Figure 11. K in the figure is the increase coefficient of concrete strength caused by restraint; f c is the compression strength of the concrete cylinder; ε max is the ultimate compressive strain of concrete. The reinforcement adopts the double straight line calculation model, ignoring the stress-strain relationship in the strengthening stage; see Figure 12, in which f y is the yield stress and ε y is the yield strain. E 0 is the initial elastic modulus and b is the hardening ratio, with a value of 0.01. LRBs are used as the isolation bearings of the bridge, and the modified bilinear model is used for both; see Figure 13. In Figure 13, K 1 represents the stiffness before yield, K 2 represents the post-yielding stiffness, Q d represents yield force, K eq represents the equivalent horizontal stiffness, and u 1 represents yield displacement.

Material Constitutive Model
The Scott-Kent-Park model is adopted for concrete in this st

Establishment of a Bridge Finite Model and the Selection of Ground
The probability of damage of the main beam under an earthq pier and bearing are the most likely to damage under the earthquak elastic beam-column element was used to imitate the working cha beam when building the bridge structure model. The pier was the nent, which bore the gravity of the superstructure and resisted t same time, it dissipated the seismic energy through its own ductil structure. The fiber plastic hinge element was used to simulate the the ratio of the calculated height of the pier to the short side len section is less than 8, the influence of the P-Δ effect is ignored in

Establishment of a Bridge Finite Model and the Selection of Ground
The probability of damage of the main beam under an earth pier and bearing are the most likely to damage under the earthquak elastic beam-column element was used to imitate the working cha beam when building the bridge structure model. The pier was the nent, which bore the gravity of the superstructure and resisted same time, it dissipated the seismic energy through its own ducti structure. The fiber plastic hinge element was used to simulate the the ratio of the calculated height of the pier to the short side len section is less than 8, the influence of the P-Δ effect is ignored in specific location of the plastic hinge is shown in Figure 14. And th

Establishment of a Bridge Finite Model and the Selection of Ground Motion
The probability of damage of the main beam under an earthquake is small, and the pier and bearing are the most likely to damage under the earthquake. Therefore, the linear elastic beam-column element was used to imitate the working characteristics of the main beam when building the bridge structure model. The pier was the main stressed component, which bore the gravity of the superstructure and resisted the earthquake. At the same time, it dissipated the seismic energy through its own ductility to protect the main structure. The fiber plastic hinge element was used to simulate the pier. Considering that the ratio of the calculated height of the pier to the short side length of the rectangular section is less than 8, the influence of the P-∆ effect is ignored in the analysis [37]. The specific location of the plastic hinge is shown in Figure 14. And the blue dotted box is an enlarged picture of the content of the red dotted box in Figure 14. For the key component connecting the superstructure and substructure of the bridge-bridge isolation bearing, the simulation adopted a double rubber isolator element. Both Chinese code [38] and American AASHTO specifications recommend using 3 or 7 seismic waves for seismic time history analysis, and the maximum response value is taken as the representative value when using 3 seismic waves, while the average response value is taken as the representative value when using seismic waves. In this paper, three seismic waves that meet the site conditions are selected from the latest seismic database of the Pacific seismic engineering research center (peer) [39], and the nonlinear dynamic time history analysis is carried out along the longitudinal input of the bridge. The selected ground motion acceleration response spectrum characteristics are shown in Figure 15, the ground motion information is shown in Table 7, and the normalized ground motion acceleration time history curve is shown in Figure 16.  Both Chinese code [38] and American AASHTO specifications recommend using 3 or 7 seismic waves for seismic time history analysis, and the maximum response value is taken as the representative value when using 3 seismic waves, while the average response value is taken as the representative value when using seismic waves. In this paper, three seismic waves that meet the site conditions are selected from the latest seismic database of the Pacific seismic engineering research center (peer) [39], and the nonlinear dynamic time history analysis is carried out along the longitudinal input of the bridge. The selected ground motion acceleration response spectrum characteristics are shown in Figure 15, the ground motion information is shown in Table 7, and the normalized ground motion acceleration time history curve is shown in Figure 16. Both Chinese code [38] and American AASHTO specificati or 7 seismic waves for seismic time history analysis, and the max taken as the representative value when using 3 seismic waves, wh value is taken as the representative value when using seismic wa seismic waves that meet the site conditions are selected from the of the Pacific seismic engineering research center (peer) [39], and time history analysis is carried out along the longitudinal input of ground motion acceleration response spectrum characteristics are ground motion information is shown in Table 7, and the normal celeration time history curve is shown in Figure 16.

Determination of LRB Time-Varying Parameters
According to the parameter information of LRBs given in Table 6, combined with the time-varying law formula of LRB horizontal stiffness and vertical stiffness under alternation of aging and seawater corrosion (see Formulas (1) and (2)) and the time-dependent law of LRB post-yield stiffness, yield stress, and pre-yield stiffness obtained by the research group, see Formula (6) to Formula (8) [40], the mechanical performance parameters of LRBs within 120 years of service are calculated, as shown in Table 8.
are, respectively, the post-yielding stiff-

Determination of LRB Time-Varying Parameters
According to the parameter information of LRBs given in Table 6, combined with the time-varying law formula of LRB horizontal stiffness and vertical stiffness under alternation of aging and seawater corrosion (see Formulas (1) and (2)) and the time-dependent law of LRB post-yield stiffness, yield stress, and pre-yield stiffness obtained by the research group, see Formula (6) to Formula (8) [40], the mechanical performance parameters of LRBs within 120 years of service are calculated, as shown in Table 8.
where K d-LRB (Y), Q d-LRB (Y), and K 1-LRB (Y) are, respectively, the post-yielding stiffness, yield stress, and pre-yield stiffness corresponding to the service time of Y years and K d-LRB (0), Q d-LRB (0), and K 1-LRB (0) are the corresponding post-yield stiffness, yield stress, and pre-yield stiffness when the service time is 0 years. In this study, SAP2000 was used to analyze the seismic performance of a bridge. The modal analysis of the finite-element model of an isolated continuous bridge was carried out, and the dynamic characteristics of the bridge structure were obtained. The structural period corresponding to the first six vibration modes at service times of 0, 30, 60, 90 and 120 years is drawn as Figure 17. In this study, SAP2000 was used to analyze the seismic performance of a bridge. The modal analysis of the finite-element model of an isolated continuous bridge was carried out, and the dynamic characteristics of the bridge structure were obtained. The structural period corresponding to the first six vibration modes at service times of 0, 30, 60, 90 and 120 years is drawn as Figure 17.  Figure 17 indicates that, when different bearings are degraded, the isolation structure cycle of the first six vibration modes decreases with increasing service duration, which is because the horizontal equivalent stiffness of the bearing increases with increasing service time, and, after 120 years of service, the first vibration mode cycle of LRB degradation decreases by 5.6%. To sum up, the deterioration of bearings reduces the structural period, reduce the damping effect of the structure and deteriorating the earthquake resistance performance. Thus, it is necessary to analyze the influence of bridge bearing degradation on the seismic performance of the bridge.   Figure 17 indicates that, when different bearings are degraded, the isolation structure cycle of the first six vibration modes decreases with increasing service duration, which is because the horizontal equivalent stiffness of the bearing increases with increasing service time, and, after 120 years of service, the first vibration mode cycle of LRB degradation decreases by 5.6%. To sum up, the deterioration of bearings reduces the structural period, reduce the damping effect of the structure and deteriorating the earthquake resistance performance. Thus, it is necessary to analyze the influence of bridge bearing degradation on the seismic performance of the bridge.   Figures 18 and 19 show that, considering the deterioration of bearing perfo there is no significant difference between the top displacement and pier bottom moment of the bridge at 60 and 120 years of service at the initial stage of the ear   Figures 18 and 19 show that, considering the deterioration of bearing perfo there is no significant difference between the top displacement and pier bottom b moment of the bridge at 60 and 120 years of service at the initial stage of the eart time, which leads to the decrease of the energy dissipation capacity of the bear increases the earthquake response of the main body of the isolated bridge struct pecially when it has been in service for 30 years, the shear force of the bearing in obviously and the shear displacement decreases obviously.  Figure 21 states that the isolation bearing has a certain impact on the hysteret of the pier column. With the increase of service time, the pier-column bending m increases slightly, while the angular displacement increases significantly. This is the deterioration of the bending increases its yield stiffness and yield force, and the dissipation of the bearing decreases, resulting in the increase of angular displace pier bottom. The absolute value of the ratio between the maximum structural response service for Y years and the response when in service for 0 years is defined as the m value ratio of structural response. The variation law of the maximum value ratio tural response with the service time is shown in Figure 22.  Figures 18 and 19 show that, considering the deterioration of bearing performance, there is no significant difference between the top displacement and pier bottom bending moment of the bridge at 60 and 120 years of service at the initial stage of the earthquake and the value at the initial 0 year. At this time, the bearing has not yielded. With the continuous ground motion, both the pier displacement and the pier bottom bending gradually increase, and the bridge isolation bearing may reach the yield point and have nonlinear deformation. From 60 to 120 years of bearing deterioration, the top displacement and pier bottom bending increase with increasing deterioration time, which is due to the increase of bridge bearing stiffness, the decrease of the isolation effect, and the increase of structural response. Figure 20 indicates that the yield stress and post-yielding stiffness of the LRB becomes larger with the increase of deterioration time, while the ultimate displacement becomes smaller. Additionally, the LRB's hysteretic loop area decreases with deterioration time, which leads to the decrease of the energy dissipation capacity of the bearing and increases the earthquake response of the main body of the isolated bridge structure. Especially when it has been in service for 30 years, the shear force of the bearing increases obviously and the shear displacement decreases obviously. Figure 21 states that the isolation bearing has a certain impact on the hysteretic curve of the pier column. With the increase of service time, the pier-column bending moment increases slightly, while the angular displacement increases significantly. This is because the deterioration of the bending increases its yield stiffness and yield force, and the energy dissipation of the bearing decreases, resulting in the increase of angular displacement of pier bottom.
The absolute value of the ratio between the maximum structural response when in service for Y years and the response when in service for 0 years is defined as the maximum value ratio of structural response. The variation law of the maximum value ratio of structural response with the service time is shown in Figure 22. Figure 22 states clearly that the maximum displacement of the pier top increases with the increase of service time under the action of 0.443 g ground motion. After 120 years of service, the maximum displacement increase amplitude of the pier top is 14.2% under the condition of LRB deterioration. Additionally, the deterioration of the isolation bearing has little effect on the maximum bending moment at the pier bottom, and after servicing for 120 years, the maximum bending moment at the pier bottom increases by 6.6% under the condition of LRB deterioration. The rubber bearing's maximum displacement decreases with increasing service duration when considering that the bearing deteriorates alone. The bearing's maximum displacement reduces by 9.1% after it is in service for 120 years. This indicates that the deformation and energy dissipation capacity of the bearing decreases, the isolation effect decreases, the response of the main structure increases, and the protection effect of the bearing on the main structure decreases. Figure 20. Comparison of the hysteresis curves of the LRB at different deterioration time p Figure 21 states that the isolation bearing has a certain impact on the hystere of the pier column. With the increase of service time, the pier-column bending increases slightly, while the angular displacement increases significantly. This is the deterioration of the bending increases its yield stiffness and yield force, and th dissipation of the bearing decreases, resulting in the increase of angular displace pier bottom. The absolute value of the ratio between the maximum structural response service for Y years and the response when in service for 0 years is defined as the m value ratio of structural response. The variation law of the maximum value ratio tural response with the service time is shown in Figure 22.   Figure 22 states clearly that the maximum displacement of the pier top increa the increase of service time under the action of 0.443 g ground motion. After 120 service, the maximum displacement increase amplitude of the pier top is 14.2% un condition of LRB deterioration. Additionally, the deterioration of the isolation bea little effect on the maximum bending moment at the pier bottom, and after servi 120 years, the maximum bending moment at the pier bottom increases by 6.6% un condition of LRB deterioration. The rubber bearing's maximum displacement d with increasing service duration when considering that the bearing deteriorate  To sum up, the finite element analysis of the offshore isolation bridge is carried out by SAP2000 in this study. The pier top displacement time history curve, pier bottom bending moment time history curve, pier bottom bending moment rotation angle curve, and isolation bearing hysteretic curve of the pier column under the single deterioration of LRB are obtained; see  The results show that the deterioration of lead rubber isolation bearing has a great influence on the seismic performance of the offshore isolation bridge. In the seismic performance analysis of the offshore isolation bridge, not only the influence of concrete materials such as the pier column but also the influence of isolation bearing deterioration should be considered.

Summary and Conclusions
The aim of this study is to investigate the influence of the alternation of aging and seawater corrosion on the performance deterioration law of lead rubber bearings used in offshore bridges. The effect of LRB deterioration on the earthquake resistant behavior of an offshore isolation bride was also studied in this paper. Thus, a 120-day alternating aging-seawater corrosion test on lead rubber bearings and rubber material was carried out, and the time-dependent law of the LRB basic properties and rubber material constitutive parameters were also obtained in this paper. Then, rubber material parameters obtained were substituted into the finite-element model of LRBs to simulate the horizontal and vertical stiffness at different test time points, and the fitting results, simulation results, and test results of those were compared. Finally, the time-variable law of the seismic performance of offshore bridge structures was also analyzed, which was based on the time-variable law of the horizontal and vertical stiffness ratio of LRBs during the 120-year service period, the time-dependent law of the seismic performance of offshore bridge structures was analyzed. The results state that: The horizontal stiffness and vertical stiffness of LRBs increase with increasing aging and seawater corrosion alternation time. After 120 days of testing, the increase of the two was 16.3% and 24.3%, respectively; the rubber material parameter C 10 of LRBs increases with the test time, while parameter C 01 decreases with the increase of test time, and the material parameters change greatly. The time-dependent law of the material parameters of LRBs is revealed in Formulas (4) and (5); the simulation results are generally consistent with the fitting values of the corresponding test results, which verifies the rationality of the deterioration law of horizontal stiffness and vertical stiffness with the alternation of aging and seawater corrosion test duration; after servicing for 120 years, the variation amplitudes of the maximum pier top displacement, the maximum pier bottom bending, and the maximum bearing displacement of the bridge structure are 14.2%, 6.6%, and 9.1% respectively, under the condition of LRB deterioration. To sum up, the alternation of aging and seawater corrosion plays a significant role in LRB basic performance, and the influence of LRB degradation on the seismic behavior of offshore isolated bridges cannot be ignored. In the next study, we will carry out a comparative study on the performance deterioration of different kinds of rubber isolations and its impact on the earthquake resistance behavior of bridge structures, and propose solutions to bearing performance degradation.