The Inﬂuence of the Post-Weld Heat Treatment on the Microstructure of Inconel 625/Carbon Steel Bimetal Joint Obtained by Explosive Welding

: Inconel 625 and steel P355NH were bonded by explosive welding in this study. Explosively welded bimetal clad-plate was subjected to the two separated post-weld heat treatment processes: stress relief annealing (at 620 ◦ C for 90 min) and normalizing (at 910 ◦ C for 30 min). Effect of heat treatments on the microstructure of the joint has been evaluated using light and scanning electron microscopy, EDS analysis techniques, and microhardness tests, respectively. It has been stated that stress relief annealing leads to partial recrystallization of steel P355NH microstructure in the joint zone. At the same time, normalizing caused not only the recrystallization of both materials, but also the formation of a diffusion zone and precipitates in Inconel 625. The precipitates in Inconel 625 have been identiﬁed as two types of carbides: chromium-rich M 23 C 6 and molybdenum-rich M 6 C. It has been reported that diffusion of alloying elements into steel P355NH takes place along grain boundaries with additional formation of voids. Scanning transmission electron microscope observation of the grain microstructure in the diffusion zone shows that this area consists of equiaxed grains (at the side of Inconel 625 alloy) and columnar grains (at the side of steel P355NH).


Introduction
Corrosive wear is a significant problem for the utilization of components of equipment operating in an aggressive environment, such as reactors, tanks, heat exchangers, and pipelines in the chemical industry and geothermal power plants [1,2]. Basically, the alloys which can provide a specified resistant against corrosion in the aggressive environment are expensive. However, there is no need for making the entire component from corrosion resistant material-only its surface, which has direct contact with an aggressive medium. An approach worth considering is the use of relatively inexpensive material (e.g., non-alloy steel) and cladding it with layer of corrosion resistant alloy, such as stainless steel or nickel alloy providing potentiality of operating in the aggressive environment. This solution allows to reduce the material cost of industry equipment significantly depending on used manufacturing technique [3][4][5]. As an example of such bimetal clad plate Inconel/steel system can be given, in which steel is a load-bearing component while Inconel provides resistance to an aggressive environment. This paper investigates steel P355NH cladded with Inconel 625 as bimetallic material of the above type. A pressure vessel steel grade P355NH, weldable constructional steel with fine grain microstructure, is used as material for the manufacture of pressure equipment operating under high temperature (up to 450 • C) [6]. The poor corrosion resistance of this steel limits its applications as a construction

Materials and Methods
In this study, the materials used for the manufacturing of bimetal clad-plate were a 10 mm thick plate of steel P355NH and a 3 mm thick sheet of Inconel 625 alloy. The dimensions of plates were equal to 860 × 1000 mm. The surfaces to be joined have been polished and cleaned with acetone before welding. The chemical compositions of the materials are presented in Table 1. The samples were cut out of the workpieces in order to perform a microstructure investigation of materials in the as-received. The process of explosive welding of steel P355NH and Inconel 625 alloy was performed by EXPLOMET High-Energy Techniques Works company (Opole, Poland). The explosive used in the process was modified ammonium nitrate fuel oil (ANFO), with detonation velocity of 2700 m/s, which has been determined using optical fiber sensors. The stand-off distance between plates was equal to 3 mm. The explosive has been placed directly on Inconel 625 plate and no buffer plate has been used. Three samples were cut out of the bimetallic clad-plate produced by explosive welding, as shown in Figure 1.

Materials and Methods
In this study, the materials used for the manufacturing of bimetal clad-plate were a 10 mm thick plate of steel P355NH and a 3 mm thick sheet of Inconel 625 alloy. The dimensions of plates were equal to 860 × 1000 mm. The surfaces to be joined have been polished and cleaned with acetone before welding. The chemical compositions of the materials are presented in Table 1. The samples were cut out of the workpieces in order to perform a microstructure investigation of materials in the asreceived. The process of explosive welding of steel P355NH and Inconel 625 alloy was performed by EXPLOMET High-Energy Techniques Works company (Opole, Poland). The explosive used in the process was modified ammonium nitrate fuel oil (ANFO), with detonation velocity of 2700 m/s, which has been determined using optical fiber sensors. The stand-off distance between plates was equal to 3 mm. The explosive has been placed directly on Inconel 625 plate and no buffer plate has been used. Three samples were cut out of the bimetallic clad-plate produced by explosive welding, as shown in Figure 1.  In order to analyze the influence of the post-weld heat treatment on the microstructure of the obtained joint, the first sample has been investigated in the as-welded state, the second sample has been subjected to heat treatment of stress relief annealing (at 620 °C for 90 min), and the third sample was subjected to the normalizing (at 910 °C for 30 min). The parameters of the post-weld heat treatment have been selected for base material (P355NH), which plays a load-bearing role in the investigated clad-plate. As a result, for the further investigation the three samples were obtained: a sample after explosive welding (InSt EXW), sample after post-weld stress relief annealing (InSt HTR) and sample after post-weld normalizing (InSt HTN). In order to perform the microstructure analysis, the samples have been subjected to the metallographic preparation. The cut samples were mounted in hot-mounting resin, ground with abrasive paper of 80, 320, 600, 1200 and 2400 gradations and polished using diamond paste of 1 µm gradation. In order to reveal the microstructure of steel P355NH, 2% nital etchant with etching time of 5-10 seconds was used and in case of Inconel 625 alloy, In order to analyze the influence of the post-weld heat treatment on the microstructure of the obtained joint, the first sample has been investigated in the as-welded state, the second sample has been subjected to heat treatment of stress relief annealing (at 620 • C for 90 min), and the third sample was subjected to the normalizing (at 910 • C for 30 min). The parameters of the post-weld heat treatment have been selected for base material (P355NH), which plays a load-bearing role in the investigated clad-plate. As a result, for the further investigation the three samples were obtained: a sample after explosive welding (InSt EXW), sample after post-weld stress relief annealing (InSt HTR) and sample after post-weld normalizing (InSt HTN). In order to perform the microstructure analysis, Metals 2019, 9, 246 4 of 16 the samples have been subjected to the metallographic preparation. The cut samples were mounted in hot-mounting resin, ground with abrasive paper of 80, 320, 600, 1200 and 2400 gradations and polished using diamond paste of 1 µm gradation. In order to reveal the microstructure of steel P355NH, 2% nital etchant with etching time of 5-10 seconds was used and in case of Inconel 625 alloy, acetic glyceregia (15 mL HCl 38%, 10 mL of acetic acid 99%, 5 mL HNO 3 65%, 1-2 drops of glycerol) with etching time of 15 min. Grain size of the materials has been measured with Mountains Map 7 software. The microstructure of the samples was investigated using light microscope OLYMPUS LEXT OLS 4100 (Military University of Technology, Warsaw, Poland) and scanning electron microscope (SEM) Jeol JSM 6610 (Military University of Technology, Warsaw, Poland) equipped with energy-dispersive x-ray spectroscopy (EDS) and back-scattered electron (BSE) detector. The diffusion zone, which has been formed in the post-weld normalizing (InSt HTN) sample was investigated using scanning transmission electron microscope (STEM) Hitachi S-5500N (Military University of Technology, Warsaw, Poland). The sample for STEM was prepared using dual beam system Hitachi NB-5000 (Military University of Technology, Warsaw, Poland). In order to establish the strain hardening of analyzed samples the Vickers microhardness test was performed with loading of 100 g. Microhardness distributions were prepared for each sample. The first two measurements were performed 200 µm from the joint line, in the layer of Inconel 625 alloy and in steel P355NH as shown in Figure 2. Subsequently, measurement imprints were guided towards the edge of the samples, at the distance of 2000 µm.  Figure 2. Subsequently, measurement imprints were guided towards the edge of the samples, at the distance of 2000 µm.

Microstructure of the Raw Materials
In the first part of the investigation the light microscopy observations of the base materials after etching have been performed. The microstructures of steel P355NH ( Figure 3A) and Inconel 625 alloy ( Figure 3B) in the as-received state are presented in Figure 3. As it can be observed, the steel P355NH has a ferrite-pearlite microstructure with noticeable pearlite bands, characteristic for the plates after rolling process. The microstructure of steel has fine equiaxial grains with their measured size equal to 15.5 ± 4.1 µm. At the same time, Inconel 625 alloy has far more heterogenous microstructure characterized by presence of twins and measured grain size of 49.4 ± 15.6 µm. Additionally, the microhardness of base materials has been measured with registered values of 150.6 ± 4.9 HV0.1 for steel P355NH and 249.6 ± 16.3 HV0.1 for Inconel 625 alloy, respectively.

Microstructure of the Raw Materials
In the first part of the investigation the light microscopy observations of the base materials after etching have been performed. The microstructures of steel P355NH ( Figure 3A) and Inconel 625 alloy ( Figure 3B) in the as-received state are presented in Figure 3. As it can be observed, the steel P355NH has a ferrite-pearlite microstructure with noticeable pearlite bands, characteristic for the plates after rolling process. The microstructure of steel has fine equiaxial grains with their measured size equal to 15.5 ± 4.1 µm. At the same time, Inconel 625 alloy has far more heterogenous microstructure characterized by presence of twins and measured grain size of 49.4 ± 15.6 µm. Additionally, the microhardness of base materials has been measured with registered values of 150.6 ± 4.9 HV0.1 for steel P355NH and 249.6 ± 16.3 HV0.1 for Inconel 625 alloy, respectively.

Microstructure of a Sample After Explosive Welding (InSt EXW) Joint
The obtained joint has a wavy structure, typical for explosively welded bond. The grains of both materials in the joint zone are deformed due to severe plastic deformation during collision, as it can be observed after etching of steel P355NH ( Figure 4A) and Inconel 625 alloy ( Figure 4B). The observations using scanning electron microscope (BSE) show the occurrence of melted zones in the joint, where the two welded materials have been stirred together ( Figure 5A). In the melted zones, the investigation revealed the presence of joint imperfections in the form of both cracks and fragments of steel P355NH surface layer, which underwent partial fragmentation during explosive welding process, as evidenced by linear analysis of the chemical composition ( Figure 5B). The results of the chemical composition analysis indicate on the highest participation of Inconel 625 alloying elements in this area with small fluctuations near to the steel P355NH fragment.

Microstructure of a Sample After Explosive Welding (InSt EXW) Joint
The obtained joint has a wavy structure, typical for explosively welded bond. The grains of both materials in the joint zone are deformed due to severe plastic deformation during collision, as it can be observed after etching of steel P355NH ( Figure 4A) and Inconel 625 alloy ( Figure 4B).

Microstructure of a Sample After Explosive Welding (InSt EXW) Joint
The obtained joint has a wavy structure, typical for explosively welded bond. The grains of both materials in the joint zone are deformed due to severe plastic deformation during collision, as it can be observed after etching of steel P355NH ( Figure 4A) and Inconel 625 alloy ( Figure 4B). The observations using scanning electron microscope (BSE) show the occurrence of melted zones in the joint, where the two welded materials have been stirred together ( Figure 5A). In the melted zones, the investigation revealed the presence of joint imperfections in the form of both cracks and fragments of steel P355NH surface layer, which underwent partial fragmentation during explosive welding process, as evidenced by linear analysis of the chemical composition ( Figure 5B). The results of the chemical composition analysis indicate on the highest participation of Inconel 625 alloying elements in this area with small fluctuations near to the steel P355NH fragment. The observations using scanning electron microscope (BSE) show the occurrence of melted zones in the joint, where the two welded materials have been stirred together ( Figure 5A). In the melted zones, the investigation revealed the presence of joint imperfections in the form of both cracks and fragments of steel P355NH surface layer, which underwent partial fragmentation during explosive welding process, as evidenced by linear analysis of the chemical composition ( Figure 5B). The results of the chemical composition analysis indicate on the highest participation of Inconel 625 alloying elements in this area with small fluctuations near to the steel P355NH fragment.

Microstructure of Sample After Post-Weld Stress Relief Annealing (InSt HTR) Joint
Post-weld stress relief annealing of Inconel 625/steel P355NH bimetallic clad-plate, performed at 620 °C for 90 min slightly influences the microstructure of the joint zone. The partial recrystallization of steel P355NH microstructure has been reported in the area of 20-30 μm from the joint line ( Figure 6A). New, equiaxial grains formed on the joint line do not have deformation texture of previous compressed, elongated grains. The microstructure of steel P355NH farther from the joint line (about 30 μm) maintains the deformation texture and no recrystallized grains have been observed. On the other hand, the microstructure of Inconel 625 alloy did not reveal any visible changes in the grain morphology after stress relief annealing compared with its microstructure in the as-welded state ( Figure 6B).

Microstructure of Sample After Post-Weld Stress Relief Annealing (InSt HTR) Joint
Post-weld stress relief annealing of Inconel 625/steel P355NH bimetallic clad-plate, performed at 620 • C for 90 min slightly influences the microstructure of the joint zone. The partial recrystallization of steel P355NH microstructure has been reported in the area of 20-30 µm from the joint line ( Figure 6A). New, equiaxial grains formed on the joint line do not have deformation texture of previous compressed, elongated grains. The microstructure of steel P355NH farther from the joint line (about 30 µm) maintains the deformation texture and no recrystallized grains have been observed. On the other hand, the microstructure of Inconel 625 alloy did not reveal any visible changes in the grain morphology after stress relief annealing compared with its microstructure in the as-welded state ( Figure 6B).

Microstructure of InSt HTN Joint
The microstructure of the joint subjected to normalizing at 910 °C for 30 min changed significantly. It has been reported that due to this post-weld heat treatment the complete recrystallization of microstructure of both joined materials-steel P355NH ( Figure 8A) and Inconel 625 ( Figure 8B) occurs. The welded materials have microstructures consisting of fine, equiaxial grains and no deformation texture is noticeable. The size of steel grains is about 20 μm, which is a typical value for this material after normalizing. Additionally, it has been observed the presence of ultrafine grains with size about 5 µm of steel P355NH on the joint line (Figure 8a). In case of Inconel 625 grains have size also about 20 µm with low participation of twins and significant amount of precipitates localized on grain boundaries.

Microstructure of InSt HTN Joint
The microstructure of the joint subjected to normalizing at 910 °C for 30 min changed significantly. It has been reported that due to this post-weld heat treatment the complete recrystallization of microstructure of both joined materials-steel P355NH ( Figure 8A) and Inconel 625 ( Figure 8B) occurs. The welded materials have microstructures consisting of fine, equiaxial grains and no deformation texture is noticeable. The size of steel grains is about 20 μm, which is a typical value for this material after normalizing. Additionally, it has been observed the presence of ultrafine grains with size about 5 µm of steel P355NH on the joint line (Figure 8a). In case of Inconel 625 grains have size also about 20 µm with low participation of twins and significant amount of precipitates localized on grain boundaries.

Microstructure of InSt HTN Joint
The microstructure of the joint subjected to normalizing at 910 • C for 30 min changed significantly. It has been reported that due to this post-weld heat treatment the complete recrystallization of microstructure of both joined materials-steel P355NH ( Figure 8A) and Inconel 625 ( Figure 8B) occurs. The welded materials have microstructures consisting of fine, equiaxial grains and no deformation texture is noticeable. The size of steel grains is about 20 µm, which is a typical value for this material after normalizing. Additionally, it has been observed the presence of ultrafine grains with size about 5 µm of steel P355NH on the joint line ( Figure 8A). In case of Inconel 625 grains have size also about 20 µm with low participation of twins and significant amount of precipitates localized on grain boundaries. The observations using scanning electron microscope show significant changes in the concentration of alloying elements in the joint area. It has been stated that alloying elements of Inconel 625 were found to diffuse into steel P355NH along grain boundaries ( Figure 9A). Additionally, diffusion zone contains voids, which are localized mainly on grain boundaries and the joint line at the side of steel P355NH ( Figure 9B). Another noticeable change compared with the joint in the aswelded state is formation of precipitates in the joint zone, which are localized in Inconel 625 alloy ( Figure 9A,B). Scanning electron microscope observations revealed the presence of two types of precipitates in Inconel 625 alloy-light precipitates (suggesting a high concentration of alloying elements heavier than nickel) and dark precipitates (high concentration of alloying elements lighter than nickel). The size of precipitates is about 0.5-1 µm ( Figure 10A). In order to establish a chemical composition of precipitates EDX area analysis has been performed. Dark precipitates are characterized by high concentration of chromium and increased participation of molybdenum ( Figure 10B). At the same time, it has been found that chemical composition of light precipitates has high molybdenum and niobium content ( Figure 10C). Additionally, the presence of carbon in both types of precipitates has been reported. The observations using scanning electron microscope show significant changes in the concentration of alloying elements in the joint area. It has been stated that alloying elements of Inconel 625 were found to diffuse into steel P355NH along grain boundaries ( Figure 9A). Additionally, diffusion zone contains voids, which are localized mainly on grain boundaries and the joint line at the side of steel P355NH ( Figure 9B). Another noticeable change compared with the joint in the as-welded state is formation of precipitates in the joint zone, which are localized in Inconel 625 alloy ( Figure 9A,B). The observations using scanning electron microscope show significant changes in the concentration of alloying elements in the joint area. It has been stated that alloying elements of Inconel 625 were found to diffuse into steel P355NH along grain boundaries ( Figure 9A). Additionally, diffusion zone contains voids, which are localized mainly on grain boundaries and the joint line at the side of steel P355NH ( Figure 9B). Another noticeable change compared with the joint in the aswelded state is formation of precipitates in the joint zone, which are localized in Inconel 625 alloy ( Figure 9A,B). Scanning electron microscope observations revealed the presence of two types of precipitates in Inconel 625 alloy-light precipitates (suggesting a high concentration of alloying elements heavier than nickel) and dark precipitates (high concentration of alloying elements lighter than nickel). The size of precipitates is about 0.5-1 µm ( Figure 10A). In order to establish a chemical composition of precipitates EDX area analysis has been performed. Dark precipitates are characterized by high concentration of chromium and increased participation of molybdenum ( Figure 10B). At the same time, it has been found that chemical composition of light precipitates has high molybdenum and niobium content ( Figure 10C). Additionally, the presence of carbon in both types of precipitates has been reported. Scanning electron microscope observations revealed the presence of two types of precipitates in Inconel 625 alloy-light precipitates (suggesting a high concentration of alloying elements heavier than nickel) and dark precipitates (high concentration of alloying elements lighter than nickel). The size of precipitates is about 0.5-1 µm ( Figure 10A). In order to establish a chemical composition of precipitates EDX area analysis has been performed. Dark precipitates are characterized by high concentration of chromium and increased participation of molybdenum ( Figure 10B). At the same time, it has been Metals 2019, 9, 246 9 of 16 found that chemical composition of light precipitates has high molybdenum and niobium content ( Figure 10C). Additionally, the presence of carbon in both types of precipitates has been reported. The width of the diffusion zone in InSt HTN sample ( Figure 11A) has been estimated using linear analysis of chemical composition ( Figure 11B). The diffusion zone has about 15 μm width and can be divided into two sections: iron-rich and chromium and nickel-rich. (Figure 11B). The width of the diffusion zone in InSt HTN sample ( Figure 11A) has been estimated using linear analysis of chemical composition ( Figure 11B). The diffusion zone has about 15 µm width and can be divided into two sections: iron-rich and chromium and nickel-rich. (Figure 11B).

Scanning Transmission Electron Microscope Observations of the Diffusion Zone
Observations of the diffusion zone performed on scanning transmission electron microscope allow to investigate the grainy microstructure of this area. It has been stated that in terms of grain structure the diffusion zone consists of two subzones: area of equiaxed grains (at side of Inconel 625 alloy) and area of columnar grains (at side of steel P355NH) ( Figure 12A). In both cases, the microstructure consists of ultrafine grains with their size within the range of 400 nm-1 μm. Predominantly, the finer grains close to Inconel 625 are equiaxed and columnar grains close to P355NH have slightly larger size. Additionally, it has been reported the occurrence of precipitates with their width about 50 nm in the diffusion zone ( Figure 12B).

Scanning Transmission Electron Microscope Observations of the Diffusion Zone
Observations of the diffusion zone performed on scanning transmission electron microscope allow to investigate the grainy microstructure of this area. It has been stated that in terms of grain structure the diffusion zone consists of two subzones: area of equiaxed grains (at side of Inconel 625 alloy) and area of columnar grains (at side of steel P355NH) ( Figure 12A). In both cases, the microstructure consists of ultrafine grains with their size within the range of 400 nm-1 µm. Predominantly, the finer grains close to Inconel 625 are equiaxed and columnar grains close to P355NH have slightly larger size. Additionally, it has been reported the occurrence of precipitates with their width about 50 nm in the diffusion zone ( Figure 12B).

Scanning Transmission Electron Microscope Observations of the Diffusion Zone
Observations of the diffusion zone performed on scanning transmission electron microscope allow to investigate the grainy microstructure of this area. It has been stated that in terms of grain structure the diffusion zone consists of two subzones: area of equiaxed grains (at side of Inconel 625 alloy) and area of columnar grains (at side of steel P355NH) ( Figure 12A). In both cases, the microstructure consists of ultrafine grains with their size within the range of 400 nm-1 μm. Predominantly, the finer grains close to Inconel 625 are equiaxed and columnar grains close to P355NH have slightly larger size. Additionally, it has been reported the occurrence of precipitates with their width about 50 nm in the diffusion zone ( Figure 12B).  The linear analysis of chemical composition has been performed in order to investigate subzone of columnar grains (Figure 13). Results indicate on similar concentration of chromium and niobium in the analyzed area. On the other hand, the elements such as iron and nickel, which are main components of the diffusion zone, show significant fluctuations in their concentration in this zone. It has been reported that concentration of nickel decreases drastically on the border between columnar grains area of the diffusion zone and steel P355NH. At the same time the concentration of iron increases, also rapidly. The results of linear analysis together with scanning transmission electron microscopy observations of this area suggest the predominate role of nickel and iron concentration ratio in the forming of diffusion zone. The precipitates founded in this area were a subject of further investigation and observations performed on scanning transmission electron microscope reveal their specific structure consisted of core and shell ( Figure 12B). In order to examine chemical composition of precipitate in the diffusion zone the linear analysis was performed ( Figure 14). The shell-core structure has been confirmed in terms of chemical composition, since it has been reported that in the precipitate area there are significant differences in distribution of alloying elements. The shell has high concentration of niobium and molybdenum, while core consists of chromium and also of niobium and molybdenum (compared to the average value of concentration of these elements in the diffusion zone). The linear analysis of chemical composition has been performed in order to investigate subzone of columnar grains ( Figure 13). Results indicate on similar concentration of chromium and niobium in the analyzed area. On the other hand, the elements such as iron and nickel, which are main components of the diffusion zone, show significant fluctuations in their concentration in this zone. It has been reported that concentration of nickel decreases drastically on the border between columnar grains area of the diffusion zone and steel P355NH. At the same time the concentration of iron increases, also rapidly. The results of linear analysis together with scanning transmission electron microscopy observations of this area suggest the predominate role of nickel and iron concentration ratio in the forming of diffusion zone. The precipitates founded in this area were a subject of further investigation and observations performed on scanning transmission electron microscope reveal their specific structure consisted of core and shell ( Figure 12B). In order to examine chemical composition of precipitate in the diffusion zone the linear analysis was performed ( Figure 14). The shell-core structure has been confirmed in terms of chemical composition, since it has been reported that in the precipitate area there are significant differences in distribution of alloying elements. The shell has high concentration of niobium and molybdenum, while core consists of chromium and also of niobium and molybdenum (compared to the average value of concentration of these elements in the diffusion zone). The linear analysis of chemical composition has been performed in order to investigate subzone of columnar grains ( Figure 13). Results indicate on similar concentration of chromium and niobium in the analyzed area. On the other hand, the elements such as iron and nickel, which are main components of the diffusion zone, show significant fluctuations in their concentration in this zone. It has been reported that concentration of nickel decreases drastically on the border between columnar grains area of the diffusion zone and steel P355NH. At the same time the concentration of iron increases, also rapidly. The results of linear analysis together with scanning transmission electron microscopy observations of this area suggest the predominate role of nickel and iron concentration ratio in the forming of diffusion zone. The precipitates founded in this area were a subject of further investigation and observations performed on scanning transmission electron microscope reveal their specific structure consisted of core and shell ( Figure 12B). In order to examine chemical composition of precipitate in the diffusion zone the linear analysis was performed ( Figure 14). The shell-core structure has been confirmed in terms of chemical composition, since it has been reported that in the precipitate area there are significant differences in distribution of alloying elements. The shell has high concentration of niobium and molybdenum, while core consists of chromium and also of niobium and molybdenum (compared to the average value of concentration of these elements in the diffusion zone).

Microhardness Analysis
The influence of the explosive welding process on the joined materials in terms of strain hardening was established by microhardness analysis (Figure 15). The highest degree of strain hardening has been revealed close to the joint line, where welded materials were subjected to the severest plastic deformation due to high velocity collision during explosive welding process. In this area, the microhardness of Inconel 625 alloy increased by about 200 HV0.1 and in case of steel P355NH by about 100 HV0.1. Stress relief annealing reduced the microhardness of steel P355NH by about 40 HV0.1. It is mostly related to recrystallization of steel P355NH grains and presumably the decreasing of the residual stress of the welded materials in the joint zone. The post-weld heat treatment in the form of normalizing reduced the microhardness of steel P355NH and Inconel 625 to their baseline value, measured in the as-received state.

Microhardness Analysis
The influence of the explosive welding process on the joined materials in terms of strain hardening was established by microhardness analysis (Figure 15). The highest degree of strain hardening has been revealed close to the joint line, where welded materials were subjected to the severest plastic deformation due to high velocity collision during explosive welding process. In this area, the microhardness of Inconel 625 alloy increased by about 200 HV0.1 and in case of steel P355NH by about 100 HV0.1. Stress relief annealing reduced the microhardness of steel P355NH by about 40 HV0.1. It is mostly related to recrystallization of steel P355NH grains and presumably the decreasing of the residual stress of the welded materials in the joint zone. The post-weld heat treatment in the form of normalizing reduced the microhardness of steel P355NH and Inconel 625 to their baseline value, measured in the as-received state.

Discussion
Both heat treatments cause changes in the microstructure of investigated joint. Stress relief annealing has a lowest impact on grainy microstructure and leads only to partial recrystallization of steel P355NH grains in the joint zone. On the other hand normalizing the complete restructure of steel grainy microstructure has been noticed. It is a well-known fact that the higher degree of plastic deformation, the lower energy is necessary to initiate and complete heat-activated phenomena and therefore the recrystallization temperature is lower, which explains the incomplete restructure of the deformed steel structure after stress relief annealing. Additionally, it can be observed a disappear of pearlite bands close to the joint line, what can suggest the diffusion process of carbon into Inconel 625 alloy. Inconel contains chemical elements having a high affinity for carbon, such as chromium, molybdenum and niobium and for this reason carbon diffusion can result in formation of brittle carbides in the joint zone [15,[41][42][43]. Inconel 625 isothermal transformation diagram shows that the parameters of the normalizing are close to the area of carbides formation, especially MC and M6C types ( Figure 16).

Discussion
Both heat treatments cause changes in the microstructure of investigated joint. Stress relief annealing has a lowest impact on grainy microstructure and leads only to partial recrystallization of steel P355NH grains in the joint zone. On the other hand normalizing the complete restructure of steel grainy microstructure has been noticed. It is a well-known fact that the higher degree of plastic deformation, the lower energy is necessary to initiate and complete heat-activated phenomena and therefore the recrystallization temperature is lower, which explains the incomplete restructure of the deformed steel structure after stress relief annealing. Additionally, it can be observed a disappear of pearlite bands close to the joint line, what can suggest the diffusion process of carbon into Inconel 625 alloy. Inconel contains chemical elements having a high affinity for carbon, such as chromium, molybdenum and niobium and for this reason carbon diffusion can result in formation of brittle carbides in the joint zone [15,[41][42][43]. Inconel 625 isothermal transformation diagram shows that the parameters of the normalizing are close to the area of carbides formation, especially MC and M 6 C types ( Figure 16).  [35]. Parameters of stress relief annealing and normalizing have been marked.
As it was mentioned in the introduction part, the plastic deformation of Inconel 625 alloy, which took place in the joint results in reducing of the energy of heat-activated processes, including precipitate processes. The diffusion of carbon from steel P355NH into Inconel 625 alloy is an additional factor, which has a significant impact on the carbides precipitation processes in the layer of Inconel 625 near to the joint line. Scanning electron microscopy observations of sample subjected to the normalizing revealed presence of precipitates in Inconel 625 close to the joint line. The results of chemical composition analysis of precipitates indicate to two types of compounds: light, molybdenum-rich and dark, chromium-rich. The presence of carbon in both precipitates has been reported. The literature on the diffusion bonding of Inconel 625 and low-alloy steel describes both morphology and chemical composition of carbides formed in that bimetallic system, identifying the precipitates as carbides of M6C type in the case of high molybdenum concentration and of M23C6 type in the case of high chromium concentration [41,43]. Additionally, M6C carbides have been characterized by increased concentration of niobium and iron what has been confirmed in this investigation [41]. Scanning electron microscopy observation of the diffusion zone formed due to normalizing, allow one to draw a conclusion that chemical elements of Inconel 625 alloy diffuse into steel P355NH along grain boundaries. Diffusion zone has about 15 μm width and can be divided into two sections in terms of iron, nickel and chromium concentrations. The first, iron-rich section consists of about 90% of iron and below 10% of nickel and chromium. An analysis of the Fe-Ni-Cr phase equilibrium diagram suggests that this section is composed predominantly of γ phase and very small amount of α phase (Figure 17). At the same time, the second section is characterized by high concentration of nickel (ca. 45%) and chromium (ca. 30%). Phase diagram analysis also indicates on γ phase, as the main component of the section with the small addition of α' phase ( Figure 17).  [35]. Parameters of stress relief annealing and normalizing have been marked.
As it was mentioned in the introduction part, the plastic deformation of Inconel 625 alloy, which took place in the joint results in reducing of the energy of heat-activated processes, including precipitate processes. The diffusion of carbon from steel P355NH into Inconel 625 alloy is an additional factor, which has a significant impact on the carbides precipitation processes in the layer of Inconel 625 near to the joint line. Scanning electron microscopy observations of sample subjected to the normalizing revealed presence of precipitates in Inconel 625 close to the joint line. The results of chemical composition analysis of precipitates indicate to two types of compounds: light, molybdenum-rich and dark, chromium-rich. The presence of carbon in both precipitates has been reported. The literature on the diffusion bonding of Inconel 625 and low-alloy steel describes both morphology and chemical composition of carbides formed in that bimetallic system, identifying the precipitates as carbides of M 6 C type in the case of high molybdenum concentration and of M 23 C 6 type in the case of high chromium concentration [41,43]. Additionally, M 6 C carbides have been characterized by increased concentration of niobium and iron what has been confirmed in this investigation [41]. Scanning electron microscopy observation of the diffusion zone formed due to normalizing, allow one to draw a conclusion that chemical elements of Inconel 625 alloy diffuse into steel P355NH along grain boundaries. Diffusion zone has about 15 µm width and can be divided into two sections in terms of iron, nickel and chromium concentrations. The first, iron-rich section consists of about 90% of iron and below 10% of nickel and chromium. An analysis of the Fe-Ni-Cr phase equilibrium diagram suggests that this section is composed predominantly of γ phase and very small amount of α phase (Figure 17). At the same time, the second section is characterized by high concentration of nickel (ca. 45%) and chromium (ca. 30%). Phase diagram analysis also indicates on γ phase, as the main component of the section with the small addition of α' phase ( Figure 17).
Scanning transmission electron microscopy observations, allowed to investigate the diffusion zone microstructure, which consists of equiaxed, columnar grains with presence of 50 nm chromium-rich precipitates having core-shell structure. It can be stated that both observed diffusion-based phenomena in sample after normalizing, including diffusion zone with presence of voids and carbides in Inconel 625 alloy have their detrimental effect on the joint strength. The carbides localized in Inconel 625 alloy layer, also result in decreasing of material coherence at the most crucial region-the joint. These factors might cause the deterioration of the joint quality established by the shear test in the previous investigation performed by the authors of this paper [22]. Scanning transmission electron microscopy observations, allowed to investigate the diffusion zone microstructure, which consists of equiaxed, columnar grains with presence of 50 nm chromiumrich precipitates having core-shell structure. It can be stated that both observed diffusion-based phenomena in sample after normalizing, including diffusion zone with presence of voids and carbides in Inconel 625 alloy have their detrimental effect on the joint strength. The carbides localized in Inconel 625 alloy layer, also result in decreasing of material coherence at the most crucial regionthe joint. These factors might cause the deterioration of the joint quality established by the shear test in the previous investigation performed by the authors of this paper [22].

Conclusions
Analysis of Inconel 625/steel P355NH joint microstructure in the as-welded state and after two different, separated types of heat treatment (stress relief annealing and normalizing) allowed the following conclusions to be drawn. 1. The explosive welding process allowed to obtain joint between steel P355NH and Inconel 625 alloy. The wavy-shape joint was found to include melted zones having high concentration of imperfections such as cracks, voids and fragments of steel P355NH surface layer. 2. Stress relief annealing (620 °C/90 min) led to partial recrystallization of steel P355NH in the joint area. At the same time no changes in the grainy microstructure of Inconel 625 and chemical composition of the joint have been noticed. 3. Heat treatment in the form of normalizing (910 °C/30 min) resulted in complete recrystallization of grainy microstructure of both bonded materials. 4. As the result of normalizing the diffusion of Inconel 625 alloying elements into steel P355NH took place along the grain boundaries with tendency to formation of voids. 5. Additionally, another effect of post-weld normalizing is the formation of M6C and M23C6 carbides in Inconel 625 alloy in the joint zone.
Author Contributions: For research articles with several authors, a short paragraph specifying their individual contributions must be provided. The following statements should be used "conceptualization, R.K.; methodology, M.W. and M.G.; formal analysis, R.K.; investigation, R.K., M.W. and M.G.; writing-original draft preparation, R.K. and M.W.; writing-review and editing, M.W. and L.Ś.; supervision, L.Ś.", please turn to the CRediT taxonomy for the term explanation. Authorship must be limited to those who have contributed substantially to the work reported. Figure 17. Fe-Ni-Cr phase diagram [44] together with marked compositions of: iron-rich section (green dot) and nickel-chromium-rich section (red dot).