Structure and Thermal Properties of an Al-Based Metallic Glass-Polymer Composite

A composite material based on polyethylene terephthalate (PET, about 1% by mass) and Al85Y8Ni5Co2 metallic glass was obtained by mechanical alloying and consequent spark plasma sintering. The spark plasma sintering was performed at a temperature near to the super cooled liquid region of the metallic glass. Mechanical properties and the structural characterization of the composite material were obtained. It was conceived that composite samples (Al85Y8Ni5Co2/PET) have a better thermal conductivity in comparison with pure PET samples. The formation of the crystalline phases causes degradation of physical properties. It was calculated that the activation energy for crystallization of the Al85Ni5Y8Co2 metallic glass is higher than that of the other types of metallic glasses (Mg67.5Ca5Zn27.5 and Cu54Pd28P18) used for composite preparation previously. This denotes a good thermal stability of the chosen metallic glass.


Introduction
The unique properties of composite materials often make them more desirable than pure components. A combination of two different materials can result in enhanced properties, such as high strength and good ductility. The reinforcement elements help to improve the mechanical properties [1] of the composites. Metallic glasses have gained attention because of their remarkable properties [2]. They have outstanding corrosion and wear resistance and show unusual magnetic softness [3,4]. The procedure for casting metallic glasses is generally an inexpensive process. Metallic glasses have various applications in optical, electrical, magnetic, and mechanical materials, as well as in membranes, biological materials, and biotechnology [5].
Research activities have shown that polyethylene terephthalate (PET) can be used as an anti-friction polymer material [6]. The addition of a small quantity of polymer (PET) does not decrease the mechanical properties of the matrix that much during the process. The work of Yusof et al. [7] confirmed that PET can be used as anti-friction material within aluminum alloys. A composite material with enhanced properties was obtained by Kundig et al. [8]. The process for composite material preparation is done by co-extrusion or ball milling [9][10][11]. PET can control electrical properties of the materials [12]. A functional block copolymer [13] structure can also be produced with metallic nanoparticles.
Metallic glasses, which have low glass transition temperatures near the melting point of the polymer, can be used to produce metallic glass polymer composites. This allows the con-thermal-plastic deformation. Al-based metal glasses are good choices for this purpose. For example, Wang et al. presented Al-based matrix composites, reinforced with different fillers, with good mechanical properties [14][15][16][17][18]. The twist extrusion technique was used for processing polymers with metallic glass, and the mechanical properties of aluminum based alloys were improved [19]. Therefore, this technique can be used for aluminum based alloys, especially for merging aluminum based metallic glasses. Various types of hybrid composite materials were also produced [19,20].
This work is an extension of the earlier works related to composite materials preparation. In the previous work [21], a composite material based on high-density polyethylene (HDPE) reinforced with Mg 67.5 Ca 5 Zn 27.5 metallic glass (about 10% by mass) was obtained by co-extrusion and compression. The co-extrusion and compression procedures were performed at the temperatures in the supercooled liquid temperature region for both materials, between the glass transition temperature (T g ) and crystallization temperature (T x ). It was found that the composite samples (HDPE/Mg 67.5 Ca 5 Zn 27.5 ) had excellent adhesion towards each other, good thermal conductivity, and high elastic modulus. In another study [22], bulk composites based on Cu 54 Pd 28 P 18 metallic glass and polytetrafluoroethylene (PTFE, about 1% by mass) were obtained by ball milling and subsequent spark plasma sintering (SPS) methods. The spark plasma sintering procedure was carried out at the temperature close to the supercooled liquid temperature region of the metallic glass. The mechanical and structural characterization of the obtained metallic glass/polymeric composite samples was performed. It was found that composite samples (Cu 54 Pd 28 P 18 /PTFE) have better thermal conductivity in comparison with the pure PTFE samples. It was also shown that precipitation of the crystalline phases on the interface between the metallic glass particles leads to the degradation of their physical properties.
In the present work, the composite material based on the Al 85 Y 8 Ni 5 Co 2 metallic glass mixed with polyethylene terephthalate (PET, about 1% BY mass) was obtained and studied. Investigations of the structure and thermal properties of the obtained composites were performed.

Materials and Methods
A metallic glass ribbon (Al 85 Y 8 Ni 5 Co 2 ) was used for the sample preparation. Al-Y-Ni-Co alloy ingots were prepared by argon arc melting from the mixtures of pure Al, Ni, Co, and Y metals (purity of about 99.9% by mass). The ribbon samples were prepared by a copper roller melt spinning technique. The thickness of the resulting ribbon ranged from 0.02 to 0.03 mm, and the width ranged from 4.7 to 4.9 mm. A high density polyethylene terephthalate (PET) with an average particle size of about 200 µm was also used.
X-ray diffraction (XRD) experiments were performed with a DRON (CoKα radiation) diffractometer (Research and production enterprise "Bourevestnik", Saint Petersburg, Russian Federation) (2θ angles: from 10 to 120 degree. Step: 0.1 degree. Exposition time per step: 5 s. Beam size: 6-8 mm). The lattice parameters and phase compositions were determined with an accuracy of ±0.0001 nm and ±5%, respectively. The size of the crystallites in the powders was determined by the broadening of the diffraction pattern profiles with Cauchy functions. The accuracy of the crystallite size determination was ±1 nm. The percentage of the amorphous phase was determined, according to a kinematic standard method and annealed nickel powder as a standard [23].
The thermal properties of the prepared samples were examined using the NETZSCH DSC 204 F1 Phoenix Differential Scanning Calorimeter (DSC) (Netzsch Erich Netzsch GmbH & Co, Selb, Upper Franconia, Bavaria, Germany) with a heating rate of 10 • C/min. The maximum temperature was The glass transition temperature (T g ) and the crystallization temperature (T x ) were estimated from the DSC curves using the standard computer application.
The Netzsch LFA 447 NanoFlash provided the thermal diffusivity analyses of composite materials. Composite materials have been studied in the temperature range from 25 to 200 • C. The thermal conductivity was analyzed, according to the requirements of ASTM E1461.
The density of the samples obtained was measured by the hydrostatic weighing method using an analytical balance and the GR-202, using the density determination set and AD-1653, in ethanol.
Thermal conductivity of the samples was calculated using the following relation [24]: where α is the thermal diffusivity [mm 2 /s], C p is the specific heat capacity [J/g·K] and ρ is the sample density [g/cm 3 ]. The thermal conductivity, heat capacity, thermal diffusivity, and density of the obtained samples were determined with an accuracy of ±3%, ±5%, ±3%, and ±0.01 g/cm 3 , respectively. The accuracy of the activation energy estimation was of about ±5 kJ/mol. The activation energy of the crystallization was estimated by measuring the kinetics of crystallization at heating rates of 5, 10, 20, and 40 • C/min, according to the methods of Kissinger [25] (2) and Ozava [26] (3).

ln
T 2 where V is the heating rate, R is the gas constant, E is the activation energy, and C is a fitting constant. The pulverization of the metallic glass and the subsequent blending of the PET were carried out by the ball milling (BM) technique using a water-cooled high energy planetary ball mill (AGO-2S) with a rotation speed of 840 min −1 . Steel reactors and balls (4 mm diameter) were used. The mass ratio of the beads and the powder mixture was 10:1. The grinding time for pulverization of the glass ribbon was 45 min. The grinding time for mixing the metallic materials and the polymers was about 5 min.
The prepared composite powder mixture was placed into a cylindrical graphite die with 12.7 mm inside diameter, 30 mm outside diameter, and 30 mm height. The sample was also wrapped in a graphite sheet, 0.2 mm thick. The sintering was done using a spark plasma sintering system (SPS) (Labox 650, Sinter Land, Japan) [27][28][29][30] under the following conditions: heating rate 50 • C/min, maximum temperature of 245 • C, pressure up to 50 MPa, residence time 5 min. The parameters of the SPS configuration and the device schema are shown in Reference [27]. The SPS processing parameters, such as pressure, voltage, or pressing time, can be varied to achieve the required properties. The

Results and Discussion
The XRD diffraction pattern of the Al85Y8Ni5Co2 bands contained only one amorphous halo ( Figure 2a); no evidence of residual crystallinity peaks was detected. According to the XRD analysis, the curves are totally amorphous. DSC analysis of the ribbons showed that the metallic glass had a low transition temperature (Tg) of about 120 °C and a crystallization temperature (Tx) of about 260 °C (Figure 3a).
The main criterion for the selection of the polymeric material was its ability to get soft in the super cooled temperature region of the metallic glass phase. Polyethylene terephthalate (PET) is relative to this temperature range. This polymeric material is in the liquid state at a temperature close to the supercooled liquid region of the chosen metallic glass, and is capable of interacting with the metallic glass particles. Similarly, PET was chosen for its wide distribution and low cost.
The DSC curve of PET shows that, although the melting temperature of the polymer is 250 °C, it starts to change its properties and transform into a viscous liquid somewhat above 75 °C (Figure 2a). Thus, at temperatures above 250 °C both materials (Al85Y8Ni5Co2 metallic glass and PET) are in a viscous liquid state. Hence, it should be feasible to prepare the composite samples between their Tg and Tx.
To prepare bulk composite samples, starting with the SPS method, the initial materials must be in powder form. Therefore, grinding of the metallic glass ribbon (Al85Y8Ni5Co2) in a dispersed powder using the mechanical alloy method in a planetary ball mill was performed. It was found that the grinding process by ball milling results in the formation of the crystalline phases based on Al of approximately 20% (see Figure 2b and Table 1). For the SPS process, different temperatures from 200 °C and higher were applied, and the quality of the samples obtained was not so good. Hence, the temperature near Tg of the metallic glass Al85Y8Ni5Co2 (of approximately 250 °C) was chosen. However, the SPS process of the amorphous powder Al85Y8Ni5Co2 at 250 °C caused a small amount of crystalline phases to increase. In addition to the Al phase, the Al9Co2Ni phase was also found. Consequently, the total amount of the crystalline phases was about 25% (see Figure 2c and Table 1).
It should be recognized that the structure of the polymer after SPS is semi-crystalline/semiamorphous, and that most of x-ray diffraction peaks are below 30 degrees 2θ (Figure 2d). To obtain the composite samples, 1% by weight of PET polymer powders is added to Al85Y8Ni5Co2 powders during mechanical alloying. After ball milling, the amount of crystalline phase increases up to 30% (see Figure   Figure 1. Scheme used for manufacturing samples using a ball milling technique and subsequent spark plasma sintering.

Results and Discussion
The XRD diffraction pattern of the Al 85 Y 8 Ni 5 Co 2 bands contained only one amorphous halo ( Figure 2a); no evidence of residual crystallinity peaks was detected. According to the XRD analysis, the curves are totally amorphous. DSC analysis of the ribbons showed that the metallic glass had a low transition temperature (T g ) of about 120 • C and a crystallization temperature (T x ) of about 260 • C (Figure 3a).
The main criterion for the selection of the polymeric material was its ability to get soft in the super cooled temperature region of the metallic glass phase. Polyethylene terephthalate (PET) is relative to this temperature range. This polymeric material is in the liquid state at a temperature close to the supercooled liquid region of the chosen metallic glass, and is capable of interacting with the metallic glass particles. Similarly, PET was chosen for its wide distribution and low cost.
The DSC curve of PET shows that, although the melting temperature of the polymer is 250 • C, it starts to change its properties and transform into a viscous liquid somewhat above 75 • C (Figure 2a). Thus, at temperatures above 250 • C both materials (Al 85 Y 8 Ni 5 Co 2 metallic glass and PET) are in a viscous liquid state. Hence, it should be feasible to prepare the composite samples between their T g and T x .
To prepare bulk composite samples, starting with the SPS method, the initial materials must be in powder form. Therefore, grinding of the metallic glass ribbon (Al 85 Y 8 Ni 5 Co 2 ) in a dispersed powder using the mechanical alloy method in a planetary ball mill was performed. It was found that the grinding process by ball milling results in the formation of the crystalline phases based on Al of approximately 20% (see Figure 2b and Table 1). For the SPS process, different temperatures from 200 • C and higher were applied, and the quality of the samples obtained was not so good. Hence, the temperature near T g of the metallic glass Al 85 Y 8 Ni 5 Co 2 (of approximately 250 • C) was chosen. However, the SPS process of the amorphous powder Al 85 Y 8 Ni 5 Co 2 at 250 • C caused a small amount of crystalline phases to increase. In addition to the Al phase, the Al 9 Co 2 Ni phase was also found. Consequently, the total amount of the crystalline phases was about 25% (see Figure 2c and Table 1). 2e and Table 1). After the SPS process at 250 °C of the composite powder (Al85Y8Ni5Co2/PET metal glass), the amount of crystalline phases increases to 40% (Figure 2f and Table 1).         It should be recognized that the structure of the polymer after SPS is semi-crystalline/ semi-amorphous, and that most of x-ray diffraction peaks are below 30 degrees 2θ (Figure 2d). To obtain the composite samples, 1% by weight of PET polymer powders is added to Al 85 Y 8 Ni 5 Co 2 powders during mechanical alloying. After ball milling, the amount of crystalline phase increases up to 30% (see Figure 2e and Table 1). After the SPS process at 250 • C of the composite powder (Al 85 Y 8 Ni 5 Co 2 /PET metal glass), the amount of crystalline phases increases to 40% (Figure 2f and Table 1).
The thermal conductivity analysis of the prepared bulk samples is presented in Table 2 and Figure 3b. It is clearly shown that the thermal conductivity of the composite material is reduced by adding only 1% by weight of PET, relative to the pure metal glass sample. The difference between the thermal conductivity of the composite sample and the metal glass sample is about 50%. This difference is much greater compared to the results presented in our previous works (in the case of composite materials with other polymers and metallic glass materials) [21,22]. It must also be taken into account that the bulk composite samples obtained by SPS were fragile. This reduction in thermal conductivity and brittleness of the bulk samples, obtained by the SPS, should be explained by the formation of the thin PET films on the boundaries between the metallic glass powder particles and, thus, the appearance of the photon scattering centers. In addition, this could be explained by the protective layer of Al oxide on the surface of the particles of metallic glass powder and the absence of diffusion reaction between the particles, as indicated in the previous work [21].
The SEM images of the bulk sample prepared by SPS are shown in Figure 4a. The compound after SPS is very porous. Some of the metallic glass particles are covered with the polymer (Figure 4b), and some of them were connected to each other by the necks (Figure 4c,d). However, such interactions between particles were not observed everywhere. The surface of the Al 85 Y 8 Ni 5 Co 2 metallic glass strip and the surface of the overall sample of pure PET polymer, obtained by SPS, are shown in Figure 4e,f for comparison. The porous structure of the bulk samples was also responsible for the low thermal conductivity.  The activation energy of the crystallization process was calculated using the equations of Kissinger (2) and Ozava (3). These values are shown in Table 3 in comparison with the activation energies of other types of metallic glasses studied in our previous works (Mg67.5Ca5Zn27.5 and Cu54Pd28P18) [21,22]. The activation energy of the Al85Y8Ni5Co2 metallic glass is greater (Table 3); in addition, it is in a good correspondence with the activation energy of the metallic glasses based on Al, obtained in Reference [31]. Therefore, we can assume that, indirectly, it influences the quality of the bulk composite samples. Therefore, at higher activation energies for crystallization, it is more The activation energy of the crystallization process was calculated using the equations of Kissinger (2) and Ozava (3). These values are shown in Table 3 in comparison with the activation energies of other types of metallic glasses studied in our previous works (Mg 67.5 Ca 5 Zn 27.5 and Cu 54 Pd 28 P 18 ) [21,22]. The activation energy of the Al 85 Y 8 Ni 5 Co 2 metallic glass is greater (Table 3); in addition, it is in a good correspondence with the activation energy of the metallic glasses based on Al, obtained in Reference [31]. Therefore, we can assume that, indirectly, it influences the quality of the bulk composite samples. Therefore, at higher activation energies for crystallization, it is more difficult to initialize the interaction process between the metallic glassy particles and the mass transfer obtained between the two different materials in the neighboring particles.

Conclusions
A method was proposed that allows obtaining a composite material based on a polyethylene terephthalate and Al 85 Y 8 Ni 5 Co 2 metallic glass. The method comprises SPS consolidation of the polymer blending with the metallic glass particles at a temperature near the temperature of the supercooled liquid of the metallic glass and the melting temperature of the PET.
The obtained composite samples have a superior thermal conductivity compared to the pure PET samples. The activation energy of the crystallization process has been calculated and compared with the activation energies of other types of metallic glasses used for composites preparation in previous works (Mg 67.5 Ca 5 Zn 27.5 and Cu 54 Pd 28 P 18 ). It was shown that the Al 85 Y 8 Ni 5 Co 2 metallic glass has the highest activation energy in comparison with the other metallic glasses (Mg 67.5 Ca 5 Zn 27.5 and Cu 54 Pd 28 P 18 ). The relatively higher activation energy of the amorphous alloy studied in this research indicates its higher stability with respect to the crystallization process upon heating. However, significant oxidation of the surface of the alloy particles leads to a modification in the chemical composition of the surface layers of the material, and as a result, to a partial surface crystallization of the powder. This affects the quality of the composites produced, since the appearance of crystalline phases in metallic glass usually leads to deterioration of physical properties. The obtained results can be beneficial in terms of obtaining different antifriction composite materials based on metallic glass and self-lubricated polymers.