The Tribocorrosion Behavior of High-Nitrogen Bearing Stainless Steel in Acetic Acid at Various Applied Loads

: High-nitrogen stainless steels, which are developed by replacing nickel with nitrogen, have been widely applied in manufacturing wear parts in mechanical engineering. In this study, the tribocorrosion performance of a ferritic high-nitrogen bearing stainless steel (40Cr15Mo2VN) under acetic acid solution with a pH of 3.0 was investigated under different loads ranging from 25 N to 125 N. Quantitative calculations indicated that pure mechanical wear was the predominant cause of material degradation, while the corrosion-accelerated wear component also played a crucial role. The material loss induced by both tribocorrosion and mechanical wear increased with increasing load, leading to severe delamination at sliding surfaces and larger wear debris.


Introduction
Helicopter structural components are being subjected to the ever-increasing demand for materials with improved performance and safety.However, these structures are inevitably exposed to harsh conditions and continually influenced by high temperature, salt fog and acid rain.For moving components such as bearings or gears, the damage induced by wear, scuffing and debris damage will also lead to premature failure.A comprehensive investigation revealed that scuffing and debris damage due to wear and pitting induced by corrosion account for over 61% of the causes of failure occurring in helicopter structural components [1].In the case of bearings, as the components most likely to fail, it appears that the majority of failures involve specific low-alloy bearing steels such as SAE 52100.
High-nitrogen stainless steel has become an increasingly important structural material, being widely used in helicopter bearings [2][3][4][5].High-nitrogen stainless steel is widely used in the aerospace, marine, nuclear and other high-end manufacturing industries, and, at the same time, is also expected to play a role in lightweight automobiles, new energy and other fields, as a promising material for the sustainable development of human society [6][7][8].Alloying steel with nitrogen has a beneficial effect on mechanical performance, corrosion and fatigue resistance [9].During the last few decades, the effect of nitrogen in steels on pitting, crevices and general corrosion has been identified [10,11].The incorporation of nitrogen in steels can not only enhance yield strength, toughness and wear resistance but also improve steel's repassivation ability and resistance against corrosion [12].Although the effect of nitrogen on general corrosion differs due to the uncontrollable preparation method and experimental conditions, the effect of nitrogen on pitting corrosion and crevice corrosion has been clearly identified [11].Gavriljudk et al. reported a positive effect of nitrogen on austenitic stainless steels as a consequence of the enhanced thermodynamic stability of a solid solution and thus its much-improved mechanical properties and corrosion resistance [13,14] Similar conclusions have been continually obtained, revealing that nitrogen expands and stabilizes the austenitic-phase region and serves as an interstitial element that improves solid-solution strengthening [15,16].
More recently, the electrochemical corrosion behavior of high-nitrogen stainless steel in aqueous solutions has been addressed [16][17][18].The corrosion resistance of all types of austenitic stainless steel generally depends on the bilayer structure of the formed passive film in an aqueous solution.Specifically, passive films of high-nitrogen stainless steel have a double-layer structure of inner metal oxides and outer metal hydroxides depending on the exposed environment [19].However, the experiments conducted by Qiao et al. revealed that the formed passive films were not stable in acetic acid, and the corrosion behavior was influenced by oxygen content, sulfuric acid concentration and surface roughness [20].
The more difficult aspect of the tribocorrosion behavior is the need to combine the sciences of tribology together with simultaneous corrosion.Current research is focused on tribocorrosion in seawater environments [5,[21][22][23], but less research has been conducted in acidic solutions.M.M. Singh studied the corrosion behavior of mild steel in acetic acid solutions, and the variation in the corrosion rate of mild steel with varying concentrations of acetic acid solution was evaluated and showed a notable resemblance [24].When corrosion is coupled with mechanical wear, the total material loss is not simply the sum of wear-corrosion synergism [25].The results for the interaction between corrosion and wear are not consistent; publications referring to both its positive and negative effects, which depend on the steel type and corrosive medium, have been reported [21][22][23].For highnitrogen stainless steel, wear-corrosion and their interaction are not yet fully understood, and limiting the suitable choices for a given application will extend its service life [26,27].
In this study, the tribocorrosion behavior of 40Cr15Mo2VN as a high-nitrogen stainless steel in a corrosive environment was investigated.An accelerated corrosion-wear experimental method was established using acetic acid solution with a pH value of 3.0 as the corrosive medium.The synergy between mechanical wear in the absence of a corrosive medium and corrosion in the absence of wear was determined and discussed.Special attention was given to the microstructural evolution at surfaces under different applied loads, which is imperative to the efficient and safe use of high-nitrogen stainless steel in corrosive conditions.

Materials and Solutions
A commercial high-nitrogen stainless-steel 40Cr15Mo2VN was provided by Luoyang LYC Bearing Co., LTD., in China, and its chemical composition is listed in Table 1.Before wear tests, the 40Cr15Mo2VN specimen needed to be machined to the specified ring block-dimensions.The ring block machining requirements were a 54 mm outer diameter, 38 mm inner diameter and 13 mm height.Analytical-grade acetic acid was provided by Lianlong Bohua (Tianjin) Pharmaceutical Chemistry Co., Ltd.(China).The counterpart made of a ceramic Si 3 N 4 pin was provided by Dongguan Kezhong Ceramic Co., Ltd.(Dongguan, China) The Si 3 N 4 counterpart had dimensions of Φ5.0 × 15 mm with a 0.1 mm chamfer and a flat working surface with a radius of 4.80 mm.The corrosive medium was prepared by dissolving acetic acid in deionized water with a constant pH value of 3.0, and the experimental medium used for mechanical wear experiments was deionized water.To achieve as consistent a surface roughness as possible for the experimental samples, 800-grit SiC sandpaper was used for uniform sanding, sanding and ultrasonic cleaning with alcohol, and insulating paint was used for the other sides of the ring block, except for the working surface.

Tribocorrosion Tests
The tribocorrosion behavior of 40Cr15Mo2VN in acetic acid solution was studied by coupling the vertical universal friction machine MMW-1 with the electrochemical workstation Prinception Versa STAT 3F and selecting a three-pin-disk model.In the equipment construction, 40Cr15Mo2VN rings were used as the working electrode, Pt gauze was used as the counter electrode, and a commercial Ag/AgCl electrode was selected as the reference electrode.A schematic illustration of the tribocorrosion apparatus is presented in Figure 1, for which it was possible to obtain the trend of the real-time electrochemical signal during the experiment.

Tribocorrosion Tests
The tribocorrosion behavior of 40Cr15Mo2VN in acetic acid solution was studie coupling the vertical universal friction machine MMW-1 with the electrochemical w station Prinception Versa STAT 3F and selecting a three-pin-disk model.In the equipm construction, 40Cr15Mo2VN rings were used as the working electrode, Pt gauze was as the counter electrode, and a commercial Ag/AgCl electrode was selected as the r ence electrode.A schematic illustration of the tribocorrosion apparatus is presente Figure 1, for which it was possible to obtain the trend of the real-time electrochem signal during the experiment.The interaction between corrosion and mechanical wear was evaluated in accord with the ASTM G119-09 standard.The total mass loss rate T was calculated accordin We conducted tribocorrosion and mechanical wear tests at different loads ranging from 25 N to 125 N with a speed of 120 mm/s for 30 min.The open-circuit potential (OCP) curve was measured at different loads for 5 min with a constant interval of 10 min.The Tafel polarization curves were monitored using a scan rate of 10 mV/s from −0.6 V to 0.3 V in acetic acid solution before and during tribocorrosion tests.Pure mechanical wear was carried out in deionized water.
The interaction between corrosion and mechanical wear was evaluated in accordance with the ASTM G119-09 standard.The total mass loss rate T was calculated according to Equation (1).
where C 0 is the material loss induced by corrosion in the absence of wear, W 0 is the material loss induced by wear in the absence of a corrosive medium, and S is the wear-corrosion synergism.
where m 0 is the initial sample mass; m 1 is the final mass of the sample tested in deionized water; and m 2 is the final mass of the sample after tribocorrosion.A is the abrasion mark area, which measured 671.0 mm 2 in this experiment, and ρ is the density of 40Cr15Mo2VN, which was 7.704 g/cm 3 .t is the test duration.
The corrosion component without wear C 0 and total corrosion component C w could be calculated based on Equations ( 4) and ( 5) [22,23].
where i 0 and i are the corrosion current densities of the static corrosion and tribocorrosion processes, respectively.E w is the equivalent weight of the alloy, which was 27.92 in this study.

Characterization
The morphology of the damaged surface and wear debris of 40Cr15Mo2VN were observed with a JEM-5600LV scanning electron microscope (SEM, JEOL Ltd., Tokyo, Japan) with an operating voltage of 200 V, a working distance of 20 mm and a speckle beam current of 20 A. The morphology of 40Cr15Mo2VN was observed using Electron Backscatter Diffraction (EBSD, EDAX Hikari Plus, EDAX Inc., Mahwah, NJ, USA).To obtain an ideal EBSD sample with no residual stress layer, the ion beam treatment was made to be extremely flat, free of abrasive contamination and scratch-free, with little damage to the sample and essentially no deformation layer.A D8 Discover25 high-resolution X-ray diffractometer (XRD, Bruker Corporation, Karlsruhe, Germany) was used to test the metal surface and to obtain the curves, with a scanning angle range of 30-110 • and step of 0.02 • .The rubbed surface of the worn pin was observed using an OLYMPUS STM6 optical microscope (Olympus Ltd., Tokyo, Japan), and pictures were captured.

Microstructure
Figure 2 shows the crystalline structure of 40Cr15Mo2VN with 0.18 w.t.% nitrogen.The X-ray diffraction pattern of the as-received 40Cr15Mo2VN indicates that its phase composition consisted of only ferrite.Meanwhile, no obvious peaks assigned to austenite or nitride were observed due to the relatively low nitrogen content [28,29] The IPF map further confirms that 40Cr15Mo2VN consisted of equiaxed crystals that exhibited a relatively uniform grain size and aggregation of <110>, <200> and <211> orientations.The average grain size was approximately 10 µm, which is lower than that of typical austenitic highnitrogen stainless steel [20].

Tribocorrosion Behavior
The tribocorrosion behavior of 40Cr15Mo2VN in acetic acid was investigated, an the friction coefficient and material loss rate under different loads are shown in Figure The friction coefficient under both tribocorrosion and mechanical wear increased linear with increasing load.Typically, the friction coefficient generated by sliding during m chanical wear is higher than that produced during corrosive wear, especially at low loads.However, the material loss rate under fretting wear was higher than that und mechanical wear, and the difference became more significant as the load increased.Whe the applied load was 25 N, the wear coefficient in the tribocorrosion condition was 1.9 10 −4 mm 3 /Nm, while the wear coefficient in the mechanical wear condition was slight lower at 1.6 × 10 −4 mm 3 /Nm.At 125 N, the wear coefficient induced by tribocorrosio reached 21.9 × 10 −4 mm 3 /Nm, and the mechanical wear coefficient under the same loa was measured as 4.1 × 10 −4 mm 3 /Nm.That is, the incorporation of simultaneous corrosio promoted wear loss but prevented severe friction.The components of corrosion-wear synergism are shown in Figure 4.As can be see in Figure 4a, the total material loss T mainly consisted of mechanical wear W0 and corr sion-wear interaction S since the material loss induced by corrosion was negligible, whic

Tribocorrosion Behavior
The tribocorrosion behavior of 40Cr15Mo2VN in acetic acid was investigated, and the friction coefficient and material loss rate under different loads are shown in Figure 3.The friction coefficient under both tribocorrosion and mechanical wear increased linearly with increasing load.Typically, the friction coefficient generated by sliding during mechanical wear is higher than that produced during corrosive wear, especially at lower loads.However, the material loss rate under fretting wear was higher than that under mechanical wear, and the difference became more significant as the load increased.When the applied load was 25 N, the wear coefficient in the tribocorrosion condition was 1.9 × 10 −4 mm 3 /Nm, while the wear coefficient in the mechanical wear condition was slightly lower at 1.6 × 10 −4 mm 3 /Nm.At 125 N, the wear coefficient induced by tribocorrosion reached 21.9 × 10 −4 mm 3 /Nm, and the mechanical wear coefficient under the same load was measured as 4.1 × 10 −4 mm 3 /Nm.That is, the incorporation of simultaneous corrosion promoted wear loss but prevented severe friction.

Tribocorrosion Behavior
The tribocorrosion behavior of 40Cr15Mo2VN in acetic acid was investigated, a the friction coefficient and material loss rate under different loads are shown in Figure The friction coefficient under both tribocorrosion and mechanical wear increased linear with increasing load.Typically, the friction coefficient generated by sliding during m chanical wear is higher than that produced during corrosive wear, especially at low loads.However, the material loss rate under fretting wear was higher than that und mechanical wear, and the difference became more significant as the load increased.Wh the applied load was 25 N, the wear coefficient in the tribocorrosion condition was 1.9 10 −4 mm 3 /Nm, while the wear coefficient in the mechanical wear condition was sligh lower at 1.6 × 10 −4 mm 3 /Nm.At 125 N, the wear coefficient induced by tribocorrosi reached 21.9 × 10 −4 mm 3 /Nm, and the mechanical wear coefficient under the same lo was measured as 4.1 × 10 −4 mm 3 /Nm.That is, the incorporation of simultaneous corrosi promoted wear loss but prevented severe friction.The components of corrosion-wear synergism are shown in Figure 4.As can be se in Figure 4a, the total material loss T mainly consisted of mechanical wear W0 and corr sion-wear interaction S since the material loss induced by corrosion was negligible, whi being typically three orders lower than the values of both W0 and S. All the material lo components were significantly affected by the applied load.The corrosion-wear intera tion showed positive values, illustrating that corrosion produces additional wear.Regar The components of corrosion-wear synergism are shown in Figure 4.As can be seen in Figure 4a, the total material loss T mainly consisted of mechanical wear W 0 and corrosion-wear interaction S since the material loss induced by corrosion was negligible, Metals 2023, 13, 1287 6 of 12 which being typically three orders lower than the values of both W 0 and S. All the material loss components were significantly affected by the applied load.The corrosion-wear interaction showed positive values, illustrating that corrosion produces additional wear.Regarding the synergy in wear components shown in Figure 4b, it is clear that the mechanical wear was accelerated by corrosion, showing a positive value of ∆W c .At higher loads, the synergy ∆W c accounted for a larger proportion than mechanical wear W 0 of total wear loss W c .At 25 N, the value of synergy ∆W c was measured as 1.4 mm/y, accounting for approximately 6% of the total wear loss W c of 25.1 mm/y.As the load increased to 125 N, the synergy ∆W c grew to 1385.4 mm/y, contributing over 83% of the total wear loss W c .The unit is millimeters per year, which measures the thickness of the material surface that is consumed by corrosion each year.The wear-corrosion components increased at higher loads, showing mutually accelerated wear and corrosion.The total material loss mainly consisted of two parts, namely, pure mechanical wear (W 0 ) and corrosion-accelerated wear (∆W c ).For 40Cr15Mo2VN sliding against the harder ceramic counterpart, the mechanical shear and removal became more prominent with increasing load.Then, the fresh surface was exposed to acetic acid, and larger-scale anodic dissolution took place.That is, increased contact stress and accelerated corrosion in the form of anodic dissolution conspired to increase both W 0 and ∆W c .als 2023, 13, x FOR PEER REVIEW 6 of synergy ΔWc accounted for a larger proportion than mechanical wear W0 of total wear l Wc.At 25 N, the value of synergy ΔWc was measured as 1.4 mm/y, accounting for appr imately 6% of the total wear loss Wc of 25.1 mm/y.As the load increased to 125 N, synergy ΔWc grew to 1385.4 mm/y, contributing over 83% of the total wear loss Wc.T unit is millimeters per year, which measures the thickness of the material surface tha consumed by corrosion each year.The wear-corrosion components increased at high loads, showing mutually accelerated wear and corrosion.The total material loss mai consisted of two parts, namely, pure mechanical wear (W0) and corrosion-accelera wear (ΔWc).For 40Cr15Mo2VN sliding against the harder ceramic counterpart, the m chanical shear and removal became more prominent with increasing load.Then, the fre surface was exposed to acetic acid, and larger-scale anodic dissolution took place.That increased contact stress and accelerated corrosion in the form of anodic dissolution co spired to increase both W0 and ΔWc.

Electrochemical Tests
Figure 5a shows the open-circuit potential of the 40Cr15Mo2VN alloy under differ applied loads.As 40Cr15Mo2VN was exposed to acetic acid, the corrosion poten shifted toward the positive direction, indicating that the 40Cr15Mo2VN alloy has a stro passivation ability.The passive tread terminated immediately after the sliding proc began and rapidly reached the balance between passivation and wear of the formed p sive film, showing a constant value of corrosion potential during sliding.As the appl load increased from 25 N to 125 N, the corrosion potential decreased from −0.49 V to −0 V, which is closely related to the degraded corrosion resistance at higher loads.Figure shows the potentiodynamic polarization curves of 40Cr15Mo2VN at various loads, a the Ecorr and icorr determined by fitting the potentiodynamic polarization curves are list in Table 2.The applied load had a considerable effect on Ecorr, which was −0.418 V befo sliding and gradually decreased from −0.471 V at 25 N to −0.548 V at 125 N during slidi with increasing load.The increasing icorr shows that the passive films formed under high loads had lower stability.When the applied load increased to 125 N, the value of icorr s nificantly increased, being approximately 100 times higher than that at 25 N.These obs

Electrochemical Tests
Figure 5a shows the open-circuit potential of the 40Cr15Mo2VN alloy under different applied loads.As 40Cr15Mo2VN was exposed to acetic acid, the corrosion potential shifted toward the positive direction, indicating that the 40Cr15Mo2VN alloy has a strong passivation ability.The passive tread terminated immediately after the sliding process began and rapidly reached the balance between passivation and wear of the formed passive film, showing a constant value of corrosion potential during sliding.As the applied load increased from 25 N to 125 N, the corrosion potential decreased from −0.49 V to −0.54 V, which is closely related to the degraded corrosion resistance at higher loads.Figure 5b shows the potentiodynamic polarization curves of 40Cr15Mo2VN at various loads, and the E corr and i corr determined by fitting the potentiodynamic polarization curves are listed in Table 2.The applied load had a considerable effect on E corr , which was −0.418 V before sliding and gradually decreased from −0.471 V at 25 N to −0.548 V at 125 N during sliding with increasing load.The increasing i corr shows that the passive films formed under higher loads had lower stability.When the applied load increased to 125 N, the value of i corr significantly increased, being approximately 100 times higher than that at 25 N.These observations demonstrate that corrosion damage is exacerbated at higher loads.
The anodic iron dissolution was accompanied by two parallel cathodic reacti namely, hydrogen ion reduction and the direct reduction of the undissociated acetic a which are shown in Equations ( 7) and ( 8) [27,32].

Damage Surface Morphologies
Figure 6 shows the typical damage morphology of the 40Cr15Mo2VN alloy un both tribocorrosion and mechanical wear conditions.The damage mechanism of mate loss of 40Cr15Mo2VN was delamination of the metallic matrix, which became more pr inent with increasing load.The damage induced by tribocorrosion was much more sev than that induced by mechanical wear, which is consistent with the previously de mined higher material loss.The corrosion of acetic acid leads to higher wear due to di lution of the surface layer, causing a rougher surface and thus making it easier to rem under the continual shear of the ceramic counterpart.Sufficient studies have been conducted to interpret the tribocorrosion mechanisms of stainless steels in the presence of acetic acid.The material loss of 40Cr15Mo2VN induced by corrosion in acetic acid with a relatively low pH value of 3.0 was due to iron dissolution, which is expressed as shown in Equation (6) [30,31].
The anodic iron dissolution was accompanied by two parallel cathodic reactions, namely, hydrogen ion reduction and the direct reduction of the undissociated acetic acid, which are shown in Equations ( 7) and (8) [27,32].

Damage Surface Morphologies
Figure 6 shows the typical damage morphology of the 40Cr15Mo2VN alloy under both tribocorrosion and mechanical wear conditions.The damage mechanism of material loss of 40Cr15Mo2VN was delamination of the metallic matrix, which became more prominent with increasing load.The damage induced by tribocorrosion was much more severe than that induced by mechanical wear, which is consistent with the previously determined higher material loss.The corrosion of acetic acid leads to higher wear due to dissolution of the surface layer, causing a rougher surface and thus making it easier to remove under the continual shear of the ceramic counterpart.In both tribocorrosion and mechanical wear conditions, ploughs and furrows paralle the sliding direction were observed on the worn counterfaces, which was caused by sliding between the asperities of 40Cr15Mo2VN and its ceramic counterpart.This i cates abrasive wear in the principal damage mechanism with or without the corro medium.At higher applied loads, the abrasive wear became more severe, being cha terized by a larger wear area and deeper grooves in the microscopic view.Compared w  In both tribocorrosion and mechanical wear conditions, ploughs and furrows parallel to the sliding direction were observed on the worn counterfaces, which was caused by the sliding between the asperities of 40Cr15Mo2VN and its ceramic counterpart.This indicates abrasive wear in the principal damage mechanism with or without the corrosive medium.At higher applied loads, the abrasive wear became more severe, being characterized by a larger wear area and deeper grooves in the microscopic view.Compared with mechanical wear, the damage induced by the combined effect of wear and corrosion was more prominent, possibly due to the contact surfaces of 40Cr15Mo2VN, which were roughened by corrosion, further leading to the acceleration of abrasive wear.Meanwhile, it can be seen that the ceramic counterpart was patched with adhered or transferred 40Cr15Mo2VN composed of many small clumps that had gathered during continuous sliding friction, which was sheared from 40Cr15Mo2VN by the asperities of the harder Si 3 N 4 ceramic counterpart.The typical wear debris is shown in Figure 8.On a morphological level, it w vealed that the wear debris generated under both tribocorrosion and mechanical wea in the form of laminar flakes with different scales ranging from several microns to se hundred microns, depending on the applied load.Corrosion also influenced the mor ogy of wear debris, generating much finer and looser detached particles during trib The typical wear debris is shown in Figure 8.On a morphological level, it was revealed that the wear debris generated under both tribocorrosion and mechanical wear was in the form of laminar flakes with different scales ranging from several microns to several hundred microns, depending on the applied load.Corrosion also influenced the morphology of wear debris, generating much finer and looser detached particles during tribocorrosion under the same load.It seems that the detached debris, due to wear, was removed from the contact area immediately after the contact between the metallic surface and the hard ceramic counterface, implying that the surface damage was primarily induced by the combined effect of chemical corrosion and mechanical wear.In other words, the removal of wear debris prevents the formation of a third body that further abrades the metallic surfaces and generates secondary damage as plows and furrows.As the applied load increases, increasing the ability of the pins to jackknife into the metal, when the rotation begins, plastic flow of the metal occurs, changing from furrow wear to spalling wear.

Conclusions
The tribocorrosion behavior of high-nitrogen stainless-steel 40Cr15Mo2VN under different loads in acetic acid solution with a pH of 3.0 was investigated in this study.The components of mechanical wear, corrosion and wear-corrosion interaction were quanti-

Conclusions
The tribocorrosion behavior of high-nitrogen stainless-steel 40Cr15Mo2VN under different loads in acetic acid solution with a pH of 3.0 was investigated in this study.The components of mechanical wear, corrosion and wear-corrosion interaction were quantitatively determined.The aim of this study was to develop engineering applications of nickel-free high-nitrogen steels, such as bearings, shafts and gears, in corrosive environments.However, the microstructural evolution and damage mechanisms under both tribocorrosion and mechanical wear and under different corrosive environments are not clear and need more investigation.The main conclusions of this work are presented below: 1.
A positive synergy between corrosion and wear was quantitatively determined.Simultaneous corrosion significantly promoted mechanical wear during the tribocorrosion process.2.
The material loss induced by the tribocorrosion process in acetic acid solution primarily consisted of mechanical wear and corrosion-accelerated wear.The contribution of corrosion-wear synergism increased from approximately 6% at 25 N to over 83% at the highest load of 125 N.

3.
The material loss induced by mechanical wear increased with increasing load.The failure of 40Cr15Mo2VN was dominated by typical delamination wear.4.
The corrosion mechanism of 40Cr15Mo2VN in acetic acid solution was mainly induced by general anodic dissolution, which promotes wear damage at surfaces.

Figure 1 .
Figure 1.A schematic diagram of the tribocorrosion apparatus.

Figure 1 .
Figure 1.A schematic diagram of the tribocorrosion apparatus.

Figure 3 .
Figure 3. (a) Friction coefficient and (b) wear rate of 40Cr15Mo2VN under different applied loads acetic acid solution with a pH value of 3.

Figure 3 .
Figure 3. (a) Friction coefficient and (b) wear rate of 40Cr15Mo2VN under different applied loads acetic acid solution with a pH value of 3.

Figure 3 .
Figure 3. (a) Friction coefficient and (b) wear rate of 40Cr15Mo2VN under different applied loads in acetic acid solution with a pH value of 3.

Figure 4 .
Figure 4. (a) The contribution of wear (W0), corrosion (C0) and wear-corrosion synergy (S) to total material loss rate (T) and (b) total wear rate (Wc), mechanical wear rate (W0) and the change the mechanical wear rate due to corrosion (∆Wc) of 40Cr15Mo2VN under different applied load acetic acid solution with a pH value of 3.

Figure 4 .
Figure 4. (a) The contribution of wear (W 0 ), corrosion (C 0 ) and wear-corrosion synergy (S) to the total material loss rate (T) and (b) total wear rate (W c ), mechanical wear rate (W 0 ) and the change in the mechanical wear rate due to corrosion (∆W c ) of 40Cr15Mo2VN under different applied loads in acetic acid solution with a pH value of 3.

Figure 5 .
Figure 5. (a) Open-circuit potential (OCP) curves and (b) Tafel polarization curves of 40Cr15Mo2 under different applied loads in acetic acid solution with a pH value of 3.

Figure 5 .
Figure 5. (a) Open-circuit potential (OCP) curves and (b) Tafel polarization curves of 40Cr15Mo2VN under different applied loads in acetic acid solution with a pH value of 3.

Figure 6 .
Figure 6.Typical morphologies of damaged surfaces of 40Cr15Mo2VN under different app loads of 50 N, 100 N and 125 N.

Figure 7
Figure7displays the corresponding worn surfaces of the Si3N4 ceramic counterpa In both tribocorrosion and mechanical wear conditions, ploughs and furrows paralle the sliding direction were observed on the worn counterfaces, which was caused by sliding between the asperities of 40Cr15Mo2VN and its ceramic counterpart.This i cates abrasive wear in the principal damage mechanism with or without the corro medium.At higher applied loads, the abrasive wear became more severe, being cha terized by a larger wear area and deeper grooves in the microscopic view.Compared w

Figure 6 .
Figure 6.Typical morphologies of damaged surfaces of 40Cr15Mo2VN under different applied loads of 50 N, 100 N and 125 N.

Figure 7
Figure 7 displays the corresponding worn surfaces of the Si 3 N 4 ceramic counterparts.In both tribocorrosion and mechanical wear conditions, ploughs and furrows parallel to the sliding direction were observed on the worn counterfaces, which was caused by the sliding between the asperities of 40Cr15Mo2VN and its ceramic counterpart.This indicates abrasive wear in the principal damage mechanism with or without the corrosive medium.At higher applied loads, the abrasive wear became more severe, being characterized by a larger wear area and deeper grooves in the microscopic view.Compared with mechanical wear,

REVIEW 9 Figure 7 .
Figure 7.Typical morphologies of Si3N4 ceramic counterfaces under different applied loads of 100 N and 125 N.

Figure 7 .
Figure 7.Typical morphologies of Si 3 N 4 ceramic counterfaces under different applied loads of 50 N, 100 N and 125 N.

REVIEW 10 of 12 Figure 8 .
Figure 8.Typical morphologies of wear debris of 40Cr15Mo2VN under different applied loads of 50 N, 100 N and 125 N.

Figure 8 .
Figure 8.Typical morphologies of wear debris of 40Cr15Mo2VN under different applied loads of 50 N, 100 N and 125 N.

Table 2 .
Corrosion potential and corrosion current density of 40Cr15Mo2VN under different applied loads in acetic acid solution with a pH value of 3.