A Comprehensive Review on the Conventional and Non-Conventional Machining and Tool-Wear Mechanisms of INCONEL ®

: Nickel-based superalloys, namely INCONEL ® variants, have had an increase in applications throughout various industries like aeronautics, automotive and energy power plants. These superalloys can withstand high-temperature applications without suffering from creep, making them extremely appealing and suitable for manufactured goods such as jet engines or steam turbines. Nevertheless, INCONEL ® alloys are considered difﬁcult-to-cut materials, not only due to their superior material properties but also because of their poor thermal conductivity ( k ) and severe work hardening, which may lead to premature tool wear (TW) and poor ﬁnal product ﬁnishing. In this regard, it is of paramount importance to optimise the machining parameters, to strengthen the process performance outcomes concerning the quality and cost of the product. The present review aims to systematically summarize and analyse the progress taken within the ﬁeld of INCONEL ® machining sensitively over the past ﬁve years, with some exceptions, and present the most recent solutions found in the industry, as well as the prospects from researchers. To accomplish this article, ScienceDirect, Springer, Taylor & Francis, Wiley and ASME have been used as sources of information as a result of great ﬁdelity knowledge. Books from Woodhead Publishing Series, CRC Press and Academic Press have been also used. The main keywords used in searching information were: “Nickel-based superalloys”, “INCONEL ® 718”, “INCONEL ® 625” “INCONEL ® Machining processes” and “Tool-wear mechanisms”. The combined use of these keywords was crucial to ﬁlter the huge information currently available about the evolution of INCONEL ® machining technologies. As a main contribution to this work, three SWOT analyses are provided on information that is dispersed in several articles. It was found that signiﬁcant progress in the traditional cutting tool technologies has been made, nonetheless, the machining of INCONEL ® 718 and 625 is still considered a great challenge due to the intrinsic characteristics of those Ni-based-superalloys, whose machining promotes high-wear to the tools and coatings used.


Introduction
With the increasing requirement to achieve the best thermal efficiency in the field of aeronautics [1,2] and energy power plants steam turbines [3], applications in which aluminium and steel would succumb to creep [4] as a result of thermally induced crystal vacancies [5], nickel-based (Table 1) alloys became a very attractive solution for hightemperature operation [6][7][8][9].Ni-Cr-Fe superalloys (Figure 1, blue zone), better known as INCONEL ® (trademark registered by the International Nickel Company of Delaware and New York [10]), are materials resistant to oxidation, caustic and high-purity water corrosion, and stress-corrosion cracking (SCC) [11], optimal for service in extreme environments subjected to high mechanical loads [12], within numerous applications and characteristics (Table 2).
Table 1.Some physical properties of nickel (adapted from [7]).A brief insight is provided with the most known alloys, including the INCONEL ® 600, a Ni-Cr alloy that offers high levels of resistance to several corrosive elements.In high-temperature situations, INCONEL ® 600 will not succumb to Cl-ion SCC or general oxidation, but it can still undergo corrosion by sulphuration deterioration in the high-temperature flue gas.This was a research topic by Wei,et al. [14].INCONEL ® 600 also suffers from severe hydrogen embrittlement at 250 • C [15].Nonetheless, this alloy is recommended for use in furnace components and chemical processing equipment [16].Moreover, INCONEL ® 600 is also effectively used in the food industry and nuclear engineering due to its constant crystalline structure in applications that would cause permanent distortion to other alloys [17].The INCONEL ® 601 alloy, similarly to INCONEL ® 600, resists various forms of high-temperature corrosion and oxidization [20].Nevertheless, this Ni-Cr alloy has an addition of aluminium which results in higher mechanical properties, even in extremely hot environments.INCONEL ® 601 can prevent the significant strains (ε) that would appear under operating loads when exposed to high-temperature environments.The applications go from the use in furnaces to heat-treating equipment like retorts, baskets and gas-turbine components [21] to petrochemical processing equipment.The INCONEL ® 625, which will have a special focus during this study, is a rare alloy that gains strength without having to undergo an extensive strengthening heat treatment [22].It is a Ni-Cr-Mo alloy with an addition of Nb.The Nb reacts with Mo, causing the alloy's matrix to stiffen and increase its strength [23].Like most INCONEL ® alloys, the INCONEL ® 625 has high resistance to several corrosive elements [24], withstanding harsh environments that would severely affect the performance of other alloys.This alloy is particularly effective when it comes to stavingoff crevice corrosion and pitting.The INCONEL ® 625 is a versatile alloy that is effectively used in the marine engineering, aerospace, chemical, and energy industries, among other applications [25,26].The INCONEL ® 690 alloy, unlike others in the group, is a high Ni and Cr alloy (Cr gives it particularly strong resistance to corrosion [15,27] that occurs in aqueous atmospheres).Along with its ability to resist the corrosion caused by oxidizing acids and salts, INCONEL ® 690 can also withstand the sulfidation that takes place at extremely high temperatures (T).One of the most known INCONEL ® alloys is the 718 alloy.This alloy, along with the formerly mentioned 625 alloy, will also have a special focus.INCONEL ® 718 differs from other INCONEL ® variants in structure and response, since it is designed for operation at T ≤ 650 • C [28].The 718 alloy is obtained by precipitation hardening [29,30].It contains substantial levels of Fe, Mo, and Nb, as well as trace amounts of Ti and Al [31].It has good weldability, which is not matched by most INCONEL ® alloys [32], and combines anti-corrosive elements with a high level of strength and flexibility.It is particularly resistant to post-weld cracking, maintaining its structure in both hightemperature and aqueous environments as well, being most widely used in different industries, such as petrochemical, aeronautics, energy, and aerospace [33].INCONEL ® alloys tend to form a thick and stable passivating oxide layer to protect the surface from further attack, retaining strength over a wide T range, making INCONEL ® an attractive material for high-temperature applications [34].The strength at high-temperatures of INCONEL ® alloys may be developed by solid solution strengthening or precipitation strengthening, depending on the alloy [35].In those processes, small amounts of niobium combine with nickel to form the intermetallic compound Ni 3 Nb or γ-prime, which consists of small cubic crystals that inhibit slip and creep effectively at elevated T [36].

Characteristic
Concerning the roles of major phases or composition elements that contribute to the INCONEL ® alloys, an overview is presented in Table 3 on the effects of Ni-alloying to better comprehend the compositions presented in Table 4.  -Imparts extra passivation to some alloys in certain liquid media.
As it was possible to find out, some of the consequences of alloying Ni with certain chemical elements make INCONEL ® alloys [46] a difficult-to-machine material [47] (Figure 2) and difficult to metal shape [48], identically to stainless steel [49,50].As opposed to other alloys, like Al-alloys [36,51], Magnesium (Mg) alloys [51], steel alloys [52] or Tialloys [51], INCONEL ® alloys do not benefit from better-established wear mechanisms between the pair tool-workpiece.Table 5 presents the most relevant and used models of the better-established wear mechanisms referred to, based on physics and experiments for heat partition coefficient R chip , for common materials like aluminium and low carbon mild steels.
Table 5. Predictive models based on physics and experiment for heat partition coefficient R chip [53].

A Predictive Model for Heat
Partition Coefficient R chip Equation Establishment Basis Dry-cutting process of AISI 1113 steel with K 2 S cemented carbide tool (cutting speed, v c = 30-182 m/min).
Surface grinding process of stainless steel/carbon steel with Al-oxide wheel.

Gecim-Winer
Based on the thermal behaviour of the two-dimensional, transient T distribution in the vicinity of a small, stationary, circular heat source equation of the average T of the moving and stationary heat sources between a frictional contact.Reznikov [59] R R = Based on the Green function to analyse the chip deformation and friction work along the tool rake face.Berliner-Krajnov [60] Consideration of Peclet numbers for the tool and workpiece materials in sliding tribological contact.
Caption: A-area shape factor; l c -tool-chip contact length; q F -frictional heat flux generated in SDZ; R chip -heat partition coefficient into the moving chip from the secondary deformation zone (SDZ); v ch -chip moving speed; α T -tool thermal diffusivity; w-tool-chip contact area; α W -workpiece thermal diffusivity; ∆θ p max -maximum tool-chip interface temperature rise due to heat generation in PDZ; θ 0 -environment temperature; λ T -tool thermal conductivity; λ W -workpiece thermal conductivity.
It is suggested to consult the work of Zhao, et al. [53] to better understand the additional variables described in Table 5.
Figure 3 explains how superficial hardness is affected in INCONEL ® alloys when machined after cold work processes, compared to some more stable materials like Cu, Al and mild steel.Machining (or surface) cold working may result from mechanical machining (milling, lathing, grinding) [61] or surface treatment (sandblasting, shot-peening), and may introduce residual tensile or compressive stresses into the surface of materials.Compressive stresses generated by shot-peening processes prevent the occurrence of stress corrosion cracks.In the case of plastic strain, tensile stresses appear instead, and the resulting stress levels may be extremely high [62].A curious detail patent in Figure 3 is the similarity behaviour between INCONEL ® 718 and 625 alloys after the 20% cold reduction.As a consequence of low k [36] of nickel-based alloys, which significantly influences heat distribution during the machining process, the surface integrity is affected when applying traditional cold forming techniques, due to the rapid work hardening (Figure 3) in the chip formation region [63].This phenomenon leads to plastic deformation of either the INCONEL ® workpiece or the tool, on subsequent machining passes [64], eventually resulting in built-up-edge (BUE) formation [31] (Figure 4) and consequentially in premature tool failure [65].For this reason, age-hardened INCONEL ® alloys, such as the 718 alloy, are typically machined using an aggressive but slow cut with a hard tool, minimizing the number of passes required [66].The BUE phenomenon occurs because of an accumulation of hot debris generated by the chip-start cutting process and deposited on the tool surface during machining, leading afterwards to adhesion and abrasion TW.From an experimental point of view, some authors noted that the BUE is significantly affected by the state of stress around the tool cutting edge and happens under extreme contact conditions at the tool-chip interface as high friction, high pressure, and high sliding velocity [68].INCONEL ® alloys are well known to abrade tools and develop BUE [69], especially the 718 alloy.Also during the machining of INCONEL ® 625, heat concentration is likely to occur at the cutting edges, resulting in early tool failure and consequent BUE [70].

Method of Research
The research and information compiling method are illustrated in the flowchart of Figure 5, which is simple to visually interpret and track down all the inherent steps in the making of this specific paper.In the flowchart, all the consulted databases and most used keywords are found (in the topic of this document), to find information about conventional and non-conventional machining and tool-wear mechanisms of INCONEL ® alloys.
Additionally, will be provided three attachments containing abbreviations, symbols and units used within the article.

Conventional Manufacturing Processes
The machining process of chip-start cutting is a technological process able to transform a wrought stock into a component, using a cutting tool.The surplus material from the wrought stock, or just stock, is removed in the form of chips; a consequence of the mechanical action of a cutting wedge with higher hardness than the material of the component that is meant to manufacture.In the following literature review, Milling, Turning, Drilling and Boring will be the discussed processes, in which chip-start cutting is a key and common factor to all these traditional processes.Making use of Figure 6, and taking into account that the chip-start cutting process is very much equal to the machining of INCONEL ® 718 and 625, Bonnet et al. [72] described the different friction parts on the rake face in the machining of steel.Directly behind the cutting edge, the chip velocity rapidly shrinks to zero.For a certain contact length, the chip material has a sliding velocity of zero, which starts to increase for the rest of the tool-chip interface, before the chip loses contact with the tool [72].
Due to the friction created around the chip creation process, three distinct heat zones are created within the vicinities of the cutting wedge.In Figure 7, the three different thermal affected regions between the tool-workpiece are visible.In Figure 7a there is a thermo-mechanical deformation of the primary shear region (or primary deformation zone, PDZ) where the majority of the energy is converted into heat due to the internal friction of the material to be cut.In Figure 7b there is a tool-material interface region, or SDZ, of the tool rake surface and the chip rear face where heat is generated by the rubbing between the chip and the tool and finally.In Figure 7c the contact between the flank of the tool and the already machined surface takes place, called tertiary deformation zone (TDZ).A novel approach to improve the efficiency of the traditional chip-start cutting process is laser-assisted machining (LAM), illustrated in Figure 8, which consists of preheating the material to cut and lowering the superficial hardness to facilitate tool cutting.This solution is common to turning, milling and grinding.Kim and Lee [74] also worked on a machining preheat approach for the INCONEL ® 718 alloy, which includes a magnetic induction coil instead of a laser.

Milling
Milling is the nomenclature given to the machining process that uses rotary cutting tools to remove excess material from the wrought stock.Nowadays, with the use of CNCs, milling can be done at a maximum of six degrees of freedom (DOF).Traditional milling tends to have lower a p values and higher a e values compared to more advanced milling techniques.However, this would cause a concentration of all heat generated in a small portion of the cutting edge, which in this case is the tip of the tool.It would require more axial passes too.This problem can be well managed in aluminium and steel alloys, but not with refractory materials like INCONEL ® alloys.Many milling approaches can be tackled to enhance INCONEL ® machining, such as up and downmilling, studied by Hadi et al. [77] in INCONEL ® 718 machining, illustrated by Figure 9. Another interesting and efficient technique [78] that enriches milling INCONEL ® 718 and 625 is trochoidal milling, illustrated by Figure 10, which consists of making the centre of the cutting tool walk a "helical horizontal" path.This procedure not only prevents tool jamming due to workpiece heat-dilation, but it also enables cutting bigger a e dimensions, with lower a p , improving heat-spread over the entire tool with more radial passes.

Author Challenges Remarks
Guimaraes, et al. [64] Evaluation of how the machining processes deteriorate the surface integrity to extend the service life of the INCONEL ® 625 components as long as possible.The influence of tool geometry, feed rate (f ), and tool rotational speed (s) on surface integrity were evaluated for the milling process.
The results indicate that s has the greatest influence on specific cutting pressure (β).The parameters s and f were the main factors that affected the thickness of the cold worked zone.The results suggest that R a after machining is driven by mechanical-thermal loadings and causes beneficial results related to corrosion resistance and compressive residual stress.
Pleta, et al. [80] Assessment of the INCONEL ® 718 trochoidal milling process and optimization for manufacturing scenarios.
To accomplish this goal, the modelling of the cutting forces (F c ) must be investigated with semi-mechanistic methods.Furthermore, machining parameters are investigated as to how they relate to the improvement of tool life and F c utilizing the Taguchi method.
It is found that TW increases the depth of the machining affected zone as does increasing h ch .Nutational rate ( .ϕ) and rotational rate ( .θ) have the largest interactions with both F c and tool VB.It was found that h ch and TW increased the depth of the plastically deformed and elongated grains in both the radial and axial orientations.Shankar, et al. [81] This investigation has designed a tool condition monitoring system (TCM) while milling INCONEL ® 625 based on sound and vibration signatures.The experiments were carried out based on response surface methodology (RSM).
The process parameters such as s, f, a p and vegetable-based cutting fluids were optimized based on R a and flank wear (VB).It was determined that the sound pressure and vibration signatures have a direct relation with VB.The statistical features values were extracted from the experimental data and the cutting tool VB was predicted with a mean square error (MSE) of 8.4212%.The R a of the machined surface varies from 0.081-0.273µm.The VB of the cutting tool varies from 0.0187-0.0254mm.Based on the desirability function, s = 221 rpm, f = 0.02 mm/rev and a p = 0.17 mm were identified as optimal process parameters.The average values of sound pressure for a brand-new, normal life (or useful life), and dull tools are 0.01955, 0.2513 and 0.4858 Pa, respectively.Similarly, the vibration signal range for a brand new, normal life (or useful life), and dull tools is 0.029-0.4394g, 0.0780-1.32g and 0.120-5 g.Table 6.Cont.

Author Challenges Remarks
Alonso, et al. [82] Slot milling operations were performed to investigate the influence of s and machining direction in INCONEL ® 718 alloy.
It was observed at higher s, lower values of R a and lower torque (M) values were obtained.Moreover, the main novelty of this work is the influence of the anisotropy of Wire and Arc Additive Manufacturing (WAAM) INCONEL ® 718 alloy on its machinability.Milling along the extruder travel direction offers better dimensional tolerance values with lower cutting M, being the more efficient way.
Boozarpoor, et al. [83] Turn-milling technology was utilized to machine cylindrical samples of INCONEL ® 718 alloy.The effect of process factors such as tool rotational speed (or spindle, s), workpiece rotational speed (v c ), f and eccentricity (e) on surface roughness (R a ) and tensile residual stress was analysed.
The results showed that f is the most influential parameter that determines the value of R a and residual stress.Furthermore, by considering production rate as a constraint, it was logically discussed that a setting of 1000 rpm cutter-speed, 300 rpm work rotational speed, 0.12 mm/rev feed rate and 0.2 mm eccentricity can guarantee maximum production rate as well minimum R a and tensile residual stress.

Anburaj and Pradeep
Kumar [70] Face milling was carried out on INCONEL ® 625 and twenty-seven iterations (L 27 ) were conducted using Design of Experiments (DOE), including three levels of v c and f z with constant a p .The study included three lubrication conditions such as dry-machining, normal coolant (wet) and cryogenic CO 2 (l) coolant.The output responses such as cutting temperature (T cut ), cutting feed force (F x ), cutting normal force (F y ), cutting axial force (F z ) and R a were evaluated.
The results were optimized using the TOPSIS technique with ANOVA tests, as the results of the highest closeness coefficient (C i ) value indicated the cryogenic CO 2 (l) coolant environment, and the input optimized parameters were v c = 80 m/min and f z = 0.05 mm/tooth.Other parameters such as T cut = 57.38 • C, F x = 201.5 N, F y = 251.1 N, F z = 335.9N, and R a = 0.159 µm were found optimal parameters, in the 19th iteration having obtained C i = 0.928835.

Turning
Opposed to milling, the turning process takes place in a lathe for components with a revolution axis, i.e., turbine shafts.The workpiece spins in a lathe while the fixed tools, with or without inserts, remove the surplus material.It is patent in Figure 11 the normal movement of the tool while turning a sort of shaft and some intrinsic characteristics of the inserts used.Some of the main problems in turning INCONEL ® 718 and 625 are the specific cutting energy (SCE) and rapid augment of surface hardening upon cutting material.Moreover, since shafts must comply with certain geometric specs for the better functionality of the component, R a is a key factor to be studied, varying v c , f and a p .

Author Challenges Remarks
Waghmode and Dabade [23] Examination and observation of the response parameters like F c and R a on input parameters such as v c , f and a p .Experimentation was conducted as per Taguchi's L 9 orthogonal array during INCONEL ® 625 alloy turning operation.
The results are analysed using the ANOVA method.
ANOVA suggests that the a p has a 55.05% contribution to F c .In thrust force (F z ), the contribution of a p is 55.83% which is the parameter with the most influence.As a p increases, F z increase.The main contribution for the feed force is provided by the a p , with 83.39%.Parameters f and a p highly affect R a , having 20.61 and 51.68% contribution, respectively.As f increases, R a increases too.With parameter v c , it shows an inverse trend.
Kosaraju, et al. [25] A multi-objective optimization based on the Taguchi-based Grey Relation Analysis (TGRA) method was employed to find the optimal levels of turning INCONEL ® 625 parameters for the objective of lower F c and better R a under dry-cutting conditions.
From the statistical analysis, the results show that f is identified as the most significant parameter for the turning operation according to the weighted sum of F c and R a .The optimal combination of control factors and their levels are v c = 75 m/min, f = 0.103 mm/rev and a p = 0.2 mm.
Vignesh and Ramanujam [75] Evaluate the influence of laser-assisted high-speed machining (LAHSM) on the F c (F z in Figure 8), R a , TW and the chip morphology during the INCONEL ® 718 turning process.
LAHSM optimal parameters were v c = 80 m/min, f = 0.08 mm/rev and laser power, P Laser = 1300 W. F c , R a and TW values were better over the conventional turning process ones, leading to a reduction of F c by 24.5%, R a by 56% and TW by 29%.
Raykar, et al. [85] High-pressure cooling (HPC) of cutting tools can be very effective when machining difficult-to-cut materials like INCONEL ® 718.An analysis of microhardness and degree of work hardening (DWH) is carried out to evaluate the machinability of the INCONEL ® 718 alloy while turning in a high-pressure coolant environment.
Microhardness has a sudden change between 30-120 µm bellow the machined surface.After this region, the microhardness value is similar to the bulk, which is found at 270-300 µm below the machined surface for all samples.The microhardness near the machined surface is found to be 1.11× the bulk microhardness.Microhardness variation is unaffected by the changes in the process parameters since none is statistically significant at a 95% confidence level.A significant microhardness value is noticed at a depth of 90 µm.
Infante-García, et al. [86] The increase of the undeformed chip cross-section and the high SCE of INCONEL ® 718 give rise to load peaks during machining.Different tests involving multipass finishing turning have been carried out to study the magnitude of the load peaks for different cutting conditions.
Initial results have shown a significant peak in the machining loads, predicted by Altintas force law [87].This peak is related to the tool tip radius and the cutting parameters, after the second and successive passes.The main factor that contributes to that is the increase of undeformed chip cross section during a short interval.Thus, the progression of TW is significantly influenced.The machining load at the end of a turning pass can significantly increase during a short interval.Consequently, this effect may influence TW progression leading to premature tool failure.

Author Challenges Remarks
Airao, et al. [89] Examination of the machinability of the INCONEL ® 718 alloy in conventional and ultrasonic assisted turning (UAT) under dry, wet, minimal quantity lubrication (MQL), and CO 2 (l) strategies.The experiments are performed in an in-house developed ultrasonic-assisted turning (UAT) setup, keeping all the machining parameters constant.
The CO 2 (l) reduces edge chipping, nose wear, adhesion, and abrasion wear.The conventional turning under CO 2 (l) reduces the VB by 32-60% and power consumption (P in ) by 5-31% compared to dry, wet, and MQL strategies.Similarly, the UAT under CO 2 (l) reduces the VB by 32-53% and P in by 11-40% compared to dry, wet, and MQL strategies.The UAT reduces R a compared to conventional turning when used under MQL and CO 2 (l).The CO 2 (l), in conjunction with ultrasonic vibration, significantly reduces SCE and TW without compromising R a .
Moreover, this combination also helps in enhancing the chip breakability and reducing ε concentration.

Drilling
Drilling is a cutting process where a drill bit is spun to cut a circular hole in a component.In INCONEL ® applications, drilling is important to create micro holes that will permit the cooling of gas turbines, as illustrated by Figure 12 and studied by Venkatesan et al. [90] on the hole quality assessment in INCONEL ® 625 alloy parts.The INCONEL ® 718 alloy has many challenges in deep-hole-drilling as well since the process is prone to drill jamming due to material expansion inside the holes.Table 8 presents the latest experimental challenges and developments in the machining of INCONEL ® alloys with the drilling process.

Author Challenges Remarks
Neo, et al. [92] The traditional carbide-tipped gun drills often get worn at an accelerated rate and require repetitive re-sharpening or replacement when drilling INCONEL ® 718 alloys.This occurrence lowers productivity and increases costs.Furthermore, it is also a challenging task to meet the stringent hole-straightness requirement of 1/1000 mm for deep-hole drilling (DHD).
In contrast to traditional carbide-tipped gun drills, the developed PCBN-tipped gun drill can operate at higher v c and reduce drilling forces, drilling M, and TW.Furthermore, the surface quality of drilled holes is much better than those drilled by traditional carbide gun drills.For a stable drilling condition, it is also recommended to perform deep-hole drilling with the developed PcBN gun drill on INCONEL ® 718 at v c ≥ 50 m/min.Use of cryogenically treated drill bits in INCONEL ® 718 alloy machining.Drill bits are conditioned under two different environments i.e., cryogenically treated with single-tempered drill bits, and cryogenically treated with double-tempered drill bits.The Taguchi method was used for trial design and optimization of factors along with the Whale optimization algorithm.
Results show that f is the most contributing parameter to maximize F z , while s is the most contributing parameter to maximising M. Also, tool condition is the most contributing factor to minimising R a .By maximizing the F z , up to 184 N, and M, up to 0.72 Nm, during drilling operation on INCONEL ® 718, using cryogenically treated and single tempered drill bit, it was found that the optimal parameter settings were s = 215 rpm and f = 0.106 mm/rev.R a was minimized to 3.77 µm.It was also seen that cryogenically treated and the single-tempered drill bit was more influential in attaining maximum F z and M, while cryogenically treated and the double-tempered drill bit was more influential in attaining minimum R a .

Boring
Boring is the manufacturing process in which previously drilled holes are enlarged by a single-point cutting tool.Not much information is available about the boring process on INCONEL ® alloys whereby it is only presented in the study carried out by Ratnam et al. [94], whose challenges involved the investigation of the machining parameters' effect on R a , TW, F c on the cutting tool and workpiece vibration during dry boring of INCONEL ® 718 with TiCN-Al 2 O 3 -TiN coated inserts using response surface methodology (RSM).It was found that the use of accelerometers, radioactive sensors and piezoelectric actuators does not make it possible to measure rotating objects' vibrations.On the other hand, the LDVs are capable to measure rotating objects' vibrations with a simple experimental arrangement.Parameters s and f were found to have a significant influence on R a .The parameter a p was found to be significant on VB, F c , and workpiece vibration amplitude (VA).The optimal machining parametric combination was obtained using the desirability function.Cutting condition parameters such as s = 360 rpm, f = 0.14 mm/rev and a p = 0.4949 mm was obtained for VA = 38.7 µm, minimum F = 117.8N, VB = 0.3 mm and minimum R a = 2.55 µm.The proposed RSM approach was an easy method to obtain maximum information with a smaller number of experiments.and successfully used by different authors in the improvement of process parameters.

Non-Conventional Manufacturing Processes-Electrical Discharge Machining (EDM)
This review also presents some new insights into a non-conventional process, which is Electrical Discharge Machining (EDM).The process is a non-conventional machining method that allows the production of pieces with complex shapes, and it can be used in materials such as INCONEL ® 718 and 625.This particular manufacturing technique removes material from the wrought-stock thanks to melting and vaporising cavities using electrical discharges that come from a scrolling wire [95], as illustrated in Figure 13.

Author Challenges Remarks
Mohapatra, et al. [39] Comparative study of the chemical and mechanical properties of INCONEL ® 718, 625, 825 and 601.Evaluation of the machinability of different grades of alloys using EDM.
An increase in the peak current resulted in improved material removal rate (MRR) by keeping the gap voltage (V g ), pulse-on time (T on ), duty factor (τ) and dielectric circulation flushing pressure (F p ) fixed at a constant value, for the different INCONEL ® grades.An increase in R a is observed by incrementing the peak discharge current (I p ).In the case of surface crack density (SCD), with an increase in I p , SCD ends to decrease, again followed by an increasing trend; and then finally remained constant.
Manikandan, et al. [97] INCONEL ® 625 is one of the hard-to-machine materials extensively used in high-temperature applications.It has better strength and lower k, compared with more common materials, which leads to poor machinability by traditional processes.To overcome such kind of disadvantages, unconventional manufacturing methods have been developed and proposed to be suitable substitutes, such as WEDM.
This work details a single-aspect optimization problem of WEDM of INCONEL ® 625 with the help of Taguchi analysis.In this investigation, the MRR and Overcut (OC) were deemed as the performance characteristics, and the Taguchi response showed that the best parameter combination to maximize the performance of R a is T on = 30 µs, T off = 15 µs and I p = 3 A. The best set of process parameters for attaining better OC is T on = 30 µs, T off = 5 µs and I p = 1 A. Contour plots were also explored to reveal the combined influence of process parameters on the preferred performance measures.

Author Challenges Remarks
Hussain, et al. [98] Cost reduction in machining through increased MRR using optimum machining process parameters.An experimental study is presented for optimizing process parameters T on , I p and T off to maximize MRR for subtracting material from INCONEL ® 625 work part using Taguchi DOE and its analysis.
A Taguchi orthogonal array L 9 is applied for experimental design and analysis.Optimized values of performance factors obtained by analysis are I p = 12 A, T on = 160 µs, and T off = 35 µs.The maximum MRR, of 24.48 mm 3 /mm, was obtained with optimum values of performance parameters.Under these conditions, it was found that, R 2 = 98% which reflects a high confidence level in the experiment.It is also found that both T off and I p have a considerable impact on MRR.This is because higher values of T on and I p enhance the amount of energy discharge on the workpiece, which leads to increased material melting and vaporisation.

Liu, et al. [95]
Enhancing the machining process of INCONEL ® 718 using zinc-diffused coating brass wire electrode and Taguchi-Data Envelopment Analysis-based Ranking (DEAR).
MRR, kerf width (K w ), and R a were considered as the quality measures.In the WEDM process, the brass wire electrode worked as expected and the optimal arrangement of input factors was found as T on = 140 µs, T off = 50 µs, SV = 60 V, and WT = 5 kg, which are the most relevant factors with a C i = 0.989.

Rahul, et al. [99]
INCONEL ® 718, 625, 825 and 601 machinability was experimentally analysed during the execution of EDM.The experimental design was planned according to a 5-factor/4-level L 16 orthogonal array.The following process variables were considered: V g , I p , pulse-on time (T on ), duty factor (τ) and F p .Machinability was assessed in consideration of MRR, electrode wear rate, R a and surface crack density (SCD) at the already worked surface.The satisfaction function approach integrated with the Taguchi method was attempted to determine optimal parameter settings.
The MRR efficiency was found to vary from: In this regard, detailed statistical and microscopical analyses are employed with mono and multi-objective process optimization by employing the TGRA method.
Process parameters are more influential on radius deviation as compared to angular error.At F p = 4 kg/cm 2 , the radius deviation is around 4%, which increased to 5.4% at F p = 12 kg/cm 2 .A low F p value agglomerates debris, which resulted in a coarser surface due to the re-solidification, with a R a = 2.12 µm.However, with the increase of F p to 12 kg/cm 2 , the surface quality improved and resulted in R a = 1.93 µm.An increasing trend is observed where S G increased with the magnitude of F p .Using F p = 4 kg/cm 2 resulted in S G = 107 µm.With the increase up to F p = 12 kg/cm 2 , values of S G = 111.5 µm were attained.
Similarly, an increase in Ø N from 4 mm to 8 mm not only increased S G from 108.5 µm to 110 µm but also increased angular error from 0.255% to 0.6%.The high Ø N increased the entry of dielectric flow, which hindered the stability of the thermo-electric erosion process near corners.The F p and Ø N parameters showed a significant effect on the R a .The optimized parametric settings are SV = 50 V, F p = 4 kg/cm 2 , Ø N = 8 mm, and W D = 10 mm.The confirmatory experiment reduced the process's limitations to an S G = 109 µm spark gap, 0.956% angular error, 3.49% cylindricity error, and R a = 2.2 µm.

Tool Wear
With the tool operation in machining, wear starts to be a key factor in quality and productivity, namely with INCONEL ® alloys, such as 718 and 625.To identify a worn milling tool, the ISO 8688-2 [101] standard predicts that a tool presenting either VB = 300 µm or VB max = 500 µm on the flank is considered a worn tool [69].For turning tools or inserts, the ISO 3685 standard is the one to consult [102].Taking into account a novel lubrication method, Bartolomeis et al. [69] observed that the tool wear behaviour mechanisms during EL conditions were abrasion and microchipping on the cutting edge, due to the tendency of INCONEL ® 718 to develop BUE.
Figure 14 packs the initial causes of wear, the various wear mechanisms that lead to different types of wear and the final consequences from the tool-wear due to INCONEL ® machining.As a complement to Figure 14, Table 10 presents the typical TW mathematical models, used to characterize the numerous TW mechanisms.It is suggested to consult the work of Wang et al. [37] to better understand the additional variables described in Table 10.

TW Model Comments
Taylor Taylor's empirical tool life model.
Pálmai [115] dW TW model, considering the effects of wear-induced cutting, force, and T rise on TW.
Halila [116,117] TW model is dependent on the material removal rate.

Tool Materials
As previously mentioned, due to poor k from INCONEL ® alloys, which lead to a substantial increase of T in the three heat-zones when machining, the used tools are more prone to premature wear since the heat generated will end up creating BUE, which will rapidly degrade coatings and the tool material itself.The TW mechanisms, which include abrasive wear, adhesive wear, and plastic deformation, are following described.Severe TW is one of the key reasons for machining inefficiency [118].Tool materials, depending on their application, may vary as hard metal, high-speed steel (HSS, and its variant HSS-Co), cermets, ceramics (where carbides are inserted), PcBN and many more.Table 11 presents the latest experimental observations and performance of non-coated tools in the machining of INCONEL ® alloys.PcBN inserts v c = 300 m/min f = 0.07, 0.1 and 0.15 mm/rev a p = 0.15, 0.25 and 0.5 mm A significant peak in the machining forces, predicted by the Altintas force law [87], is related to the tool tip radius and the cutting parameters, after the second and successive passes.The rapid development and magnitude of the peak loads influence the tool wear progression, as a premature notch developed along the cutting edge, observed after the test with a p = 0.5 mm and f = 0.15 mm/rev.The low machinability of INCONEL ® 718, along with the brittleness of PCBN tools, leads to a premature failure of the cutting tool when this phenomenon is not considered in conventional turning.
The ISO 3685:1993 [102] standard was used as a reference for the VB measurement.Pulsed laser ablation (PLA) using ns-laser leads to a transformation of cBN to hBN in all considered laser parameter combinations.The cutting tool hardness is significantly decreased by the hBN formation, from over 3400 HV down to 1700 HV, However, not all laser parameters reduce hardness by the same amount.Tools with laser-prepared cutting edges achieve comparable tool wear to reference tools when applying appropriate laser parameters.There is an indication that the transformed hBN acts as a solid lubricant, which leads to a decrease in the cutting forces.The ISO 3685:1993 [102] standard was used as a reference for the VB measurement.Among all four cooling conditions, the minimum R a , VB, and main F c were obtained for cryogenic machining using N 2 (l)-air mixture as a coolant.This result indicates that cryogenic coolants are well-suitable for the machining of INCONEL ® 625 alloys.The lowest R a = 0.481 µm was obtained under cryogenic machining with the parameter setting of v c = 60 m/min, f = 0.15 mm/rev, and a p = 0.6 mm.Reductions of 38.49%, 34.56% and 30.08% in R a were achieved with cryogenic machining when compared to dry, MQL and nMQL, respectively, under the same parameters.The minimum value of VB was observed at the lowest levels of cutting parameters, irrespective of the cooling conditions.Also, the lowest VB = 85.52 µm was noticed under cryogenic machining, when machining with parameter settings of v c = 60 m/min, f = 0.05 mm/rev and a p = 0.6 mm.The VB reductions by cryogenic machining, when compared to dry, MQL and nMQL, are 20.32%,11.42%, and 8.81%, respectively.A high-speed ultrasonic vibration cutting (HUVC) method has been proposed for the precision machining of INCONEL ® 718.The TGRA L 9 array method was used for analysis.Owing to the limitations of the cooling pressure and duty cycle, the useful highspeed stable region for INCONEL ® 718 was v c = 80-300 m/min.In this range, compared to the conventional effective cutting region, the cutting efficiency was significantly improved.The HUVC-Taylor's equation developed in this study aimed to provide a comprehensive understanding of the most recently proposed high-speed ultrasonic precision machining methods and provided guidance for appropriate practical applications in the future.The impact effect due to the tool-workpiece separation was a factor that needs to be suppressed.This effect was the core reason for the failed region in ultra-high-speed machining.In this regard, developing the impact-resistant tool could be seen as the next meaningful work for further cutting speed enhancement.This method is of particular interest to developing a deeper understanding of relative wear rates associated with the machining of different workpiece classes and alloys.The parameter VB = 185 µm is below the maximum limit imposed by the standard.

Tool Coatings
Some tool materials have enough hardness to cut through INCONEL ® , as it is shown in Figure 15, although others require a coating to protect the core material from abrasion when machining.The binomial substrate/coating is selected, as a function of specific requisites, from each application which often demands from the cutting tool antagonistic characteristics like tenacity and hardness.The usage of coated tools is highly advantageous from a production point of view, not because it is only possible to escalate v c or s values, but also to promote better quality to the fabricated components, and some of them can be multilayer, in which each layer has its unique function.The preferred manufacturing processes to make coated tools are metallurgical powder processes, chemical vapour deposition (CVD) or even physical vapour deposition (PVD).The hardness of different coating materials with a lower limit and suitable performance range [125].
A schematic of how different coatings can appear in a tool is presented in Figure 16, whereas Figure 17 demonstrates how crack propagation occurs inside the coatings due to TW. Figure 18 shows the lower limits and the hardness performance range of some of the most used tool coatings.Examples of preferred coatings to machine INCONEL ® 718 include TiAlN, TiAlCrN, TiCN, TiN/AlTiN, and TiAlCrSiYN/TiAlCrN [126].
Table 12 presents the latest experimental observations and performance of coated tools in the machining of INCONEL ® .The tool life of the Al-Si coating was more than 6× higher than that of the uncoated tool and around 3× higher than the TiAlN coating, and the F c of the soft Al-Si coating was around 1 /2 that of the uncoated tool.These improvements can be attributed to better lubricity and frictional behaviour in the tool-chip interface due to the superior lubricity of the Al-Si coating, which resulted in lower adhesion and BUE formation, less contact pressure at the cutting zone and lower friction.As v c and f further increased, the tool began to peel, tip, or even fracture.A two-dimensional TW map based on v c and f was drawn.In the wear map, three tool failure limits, i.e., BUE limit; crater wear limit; and chipping, tipping, and fracture limit were determined.A safety zone was planned to determine the optimum cutting parameter range.A method of optimizing the cutting parameters by combining the wear map, tool wear, and R a of the machined workpiece was proposed.The optimum cutting parameters were v c = 60 m/min, f = 0.1 mm/rev, and a p = 0.5 mm.A complete tool life experiment was performed with the optimized cutting parameters and a tool life distribution model obeying a normal distribution was established.When reliability was 0.9, the recommended tool-life was 70 min.
Criado, et al.Carbide tools have a longer tool life than PcBN tools, but PcBN tools higher allow speeds between 4x and 6x.In terms of machined surface per edge, it has been proven that, at f = 0.15 mm/ver, more machined volume is obtained, while for f = 0.1 mm/rev, the machined surface quality is maintained in the PcBN tools.For this reason, the viability of using PcBN tools in finishing operations in INCONEL ® 718 is demonstrated.The best combination found for the PcBN tool was at v c = 250 m/min and f = 0.15 mm/rev.It was found that the tool life increases at low cutting speeds, although f does not affect it significantly.The finished surface machined with the PcBN tool obtains a more constant behaviour and excellent R a during most of the machining.However, no significant changes were observed depending on the cutting conditions.The Taguchi L 8 array method was used in the analysis.a p is found to be the statistically significant parameter for tool life with a 95% confidence level.Tool life is most affected by a p followed by f z with percentile contributions (PCR) of 45.43% and 18.425%, respectively, with lower values of the parameters resulting in better performance in general.A maximum tool life of 42.8 min was achieved when machining was done employing f z = 0.08 mm/tooth and a p = 0.25 mm with v c = 45 m/min.A SEM analysis indicates adhesion, BUE, attrition and chipping to be the main wear mechanism in general.

Discussion
After all that has been presented throughout this paper, a SWOT analysis was performed to discuss present perceptions of the INCONEL ® machinability (Table 13), tool-wear (Table 14) and coatings utility to the tools (Table 15).

Conclusions
Despite significant progress in the traditional cutting tool technologies, the machining of INCONEL ® 718 and 625 is still considered a great challenge because of the intrinsic characteristics of those Ni-superalloys.It is notable, nevertheless, that there has been a pursuit to bring ease to conventional processes, resulting from the evolution of techniques and tool materials, to get better machinability with the Ni-based superalloys.From another point of view, by introducing non-conventional processes and assists like EDM, and hybrid techniques such as LAM and UAT, the evolution differential has a great potential to bring down manufacturing costs.Likewise, the conventional processes have had several improvements in the last five years, as reviewed along all states of the art, calling upon Taguchi DOE methods for improving tool-wear and for improving R a , either with a lubrication environment or not.This is important for the own component's wear resistance.A constructive criticism is made of the usage of TGRA and DOE methods, which were several times noticed to be used by different research in the states of the art of this paper.It is efficient to take advantage of such powerful methods to evaluate a series of parameters in an L x array, and through the combination between them, to achieve the best result of R a .Nonetheless, it is known that one of the main challenges in tackling INCONEL ® machining is the high costs of the manufacturing processes, due to the elapsed time milling, and turning, and this key factor has been neglected.With this review paper, it is suggested to the forthcoming authors to take advantage of TGRA and ANOVA analyses, concerning the achievement of low-cost solutions when machining INCONEL ® , at the same time quality is preserved by taking R a parameter into account as it has been done so far.The present work highlighted a large amount of information regarding INCONEL ® 718 traditional machining and applications, within the academic and scientific community, compared to its counterpart INCONEL ® 625.On the other hand, the INCONEL ® 625 showed advancements in non-conventional processes due to difficulties at the onset of chip cutting.Henceforward, research work is planned with the prospect of delivering a review paper regarding the evolution of lubrication environments, allied to the traditional machining of INCONEL ® .

Figure 3 .
Figure 3.Effect of cold work on hardness for different INCONEL ® alloys and comparison with other materials [1].

Figure 5 .
Figure 5. Research method accomplished to achieve a better redacting result to the review paper.

Figure 6 .
Figure 6.Evolution of the sliding velocity along the tool-material interface [71].

Figure 9 .
Figure 9. Chip formation showing (A) chip formation showing cutter tooth entry angle in downmilling and cutter tooth exit angle in up-milling, (B) maximum chip thickness, h max , and (C) chip length, L c [76].

Figure 14 .
Figure 14.The wear causes, wear mechanisms, wear types, and wear consequences in the cutting of Ni-based superalloys [118].

Figure 15 .
Figure 15.(a) Hot hardness characteristic curve of CBN, Ceramic and Carbide tool materials compared with the γ structure of INCONEL ® 718, (b) Thermal conductivity of tungsten carbide (WC), INCONEL ® 718 and different coatings for carbide tools against T (adapted from [119]).

Figure 16 .
Figure 16.Scheme of how different types of coatings look when applied on the substrate [123].

Figure 17 .
Figure 17.Crack propagation behaviour for each of the common coating structures [124].

Figure 18 .
Figure18.The hardness of different coating materials with a lower limit and suitable performance range[125].
M 6 C and MC carbide precipitation.Formation of Co 2 Ta intermetallic.Reduces surface stability.High-solid solution hardening.TaC carbide precipitation.A large increase in γ vt%.Improves oxidation resistance.

Table 6
presents the latest experimental challenges and developments in the machining of INCONEL ® with the milling process.

Table 6 .
Critical challenges and developments in the milling process of INCONEL ® .

Table 7
presents the latest experimental challenges and developments in the machining of INCONEL ® with the turning process.

Table 7 .
Critical challenges and developments in the turning process of INCONEL ® .

Table 8 .
Critical challenges and developments in the drilling process of INCONEL ® .

Table 9
presents the latest experimental challenges and developments in the machining of INCONEL ® alloys with EDM.

Table 9 .
Critical challenges and developments in the EDM process of INCONEL ® .

Table 11 .
Machinability performance during non-coated tools assisted machining of INCONEL ® .
Wear topography and surface-induced plastic deformation were evaluated.Abrasion marks and grooves on different length scales indicate that VB was caused by abrasion during sliding contact of the tool with the workpiece.Examination of worn WC grains employing EBSD proved to be a suitable method to assess the contribution of plastic deformation to TW in metal cutting.

Table 12 .
Machinability performance during coated tools assisted machining of INCONEL ® .Irrespectively of the tool type, the tool-chip contact length was decreased with the increase of v c .The tool-chip contact length and crater wear for the PVD AlTiN coated carbide tool was decreased compared with that of the uncoated carbide tool in dry orthogonal cutting of INCONEL ® 718.A PVD AlTiN coated carbide tool decreased by 5.94 µm or 5.26% the h ch , compared with an uncoated tool at v c = 120 m/min.The maximum T cut for the PVD AlTiN coated carbide tool decreased by 14.00 • C or 2.11%, 25.00 • C or 3.64%, and 39.00 • C or 5.47%, compared with that for an uncoated WC tool in dry orthogonal cutting of INCONEL ® 718 at v c = 40, 80 and 120 m/min, respectively.For uncoated carbide tools, the relative error ( Σ|δ|) from the predictive model-R G-W , compared to the measured T at v c = 40, 80 and 120 m/min was 31.83%.
The proposed method was implemented in the form of an automated computational program, and a series of experiments were performed to analyse the progression of the VB area of the tool over the volume of material removed.Based on the outcomes of the present study, it has been realized that the image processing method presented in this study can accurately and efficiently evaluate the VB width and wear area.Also, the proposed methodology was able to replicate the well-known curve of the VB area versus the volume of material removed.TiAlN-coated carbide tool exceeded t = 10 min.It was found that the main TW morphologies of the tool were the BUE, crater wear, chipping, tipping, and fracturing.The main TW mechanisms were abrasion, adhesion, and oxidation.Adhesion wear under low v c yielded a BUE wear morphology, whereas adhesion wear and oxidation wear under high v c resulted in crater wear.

Table 14 .
SWOT analysis of TW resultant from INCONEL ® machining.

Table 15 .
SWOT analysis about cutting tools coatings.