Suitability of Eroded Particles from Die-Sink Electro Discharge Machining for Additive Manufacturing—Review, Characterization and Processing

: In this bipartite study, waste products of die-sink electro discharge machining (die-sink EDM) are investigated. EDM is based on an erosive character of discharges leading to material removal and molten material congeals in the dielectric. The aim is to show a theoretical suitability of these particles for a further usage as a secondary, recycled material in additive manufacturing (AM). Due to the energy-and cost-intensive process of gas atomization for AM powders, there is a need for alternative concepts for particle generation. The ﬁrst part deals with an intensive review of references from the literature regarding particle size and circularity using image analysis. Secondly, real waste streams were investigated after washing and cleaning processes for oil removal via laser diffraction, dynamic image analysis, SEM with energy dispersive X-ray spectroscopy (EDX) as well as optical emission spectroscopy (ICP OES), categorized within the literature and compared to commercial AM powders. In general, it could be shown that, in principle, recycled particles fulﬁll main requirements for an AM usage regarding size and shape. Reference powders show median particle sizes of 30 µ m to 34 µ m and circularities of 0.90 to 0.93, whereas eroded particles exhibit an x 50 value of 27 µ m and circularity of 0.90, too. However, chemical purity, mainly caused by carbon contamination (5.4 wt% in eroded powder compared to 0.4 wt% in reference powder), must be improved before printing via AM machines. Additionally, several separation techniques have to be applied to remove undesired elements (alumina).


Introduction
Electrical discharge machining (EDM), alternatively spark erosion, is one technique to postprocess components in their shape and texture [1][2][3][4][5], or even to produce metallic and ceramic microspheres [6][7][8][9].In principle, spark erosion techniques are based on an electrical discharge between two electrodes, where a conversion from electrical into thermal energy leads to different mechanisms of material removal in a fluid medium-the socalled dielectric.Historically, this erosive effect was first noted by Joseph Priestley around 1770 [10].Afterwards two Russian scientists inverted this effect for material removal and invented the first EDM machine [11,12].In the following years, more and more studies were carried out exploiting this effect for several applications and improving the process to a standard procedure [13][14][15][16].
Nowadays, the two dominant techniques are die-sink EDM and wire EDM [17], which are important for several industries, e.g., within mold and vehicle construction for implementing features with high aspect ratios like cavities or slots.It has to be mentioned that the predominantly hard materials have to be electrically conductive.Most of all, several die or hot work steels (martensitic in general) are processed via both technologies, but besides that, other steel types (ferritic, austenitic, etc.) or nickel and aluminum alloys as well.Main differences are on the one hand the used dielectric fluids and on the other hand the tool electrode geometry as well as the material combination.In die-sink EDM, copper or graphite electrodes are common, whereas in wire EDM a brass or copper wire, which can be partially coated, is used.These processes are performed in synthetic hydrocarbon oil, kerosene in former days (both in die-sink EDM) and deionized water (wire EDM), respectively.Li et al. [18] gave a lucid comparison of these two machining types.Furthermore, some special techniques have been developed, like fast hole drilling EDM [19], micro-EDM [20], near dry EDM [21] or magnetic field/ultrasound assisted EDM [22,23].
In contrast to that, the-compared to EDM-emergent field of additive manufacturing (AM) is becoming more and more important for several industrial sectors and is gaining greater influence and a bigger role every year.Reasons for that are, for example, the very good flexibility, variability and geometrical complexity of producible components.Moreover, a bunch of different materials can be used in a wide range of AM techniques.In the literature, very recommendable reviews can be found that deal with a wide range of usable materials (metals, ceramics, polymers, composite materials, organic/biological material), different AM techniques as well as resulting material properties and specific customized applications [24][25][26][27][28].In this study, the main focus is on metallic powders only.Some disadvantages are the limitations in manufacturing speed or the post-treatment of the surfaces.Besides that, the AM powders are highly expensive due to their tight specifications regarding particle size distribution (PSD), composition and purity as well as the number of defects accepted.However, these powders should have a narrow particle size distribution (PSD) depending on the manufacturing process.Particles in the size range smaller than 50 µm (median particle size x 50 around 30 µm) for a selective laser melting (SLM) process or 60 µm to 100 µm (x 50 around 70 µm to 80 µm, max.particle size around 125 µm) for an electron beam melting (EBM) process, according to [29,30] are commonly used.Moreover, a high circularity/sphericity concerning particle morphology and a low number of defects or hollow particles are required [24].According to Lui et al., a narrower range of particle sizes leads to better flowability and higher tensile strength and hardness on the one hand, while wider ranges of particle sizes lead to higher powder bed densities, lower laser energy intensities and smoother surface finishes [31].Apart from that, other important parameters for AM parts are the structure distribution, inherent stress conditions, porosity, laser energy and energy source settings [32,33], respectively.
In Germany, the costs for raw materials in the AM industry for small-and mediumsized enterprises amount to 46% of the total manufacturing costs, according to the Federal Statistical Office [34].The main reason for that is the production of these specific powders.Right now, there is just the opportunity to generate powders via gas atomization of metal melts [35], which is very energy intensive, too.Therefore, to lower the costs plus energy balance and give, e.g., smaller companies the chance to establish their market presence, an alternative way of supplying and generating metal powders for AM is indispensable.
As a waste product in EDM, so-called erosion sludges or debris, respectively, accumulate.These contain a highly viscous mixture of eroded particles from the two electrodes as well as the oily phase and reaction products from the dielectric.Usually, the debris is led in a filter cartridge or a backflush filter, is filtrated and the dielectric fluid can be used again for several months and years.The disposal of the filters with debris should take place via specialized companies and should follow the waste code AVV 120118, which applies for waste containing mineral oil derivates in Germany.However, not everyone follows these recommendations; some dispose of mineral oil derivatives in residual waste incorrectly.That has to be considered when looking at the environmental aspects.Yeo et al. [36] reported that, on the one hand, the waste products resulting from the dielectric could be toxic and are not recyclable, and, on the other hand, produced gaseous components can to a minor or major degree be dangerous, such as acetylene, ethylene or hydrogen.Additionally, the electrical energy consumed during the process, mainly in die-sink EDM, cannot be neglected.In a further study, presented by Leão et al. [37], the main source of pollution was determined in the dielectric fluid with the hydrocarbon oil and the debris, which can cause skin problems or adverse effects to health after inhaling.
Considering the particle sizes as well as the form and circularity of these eroded particles in general, a usage as a secondary material for AM processes should be investigated.Therefore, in this study the first focus lies on an overview of different references dealing with eroded particles in waste material streams from EDM and spark erosion, concerning aspects like size, size distribution, morphology and composition.Secondly, the paper will show an extensive cross-compilation of die-sink EDM sludge and included particles gained from several medium-sized enterprises in middle-east Germany.The results presented should show the theoretical suitability of the particles generated out of these sludges as an alternative, more energy efficient and less expensive AM powder.Concluding, the main focus deals with the particle sizes and forms within the waste streams and not the machining settings or any kind of improvements in the EDM mechanism itself.

Particle-Generation Mechanisms
As already mentioned, the main process in EDM is based on an erosive character of generated electrical discharges, caused by the transformation of electrical energy into thermal energy, which leads to a material removal.Therefore, an electrical potential is applied between the two movable/flexible electrodes.The upper electrode is the tool electrode and the lower one the workpiece electrode, which represents the machined component.The dielectric fluid is located in between.The potential leads to the generation of an electrical field and its strength increases until the dielectric strength is exceeded, which leads to the electrical discharge.That discharge takes place at the shortest distance between the electrodes, which is called gap size or spark gap and has a significant influence on the process.As a result, temperature rises in the working zone clearly over 10,000 K, whereby the materials melt.In principle, the whole process is divided into four phases, which are repetitive with a defined frequency adjusted by the pulse generator [17,38].The first phase contains the impact ionization of the dielectric, where electrons are smashed out of the molecules and form positive ions due to the force of the electric field.Secondly, the phase of ignition follows, dominated by a current flow.The positive ions start to migrate to the workpiece electrode and the negative electrons move to the tool electrode, resulting in a formation of a discharge channel and a temperature and pressure rise.In the third phase, when a constant current flow is reached, the discharge channel expands, plasma is generated and the materials start to melt and vaporize, resulting in a growing cavitation bubble.Finally, in the fourth phase the potential feed is interrupted and the discharge channel collapses.Thereby, the temperature decreases abruptly, the cavitation bubble collapses and the melt vaporizes explosively and carries molten material from deeper areas, which is transported away by the dielectric.Several pulses are repeating in a defined time frame of several micro-or milliseconds until the desired material removal is completed.A schematic sketch of the EDM process is shown in Figure 1.
The eroded particles differ in their size and shape.Dvornik et al. [39] described three characteristic mechanisms for the particle formation.They stated that approx.10% by volume erode into the vapor phase and the particles are synthesized due to condensation of vaporized material (vaporized particles).This particle fraction is very small (sub-µm or even colloidal), spherical and tends to form agglomerates or attaches on surfaces of bigger particles.A second fraction with 10% by volume, as well, is generated due to brittle failure of the material under the thermal stress and erodes into the solid phase (solid particles).These particles have an irregular shape and differ strongly in their size, which is up to several hundred µm.The majority (about 80 vol.%) erode into the liquid phase due to congealing/solidification of molten metal droplets (molten particles) as well as decreasing of bubbles [40], expulsion of molten material due to bubble explosion of vaporized material or pressure drop [41] at the end of discharge.These generated particles are mostly spherical and the sizes can differ from below 10 µm up to approx.100 µm.Sizes and ratios of these Metals 2022, 12, 1447 4 of 20 three particle generations are strongly influenced by machining conditions.Considering the size ranges and morphology of these three fractions, the particles from the liquid phase are of greatest interest.Vaporized particles are too small for an AM process and stresscracked particles are too big, irregular in shape and do not show the required sphericity and circularity, respectively.The surface tension forces are responsible for the generation of spherically shaped particles [41][42][43].A spherical shape represents the least surface area, which is energetically the best state caused by the time for spheroidization.Thereby, particles tend to form spheres when the time frame is shorter compared to the time for solidification [44][45][46].Apart from that, another essential property is the composition of solidified particles, which can significantly change by the formation of several distributed elements in the particle volume, as shown in the literature [39,[47][48][49].In contrast, vaporized and stress-cracked particles change their phase composition insignificantly.Moreover, an alloying of the eroded particles from the workpiece electrode takes place with material and elements of the tool electrode and dielectric [44,50,51].In general, spherical particles mostly consist of workpiece material, whereas non-spherical particles consist of tool material.However, there are some major defects observable for a few particles.A lot of them are obtained due to different collision processes of molten droplets and earlier solidified particles.Other common deviations from the spherical shape are particle fusion, cracked or dented surfaces, contaminated surfaces or a satellite formation of smaller particles or agglomerates at the surfaces.The high cooling rate during solidification has a big influence on these factors.Some examples and theories have already been stated in [44,46,52].Furthermore, a more important problem represents the formation of hollow particles, i.e., hollow spheres.They are caused due to gas entrapments and the charge carriers present in the spark gap [53].
sludges as an alternative, more energy efficient and less expensive AM powder.Concluding, the main focus deals with the particle sizes and forms within the waste streams and not the machining settings or any kind of improvements in the EDM mechanism itself.

Particle-Generation Mechanisms
As already mentioned, the main process in EDM is based on an erosive character of generated electrical discharges, caused by the transformation of electrical energy into thermal energy, which leads to a material removal.Therefore, an electrical potential is applied between the two movable/flexible electrodes.The upper electrode is the tool electrode and the lower one the workpiece electrode, which represents the machined component.The dielectric fluid is located in between.The potential leads to the generation of an electrical field and its strength increases until the dielectric strength is exceeded, which leads to the electrical discharge.That discharge takes place at the shortest distance between the electrodes, which is called gap size or spark gap and has a significant influence on the process.As a result, temperature rises in the working zone clearly over 10,000 K, whereby the materials melt.In principle, the whole process is divided into four phases, which are repetitive with a defined frequency adjusted by the pulse generator [17,38].The first phase contains the impact ionization of the dielectric, where electrons are smashed out of the molecules and form positive ions due to the force of the electric field.Secondly, the phase of ignition follows, dominated by a current flow.The positive ions start to migrate to the workpiece electrode and the negative electrons move to the tool electrode, resulting in a formation of a discharge channel and a temperature and pressure rise.In the third phase, when a constant current flow is reached, the discharge channel expands, plasma is generated and the materials start to melt and vaporize, resulting in a growing cavitation bubble.Finally, in the fourth phase the potential feed is interrupted and the discharge channel collapses.Thereby, the temperature decreases abruptly, the cavitation bubble collapses and the melt vaporizes explosively and carries molten material from deeper areas, which is transported away by the dielectric.Several pulses are repeating in a defined time frame of several micro-or milliseconds until the desired material removal is completed.A schematic sketch of the EDM process is shown in Figure 1.

Influence of Machining Settings
Commonly used ranges of machining parameters are shown in Table 1, in accordance with the literature [2,5,17,38].The determining parameters are voltage, discharge current, pulse width/time and gap size.Besides that, the material removal rate (MRR) and tool wear rate (TWR) are two important factors, as well.Hereafter, changes of influencing parameters are shown on size properties, regarding eroded and debris particles, respectively.The first three parameters mentioned in the table above have the most significant influence on particle size and distribution, respectively.For the applied voltage, thus the energy input into the machining area between both electrodes, Khanra et al. [46] stated that the average particle size increases with higher energy values.Furthermore, a higher energy input results in higher currents and pulse lengths as well, which is additionally proven by Katiyar et al. [54].As a negative side effect, the number of defects also increases, which leads to more dents and cracks on the surfaces due to the higher possibility of collisions among the particles [46,54].Walter et al. [55] described that the yield of smaller particles decreases with increasing energy and longer time periods.Considering the influence of the chosen discharge current, it goes along with the energy and pulse time.A higher current and longer pulse time leads to higher energy for melting the material, which results in larger-sized particles [52].In contrast to that, Oßwald et al. [56] could prove smaller particles at a lower discharge current.Furthermore, when applying an increased current at a constant pulse duration, the generated particle sizes increase again, as described by Lin et al. [43].Khanra et al. confirmed the influence on resulting particle sizes by customizing the pulse time [46].Longer pulse durations lead to larger particles and shorter ones to smaller particles.This was already reported by Berkowitz et al. [57,58].In the time period of shorter pulses, more material will be vaporized rather than made molten, which results in smaller particle sizes.Another argument for smaller particles with shorter pulses could be justified by the faster solidification time, as mentioned in [54,56].
One of the most important parameters for the particle composition as well as the size is the choice of the dielectric fluid.Comparing deionized (DI) water with hydrocarbon-based oil, Muttamara et al. [59] described for steels in DI water an oxide formation and generation of the austenitic phase.In contrast to that, machining in oil leads to a carbide formation including development of the martensitic phase with retained austenite, which appears as a dendritic structure.Apart from that, particles eroded in DI water tend to be smaller because water generates a bigger vapor volume in the discharge gap, whereas particles eroded in kerosene/oil became bigger.Some investigations conducted by Leão et al. came to the same results [37].Moreover, the usage of oil leads to reactions of particles with carbon, hydrogen and oxygen as well as higher carbon and carbide contents due to a pyrolysis of the dielectric [57].One advantage in using DI is the non-occurrence of contamination in the gap, because no carbon is present, according to Shabgard et al. [60].As a side effect, discoloration of the fluid can occur, which indicates reaction and oxidization processes within the dielectric itself.Tsukahara et al. reported [61] that metallic particles reacting with this altered oil form organometallic compounds with lipophilic properties.Sanghani et al. [62] offered a detailed review about effects of various dielectrics and powder additives on the machining performance and resulting particle properties.It has to be mentioned that gas can be used as a dielectric, e.g., in near-dry EDM [21], as well.
The MRR und TWR have to be considered as well when discussing the output of debris particles.In general, a higher material removal indicates a higher volume and numbers of eroded particles.It was figured out that MRR and TWR are lower in plain water than in oil [37].Water has a lower viscosity, which reduces the energy density in the gap and leads to smaller particles and less material removal.In addition, the raised viscosity of a hydrocarbon-based dielectric decreases the MMR due to higher energy densities.Furthermore, decomposing at higher pressures improves the removal rates once more.According to Lin et al. [43], the values for MRR and TWR for cemented tungsten carbide increase with higher discharge currents on the one hand, but decrease with longer pulse duration on the other hand.Li et al. [63] stated that the wear at both electrodes as well as the total machining time are highest in hydrocarbon-based dielectrics.High machining times are induced by thermal decomposition of the dielectric.Singh et al. [64] studied the influence of different electrode materials on the material removal.Thereby, copper and alumina showed the highest material removal.
The gap size represents the discharge length and has to be adapted to the machining conditions.When the gap is increased, a better flushing performance of the dielectric as well as debris removal are achieved, respectively, as claimed by Prohaszka et al. [65].Apart from that, the build-up of debris material within the gap, which affects the plasma channel and discharges itself negatively, can be inhibited by varying the gap size to find an acceptable balance between a too short and too long discharge distance [41].Commonly, the ablated workpiece material solidifies in the dielectric fluid and should be flushed away from this.In contrast to that, Murray et al. [66] observed that machined material could attach on the electrode surface and becomes molten again, which can lead to an undesired debris build-up and inhibition of the flushing process within the gap.This debris migration back to the tool is one discharge gap phenomenon.Within the gap, the flushing performance and removal of the molten and vaporized material is important, which is realized with different flushing modes and electrode geometries [67,68].
In the following, some special cases are listed.Soni et al. [44] found that a higher rotation of the tool electrode in rotary EDM causes smaller particles.Besides that, ultrasonic assistance during the EDM process leads to greater sphericity of the particles, but simultaneously to a larger number of collision dents and defect areas [52].Last but not least, the addition of specific surfactants inside the dielectric fluid increases the machining efficiency in general, which was discovered by Wu et al. [69].Another interesting feature caused by a surfactant is more stable and stronger discharge, reducing the particle agglomeration within the debris; this shows a narrower PSD.

Comprehensive Overview of Selected Literature
This section of the study shows an overview of different references from the literature, including journal articles, conference papers, lecture books and brochures, regarding different electrode materials, dielectrics, machining parameters and resulting size and shape properties of eroded particles.Table 2 represents a collection and cross comparison of at least 16 references dealing with characteristic material combinations in the field of electro discharge machining and spark erosion, respectively, in the past and present times.Therefore, several tables, PSD and SEM images of these references were exploited.Values out of tables and PSD were adopted in Table 2. To generate quantitative particle size data out of SEM images, the software ImageJ was used by setting a scale bar and measuring the diameters, here the diameter of a circle of equal projection area (EQPC), of depicted particles.Out of these findings the x 50 /median values, standard deviations and average circularities were calculated and presented with the largest particle size.To visualize the range of particles sizes, nine PSDs out of seven references are shown in Figure 2. Two more shown PSDs result from three different machining settings (pulse on time), which were investigated in that specific study, to show the effects discussed in Section 2.2.Apparently, there is a wide range of material combinations and dielectrics, respectively.Furthermore, different machining settings were used, and sometimes a comparison of changing machining settings was investigated for the same system.
( To visualize the range of particles sizes, nine PSDs out of seven references are shown in Figure 2. Two more shown PSDs result from three different machining settings (pulse on time), which were investigated in that specific study, to show the effects discussed in Section 2.2.Apparently, there is a wide range of material combinations and dielectrics, respectively.Furthermore, different machining settings were used, and sometimes a comparison of changing machining settings was investigated for the same system.Katiyar 2018 [54] Golubeva 2017 [73] König 2007 [17] Storr 2006 [38] Cabanillas 2007 [75] Figure 2. Particle size distributions for selected references gained from ImageJ analysis.Data from [17,38,46,54,71,73,75].As highlighted in Figure 2, particles from all PSDs presented would be suitable for AM components.The dotted black lines at 10 µm and 100 µm particle size can be defined as borders of AM powder requirements, as mentioned in the introduction.Apart from that, not just the sizes in general, but even the distributions show acceptable results.Thereby, no classifying techniques were applied on these particle systems.Theoretically, by using sieving and/or sifting processes with upper (100 µm to 125 µm) and lower (10 µm to 15 µm) separation cuts, even better results should be achieved.Relatively narrow particle size distributions are observable for nearly all references, which are suitable for an AM process.The x 50 values and particle sizes indicate a usage for more than one single AM process-techniques from SLM to EBM, direct metal deposition (DMD) or binder jetting are possible.Moreover, the PSDs differ quite strongly, as shown in Katiyar et al. [54], with an x 50 of around 8 µm for die steel, both machined in synthetic oil, or Haas et al. [71] at around 89 µm for an unknown steel, which represents the highest investigated value as well.It is important to mention that AM powders require an x 50 values of minimum 20 µm to 25 µm.Taking this into account, the first three and the last reference particles could not be used for further steps without removing the smallest and biggest particles, respectively.Sieving processes would solve this problem and the remaining particles could be used for an AM process.So, for instance, by using an ultra-fine grain sifter for the particle system described in reference (10) [54], the lower separation cut could be set at 15 µm, resulting in a theoretical usage of the upper approx.35% of the particles.The remaining particles below 15 µm are suitable for a binder jetting process, etc.In addition to that, nearly all particles in reference (2) [46] fit well to AM requirements and could be used further in an SLM process.Moreover, considering the PSD obtained from (6) [71] nearly 30% to 40% of the particles, which are larger than 125 µm, are not useable in AM and should be removed with a sieve.For a handful of cases, some partitions between an SLM or EBM technique should be made.Sieving processes would result in-minimum-two size fractions, whereby each fraction is suitable for one AM technique.This would make sense in the case of analyzed references (11) [73] or (15) [75].
Smallest particle sizes were obtained by Ayers et al. [76] for tungsten machined in kerosene with around five microns.In general, it is quite conspicuous that a lot of the smallest particle sizes were reported when machining tungsten and tungsten-based alloys and materials [39,60], with the aim of producing metal carbides [6].Quite a few analyzed circularity values do not meet the specifications for an AM powder.The minimum value for circularity should be 0.85, whereby a value of 1 represents the ideal circle.The best results were obtained for references (2) [46] and (5) [56], combined with their x 50 values; the particle systems fit nearly completely to requirements for further applications.Bad examples are shown for references (8) [57] and (13) [74], whereby the image quality and brightness as well as the contrast ratios led to unsatisfactory results, even though acceptable particle shapes are visible.

Materials and Methods
Filter cartridges from die-sink EDM machines were collected from regional companies and were sent to the research facility.The amount of delivered cartridges or sludges differs quite strongly for each company and these are registered simultaneously to obtain an impression of accumulating waste.Thereby, the operating time of a cartridge can be very high, meaning that some companies can provide several cartridges per year, which would be around some kilograms of waste, whereas others produce significantly higher kg amounts.Additionally, cartridges operate until a defined time period of machining hours is exceeded or until reaching a pressure indication.Furthermore, raw sludge can be collected in small containers.Information about geometries, masses and used materials of received sample cartridges is stated in Table 3, and representative images are given in Figure 3.It has to be mentioned that no information about processing/machining parameters for the sludge containing cartridges is available.The implemented software in these used EDM machines automatically adjusts parameters for current, voltage, pulse width and gap size according to the component, depending on geometry, desired shape or material.To extract the sludges/debris, a dismantling step was necessary due to the design of the cartridges (Figure 4).The black and oily sludge was enclosed in a metallic cylinder with a perforated mesh.With the help of some tools, it was possible to remove these parts and to uncover filter material and slats, which collect the sludge after the flushing mechanism to reuse the dielectric.Finally, the material from the nonwoven fabric was scraped off and collected.In Figure 3, all steps of dismantling are shown.For another filter type, the filter material without any shell was delivered.In general, sludge consists of three different components, which are the oily phase, particles from the tool electrode-graphite-and particles from the workpiece electrode-always metallic particles.To extract the sludges/debris, a dismantling step was necessary due to the design of the cartridges (Figure 4).The black and oily sludge was enclosed in a metallic cylinder with a perforated mesh.With the help of some tools, it was possible to remove these parts and to uncover filter material and slats, which collect the sludge after the flushing mechanism to reuse the dielectric.Finally, the material from the nonwoven fabric was scraped off and collected.In Figure 3, all steps of dismantling are shown.For another filter type, the filter material without any shell was delivered.In general, sludge consists of three different components, which are the oily phase, particles from the tool electrode-graphite-and particles from the workpiece electrode-always metallic particles.To extract the sludges/debris, a dismantling step was necessary due to the design of the cartridges (Figure 4).The black and oily sludge was enclosed in a metallic cylinder with a perforated mesh.With the help of some tools, it was possible to remove these parts and to uncover filter material and slats, which collect the sludge after the flushing mechanism to reuse the dielectric.Finally, the material from the nonwoven fabric was scraped off and collected.In Figure 3, all steps of dismantling are shown.For another filter type, the filter material without any shell was delivered.In general, sludge consists of three different components, which are the oily phase, particles from the tool electrode-graphite-and particles from the workpiece electrode-always metallic particles.After filtration, the particles were washed again in acetone and/or isopropanol and finally dried in an oven overnight at 80 °C.As a side effect of the filtration processes, effects of sedimentation behavior were investigated.With time, the heavier steel particles settled at the bottom of the flasks and the supernatant solution containing the lighter particles and most of the graphite was decantated, resulting in two different fractions of particles for further characterization, which were mostly graphitic flakes of the filter cake on the paper, and metallic residues in the glass flasks.
Measurements with laser diffraction, permanently with cuvette R3, and with dynamic image analysis in 300 mL liquid with a stirrer at 600 rpm and pump speed at 65 rpm (HELOS and QICPIC LIXELL, both Sympatec GmbH, Clausthal-Zellerfeld, Germany) were carried out to quantify particle size and shape, especially circularity, in a dry or wet (dispersed in isopropanol and/or DI water) state.The initial sludge could be suspended in isopropanol with ultrasound assistance (3 min, 50% amplitude, cycle 1) and was measured with laser diffraction as well to compare size values before and after filtration and cleaning procedures.All of the following investigations were performed with After filtration, the particles were washed again in acetone and/or isopropanol and finally dried in an oven overnight at 80 • C. As a side effect of the filtration processes, effects of sedimentation behavior were investigated.With time, the heavier steel particles settled at the bottom of the flasks and the supernatant solution containing the lighter particles and most of the graphite was decantated, resulting in two different fractions of particles for further characterization, which were mostly graphitic flakes of the filter cake on the paper, and metallic residues in the glass flasks.
Measurements with laser diffraction, permanently with cuvette R3, and with dynamic image analysis in 300 mL liquid with a stirrer at 600 rpm and pump speed at 65 rpm (HELOS and QICPIC LIXELL, both Sympatec GmbH, Clausthal-Zellerfeld, Germany) were carried out to quantify particle size and shape, especially circularity, in a dry or wet (dispersed in isopropanol and/or DI water) state.The initial sludge could be suspended in isopropanol with ultrasound assistance (3 min, 50% amplitude, cycle 1) and was measured with laser diffraction as well to compare size values before and after filtration and cleaning procedures.All of the following investigations were performed with cleaned and processed particles and fractions.An upper separation cut was introduced with sieves of a mesh size of 125 µm.
Apart from that, images were taken via a desktop SEM (with 10 kV, Phenom, FEI/Thermo Fisher Scientific Inc., Waltham, MA, USA) with BSE imaging (through backscattered electrons) to achieve additional size and shape information as well as typical particle defects like cracks, dents and satellites.For an impression of the chemical composition of eroded particles, investigations with another SEM in BSE mode (with 10 kV or 20 kV, XL30 ESEM FEG, FEI/Thermo Fisher Scientific Inc., Waltham, MA, USA) combined with energy-dispersive Xray spectroscopy (Software EDAX Genesis, Ametek Inc., Berwyn, IL, USA) were conducted on sputtered samples.
Afterwards, a new standard for optical emission spectroscopy with inductively coupled plasma (ICP OES; iCAP 6300, Thermo Fisher Scientific Inc., Waltham, MA, USA) could be calibrated containing elements out of EDX results of typical alloy elements.These were Al, Co, Cr, Cu, Fe, Mn, Mo, Ni, P, Si and V.The standard solutions were obtained from Carl Roth (GmbH and Co. KG, Karlsruhe, Germany).Before measuring, samples were dissolved and boiled in aqua regia.The sample masses differ between 100 mg and 300 mg.The carbon and sulfur content was measured using a G4 Icarus C-S-Analyzer (Bruker AXS GmbH, Karlsruhe, Germany).Thereby, around 1 g of sample material was combusted in an oxygen stream and measured with two infrared detectors each for C and S after calibrating the device with certified steel reference materials.
Hereafter, thermogravimetric analysis (TGA) via differential scanning calorimetry (DSC; STA 443 F3 Jupiter, Netzsch GmbH and Co. KG, Selb, Germany) was performed for oil containing samples SE_01-MT and SE_02-AP in a nitrogen atmosphere from room temperature up to 1000 • C with a heat rate of 10 K min −1 .
To compare results of eroded particles, two reference materials were chosen and investigated with exactly the same methods.Reference materials were steel powder of austenitic stainless steel 316L/1.4404/X2CrNiMo17-12-3(Hoeganaes Corporation, Starck Surface Technology and Ceramic Powders GmbH, Goslar, Germany) with a particle size range of 15 µm to 45 µm (max.5% over-/undersize) and martensitic hot work steel H11/1.2343/X37CrMoV5-1(GKN Powder Metallurgy/GKN Hoeganaes Corporation Europe, Buzau, Romania) with a range of 15 µm to 53 µm, respectively, according to data sheets.The reasons for choosing these two specific powders are explained in Section 5.3 regarding the results of the analysis of their chemical composition.

Comparison of Literarue Values, Real Waste Streams and AM Reference Materials
In Figure 5, the analyzed x 50 values of 13 particle systems out of eight representative literature references, which were generated with different machining settings, are plotted against their circularity values and compared to each other as well as to reference materials and eroded particles, respectively.Dotted vertical lines represent the upper and lower median particle sizes for AM processes and the horizontal line indicates the minimum value for their circularity.The abbreviation 'Set X' indicates a specific machining setting within the same material system of the particular literature and 'AM Ref' a commercial reference material used in AM.Particle systems showing low circularity values are not presented in Figure 5 due to their lack of suitability, but are displayed in Table 3.Moreover, some particle systems show a big scattering within their circularity values as well as their x 50 values.Overall, it can be stated that the eroded particles extracted from SE_01 (cyan star) already fit well with the requirements with an x 50 close to 30 µm and a circularity of 0.9.By removing agglomerates from the SE_01 sample, visible in dynamic image analysis, which results from attachments of several smaller spherical particles, the values for circularity can even be increased.With sieving and sifting, the median particle size of this sample can be optimized.Comparing SE_01 with eroded particles from Golubeva et.al. [73], who tried a printing process of components in an SLM machine, SE_01 shows better properties.Their results were not acceptable because printed parts collapsed and were not stable enough.Maybe the PSD was not optimized; thus, there is no detailed information given, just a very narrow range of 30 µm to 50 µm.Besides that, from image analysis it is conspicuous that the circularity is definitely not high enough at below 0.8 and it scatters as well, whereas the x50 value is ok, maybe a little too high.Moreover, Oßwald et al. [56] reported one machined fraction, which fits very well with the requirements.Two others with different machining settings have too small median particle sizes, which should be optimized by  [38,46,54,56,58,71,73,76].
Comparing SE_01 with eroded particles from Golubeva et.al. [73], who tried a printing process of components in an SLM machine, SE_01 shows better properties.Their results were not acceptable because printed parts collapsed and were not stable enough.Maybe the PSD was not optimized; thus, there is no detailed information given, just a very narrow range of 30 µm to 50 µm.Besides that, from image analysis it is conspicuous that the circularity is definitely not high enough at below 0.8 and it scatters as well, whereas the x 50 Metals 2022, 12, 1447 12 of 20 value is ok, maybe a little too high.Moreover, Oßwald et al. [56] reported one machined fraction, which fits very well with the requirements.Two others with different machining settings have too small median particle sizes, which should be optimized by processing steps, but have good circularities.References [54,58] cannot fulfill any requirement, thus representing unsuitable waste streams, whereas references [38,71] and maybe [76] fulfill requirements regarding their circularities.With additional processing steps, x 50 values can be shifted to desired sizes.
Looking at the performance of eroded particles compared to both acquired commercial AM materials, sample SE_01 is already on a very good level.The data points are very close together, just with a little bit lower x 50 value, but even equally high circularity, which is underlined in Figure 6, too.The green triangle is an AM reference as well, and overlaps nearly perfectly with our investigated recycled powder.In fractions resulting from different machining settings shown in [46,56], very good results for circularities are achieved.Only median particle sizes have to be adjusted.It can be concluded that several eroded particle systems fulfill the main requirements and should be considered for a direct recycling chain.

Particle Size Distributions and Particle Morphologies
Figure 6 illustrates different PSDs as well as circularities for both die-sink EDM sludges (unfilled), processed eroded particles of SE_01 and both reference materials (filled).Circularities are shown as single data points.In Table 3, the characteristic particle values are outlined.
The size distribution of both sludges is obviously bimodal and has a very wide range of particle sizes.Svedberg already claimed in 1924 that a bimodal PSD could be a consequence of an oscillatory arc [42], as it is used in EDM.Already 13% (SE_01) or even up to 20% (SE_02) of all particles are 0.9 µm or smaller, which is the technical limit of the used cuvette.By looking at the targeted minimum particle size for the chosen AM processes of 10 µm to 15 µm, it is quite underwhelming for SE_02 that only approx.15% of the particles could be used in further processes.In contrast to that, for SE_01, nearly 40% could be recycled.These results are comparable to investigations from Walter et al. [55] or Berkowitz et al. [57], who found for their particle system that up to 70% of the particles are smaller than 20 µm.Compared to Golubeva et al. [73], where only 15% of the particles are in a suitable size range, particles from SE_01 show better results.It is not clear which material from which electrode is present in each size class.Due to thermal stresses and vaporization effects, amounts of graphitic electrode material could accrue in the smallest

Particle Size Distributions and Particle Morphologies
Figure 6 illustrates different PSDs as well as circularities for both die-sink EDM sludges (unfilled), processed eroded particles of SE_01 and both reference materials (filled).Circularities are shown as single data points.In Table 3, the characteristic particle values are outlined.
The size distribution of both sludges is obviously bimodal and has a very wide range of particle sizes.Svedberg already claimed in 1924 that a bimodal PSD could be a consequence of an oscillatory arc [42], as it is used in EDM.Already 13% (SE_01) or even up to 20% (SE_02) of all particles are 0.9 µm or smaller, which is the technical limit of the used cuvette.By looking at the targeted minimum particle size for the chosen AM processes of 10 µm to 15 µm, it is quite underwhelming for SE_02 that only approx.15% of the particles could be used in further processes.In contrast to that, for SE_01, nearly 40% could be recycled.These results are comparable to investigations from Walter et al. [55] or Berkowitz et al. [57], who found for their particle system that up to 70% of the particles are smaller than 20 µm.
Compared to Golubeva et al. [73], where only 15% of the particles are in a suitable size range, particles from SE_01 show better results.It is not clear which material from which electrode is present in each size class.Due to thermal stresses and vaporization effects, amounts of graphitic electrode material could accrue in the smallest and largest size classes, whereas the congealed material from the steel electrode tends to erode more into liquid than into vapor due to its ductile behavior [39] resulting in bigger particles from the liquid phase.Besides that, graphite particles distinguish clearly from metal particles, as seen in Figures 7 and 8. Their shapes are irregular and differ strongly, whereas metallic particles tend to form spheres with high circularity.However, circularities cannot be measured with certainty for small particle sizes, since the resolution limit in a dynamic image analysis device is reached below 5 µm to 10 µm.For processed, dried and sieved SE_01 particles, a lower separation cut is visible.Compared to raw sludge, approx.1% instead of 65% are below 10 µm.The x50 value shifted from 5.21 µm to 27.52 µm and is close to the references with 34.66 µm and 30.08 µm, respectively.Besides that, the PSD is not as narrow as it should be for a secondary usage, as can be seen in the x10 and x90 values.Therefore, additional sieving and sifting processes are suggested to create at least two or three fractions.However, the x90 value for the H11 reference is relatively high with 61.68 µm, compared to the 316L reference.With an ultra-fine grain sifter, the lower separation cut will be optimized.Afterwards, sieving with a 45 µm or 63 µm sieve to obtain a fraction for SLM processes (approx.60%) should be carried out.The remaining 30% of the particles up to 125 µm are suitable for EBM  For processed, dried and sieved SE_01 particles, a lower separation cut is visible.Compared to raw sludge, approx.1% instead of 65% are below 10 µm.The x50 value shifted from 5.21 µm to 27.52 µm and is close to the references with 34.66 µm and 30.08 µm, respectively.Besides that, the PSD is not as narrow as it should be for a secondary usage, as can be seen in the x10 and x90 values.Therefore, additional sieving and sifting processes are suggested to create at least two or three fractions.However, the x90 value for the H11 reference is relatively high with 61.68 µm, compared to the 316L reference.With an ultra-fine grain sifter, the lower separation cut will be optimized.Afterwards, sieving with a 45 µm or 63 µm sieve to obtain a fraction for SLM processes (approx.60%) should For processed, dried and sieved SE_01 particles, a lower separation cut is visible.Compared to raw sludge, approx.1% instead of 65% are below 10 µm.The x 50 value shifted from 5.21 µm to 27.52 µm and is close to the references with 34.66 µm and 30.08 µm, respectively.Besides that, the PSD is not as narrow as it should be for a secondary usage, as can be seen in the x 10 and x 90 values.Therefore, additional sieving and sifting processes are suggested to create at least two or three fractions.However, the x 90 value for the H11 reference is relatively high with 61.68 µm, compared to the 316L reference.With an ultra-fine grain sifter, the lower separation cut will be optimized.Afterwards, sieving with a 45 µm or 63 µm sieve to obtain a fraction for SLM processes (approx.60%) should be carried out.The remaining 30% of the particles up to 125 µm are suitable for EBM processes.Particles below 15 µm to 20 µm can be considered for a usage in binder jetting.
Both reference materials show a narrow and normally distributed PSD, as could be assumed.Their particle sizes differ between approx.10 µm and 60 µm.Circularity values (in Table 4) are on a high and mostly constant level of around 0.9, but decrease slightly with an increase in the particle size, maybe caused by the optical resolution.For the smallest particles, a downshift in circularities is observed, too.This trend is noticeable for eroded particles, as well.However, the H11 reference has the highest circularity with 0.93, whereas the chemically related SE_01 powder and different reference 316L show both values of 0.90, which fulfills the requirements for AM powders as well, combined with the overall good x 50 values.Upper and lower cuts for SE_01 must be improved in further steps via sieving and sifting.Information about the masses of oil and solid phase, which is split up into graphitic and metallic parts roughly, was gained via filtration and washing experiments as well as TGA-DSC analysis.Sludge SE_01 shows an oil content of around 55 wt% to 60 wt%, whereas SE_02 contains significantly more oil with around 85 wt%.By means of filtration and decanting, the solid contents of SE_01 could be roughly separated from each other and have amounts of approx.15 wt% for metallic residues in the flasks and around 20 wt% to 25 wt% of graphitic flakes with metallic inclusions.It is important to mention that it was not possible to gain enough metallic material out of cartridge SE_02-AP.The very high oil content and very high amount of extremely small particle sizes, as seen in Figure 6 (PSD), was quite challenging.Besides that, the amount of sludge in these filter cartridges is very low in general; it would not be useful or profitable enough to consider this specific waste stream for further usage; see Table 3.Therefore, no measurements with laser diffraction and dynamic image analysis of dry powder could be performed.
SEM images in Figure 7 show morphological properties of both commercial reference AM powders (a + b) and the processed particles of SE_01 (c).What was already seen in the PSD and associated Table 4 can be confirmed.All three particle systems have a quite similar size range, though for SE_01 some very small as well as sometimes big particles are present, since this is the virgin material without further processing.For both reference powders, typical defects like satellites or particle fusion are visible, though not in that low amount compared to eroded particles.Thereby, nearly all particles show very constant circular shapes.However, for some particles, strong surface contaminations, resulting in rougher surfaces, are visible; their origin is investigated and explained in Section 5.3 via EDX analysis.Besides that, due to the ordinal number/material contrast, a mixture of brighter and darker particles is observable (also demonstrated in Figure 9b), whereas brighter ones are present in larger numbers.Darker particles can be distinguished between surface contaminated brighter ones and regular darker ones consisting of second metallic material caused by machining of two sufficiently different metallic components in the same device.
rougher surfaces, are visible; their origin is investigated and explained in Section 5.3 via EDX analysis.Besides that, due to the ordinal number/material contrast, a mixture of brighter and darker particles is observable (also demonstrated in Figure 9b), whereas brighter ones are present in larger numbers.Darker particles can be distinguished between surface contaminated brighter ones and regular darker ones consisting of second metallic material caused by machining of two sufficiently different metallic components in the same device.Overall, the morphologies of all metal powders look quite good.Particles show good spherical shapes and a low number of defects, which could be confirmed by the measurements applying dynamical image analysis (Table 4).The surfaces appear relatively smooth.Measurements with atomic force microscopy (AFM) may confirm these assumptions in the future by comparing the surface roughness values of all the particle systems regarding the influence of the different cooling speeds and temperature gradients during resolidification.Moreover, reference powders appear to have a higher number of satellites, which is due to the atomization process.
However, there are some typical defects observable in eroded particles as well, which are collected in Figure 8.It is quite common that some particles show irregular shapes and anomalies in their shape, structure or surface.Khanra et al. [46] and Murti et al. [52] discussed typical particle defects in erosion sludges, which are comparable to the ones presented here.All defects are shown for commercial AM powders in the literature [29, 77,78] as well, and can also be confirmed in Figure 7a,b.The number of these defects should always be low and in an acceptable range, which can be correlated with circularity values or circularity distributions, respectively.Particles with low circularities will have some defects like particle fusion, agglomeration, gas entrapments, dents, splats or cracks.Other typical observations are dendritic structures of surface contaminations.Latter ones should definitely be removed or minimized, which will be achieved with a secondary cleaning and washing step and/or ultrasonic assistance during oil removal.

Chemical Composition
At first, an EDX analysis of SE_01 was performed to obtain an impression about machined metallic components.Some characteristic areas, which were analyzed via the x-ray beam, are shown in Figure 9. Sometimes, metallic particles are enclosed in or agglomerated around graphitic fragments, which are caused by thermal stresses and induced brittle failure (Figure 9a).In Figure 9b, a mixture of brighter and darker particles is presentbrighter ones are detected as steel particles and darker ones as alumina (partially oxidized) particles.The amount of alumina particles is significantly lower.Surface contaminations are observable again (e.g., Figure 9c) and could be identified as carbon structures originating from the pyrolysis of the dielectric fluid and/or the graphitic electrode.Mainly, the results indicate a machining of two different metallic components, which should be separated from each other in an additional processing step, for example, by magnetic or density separation (susceptibility and density values differ sufficiently).In the following, Al particles are not considered further due to their low amount and the high oxygen peaks in their EDX spectra.The iron-based eroded particles are assignable to a typical alloy, which is mainly used in the sector of mold and vehicle construction, namely H11, 1.2343 or X37CrMoV5-1.Considering these results, the choice of reference materials was unequivocal.To compare properties of eroded particles, commercial AM powder for SLM machines of martensitic hot work steel H11/1.2343 was chosen.Additionally, a second and most commonly used AM material in laser powder bed fusion and the automotive sector was investigated to have another comparison with industrial products.This is stainless steel 316L, 1.4404 or X2CrNiMo17-12-3, which shows a different magnetic behavior due to the austenitic microstructure [79].For both reference powders, PSDs and SEM images are shown above (Figures 6 and 7a,b) and chemical compositions in Table 5 below.The chemical compositions of several samples of eroded particles (1-3) and reference material H11 (4) are shown in Table 5. Thereby, for SE_01, one should distinguish between two fractions resulting from the cleaning/washing steps.These are silver-grey metallic residues (3) and black-graphitic flakes with metallic inclusions (1) out of the filtration process.The content of iron always maintains the remaining balance.
A comparison of SE_01 (1) with SE_02 (2) shows nearly the same composition of hot-work steel H11/1.2343,without any side elements in SE_02.After queries with the companies, H11/1.2343 was confirmed.It is interesting to observe the untypical amount of Al, Ni and Co in SE_01 samples, which results from a different alloy resulting from machined Al-based materials with typical alloying elements Ni and Co, including an amount of Cu.When comparing the metallic residue (3) with the filter cake (1), in residues a significantly higher iron amount in balance is observable.By contrast, the Al amount in filter cake structures is about five times bigger.This results from the step of decanting and the high difference in the density values, which distinguish between 7.8 g cm −3 for steel particles, 2.7 g cm −3 for Al particles and 2.2 g cm −3 for remaining graphite particles.High amounts of Fe-based particles as well as bigger/heavier Al and graphite particles in the suspension settle down, whereas lighter ones, mostly Al and graphite, but also very small Fe-based particles, are decanted and filtrated.Besides that, the values for Si and Cr are a little bit too low, but overall the alloy composition is sufficient enough.
Results from the C-S-Analyzer confirm the assumptions of a higher carbon content after machining due to alloying effects from the graphite electrode as well as a pyrolysis of the hydrocarbon-based dielectric.Values for C in data sheets are given with 0.33 wt% to 0.43 wt%, whereas around 5.4 wt% C was investigated for eroded particles of SE_01, which is stated and comparable to another study with 4.69 wt% [56].To decrease the carbon content to an acceptable range, several options may be possible.On the one hand, the contaminated surfaces can be cleaned properly to remove excessive carbon, which can be achieved via an energy input by an ultrasound sonotrode and/or by stressing the particles in a (wet grinding) ball mill without additional grinding balls to expose the particles to mutual shear processes and shear forces due to particle collision and induce a cleaning effect.On the other hand, via density separation techniques, excessive carbon between the particles in each size class could be removed simultaneously with Al particles.A certain amount of carbon cannot be resolved because, due to diffusion processes during the melting and congealing phases, an increased irreversible migration of carbon atoms into the crystal lattice of iron can be expected.
The amount of sulfur is in an acceptable range.In datasheets, a maximum is given with about 0.02 wt.% to 0.03 wt% max., whereas eroded particles show a value of approx.0.013 wt%.However, the chemical purity in general must be improved.

Conclusions and Outlook
In this study, the principle suitability of eroded particles originating from electro discharge machining after processing and cleaning steps could be shown.By investigating several literature references using image analysis software and evaluating SEM images as well as particle size distributions given in these articles, a theoretical suitability of eroded particles was underlined.After processing the sludges via cleaning, washing, filtrating, decanting in organic solvents and classifying, characterizations of these particles were performed regarding the important specifications such as particles size distribution, morphology, circularity as well as chemical composition.The particle sizes (distribution) of eroded particles already fits quite well with those of the references by looking at the x 50 values, but they are not as narrow as they should be; this can be customized by sieving and sifting processes.The circularities are overall on a high level and comparable with commercial materials.
Further steps will be implemented in following studies to enhance the quality of the recycled powders to improve their suitability as a secondary AM material and, finally, to investigate their performance in AM processes comparing to chosen reference materials.Additionally, the chemical purity must be improved.Sieving and sifting processes will be performed to create two or three size fractions.To separate the Al particles and remaining graphite particles from the steel particles, different physical separation characteristics will be considered.Other characterization methods of powder samples will be carried out to obtain further detailed information about the particle systems, e.g., bulk solid mechanics.By using reference materials, parameter settings in AM machines will be found and optimized, followed by the production of different specimens and investigations of them via several mechanical tests.Moreover, upper and lower rejects from processing could be used in further AM techniques and it is worth considering a secondary usage of graphitic residues in different applications as well.In the near future, a focus on wire-EDM machines, which operate in hydrocarbon oil as well, may be conceivable.

Figure 1 .
Figure 1.Scheme of electrical discharge mechanism used in EDM.The dotted blue lines represent the phases of the discharge-ionization, ignition, discharge, collapse-red lines the electron and proton migration forming the discharge channel and orange lines the direction of material removal stream.
Metals 2022, 12, x FOR PEER REVIEW 10 of 21and gap size according to the component, depending on geometry, desired shape or material.

Figure 4 .
Figure 4. Flow sheet of dismantling, extraction of waste debris/sludge, example for SE_01.

Figure 4 .
Figure 4. Flow sheet of dismantling, extraction of waste debris/sludge, example for SE_01.

Figure 9 .
Figure 9. SEM images of SE_01-MT sample used for EDX analysis: (a) graphite particles with enclosed metallic spheres, (b) spherical debris of steel and aluminum alloy with lots of (sub-micron) agglomerates, (c) spherical particle with carbon contamination on surface, lamellar structure.

Figure 9 .
Figure 9. SEM images of SE_01-MT sample used for EDX analysis: (a) graphite particles with enclosed metallic spheres, (b) spherical debris of steel and aluminum alloy with lots of (sub-micron) agglomerates, (c) spherical particle with carbon contamination on surface, lamellar structure.

Table 2 .
Overview of debris particle sizes and form factors as well as used parameters.

Table 3 .
Overview of investigated filter cartridges.

Table 3 .
Overview of investigated filter cartridges.

Table 4 .
x 50 and circularity values for die-sink EDM particles and both AM reference materials.