Differences in Deformation Behaviors Caused by Microband-Induced Plasticity of [0 0 1]- and [1 1 1]-Oriented Austenite Micro-Pillars

: A uniaxial compression test and scanning/transmission electron microscopy observations were performed to investigate the differences in mechanical behavior and deformed microstructure between focused ion beam-manufactured [1 1 1]- and [0 0 1]-oriented austenite micro-pillars with 5 µ m diameter from duplex stainless steel. After yielding, the strain hardening of two orientation micro-pillars increased sharply as a result of the formation of a microband, namely microband-induced plasticity, MBIP. The same phenomenon could be observed in a [0 0 1]-oriented pillar due to the activation of the secondary slip system, while slight strain hardening behavior was observed in the [1 1 1] orientation because of the reﬁnement of the microband. Furthermore, the trend of the calculated strain hardening rates of both [1 1 1]- and [0 0 1]-oriented micro-pillars were in good agreement with the experimental data. This study proved that MBIP can be helpful for the mechanical property enhancement of steels. investigation, Y.-Y.C.; resources, Y.-F.J. and F.-Z.X.; data curation, Y.-Y.C. and Y.-F.J.; writing—original draft preparation, Y.-Y.C.; writing—review and editing, Y.-F.J.; visualization, Y.-Y.C. and Y.-F.J.; supervision, F.-Z.X; F.-Z.X.; acquisition, Y.-F.J.


Introduction
Austenite-ferrite duplex stainless steels (DSS) are widely used as the pressure vessel and piping in thermal power, nuclear power and other industries [1,2]. As a dual-phase steel, DSS takes advantage of the beneficial properties of its constituent phase, exhibiting higher strength than pure austenite or ferrite stainless steels and not less than 15% elongation, i.e., excellent work hardening performance. Compared with the ferrite phase, the austenite phase undertakes most of the plastic deformation during straining, which mainly determines the overall ductility of DSS [3,4]. Hence, the investigation of the plasticity of local austenite phase is helpful to understand and improve the mechanical properties of whole DSS steel. Depending on the value of stacking fault energy (SFE), plastic deformation mechanisms of austenite phase include austenite-to-martensite transformation-induced plasticity (TRIP, SFE < 20 mJ/m 2 ) [5][6][7], twinning-induced plasticity (TWIP, 20 mJ/m 2 < SFE < 50 mJ/m 2 ) [8][9][10][11] and microband-induced plasticity (MBIP, SFE > 50 mJ/m 2 ) [12][13][14][15]. Many studies have reported the enhancement effect of the formation and evolution of strain-induced martensite and mechanical twinning on plasticity and ductility under uniaxial stress by macro-tensile test [16][17][18][19][20][21] and micro-pillar compression test [22][23][24][25]. I. V. Kireeva et al. [20] pointed out that strain hardening reached the maximum when twinning developed in two systems and decreased in a transition period of the development of twinning predominantly in one system simultaneously with slip. Soares et al. [21] showed strain hardening behavior and microstructural evolution of AISI 304 steel by uniaxial tensile test and found complex strain hardening behavior due to the formation of straininduced martensitic transformation. Choi et al. [23] conducted the compression tests on micro-pillars fabricated from an austenitic Fe-Mn-C twinning-induced plasticity steel and Metals 2021, 11, 1179 2 of 10 learned that deformation twinning induced higher flow stresses and dislocation glide produced more stable work hardening behaviors. Compared with TRIP and TWIP steels, MBIP steel possesses the same excellent combination of strength and ductility, but more stable and continuous strain hardening behavior during straining and more homogeneous microstructure and better strain coordination after deformation. There have been some studies about the strain hardening behavior of nickel compression pillars caused by the dislocation interaction [26][27][28], but little research has been conducted to investigate the contribution of microband formation to the work hardening behavior of the austenite phase at the micro-scale. Hence, in this paper, the plasticity caused by micro-band evolution was studied by compression test on two austenite micro-pillars with different orientations.

Materials and Methods
Studied austenite crystals were from commercial austenite-ferrite duplex stainless steel obtained from Baosteel stainless steel Co., Ltd (Shanghai, China). The chemical compositions and stacking fault energy of the tested austenite phase are shown in Table 1. According to the calculation based on the research result Dai et al. [29], SFE of austenite phase at room temperature was estimated to be 58-73 mJ/m 2 . More information was described in detail previously [30]. As-received material was solution-annealed at 1050 • C for 12 h followed by water quenching to obtain recrystallized coarse grain. Crystallographic orientations of austenite grains were characterized by Electron Backscatter Diffraction analysis (EBSD, Oxford Instruments). Figure 1 shows the EBSD inverse pole figure to Z axis (IPF-Z) of austenite and ferrite grains in the studied DSS. As the surrounded black and white circles show in Figure 1 cos ψ cos ϕ − sin ψ sin ϕ cos θ sin ψ cos θ + cos ψ sin ϕ cos θ sin ϕ sin θ − cos ψ sin ϕ − sin ψ cos ϕ cos θ − sin ψ sin ϕ + cos ψ cos θ cos ϕ sin θ sin ψ sin θ − cos ψ sin θ cos θ        Figure 3 shows the SEM microtopography of compressed austenite micro-pillars. After dramatic deformation with strain larger than 30%, distinct glide traces of inclined slip planes were visible and concentrated on the top and middle of both [0 0 1]-and [1 1 1]-oriented deformed micro-pillar surface. However, the appearance of slip planes on the surface was also crystallographic orientation-dependent. As presented in Figure 3a, in the [1 1 1]-oriented pillar, surface steps were concentrated on one slip plane exclusively and uniformly, i.e., presented in the primary slip system. The repeated gliding on the same plane led to obvious lattice torsion. The angle between activated slip planes and the normal direction of experimental pillar was measured to be 63.9°. By contrast, the surface of the [0 0 1]-oriented deformed micro-pillar presented two glide traces on different slip systems, marked by white and black dashed lines, as shown in Figure 3b, which indicated that, besides the primary slip system, the second set of slip planes was activated. Because of the relatively homogeneous distribution and smaller spacing, the slip traces marked by red dashed lines were considered as the primary slip system, which had a deviation angle of 58.5°. Several slip lines with different angles were found near the top of the [1 1 1]-oriented micro-pillar, indicating that another slip system was activated, which could be explained by the inhomogeneous distribution of compression stress near the top surface of the micro-pillar. The same phenomenon can be observed in another study [31]. The effect of this slipping on strain hardening behavior was negligible to this study.  Figure 3 shows the SEM microtopography of compressed austenite micro-pillars. After dramatic deformation with strain larger than 30%, distinct glide traces of inclined slip planes were visible and concentrated on the top and middle of both [0 0 1]-and [1 1 1]-oriented deformed micro-pillar surface. However, the appearance of slip planes on the surface was also crystallographic orientation-dependent. As presented in Figure 3a, in the [1 1 1]-oriented pillar, surface steps were concentrated on one slip plane exclusively and uniformly, i.e., presented in the primary slip system. The repeated gliding on the same plane led to obvious lattice torsion. The angle between activated slip planes and the normal direction of experimental pillar was measured to be 63.9 • . By contrast, the surface of the [0 0 1]-oriented deformed micro-pillar presented two glide traces on different slip systems, marked by white and black dashed lines, as shown in Figure 3b, which indicated that, besides the primary slip system, the second set of slip planes was activated. Because of the relatively homogeneous distribution and smaller spacing, the slip traces marked by red dashed lines were considered as the primary slip system, which had a deviation angle of 58.5 • . Several slip lines with different angles were found near the top of the [1 1 1]-oriented micro-pillar, indicating that another slip system was activated, which could be explained by the inhomogeneous distribution of compression stress near the top surface of the micro-pillar. The same phenomenon can be observed in another study [31]. The effect of this slipping on strain hardening behavior was negligible to this study.  Figure 3 shows the SEM microtopography of compressed austenite micro-pillars. After dramatic deformation with strain larger than 30%, distinct glide traces of inclined slip planes were visible and concentrated on the top and middle of both [0 0 1]-and [1 1 1]-oriented deformed micro-pillar surface. However, the appearance of slip planes on the surface was also crystallographic orientation-dependent. As presented in Figure 3a, in the [1 1 1]-oriented pillar, surface steps were concentrated on one slip plane exclusively and uniformly, i.e., presented in the primary slip system. The repeated gliding on the same plane led to obvious lattice torsion. The angle between activated slip planes and the normal direction of experimental pillar was measured to be 63.9°. By contrast, the surface of the [0 0 1]-oriented deformed micro-pillar presented two glide traces on different slip systems, marked by white and black dashed lines, as shown in Figure 3b, which indicated that, besides the primary slip system, the second set of slip planes was activated. Because of the relatively homogeneous distribution and smaller spacing, the slip traces marked by red dashed lines were considered as the primary slip system, which had a deviation angle of 58.5°. Several slip lines with different angles were found near the top of the [1 1 1]-oriented micro-pillar, indicating that another slip system was activated, which could be explained by the inhomogeneous distribution of compression stress near the top surface of the micro-pillar. The same phenomenon can be observed in another study [31]. The effect of this slipping on strain hardening behavior was negligible to this study.  Table 2 lists the Schmid factor and deviation angle of all potential slip systems under the theoretical and experimented loading conditions. The ideal [1 1 1]-oriented austenite micro-pillar had the same tendency on six slipping systems. Practical direction of the studied [1 1 1]-oriented austenite pillar was more inclined to [12 14 17]-orientation, and the deviation angle (8 • ), smaller than 10 • , was acceptable. Slip trace analysis indicated that (−1 1 1)[1 0 1] slip direction had the highest Schmid factor of 0.36, i.e., proved to be the primary activate slip system. The angle between the normal of the slip plane and the compression axis should be 63.9 • by the calculation result of the geometric relationship. The measured angle was 61.8 • , however, having a very small difference, which could be caused by the measurement issue, and the deviation was acceptable. The tested [0 0 1]-oriented micro-pillar exhibited two obvious slip systems during the deformation. The actual compressive axis along the [1 0 18] direction had tendentious slip systems of (−1 1 1)[1 0 1] and (1 1 −1)[0 1 1] with Schmid factors of 0.41 and 0.38., respectively. The inclined angle of above two slip system was observed to be 58.5 • , in good agreement with the theoretical angle of 57 • . The activation of the second slip system was attributed to the increase of the resolved shear stress on the second slip plane with increasing strain.  Figure 4 illustrates cross-sectional TEM bright field images and the selected area diffraction pattern of [1 1 1]-and [0 0 1]-oriented compressed micro-pillars. One can note from both microstructure characterization results that clear slip traces could be observed, and no transformation-induced twinning and martensite phase could be found due to high stacking fault energy of the tested austenite crystals. For [1 1 1] orientation, the slip traces were parallel in the exclusive glide plane, and the distribution was uniform and dense on the top of micro-pillar, as shown in Figure 4a. Due to the crystal lattice twist, the slip bands exhibited arc-shaped traces, i.e., had a radian. Compared with the arc-shaped traces of the [1 1 1]-oriented pillar, the slip traces of compressed [0 0 1]-orientation were in the shape of straight lines. Two slip planes with an intersect angle of 69.57 • could be observed, indicating that the secondary slip system was activated. Differently from the whole slip traces with radian in the [1 1 1]-oriented micro-pillar, some of those in the [0 0 1] orientation were inflected, which was considered to be caused by jogged dislocation, marked by white arrows in Figure 4b. The caused dislocation stairs could also be observed on the surface of the deformed micro-pillar characterized by SEM. Some short dislocation fragments could be observed near the bottom of micro-pillar, marked by yellow arrows in Figure 4b, believed to be independent of deformation, i.e., presented in the initial dislocation. tion stairs could also be observed on the surface of the deformed micro-pillar characterized by SEM. Some short dislocation fragments could be observed near the bottom of micro-pillar, marked by yellow arrows in Figure 4b, believed to be independent of deformation, i.e., presented in the initial dislocation.

Elastic Deformation
From the above we can see that for single crystal micro-pillars, the mechanical responses were dependent on the crystallographic orientation. During the elastic deformation stage, the [ and thus, A111 and A001 have the largest discrepancy of 0 and 1/3, respectively. The relationship between Ehkl and Ahkl can be expressed by: where S11, S12 and S44 are three independent factors of a cubic system, taken as 10.7 × 10 −3 , 4.25 × 10 −3 and 8.6 × 10 −3 , respectively [33]. Hence, E111 should be much higher than E001, which is in accordance with our experimental result.

Plastic Deformation
From Figure 2, the yield stresses of [0 0 1]-and [1 1 1]-oriented austenite micro-pillars were 426.9 MPa and 492.5 MPa, respectively. Combined with the Schmid factors of the primary slip system verified by the deformed microstructure observation, the Critical Shear Stresses (CRSS) of [0 0 1]-and [1 1 1]-oriented micro-pillars were calculated to be 183.6 MPa and 173.3 MPa, respectively. The average value of CRSS was calculated to be 178.5 MPa, and the deviation was about 5%, which was negligible here. Other research has also shown that the CRSS value is related to the materials and independent of grain orientation [9,23]. After yielding, the engineering stress-strain curves of both

Elastic Deformation
From the above we can see that for single crystal micro-pillars, the mechanical responses were dependent on the crystallographic orientation. During the elastic deformation stage, the [1 1 1]-oriented micro-pillar possessed a higher Young's modulus of 273.3 GPa than the [0 0 1]-orientation with that of 197.2 GPa. The increase in E 111 can be explained by the anisotropy parameter [32]: and thus, A 111 and A 001 have the largest discrepancy of 0 and 1/3, respectively. The relationship between E hkl and A hkl can be expressed by: where S 11 , S 12 and S 44 are three independent factors of a cubic system, taken as 10.7 × 10 −3 , 4.25 × 10 −3 and 8.6 × 10 −3 , respectively [33]. Hence, E 111 should be much higher than E 001 , which is in accordance with our experimental result.

Plastic Deformation
From Figure 2, the yield stresses of [0 0 1]-and [1 1 1]-oriented austenite micro-pillars were 426.9 MPa and 492.5 MPa, respectively. Combined with the Schmid factors of the primary slip system verified by the deformed microstructure observation, the Critical Shear Stresses (CRSS) of [0 0 1]-and [1 1 1]-oriented micro-pillars were calculated to be 183.6 MPa and 173.3 MPa, respectively. The average value of CRSS was calculated to be 178.5 MPa, and the deviation was about 5%, which was negligible here. Other research has also shown that the CRSS value is related to the materials and independent of grain orientation [9,23]. After yielding, the engineering stress-strain curves of both [0 0 1]-and [1 1 1]-oriented micro-pillars exhibited multiple plastic deformation stages with different strain hardening rates. Compared with the slight strain hardening of the [1 1 1]-oriented micro-pillar from stage III, the deformation response of the [0 0 1]-orientation showed a climb in stage IV. Based on SEM and TEM observation of the tested austenite micro-pillars, the deformed microstructure was characterized by a pronounced dislocation glide plane, which led to the formation of crystallographic slip bands on the activated slip systems, i.e., microband-induced plasticity, MBIP. The tested [1 1 1]-oriented micro-pillar exhibited dislocation glide traces with the same direction while the [0 0 1]-orientation revealed the secondary slip system. Hence, the activation of the secondary slip system induced higher flow stresses.

Flow Stress Expression
The total flow stress (σ t ) after the yielding can be expressed by: (4) where σ y is the yield stress and σ(ε) is the plasticity-driven strain hardening capacity in the flow stress. The first term, σ y , representing the activation of perfect dislocation in the present tests, can be calculated by [8]: where α 0 is a constant describing the character of dislocation, considered as 0.5 for pure edge dislocations here [8], b p is the magnitude of the Burgers vector for perfect dislocation, considered as 0.256 nm for face-centered crystal lattice [8,13] and G is the shear modulus, which was taken as 105.1 GPa and 75.8 GPa for [0 0 1]-oriented and [1 1 1]-oriented micropillars, respectively. Additionally, Λ mentioned before is defined as the "mean free path", which is the average feasible distance of dislocations before they stored or annihilated [34]. The values of Λ were calculated to be 319.7 nm and 206.1 nm for the [1 1 1]-and [0 0 1]-oriented micro-pillars, respectively. For pure dislocation-dislocation mediated plasticity steels, the change of flow stress can be expressed by the evolution of dislocation density, ρ, invariably [35]: where α is a factor related to the material, generally ranged from 0.3 to 0.5 [35]. Differentiating both sides of Equation (6) to the strain, the strain hardening rate, Θ = dσ dε , can be expressed as: where the rate of dislocation accumulation to the strain can be formally expressed as dρ dε = 1 bΛ . Hence, the strain hardening itself can be expressed as: where D is the mean dislocation spacing, expressed as D = 1/ √ ρ. According to Equation (8), the strain hardening rate of the research material during plastic deformation is proportional to the ratio of the mean dislocation spacing and the mean free path. The trend of experimental and calculated strain hardening rates of [0 0 1]-and [1 1 1]-oriented micro-pillars are presented in Figure 5a,b, respectively. For better comparison, all experimental and calculated strain hardening rates were standardized by the strain hardening rate at the yield point. The calculation results had a good description of the trend of strain hardening rate. Micro-pillar compression tests combined with SEM/TEM observation were carried out in this work to describe the differences in mechanical responses and properties of [0 0 1]-and [1 1 1]-oriented single crystal austenite micro-pillars with high SFE value. Another task will be to explore the deformation behaviors of ferrite grains and the effect of grain boundaries on the mechanical property by the same experimental method. The research results can provide a local deformation mechanism support for the overall mechanical description and safety prediction of duplex stainless steel components.

Conclusions
The deformation behaviors and micro-structure evolution of austenite micro-pillars were investigated by a compression test and SEM and TEM observation. The main conclusions are:  Data Availability Statement: Not applicable.

Conflicts of Interest:
The authors declare no conflict of interest. Micro-pillar compression tests combined with SEM/TEM observation were carried out in this work to describe the differences in mechanical responses and properties of [0 0 1]-and [1 1 1]-oriented single crystal austenite micro-pillars with high SFE value. Another task will be to explore the deformation behaviors of ferrite grains and the effect of grain boundaries on the mechanical property by the same experimental method. The research results can provide a local deformation mechanism support for the overall mechanical description and safety prediction of duplex stainless steel components.

Conclusions
The deformation behaviors and micro-structure evolution of austenite micro-pillars were investigated by a compression test and SEM and TEM observation. The main conclusions are: Deformation microstructures of both micro-pillars were characterized by pronounced planar slip. The slipping band structure undergoes refinement during straining, resulting in the strain hardening behavior.

3.
Higher flow stress and unstable strain hardening behavior in [0 0 1]-oriented austenite micro-pillars were assumed to be caused by the easy activation of secondary slip systems.  Data Availability Statement: Not applicable.

Conflicts of Interest:
The authors declare no conflict of interest.