Copper-Tantalum Metal Matrix Composites Consolidated from Powder Blends by Severe Plastic Deformation

: We investigated the effectiveness of severe plastic deformation by equal channel angular extrusion (ECAE) for consolidation of metal powders into metal matrix composites. Equal volumes of copper (Cu) and tantalum (Ta) powders were consolidated at ambient temperature via different ECAE routes. Composites processed by ECAE routes 4E and 4Bc were also processed at 300 ◦ C. The resulting materials were characterized by scanning electron microscopy (SEM) and compression testing. Processing by route 4Bc at 300 ◦ C resulted in the highest compressive strength, lowest anisotropy, and least strain rate sensitivity. We conclude that the superior properties achieved by this route arise from mechanical bonding due to interlocking Cu and Ta phases as well as enhanced metallurgical bonds from contact of pristine metal surfaces when the material is sheared along orthogonal planes.


Metal Matrix Composites
Our goal is to examine the prospects for using equal channel angular extrusion (ECAE) to consolidate powders at low temperature (i.e., without sintering) into metal matrix composites (MMCs) with controlled microstructure. MMCs, also referred to as pseudo-alloys, are a class of materials that have a composite structure with a metal matrix. The matrix phase can either be an alloy [1] or single element [2], while the filler phase can be metal [3,4], intermetallic [5,6], or ceramic [7,8]. Like all composites, MMCs have the potential for unique combinations of properties that can exceed those of their constituent components. Multiple variables influence the properties of MMCs, including composition [9,10], microstructure [11], and processing history [12][13][14][15][16][17][18]. For example, tungsten heavy alloys combine the high density, strength, and thermal stability of tungsten while enhancing ductility through the incorporation of an iron or nickel alloy matrix [19,20].
MMC fabrication usually involves powder consolidation and may be broadly divided into liquid or solid-state processing [21]. Liquid processing includes dispersion of fillers in a liquid matrix phase, infiltration of fiber networks with molten metal, or thermal spray processing. This approach can be used to produce large parts with methods similar to traditional casting and forming. However, it is limited to low melting temperature alloys. Moreover, maintaining uniform composition can be challenging. Finally, constituent reactions, grain coarsening, and oxidation can degrade mechanical properties [22].
Solid state processing, including powder metallurgy (PM) methods, can also be used to produce MMC [23]. This approach can impart greater property uniformity due to better control over powder mixtures prior to fabrication. This approach may be used on materials with very high melting points. Nevertheless, while sintering temperatures are lower than

ECAE
The ECAE process involves extruding a billet-typically with square or circular cross section-through a confined channel with a sharp change in direction between the inlet and exit. Common angles for this direction shift are 90 • and 120 • , however any angle between 90 • and 180 • may be used. As the work piece is forced through the intersecting channels, the material undergoes simple shear, imparting a significant amount of strain. For a 90 • -intersecting angle, the resulting shear strain is approximately 1.16, which is roughly equivalent to a 69% area reduction in conventional extrusion. A detailed review on ECAE may be found in Segal's work [37,38].
Unlike rolling, drawing, or swaging, ECAE may be used to produce a variety of microstructure morphologies and textures by varying the ECAE processing route, i.e., the types and sequence of billet rotations between extrusions. The microstructures that can be produced fall into three categories: lamellar, filamentary, and equiaxed. Repeated extrusions without billet rotation continuously elongate the microstructures along one plane producing lamellar structures [39]. Rotation of the billet by alternating +90 • and −90 • rotations between extrusion passes deforms the microstructure along both the longitudinal and flow planes, elongating structures on two axes producing a fibrous structure, and is referred to as route B [16]. Finally, by rotating the billet so that an initial volume element is restored produces an equiaxed microstructure. Three different routes yield this outcome: C, E, and Bc. Route C is the simplest of these and is accomplished by rotating the billet 180 • between extrusions. Route E builds on route C, by combining two route C extrusions with a 90 • rotation between them. For route Bc, the billet is rotated +90 • between each extrusion, and after 4 extrusions the volume element is restored. For this reason, it is uncommon to see routes with the Bc suffix without a multiple of 4 in front of them, e.g., 4Bc or 8Bc. The ability to control microstructure combined with the large strain space accessible and bulk workpiece dimensions make ECAE an ideal tool for studying the impact of microstructure morphology on the mechanical behavior of MMCs.

Materials and Methods
We have examined the impact of processing route, total strain, and processing temperature on the mechanical behavior of copper (Cu)-tantalum (Ta) blended powder composites. Cu and Ta do not form compounds and have minimal solubility over their entire composition up to the solidus. Their differing crystal structures (Cu is FCC while Ta is BCC) and densities (8.96 g/cm 3 for Cu and 16.65 g/cm 3 for Ta) make them interesting model materials for high strain rate mechanical testing, in particular to study the influence of heterophase interfaces and large elastic impedance mismatch.
The consolidation process is optimized by initially conducting extrusions at ambient temperatures following a variety of routes followed by characterization of the microstructure and mechanical behavior of the consolidated material. Promising routes were selected for processing at 300 • C. Materials consolidated at these elevated temperatures were then mechanically tested in multiple orientations and at different strain rates in order to determine the effectiveness of the processing.
The Cu and Ta powders used in this investigation are pictured in Figure 1. Their size and aspect ratio were found by analyzing scanning electron microscopy (SEM) images with the Fiji ImageJ software [40]. and flow planes, elongating structures on two axes producing a fibrous structure, and is referred to as route B [16].
Finally, by rotating the billet so that an initial volume element is restored produces an equiaxed microstructure. Three different routes yield this outcome: C, E, and Bc. Route C is the simplest of these and is accomplished by rotating the billet 180° between extrusions. Route E builds on route C, by combining two route C extrusions with a 90° rotation between them. For route Bc, the billet is rotated +90° between each extrusion, and after 4 extrusions the volume element is restored. For this reason, it is uncommon to see routes with the Bc suffix without a multiple of 4 in front of them, e.g., 4Bc or 8Bc. The ability to control microstructure combined with the large strain space accessible and bulk workpiece dimensions make ECAE an ideal tool for studying the impact of microstructure morphology on the mechanical behavior of MMCs.

Materials and Methods
We have examined the impact of processing route, total strain, and processing temperature on the mechanical behavior of copper (Cu)-tantalum (Ta) blended powder composites. Cu and Ta do not form compounds and have minimal solubility over their entire composition up to the solidus. Their differing crystal structures (Cu is FCC while Ta is BCC) and densities (8.96 g/cm 3 for Cu and 16.65 g/cm 3 for Ta) make them interesting model materials for high strain rate mechanical testing, in particular to study the influence of heterophase interfaces and large elastic impedance mismatch.
The consolidation process is optimized by initially conducting extrusions at ambient temperatures following a variety of routes followed by characterization of the microstructure and mechanical behavior of the consolidated material. Promising routes were selected for processing at 300 °C. Materials consolidated at these elevated temperatures were then mechanically tested in multiple orientations and at different strain rates in order to determine the effectiveness of the processing.
The Cu and Ta powders used in this investigation are pictured in Figure 1. Their size and aspect ratio were found by analyzing scanning electron microscopy (SEM) images with the Fiji ImageJ software [40]. The Cu powder was sourced from Alfa Aesar (Haverhill, MA, USA). It is spherical with an average diameter of 126 μm ± 15 μm and an aspect ratio of 1.2 ± 0.2. Ta powder was provided by H.C. Stark (Goslar, DEU) and is HRC grade capacitor powder. The particles possess an average diameter of 153 μm ± 47 μm and aspect ratio of 1.8 ± 0.6. Cans The Cu powder was sourced from Alfa Aesar (Haverhill, MA, USA). It is spherical with an average diameter of 126 µm ± 15 µm and an aspect ratio of 1.2 ± 0.2. Ta powder was provided by H.C. Stark (Goslar, DEU) and is HRC grade capacitor powder. The particles possess an average diameter of 153 µm ± 47 µm and aspect ratio of 1.8 ± 0.6. Cans used for extrusion were made of 304 stainless steel. Each can was approximately 178 mm long, with a cross section of 25 mm × 25 mm and included a circular center cavity Powders were combined in a 1:1 ratio by volume, equivalent to a mass ratio of 1:1.86. The powder mixture was then sealed inside a plastic wide-mouth Nalgene bottle. The Nalgene bottle was removed from the glove box and agitated inside a Turbula T2F Powder Mixer Shaker (WAB US Corp., Allendale, NJ, USA) for 20 min. Mixed powders were added to the cans inside the glove box and a metal plug inserted and sealed with black electrical tape. Prior to extrusion, cans were pre-compacted and sealed with a manually operated hydraulic press in order to minimize oxidation. Graphite sheet was wrapped around the cans to reduce friction during ECAE.
The cans were extruded using a 25.4 mm 2 square cross section, sliding wall, zero degree fan angle ECAE tool at approximately 10 mm/s. For processing at elevated temperatures, the ECAE tool was pre-heated to the desired temperature. Billets were placed into the tool pre-upset to ensure good contact with the channel walls and to maintain the seal between the plug and can wall. They were allowed to reach thermal equilibrium with the tool for 30 min before extrusion.
Mechanical properties were obtained through uniaxial compression testing at a quasistatic strain rate of 10 −3 /s. Samples were prepared by sectioning with a silicon carbide cutting saw and mechanically polished down to 800-grit using silicon carbide polishing pads. The samples processed at ambient temperature measured 3 × 3 × 6 mm 3 while those processed at elevated temperature measured 4 × 4 × 8 mm 3 . The length-to-width ratios of these samples are small enough to ensure that buckling is not a concern for these compression tests. The load frame used during testing has high compliance. Therefore, our stress-strain curves do not permit the reliable determination of elastic moduli.
During testing, samples were placed between tungsten carbide platens affixed to the load frame. Graphite sheet was used as a lubricant between the sample and the platens. Strain was measured at the tungsten carbide platens by an MTS model 632.53E-14 extensometer (MTS, Eden Prairie, MN, USA) with a gauge length of 12.7 mm. The platen/graphite sheet/sample/graphite sheet/platen stack nevertheless appears to have significant compliance (as evidenced in the different loading/unloading moduli shown in Supplementary  Table S1), so we do not believe our stress-strain curves permit reliable determination of elastic moduli. Material processed at elevated temperature was tested along the three primary extrusion orientations: longitudinal, extrusion, and flow directions. Two additional strain rates-10 −2 /s and 10 −1 /s-were investigated for the high temperature material along the extrusion direction. Material quantity limitations permitted a limited number of these additional tests. Compression testing was halted when either the load frame reached its safe limit, the load on the samples dropped, or deflection of the sample reached a critical state which might harm the test frame or extensometer.
Material microstructure was characterized using optical microscopy and SEM. Samples were hand polished with silicon carbide pads to 800 grit followed by polishing on a felt pad with colloidal silica and finished on a vibratory polisher with colloidal silica.

Room Temperature Processing
The scanning electron micrographs in Figure 2 show materials processed by routes 1A, 2A, 2A × 2A, 2C and 4E at ambient temperature. Ta is the brighter phase. Images are taken along the flow plane of extrusion; the arrow indicates the extrusion direction. Visual inspection suggests that the constituents are well-consolidated, with intimate contact between the Cu and Ta phases and no apparent porosity. Route 1A (top left) produced an elongated microstructure, as anticipated. A small pore can be seen in the copper phase at the interface of the Ta phase which is indicated by an arrow. In the 2A material (top middle), the substantial increase in elongation over the 1A is clearly evident. This outcome is to be expected, as the degree of elongation compounds with each route A type extrusion.
Metals 2021, 11, x FOR PEER REVIEW 5 of 13 elongated microstructure, as anticipated. A small pore can be seen in the copper phase at the interface of the Ta phase which is indicated by an arrow. In the 2A material (top middle), the substantial increase in elongation over the 1A is clearly evident. This outcome is to be expected, as the degree of elongation compounds with each route A type extrusion. Route 2A×2A is an experimental extrusion route where, after two route A extrusions, the billet was rotated 180° and extruded two more times by route A, thereby returning the deformed volume element to its original shape. This was done with the intent of producing the maximum amount of diffusion bonding between the Cu and Ta phases by maximizing their contact area while still arriving at an equiaxed microstructure at the end of processing. However, the intended effect was not achieved. As can be seen from the micrograph labeled 2A×2A (top right), the material components folded, instead of returning to their original shapes. This folding may have begun by shear localization or kinking of the layered morphology in 2A. A pore is noted by an arrow in this material.
Deformation caused by shear localization may be seen in the micrograph of the sample processed by route 2C (bottom left), and indicated by arrows, where the Ta layer has been drawn out at an angle from the extrusion direction. Route 4E (bottom right), which involves a 2C extrusion followed by a 90° rotation and then another 2C extrusion, has the most equiaxed structure. The same type of shear localization that occurred in the 2C sample is not observed in the 4E material. This is unexpected as both entail the same 2C processing steps. However, as Figure 2 only shows a limited sample area, we cannot exclude the possibility of folded phase morphologies in other parts of the 4E sample. Route 2A×2A is an experimental extrusion route where, after two route A extrusions, the billet was rotated 180 • and extruded two more times by route A, thereby returning the deformed volume element to its original shape. This was done with the intent of producing the maximum amount of diffusion bonding between the Cu and Ta phases by maximizing their contact area while still arriving at an equiaxed microstructure at the end of processing. However, the intended effect was not achieved. As can be seen from the micrograph labeled 2A×2A (top right), the material components folded, instead of returning to their original shapes. This folding may have begun by shear localization or kinking of the layered morphology in 2A. A pore is noted by an arrow in this material.
Deformation caused by shear localization may be seen in the micrograph of the sample processed by route 2C (bottom left), and indicated by arrows, where the Ta layer has been drawn out at an angle from the extrusion direction. Route 4E (bottom right), which involves a 2C extrusion followed by a 90 • rotation and then another 2C extrusion, has the most equiaxed structure. The same type of shear localization that occurred in the 2C sample is not observed in the 4E material. This is unexpected as both entail the same 2C processing steps. However, as Figure 2 only shows a limited sample area, we cannot exclude the possibility of folded phase morphologies in other parts of the 4E sample.
A summary of the results obtained from the ambient temperature extruded samples is shown in Table 1, which includes the accumulated strain, the Vickers hardness measured with a 300 g load, the area fraction of the Cu phase, and the Cu-Ta interface trace length per unit area of the section. The values following the plus/minus (±) sign are the standard deviations of the measured value. Vickers hardness values increase with the amount of strain, consistent with an increase in dislocation density and refinement of grains. These processes typically occur in cold worked material and have been observed in both pure Cu [41] and Ta [29] processed by ECAE. The area fraction of Cu area nominally ought to be 50% in all samples, since all were prepared from 50% Cu powder, by volume. Deviations from this expected value may be attributed to a several possible sources. Powders may have segregated somewhat while samples were prepared, transferred, or extruded creating a non-uniform distribution of the Cu and Ta. ECAE processing may have induced an anisotropic phase distribution, resulting in an observed area fraction that depends on sectioning plane. This conclusion is consistent with the 4E sample, which has the most equiaxed microstructure but a Cu area greater than 50%. The interface trace length per unit area was determined using the ImageJ software. The substantial differences in this quantity from sample to sample are due to the differing aspect ratios of the constituent phases.

Mechanical Behavior
The mechanical response of the room temperature processed composites was evaluated by quasi-static (10 −3 /s) compression testing. Characteristic experimental stress-strain curves for each test condition are shown in Figure 3. The curves presented are representative of the individual cases and were selected to illustrate the differences in mechanical behavior of each processing condition. Two sets of compression tests were conducted; the first was under monotonic loading, displayed in Figure 3, and the second with periodic unloads. For most samples, 1A, 2A, 2A×2A and 2C, a pronounced load drop occurred before unloading could be applied, or shortly thereafter. material. Moreover, while both of these materials were initially expected to have similar phase morphology, Figure 2 shows that they do not. Their comparable behavior may be the outcome of similar pre-existing flaw distributions. Processing by route 2A appears to be the least successful at consolidation, as evidenced by this material's early deviation from elastic behavior and low ultimate stress and strain.

Microstructure
Based on the initial stress-strain data, route 4E was selected for further investigation in elevated temperature (300 °C) consolidation. We also conducted elevated temperature processing by route 4Bc as it gives rise to similar volume element deformation as route 4E: both routes produce an equiaxed final microstructure as the initial volume element is restored. The difference between these routes is related to the order of billet rotation between extrusion passes. In route 4E the volume element is returned to its initial condition in the second and fourth passes with a 90° rotation between the second and third, while in route 4Bc the volume element is only restored upon the fourth extrusion. Thus, route Most of the samples exhibited a sharp decline in load near the elastic limit. During testing, samples did not barrel but instead tended to shear, resulting in a lateral deflection of the top and bottom surfaces of the compression sample, which in turn put lateral stress on the load frame. When this occurred, testing was halted in order to minimize any risk of damaging the load frame. Samples did not fracture in these tests. Rather, they appeared to shear, sometimes fissures appeared, but the samples always remained intact such that no fracture surfaces were available for inspection. The material processed by route 4E deformed well beyond the elastic limit and work-hardened prior to exhibiting a load drop. We conclude that this processing route was the most successful at producing a well-bonded composite. All associated stress-strain curves pertaining to this work are included in the Supplementary Information.
The 2A×2A and 2C materials have similar strains and stresses beyond the elastic limit. This finding is unexpected as the 2A×2A material has twice the working of the 2C material. Moreover, while both of these materials were initially expected to have similar phase morphology, Figure 2 shows that they do not. Their comparable behavior may be the outcome of similar pre-existing flaw distributions. Processing by route 2A appears to be the least successful at consolidation, as evidenced by this material's early deviation from elastic behavior and low ultimate stress and strain.

Microstructure
Based on the initial stress-strain data, route 4E was selected for further investigation in elevated temperature (300 • C) consolidation. We also conducted elevated temperature processing by route 4Bc as it gives rise to similar volume element deformation as route 4E: both routes produce an equiaxed final microstructure as the initial volume element is restored. The difference between these routes is related to the order of billet rotation between extrusion passes. In route 4E the volume element is returned to its initial condition in the second and fourth passes with a 90 • rotation between the second and third, while in route 4Bc the volume element is only restored upon the fourth extrusion. Thus, route 4Bc is expected to impose greater elongation of the particles between the first and second extrusions, increasing the amount of particle-particle bonding.
Composite images of microstructures along the flow, longitudinal, and extrusion planes for both processing routes are shown in Figure 4. Cu is the darker phase. Table 2 summarizes the Cu area fraction as well as the interface trace length per unit area for both samples. The marked differences in Cu area fraction on the different sectioning planes suggest that the anisotropy of the composite structure is the likely cause of variations in these quantities reported in Table 1 for the samples processed at ambient temperature. The difference in interface trace length for 4Bc indicates a greater Cu-Ta interface area and improved bonding between phases.

Mechanical Behavior
Compression stress-strain curves for route 4E and 4Bc materials processed at 300 °C are shown in Figure 5. For comparison, the stress-strain curve for route 4E consolidation at ambient temperature is also shown. Both 300 °C materials exhibit comparable mechanical response. They are more ductile than the ambient temperature processed material, as neither exhibited a load drop in the test range. Their yield stresses are nearly the same. However, the 4Bc material appears to undergo more strain hardening than the 4E material. By contrast, the ambient temperature processed material is approximately 20% stronger than both samples processed at 300 °C. This difference may be due to greater recovery of dislocation densities in the Cu phase of the composites processed at elevated temperature.
Mechanical anisotropy in the 300 °C-processed materials was investigated by conducting quasistatic (10 −3 /s) compression tests in the three orthogonal ECAE directions: longitudinal (LD), extrusion (ED) and flow (FD), as shown in Figure 4. Stress-strain curves for the 4E and 4Bc 300 °C tests are shown in Figure 6 (a,b). Both materials are plastically isotropic, to a good approximation. The largest deviation in isotropy occurs for deformation of the route 4E material along the extrusion direction (ED). The greater anisotropy in 4Bc material may be due to the increase in phase interface area noted in Table 2. This greater interface area likely results in improved bonding, and a more homogenous mechanical response and may also increase strength.

Mechanical Behavior
Compression stress-strain curves for route 4E and 4Bc materials processed at 300 • C are shown in Figure 5. For comparison, the stress-strain curve for route 4E consolidation at ambient temperature is also shown. Both 300 • C materials exhibit comparable mechanical response. They are more ductile than the ambient temperature processed material, as neither exhibited a load drop in the test range. Their yield stresses are nearly the same. However, the 4Bc material appears to undergo more strain hardening than the 4E material. By contrast, the ambient temperature processed material is approximately 20% stronger than both samples processed at 300 • C. This difference may be due to greater recovery of dislocation densities in the Cu phase of the composites processed at elevated temperature. Mechanical anisotropy in the 300 • C-processed materials was investigated by conducting quasistatic (10 −3 /s) compression tests in the three orthogonal ECAE directions: longitudinal (LD), extrusion (ED) and flow (FD), as shown in Figure 4. Stress-strain curves for the 4E and 4Bc 300 • C tests are shown in Figure 6a,b. Both materials are plastically isotropic, to a good approximation. The largest deviation in isotropy occurs for deformation of the route 4E material along the extrusion direction (ED). The greater anisotropy in 4Bc material may be due to the increase in phase interface area noted in Table 2. This greater interface area likely results in improved bonding, and a more homogenous mechanical response and may also increase strength. To assess strain rate sensitivity, the 300 °C -processed composites were further tested under two additional strain rates along the extrusion direction (ED): 10 −2 /s and 10 −1 /s. Corresponding stress-strain curves are shown in Figure 7. A summary of the results for all testing directions and strain rates is shown in Table 3. The strain rate sensitivity exponent To assess strain rate sensitivity, the 300 • C -processed composites were further tested under two additional strain rates along the extrusion direction (ED): 10 −2 /s and 10 −1 /s. Corresponding stress-strain curves are shown in Figure 7. A summary of the results for all testing directions and strain rates is shown in Table 3. The strain rate sensitivity exponent m was calculated by determining the slope of the log-log plot of strain rate vs. stress at stains at 5% and 10%. For the 4E material the strain rate sensitivity exponent m is 0.0115 ± 0.01 at 5%, and 0.016 ± 0.001 at 10% strain, while for the 4Bc material, m is 0.0121 ± 0.012 at 5% and 0.012 ± 0.006 at 10% strain.
Metals 2021, 11, x FOR PEER REVIEW 10 of 13 m was calculated by determining the slope of the log-log plot of strain rate vs. stress at stains at 5% and 10%. For the 4E material the strain rate sensitivity exponent m is 0.0115 ± 0.01 at 5%, and 0.016 ± 0.001 at 10% strain, while for the 4Bc material, m is 0.0121 ± 0.012 at 5% and 0.012 ± 0.006 at 10% strain.

Discussion and Conclusions
We have shown that ECAE processing may be used to consolidate Cu-Ta metal matrix composites from blended powders. ECAE routes that deform the material on multiple planes, such as routes 4E and 4Bc, are most effective for bonding the constituent phases. Elevating the processing temperature from ambient to 300 • C produces a more malleable composite with reduced strength. Increasing the surface area between the Cu and Ta phases appears to increase yield strength while reducing plastic anisotropy and strain rate sensitivity.
Based on our findings, we conclude that the morphology of the composite constituent phases has a significant impact on consolidation and mechanical behavior of the final product. The trace length per phase area indicates strong mechanical interlocking of the Cu-Ta interface. The amount of interlocking appears to be impacted not only by the total strain but also its path during deformation, as is the case when comparing material processing at ambient temperature. The 4E, material being deformed along two separate planes due to the 90 • rotations between extrusions, has rough (longer) Cu-Ta interfaces, mechanically interlocking the phases, as well as improved metallurgical bonds from the disruption of contaminated surfaces. In contrast, material 2A, which had the poorest mechanical behavior, may be well bonded along the single flow plane of extrusion. However, relatively poorer bonding along other planes may cause the constituent phases to buckle and separate from each other upon further deformation, resulting in reduced overall mechanical performance.
While processing routes 4E and 4Bc both restore the shape of the initial volume element, there are nevertheless some differences in their microstructure and mechanical behavior. In particular, route 4Bc results in greater interface trace length per unit section area, as shown in Table 2. This difference may account for improved bonding between the Cu and Ta phases, resulting in higher strength, more isotropic mechanical properties, and reduced sensitivity to strain rate.

Future Work
There are a number of avenues for continued improvement of consolidation by ECAE. Eliminating surface oxides by heating powders in a reducing atmosphere may enhance particle bonding. However, lack of surface oxides may accelerate ambient temperature bonding, thereby making it difficult to disperse the powders uniformly. To circumvent this possibility, methods for removing oxides after powder mixing should be explored.
Other possible routes for enhancing bonding and reducing porosity are pre-consolidation through ball milling, cold isotactic pressing (CIP), or increasing the number of ECAE passes. For instance, since route 4Bc proved effective, ECAE may be performed by route 8Bc, the latter involving double the total number of passes. The additional ECAE passes need not be performed at the same temperature as the initial ones. For example, 4Bc may first be carried out at 300 • C followed by additional passes at room temperature.
The current work focused on Cu-Ta composites with equal phase fractions by volume. Future work may also explore other Cu and Ta proportions. We anticipate that consolidation at high Ta fractions will pose challenges as Ta-Ta bonding may be weaker than the Cu-Cu bonding at any processing temperature. Thus, maintaining a continuous Cu network may be beneficial.
Another avenue of future studies would be to explore combinations of Cu with other BCC metals, including W, Mo, Nb, W, Cr, and V. Since all of these BCC metals have vanishingly low solubility in Cu, we anticipate their bonding behavior to be similar to that of Cu-Ta. Enhanced bonding may be achievable in combinations of metals that are mutually soluble or that react to form intermetallic compounds. Examples include combinations BCC metals with HCP metals, such as Ti or Zr.