Effects of La on Thermal Stability, Phase Formation and Magnetic Properties of Fe–Co–Ni–Si–B–La High Entropy Alloys

: The microstructure, phase formation, thermal stability and soft magnetic properties of melt-spun high entropy alloys (HEAs) Fe 27 Co 27 Ni 27 Si 10 − x B 9 La x with various La substitutions for Si (x = 0, 0.2, 0.4, 0.6, 0.8, and 1) were investigated in this work. The Fe 27 Co 27 Ni 27 Si 10 − x B 9 La 0.6 alloy shows superior soft magnetic properties with low coercivity H c of ~7.1 A/m and high saturation magnetization B s of 1.07 T. The content of La has an important effect on the primary crystallization temperature ( T x1 ) and the secondary crystallization temperature ( T x2 ) of the alloys. After annealing at relatively low temperature, the saturation magnetization of the alloy increases and the microstructure with a small amount of body-centered cubic (BCC) phase embedded in amorphous matrix is observed. Increasing the annealing temperature reduces the magnetization due to the transformation of BCC phase into face-centered cubic (FCC) phase.


Introduction
High entropy alloys (HEAs), defined as the alloys consisting of at least five principal elements without obvious base element, have been proposed by Cantor et al. [1] and Yeh et al. [2] in 2004, independently.Up to now, there are two commonly used definitions of HEAs.One is the composition-based concept, i.e., the alloys composed of five or more principal elements in equal or near equal molar ratio between 5 atom percent (at.%) and 35 atom percent (at.%).The other definition is based on total configurational molar entropy (S mix ).The alloys with S mix < 1 R, 1 R < S mix < 1.5 R, and S mix >1.5 R, where R is the gas constant, are defined as low entropy alloys, medium entropy alloys, and high entropy alloys, respectively [3,4].As a new type of alloys with unique properties of high strength, hardness, corrosion resistance, abrasion resistance and high fatigue resistance, HEAs have received extensive attention.Instead of forming a complex crystal structure, HEAs usually tend to form a solid solution with a face-centered cubic (FCC) or body-centered cubic (BCC) structure, or a mixture thereof [5,6], although a hexagonal close-packed (HCP) structure may be found in a few of HEAs [7].
Studying the compositions, microstructure and their fundamental properties to establish a fundamental database is currently the most essential work for HEAs [8,9].Up to now, a series of HEAs have been prepared, including Fe-based, Co-based [10], Fe-Co-Nibased [11] and rare earth-based high-entropy alloys [12,13].However, most of the previous work focused on their mechanical properties and microstructure [9,14], and their physical properties have not been fully investigated.As Fe, Co and Ni are common constituent elements used in HEAs [15], it is very interesting to explore the magnetic properties of the HEAs.As we know, the soft magnetic materials are developing towards low coercivity (H c ) and high magnetization (M s ), which are essential for promoting the energy conservation efficiency and miniaturization of the electromagnetic device.However, some existing reports on the high-entropy soft magnetic alloys indicate that the saturation induction B s of the HEAs is still low, typically less than 1 T and their crystallization temperature (T x ) is also less than 670 K [16-19], which are both less than what we expected.
On the other hand, the rare earth elements (RE) have been frequently employed in the soft magnetic alloys [20,21], and the results showed that the addition of RE elements such as Gd and Tb can increase the curie temperature [20], and modify the crystallization temperature of the alloy.The addition of RE can also decrease the magnetic permeability.However, the influence of trace rare earth elements on HEAs has rarely been studied.In this work, La is selected to substitute Si for improving the performance of Fe-Co-Ni-Si-B HEAs.La exhibits low solubility with Fe, Co, and Ni elements, and it may play a role of micro-alloying.The thermodynamic properties, glass-forming ability (GFA) and magnetic properties of Fe-Co-Ni-Si-B-La HEAs are studied in detail.

Experimental
The alloy ingots of Fe 27 Co 27 Ni 27 Si 10−x B 9 La x with x = 0, 0.2, 0.4, 0.6, 0.8, and 1 (atomic ratio), denoted as La 0 , La 0.2 , La 0.4 , La 0.6 , La 0.8 , and La 1 , respectively, were prepared by arc-melting pure Fe (99.5 wt.%), Co (99.9 wt.%), Ni (99.96 wt.%), La (99.9 wt.%) metals, FeB (with Fe 83.78 wt.% and B 16.22 wt.%) and Si (99.99 wt.%) crystals under argon atmosphere.The ingots were melted 5 times to ensure chemical homogeneity.The ribbons with width of ~1.2 mm and thickness of ~0.025 mm were prepared by single-roller melt spinning method with the wheel speeds of 45 m/s.The phase structures of the alloys were characterized by X-ray diffraction (XRD) with Cu Kα radiation.Thermal stability was studied by differential scanning calorimetry (DSC) at a heating rate of 10 K/min and under argon atmosphere.The saturation magnetization (B s ) of ribbons were measured under an applied field of 250 kA/m with a vibrating sample magnetometer (VSM).The coercive force (H c ) was measured with a MATS-2010SD hysteresis curve (DC) test system using ribbons about 50 mm in length.

Results and Discussion
It is reported that HEAs trend to form simple fcc and/or bcc solid solution structure or metallic glass.Figure 1 shows the XRD pattern of arc melt Fe 27 Co 27 Ni 27 Si 10−x B 9 La x (x = 0, 0.6, and 1) ingots.In all the ingots, the fcc phase, (FeCoNi) 2 B and Ni 31 Si 12 phases were detected [18,19].
conservation efficiency and miniaturization of the electromagnetic device.However some existing reports on the high-entropy soft magnetic alloys indicate that the saturation induction Bs of the HEAs is still low, typically less than 1 T and their crystallization tem perature (Tx) is also less than 670 K [16 -19], which are both less than what we expected.
On the other hand, the rare earth elements (RE) have been frequently employed in the soft magnetic alloys [20,21], and the results showed that the addition of RE element such as Gd and Tb can increase the curie temperature [20], and modify the crystallization temperature of the alloy.The addition of RE can also decrease the magnetic permeability However, the influence of trace rare earth elements on HEAs has rarely been studied.In this work, La is selected to substitute Si for improving the performance of Fe-Co-Ni-Si-B HEAs.La exhibits low solubility with Fe, Co, and Ni elements, and it may play a role o micro-alloying.The thermodynamic properties, glass-forming ability (GFA) and magnetic properties of Fe-Co-Ni-Si-B-La HEAs are studied in detail.

Results and Discussion
It is reported that HEAs trend to form simple fcc and/or bcc solid solution structure or metallic glass.Figure 1 shows the XRD pattern of arc melt Fe27Co27Ni27Si10−xB9Lax (x = 0 0.6, and 1) ingots.In all the ingots, the fcc phase, (FeCoNi)2B and Ni31Si12 phases were detected [18,19].According to prior research [22], there are many phases in high entropy alloys, including solid solutions, intermetallic compounds, and amorphous phases.The phase evolution in HEAs can be predicted mainly by three parameters, namely atomic size difference Metals 2021, 11, 1907 3 of 8 (∆), mixing enthalpy (∆H mix ), mixing entropy (∆S mix ) and valence electron concentration (VEC) [23,24].The ∆, ∆H mix , ∆S mix , and VEC are defined as: 1) where N is the number of the components in HEAs, R is gas constant, c i is the atomic fraction of i-th component, and − r is the average atomic radius.r i is the atomic radius, which can be obtained from References [15,24].VEC, ∆H mix , and ∆S mix between atomic pairs also be obtained in References [15,24].The values of ∆, ∆H mix , ∆S mix , and VEC for Fe 27 Co 27 Ni 27 Si 10-x B 9 La x alloys are summarized in Table 1.It is clear that all VEC values are near 8.0.Guo et al. [25] pointed out that fcc phase forms in the alloy with VEC ≥ 8.0, bcc phase forms at VEC ≤ 6.87, and a mixture of fcc and bcc phases at 6.87 ≤ VEC ≤ 8.0.Hence, these Fe 27 Co 27 Ni 27 Si 10−x B 9 La x alloys trend to form fcc solid solution and intermetallic compounds.Figure 2a shows the XRD patterns of as-spun Fe 27 Co 27 Ni 27 Si 10−x B 9 La x alloys.Only a broad diffraction peak appears at near 45 • without any detectable crystalline peaks for all alloys, indicating fully amorphous structure.Figure 2b shows the DSC curves of the as-spun Fe 27 Co 27 Ni 27 Si 10−x B 9 La x ribbons.All curves have two distinct exothermic peaks and one endothermic peak, giving two-stage crystallization and melting processes.The glass transition temperature (T g ), phase transition temperature (T p ) [16], liquidus temperature (T l ), primary crystallization temperature (T x1 ), and secondary crystallization temperature (T x2 ) are marked by arrows.As shown in Figure 2b, The T g of amorphous ribbons range from 642 to 694 K.The T x1 and T x2 for the alloys with different La contents are in the region of 707-743 K and 802-839 K, respectively.The T x1 initially increases from 722 to 743 K with increasing La content from 0 to 0.2 at.%, and then decreases to 707 K with increasing La to 1 at.%.The largest T x1 of 743 K is obtained in the alloy with 0.2 at.%La substitution.Similarly, T x2 increase from 802 to 839 K with further increase of La.At 1 at.%La substitution, T x2 reaches the largest value of about 839 K.The value of ∆T x (= T x − T g ) of these alloys are in the region of 43-65 K, and it becomes large as x increases up to 1, which indicates that less than 1 at.%La substitution is beneficial to forming amorphous structure and hindering crystallization process [26].The large ∆T x up to 65 K for Fe 27 Co 27 Ni 27 Si 9 B 9 La 1 alloy shows good thermal stability of the supercooled liquid.In addition, T l of alloys increases from 1318 to 1439 K as x increase from 0 to 0.6 at.%, then decreases to 1324 K with x increases to 1 at.%.The T g , T x , T l , ∆T x , reduced glass transition temperature T rg (= T g /T l ) [27], and S (= ∆T x /(T l − T g ) [28] are listed in Table 2.The S values and T rg values exhibit good correlation with ∆T x , and the largest S value of 0.096 is obtained at x = 1.
that less than 1 at.%La substitution is beneficial to forming amorphous structure and hindering crystallization process [26].The large ΔTx up to 65 K for Fe27Co27Ni27Si9B9La1 alloy shows good thermal stability of the supercooled liquid.In addition, Tl of alloys increases from 1318 to 1439 K as x increase from 0 to 0.6 at.%, then decreases to 1324 K with x increases to 1 at.%.The Tg, Tx, Tl, ΔTx, reduced glass transition temperature Trg (= Tg/Tl) [27], and S (= ΔTx/(Tl − Tg) [28] are listed in Table 2.The S values and Trg values exhibit good correlation with ΔTx, and the largest S value of 0.096 is obtained at x = 1.To further study the crystallization behavior of Fe27Co27Ni27Si10−xB9Lax ribbons with different La contents, the Fe27Co27Ni27Si10−xB9Lax (x = 0, 0.6, 1) ribbons were annealed at different temperatures.Figure 2c shows the XRD patterns of Fe27Co27Ni27Si10−xB9Lax (x = 0,   2c shows the XRD patterns of Fe 27 Co 27 Ni 27 Si 10−x B 9 La x (x = 0, 0.6, 1) alloys after annealing at 853 and 973 K (above T p ) for 5 min.After annealing at 853 K, between T x1 and T x2 , a bcc phase precipitates in the amorphous matrix.With the annealing temperature increased to 973 K, the bcc phase disappeared and fcc crystals formed.The transformation of bcc phase to fcc phase can also be observed in Fe-Co-Ni-Si-B HEAs at high temperature [29].Combined with the DSC analysis results, the first exothermic peak is due to the precipitation of bcc phase and the second peak originates from bcc phase and Ni 31 Si 12 phases, and T p represents the transformation of bcc phase to fcc phase.For the alloy without La-substitution, after annealing at 973 K, a small amount of intermetallic compounds was detected, indexed as Ni 31 Si 12 phase.Previous research has demonstrated that the Ni element is easy to segregate from Fe-rich bcc phases, resulting in the formation of fcc phase, and the over-saturated Si in Ni may form the Ni-Si intermetallic compounds [29,30].However, after La addition, no Ni 31 Si 12 phase was detected in annealed samples.Previous study [29] also showed that in Fe-Co-Ni-Si-B HEAs, Ni 31 Si 12 phase could exist in high temperature.Thus, in the present alloys, the addition of La can suppress the formation of Ni 31 Si 12 phase.Based on above discussion, the phase transition in Fe 27 Co 27 Ni 27 Si 10−x B 9 La x amorphous alloys after annealing occurs through the process of amorphous → amorphous' + bcc phase + Ni 31 Si 12 → fcc phase.
Figure 3a shows the magnetic hysteresis loops (M-H curves) of as-spun Fe 27 Co 27 Ni 27 -Si 10−x B 9 La x (x = 0 to 1) alloys.All alloys show soft magnetic behavior.The saturation magnetization M s of these alloys increases from 0.86 T to 1.01 T as x increases from 0 to 0.4, and then decreases to 0.88 T with x increasing to 1. Figure 3b shows the M-H curves of the Fe 27 Co 27 Ni 27 Si 10−x B 9 La x (x = 0, 0.6, 1) alloys after annealing at 573 K (below glass transition temperature) and 703 K (below crystallization temperature) for 5 min.The saturation magnetization M s increases with the increasing annealing temperature.The M s values of the alloys with x = 0, 0.6 and 1 annealed at 703 K is about 0.96 T, 0.99 T and 0.97 T, respectively.The coercivity H c values were measured as 10.3, 7.1, and 8.5 A/m at 573 K, respectively.As the heat treatment temperature increased to 703 K, the coercivity values were obtained as 18.As the annealing temperature rises above the crystallization temperature, the solid solution phase or other phases precipitate in the alloy.It is important to confirm the influence of the precipitation of the solid solution phase on the soft magnetic properties of HEAs.The magnetization curves of the annealing Fe 27 Co 27 Ni 27 Si 10−x B 9 La x (x = 0, 0.6, and 1) ribbons are shown in Figure 4.After annealing at 853 K, the saturation magnetization of the HEAs ribbons is increased.The M s values of the alloys with x = 0, 0.6 and 1 annealed at 853 K is about 1.05 T, 1.06 T and 1.07 T, respectively.With increasing annealing temperature to 973 K, M s and H c decrease simultaneously.The M s values of the alloys with x = 0, 0.6 and 1 is about 0.93 T, 0.89 T and 1.0 T, respectively.After annealing at higher temperature, the values of M s increased, but the coercivity was deteriorated dramatically.As shown in Figure 5, the coercivity H c , after crystallization annealing is greatly increased.This phenomenon may be related to the fine grains precipitated in the amorphous matrix.Small crystal grains hinder the movement of magnetic domains and play a pinning role.According to the current experimental data, the addition of La element can increase the recrystallization temperature, so an appropriate amount of La can reduce the effect of heat treatment on the reduction of saturation magnetization (sample La 1 have highest B s after annealing at 973 K).At the same time, the coercivity of the alloys with La element after annealing is relatively small.The current results thus show that La element substitution for Si has a great influence on the crystallization temperature of the alloy, and it is interesting that La can inhibit the formation of intermetallic compounds.Furthermore, under the same heat treatment conditions, the saturation magnetization of the strip with a certain La content is higher, while the coercivity is relatively lower.

Conclusions
A new type of soft magnetic Fe27Co27Ni27Si10−xB9Lax HEAs were developed in this work.The effects of La on the phase stability, amorphous forming ability and magnetic properties of Fe-Co-Ni-Si-B HE-MGs were investigated.It was found that the soft magnetic properties of Fe27Co27Ni27Si10−xB9Lax HEAs can be effectively tailored by adjusting their phase structure by annealing treatment.These alloys exhibit a low Hc and a high Bs, in which the values are less than 25 A/m and higher than 1.0 T, respectively.The La con- The current results thus show that La element substitution for Si has a great influence on the crystallization temperature of the alloy, and it is interesting that La can inhibit the formation of intermetallic compounds.Furthermore, under the same heat treatment conditions, the saturation magnetization of the strip with a certain La content is higher, while the coercivity is relatively lower.

Conclusions
A new type of soft magnetic Fe 27 Co 27 Ni 27 Si 10−x B 9 La x HEAs were developed in this work.The effects of La on the phase stability, amorphous forming ability and magnetic properties of Fe-Co-Ni-Si-B HE-MGs were investigated.It was found that the soft magnetic properties of Fe 27 Co 27 Ni 27 Si 10−x B 9 La x HEAs can be effectively tailored by adjusting their phase structure by annealing treatment.These alloys exhibit a low H c and a high B s , in which the values are less than 25 A/m and higher than 1.0 T, respectively.The La content has an important effect on the values of T x1 and T x2 of the alloys.By increasing the annealing temperature, these alloys precipitated the BCC phase at the first crystallization temperature and transformed into the FCC phase at the phase transition temperature.In additionally, La can inhibit the formation of intermetallic compounds at high temperatures.This work suggests that an optimized annealing temperature is required to obtain good combination of the soft magnetic properties for HEAS.

Figure 2 .
Figure 2. (a) XRD patterns of as-spun Fe 27 Co 27 Ni 27 Si 10−x B 9 La x (x = 0 to 1) alloys, (b) DSC curve of as-spun Fe 27 Co 27 Ni 27 Si 10−x B 9 La x alloys, and (c) XRD patterns of amorphous ribbons annealed for 5 min at 853 and 973 K.

Figure 3 .
Figure 3. (a) The M-H curves of as-spun Fe 27 Co 27 Ni 27 Si 10−x B 9 La x (x = 0 to 1) alloys, and (b) the M-H curves of Fe 27 Co 27 Ni 27 Si 10−x B 9 La x (x = 0, 0.6, 1) alloys after heat treatment at different temperatures for 5 min.

Table 2 .
Thermal parameters of Fe 27 Co 27 Ni 27 Si 10−x B 9 La x amorphous ribbons.

Composition (at.%) T g (K) T x1 (K) T x2 (K) ∆T x (K) T l (K) T rg S
Fe 27 Co 27 Ni 27 Si 10 B 9 To further study the crystallization behavior of Fe 27 Co 27 Ni 27 Si 10−x B 9 La x ribbons with different La contents, the Fe 27 Co 27 Ni 27 Si 10−x B 9 La x (x = 0, 0.6, 1) ribbons were annealed at different temperatures.Figure