Numerical Analysis of Serrated Chip Formation Mechanism with Johnson-Cook Parameters in Micro-Cutting of Ti6Al4V

: Previous studies have reported signiﬁcant differences in the Johnson-Cook (J-C) parameters of Ti6Al4V alloy. Thus, various serrated chip morphologies, cutting forces, and cutting temperatures are obtained when different constitutive parameters are used for numerical and simulation analyses, which decreases the reliability of the simulation model. Therefore, it is necessary to investigate and analyze simulation errors due to differences in the J-C parameters. In this study, the mechanism of the serrated chip formation of Ti6Al4V is thoroughly analyzed using the uniformly proportional J-C parameters. The serrated chip sensitivity, shear band spacing, serrated segmentation frequency, chip serration intensity, temperature ﬁeld, strain energy, and cutting force is obtained. This study aims to improve the accuracy and reliability of the micro-cutting simulation models, as well as a reference for the selection of J-C constitutive parameters of simulation with Ti6Al4V manufactured with different heat treatments and additive manufacturing.


Introduction
The development of technology has led to the demand for micro-products in the automotive, aerospace, electronics, medical implants, biomedicine, and robotics industries, among others. Micro-cutting is the key technology to suffice an industry in terms of functionality and size miniaturization [1]. Cheng et al. [2] indicated that the cutting depth is generally less than 200 µm, the processing size of micro turning is less than 100 µm, and the slots of the micro-milling processing width are within 50 µm. Given the exceptional material properties of titanium alloys, Ti6Al4V has been analyzed and applied to micro-cutting in several studies [3,4]. Owing to the low thermal conductivity of Ti6Al4V and relatively slow heat dissipation, it is relatively easy to form adiabatic shear bands and serrated chips in traditional micro-cutting machining [5,6]. Periodically fluctuating cutting forces are generated during the formation of serrated chips, which accelerates tool wear and affects the surface quality of machined parts [7,8]. However, the experimental studies regarding Ti6Al4V processing technology continue to encounter several challenges, including cost and time constraints [9]. Therefore, the finite element numerical analysis method constitutes an imperative method to overcome experimental limitations and better explain the experimental mechanism [10,11].
An accurate cutting simulation model directly determines the accuracy of the formation mechanism of the serrated chips. In any finite element model (F.E.M.), an essential input defines the material properties; it is usually modeled by constitutive equations expressing the stress-strain response along with its dependence on strain rate, temperature, and work hardening [12]. Therefore, an accurate material constitutive corresponds to the key issue for developing an accurate cutting simulation model [13][14][15]. Currently, in the metal cutting simulation process, the Johnson-Cook (J-C) constitutive model is the most where σ, ε, . ε, and . ε p denote the equivalent flow stress, plastic strain, strain rate, and reference strain rate, respectively. Additionally, T, T m , and T r denote the current temperature, melting temperature of the working material, and room temperature, respectively.
The J-C constitutive model is generally obtained by a split Hopkinson pressure bar (SHPB) test, and the experimental configuration allows a strain rate of 0.5-10 4 [23,24], or the J-C constitutive constant is fitted via numerical methods [25]. Zhao et al. [26] obtained the effects of a high strain rate and elevated temperatures on the deformation behavior of laser assisted manufacturing FeCr alloy using the SHPB tests (Split Hopkinson Pressure Bar). Based on the experimental results, the J-C model and modified Johnson-Cook model were established. Zhou et al. [27] investigated the mechanical properties of the titanium alloy Ti6Al4V through the SHPB test and the quasi-static tensile test to determine the parameters for the classical J-C constitutive model. Özel [25] presented a methodology to determine the deformation behavior of working materials under highstrain-rate metal cutting conditions by utilizing evolutionary computational methods to identify constitutive model parameters. The J-C constitutive model is mostly obtained through SHPB experiments; the J-C constitutive parameters for materials of the same composition are similar.
Although several studies regarding the constitutive of J-C materials on titanium alloys through SHPB or other methods have been conducted, the specific constitutive parameter values shown in Table 1 are different. Further analysis indicates that some parameters are significantly different. The maximum initial yield stress A (1098 MPa [10]) increased by 50% compared to the minimum initial yield stress A (742 MPa [28]). The highest strain hardening parameter B (1092 MPa [29]) was 229% larger than the lowest strain hardening parameter B (331.2 MPa [30]). Similarly, the strain rate sensitivity coefficient C, thermal softening coefficient m, and hardening coefficient n differ significantly in various studies. The difference in the J-C constitutive coefficients for the same Ti6Al4V material in various studies is mainly due to the differences in the experimental conditions and methods [31,32].  [32] 881 468 0.122 0.039 0.7 / / Lee et al. [28] 724.7 683.1 0.47 0.035 1.0 10 −5 SHPB Lee et al. [33] 782.7 498.4 0.28 0.028 1.0 10 −5 SHPB Leseur et al. [29] 1098 1092 0.93 0.014 1.1 / SHPB Seo et al. [34] 997.9 653.1 0.45 0.0198 0.7 1 SHPB Khan et al. [35] 1080 1007 0.5975 0.01304 0.7701 1 SHPB Li et al. [15] 968 380 0.421 0.0197 0.577 0.1 SHPB Özel et al. [25] 803 As shown in Table 1, the method to obtain the J-C constitutive constant is different, and the SHPB test corresponds to the mainstream method. For the same SHPB test method, the J-C constitutive constants that are obtained are different due to the various experimental conditions. Varying reference strain rate parameters, strain rate change gradients, and temperature change gradients were used in different studies. The actual stress-strain curves obtained from the tests are slightly different, as well as the J-C constitutive constants. Different J-C constitutive constants of Ti6Al4V were used for cutting simulation in several references [14,41]. Thepsonthi et al. [42] analyzed the two-dimensional elastoplastic viscoplastic finite element simulation of the formation of zigzag chips in the micro-milling of Ti6Al4V titanium alloy; the J-C constitutive constant of Ti6Al4V proposed by Lee et al. [33] was used. Sahoo et al. [43] proposed a hybrid approach for the prediction of cutting forces in the micro end milling of titanium alloy Ti6Al4V by finite element simulation; the J-C constitutive constant of Ti6Al4V proposed by Lee et al. [33] was used. Sun et al. [44] established the one-tool and double-tool cutting models based on the coupling Eulerian-Lagrangian (C.E.L.) finite element (F.E.) method; the J-C constitutive constant of Ti6Al4V proposed by Lee and Lin [29] was used. Bai et al. [45] proposed an analytical model of chip formation for an accurate prediction of the orthogonal cutting of Ti6Al4V; the J-C constitutive constant of Ti6Al4V proposed by Johnson [30] was used. Yadav et al. [46] established the finite element modeling of burr formation in the high-speed micro-milling of Ti6Al4V; the J-C constitutive constant of Ti6Al4V proposed was from Leseur et al. [28].
Moreover, Wan et al. [47] developed an analytical model to predict the position and shape of the dead metal zone in the micro-cutting process; the J-C constitutive constant of Ti6Al4V proposed was from Leseur et al. [28]. Kim [48] developed a predictive cutting force model for the cryogenic machining of Ti6Al4V; this model adopted the J-C constitutive constant proposed by Vyas et al. [39]. Du et al. [49] derived a new analytical formula for the friction coefficient at the tool-chip-workpiece interface. They applied it in the highspeed machining simulation of Ti6Al4V, the J-C constitutive model of Ti6Al4V proposed by Lee [33] was used in the cutting simulation modeling. Banerjee et al. [50] developed an F.E.A. model of the Effect of the minimum quantity lubrication (M.Q.L.) machining process to simulate cutting force and chip formation; the J-C constitutive constant of Ti6Al4V proposed was from Dumitrescu et al. [40]. Thus, different serrated chip morphology, cutting forces, and cutting temperatures are obtained when various constitutive parameters are used for numerical and simulation analyses. Additionally, note that the mechanical properties of additively manufactured (A.M.) Ti6Al4V are entirely different from traditional casting Ti6Al4V [51,52]. This also implies that the J-C constitutive of additively manufactured Ti6Al4V is significantly different from traditional casting. Therefore, the traditional Metals 2021, 11, 102 4 of 23 J-C constitutive parameters used to simulate the additive manufacturing Ti6Al4V process will also reduce the reliability of the results. Therefore, it is necessary to analyze the simulation errors due to differences in the J-C parameters. Yaich et al. [53] presented the influence of constitutive parameters on the simulation results of Ti6Al4V, including J-C constitutive parameters, damage parameters, and damage failure parameters. Wang et al. [54] conducted a shear localization sensitivity analysis for the Johnson-Cook constitutive parameters on serrated chips during the highspeed machining of Ti6Al4V. Gao performed simulations of high-speed machining Ti6Al4V using J-C constitutive methods proposed by Lee et al. [33], Merer et al., Khan et al. [35], and Seo et al. [34]. The results indicated that the parameters of the constitutive model proposed by Seo et al. are more accurate and the cutting force is closer to the real parameters [32]. Calamaz et al. [55] analyzed the influence of the material characteristics (strain softening, thermal softening, etc.) and machining parameters on the cutting forces and chip morphology. Özel et al. [56] performed Simulation of Machining Ti-6Al-4V Titanium Alloy using J-C constitutive methods proposed by Lee et al. [33], Johnson [30], and Leseur et al. [28]. Their research results found that Leseur's model is not found suitable for FE simulations. These do not consider the influence of the J-C constitutive parameters in the micro-cutting process. As the amount of material removal in the micro-cutting process is significantly lesser than that of traditional machining, which leads to the redistribution of thermal softening and hardening effects in the micro-cutting process, the influence of the J-C constitutive parameters on serrated chips is not entirely similar to traditional cutting.
Therefore, the serrated chip formation mechanism using the Johnson-Cook parameters in the micro-cutting of Ti6Al4V is analyzed. Although several studies regarding the experiment and simulation of the serrated formation mechanism of Ti6Al4V have been conducted, a thorough analysis of the J-C constitutive parameters concerning the serrated chip formation mechanism in the micro-cutting of Ti6Al4V is limited. Aiming to reduce the inconsistency between the experimental and cutting simulation results due to varying J-C constitutive parameters, as well as to increase the reliability of the cutting simulation model, the serrated chip formation mechanism with the Johnson-Cook parameters in the micro-cutting of Ti6Al4V are analyzed. Serrated chip sensitivity, shear band spacing, serrated segmentation frequency, chip serrated intensity, temperature field, and cutting force are obtained and analyzed. Further, this study provides guidance to improve the accuracy of cutting simulation models.

Geometric Model of Micro-Cutting
The commercial software, Abaqus/Explicit, was used to establish an orthogonal micro-cutting model to accurately analyze the effect of J-C constitutive parameters on the formation mechanism of Ti6Al4V serrated chips. The model adopts temperaturedisplacement coupling in an eight-node element. Temperature-displacement coupling, a four-node element, was used by the tool model. In general, the cutting tool is rigid due to the significant hardness between the tool and working materials [57]. To balance the accuracy and efficiency of the model, the Lagrangian meshing technique used in micro-cutting models and local mesh refinement is required to reproduce the serrated chip better and decrease calculation time. The workpiece in the micro-cutting model is divided into two parts: the upper part that mainly corresponds to the chip layer and a grid with dimensions of 1 µm × 1 µm × 1 µm. The grid size decreases gradually and increases away from the cutting layer. All material properties of the workpiece are identical. The rake angle of the tool is 10 • , the flank angle is 6 • , and the radius of cutting wedge is 1 µm. The micro-cutting simulation geometry model of Ti6Al4V is shown in Figure 1.
parts: the upper part that mainly corresponds to the chip layer and a grid with dime of 1 μm × 1 μm × 1 μm. The grid size decreases gradually and increases away fro cutting layer. All material properties of the workpiece are identical. The rake angle tool is 10°, the flank angle is 6°, and the radius of cutting wedge is 1 μm. The micro-c simulation geometry model of Ti6Al4V is shown in Figure 1. Boundary constraints correspond to the bottom and sides of the workpiece; the Y directions of the tool are fixed. The degree of freedom in the X-direction of the retained such that the tool can move in the X-direction. Simultaneously, the rake f the tool is defined as the main contact surface, and the workpiece is defined as the contact surface. Therefore, the grid of the rake surface of the tool must exceed the gr of the workpiece. The initial temperature of the entire model is set to 25 °C. Notably pared with traditional machining parameters, the amount of material removal in t cro-cutting process is less, which leads to the redistribution of thermal softening and ening effects in the micro-cutting process, the influence of the J-C constitutive param on serrated chips is not entirely similar to traditional cutting. Although the tool have a certain effect on the results, this article focuses on the analysis of the influe the JC parameters on the constant tool radius. Therefore, the effect of size on the se chip was not considered in the simulation.

Material Model
Considering the micro-cutting simulation modeling of Ti6Al4V, selecting a r material for the constitutive model to evaluate the dynamic mechanical behavior material under different cutting conditions is crucial [58]. An accurate material flow model is necessary to represent the constitutive behavior of the working material high strain rate deformation conditions. Therefore, formulating a material model th truly reflect the stress-strain characteristics and the corresponding relationship be the strain rate strengthening and temperature of the material being processed cons the basis and key to ensure the accuracy of the micro-cutting simulation.
In the micro-cutting simulation model, the J-C constitutive parameters of Ti are shown in Table 1, and their physical and mechanical properties are shown in T The physical and mechanical properties of the tool are listed in Table 3. Boundary constraints correspond to the bottom and sides of the workpiece; the Z and Y directions of the tool are fixed. The degree of freedom in the X-direction of the tool is retained such that the tool can move in the X-direction. Simultaneously, the rake face of the tool is defined as the main contact surface, and the workpiece is defined as the slave contact surface. Therefore, the grid of the rake surface of the tool must exceed the grid size of the workpiece. The initial temperature of the entire model is set to 25 • C. Notably, compared with traditional machining parameters, the amount of material removal in the micro-cutting process is less, which leads to the redistribution of thermal softening and hardening effects in the micro-cutting process, the influence of the J-C constitutive parameters on serrated chips is not entirely similar to traditional cutting. Although the tool radius have a certain effect on the results, this article focuses on the analysis of the influence of the JC parameters on the constant tool radius. Therefore, the effect of size on the serrated chip was not considered in the simulation.

Material Model
Considering the micro-cutting simulation modeling of Ti6Al4V, selecting a reliable material for the constitutive model to evaluate the dynamic mechanical behavior of the material under different cutting conditions is crucial [58]. An accurate material flow stress model is necessary to represent the constitutive behavior of the working material under high strain rate deformation conditions. Therefore, formulating a material model that can truly reflect the stress-strain characteristics and the corresponding relationship between the strain rate strengthening and temperature of the material being processed constitutes the basis and key to ensure the accuracy of the micro-cutting simulation.
In the micro-cutting simulation model, the J-C constitutive parameters of Ti6Al4V are shown in Table 1, and their physical and mechanical properties are shown in Table 2. The physical and mechanical properties of the tool are listed in Table 3. Table 2. Physical and mechanical properties of Ti6Al4V [22,59,60].  In the cutting simulation process of Ti6Al4V, the cutting process undergoes three stages [62]. The first stage is initially linear elastic (a-b), the second stage is plastic yielding with strain hardening (b-c), and the third stage is the material damage evolution stage (c-d). Among the three stages, the J-C constitutive model, which represents the plastic deformation stage of the material, belongs to the second stage. As shown in Figure 2, the solid line l abcd denotes the stress-strain relationship considering material damage and the dashed line l abcd denotes the stress-strain relationship without considering material damage. The strength of the material begins to decrease at the initial critical point c indicating material damage. When it reaches point d, it reaches the fracture quasi-side wherein the material stiffness is completely lost and the material is fractured [63]. The material begins to fail after the plastic strain of the material reaches the initial damage point c. In the Ti6Al4V cutting simulation process, the equivalent plastic strain based on the integral point of the element is used to define the damage parameter J.

Elastic Modulus (GPa) Poisson's Ratio Thermal Conductivity (W/m K)
Specific (J/kg 119,000 534 0. 22 50 400 In the cutting simulation process of Ti6Al4V, the cutting process undergoe stages [62]. The first stage is initially linear elastic (a-b), the second stage is plastic y with strain hardening (b-c), and the third stage is the material damage evolution st d). Among the three stages, the J-C constitutive model, which represents the plastic mation stage of the material, belongs to the second stage. As shown in Figure 2, th line denotes the stress-strain relationship considering material damage a dashed line ′ denotes the stress-strain relationship without considering m damage. The strength of the material begins to decrease at the initial critical point cating material damage. When it reaches point , it reaches the fracture qua wherein the material stiffness is completely lost and the material is fractured [6 material begins to fail after the plastic strain of the material reaches the initial d point . In the Ti6Al4V cutting simulation process, the equivalent plastic strain ba the integral point of the element is used to define the damage parameter . When the damage parameter > 1, the workpiece material is fractured, the lo terial stiffness is completely lost, the element mesh is deleted, and chips begin t The J-C shear failure criterion and shear strain criterion are commonly expressed a tion (2) [64]: where denotes the damage initiation parameter, ∆ ̅ denotes the equivalent strain increment, and ̅ denotes the critical equivalent plastic strain. The specific sion is as Equation (3): When the damage parameter J > 1, the workpiece material is fractured, the local material stiffness is completely lost, the element mesh is deleted, and chips begin to form. The J-C shear failure criterion and shear strain criterion are commonly expressed as Equation (2) [64]: where J denotes the damage initiation parameter, ∆ε denotes the equivalent plastic strain increment, and ε JC denotes the critical equivalent plastic strain. The specific expression is as Equation (3): The ratio of p/σ is defined as the stress triaxiality, D 1 , D 2 , D 3 denotes the damage parameter of the material, . ε denotes the equivalent strain rate, and . ε 0 denotes the reference strain rate. Additionally, T denotes the current temperature, T m denotes the melting temperature of the workpiece material, and T r denotes the room temperature. The J-C damage parameters are listed in Table 4. The stress gradually decreases during the simulated damage evolution stage. The material fails when D = 1 (D ∈ [0, 1]) is the stiffness attenuation factor). The specific stress value is expressed as Equation (4) [65]: The evolution stage of cutting damage involves two main ways, namely damage displacement and fracture energy. The fracture equation for the damage displacement method is expressed as Equation (5): where u p denotes equivalent plastic displacement, u f denotes the equivalent plastic displacement at failure, L denotes the characteristic element length, and ε p denotes the equivalent plastic strain. The equation is as Equation (6): where u −p denotes equivalent plastic displacement, G f denotes the fracture strain energy, K C denotes fracture toughness, v denotes poisson's ratio, and E denotes elastic modulus.

Heat Conduction Model of the Workpiece-Tool
In the micro-cutting process of Ti6Al4V, a large amount of heat is generated during the cutting process, and this causes the tool temperature to increase, and the material to soften. Heat is caused by plastic deformation in the primary deformation zone. It is difficult to transfer heat in a short time, and this increases the temperature of the workpiece and tool and affects the tool life, processed surface, and processing efficiency. The partial differential equation of plane orthogonal cutting heat conduction in the primary deformation zone is expressed as Equation (8) [22]: .
where λ denotes the thermal conductivity coefficient, ρ denotes the material density, C denotes the specific heat of the material, .
Q denotes the heat generation rate per unit volume of mechanical energy converted to thermal energy, x, and y are cartesian coordinates, µ and υ denote the velocity component of the moving heat source in the x and y direction, σ ij denotes the material stress, . ε ij denotes the material strain, and κ denotes the work-heat conversion coefficient.
In the finite element simulation cutting process, κ is typically assumed such that 90% of the plastic deformation can be converted into heat and transferred to the workpiece and tool [61].
The secondary deformation zone is formed since the rake face is affected by chip crushing and friction. The heat generated by the friction increase as the temperature of the chip contact surface and increases the cutting heat generated in the process. It directly affects the wear and service life of the tool. During the micro-cutting process, the friction between the rake face and chips causes severe tool wear. Zorcv [66] proposed a viscous-slip friction model without considering temperature effects in 1963. The model obeys the coulomb's law of friction. The equation is as Equation (10): where µ denotes the coefficient of friction, σ n denotes the positive pressure at the tool-chip interface, and τ max denotes the ultimate shear stress of the material, and the coefficient of The heat in the secondary deformation zone is mainly due to the friction between the rake face and chips. The heat generated by the friction is expressed as Equation (11): where τ f denotes the shear stress between the chip and rake face, and υ f denotes the relative speed between the chip and rake face.

Numerical Results and Analysis
In the process of micro-cutting Ti6Al4V, the most important feature is that serrated chips are formed easily, which directly affects the cutting process. As the formation of serrated chips increases, there is an increase in the frequency and amplitude of the cutting force; the tool is significantly sensitive to distance, wear, and bounces, and the roughness of the machining surface increases. Therefore, it is extremely important to examine the mechanism of serrated chip formation. This section focuses on the formation mechanism of the Ti6Al4V serrated chip, the effect of the J-C constitutive parameters on the morphology mechanism of the serrated chip, and the effect of the J-C damage parameters on the formation mechanism of the serrated chip. The simulation cutting parameters remain identical to analyze the effect of the J-C constitutive parameters on the serrated chips. The cutting speed, cutting depth (t o ), and cutting width (w) correspond to 3 m/s, 20 µm, and 0.2 mm, respectively.

Formation of Serrated Chips
To explain the formation of serrated chips during the micro-cutting process, the distribution of stress and temperature field are used to study the changes of each stage of the detailed serrated chips. Additionally, the stress S 12 and temperature of the serrated formation process were sampled along the shear zone area. Stress S12 refers to the shear stress acting in the Y direction on the Y.Z. plane, which is one of the components of stress [67], allowing the determination of whether the stress in the serrated chip is uniformly distributed. Currently, several studies have emphasized the formation mechanism of serrated chips. Wang et al. [68] indicated that the elastic strain is one of the dominant factors leading to the formation of shear bands, and the onset of the highly localized material softening effects. Vyast et al. [69] proposed the theory of periodic fracture and suggested that the serrated chips are formed by shearing and squeezing. However, Recht and Komanduri [70] indicated that a serrated chip is caused by the softness of the material due to the significant heat generated in the shear zone, and thus proposed the adiabatic shear theory. The representative theories correspond to the adiabatic shear theory. Figure 3 presents the strain of the S 12 rule during the formation of the serrated chips in the micro-cutting of Ti6Al4V. Figure 4 presents the temperature field during the formation of the serrated chips in the micro-cutting of Ti6Al4V. Figures 4a and 5a present the material deformation state of the newly serrated chip when the previous chip is formed, and the deformation of the workpiece due to compressive stress, respectively. Furthermore, S 12 denotes tensile stress, and the temperature in the shear zone is approximately 100-200 • C. When the tool continues moving forward, the workpiece in the contact area that is continuously squeezed by the tool begins to bulge, as shown in Figures 3b and 4b. At this stage, the temperature of the shear zone increases to 500 • C, and the workpiece begins to soften in the shear zone.
surface of the workpiece intensifies, thereby leading to the plastic instability of the wo piece; this phenomenon can be confirmed by Dargusch [71]. The free surface of the rated chip is formed, and the adiabatic shear zone becomes more pronounced. Thi mainly due to the plastic deformation in the primary deformation zone, which gener a significant amount of heat. Thus, the temperature goes up to 600 °C and results in t mal softening of the material in the adiabatic shear zone (A.S.B.), thereby rapidly decr ing the shear resistance. At the end of this phase, S12 continues to increase and is confi to a relatively narrow area. When the micro-cutting process reaches the states in Fig  3d and 4d, the expanded material continues to squeeze and narrows when the comp sive stress S12 decreases, where the adiabatic shear zone reaches the highest temperat which exceeds 700 °C. The serrated chip gradually starts to form from the back surfac   Figure 5a presents the stress S12 sampled along the path of the shear zone (pat path 2, path 3, and path 4). The compressive stress S12 (+) apparently decreases with formation of the serrated chips, thereby indicating that the micro-crack tendency occ at the stage where the serrated morphology is formed. Figure 5b presents the temperat along the path of the shear zone (path 1, path 2, path 3, and path 4). As clearly show As shown in Figures 3c and 4c, the stress concentration in the bulging area of the surface of the workpiece intensifies, thereby leading to the plastic instability of the workpiece; this phenomenon can be confirmed by Dargusch [71]. The free surface of the serrated chip is formed, and the adiabatic shear zone becomes more pronounced. This is mainly due to the plastic deformation in the primary deformation zone, which generates a significant amount of heat. Thus, the temperature goes up to 600 °C and results in thermal softening of the material in the adiabatic shear zone (A.S.B.), thereby rapidly decreasing the shear resistance. At the end of this phase, S12 continues to increase and is confined to a relatively narrow area. When the micro-cutting process reaches the states in Figure  3d and 4d, the expanded material continues to squeeze and narrows when the compressive stress S12 decreases, where the adiabatic shear zone reaches the highest temperature which exceeds 700 °C. The serrated chip gradually starts to form from the back surface.   Figure 5a presents the stress S12 sampled along the path of the shear zone (path 1 path 2, path 3, and path 4). The compressive stress S12 (+) apparently decreases with the formation of the serrated chips, thereby indicating that the micro-crack tendency occurs at the stage where the serrated morphology is formed. Figure 5b presents the temperature along the path of the shear zone (path 1, path 2, path 3, and path 4). As clearly shown in The temperature is also observed to gradually increase as it moves along the path of the shear zone, which indicates that the temperature of the secondary deformation zone exceeds the temperature of the primary deformation zone. This viewpoint is provided in a previous study by Liu [72]; it also indicates that the cutting simulation model is reliable.

Analysis of J-C Constitutive Parameters on Chip Morphology
To reveal the dependence of J-C parameters on serrated chip morphology, J-C constitutive models with different gradients were designed. The J-C constitutive parameters proposed by Seo et al. [34] are as original parameters, and the original J-C constitutive parameters are listed in Table 1. The gradients are obtained as −10%, −20%, −30, +10%, As shown in Figures 3c and 4c, the stress concentration in the bulging area of the surface of the workpiece intensifies, thereby leading to the plastic instability of the workpiece; this phenomenon can be confirmed by Dargusch [71]. The free surface of the serrated chip is formed, and the adiabatic shear zone becomes more pronounced. This is mainly due to the plastic deformation in the primary deformation zone, which generates a significant amount of heat. Thus, the temperature goes up to 600 • C and results in thermal softening of the material in the adiabatic shear zone (A.S.B.), thereby rapidly decreasing the shear resistance. At the end of this phase, S 12 continues to increase and is confined to a relatively narrow area. When the micro-cutting process reaches the states in Figures 3d and 4d, the expanded material continues to squeeze and narrows when the compressive stress S 12 decreases, where the adiabatic shear zone reaches the highest temperature, which exceeds 700 • C. The serrated chip gradually starts to form from the back surface. Figure 5a presents the stress S 12 sampled along the path of the shear zone (path 1, path 2, path 3, and path 4). The compressive stress S 12 (+) apparently decreases with the formation of the serrated chips, thereby indicating that the micro-crack tendency occurs at the stage where the serrated morphology is formed. Figure 5b presents the temperature along the path of the shear zone (path 1, path 2, path 3, and path 4). As clearly shown in the figure, the temperature in the shear zone increases with the formation of the serrated chips. The temperature is also observed to gradually increase as it moves along the path of the shear zone, which indicates that the temperature of the secondary deformation zone exceeds the temperature of the primary deformation zone. This viewpoint is provided in a previous study by Liu [72]; it also indicates that the cutting simulation model is reliable.

Analysis of J-C Constitutive Parameters on Chip Morphology
To reveal the dependence of J-C parameters on serrated chip morphology, J-C constitutive models with different gradients were designed. The J-C constitutive parameters proposed by Seo et al. [34] are as original parameters, and the original J-C constitutive parameters are listed in Table 1. The gradients are obtained as −10%, −20%, −30, +10%, +20%, and +30% of the original parameter values. The variation of Johnson-Cook constitutive parameters for Ti6Al4V is shown in Table 5. The cutting speed, depth, and width correspond to 3 m/s, 20 µm, and 0.2 mm, respectively.  Schulz [73] proposed a coefficient to express the degree of the serrated chip G s . In the study, to compare the effect of different constitutive parameters on the serrated chip, the sensitivity coefficient S i is expressed as follows: where H denotes the height of the tooth top of the serrated chip and h denotes the root height of the serrated chip. Figure 6 presents the distribution of equivalent plastic strain (PEEQ) of the serrated chip of Ti6Al4V under different J-C constitutive model parameters. The Ti6Al4V chip apparently exhibits significant differences when various J-C constitutive parameters are changed under the same cutting parameters. When the strain rate sensitivity coefficient C increased from −30% to +30%, the chip morphology changed from band chips to serrated chips, and the serrated sensitivity parameter S i gradually increased from a negative to a positive value. Thus, when the initial yield stress A gradually increases, more energy is required when the same plastic deformation occurs. In the primary deformation area of the chip, the heat converted by plastic deformation increases, making the degree of jaggedness more apparent, further confirming the indications by Wang et al. [54]. However, the micro-cutting simulation of the study indicates that the hardening modulus B is not similar to that described by Wang et al. As shown in Figure 6, the serrated sensitivity coefficient increases with increasing strain rate sensitivity coefficient C, which indicates the effect is the same as the initial yield stress A.
where denotes the height of the tooth top of the serrated chip and ℎ denotes the root height of the serrated chip. Figure 6 presents the distribution of equivalent plastic strain (PEEQ) of the serrated chip of Ti6Al4V under different J-C constitutive model parameters. The Ti6Al4V chip apparently exhibits significant differences when various J-C constitutive parameters are changed under the same cutting parameters. When the strain rate sensitivity coefficient C increased from −30% to +30%, the chip morphology changed from band chips to serrated chips, and the serrated sensitivity parameter gradually increased from a negative to a positive value. Thus, when the initial yield stress A gradually increases, more energy is required when the same plastic deformation occurs. In the primary deformation area of the chip, the heat converted by plastic deformation increases, making the degree of jaggedness more apparent, further confirming the indications by Wang et al. [54]. However, the micro-cutting simulation of the study indicates that the hardening modulus B is not similar to that described by Wang et al. As shown in Figure 6, the serrated sensitivity coefficient increases with increasing strain rate sensitivity coefficient C, which indicates the effect is the same as the initial yield stress A.   Figure 7, the initial yield stress A and the thermal softening coe m have the greatest effect on the sensitivity coefficient of the serrated chip. When th yield stress A decreases from −30 to +30% based on the original value, the serrate tivity coefficient increases from −63 to +69%. The thermal softening coefficie within the same range and the serrated chip sensitivity coefficient decreases fr to −17%.   To further examine the frequency of the serrated chip and the chip serration in (C.S.I.) of the titanium alloy Ti6Al4V, an equivalent plastic strain was sampled al middle of the chip. The specific path is shown in Figure 9a with the equivalent Conversely, the serrated sensitivity parameter S i exhibits decrease with increasing hardening modulus B, strain rate dependency coefficient n, and thermal softening coefficient m. When the J-C parameters B, n, and m increase from −30 to +30% of the original parameters, the serrated sensitive parameters S i a decrease from positive to negative values. This result is mainly due to the increase in the J-C parameters (B, n, m), leading to increased hardening capacity of the material. Ultimately, the degree of serrated chips decreases.

As shown in
As shown in Figure 7, the initial yield stress A and the thermal softening coefficient m have the greatest effect on the sensitivity coefficient of the serrated chip. When the initial yield stress A decreases from −30 to +30% based on the original value, the serrated sensitivity coefficient S A increases from −63 to +69%. The thermal softening coefficient m is within the same range and the serrated chip sensitivity coefficient S m decreases from +60 to −17%. Figure 8a presents a micro-cutting simulation model without considering temperature, and Figure 8b presents a micro-cutting simulation model considering the temperature. The constitutive parameters and cutting parameters are identical. The micro-cutting simulation model considering temperature exhibits apparent adiabatic shear bands and serrated chips, while the cutting simulation model that does not consider temperature effects does not exhibit the serrated chips. This further illustrates that the plastic deformation in the shear zone generates a significant amount of heat and the adiabatic shear zone undergoes softening.
Conversely, the serrated sensitivity parameter exhibits decrease with increasi hardening modulus B, strain rate dependency coefficient n, and thermal softening coe cient m. When the J-C parameters B, n, and m increase from −30 to +30% of the origin parameters, the serrated sensitive parameters a decrease from positive to negative v ues. This result is mainly due to the increase in the J-C parameters (B, n, m), leading increased hardening capacity of the material. Ultimately, the degree of serrated chips d creases.
As shown in Figure 7, the initial yield stress A and the thermal softening coefficie m have the greatest effect on the sensitivity coefficient of the serrated chip. When the init yield stress A decreases from −30 to +30% based on the original value, the serrated sen tivity coefficient increases from −63 to +69%. The thermal softening coefficient m within the same range and the serrated chip sensitivity coefficient decreases from + to −17%.   Figure 8b presents a micro-cutting simulation model considering the tempe ture. The constitutive parameters and cutting parameters are identical. The micro-cutti simulation model considering temperature exhibits apparent adiabatic shear bands a serrated chips, while the cutting simulation model that does not consider temperatu effects does not exhibit the serrated chips. This further illustrates that the plastic def mation in the shear zone generates a significant amount of heat and the adiabatic she zone undergoes softening. To further examine the frequency of the serrated chip and the chip serration intens (C.S.I.) of the titanium alloy Ti6Al4V, an equivalent plastic strain was sampled along t middle of the chip. The specific path is shown in Figure 9a with the equivalent plas To further examine the frequency of the serrated chip and the chip serration intensity (C.S.I.) of the titanium alloy Ti6Al4V, an equivalent plastic strain was sampled along the middle of the chip. The specific path is shown in Figure 9a with the equivalent plastic strain curve. In this section, the C.S.I. proposed by Kouadri et al. [53] is used to represent the compression deformation of the serrated chip and is expressed as follows in Equation (14): where ε p.peak denotes the equivalent plastic strain at the top of the tooth and ε p.valley denotes the equivalent plastic strain at the root of the tooth.

= .
where . denotes the equivalent plastic strain at the top of the tooth and notes the equivalent plastic strain at the root of the tooth.
The serrated frequency refers to the number of serrated chip units per u length. Belhadi et al. calculated the serrated frequency by measuring the length of a single serrated chip. The formation of the serrated chips is usually accom the appearance of adiabatic shear bands. Therefore, the peaks of the adiabatic s are used as the dividing line. The expression used to calculate the frequency of t chips is presented by Equation (15) parameters (B, n, m) increase. Am the hardening modulus B exhibits the smallest effect on C.S.I., and the initial y A exhibits the largest effect. When the initial yield stress A increases from −30 of the original parameter, C.S.I. increases from 1.2 to 14, which is a 10.6-fold inc ing to increasing in the initial yield stress A increase the amount of heat gene equivalent plastic stress increases after compression in the shear zone after th tening. Figure 10b indicates that the frequency of the serrated chip increases as th tive parameter (A, C) increases; conversely, it decreases when the constitutive p   parameters (B, n, m) increase. Among them, the hardening modulus B exhibits the smallest effect on C.S.I., and the initial yield stress A exhibits the largest effect. When the initial yield stress A increases from −30% to +30% of the original parameter, C.S.I. increases from 1.2 to 14, which is a 10.6-fold increase. Owing to increasing in the initial yield stress A increase the amount of heat generated, and equivalent plastic stress increases after compression in the shear zone after thermal softening.
1, 11, x FOR PEER REVIEW decrease the C.S.I. to a certain serrated frequency, which is conducive to reducin wear. The dependence of the J-C parameter on the shear field temperature and cuttin is analyzed to further examine the effect of the constitutive parameters of Ti6Al4V formation mechanism of the serrated chip. Figure 11 presents the temperature field primary shear zone under different constitutive parameters. The temperature of t mary shear zone gradually increases when the initial yield stress A, the hardening lus B, the strain rate dependency coefficient C, and the thermal softening coeffic increase from −30 to +30% based on the original value. This is mainly due to the co tive parameter (A, B, C, and m) affecting the strength of the bond inside the materi increasing the energy required for the micro-cutting process, thereby increasin amount of heat in the cutting zone.  Figure 10b indicates that the frequency of the serrated chip increases as the constitutive parameter (A, C) increases; conversely, it decreases when the constitutive parameters (B, n, m) of the material increase. The frequency of the serrated chips is inversely proportional to the C.S.I. The results indicate that the decreases in the serrated frequency result in increased C.S.I. Although the number of serrations per unit length decreases, the damage to a single serration increases damage to the tool. Therefore, it is recommended to decrease the C.S.I. to a certain serrated frequency, which is conducive to reducing tool wear.
The dependence of the J-C parameter on the shear field temperature and cutting force is analyzed to further examine the effect of the constitutive parameters of Ti6Al4V on the formation mechanism of the serrated chip. Figure 11 presents the temperature field in the primary shear zone under different constitutive parameters. The temperature of the primary shear zone gradually increases when the initial yield stress A, the hardening modulus B, the strain rate dependency coefficient C, and the thermal softening coefficient m increase from −30 to +30% based on the original value. This is mainly due to the constitutive parameter (A, B, C, and m) affecting the strength of the bond inside the material and increasing the energy required for the micro-cutting process, thereby increasing the amount of heat in the cutting zone.
Conversely, an increase in the hardening parameter n decreases the temperature in the adiabatic shear zone. The serrated chips become less apparent with a decrease in temperature. This further proves that an increase in the hardening index decreases the serrated sensitivity coefficient. Figure 12a presents the temperature of the chip sampled along the middle of the serrated chip. As shown in Figure 12a, the highest temperature in the second shear zone is due to friction between the tool and chips; thus, a significant amount of heat is generated on the rake face. The temperature of the adiabatic shear band (A.S.B.) exceeds the temperature on both sides of the adiabatic shear zone, which is mainly due to the plastic deformation in the adiabatic shear zone and low thermal conductivity of Ti6Al4V. Hence, heat in the shear zone is not transferred.
lus B, the strain rate dependency coefficient C, and the thermal softening coefficie increase from −30 to +30% based on the original value. This is mainly due to the cons tive parameter (A, B, C, and m) affecting the strength of the bond inside the material increasing the energy required for the micro-cutting process, thereby increasing amount of heat in the cutting zone.  Conversely, an increase in the hardening parameter n decreases the temperature in the adiabatic shear zone. The serrated chips become less apparent with a decrease in temperature. This further proves that an increase in the hardening index decreases the serrated sensitivity coefficient. Figure 12a presents the temperature of the chip sampled along the middle of the serrated chip. As shown in Figure 12a, the highest temperature in the second shear zone is due to friction between the tool and chips; thus, a significant amount of heat is generated on the rake face. The temperature of the adiabatic shear band (A.S.B.) exceeds the temperature on both sides of the adiabatic shear zone, which is mainly due to the plastic deformation in the adiabatic shear zone and low thermal conductivity of Ti6Al4V. Hence, heat in the shear zone is not transferred.
As shown in Figure 12b, the temperature of ASB I is the highest, and that of ASB III is the lowest. However, the temperature on both sides of ASB I is the lowest, and the temperature on both sides of ASB III is the highest. When the chips are discharged, the temperature of the adiabatic shear zone gradually passes to both sides, and the temperature difference between the adiabatic shear zone and its sides gradually decreases.  Figure 13 presents the changes in strain energy during the micro-cutting process of Ti6Al4V, where -in Figure 13b corresponds to the strain energy of -in Figure 13a, and ′ -′ in Figure 13b corresponds to the strain energy of ′ -′ in Figure 13a. The crests and troughs of each sawtooth are observed primarily because a significant amount of heat As shown in Figure 12b, the temperature of ASB I is the highest, and that of ASB III is the lowest. However, the temperature on both sides of ASB I is the lowest, and the temperature on both sides of ASB III is the highest. When the chips are discharged, the temperature of the adiabatic shear zone gradually passes to both sides, and the temperature difference between the adiabatic shear zone and its sides gradually decreases. Figure 13 presents the changes in strain energy during the micro-cutting process of Ti6Al4V, where a-i in Figure 13b corresponds to the strain energy of a-i in Figure 13a, and a -i in Figure 13b corresponds to the strain energy of a -i in Figure 13a. The crests and troughs of each sawtooth are observed primarily because a significant amount of heat is generated via plastic deformation in the primary deformation zone during the formation of the serrated chip to form an adiabatic shear zone.  Figure 14a presents the curve of the cutting force during the micro-cutting process of Ti6Al4V. When the first serrated chip starts to form, the cutting force value is relatively high and then gradually decreases. The cutting force decreases to a minimum after the first serrated chip is formed. The subsequent serrated chip then repeats the aforementioned law of cutting force; this phenomenon can be confirmed in a previous study by Wang et al. [67]. The decrease in cutting force is due to the significant heat that is generated by the adiabatic shear zone, which makes the material softer and decreases the cutting force required for the cutting process, thereby resulting in periodic changes in the cutting force. This is because the cutting force changes periodically, and the tool generates a periodic vibration, thereby accelerating tool wear. Figure 14b presents the average cutting force under different J-C constitutive parameters. As shown in the figure, the cutting force corresponding to the initial yield tress A, the hardening modulus B, strain rate sensitivity coefficient C, and thermal softening coefficient m gradually increase when the J-C material constitutive parameter increases from −30% of the original value to +30%. Conversely, the cutting force parameter of the material hardening parameter n decreases. The cutting force trend is consistent with the cutting heat in the shear zone, which indicates that an increase in the cutting force increases the amount of heat released. However, this does not indicate that increases in the amount of heat released promotes sawtooth sensitivity.  Figure 14a presents the curve of the cutting force during the micro-cutting process of Ti6Al4V. When the first serrated chip starts to form, the cutting force value is relatively high and then gradually decreases. The cutting force decreases to a minimum after the first serrated chip is formed. The subsequent serrated chip then repeats the aforementioned law of cutting force; this phenomenon can be confirmed in a previous study by Wang et al. [67]. The decrease in cutting force is due to the significant heat that is generated by the adiabatic shear zone, which makes the material softer and decreases the cutting force required for the cutting process, thereby resulting in periodic changes in the cutting force. This is because the cutting force changes periodically, and the tool generates a periodic vibration, thereby accelerating tool wear. Figure 14b presents the average cutting force under different J-C constitutive parameters. As shown in the figure, the cutting force corresponding to the initial yield tress A, the hardening modulus B, strain rate sensitivity coefficient C, and thermal softening coefficient m gradually increase when the J-C material constitutive parameter increases from −30% of the original value to +30%. Conversely, the cutting force parameter of the material hardening parameter n decreases. The cutting force trend is consistent with the cutting heat in the shear zone, which indicates that an increase in the cutting force increases the amount of heat released. However, this does not indicate that increases in the amount of heat released promotes sawtooth sensitivity. −30% of the original value to +30%. Conversely, the cutting force parameter of the mater hardening parameter n decreases. The cutting force trend is consistent with the cuttin heat in the shear zone, which indicates that an increase in the cutting force increases t amount of heat released. However, this does not indicate that increases in the amount heat released promotes sawtooth sensitivity.

Analysis of J-C Damage Parameters on the Formation of Serrated Chip
The J-C damage parameter is an important factor governing material deformation and failure. To perform a detailed examination of the mechanism of the J-C damage parameters on the formation of serrated chips during the cutting simulation of Ti6Al4V, the Johnson-Cook damage parameter (D 1 , D 2 , D 3 , D 4 , and D 5 ) is increased by +50%, +100%, and decreased by 50% and 100% based on the original parameters. The original J-C damage parameters are listed in Table 4. Figure 15 presents the micro-cutting simulation results of the Ti6Al4V under different J-C damage parameters; the J-C damage parameters apparently affect the serrated chip morphology under different gradient damage models. Specifically, when the D 2 damage parameter increases from −100% to 100% of the original parameter, the serrated chip morphology of Ti6Al4V changes from the sawtooth to band morphology. Figure 16 indicates that the exponent factor D 2 mostly affects the sensitivity of the serrated chip morphology. The serrated chip increases with increases in the D 2 parameter; the sensitivity coefficient increases from −80% to +20%.
Given that D 2 is the factor that maximally affects the sensitivity of the serrated chips, the equivalent plastic strain is sampled along the middle of the serrated chip morphology. As shown in Figure 17, the equivalent plastic strain strength decreases with increases in D 2 . The chip serration intensity C.S.I. corresponds to 1.1 when D 2 increases to 100% of the initial value; the chip serration intensity C.S.I. corresponds to 8 when the material damage parameter D 2 decreases to the original parameter above 50%. The results also indicate that the frequency of the serrated chip segmentation changes significantly. When the material damage parameter D 2 decreases, the peak value of the equivalent plastic strain adjacent to each other gradually increases, and the number of segments decreases. When the material damage parameter D 2 corresponds to −100% of the original parameter, the Ti6Al4V serrated chip division frequency corresponds to 60 unit/mm; the Ti6Al4V serrated chip division frequency corresponds to 35 unit/mm when the material damage parameter D 2 decreases to 100% of the original parameter. Therefore, the material damage parameters cannot be ignored for high-precision micro-cutting simulation models. Figure 15 presents the micro-cutting simulation results of the Ti6Al4V under different J-C damage parameters; the J-C damage parameters apparently affect the serrated chip morphology under different gradient damage models. Specifically, when the D2 damage parameter increases from −100% to 100% of the original parameter, the serrated chip morphology of Ti6Al4V changes from the sawtooth to band morphology. Figure 16 indicates that the exponent factor D2 mostly affects the sensitivity of the serrated chip morphology. The serrated chip increases with increases in the D2 parameter; the sensitivity coefficient increases from −80% to +20%.  Given that D2 is the factor that maximally affects the sensitivity of the serrated chips, the equivalent plastic strain is sampled along the middle of the serrated chip morphology. As shown in Figure 17, the equivalent plastic strain strength decreases with increases in D2. The chip serration intensity C.S.I. corresponds to 1.1 when D2 increases to 100% of the initial value; the chip serration intensity C.S.I. corresponds to 8 when the material damage to each other gradually increases, and the number of segments decreases. When the terial damage parameter D2 corresponds to −100% of the original parameter, the Ti6A serrated chip division frequency corresponds to 60 unit/mm; the Ti6Al4V serrated division frequency corresponds to 35 unit/mm when the material damage paramet decreases to 100% of the original parameter. Therefore, the material damage param cannot be ignored for high-precision micro-cutting simulation models. Figure 17. Comparison of the equivalent plastic strain under different variation of the expone factor D2 (−100%, −50%, +50%, +100%, respectively). Figure 18 presents the temperature value sampled along the middle of the Ti6A serrated chip under different J-C damage parameters. As shown in the figure, the tem atures of the adiabatic shear band I, II, and III exceed the temperatures on both sides temperature from the adiabatic shear band I to III gradually decreases because the c Figure 17. Comparison of the equivalent plastic strain under different variation of the exponent factor D 2 (−100%, −50%, +50%, +100%, respectively). Figure 18 presents the temperature value sampled along the middle of the Ti6Al4V serrated chip under different J-C damage parameters. As shown in the figure, the temperatures of the adiabatic shear band I, II, and III exceed the temperatures on both sides. The temperature from the adiabatic shear band I to III gradually decreases because the chips are no longer deformed by compression. When the material damage parameter D 2 increases from the original parameter to +100%, the temperature region of the serrated chip is stable, and evident wave peaks or valleys are not observed.
Metals 2021, 11, x FOR PEER REVIEW are no longer deformed by compression. When the material damage param creases from the original parameter to +100%, the temperature region of the se is stable, and evident wave peaks or valleys are not observed.  Figure 19 presents the corresponding cutting force under different J-C d rameters. As shown in the figure, the damage parameter exhibits a low effect ting force, and the cutting force changes within 10 N. Specifically, when the cu of the exponent factor D2 increases from −100% to + 100%, the cutting force in 6.7%, and this is within the controllable range. Therefore, the J-C damage par hibits a low effect on the cutting force of the sawtooth although the serrated ch temperature of the shear zone can significantly change.  Figure 19 presents the corresponding cutting force under different J-C damage parameters. As shown in the figure, the damage parameter exhibits a low effect on the cutting force, and the cutting force changes within 10 N. Specifically, when the cutting force of the exponent factor D 2 increases from −100% to + 100%, the cutting force increases by 6.7%, and this is within the controllable range. Therefore, the J-C damage parameter exhibits a low effect on the cutting force of the sawtooth although the serrated chip and the temperature of the shear zone can significantly change.
rameters. As shown in the figure, the damage parameter exhibits a low effect on ting force, and the cutting force changes within 10 N. Specifically, when the cutti of the exponent factor D2 increases from −100% to + 100%, the cutting force incre 6.7%, and this is within the controllable range. Therefore, the J-C damage param hibits a low effect on the cutting force of the sawtooth although the serrated chip temperature of the shear zone can significantly change.

Conclusions
This study mainly analyzed the dependence of J-C parameters on the fo mechanism of serrated chips. The J-C parameters of Ti6Al4V reported in previous differ significantly, which decreases the reliability of the cutting simulation. It also to improve the accuracy of cutting simulation models, as well as a reference for th tion of J-C constitutive parameters of simulation with Ti6Al4V manufactured wit ent heat treatments and additive manufacturing. The following conclusions were 1. Based on Abaqus/Explicit, a Ti6Al4V micro-cutting simulation model wa lished, the formation process of Ti6Al4V serrated chips was analyzed in de

Conclusions
This study mainly analyzed the dependence of J-C parameters on the formation mechanism of serrated chips. The J-C parameters of Ti6Al4V reported in previous studies differ significantly, which decreases the reliability of the cutting simulation. It also guides to improve the accuracy of cutting simulation models, as well as a reference for the selection of J-C constitutive parameters of simulation with Ti6Al4V manufactured with different heat treatments and additive manufacturing. The following conclusions were drawn:

1.
Based on Abaqus/Explicit, a Ti6Al4V micro-cutting simulation model was established, the formation process of Ti6Al4V serrated chips was analyzed in detail, and the law of stress S 12 and the temperature field during the formation of Ti6Al4V serrated chip was revealed.

2.
Among material constitutive parameters (i.e., A, B, C, m, and n), initial yield stress A and thermal softening coefficient m exhibited the greatest effect on the sensitivity coefficient of the sawtooth. Serrated segmentation frequency and C.S.I. depend on material constitutive parameters (i.e., A, C, n, and m), while the hardening modulus B can be ignored.

3.
The temperature field and cutting force were positively related to the material constitutive parameters (i.e., A, B, C, and m), and increase with increases in the constitutive parameters while the constitutive parameter n decreases. Simultaneously, it was concluded that the temperature of the first adiabatic shear zone was the highest. 4.
The cutting force value during the micro-cutting process periodically fluctuated with the formation of the sawtooth.

5.
The damage parameters affected serrated chip sensitivity, serrated segmentation frequency, C.S.I., temperature field in the shear zone, and shear band spacing. However, the exponent factor D 2 exhibited the greatest effect.