Numerical Verification of Tests on the Influence of the Imposed Thermal Cycles on the Structure and Properties of the S700MC Heat-Affected Zone

The article presents the results of studies on the influence of simulated thermal cycles parameters on the structure and properties of the heat-affected zone (HAZ) of thermo-mechanically rolled S700MC steel. For this purpose, resistance heating tests of the tested samples were carried out to determine the effect of maximum temperatures of the imposed thermal cycles with different maximum temperatures at a constant cooling time in the temperature range between 800 and 500 °C (t8/5) and to study the influence of changes of this time on the structure and hardness as well as the tensile strength, elongation and toughness of the simulated HAZ in S700MC steel. The results of the tests, were supported by the results of finite element method (FEM) analyses in the VisualWeld (SYSWELD Code) software of the ESI Group. Selected heat distributions during heating, distributions of individual metallurgical phases and hardness were compared with results from real tests. On the basis of the results presented, an attempt was made to explain the decrease in mechanical and plastic properties in the HAZ area caused by the influence of the welding heat cycle.


Introduction
Modern, dynamically developing industry is looking for new construction materials that can meet a set criteria regarding strength, mass, aesthetics and price. The expansion of new low-density materials based on aluminium, magnesium, titanium as well as an increasing share in the market of composite polymer materials has become a significant threat to the production of smelters. Steel mills have had to show significant activity in recent decades to meet market demands. The use of modern metallurgical technologies and metallurgical processing, as well as a new look at the significance and role of alloying elements used in steels, allowed the production of various steel groups with a wide range of mechanical and plastic properties [1][2][3][4][5]. The development of new grades of steel, especially high-strength low-alloy (HSLA) with a ferritic, ferritic-pearlitic, ferritic-bainitic, bainitic or tempered martensite structure, allowed for a significant reduction in the mass of elements and structures manufactured from them. The reduction of sheet thickness produced in thermo-mechanical rolling processes (TMCP) for the needs of the automotive, shipbuilding, oil industry while maintaining all existing operational parameters allows to achieve significant savings resulting from lower expenditure on material processing and lower transport costs. Alternative materials with respect to modern steel grades still have many limitations associated with high manufacturing costs, limited resistance to elevated temperatures and difficult joining processes [5][6][7][8][9][10].
These steels are also used in civil engineering. They have proved particularly useful in the production of the largest suspension bridges in the world, reducing the number of main supports technologies [33,34,36]. The article investigated the influence of thermal cycles that allow obtaining the structure of the heat-affected zone in samples of thermo-mechanically rolled S700MC steel. Tests were carried out for two variants: the use of thermal cycles with a variable maximum temperature value and a constant temperature value of 1250 • C and changing cooling time t 8/5 allowed to obtain information about the nature of the changes occurring in the heat-affected zone of the potential welded joint of this steel; this confirmed the thesis that S700MC steel is highly sensitive to thermal cycles.
In obtaining results with a very high degree of correlation with real, material data at the software's disposal is important. Typically, mechanical properties are defined as functions that depend on temperature and the content of individual phases. In addition to the thermo-mechanical data of the material's, such as thermal conductivity, specific heat/enthalpy, density, Young's modulus, Poisson's ratio, yield strength or strengthening, metallurgical properties are also important. The system takes into account phase changes, kinetics for austenitic transformation during heating (TTA diagram) as well as transformations of ferrite, bainite and martensite during cooling (CCT, TTT diagram), Figure 1. The material bases in the SYSWELD package are constantly expanded with new materials and technologies [33,34,36]. The article investigated the influence of thermal cycles that allow obtaining the structure of the heat-affected zone in samples of thermo-mechanically rolled S700MC steel. Tests were carried out for two variants: the use of thermal cycles with a variable maximum temperature value and a constant temperature value of 1250 °C and changing cooling time t8/5 allowed to obtain information about the nature of the changes occurring in the heat-affected zone of the potential welded joint of this steel; this confirmed the thesis that S700MC steel is highly sensitive to thermal cycles.

Material Used for Research
The studies of the influence of the imposed thermal cycles on the properties and structure of the heat-affected zone of S700MC steel were carried out on 10 × 10 × 55 mm rectangular-shaped samples obtained by means of a standard industrial manufacturing process. Their chemical composition and properties are given in Tables 1 and 2. The S700MC steel is characterized by an unbalanced, fine-grained bainitic-ferritic structure and a relatively low carbon equivalent (at the level of 0.33%) which should indicate its good weldability. The high-strength properties of S700MC steel are ensured by a thermomechanical treatment process combined with the action of alloying micro-additives such as Ti, Nb and, in a small amount, V. The total content of alloying micro-additives was 0.17% by weight which did not exceed the permissible value of 0.22% for steel case with micro-additives.

Material Used for Research
The studies of the influence of the imposed thermal cycles on the properties and structure of the heat-affected zone of S700MC steel were carried out on 10 × 10 × 55 mm rectangular-shaped samples obtained by means of a standard industrial manufacturing process. Their chemical composition and properties are given in Tables 1 and 2.  The S700MC steel is characterized by an unbalanced, fine-grained bainitic-ferritic structure and a relatively low carbon equivalent (at the level of 0.33%) which should indicate its good weldability. The high-strength properties of S700MC steel are ensured by a thermomechanical treatment process combined with the action of alloying micro-additives such as Ti, Nb and, in a small amount, V. The total content of alloying micro-additives was 0.17% by weight which did not exceed the permissible value of 0.22% for steel case with micro-additives.

Assumptions for Testing Structural Changes of S700MC Steel under the Conditions of Simulated Welding Heat Cycles
The tested S700MC steel had a very low carbon concentration (0.056%), which may have affected the reduction of the impact of austenite transformations under the influence of welding thermal cycles on the strength and plastic properties of welded joints ( Table 2). For this purpose, the material database used in the calculations was also modified.
To determine the effect of maximum temperatures of the imposed thermal cycles with constant cooling time t 8/5 (cooling time in the temperature range between 800 and 500 • C) and the effect of cooling time t 8/5 cycle with a maximum temperature of 1250 • C on the structure and hardness of the simulated heat-affected zone of S700MC steel, heating samples were tested using a stand equipped with a resistive heating source and a thermal imaging camera, Figure 2. The samples obtained were subjected to impact tests, hardness measurement and metallographic microscopic tests. Material tensile test was carried out on round samples. during heating, distribution of individual metallurgical phases and hardness were compared with results from real tests.

Testing Equipment
In order to determine the influence of the maximum temperature of the thermal cycle on the properties of individual HAZ areas of the tested steel, tests with the imposed thermal cycles were carried out on a specially constructed test stand, equipped with a resistive heating source, Variocam Head HR (InfraTec GmbH, Dresden, Germany) thermal imaging camera and temperature distribution field recording system with Irbis 3 plus software (InfraTec GmbH, Dresden, Germany), allowing for the control of the camera's parameters and recording thermographic images in external memory.
(a) (b) (c) The thermal imaging camera used had an uncooled matrix of bolometric detectors, enabling the acquisition of thermographic images with a resolution of 640 × 480 pixels and temperature measurement in the range from −40 to 2000 °C. The camera was equipped with a lens with a focal length of f = 50 mm, which at a distance of the lens from the tested sample of 460 mm allowed a field of view of 140 × 110 mm and a spatial resolution of a thermographic image (IFOV) of 0.25 mm ( Figure  2). For temperature measurement, the camera was configured to obtain the lowest possible measurement uncertainty. In addition to environmental parameters, such as ambient temperature and humidity, atmosphere transmittance of 1.0 was adopted and the average emissivity for steel was set at 0.9. The emissivity is a key parameter that determines the accuracy of temperature measurement using a thermographic camera, and it depends on the temperature and surface condition of the observed object. Prior to testing, tests were carried out to determine the emissivity of the samples, which ranged 0.5-0.9 for the observed surface in the temperature range from 100 to 900 °C. During the thermal cycle simulation, the surface properties of the sample changed because of the formation of an oxide layer, which further increased the emissivity value. The results of preliminary simulations of the thermal cycle of test samples confirmed that the adopted emissivity value allows obtaining reliable results burdened with an average relative temperature measurement error not exceeding 10%. The video track ran at a height of 1550 mm. The tests were carried out at an air temperature of 23.7 °C and an air humidity of 65.7%.

Computational Model
To perform numerical analyses in the VisualWeld environment, a three-dimensional discrete As already mentioned, in the first part a simulation of HAZ thermal cycles of S700MC steel was performed with the maximum cycle temperature range from 400 to 1300 • C every 100 • C ( Table 3). The heating time was in the range of 2.3 to 5.6 s. The cooling time t 8/5 thermal cycles with a maximum temperature T max above 800 • C was maintained between 11 and 15 s. This cooling time range resulted from the analysis of the phase transformation studies of austenite in cooling time, i.e., the CCT diagram. In this t 8/5 time range, the S700MC steel was characterized by a bainitic-ferritic structure with a relatively small grain and a hardness similar to that of the initial/base material. During the test, the temperature was recorded as a function of time and the following parameters were determined: T max -maximum cycle temperature; t n -time of sample heating from 50 • C to T max ' t 8 -time after which the temperature decreased to 800 • C; t 5 -time after which the temperature decreased to 500 • C; t 8/5 -sample cooling time in the temperature range 800-500 • C, (Table 3).
In the second stage of research, tests were carried out on simulations of thermal cycles with different cooling times t 8/5 allowing for obtaining a different microstructure in a simulated HAZ, Table 4. The conducted research was also supported by the results of numerical analyses of selected, described cases as, on the one hand, verification of the results obtained and, on the other, an indication of the possibility of a significant reduction in the time spent on work and necessary to perform real tests due to the use of modern computational techniques based on the finite element method in VisualWeld (SYSWELD Code) software from the ESI Group. Selected heat distribution during heating, distribution of individual metallurgical phases and hardness were compared with results from real tests.

Testing Equipment
In order to determine the influence of the maximum temperature of the thermal cycle on the properties of individual HAZ areas of the tested steel, tests with the imposed thermal cycles were carried out on a specially constructed test stand, equipped with a resistive heating source, Variocam Head HR (InfraTec GmbH, Dresden, Germany) thermal imaging camera and temperature distribution field recording system with Irbis 3 plus software (InfraTec GmbH, Dresden, Germany), allowing for the control of the camera's parameters and recording thermographic images in external memory.
The thermal imaging camera used had an uncooled matrix of bolometric detectors, enabling the acquisition of thermographic images with a resolution of 640 × 480 pixels and temperature measurement in the range from −40 to 2000 • C. The camera was equipped with a lens with a focal length of f = 50 mm, which at a distance of the lens from the tested sample of 460 mm allowed a field of view of 140 × 110 mm and a spatial resolution of a thermographic image (IFOV) of 0.25 mm ( Figure 2). For temperature measurement, the camera was configured to obtain the lowest possible measurement uncertainty. In addition to environmental parameters, such as ambient temperature and humidity, atmosphere transmittance of 1.0 was adopted and the average emissivity for steel was set at 0.9. The emissivity is a key parameter that determines the accuracy of temperature measurement using a thermographic camera, and it depends on the temperature and surface condition of the observed object. Prior to testing, tests were carried out to determine the emissivity of the samples, which ranged 0.5-0.9 for the observed surface in the temperature range from 100 to 900 • C. During the thermal cycle simulation, the surface properties of the sample changed because of the formation of an oxide layer, which further increased the emissivity value. The results of preliminary simulations of the thermal cycle of test samples confirmed that the adopted emissivity value allows obtaining reliable results burdened with an average relative temperature measurement error not exceeding 10%. The video track ran at a height of 1550 mm. The tests were carried out at an air temperature of 23.7 • C and an air humidity of 65.7%.

Computational Model
To perform numerical analyses in the VisualWeld environment, a three-dimensional discrete model of a rectangular cuboid with dimensions of 10 × 10 × 55 mm was made, consisting of 6500 SOLID elements and 7986 nodes. The boundary conditions in the model were adopted to faithfully convey heat dissipation to the environment at 20 • C by convection and radiation. Boundary conditions for fixing were determined so that the model could deform freely while being permanently attached at one end ( Figure 3). Since no mechanical analyses were carried out, this is of secondary importance for the presented considerations. To reproduce the behaviour of the material in the conditions of a variable heat cycle, a specially prepared material database was used, containing material data enabling the prediction of metallurgical phase distribution, depending on temperature changes.
Metals 2020, 10, x FOR PEER REVIEW 8 of 24 in the conditions of a variable heat cycle, a specially prepared material database was used, containing material data enabling the prediction of metallurgical phase distribution, depending on temperature changes. The calculations were based on the "transient" technique, and the thermal cycle forcing was applied on selected model nodes as a function of "Imposed Thermal Cycle" [34]. This function allows, instead of the welding heat source model usually used in simulations of welding processes, to set any thermal cycle in the form of temperature value in time ( Figure 4). This cycle can be set both on individual elements and on their group. When using this technique, it is important to correctly map the heating curve and maximum temperature values as well as such selection of boundary conditions related to cooling to obtain simulation results consistent with real ones. In the described case, it is convenient because it is possible to precisely set the heating speed and maximum temperature of the cycle in accordance with the assumptions adopted in the tests.

The Studies of the Influence of the Thermal Cycle Maximum Temperature on the Properties of Simulated HAZ in S700MC Steel
As already mentioned, tests of thermo-mechanically simulated thermal cycles at HAZ were carried out for the cases where the thermal cycle was t8/5 for cycles, the maximum temperature over The calculations were based on the "transient" technique, and the thermal cycle forcing was applied on selected model nodes as a function of "Imposed Thermal Cycle" [34]. This function allows, instead of the welding heat source model usually used in simulations of welding processes, to set any thermal cycle in the form of temperature value in time ( Figure 4). This cycle can be set both on individual elements and on their group. When using this technique, it is important to correctly map the heating curve and maximum temperature values as well as such selection of boundary conditions related to cooling to obtain simulation results consistent with real ones. In the described case, it is convenient because it is possible to precisely set the heating speed and maximum temperature of the cycle in accordance with the assumptions adopted in the tests. in the conditions of a variable heat cycle, a specially prepared material database was used, containing material data enabling the prediction of metallurgical phase distribution, depending on temperature changes. The calculations were based on the "transient" technique, and the thermal cycle forcing was applied on selected model nodes as a function of "Imposed Thermal Cycle" [34]. This function allows, instead of the welding heat source model usually used in simulations of welding processes, to set any thermal cycle in the form of temperature value in time ( Figure 4). This cycle can be set both on individual elements and on their group. When using this technique, it is important to correctly map the heating curve and maximum temperature values as well as such selection of boundary conditions related to cooling to obtain simulation results consistent with real ones. In the described case, it is convenient because it is possible to precisely set the heating speed and maximum temperature of the cycle in accordance with the assumptions adopted in the tests.

The Studies of the Influence of the Thermal Cycle Maximum Temperature on the Properties of Simulated HAZ in S700MC Steel
As already mentioned, tests of thermo-mechanically simulated thermal cycles at HAZ were carried out for the cases where the thermal cycle was t8/5 for cycles, the maximum temperature over

The Studies of the Influence of the Thermal Cycle Maximum Temperature on the Properties of Simulated HAZ in S700MC Steel
As already mentioned, tests of thermo-mechanically simulated thermal cycles at HAZ were carried out for the cases where the thermal cycle was t 8/5 for cycles, the maximum temperature over 800 • C ranged from 11 to 15 s and the heating time to the maximum value was in the range from 2.3 to 5.6 s. The imposed thermal cycles ranged from 400 to 1300 • C every 100 • C. Based on the above recommendations and the measured actual thermal cycles, thermo-metallurgical analyses of the discussed cases were carried out using "reference" set cycle cycles (ITC400 to ITC1300) ( Figure 5, Table 3). The model was calibrated and validated in accordance with the recorded thermographic images, which confirmed the compliance of the proposed calculation method with the actual results obtained during the tests (Figures 6-8).
Metals 2020, 10, x FOR PEER REVIEW 9 of 24 800 °C ranged from 11 to 15 s and the heating time to the maximum value was in the range from 2.3 to 5.6 s. The imposed thermal cycles ranged from 400 to 1300 °C every 100 °C. Based on the above recommendations and the measured actual thermal cycles, thermo-metallurgical analyses of the discussed cases were carried out using "reference" set cycle cycles (ITC400 to ITC1300) ( Figure 5, Table 3). The model was calibrated and validated in accordance with the recorded thermographic images, which confirmed the compliance of the proposed calculation method with the actual results obtained during the tests (Figures 6-8).

Figure 5.
Forcing cycles (ITC) and calculated (STC) inside the heat-affected zone (HAZ) for thermal cycles with the maximum temperature from 400 to 1300 °C (Table 3).
(a) (b) Figure 5. Forcing cycles (ITC) and calculated (STC) inside the heat-affected zone (HAZ) for thermal cycles with the maximum temperature from 400 to 1300 • C (Table 3).
Metals 2020, 10, x FOR PEER REVIEW 9 of 24 800 °C ranged from 11 to 15 s and the heating time to the maximum value was in the range from 2.3 to 5.6 s. The imposed thermal cycles ranged from 400 to 1300 °C every 100 °C. Based on the above recommendations and the measured actual thermal cycles, thermo-metallurgical analyses of the discussed cases were carried out using "reference" set cycle cycles (ITC400 to ITC1300) ( Figure 5, Table 3). The model was calibrated and validated in accordance with the recorded thermographic images, which confirmed the compliance of the proposed calculation method with the actual results obtained during the tests (Figures 6-8).

Figure 5.
Forcing cycles (ITC) and calculated (STC) inside the heat-affected zone (HAZ) for thermal cycles with the maximum temperature from 400 to 1300 °C (Table 3).
(a) (b)   The microscopic metallographic tests of simulated HAZ areas showed that in the maximum cycle temperature range from 400 to 900 °C, the S700MC steel was characterized by a fine-grained bainitic-ferritic structure, which corresponded well with the results obtained by finite element analysis. Above the maximum cycle temperature −900 °C, there was a strong growth of the grain and it went up to 1300 °C. Microscopic studies also revealed the presence of large carbonitrides in the areas of all simulated HAZs, which proves their high thermal stability, Table 5.  The microscopic metallographic tests of simulated HAZ areas showed that in the maximum cycle temperature range from 400 to 900 • C, the S700MC steel was characterized by a fine-grained bainitic-ferritic structure, which corresponded well with the results obtained by finite element analysis. Above the maximum cycle temperature −900 • C, there was a strong growth of the grain and it went up to 1300 • C. Microscopic studies also revealed the presence of large carbonitrides in the areas of all simulated HAZs, which proves their high thermal stability, Table 5.  The microscopic metallographic tests of simulated HAZ areas showed that in the maximum cycle temperature range from 400 to 900 °C, the S700MC steel was characterized by a fine-grained bainitic-ferritic structure, which corresponded well with the results obtained by finite element analysis. Above the maximum cycle temperature −900 °C, there was a strong growth of the grain and it went up to 1300 °C. Microscopic studies also revealed the presence of large carbonitrides in the areas of all simulated HAZs, which proves their high thermal stability, Table 5.  The microscopic metallographic tests of simulated HAZ areas showed that in the maximum cycle temperature range from 400 to 900 °C, the S700MC steel was characterized by a fine-grained bainitic-ferritic structure, which corresponded well with the results obtained by finite element analysis. Above the maximum cycle temperature −900 °C, there was a strong growth of the grain and it went up to 1300 °C. Microscopic studies also revealed the presence of large carbonitrides in the areas of all simulated HAZs, which proves their high thermal stability, Table 5.  The microscopic metallographic tests of simulated HAZ areas showed that in the maximum cycle temperature range from 400 to 900 °C, the S700MC steel was characterized by a fine-grained bainitic-ferritic structure, which corresponded well with the results obtained by finite element analysis. Above the maximum cycle temperature −900 °C, there was a strong growth of the grain and it went up to 1300 °C. Microscopic studies also revealed the presence of large carbonitrides in the areas of all simulated HAZs, which proves their high thermal stability, Table 5.  As a result of numerical analyses, information was also obtained on the distribution of individual metallurgical phases and maximum their contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 9-11, Tables  5 and 6).  As a result of numerical analyses, information was also obtained on the distribution of individual metallurgical phases and maximum their contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 9-11, Tables  5 and 6). As a result of numerical analyses, information was also obtained on the distribution of individual metallurgical phases and maximum their contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 9-11, Tables  5 and 6).  As a result of numerical analyses, information was also obtained on the distribution of individual metallurgical phases and maximum their contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 9-11, Tables  5 and 6).
As a result of numerical analyses, information was also obtained on the distribution of individual metallurgical phases and maximum their contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 9-11, Tables 5 and 6). Tmax = 1000 °C Tmax = 1100 °C Tmax = 1200 °C As a result of numerical analyses, information was also obtained on the distribution of individual metallurgical phases and maximum their contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 9-11, Tables  5 and 6).  (Table 6).  (Table 6).  As a result of numerical analyses, information was also obtained on the distribution of individual metallurgical phases and maximum their contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 9-11, Tables  5 and 6).  (Table 6).  (Table 6).  (Table 6).  (Table 6).
Hardness measurements carried out by the Vickers method at a test load of 1 kg showed in the range from 400 to 900 °C practically small changes and values similar to the hardness of the native material. When the temperature of the maximum heat cycle increased above 900 °C, the material softened to approximately 230 HV1 (Table 6, Figure 12).   (Table 6). Hardness measurements carried out by the Vickers method at a test load of 1 kg showed in the range from 400 to 900 • C practically small changes and values similar to the hardness of the native material. When the temperature of the maximum heat cycle increased above 900 • C, the material softened to approximately 230 HV1 (Table 6, Figure 12).  Based on the metallurgical phase distributions and the calculated cooling times t8/5, VisualWeld (SYSWELD) also allows you to calculate the hardness distribution. The results of selected analyses are presented and compared with the results of real measurements in Figures 12 and 13.

The Studies on the Influence of Stimulated Thermal Cycles with a Maximum Temperature of 1250 °C and Variable Cooling Time t8/5 on the Structure and Properties of HAZ in S700MC Steel
The next stage of the tests were tests with the imposed thermal cycles with cooling times t8/5 successively: 1.82, 3, 5, 10, 15, 30, 60 and 120 s and the maximum temperature of the thermal cycle Tmax = 1250 °C. The proposed cooling time t8/5 corresponded to the characteristic cooling times on the CCT diagram. The microscopic metallographic tests carried out confirmed the compliance of the obtained structures with the structures resulting from the developed CCT diagram. With a short cooling time, below 10 s, a mixture of bainite and low-carbon martensite occurred. The cooling time in the range from 10 to 20 s provides a bainitic-ferritic structure, the closest to the steel structure in the initial state. Further extension of the cooling time leads to an increase in the ferrite content in the structure, above the cooling time of 100 s, the steel had a ferritic-bainitic structure (Table 7). Based on the phase transformation tests of S700MC steel under the conditions of simulated thermal conditions, the CCT diagram with a supplementary graph was determined regarding changes in HV5 hardness as a function of cooling time t8/5 ( Figure 14). The latter is particularly important in the light of the considerations made.

The Studies on the Influence of Stimulated Thermal Cycles with a Maximum Temperature of 1250 • C and Variable Cooling Time t 8/5 on the Structure and Properties of HAZ in S700MC Steel
The next stage of the tests were tests with the imposed thermal cycles with cooling times t 8/5 successively: 1.82, 3, 5, 10, 15, 30, 60 and 120 s and the maximum temperature of the thermal cycle T max = 1250 • C. The proposed cooling time t 8/5 corresponded to the characteristic cooling times on the CCT diagram. The microscopic metallographic tests carried out confirmed the compliance of the obtained structures with the structures resulting from the developed CCT diagram. With a short cooling time, below 10 s, a mixture of bainite and low-carbon martensite occurred. The cooling time in the range from 10 to 20 s provides a bainitic-ferritic structure, the closest to the steel structure in the initial state. Further extension of the cooling time leads to an increase in the ferrite content in the structure, above the cooling time of 100 s, the steel had a ferritic-bainitic structure (Table 7). Based on the phase transformation tests of S700MC steel under the conditions of simulated thermal conditions, the CCT diagram with a supplementary graph was determined regarding changes in HV5 hardness as a function of cooling time t 8/5 (Figure 14). The latter is particularly important in the light of the considerations made. cooling time, below 10 s, a mixture of bainite and low-carbon martensite occurred. The cooling time in the range from 10 to 20 s provides a bainitic-ferritic structure, the closest to the steel structure in the initial state. Further extension of the cooling time leads to an increase in the ferrite content in the structure, above the cooling time of 100 s, the steel had a ferritic-bainitic structure ( Table 7). Based on the phase transformation tests of S700MC steel under the conditions of simulated thermal conditions, the CCT diagram with a supplementary graph was determined regarding changes in HV5 hardness as a function of cooling time t8/5 ( Figure 14). The latter is particularly important in the light of the considerations made. cooling time, below 10 s, a mixture of bainite and low-carbon martensite occurred. The cooling time in the range from 10 to 20 s provides a bainitic-ferritic structure, the closest to the steel structure in the initial state. Further extension of the cooling time leads to an increase in the ferrite content in the structure, above the cooling time of 100 s, the steel had a ferritic-bainitic structure (Table 7). Based on the phase transformation tests of S700MC steel under the conditions of simulated thermal conditions, the CCT diagram with a supplementary graph was determined regarding changes in HV5 hardness as a function of cooling time t8/5 ( Figure 14). The latter is particularly important in the light of the considerations made. in the range from 10 to 20 s provides a bainitic-ferritic structure, the closest to the steel structure in the initial state. Further extension of the cooling time leads to an increase in the ferrite content in the structure, above the cooling time of 100 s, the steel had a ferritic-bainitic structure (Table 7). Based on the phase transformation tests of S700MC steel under the conditions of simulated thermal conditions, the CCT diagram with a supplementary graph was determined regarding changes in HV5 hardness as a function of cooling time t8/5 ( Figure 14). The latter is particularly important in the light of the considerations made. in the range from 10 to 20 s provides a bainitic-ferritic structure, the closest to the steel structure in the initial state. Further extension of the cooling time leads to an increase in the ferrite content in the structure, above the cooling time of 100 s, the steel had a ferritic-bainitic structure ( Table 7). Based on the phase transformation tests of S700MC steel under the conditions of simulated thermal conditions, the CCT diagram with a supplementary graph was determined regarding changes in HV5 hardness as a function of cooling time t8/5 ( Figure 14). The latter is particularly important in the light of the considerations made.

The Studies on the Influence of Stimulated Thermal Cycles with a Maximum Temperature of 1250 °C and Variable Cooling Time t8/5 on the Structure and Properties of HAZ in S700MC Steel
The next stage of the tests were tests with the imposed thermal cycles with cooling times t8/5 successively: 1.82, 3, 5, 10, 15, 30, 60 and 120 s and the maximum temperature of the thermal cycle Tmax = 1250 °C. The proposed cooling time t8/5 corresponded to the characteristic cooling times on the CCT diagram. The microscopic metallographic tests carried out confirmed the compliance of the obtained structures with the structures resulting from the developed CCT diagram. With a short cooling time, below 10 s, a mixture of bainite and low-carbon martensite occurred. The cooling time in the range from 10 to 20 s provides a bainitic-ferritic structure, the closest to the steel structure in the initial state. Further extension of the cooling time leads to an increase in the ferrite content in the structure, above the cooling time of 100 s, the steel had a ferritic-bainitic structure (Table 7). Based on the phase transformation tests of S700MC steel under the conditions of simulated thermal conditions, the CCT diagram with a supplementary graph was determined regarding changes in HV5 hardness as a function of cooling time t8/5 ( Figure 14). The latter is particularly important in the light of the considerations made. in the range from 10 to 20 s provides a bainitic-ferritic structure, the closest to the steel structure in the initial state. Further extension of the cooling time leads to an increase in the ferrite content in the structure, above the cooling time of 100 s, the steel had a ferritic-bainitic structure (Table 7). Based on the phase transformation tests of S700MC steel under the conditions of simulated thermal conditions, the CCT diagram with a supplementary graph was determined regarding changes in HV5 hardness as a function of cooling time t8/5 ( Figure 14). The latter is particularly important in the light of the considerations made.  Numerical analyses were also carried out for t8/5 times (TC1: t8/5 = 1.82 s, TC1: t8/5 = 3 s, TC2: t8/5 = 5 s, TC3: t8/5 = 10 s, TC4: t8/5 = 15 s, TC5: t8/5 = 30 s, TC6: t8/5 = 60 s and TC7: t8/5 = 120 s) and the maximum temperature of the imposed thermal cycle Tmax = 1250°C. As a result of numerical analyses, information was obtained on the distribution of individual metallurgical phases and their maximum contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 15-17).
As in the case of numerical analyses of the influence of the maximum temperature of the   Numerical analyses were also carried out for t8/5 times (TC1: t8/5 = 1.82 s, TC1: t8/5 = 3 s, TC2: t8/5 = 5 s, TC3: t8/5 = 10 s, TC4: t8/5 = 15 s, TC5: t8/5 = 30 s, TC6: t8/5 = 60 s and TC7: t8/5 = 120 s) and the maximum temperature of the imposed thermal cycle Tmax = 1250°C. As a result of numerical analyses, information was obtained on the distribution of individual metallurgical phases and their maximum contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 15-17).
As in the case of numerical analyses of the influence of the maximum temperature of the   Numerical analyses were also carried out for t8/5 times (TC1: t8/5 = 1.82 s, TC1: t8/5 = 3 s, TC2: t8/5 = 5 s, TC3: t8/5 = 10 s, TC4: t8/5 = 15 s, TC5: t8/5 = 30 s, TC6: t8/5 = 60 s and TC7: t8/5 = 120 s) and the maximum temperature of the imposed thermal cycle Tmax = 1250°C. As a result of numerical analyses, information was obtained on the distribution of individual metallurgical phases and their maximum contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 15-17).
As in the case of numerical analyses of the influence of the maximum temperature of the   Numerical analyses were also carried out for t8/5 times (TC1: t8/5 = 1.82 s, TC1: t8/5 = 3 s, TC2: t8/5 = 5 s, TC3: t8/5 = 10 s, TC4: t8/5 = 15 s, TC5: t8/5 = 30 s, TC6: t8/5 = 60 s and TC7: t8/5 = 120 s) and the maximum temperature of the imposed thermal cycle Tmax = 1250°C. As a result of numerical analyses, information was obtained on the distribution of individual metallurgical phases and their maximum contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 15-17).
As in the case of numerical analyses of the influence of the maximum temperature of the   Figure 14. The results of hardness HV5 measurements in thermo-mechanically simulated HAZ areas of S700MC steel.
Numerical analyses were also carried out for t 8/5 times (TC1: t 8/5 = 1.82 s, TC1: t 8/5 = 3 s, TC2: t 8/5 = 5 s, TC3: t 8/5 = 10 s, TC4: t 8/5 = 15 s, TC5: t 8/5 = 30 s, TC6: t 8/5 = 60 s and TC7: t 8/5 = 120 s) and the maximum temperature of the imposed thermal cycle T max = 1250 • C. As a result of numerical analyses, information was obtained on the distribution of individual metallurgical phases and their maximum contents in the HAZ area in the analysed cases. Selected analysis results were compared with the results of metallographic tests (Figures 15-17).       As in the case of numerical analyses of the influence of the maximum temperature of the imposed thermal cycle on the hardness of the HAZ obtained, in the case of analyses with a variable cooling time t 8/5 , the results obtained were close to the values measured on real samples (Figures 18 and 19).

Mechanical Properties Tests
In order to determine the impact of thermal cycle parameters on the mechanical properties of thermo-mechanically simulated HAZ areas, tests were also carried out in the form of a static tensile test and impact test. A static tensile test for round samples, taken from HAZ areas of steel subjected to thermal cycles in the maximum temperature range from 400 to 700 °C, showed a tensile strength value similar to that of the native material. As the maximum temperature of the heating cycle increased, there was a clear decrease in the HAZ tensile strength compared to the parent material-

Mechanical Properties Tests
In order to determine the impact of thermal cycle parameters on the mechanical properties of thermo-mechanically simulated HAZ areas, tests were also carried out in the form of a static tensile test and impact test. A static tensile test for round samples, taken from HAZ areas of steel subjected to thermal cycles in the maximum temperature range from 400 to 700 °C, showed a tensile strength value similar to that of the native material. As the maximum temperature of the heating cycle increased, there was a clear decrease in the HAZ tensile strength compared to the parent materialup to 100 MPa. The values of HAZ elongation heated up in the temperature range from 400 to 700 °C

Mechanical Properties Tests
In order to determine the impact of thermal cycle parameters on the mechanical properties of thermo-mechanically simulated HAZ areas, tests were also carried out in the form of a static tensile test and impact test. A static tensile test for round samples, taken from HAZ areas of steel subjected to thermal cycles in the maximum temperature range from 400 to 700 • C, showed a tensile strength value similar to that of the native material. As the maximum temperature of the heating cycle increased, there was a clear decrease in the HAZ tensile strength compared to the parent material-up to 100 MPa. The values of HAZ elongation heated up in the temperature range from 400 to 700 • C were at the level of 12%, with the elongation of native material about 16%. As the HAZ heating temperature increases, the elongation decreases to approx. 6% (Figure 20). Impact tests on obtained HAZ areas carried out at −30 • C showed a significant effect of the maximum temperature of the thermal cycle on the plastic properties of steel. Heat affected zone areas heated from 400 to 700 • C had a lower impact strength compared to the impact strength of the parent material at 20 • C. In the temperature range 800-900 • C, there was a decrease in hardness and a sharp increase in impact strength to the value of approximately 300 J/cm 2 ( Figure 21).     A static tensile test of round samples taken from steel specimens subjected to thermal cycles at a temperature of 1250 • C, at different cooling times, showed a small effect of the cooling time t 8/5 on the strength properties of the S700MC steel HAZ areas. During the entire cooling time range -from 3 to 120 s-the HAZ tensile strength was less than that of the parent material. The achieved elongation values at the level of 7% were much lower than the elongation of the native material-16% ( Figure 22). A static tensile test of round samples taken from steel specimens subjected to thermal cycles at a temperature of 1250 °C, at different cooling times, showed a small effect of the cooling time t8/5 on the strength properties of the S700MC steel HAZ areas. During the entire cooling time range -from 3 to 120 s-the HAZ tensile strength was less than that of the parent material. The achieved elongation values at the level of 7% were much lower than the elongation of the native material-16% ( Figure  22). Impact tests carried out at -30 °C of thermo-mechanically simulated HAZ, subjected to thermal cycles with a maximum temperature of 1250 °C and different cooling times, showed a sharp and significant decrease in plastic properties in relation to the initial material, regardless of the cooling time t8/5, Figure 23.  A static tensile test of round samples taken from steel specimens subjected to thermal cycles at a temperature of 1250 °C, at different cooling times, showed a small effect of the cooling time t8/5 on the strength properties of the S700MC steel HAZ areas. During the entire cooling time range -from 3 to 120 s-the HAZ tensile strength was less than that of the parent material. The achieved elongation values at the level of 7% were much lower than the elongation of the native material-16% ( Figure  22). Impact tests carried out at -30 °C of thermo-mechanically simulated HAZ, subjected to thermal cycles with a maximum temperature of 1250 °C and different cooling times, showed a sharp and significant decrease in plastic properties in relation to the initial material, regardless of the cooling time t8/5, Figure 23.

Results Discussion
Preliminary tests carried out in the form of a comparison of recorded thermal cycles and calculated temperature field distributions in the tested samples allowed the calibration of calculation models but also confirmed the usefulness of the proposed calculation method in support of further considerations.
Real tests and numerical simulations allowed determining the HAZ behaviour of S700MC steel subjected to the effect of a simulated welding heat cycle. Microscopic metallographic studies of simulated HAZ areas heated by cycles of different T max showed that in the maximum cycle temperature range from 400 to 900 • C, HAZ of S700MC steel is characterized by a fine-grained bainitic-ferritic structure. Above the maximum cycle temperature of 900 • C, there was a strong grain growth and it progressed to 1300 • C (Table 5). When analysing the results obtained by numerical simulations, it can also be seen that the calculated metallurgical phase distributions confirm the results obtained during metallographic tests (Figures 7-9, Table 6). The content of the ferritic phase increases with increasing maximum cycle temperature accompanied by a slight decrease in the content of bainitic phase at the maximum value of the tested cycle temperature. The increase in the content of the ferritic phase and the disappearance of the initial (bainitic-ferritic) phase was also associated, as can be seen both from the results of actual hardness measurements and the calculated distributions, to a decrease in hardness in the area of the simulated heat-affected zone associated with the increase in the maximum temperature of the thermal cycle (Figures 11 and 12). The hardness of the HAZ areas heated in the maximum cycle temperature range from 400 to 900 • C did not change and was similar to the hardness of the native material. When the temperature of the maximum heat cycle increased above 900 • C, the material softened to approximately 230 HV1 ( Figure 12). The calculated hardness values differed from those measured by a maximum of 23 HV units.
According to the CCT diagram, a martensitic transformation occurred in the S700MC steel, but this did not result in a significant increase in hardness ( Figure 14) relative to the hardness of the parent material. It allows to state that the carbon present in the solution, to a small extent, takes part in the strengthening of steel and is also not the dominant factor in phase transitions. The S700MC steel has low hardenability due to the low concentration of unbound carbon (about 0.03%) and other alloying elements. With a short cooling time, martensite was formed, but it was low-carbon martensite which did not reduce the plasticity of steel ( Figure 22). The hardness measurements carried out in the whole range of analysed cooling times t 8/5 did not show the tendency of S700MC steel to cold cracking (the maximum measured hardness does not exceed values of 270 HV5) ( Figure 19). As the cooling time increased, the hardness decreased, which was mainly caused by an increase in the ferrite content in the structure of the steel under test and grain growth. Hardness in the HAZ area decreased from 265 HV, with cooling time of several seconds to 190 HV, with cooling time above 60 s (Figures 14 and 19). The relatively small differences in the maximum hardness values seem to confirm the thesis that in the case of S700MC steel phase transformations, γ-α and the value of the carbon equivalent cannot constitute the basis for assessing its weldability. The hardness values obtained in the HAZ area below 270 HV1, regardless of the cooling time, indicate that this area is not prone to cold cracking. Also, in this case, the results of numerical analyses seem to confirm the results obtained in real samples. Similarly calculated metallurgical phase distributions reflect the character of the described transformations and correspond well with the results of microscopic metallographic tests (Figures 15-18, Table 7).
Tests of thermo-mechanically simulated HAZ areas, heated to different maximum temperatures, showed their significant diversity in terms of strength and plastic properties. Strength properties after exceeding the temperature of the thermal cycle with a maximum temperature of 600 • C decrease in relation to the native material (Figure 20), which is associated primarily with grain growth. The plastic properties of simulated HAZ (especially impact strength) depend on the durability of strengthening phases, their dispersion and on aging processes. The HAZ areas heated from 400 to 700 • C were characterized by lower impact strength than the native material at 20 • C which should probably be associated with the aging processes, diffusion of carbon and nitrogen atoms at close distances to the dislocation nuclei and their immobilization. In the temperature range of 800-900 • C, there was a decrease in hardness and a rapid increase in impact toughness to 300 J/cm 2 which should be associated with the disappearance of secretory strengthening through coagulation of the precipitates and the passage of strengthening components to the matrix and grain recrystallization processes. Test results of thermo-mechanically simulated HAZ areas heated to different maximum temperatures have shown that the real HAZ is characterized by variable strength and plastic properties on its cross-section. The most adverse changes were noted in the area heated to a temperature above 1000 • C, when the impact strength was reduced to a few J/cm 2 . Research on the impact of the cooling time t 8/5 on the HAZ property heated to a maximum temperature of 1250 • C confirmed that this relationship remains in the entire range of the tested cooling times (Figure 23). The thermal cycle at a temperature of about 1250 • C causes a loss of properties acquired as a result of thermomechanical treatment.
Such a rapid decrease in the impact toughness of areas heated to high temperature, regardless of the cooling time, should be associated with an increase in the number of dissolved strengthening phases in the matrix and their re-uncontrolled separation in the form of numerous fine-dispersion precipitations in the matrix of several nm which cause steel to strengthen. The obtained results were consistent with the earlier analysis of the HAZ properties heated to various maximum cycle temperatures (Figures 20 and 21). Very low impact strength of the high-temperature part of HAZ, regardless of the cooling time t 8/5 , and a slight change in hardness together with the extension of the cooling time confirm the thesis that the properties of HAZ are determined by the durability of strengthening phases and the change of their dispersion, and the role of phase transformation of austenite is less important (Figures 22 and 23).
A static tensile test of round samples taken from steel subjected to thermal cycles at 1250 • C, at different cooling times, also showed a small effect of the cooling time t 8/5 on the strength properties of the HAZ of S700MC steel. During the entire analysed cooling time range, from 3 to 120 s, the HAZ tensile strength was less than that of the native material. As the cooling time increased from 3 to 120 s, the tensile strength decreased from 720 to 640 MPa. This decrease in strength should be associated primarily with the increase in the ferrite content in the structure and grain growth in the high-temperature, simulated HAZ area ( Figure 11, Table 6). The achieved elongation values of 7% are much lower than the elongation of the native material-16% ( Figure 22).
The research shows that the actual HAZ on its cross-section is characterized by variable properties. Heat affected zone areas heated in the 800-900 • C temperature range are characterized by the highest impact strength. The most dangerous HAZ area with low plasticity is its high-temperature, coarse-grained part, heated above 1200 • C. The disappearance of the secretory strengthening effect, reduction of grain growth and, consequently, reduction of the HAZ overheating section is visible here.
Therefore, the welding process should be carried out in such a way as to minimize the width of adverse HAZ areas. The presented research and analyses also show that the processes related to the γ-α allotropic transformation that occur in S700MC steel during cooling cannot constitute the basis for assessing its welding properties. In such cases, it is particularly important to learn the mechanisms responsible for the behaviour of this type of materials and, after the calibration and validation of numerical models, to include them in the design process of the structure. The use of numerical analyses in the design of technological processes, where the rules used so far cease to work, is basically the only currently available and correct direction, allowing the safe and effective use of these modern materials.

Conclusions
The presented tests and numerical analyses showed that an increase in the maximum temperature of the thermal cycle also causes an increase in the ferrite content and a decrease in the bainite content in the HAZ area (Figures 9-11, Tables 5 and 6). Low heating temperatures (up to approximately 600-700 • C), during which the bainitic structure undergoes the tempering process, do not change the hardness values. The lack of hardness changes along with the increase in tempering temperature is associated with a low concentration of elements' increasing hardenability, especially carbon.
Thus, aging processes have a dominant impact on steel properties in this temperature range, which is confirmed by the results of impact tests ( Figure 21). With increasing tempering temperatures from 100 • C, impact strength increases from 15 to 38 J/cm 2 at 600 • C but is still lower than the impact strength of the base material at ambient temperature (50 J/cm 2 ). In the temperature range of 700-1000 • C, the secretion strengthening effect disappears, as a result of coagulation of the precipitates, their coherence disappears and the internal stresses decreases. In addition, the recrystallization processes that occur reduce the hardness ( Figure 12) and increase the impact strength even up to 280 J/cm 2 . A further increase in the temperature of the thermal cycle causes partial dissolution of the precipitates in the matrix, and with the slow cooling process, the micro-additive strengthening releases again, but in an uncontrolled manner, resulting in a decrease in impact strength to a few J/cm 2 ( Figure 21).
In the case of the analysis of the effect of the cooling time t 8/5 , numerical analyses and metallographic tests showed that as the cooling rate decreased, the ferrite content in the examined HAZ area increased and bainite decreased (Figures 16 and 17). The hardness of the simulated areas together with the increase in the cooling time from 3 to 120 s slightly decreased by about 40 HV (Figure 19), which indicates the secondary role of austenite phase transformations in controlling the strength and plastic properties of welded joints.
Therefore, the tests of the influence of cooling time t 8/5 of the HAZ area heated to 1250 • C allow to conclude the dominant role of strengthening phases in the assessment of weldability of thermo-mechanically processed steels with high yield strength. In addition to the statement above, high-temperature thermal cycles, irrespective of the cooling time t 8/5 , cause in HAZ a decrease in impact toughness to the level of a few J/cm 2 ( Figure 23). The impact strength decrease in this area is caused by the durability of strengthening phases and their re-separation during cooling.
To conclude, it should be risked that low impact strength, regardless of the cooling time t 8/5 should indicate that the CCT diagram of S700MC steel cannot be the basis for an unambiguous assessment of its weldability. When welding thermo-mechanically treated steels with a high yield strength, preheating before welding is not necessary, on the contrary it can lead to deterioration of strength properties and plasticity of welded joints. Also, for repair welding, the introduction of additional heat to the material should be kept to a minimum. Repeated influence of the heat cycle during repair welding leads to a decrease in HAZ strength and plastic properties due to the fact of grain growth, aging processes and an increase in the concentration of dissolved strengthening components in the matrix. Similar to the above, in the case of welded joints of thermo-mechanically processed steels with a high yield strength, it is not recommended to carry out heat treatment after welding to stabilize the shape, as this reduces the strength and plastic properties of HAZ.