The Inﬂuence of Aluminum Content on Oxidation Resistance of New-Generation ODS Alloy at 1200 ◦ C

: The aim of the paper is to evaluate the e ﬀ ect of aluminum content on the oxidation resistance of new-generation of oxide dispersion strengthened (ODS) alloy at 1200 ◦ C. Three grades of the alloy of chemical composition Fe-15Cr- x Al-4Y 2 O 3 with di ﬀ erent Al contents x = 0.3 wt.%, 2.0 wt.% and 5.5 wt.% are prepared by mechanical alloying. The alloys are consolidated by high temperature rolling followed by heat treatment. To study the oxidation resistance the samples are isothermally aged in the air for 1 h, 4 h, 16 h and 64 h at 1200 ◦ C. The oxidation kinetics, composition and formation mechanism of the oxide layers are analyzed. The weight gain of prepared steels is estimated. The kinetics of oxidation is studied on metallographic cross-sections of the exposed samples by scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS) analysis. The oxides on the surfaces are identiﬁed by X-ray di ﬀ raction (XRD) analysis. The Al content signiﬁcantly enhances the oxidation resistance of the alloy. For a su ﬃ ciently high Al content in the alloy a compact oxide layer of α -Al 2 O 3 on the surface is formed, which signiﬁcantly suppresses further oxidation process. The specimens for oxidation tests represented by prisms of dimensions 8 × 8 × 2.5 mm are cut with a wire electric spark cutter. All the surfaces of the samples are ground to the same grade on metallographic SiC sandpapers up to density 1200. After grinding the samples are ultrasonically cleaned in acetone. The oxidation tests are performed at 1200 ◦ C in a mu ﬄ e furnace on air for 1 h, 4 h, 16 h and 64 h. For each test time and grade tested, one specimen is used. In total, twelve specimens are employed in the oxidization experiment. To account for possible oxide delamination of the specimens during cooling, each specimen is placed on an alumina plate and weighted with the plate before and after oxidation test. The alumina plates are annealed at 1250 ◦ C for 4 h to stabilize their weight before the test. An analytical balance with an accuracy of 0.1 mg is used for weighing of specimens. microstructure, surface morphology of oxide and cross-sections of oxide layers of the are by a Tescan SEM with the energy dispersive spectrometer analyzer The observation is conducted in the secondary electron mode using an acceleration voltage 20 kV and a beam spot size of 15 nm. The specimens for microstructural and cross-sectional observations of the oxide layers are hot and cold mounded with respectively. The specimens are then ground with SiC sandpaper up to density 2500 and with 3 µ m and 1 µ m diamond pastes and OPS suspension. Prior to the observation, the specimens of the oxide scales and cross-sections of the oxide layers are by a carbon ﬁlm of thickness ~17 nm to prevent charging. The oxide layer thickness is measured in ten lines on three di ﬀ erent locations of the


Introduction
The current top creep and oxidation resistant alloys are represented by Ni-based superalloys for temperatures up to 1100 • C [1][2][3] and by ferritic oxide dispersion strengthened (ODS) steels for temperatures up to 1300 • C [4][5][6][7]. The Ni-based superalloys are strengthened by coherent ordered γ -precipitates, the mechanisms of creep in single crystals are summarized in the overview paper [8] and addressed by micromechanical unit cell models [9,10]. However, the γ -phase cutting by dislocations and the instability of the γ -precipitates due to their coarsening or rafting above 900 • C limit the applicability of the Ni-based superalloys in the range of temperatures 900-1100 • C. Compared to Ni-based superalloys, current ODS ferritic steels (alloys) exhibit significant microstructural stability also in the temperature regime 1100-1300 • C [11][12][13]. The microstructure of the ODS alloys consists of an alloy matrix strengthened by the dispersion of stable nano-oxides, usually Y-based, typically of a size between 5-30 nm and of volume fraction of about 0.5%. The processing route of the ODS alloys involves two steps: (1) the nanocomposite powder consisting of the matrix and Y-nano-oxides is produced by mechanical alloying (MA) and (2) the powder is then hot consolidated. There is a variety of commercially produced ferritic ODS alloys like MA 956 or MA 957 [5,11], PM 2000 or PM 2010 [14], ODM alloys [15] as well as research variants like 14YWT [11], 12YWT [11], 9YWT [16], Eurofer ODS [17,18], etc. Excellent creep strength of the ODS alloys is associated with an attractive interaction between dislocations and nano-oxides as it is successfully modelled by Rösler and Arzt [19], who also predict a threshold stress for creep and its significant drop with coarsening of the nano-oxides. The coarsening kinetics of particles in multicomponent systems is modelled by Fisher et al. [20] and experimentally studied e.g., by Bartkova et al. [21] or by Svoboda et al. [22] indicating a very high Metals 2020, 10 resistance of Y-nano-oxides against coarsening in ODS alloys. The benefits of high creep resistance of ODS alloys at very high temperatures are conditioned by a sufficiently good oxidation resistance. It is common knowledge that Cr-alloying itself is insufficient in such temperature region, see [23][24][25], and a certain content of Al is inevitable, to ensure a sufficient oxidation resistance like, e.g., in MA 956 [5], or PM 2000 [14] ODS alloys. The research effort of the authors resulted in development of a mechanically alloyed powder with a very high content of O, allowing production of an ODS alloy (called new-generation ODS alloy by the authors) of rather high nano-oxide volume fraction of about 5%, which exceeds the volume fraction in classical ODS alloys by one order of magnitude [4,6]. The processing of the new-generation ODS alloy consists of three steps [22]: (1) MA to produce chemically homogeneous powders, (2) hot consolidation of the powders by intensive plastic deformation, e.g., by rolling, providing a compact ultra-fine grained alloy due to an intensive dynamic recrystallization and (3) heat treatment to provoke secondary recrystallization leading to rather coarse-grained microstructure conditioning an excellent creep resistance. A complex optimization of the chemical composition of the new-generation ODS alloy performed recently by the authors of the Institute of Physics of Materials leads to conclusion that pure Y-nano-oxides as strengthening particles are much better with respect to coarsening than other nano-oxides [21,22], as well as in terms of the cohesive strength of grain boundaries being influenced by wetting of the nano-oxides (unpublished results). Moreover, the influence of Mo, Ta, La, Ti, Co and Ni alloying on the creep resistance is evaluated as negative or neutral and Cr alloying as slightly positive (unpublished results). A very good creep resistance is obtained for the content of Al up to 10 wt.% (publication in preparation). Now we are in the position to complete the knowledge on the new-generation ODS alloy by studying the influence of Al alloying on high-temperature oxidation resistance.
The oxidation resistance of steels is usually increased by high Cr alloying [26,27], Al alloying [28] or their combination [29,30]. The protective oxide layer is in the case of high-Cr steels composed mainly of Cr 2 O 3 [27]. At high temperatures a significant amount of Cr 2 O 3 evaporation occurs in atmospheres containing water vapor in which the volatilization of Cr 2 O 3 is based on its reaction with oxygen and water creating CrO 2 (OH) 2 [31][32][33]. The described volatilization reaction is active at temperatures from 600 • C, and depends on the composition and parameters of the environment [32][33][34]. Next to it, at temperatures higher than 900 • C, the Cr 2 O 3 readily oxidizes in the reaction with oxygen to volatile CrO 3 [35]. Both volatilization reactions reduce the surface oxide layer, thus, lowering the protective capability of oxide scale and decreasing oxidation resistance [32,35]. The 14Cr ODS steel shows acceptable oxidation resistance at temperature slightly above 700 • C, with a more pronounced effect on mechanical properties rather than on the oxidation resistance [36]. Detailed studies on the oxidation of high-Cr ferritic-martensitic steels P92 and of ferritic stainless steel containing W and Ce are presented in [23][24][25], from which one can conclude that a high content of Cr itself can ensure the sufficient long-term oxidation resistance at temperatures only up to 700 • C, and it can be increased up to 1000 • C by addition of W, Ce and Si. However, the long-term oxidation resistance can be drastically increased by the addition of Al, as shown for steels in [29,37], and for the top creep resistant ODS alloys MA 956 and PM 2000 containing about 5 wt.% of Al, the oxidation resistance of which extends to the temperature of 1300 • C [5,38]. Excellent high-temperature oxidation resistance is achieved when Al forms a dense and continuous layer of Al 2 O 3 on the surface of the alloy. The formation and polymorphs of the Al 2 O 3 layer depends on the temperature and alloy composition [29,37,39].
The aim of the present paper is to perform a detailed study of the influence of Al alloying on oxidation resistance of the new-generation ODS alloys with a high content of Y 2 O 3 .

Materials and Methods
Three grades of new-generation ODS alloy of chemical composition Fe-15Cr-xAl-4Y 2 O 3 with different Al content of x = 0.3 wt.%, 2.0 wt.% and 5.5 wt.%, are prepared by the powder metallurgy route. A custom-made ball mill is used for MA. A vacuum-tight milling container with volume of Metals 2020, 10, 1478 3 of 13 22 dm 3 and diameter of 400 mm made from low alloyed steel is filled with 100 balls of diameter 40 mm made from hardened low carbon Maraging 350 steel (25 kg) to minimize contamination of the mechanically alloyed powder by carbon due to abrasion of milling balls. The inputs in the form of powders of pure elements or compounds (yttria) are used, which allow a very easy variation of chemical composition of the resultant ODS alloy. The following metals powders are used for the ODS powder preparation: Fe-powder ABC100.30 (Höganäs, Sweden), 100 mesh Al-powder of purity 99.9% (CNPC POWDER, Shanghai, China), Y 2 O 3 -powder of purity 99.9% of 500 mesh (Anhui Herrman Impex Co Ltd., Anhui, China) and Cr metal size 1-4 mm of purity 99.9% (Kovy a slitiny, Zaječice, Czech Republic). A total amount of 1 kg of the powder (the ball to powder ratio is 25) is mechanically alloyed by rotation of the milling container at 70 rpm along the horizontal axis. After a sufficiently long MA (two weeks) in vacuum, the powder properties become saturated and the powder particles consist of a homogeneous solid solution with a huge density of defects like dislocations and vacancies. After MA, the powder is poured under the protective atmosphere (CO 2 ) in the rolling container made from steel tube 20/1 mm, evacuated and sealed by welding. Then the container is rolled in three steps to thicknesses 7.5 mm, 4.9 mm and 3.25 mm at temperature 900 • C. The rolling leads to pore-free ultra fine-grained microstructure due to heavy plastic deformation inducing dynamic recrystallization. The strain rate during rolling is estimated as 10 s −1 . After stripping from the rolling container, the ODS alloy is secondary recrystallized by annealing at 1200 • C for 16 h. The nominal chemical composition of the grades is presented in the Table 1. The specimens for oxidation tests represented by prisms of dimensions 8 × 8 × 2.5 mm are cut with a wire electric spark cutter. All the surfaces of the samples are ground to the same grade on metallographic SiC sandpapers up to density 1200. After grinding the samples are ultrasonically cleaned in acetone. The oxidation tests are performed at 1200 • C in a muffle furnace on air for 1 h, 4 h, 16 h and 64 h. For each test time and grade tested, one specimen is used. In total, twelve specimens are employed in the oxidization experiment. To account for possible oxide delamination of the specimens during cooling, each specimen is placed on an alumina plate and weighted with the plate before and after oxidation test. The alumina plates are annealed at 1250 • C for 4 h to stabilize their weight before the test. An analytical balance with an accuracy of 0.1 mg is used for weighing of specimens. The microstructure, surface morphology of the oxide scales and cross-sections of the oxide layers of the grades are characterized by a Tescan LYRA 3 XMH FEG/SEM scanning electron microscopy (SEM, Tescan, Brno, The Czech Republic) equipped with the energy dispersive spectrometer (EDS) analyzer X-Max80 (Oxford Instruments, High Wycombe, UK). The observation is conducted in the secondary electron mode using an acceleration voltage 20 kV and a beam spot size of 15 nm. The specimens for microstructural and cross-sectional observations of the oxide layers are hot and cold mounded with resin, respectively. The specimens are then ground with SiC sandpaper up to density 2500 and polished with 3 µm and 1 µm diamond pastes and OPS suspension. Prior to the observation, the specimens of the oxide scales and cross-sections of the oxide layers are coated by a carbon film of thickness~17 nm to prevent charging. The oxide layer thickness is measured in ten lines on three different locations of the specimen.
The phase composition of the grades and of the surface oxide scales is analyzed by X-ray diffraction of the bulk material by X-ray diffractometer (Empyrean, PanAnalytical, Almelo, The Netherlands) using the Co (Kα1,2) radiation measured with beta filter and 1-D detector (Pixel3D). It works in Theta-Theta geometry, Bragg-Brentano continuous mode with step 0.04 • and 300 seconds per step. The diffracted patterns were analyzed by HighScorePlus 4 (PanAnalytical, Almelo, The Netherlands) with PDF2 and ICSD databases and by FullProffSuite [40,41]

Description of the Microstructure of As-Annealed ODS Alloys
The microstructures of the grades of new-generation ODS alloys with different Al content are shown in Figure 1. The influence of Al content on the resultant grain microstructure is significant. Grade A1 with 5.5 wt.% of Al fully recrystallizes to rather large grains. Grade A2 with 2.0 wt.% Al also fully recrystallizes, but a smaller grain size is obtained. The recrystallization process of grade A3 is, however, not completed, leading to bimodal grain size distribution. Homogeneous nanosized particles dispersion is observed in the grain interiors and on the grain boundaries of fine grains. The black large particles are identified as aluminum nitrides (AlN) by EDS analysis. The results of X-ray diffraction (XRD) revealed ferrite (α-Fe) and a relatively high amount of Y 2 O 3 nanoparticles of~4 vol.%, see Figure 2. The absence of AlN in the XRD spectrum is due to its small quantity, bellow 0.3 wt.% in the microstructure. The particle analyses by transmission electron microscopy refer for FeCrAl ODS alloys with similar chemical composition such as PM 2000 (Fe-19Cr-5.5Al-0.5Ti-0.5Y 2 O 3 ) [42] and MA 956 (Fe-19.9Cr-4.6Al-0.4Ti-0.5Y 2 O 3 ) [43], also the presence of complex Y-Al oxides YAG (bcc lattice, Y 3 Al 5 O 12 ), YAP (orthorhombic lattice, YAlO 3 ) and A 2 O 3 oxides together with Y-Al complex oxide YAP (orthorhombic lattice, YAlO 3 ). Especially for the grades with the increased Al content, i.e., A1 and A2, Al 2 O 3 oxides and Y-Al complex oxides can be expected. The lack of identification of those phases in this work is probably connected with their low amount in the microstructures of the grades and by the detection limits of performed XRD analyses.

Description of the Microstructure of As-Annealed ODS Alloys
The microstructures of the grades of new-generation ODS alloys with different Al content are shown in Figure 1. The influence of Al content on the resultant grain microstructure is significant. Grade A1 with 5.5 wt.% of Al fully recrystallizes to rather large grains. Grade A2 with 2.0 wt.% Al also fully recrystallizes, but a smaller grain size is obtained. The recrystallization process of grade A3 is, however, not completed, leading to bimodal grain size distribution. Homogeneous nanosized particles dispersion is observed in the grain interiors and on the grain boundaries of fine grains. The black large particles are identified as aluminum nitrides (AlN) by EDS analysis. The results of X-ray diffraction (XRD) revealed ferrite (α-Fe) and a relatively high amount of Y2O3 nanoparticles of ~4 vol.%, see Figure 2. The absence of AlN in the XRD spectrum is due to its small quantity, bellow 0.3 wt.% in the microstructure. The particle analyses by transmission electron microscopy refer for FeCrAl ODS alloys with similar chemical composition such as PM 2000 (Fe-19Cr-5.5Al-0.5Ti-0.5Y2O3) [42] and MA 956 (Fe-19.9Cr-4.6Al-0.4Ti-0.5Y2O3) [43], also the presence of complex Y-Al oxides YAG (bcc lattice, Y3Al5O12), YAP (orthorhombic lattice, YAlO3) and A2O3 oxides together with Y-Al complex oxide YAP (orthorhombic lattice, YAlO3). Especially for the grades with the increased Al content, i.e., A1 and A2, Al2O3 oxides and Y-Al complex oxides can be expected. The lack of identification of those phases in this work is probably connected with their low amount in the microstructures of the grades and by the detection limits of performed XRD analyses.
The effect of Al addition on microstructure and mechanical properties of the studied FeCrAl ODS alloy can be described as follows. The increase of Al content in the studied range from 0.3 wt.% to 5.5 wt.% enhances the recrystallization ability of the grades after thermo-mechanical treatment of high temperature rolling. A larger grain size with smaller portion of grain boundaries is favorable for creep properties of the alloy [4,44]. The influence of rolling temperature of thermo-mechanical treatment and of Al content between 4-11 wt.% is described in the separated study [45]. It is observed that the increase of Al content has positive effect on creep strength, the contribution of which is identified as an improved cohesion strength of grain boundaries.

Oxidation Kinetics
The oxidation kinetics of the grades at 1200 °C is shown in Figure 3. Obviously, there is a sharp decrease of the oxidation weight gain with the increase of Al content from 0.3 wt.% to 2.0 wt.%, see Figure 3a. The weight gain of grade A3 with the lowest Al content 0.3 wt.% is 3.2 mg/cm 2 , whereas that of grade A2 with 2.0 wt.%, is only 1.4 mg/cm 2 after the oxidation at 1200 °C for 64 h. Further increase of Al content to 5.5 wt.% in A1 has only a slight effect leading to the weight gain 1.3 mg/cm 2 . A similar trend of data is observed for thicknesses of oxidized layers (see Figure 3b) determined by The effect of Al addition on microstructure and mechanical properties of the studied FeCrAl ODS alloy can be described as follows. The increase of Al content in the studied range from 0.3 wt.% to 5.5 wt.% enhances the recrystallization ability of the grades after thermo-mechanical treatment of high temperature rolling. A larger grain size with smaller portion of grain boundaries is favorable for creep properties of the alloy [4,44]. The influence of rolling temperature of thermo-mechanical treatment and of Al content between 4-11 wt.% is described in the separated study [45]. It is observed that the increase of Al content has positive effect on creep strength, the contribution of which is identified as an improved cohesion strength of grain boundaries.

Oxidation Kinetics
The oxidation kinetics of the grades at 1200 • C is shown in Figure 3. Obviously, there is a sharp decrease of the oxidation weight gain with the increase of Al content from 0.3 wt.% to 2.0 wt.%, see Figure 3a. The weight gain of grade A3 with the lowest Al content 0.3 wt.% is 3.2 mg/cm 2 , whereas that of grade A2 with 2.0 wt.%, is only 1.4 mg/cm 2 after the oxidation at 1200 • C for 64 h. Further increase of Al content to 5.5 wt.% in A1 has only a slight effect leading to the weight gain 1.3 mg/cm 2 . A similar trend of data is observed for thicknesses of oxidized layers (see Figure 3b) determined by examination of the cross-sections of exposed specimens. The thickness of the oxidized layer is considered as the thickness of the surface layer, where a significant change of chemical composition with respect to the alloy matrix occurs, see Chapter 3.4. Grade A3 with the lowest Al content 0.3 wt.% shows by a factor of 20 a faster growth of the oxidized layer to that in grades A2 and A1 with Al content 2.0 wt.% and 5.5 wt.%. After the exposure for 64 h, the oxidized layer thickness for grade A3 is 180 µm in contrast to grades A2 and A1 with thicknesses of 10 µm and 9 µm, respectively.

Oxidation Kinetics
The oxidation kinetics of the grades at 1200 °C is shown in Figure 3. Obviously, there is a sharp decrease of the oxidation weight gain with the increase of Al content from 0.3 wt.% to 2.0 wt.%, see Figure 3a. The weight gain of grade A3 with the lowest Al content 0.3 wt.% is 3.2 mg/cm 2 , whereas that of grade A2 with 2.0 wt.%, is only 1.4 mg/cm 2 after the oxidation at 1200 °C for 64 h. Further increase of Al content to 5.5 wt.% in A1 has only a slight effect leading to the weight gain 1.3 mg/cm 2 . A similar trend of data is observed for thicknesses of oxidized layers (see Figure 3b) determined by examination of the cross-sections of exposed specimens. The thickness of the oxidized layer is considered as the thickness of the surface layer, where a significant change of chemical composition with respect to the alloy matrix occurs, see Chapter 3.4. Grade A3 with the lowest Al content 0.3 wt.% shows by a factor of 20 a faster growth of the oxidized layer to that in grades A2 and A1 with Al content 2.0 wt.% and 5.5 wt.%. After the exposure for 64 h, the oxidized layer thickness for grade A3 is 180 µm in contrast to grades A2 and A1 with thicknesses of 10 µm and 9 µ m, respectively. To analyze the oxidation kinetics, the time dependence of the mass gain and oxide layer thickness are described according to the Wagner's theory [46]. The data of mass gain and oxide thickness is fitted to the parabolic law using the equation: To analyze the oxidation kinetics, the time dependence of the mass gain and oxide layer thickness are described according to the Wagner's theory [46]. The data of mass gain and oxide thickness is fitted to the parabolic law using the equation: where X is either the mass gain defined as a change of the weight ∆m per unit area before the exposure A (∆m/A) or a change of oxide layer thickness ∆d, k is the oxidation rate constant, t is the exposure time in s and n is the rate exponent. For the linear, parabolic, sub-parabolic or cubic and sub-cubic oxidation kinetics, the values of n are 1, 2, ≤3 and ≤4, respectively. Assuming the n = 2 a parabolic rate constant k p can be obtained by plotting the square of the measurement variable against time, Figure 4.
In the case of k p , the data is fitted by the equation: where C is a constant. sub-cubic oxidation kinetics, the values of n are 1, 2, ≤3 and ≤4, respectively. Assuming the n = 2 a parabolic rate constant kp can be obtained by plotting the square of the measurement variable against time, Figure 4. In the case of kp, the data is fitted by the equation: where C is a constant. The results of oxidation kinetics of the weight gain data are presented in Table 2. A non-parabolic growth law is determined for the examined alloys. Grades A1 and A2 obey nearly a cubic growth law, whereas grade A3 follows a sub-parabolic growth law at studied conditions. Parabolic rate constants of grades A1 and A2 forming α-Al2O3 oxide scale layer seem to be quite similar with the ODS alloy PM 2000 with coarse grains [47]. The oxidization kinetics of grades A1 and A2 are also well comparable with the kinetics of the intermetallic ODS alloys Fe40Al Grade 3 and ALUSI 1 with one order lower values determined at 1100 °C [48]. In comparison with alumina forming Ni-based single crystal superalloy DD6 [49], the A1 and A2 grades provide only one order higher kp at 200 °C higher temperature. On the other hand, grade A3 with chromium oxide scale layer demonstrates similar oxidization kinetics as binary Ni-30Cr alloy [35] or high-Cr steel 19Cr-2Mo-0.3Mn-0.5Si [25]. The effect of Al content on the oxidization kinetics can be also noticed on the results of the 15Cr steel, with Al contents of 0.08 wt.% and 2.45 wt.% forming a chromium oxide and alumina oxide scale layer at 1000 °C [29]. Considering the lower temperature of the oxidization experiment 1000 °C, comparable results to those of grades A1, A2 and A3 are obtained. The results of oxidation kinetics of the oxide scale thickness data are presented in Table 3. The kinetics of growth of oxide layer thickness is sub-parabolic, cubic and parabolic for grade A1, A2 and A3, respectively. The parabolic rate constant of oxide layer thickness of grade A3 is three orders higher than of grades A1 and A2. Such a big difference is particularly caused by the internal oxidation of grade A3, see Chapter 3.4. The oxide scale thicknesses of grades A1, A2 and A3 are quite similar to the ODS alloys PM 2000 [47], MA 956 [50] and binary Ni 30Cr alloy [35] at corresponding exposure times, respectively. The results of oxidation kinetics of the weight gain data are presented in Table 2. A non-parabolic growth law is determined for the examined alloys. Grades A1 and A2 obey nearly a cubic growth law, whereas grade A3 follows a sub-parabolic growth law at studied conditions. Parabolic rate constants of grades A1 and A2 forming α-Al 2 O 3 oxide scale layer seem to be quite similar with the ODS alloy PM 2000 with coarse grains [47]. The oxidization kinetics of grades A1 and A2 are also well comparable with the kinetics of the intermetallic ODS alloys Fe40Al Grade 3 and ALUSI 1 with one order lower values determined at 1100 • C [48]. In comparison with alumina forming Ni-based single crystal superalloy DD6 [49], the A1 and A2 grades provide only one order higher k p at 200 • C higher temperature. On the other hand, grade A3 with chromium oxide scale layer demonstrates similar oxidization kinetics as binary Ni-30Cr alloy [35] or high-Cr steel 19Cr-2Mo-0.3Mn-0.5Si [25]. The effect of Al content on the oxidization kinetics can be also noticed on the results of the 15Cr steel, with Al contents of 0.08 wt.% and 2.45 wt.% forming a chromium oxide and alumina oxide scale layer at 1000 • C [29]. Considering the lower temperature of the oxidization experiment 1000 • C, comparable results to those of grades A1, A2 and A3 are obtained. The results of oxidation kinetics of the oxide scale thickness data are presented in Table 3. The kinetics of growth of oxide layer thickness is sub-parabolic, cubic and parabolic for grade A1, A2 and A3, respectively. The parabolic rate constant of oxide layer thickness of grade A3 is three orders higher than of grades A1 and A2. Such a big difference is particularly caused by the internal oxidation of grade A3, see Chapter 3.4. The oxide scale thicknesses of grades A1, A2 and A3 are quite similar to the ODS alloys PM 2000 [47], MA 956 [50] and binary Ni 30Cr alloy [35] at corresponding exposure times, respectively.

Surface Morphology and Phase Composition of the Oxides
The morphology of the surfaces of oxidized samples of grades A1, A2 and A3 is shown in Figure 5. The oxide grains of grades A1 and A2 are rather fine after the exposure for 64 h at 1200 • C. The equiaxed grains of grade A1 are of size less than 1.5 µm. The EDS analysis revealed that the oxides are dominantly composed of Al and O, see Chapter 3.4. Next to it, a small amount of Y, Fe and Cr are detected too. In comparison to grade A1, the equiaxed grains of surfaces oxides of the grade A2 are slightly larger (2 µm). Additionally, in the case of the A2 alloy, the EDS analysis detected that fine oxides are dominantly composed of Al and O. In addition to it, the significantly larger amounts of Y, Fe and Cr are detected too. Moreover, compared to grade A1, the bright oxides of larger size and regular distribution are presented on the oxidized surface of grade A2, compare Figure 5a,b. Based on the results of EDS measurements, these bright oxides contain Al, O, Fe and a slightly increased amount of Cr. The surface morphology of the oxide layer on the oxidized grade A3 alloy is rather coarse, see Figure 5c. One can also notice a much higher roughness of the oxide surfaces with pronounced protrusions. The oxide grains of grade A3 attain size up to 7 µm which is the largest size observed for the studied grades. According to the EDS analysis, the surfaces oxides contain O, Fe and Cr. Neither Y nor Al is detected in the surface oxides in this case.

Surface Morphology and Phase Composition of the Oxides
The morphology of the surfaces of oxidized samples of grades A1, A2 and A3 is shown in Figure 5. The oxide grains of grades A1 and A2 are rather fine after the exposure for 64 h at 1200 °C. The equiaxed grains of grade A1 are of size less than 1.5 μm. The EDS analysis revealed that the oxides are dominantly composed of Al and O, see Chapter 3.4. Next to it, a small amount of Y, Fe and Cr are detected too. In comparison to grade A1, the equiaxed grains of surfaces oxides of the grade A2 are slightly larger (2 µ m). Additionally, in the case of the A2 alloy, the EDS analysis detected that fine oxides are dominantly composed of Al and O. In addition to it, the significantly larger amounts of Y, Fe and Cr are detected too. Moreover, compared to grade A1, the bright oxides of larger size and regular distribution are presented on the oxidized surface of grade A2, compare Figure 5a,b. Based on the results of EDS measurements, these bright oxides contain Al, O, Fe and a slightly increased amount of Cr. The surface morphology of the oxide layer on the oxidized grade A3 alloy is rather coarse, see Figure 5c. One can also notice a much higher roughness of the oxide surfaces with pronounced protrusions. The oxide grains of grade A3 attain size up to 7 µ m which is the largest size observed for the studied grades. According to the EDS analysis, the surfaces oxides contain O, Fe and Cr. Neither Y nor Al is detected in the surface oxides in this case.  The XRD spectra of the oxides grown on the surfaces of specimens after the exposure for 64 h/1200 • C are given in Figure 6. The estimated penetration depth of the applied XRD measurement is 30 µm and is, therefore, considered in the interpretation of the results. The surface layer of grade A1 is dominantly composed of corundum (α-A 2 O 3 ) and of a small amount of complex Al, Y-rich oxides identified as Y 3 Al 5 O 12 (YAG). The oxidized surface of grade A2 also contains a significant amount of corundum together with a certain amount of complex Cr-Fe oxide identified as (Cr,Fe) 2 O 3 . Due to the small thickness of the oxide layers around 10 µm, both diffraction spectra of grades A1 and A2 also contain diffraction peaks of the ferritic matrix (α-Fe). On the contrary, the XRD measured only the oxide layer on the specimen of grade A3, due to its significantly larger thickness. This oxide layer is formed by nearly the same amount of complex Cr-Fe oxides analyzed as (Cr,Fe) 2 O 3 and (Fe,Cr) 3

O 4 .
h/1200 °C are given in Figure 6. The estimated penetration depth of the applied XRD measurement is 30 μm and is, therefore, considered in the interpretation of the results. The surface layer of grade A1 is dominantly composed of corundum (α-A2O3) and of a small amount of complex Al, Y-rich oxides identified as Y3Al5O12 (YAG). The oxidized surface of grade A2 also contains a significant amount of corundum together with a certain amount of complex Cr-Fe oxide identified as (Cr,Fe)2O3. Due to the small thickness of the oxide layers around 10 μm, both diffraction spectra of grades A1 and A2 also contain diffraction peaks of the ferritic matrix (α-Fe). On the contrary, the XRD measured only the oxide layer on the specimen of grade A3, due to its significantly larger thickness. This oxide layer is formed by nearly the same amount of complex Cr-Fe oxides analyzed as (Cr,Fe)2O3 and (Fe,Cr)3O4. Figure 6. X-ray diffraction (XRD) spectra and phase analysis of oxide layers on surfaces of grades A1, A2 and A3 after the exposure for 64 h/1200 °C.

The Analysis of Cross-Sections of the Oxidized Layers
The cross-sectional morphologies and corresponding EDS line scans of the specimens of grades A1, A2 and A3 exposed to 64 h/1200 °C are presented in Figure 7. It can be noticed that the thickness of the oxide layer significantly depends on the Al content as it is already shown in Figure 3b. The oxidized surface layers on grades A1 and A2 are compact with smooth outer surface, see Figure 7a,b. The oxidized surface layer is dominantly composed from corundum (α-A2O3), forming a top (outer) layer of equiaxed grains and a bottom (inner) layer containing columnar grains. The ratio of bottom to total oxide layer thickness of grade A1 continuously develops from 0.47 to 0.69 for 1 h and 64 h of exposure, respectively. The oxide scale of grade A2 follows a similar trend with the ratios 0.48 and 0.74 for corresponding exposure times. In the inner corundum layer the dendrites of YAG originated from reaction of yttria nano-oxides with corundum are observed, see Figure 6. The only sporadic isolated pores are observed inside corundum layers and no peeling of oxide layers is detected up to 64 h of exposure.
On the contrary, the oxide layer on the surface of grade A3 with Al content 0.3 wt.% consists of mixed Cr, Fe oxides, see Figure 7c. Moreover, there are significant changes of the chemical composition in the oxidized layer concerning O, Cr and Fe elements. The outer region of the oxide scale is composed mainly of O and Cr with a small amount of Fe, the amount of which decreases throughout the thickness of the oxide scale. Further, below the oxide layer, the clusters of oxides rich in Fe, Cr and Y are presented in the alloy matrix. Next, an intensive formation of small Al-Y-rich oxides can be observed at 30-180 µ m beneath the surface representing the inner region of the oxide scale. Note that these Al-Y rich isolated oxides are not detected in the as-annealed state of grade A3. Following, there is an increased amount of O in the matrix of grade A3 below the oxide scale. Regarding morphology, the oxide scale of grade A3 is rough. A significant amount of cavities, Figure 6. X-ray diffraction (XRD) spectra and phase analysis of oxide layers on surfaces of grades A1, A2 and A3 after the exposure for 64 h/1200 • C.

The Analysis of Cross-Sections of the Oxidized Layers
The cross-sectional morphologies and corresponding EDS line scans of the specimens of grades A1, A2 and A3 exposed to 64 h/1200 • C are presented in Figure 7. It can be noticed that the thickness of the oxide layer significantly depends on the Al content as it is already shown in Figure 3b. The oxidized surface layers on grades A1 and A2 are compact with smooth outer surface, see Figure 7a

Discussion of the Effect of Al Content on Oxidization Mechanisms
From the results it is evident that two significantly different oxidation mechanisms occur in the studied grades' systems. The oxidization mechanism of grades A1 and A2 is the same, and can be described as the following. At the beginning of the oxidation, the oxygen molecules are adsorbed onto the surface of the sample. The Cr and Al are both strong oxide formers which have a high affinity for oxygen. These elements are preferentially oxidized when added to a base metal such as Fe due to the lower free energy of formation [51]. In case of grade A1 with Al content 5.5 wt.%, the oxygen anions diffuse into the substrate and firstly react with Al cations to form Al2O3 nucleating on On the contrary, the oxide layer on the surface of grade A3 with Al content 0.3 wt.% consists of mixed Cr, Fe oxides, see Figure 7c. Moreover, there are significant changes of the chemical composition in the oxidized layer concerning O, Cr and Fe elements. The outer region of the oxide scale is composed mainly of O and Cr with a small amount of Fe, the amount of which decreases throughout the thickness of the oxide scale. Further, below the oxide layer, the clusters of oxides rich in Fe, Cr and Y are presented in the alloy matrix. Next, an intensive formation of small Al-Y-rich oxides can be observed at 30-180 µm beneath the surface representing the inner region of the oxide scale. Note that these Al-Y rich isolated oxides are not detected in the as-annealed state of grade A3. Following, there is an increased amount of O in the matrix of grade A3 below the oxide scale. Regarding morphology, the oxide scale of grade A3 is rough. A significant amount of cavities, presented both in the oxide scale and also on the interface of oxide scale/matrix, is observed. The cracks on the interface of oxide scale/matrix are detected too. The oxide scale is compact after 4 h of exposure but it shows a significant tendency to spall after 16 h of exposure. No additional oxidation is observed below unstuck oxide scale which indicates that the cracking/spallation of oxide scale takes place during cooling to the room temperature.

Discussion of the Effect of Al Content on Oxidization Mechanisms
From the results it is evident that two significantly different oxidation mechanisms occur in the studied grades' systems. The oxidization mechanism of grades A1 and A2 is the same, and can be described as the following. At the beginning of the oxidation, the oxygen molecules are adsorbed onto the surface of the sample. The Cr and Al are both strong oxide formers which have a high affinity for oxygen. These elements are preferentially oxidized when added to a base metal such as Fe due to the lower free energy of formation [51]. In case of grade A1 with Al content 5.5 wt.%, the oxygen anions diffuse into the substrate and firstly react with Al cations to form Al 2 O 3 nucleating on the surface. As the time extends, the crystal nucleus of Al 2 O 3 grows into a single, thin, dense and continuous α-Al 2 O 3 film. Hereafter, the interface of oxide/substrate is established and O 2− penetrate through the α-Al 2 O 3 film and react with Al 3+ at the interface. The formation of α-Al 2 O 3 layer leads to the depletion of Al 3+ at the subsurface. Therefore, the oxidation starts to be controlled by the inward diffusion of O 2− to react with Al 3+ at the oxide/metal interface, due to fact that the O 2− diffuses faster than Al 3+ throughout the Al 2 O 3 layer [48]. The oxidation layer predominantly grows by the inward displacement of the oxide/substrate interface. This is also proved by the observed dominant growth of α-Al 2 O 3 layer via columnar grains into the substrate, i.e., the inward growth of the oxide scale. Dominant inward growth of α-Al 2 O 3 is referred for the alloys with various Al content at comparable conditions of exposure [48,50,52]. This is due to the excellent protective function of the single α-Al 2 O 3 film the oxidation rate gradually decreases with the thickening of the film. The non-parabolic growth law of grades A1 and A2 seems to be a consequence of several factors, such as: the interference of the inter diffusion described by the thermodynamics models reported in [51,53,54], of the effect of the inter-diffusion of Al and Y elements and the columnar growth of α-Al 2 O 3 grains [48,50,52]. The presence of a relatively large amount of Y 2 O 3 nanoprecipitates in the system allows a significant modification of the oxide layer, because the phase diagram of the Al 2 O 3 -Y 2 O 3 binary system predicts the formation of three stoichiometric phases YAG, YAP (YAlO 3 ) and YAM (Y 4 Al 2 O 9 ) [55]. In our case having a Al 2 O 3 rich system, the mixture of Al 2 O 3 and YAG is formed as it is observed in Figure 7.
The oxide scale formation of grade A2 with Al content 2.0 wt.% follows similar oxidation mechanism as grade A1. Nevertheless, at the beginning of oxidation, the formation of a continuous α-Al 2 O 3 layer is slightly delayed owning to the lower Al content. Before the continuous α-Al 2 O 3 layer is created the Cr-Fe-rich oxides (Cr,Fe) 2 O 3 are formed in the oxide scale in the gaps between the islands of α-Al 2 O 3 . Those (Cr,Fe) 2 O 3 oxides then remain in small amount in the top part of oxide scale of this grade.
The results of the surface oxidation of specimens of grade A3 indicate that the oxidation resistance is much lower, and the process is more complex to that of grades A1 and A2. When the Al content is in a low level of 0.3 wt.%, the outer oxide layer composes of complex Cr-Fe-rich oxides identified as (Cr,Fe) 2 O 3 and (Fe,Cr) 3 O 4 . The Cr-Fe-rich oxides are formed prior to Al 2 O 3 because of the both higher content of Cr and Fe with respect to Al and a higher growth rate of (Cr,Fe) 2 O 3 compared with that of Al 2 O 3 . The Cr element plays the most important role in protecting the alloy and the diffusion of Cr 3+ cations from inner to outer layers leads to the depletion of Cr in the inner layer. The porous outer (Cr,Fe) 2 O 3 layer becomes compact with the increased oxidation time. The Cr in the initially formed (Cr,Fe) 2 O 3 gradually changes into volatile CrO 3 under a high oxygen partial pressure and flows over the oxide surface. Simultaneously, some internal Fe ions diffuse outwards creating (Fe,Cr) 3 O 4 . The oxide scale of grade A3 composed of (Cr,Fe) 2 O 3 and (Fe,Cr) 3 O 4 grows outwardly unlike for grades A1 and A2 with α-Al 2 O 3 oxide scale. This indicates that the matrix continues to maintain the supply of Cr and Fe to the oxide scale, resulting in the Cr and Fe depletion at the subsurface region and causing the local matrix enrichment of Al and Y. The oxygen anions easily penetrate through porous oxide scale composed of Cr-Fe-rich oxides and develop Al-Y-rich oxides in this region. The oxidization of Al and Y promotes the creation of Cr-Fe-rich oxides in their surroundings, leading to the formation of clusters of oxides. These oxide clusters contribute to weakening of the stability composition of the matrix solid solution accelerating the diffusion of oxygen ions into the material. The higher partial pressure of oxygen in the subsurface matrix solid solution further promotes the internal oxidation of the alloy, resulting in the formation of individual Al-Y-rich oxides in the inner region of the oxide scale. The outer oxide scale is non-compact after 16 h of exposure at 1200 • C, and shows a tendency to peel off during the cooling stage. The oxide scale spallation most probably is caused by the difference in the thermal expansion coefficient between the oxide scale and matrix of the alloy [56,57]. Next, the high Kirkendall porosity, modelled, e.g., in [53,58], together with the misfit stresses induced by volumetric changes between the oxide and metal matrix [57], may also contribute to the spallation phenomenon.
A comparison of oxidation resistance performance of three studied grades of the new-generation ODS alloy leads to the conclusion that Al content over 2 wt.% ensures an excellent resistance to high temperature oxidation. The long-time high temperature oxidation protection is conditioned by the integrity of Al 2 O 3 oxide scale layer preventing the oxygen diffusion into the material and its repetitive formation in case of oxide scale spallation. For ferritic steels, the formation of uniform Al 2 O 3 oxide scale seems to be ensured for Cr and Al concentrations larger than 14 wt.% and 2 wt.%, respectively [30]. The results of other authors show that the uniform oxide scale of α-Al 2 O 3 is repeatedly formed for ferritic steels with 4.6 wt.% of Al [59]. The long-term formation of the stable oxide layer of the A1 grade with 5.5 wt.% of Al is therefore ensured. Grade A2 with 2.0 wt.% of Al is expected to provide slower formation of a uniform Al 2 O 3 oxide layer on the surface in case of spallation and thus a less durable oxidation resistance to that of grade A1.

Conclusions
The oxidation mechanisms and kinetics are investigated for three grades of the new-generation ODS alloys of chemical composition Fe-15Cr-xAl-4Y 2 O 3 with different Al contents x = 0.3 wt.%, 2.0 wt.% and 5.5 wt.%. The results can be summarized as follows: 1.
The new-generation ODS alloys are successfully prepared by hot consolidation of mechanically alloyed powders followed by annealing.

2.
The oxidation tests using the limited number of test specimens are performed at 1200 • C on air for 1 h, 4 h, 16 h and 64 h. The oxidation kinetics obeys the non-parabolic law. 3.
In the case of sufficiently high Al content x = 2.0 wt.% and 5.5 wt.%, a compact corundum-based oxide layer of α-Al 2 O 3 is formed on the surface, which protects the alloys from internal oxidation very effectively.

4.
In the case of a low Al content x = 0.3 wt.%, a mixture of Fe, Cr oxides forms a porous and non-compact layer on the specimen surface, which cannot protect the alloy from internal oxidation and degradation of mechanical properties.

5.
As the Fe-15Cr-xAl-4Y 2 O 3 new-generation ODS alloys contains a high amount of Y 2 O 3 , the corundum-based oxide layer of the grades with the high Al content x = 2.0 wt.% and 5.5 wt.% reacts with the Y 2 O 3 and YAG dendrites grow in the layer. 6.
The Al content exceeding 2 wt.% ensures an excellent oxidation resistance of the new-generation ODS alloys. Nevertheless, for long-term oxidation resistance grade A1 with higher Al content 5.5 wt.% is expected to provide an improved performance.