Green Synthesis and Characterization of Silver Nanoparticles Using a Lythrum salicaria Extract and In Vitro Exploration of Their Biological Activities

This research describes an eco-friendly green route for the synthesis of AgNPs using an aqueous extract of Lythrum salicaria. Taguchi design was used to optimize the synthesis method, taking into account various working conditions. The optimum parameters were established using a 3 mM AgNO3 concentration, a 1:9 extract:AgNO3 volume ratio, a pH value of 8, 60 ℃ temperature, and 180 min reaction time. The synthesized AgNPs were characterized using UV-Vis and FTIR spectroscopy, and TEM and EDX analysis. The SPR band at 410 nm, as well as the functional groups of biomolecules identified by FTIR and the EDX signals at ~3 keV, confirmed the synthesis of spherical AgNPs. The average AgNPs size was determined to be 40 nm, through TEM, and the zeta potential was −19.62 mV. The antimicrobial assay showed inhibition against S. aureus and C. albicans. Moreover, the results regarding the inhibition of lipoxygenase and of peroxyl radical-mediated hemolysis assays were promising and justify further antioxidant studies.


Introduction
Noble metal (e.g., Pt, Ag, Au) nanoparticles have gained researchers' attention due to their multiple benefits in various fields, such as medicine, the food industry, material science, physics, and chemistry. In the biomedical field, noble metal nanoparticles are versatile agents used in drug delivery, diagnosis, radiotherapy enhancement, photo-ablation procedures, and hyperthermia studies [1,2]. The photophysical metal properties, such as facile synthesis in different shapes and sizes, easy derivatization with chemical and biomolecular ligands, biocompatibility, and high stability, represent the most appropriate attributes of nanoparticles, recommending them to industry [3]. Among such nanoparticles, silver nanoparticles (AgNPs) have gained special attention, due to their superior electrical conductivity, chemical stability, controlled geometry, catalytic and antibacterial properties [4]. AgNPs are used for many medical applications, including sensing devices, coating materials, catheters, bone cement and wound dressings [5].
Several methods can be applied for AgNPs synthesis, each presenting advantages and disadvantages. A general classification divides them into bottom-up and top-down techniques. In the top-down category, the principle relies upon reducing the size of bulk material by mechanical milling, laser ablation or sputtering. Although the final product presents uniform physico-chemical properties, these methods also involve high energy consumption. The bottom-up techniques use molecules or atoms to prepare nanoparticles through various

Obtaining of Extracts
For the preparation of the L. salicaria extract, 10 g of plant material, as grounded aerial part (purchased from a local natural and biological products market), were added to 100 mL distilled water, at an adjusted temperature of 40°C, while continuously stirring at 500 rpm for 30 min. After the mixture was cooled at room temperature, filtration was carried out using a Whatman filter paper no. 1 and the filtrate was stored at 4°C for further experiments.

Preparation and Optimization of Nanoparticles
The Taguchi design was used to study AgNPs synthesis conditions in an experiment that uses minimal resources and, in our case, tested five parameters. AgNPs were synthesized by adding different concentrations of extract to silver nitrate (AgNO 3 ) solution, in various volume ratios. These mixtures were subjected to magnetic stirring at 500 rpm, at different adjusted pH values, using 1 M HCl and 1 M NaOH, at different temperatures and time intervals. The change in color was monitored and the maximum absorbance was recorded in the 300-600 nm range by UV-Vis spectroscopy. The analysis was performed in triplicate.
The formed AgNPs were separated by centrifugation at 8000 rpm for approximately 30 min. After removing the supernatant, the AgNPs were purified by washing three times with distilled water and eventually dried at 40°C until constant mass.
The theoretical concentration of AgNPs in the colloidal synthesis mixture was calculated using a mathematical method [18,19]. Firstly, the average number of atoms per nanoparticle (N) was determined through Equation (1): where π = 3.14, ρ = 10.5 g/cm 3 (density of face centered cubic silver), D = 133.5 × 10 −7 cm (average diameter of nanoparticles), M = 107.868 g/mol (atomic mass of silver) and N A = 6.023 × 10 23 mol −1 (Avogadro's number). Secondly, the molar concentration of nanoparticles in the resulting colloidal mixture (C) could be calculated only by considering that all silver ions (Ag + ) were entirely converted to AgNPs in the biosynthesis process. Equation (2) was applied for the determination of C: (2) where N T = total amount of Ag atoms added as AgNO 3 (3.0 mM = 0.003 M), N = average number of atoms per nanoparticle, V = reaction volume (0.22 L) and N A = Avogadro's number [18,19].

AgNPs Characterization
Regarding the physico-chemical characterization of AgNPs, the change in mixture color was initially visually monitored and then the UV-Vis spectra were recorded, observing the presence of the peak due to surface plasmon resonance (SPR). The absorbances were recorded with a Jasco V-530 UV-Vis double beam spectrophotometer (Tokyo, Japan) in the 300-600 nm range. The functional groups involved in the green synthesis of AgNPs were analyzed by FTIR spectroscopy (Bruker Vertex 70 spectrophotometer, Bruker, Billerica, MA, USA) in the 4000-310 cm −1 range, comparing the extract and AgNPs' spectra. The other characteristics of AgNPs were examined by the following: DLS (the hydrodynamic diameter and the zeta potential), using a Delsa Nano Submicron Particle Size Analyzer (Beckman Coulter Inc., Fullerton, CA, USA); TEM (dimensions and morphology), using a Hitachi High-Tech HT 7700 Transmission Electron Microscope (Hitachi High-Technologies Cor- Furthermore, the total phenolic content of the L. salicaria extract (diluted correspondingly) and supernatant (after the first separation of AgNPs) was performed using a previously described UV-Vis spectrophotometric method, with gallic acid as standard [20]. The analysis was performed in triplicate and the results were expressed as mg gallic acid equivalents (GAE) per mL sample.

Antimicrobial Testing
The synthetized AgNPs and the corresponding extract were investigated for antimicrobial activity, using disk diffusion methods [21,22], against different bacterial (Staphylococcus aureus ATCC 25923, Pseudomonas aeruginosa ATCC 27853) and fungal (Candida albicans ATCC 90028) pathogens, obtained from the Culture Collection of the Department of Microbiology, "Grigore T. Popa" University of Medicine and Pharmacy, Iasi, Romania. Standard culture mediums, such as Mueller-Hinton agar (Biolab) for fungi and Mueller-Hinton agar (Oxoid) for bacteria, were used. After the samples and positive controls (discs containing 5 µg ciprofloxacin and 25 µg fluconazole, respectively) were applied, the plates were incubated at 35°C for 24 h. All experiments were conducted in triplicate, and, after the inhibition zones were measured (mm), the mean ± standard deviation was calculated. The Minimal Inhibitory Concentration (MIC) and Minimal Bactericidal Concentration (MBC) or Minimal Fungicidal Concentration (MFC), were determined by the broth microdilution method. Subsequent double dilutions of the tested samples in Mueller-Hinton broth were inoculated with the suspension of the microorganism test.

Antioxidant Activity
The antioxidant activities of the samples (AgNPs and extract) were determined using 15-lipoxygenase (LOX) inhibition and peroxyl radical-mediated hemolysis inhibition assays. Regarding the first method, after the mixture of lipoxygenase (in pH 9 borate buffer solution) and samples were left to stand in the dark at room temperature for 10 min, linoleic acid (in pH 9 borate buffer solution) was added, and the absorbances were recorded at 234 nm [23]. The second method focused on the determination of the inhibition capacity of erythrocyte hemolysis, mediated by peroxyl free radicals [24]. Samples treated with a solution of 2,2 -azobis-(2-amidinopropane) dihydrochloride (AAPH) (in phosphate buffer pH 7.4) and an erythrocyte suspension (10 % in 0.9 % saline) were maintained for 3 h at 37°C, cooled to room temperature, diluted with phosphate buffer (pH 7.4) and, eventually, centrifuged for 10 min. Simultaneously, a control solution containing only AAPH and erythrocyte suspension was prepared. The absorbances were recorded at 540 nm. All experiments were performed in triplicate and gallic acid was used as standard. For samples that showed an activity of more than 50 %, the EC 50 value was also calculated and expressed as µg extract/mL final solution.

Taguchi Design Experiment for Optimization of Reaction Parameters
The optimization of parameters for more efficient AgNPs synthesis was based on an L9 orthogonal array design, a method that combines mathematical and statistical principles in order to obtain a predictive knowledge of a complex process with several variables, but with a reduced number of attempts [25,26]. This design presents several advantages over the traditional more laborious and time-consuming optimization methods. In the traditional methods each variable is evaluated one by one, while the others remain constant, and, therefore, data on what happens when variables change simultaneously is not obtained [27].
The model was obtained using variables presented in Table 1 at levels 1, 2 and 3. Table 1.  In order to process the data, the S/N ratio was calculated using Equation (3). The S/N ratio measures the quality characteristic deviating from the desired value, and represents the ratio of the target value (signal) to the standard deviation for the response variable (noise), which can be calculated by selecting the formula corresponding to the quality characteristic "larger is better".
where: n = number of experiments, yi = response variable for the experiment (absorbance) [26,27]. The obtained results for the S/N ratio are presented in Table 2. Each line in the matrix contains the numbers corresponding to the level at which the factors A, B, C, D and E are expressed in Taking into account the average value of absorbance and the S/N ratio calculated for each level, the optimal synthesis conditions were A3B1C3D3E3 (line L7, A at level 3, B at level 1, C, D and E at level 3), followed by A2B1C2D2E3 (L4), and, therefore, we could say that, in both cases, a volume ratio of 1:9 extract:AgNO 3 and 180 min reaction time were optimal. The average S/N ratio for each level is presented in Table 3 and the main effect of each variable is graphically represented in Figure 1. In order to establish the optimal synthesis conditions, the maximum S/N value was investigated.  Considering the S/N ratio, the optimum conditions for AgNPs synthesis were A2B1C3D3E3, with a 3 mM AgNO3 concentration, 1:9 extract:AgNO3 ratio, a pH value of 8, 60 ℃ temperature and 180 min reaction time.
To the best of our knowledge, the present study is the only one that has used the Taguchi model to establish the reaction conditions for AgNPs synthesized using an L. salicaria extract. Moreover, the traditional optimization of synthesis can be found in a single study carried out by Srećković et al., which led to the following conditions: 20 mM AgNO3 concentration, 25 ℃, pH 12, and 30 min reaction time [17]. In both cases, the synthesis was optimal at alkaline pH, which can be explained by the change in dissociation constants values for functional groups involved in the reduction process, which leads to an increase in the availability of compounds for the synthesis process [28].

Physico-Chemical Characterization of AgNPs
AgNPs synthesis by means of green methods represents the focus of scientists, given that they imply lower costs and ease in the monitoring and sampling processes. Moreover, plants are easy to grow and safe to handle, and, implicitly, this type of eco-friendly synthesis could replace chemical techniques for obtaining AgNPs [29]. The steps implied by AgNPs synthesis are represented by the reduction of Ag + and agglomeration of colloidal nanoparticles with oligomeric clusters formation [30]. Considering the S/N ratio, the optimum conditions for AgNPs synthesis were A2B1C3D3E3, with a 3 mM AgNO 3 concentration, 1:9 extract:AgNO 3 ratio, a pH value of 8, 60°C temperature and 180 min reaction time.
To the best of our knowledge, the present study is the only one that has used the Taguchi model to establish the reaction conditions for AgNPs synthesized using an L. salicaria extract. Moreover, the traditional optimization of synthesis can be found in a single study carried out by Srećković et al., which led to the following conditions: 20 mM AgNO 3 concentration, 25°C, pH 12, and 30 min reaction time [17]. In both cases, the synthesis was optimal at alkaline pH, which can be explained by the change in dissociation constants values for functional groups involved in the reduction process, which leads to an increase in the availability of compounds for the synthesis process [28].

Physico-Chemical Characterization of AgNPs
AgNPs synthesis by means of green methods represents the focus of scientists, given that they imply lower costs and ease in the monitoring and sampling processes. Moreover, plants are easy to grow and safe to handle, and, implicitly, this type of eco-friendly synthesis could replace chemical techniques for obtaining AgNPs [29]. The steps implied by AgNPs synthesis are represented by the reduction of Ag + and agglomeration of colloidal nanoparticles with oligomeric clusters formation [30].
The first indicator of AgNPs synthesis is noticed through visual observation, but the formation of nanoparticles must be confirmed by other methods as well. Therefore, we continued monitoring the color change by means of UV-Vis spectroscopy ( Figure 2).
As seen in the inset of Figure 2, the initial color of the extract was yellow, changing to dark brown after adding AgNO 3 under specific conditions. When analyzing the UV-Vis spectra, no absorption peak was observed in the 300-600 range for either the extract or AgNO 3 solution, but a distinct peak at 410 nm was revealed for the obtained colloidal solution. This peak could be due to excitation of SPR [31], which could determine the optical, physical and chemical properties of AgNPs [29]. The presence of a single SPR peak could explain the spherical shape of AgNPs [32]. The obtained results were in accordance with other studies focusing on AgNPs synthesized using L. salicaria extracts, in which the SPR band was observed at 415 nm [16] or in the 396-415 nm range [17]. The calculated concentration of AgNPs in the colloidal solution was found to be 2 × 10 −10 mol/L. The first indicator of AgNPs synthesis is noticed through visual observation, but the formation of nanoparticles must be confirmed by other methods as well. Therefore, we continued monitoring the color change by means of UV-Vis spectroscopy ( Figure 2). As seen in the inset of Figure 2, the initial color of the extract was yellow, changing to dark brown after adding AgNO3 under specific conditions. When analyzing the UV-Vis spectra, no absorption peak was observed in the 300-600 range for either the extract or AgNO3 solution, but a distinct peak at 410 nm was revealed for the obtained colloidal solution. This peak could be due to excitation of SPR [31], which could determine the optical, physical and chemical properties of AgNPs [29]. The presence of a single SPR peak could explain the spherical shape of AgNPs [32]. The obtained results were in accordance with other studies focusing on AgNPs synthesized using L. salicaria extracts, in which the SPR band was observed at 415 nm [16] or in the 396-415 nm range [17]. The calculated concentration of AgNPs in the colloidal solution was found to be 2 × 10 −10 mol/L. Differences in the position and appearance of the peak, even for the same plant species, can be explained by different harvesting areas, different conditions for extract preparation and for AgNPs synthesis. Nonetheless, these conditions can also lead to modifications in the shape and size of AgNPs. A wide peak generally indicates larger particles [29]. Moreover, their shape can be predicted considering the position of the SPR band, for example, in the 400-490 nm range, the particles are spherical [33].
The mechanism of AgNPs synthesis is explained through biomolecules present in the extract (polyphenols, phenolic acids, phytosterols, alkaloids, proteins, enzymes, sugars, etc.), which are compounds capable of donating electrons, so the reduction process from Ag + to Ag 0 can take place. This process is generally followed by agglomeration of free silver atoms and, eventually, by the formation of the AgNPs colloidal solution. Such biomolecules also participate in the functionalization and stabilization of AgNPs [34,35]. For example, there are many studies that demonstrate that phenolic acids are some of the most important bioactive substances that participate in AgNPs synthesis and even more in the process of stabilization of nanoparticles, therefore, having a synergistic effect. Yee-Shing Liu et al. [36] combined their research with that of other studies and proposed a mechanism for AgNPs formation using caffeic acid, one of the phenolic acids present in rice husk extract, along with gallic, protocatechuic, ferulic, vanillic and syringic acids. Caffeic acid in alkaline medium releases electrons, that are transferred to Ag + , which is reduced to Ag 0 . On the other hand, caffeic acid is transformed into a free radical which, in turn, reduces another Ag + and is converted to ortho-quinone. By the coupling of two free radicals of caffeic acid, an oxidative dimer is formed which releases 4 electrons that participate in the reduction of Ag + , being transformed into quinone. The formed quinones Differences in the position and appearance of the peak, even for the same plant species, can be explained by different harvesting areas, different conditions for extract preparation and for AgNPs synthesis. Nonetheless, these conditions can also lead to modifications in the shape and size of AgNPs. A wide peak generally indicates larger particles [29]. Moreover, their shape can be predicted considering the position of the SPR band, for example, in the 400-490 nm range, the particles are spherical [33].
The mechanism of AgNPs synthesis is explained through biomolecules present in the extract (polyphenols, phenolic acids, phytosterols, alkaloids, proteins, enzymes, sugars, etc.), which are compounds capable of donating electrons, so the reduction process from Ag + to Ag 0 can take place. This process is generally followed by agglomeration of free silver atoms and, eventually, by the formation of the AgNPs colloidal solution. Such biomolecules also participate in the functionalization and stabilization of AgNPs [34,35]. For example, there are many studies that demonstrate that phenolic acids are some of the most important bioactive substances that participate in AgNPs synthesis and even more in the process of stabilization of nanoparticles, therefore, having a synergistic effect. Yee-Shing Liu et al. [36] combined their research with that of other studies and proposed a mechanism for AgNPs formation using caffeic acid, one of the phenolic acids present in rice husk extract, along with gallic, protocatechuic, ferulic, vanillic and syringic acids. Caffeic acid in alkaline medium releases electrons, that are transferred to Ag + , which is reduced to Ag 0 . On the other hand, caffeic acid is transformed into a free radical which, in turn, reduces another Ag + and is converted to ortho-quinone. By the coupling of two free radicals of caffeic acid, an oxidative dimer is formed which releases 4 electrons that participate in the reduction of Ag + , being transformed into quinone. The formed quinones can bind to AgNPs and cause steric hindrance, thus, stabilizing the particles [36]. Flavonoids can also donate electrons or hydrogen and the keto form of the nucleus reduces Ag + to Ag 0 [33]. Thus, the total phenolic content of the extract used for synthesis (in suitable dilution) and of the first collected supernatant, were measured, so as to estimate the amount of such compounds involved in the synthesis process. If, initially, the phenolic content of the extract was 1.2404 mg GAE/mL, after the first separation, the supernatant only had a remaining content of 0.1122 mg GAE/mL, which could confirm the participation of bioactive compounds in the synthesis process.
Other examples of biosubstances involved in AgNPs synthesis are triterpenes. Aazam et al. [37] proposed a mechanism for the synthesis of AgNPs using ursolic acid, the main constituent of an Ocimum sanctum extract. Following the redox reaction, the -OH group of the ursolic acid structure deprotonates and oxidizes with the formation of a radical, promoting the reduction of silver from Ag + to Ag 0 . Further agglomeration and formation of oligomeric clusters occurs. During these steps, several species of AgNPs can be formed, given that Ag + reacts with Ag 0 , forming Ag 2 + , which dimerizes to Ag 4 +2 . In order to highlight the functional groups and, implicitly, the compounds that participate in AgNPs synthesis, FTIR analysis was used. Figure 3 presents the comparative FTIR spectra of the extract and of the corresponding AgNPs.
Other examples of biosubstances involved in AgNPs synthesis are triterpenes. Aazam et al. [37] proposed a mechanism for the synthesis of AgNPs using ursolic acid, the main constituent of an Ocimum sanctum extract. Following the redox reaction, the -OH group of the ursolic acid structure deprotonates and oxidizes with the formation of a radical, promoting the reduction of silver from Ag + to Ag 0 . Further agglomeration and formation of oligomeric clusters occurs. During these steps, several species of AgNPs can be formed, given that Ag + reacts with Ag 0 , forming Ag2 + , which dimerizes to Ag4 +2 .
In order to highlight the functional groups and, implicitly, the compounds that participate in AgNPs synthesis, FTIR analysis was used. Figure 3 presents the comparative FTIR spectra of the extract and of the corresponding AgNPs. The FTIR spectrum of the extract shows a broad absorption peak at 3452 cm −1 , which was related to the stretching vibration of -OH groups found in alcohols and phenols and to the N-H stretching from amides. The peaks at 2924 cm −1 and 2854 cm −1 corresponded to C-H stretching and bending vibrations of CH3 and CH2 (alkanes) [19,28]. The bands detected at 1736 cm −1 and 1624 cm −1 were connected to the vibration of C=O from amides and carboxylic groups, and -C=C-aromatic rings, respectively [38]. The bands at 1452 cm −1 and 1364 cm −1 could be attributed to stretching vibrations of CO of carboxylic acids or esters, to bending vibration of N-H in amides or to stretching vibrations of N-H in secondary amines, or to the C-N stretch vibration of aromatic amines. Furthermore, the 1184 cm −1 and 1038 cm −1 bands could be attributed to the C-O stretching vibrations of alcohols, esters, ethers and carboxylic acids from terpenoids and flavonoids and to the C-O-C stretching of aromatic ethers and polysaccharides [39,40]. The peaks found in the 600-900 cm −1 range corresponded to CH out of plane bending vibrations and the peak at 524 cm −1 could be responsible for C=C torsion and ring torsion of phenyl, or to C-N stretch from secondary amines and amides [40,41]. Generally, similar peaks, but also shifts, The FTIR spectrum of the extract shows a broad absorption peak at 3452 cm −1 , which was related to the stretching vibration of -OH groups found in alcohols and phenols and to the N-H stretching from amides. The peaks at 2924 cm −1 and 2854 cm −1 corresponded to C-H stretching and bending vibrations of CH 3 and CH 2 (alkanes) [19,28]. The bands detected at 1736 cm −1 and 1624 cm −1 were connected to the vibration of C=O from amides and carboxylic groups, and -C=C-aromatic rings, respectively [38]. The bands at 1452 cm −1 and 1364 cm −1 could be attributed to stretching vibrations of CO of carboxylic acids or esters, to bending vibration of N-H in amides or to stretching vibrations of N-H in secondary amines, or to the C-N stretch vibration of aromatic amines. Furthermore, the 1184 cm −1 and 1038 cm −1 bands could be attributed to the C-O stretching vibrations of alcohols, esters, ethers and carboxylic acids from terpenoids and flavonoids and to the C-O-C stretching of aromatic ethers and polysaccharides [39,40]. The peaks found in the 600-900 cm −1 range corresponded to CH out of plane bending vibrations and the peak at 524 cm −1 could be responsible for C=C torsion and ring torsion of phenyl, or to C-N stretch from secondary amines and amides [40,41]. Generally, similar peaks, but also shifts, reduction or disappearance of peaks, from the extract spectrum could be observed in the FTIR spectra of AgNPs. The disappearance of peaks could be explained by the participation of these groups only in the reduction process, while modifications in peak position and intensity could indicate the involvement of the corresponding groups not only in the reduction, but also in the stabilization processes [39]. Therefore, biomolecules, such as phenolic acids, flavonoids, terpenoids and proteins, could participate in the reduction and stabilization of AgNPs. The obtained results were comparable to those obtained by Samira Mohammadalinejhad et al. and by Srećković et al. [16,17]. The first of the aforementioned groups of researchers suggested that polyphenols are involved in the reduction process, while flavonoids, polyphenols, tannins and gallic acid are responsible for the reduction process, as well as for the stabilization of nanoparticles.
The morphological analysis of AgNPs was examined by TEM ( Figure 4) and the corresponding histogram can be found in Figure 5a.  [16,17]. The first of the aforementioned groups of researchers suggested that polyphenols are involved in the reduction process, while flavonoids, polyphenols, tannins and gallic acid are responsible for the reduction process, as well as for the stabilization of nanoparticles.
The morphological analysis of AgNPs was examined by TEM ( Figure 4) and the corresponding histogram can be found in Figure 5a.    [36]. The negative zeta potential (the charge around a moving particle in the colloidal solution in electric field) of −19.62 mV could have been due to biomolecules found on the AgNPs surfaces, that might determine a repulsion between particles and implicitly prevent agglomeration [33]. This value was in accordance with that obtained by Samira Mohammadalinejhad et al. [16], namely −20 mV.
The DLS analysis revealed an average AgNPs hydrodynamic dimension of 133.5 nm (Figure 5b). Other authors obtained values in the 20-138 nm range [17] or an average of 50 nm [16]. The TEM analysis measured only the average diameter of the metallic silver reduction and stabilization of AgNPs. The obtained results were comparable to those obtained by Samira Mohammadalinejhad et al. and by Srećković et al. [16,17]. The first of the aforementioned groups of researchers suggested that polyphenols are involved in the reduction process, while flavonoids, polyphenols, tannins and gallic acid are responsible for the reduction process, as well as for the stabilization of nanoparticles.
The morphological analysis of AgNPs was examined by TEM ( Figure 4) and the corresponding histogram can be found in Figure 5a.    [36]. The negative zeta potential (the charge around a moving particle in the colloidal solution in electric field) of −19.62 mV could have been due to biomolecules found on the AgNPs surfaces, that might determine a repulsion between particles and implicitly prevent agglomeration [33]. This value was in accordance with that obtained by Samira Mohammadalinejhad et al. [16], namely −20 mV.
The DLS analysis revealed an average AgNPs hydrodynamic dimension of 133.5 nm (Figure 5b). Other authors obtained values in the 20-138 nm range [17] or an average of 50 nm [16]. The TEM analysis measured only the average diameter of the metallic silver   [36]. The negative zeta potential (the charge around a moving particle in the colloidal solution in electric field) of −19.62 mV could have been due to biomolecules found on the AgNPs surfaces, that might determine a repulsion between particles and implicitly prevent agglomeration [33]. This value was in accordance with that obtained by Samira Mohammadalinejhad et al. [16], namely −20 mV.
The DLS analysis revealed an average AgNPs hydrodynamic dimension of 133.5 nm (Figure 5b). Other authors obtained values in the 20-138 nm range [17] or an average of 50 nm [16]. The TEM analysis measured only the average diameter of the metallic silver core so it did not include any coating/stabilizing agent. On the other hand, the DLS analysis measured the dynamic fluctuation and velocity of particles in suspended clusters, meaning the metallic silver core and the molecules that were attached to the surface nanoparticles, which could, depending on the structure, undergo a process of solvation and expansion in solution. Therefore, the hydrodynamic diameter estimated by DLS was larger than the size estimated by TEM [33,42,43].
The quantitative elemental structure of AgNPs was investigated by EDX analysis (Figure 6).
Data analysis revealed that EDX spectra of AgNPs mainly contained a specific and intense peak at 3 keV for Ag (37.52 wt %), but also C (18.83 wt %), O (24.49 wt %) and small quantities of N, Br, Si, Cl and K. Consequently, the results confirmed the synthesis of AgNPs. The presence of other elements might be related to the breakdown of capping agents from the surface of nanoparticles. analysis measured the dynamic fluctuation and velocity of particles in suspended clusters, meaning the metallic silver core and the molecules that were attached to the surface nanoparticles, which could, depending on the structure, undergo a process of solvation and expansion in solution. Therefore, the hydrodynamic diameter estimated by DLS was larger than the size estimated by TEM [33,42,43].
The quantitative elemental structure of AgNPs was investigated by EDX analysis (Figure 6). Data analysis revealed that EDX spectra of AgNPs mainly contained a specific and intense peak at 3 keV for Ag (37.52 Wt %), but also C (18.83 Wt %), O (24.49 Wt %) and small quantities of N, Br, Si, Cl and K. Consequently, the results confirmed the synthesis of AgNPs. The presence of other elements might be related to the breakdown of capping agents from the surface of nanoparticles.

Antimicrobial Activity
Firstly, the disk diffusion method was used, which is a routine, simple and low-cost antimicrobial susceptibility test. The antimicrobial activity was assessed using two bacterial strains, Staphylococcus aureus (S. aureus) and Pseudomonas aeruginosa (P. aeruginosa) and a fungal strain, Candida albicans (C. albicans). The results are presented in Table 4. Table 4. Antimicrobial activity of the extract and of the corresponding AgNPs.
The AgNPs presented better activity, compared to the extract against the Grampositive bacteria and pathogenic yeast. However, no activity was detected for either in the case of the Gram-negative bacteria.
Further, the broth microdilution method was applied, in order to determine the MIC and MBC values, and since it represents a standardized method, the results could be of clinical relevance [44]. Implicitly, the MIC and MBC/MFC values of samples against S. Figure 6. Zeta potential (a) and EDX spectra (b) of AgNPs.

Antimicrobial Activity
Firstly, the disk diffusion method was used, which is a routine, simple and low-cost antimicrobial susceptibility test. The antimicrobial activity was assessed using two bacterial strains, Staphylococcus aureus (S. aureus) and Pseudomonas aeruginosa (P. aeruginosa) and a fungal strain, Candida albicans (C. albicans). The results are presented in Table 4. Table 4. Antimicrobial activity of the extract and of the corresponding AgNPs. The AgNPs presented better activity, compared to the extract against the Gram-positive bacteria and pathogenic yeast. However, no activity was detected for either in the case of the Gram-negative bacteria.

S. aureus
Further, the broth microdilution method was applied, in order to determine the MIC and MBC values, and since it represents a standardized method, the results could be of clinical relevance [44]. Implicitly, the MIC and MBC/MFC values of samples against S. aureus ATCC 25923 and C. albicans ATCC 90028 were determined and are presented in Table 5. MIC was the lowest concentration of the sample at which bacterial growth was completely inhibited after 24 h incubation at 37 • C. In the study carried out by Srećković et al. [17], the MIC value obtained for AgNPs was 0.31 mg/mL for S. aureus and 0.62 for C. albicans. In our study, we obtained the same value for S. aureus, but for C. albicans the value was smaller (0.03 mg/mL).
To the best of our knowledge, the MBC value for AgNPs synthesized from L. salicaria has not been reported until now. The highest dilution showing 100 % inhibition was 0.62 mg/mL for S. aureus and 0.31 for C. albicans. For both tested microorganisms, the obtained results for MIC and MBC/MFC for the synthesized AgNPs were better than those obtained for the extract.
Indeed, most literature studies show better antibacterial activity of AgNPs on Gramnegative bacteria than on Gram-positive bacteria [45]. However, there are several research works that prove the contrary, as in our case. For example, Yage Xing et al. obtained better antibacterial activity on S. aureus, compared to E. coli for AgNPs formed using mango peel [46]. A similar example is that of AgNPs synthetized using olive leaves extract [47]. An explanation for the higher susceptibility in the case of Gram-positive bacteria, compared to Gram-negative bacteria, could be related to the differences between the wall structures of the two types of bacteria. The cell wall of Gram-positive bacteria consists of a thick peptidoglycan layer with teichoic acid and lipoteichoic acid, while the Gram-negative bacterial cell wall is more complex, containing an extra outer lipid membrane, with lipopolysaccharides, which could make the entrance of hydrophobic substances more difficult [48]. Therefore, a reason for better antimicrobial action in the case of Gram-positive bacteria could be represented by the more facile interaction between AgNPs and bacteria [49].
Moreover, the antimicrobial activity depends on the size and shape of AgNPs. Nanoparticles of smaller sizes, with a diameter of approximately 1-10 nm, have a higher surface:volume ratio and more efficient antimicrobial activity, interacting preferentially with bacteria [50]. Truncated triangular AgNPs have the strongest biocidal action compared to those that are spherical or rod shaped [51].
The mechanism surrounding the antibacterial activity has not been fully elucidated, but several explanations are possible, taking into account that AgNPs can adhere to, or can pass through, cell walls/membranes of microorganisms, or induce cellular toxicity and ROS generation, or modulate cell signaling.
The first proposed mechanism is that, following the electrostatic attraction between AgNPs and the cell membrane, nanoparticles tend to adhere to the membrane, which leads to alteration of the structure and rupture of the cell wall. Moreover, the interaction between AgNPs and sulfur-containing proteins found in the cell wall can lead to a chain reaction, starting with structural modifications, affecting the transport process and increasing permeability, which leads to cell content (ions, proteins, reducing sugars) leakage and, sometimes, ATP synthesis inhibition.
The second mechanism consists of the penetration of AgNPs inside the cell and nucleus, which can modify cellular functioning by interacting with the cell structure or biomolecules. Therefore, the destabilization and denaturation of proteins containing thiol groups can occur via interaction with silver ions, or AgNPs, and silver ions can interact with disulfide bonds, thus, blocking the active binding site, leading to functional deficiencies in microorganisms. Moreover, AgNPs can interact with DNA, and through the reaction of Ag + ions with nucleic acids, can lead to the destruction of the double helix structure.
For the third mechanism, a high concentration of Ag + ions produce cellular oxidative stress by generation of radicals and ROS. Free radicals can cause destruction of the mitochondrial membrane and can interact with lipids, enhancing lipid peroxidation. ROS generation can lead to hyperoxidation of lipids, proteins and DNA.
The last possible mechanism focuses on the modulation of the cellular signal system, which can lead to modifications in bacterial growth, as well as affect the processes at molecular and cellular levels [52,53].

Antioxidant Activity
Given that Srećković et al. [17] determined the antioxidant potential of an L. salicaria extract, and of the corresponding AgNPs, by DPPH and ABTS scavenging activity methods, and the results showed for the extract from the aerial parts slightly better activity (86.38 ± 0.13 µg/mL by DPPH method and 65.33 ± 2.08 µg/mL by ABTS test) versus AgNPs (>100 µg/mL by DPPH and 141.66 ± 17.05 µg/mL by ABTS test) [17], we proposed the use of other methods, with different principles. Therefore, our study focused on the  Tables 6 and 7. The inhibition of lipoxygenase, which was determined using the modified Malterud method [23], can be explained by polyphenolic compounds present in the extract that have the ability to block the activity of lipoxygenase, which catalyzes the oxidation of linoleic acid, thus, reducing the absorbance measured at 234 nm. The inhibition activity was calculated using the following formula: where A E is the difference between the absorbances of the enzyme solution without inhibitor at 90 and 30 s and A EI is the difference between the absorbances of the enzyme-inhibitor solution at 90 and 30 s, respectively.  Lipoxygenases (5-, 12-, 15-lipoxygenase) are metalloenzymes that contain ferrous or ferric ions in their catalytic center, depending on the stage of the redox reaction (oxidation or reduction) [54]. Lipoxygenases catalyze the oxidation of unsaturated fatty acids with the formation of lipid peroxides, which can cause the spread of oxidation reactions or cause the oxidation of lipids, proteins, nucleic acids, thereby affecting their biological properties [55]. Uncontrolled activation of these enzymes causes oxidative stress and inflammation, and can lead to neurodegenerative diseases, atherosclerosis, diabetes or cancer [56]. AgNPs show a more intense antioxidant activity compared to the extract, the EC 50 value being also slightly better than that of gallic acid. Their influence on lipoxygenase is most probably achieved through changes in the spatial structure of the enzyme or of its active center [56].
Antioxidant compounds can also block the peroxyl radical synthesis induced by AAPH, with consequent protection of the erythrocyte membrane. The reduction in the concentration of peroxyl radicals determines the decrease of the absorbance measured at 540 nm [24]. The erythrocyte hemolysis inhibition was calculated using the formula: where A S is the absorbance of the sample and A AAPH is the absorbance of the positive control. AAPH is a prooxidant compound that causes the oxidation of hemoglobin to methemoglobin, consequently inducing hemolysis, and possibly affecting the lipophilic structure of the erythrocyte membrane [57]. The synthesized AgNPs were more active compared to the extract. However, both the extract and AgNPs can block the prooxidant and hemolytic action of AAPH, without causing hemolysis in its absence. Blocking AAPH activity is done mainly by compounds that have both hydrophilic groups, that are capable of interacting with AAPH, but also lipophilic structures that allow passage through the erythrocyte membrane and block the intracellular action of AAPH [57]. Such compounds also have a protective effect on subcellular structures, proteins and DNA and can, thus, block pathological phenomena caused by oxidative stress [58]. Generally, the prooxidant action of peroxyl radicals generated by AAPH is blocked by compounds with hydroxyl groups that are capable of neutralizing and stabilizing the formed radicals [59].

Conclusions
In the present study, AgNPs were obtained via a simple and eco-friendly method, using a robust design, namely the Taguchi method, in order to identify the optimal synthesis parameters, which was achieved, for the first time, for such nanoparticles. AgNPs were successfully synthesized using AgNO 3 as a precursor and an L. salicaria extract as a reducing and capping agent, as demonstrated by FTIR analysis, which also revealed the functional groups found in the extract that are responsible for the obtaining of AgNPs. Moreover, the synthesis was confirmed through the presence of the SPR band, by both visual observation of color change and UV-Vis spectroscopy. The presence of silver was highlighted by EDX analysis, and the negative zeta potential indicated a stable AgNPs colloidal solution. The formed nanoparticles showed antimicrobial activity against S. aureus and C. albicans. The novelty of the research consisted of, besides establishing the optimal reaction conditions using the Taguchi design, testing the antioxidant activity through inhibition of lipoxygenase and peroxyl radical-mediated hemolysis, which showed promising results for the formed nanoparticles, as well as for MBC testing. Therefore, further studies are justified, with the synthesized AgNPs being potential resources for nanotechnological applications.