Depressing Iron Mineral by Metallic-Starch Complex ( MSC ) in Reverse Flotation and Its Mechanism

A series of metallic-starch complex (MSC) solutions, synthesized by mixing relevant metallic ionic solutions with the caustic starch solution, were used as the flotation depressants to investigate their depressing effects on hematite ore. The MSC is a nano-sized colloidal complex which is configured by hydrophilic metallic hydroxide as the colloidal nucleus on which starch and hydroxyl complex are adsorbed, resulting in a larger molecule than starch itself. The flotation tests showed that the depressing abilities of various MSC (Fe3+, Zn2+, Pb2+ and Mg2+) on the iron minerals were higher than the caustic starch, and the order of depression ability was: Zn2+-starch > Pb2+-starch > Fe3+-starch > Mg2+-starch > caustic starch. Based on the adsorption analysis, the high depressing ability of the MSC arose from increasing the adsorption density of starch on iron minerals and slightly reducing the absorption of the collector dodecylamine. Adsorption behaviour also indicated that the adsorption of the MSC on mineral surfaces was thicker than the caustic starch, and among various MSC the adsorption of Fe3+-starch exhibited the thickest adsorption layer while that of Mg2+-starch the thinnest. Zeta potential indicated that with a weaker electronegativity than the caustic starch, MSC adsorbed onto iron minerals more easily, and the strong electrostatic adsorption with the aid of the hydrogen bonding and chemisorption agreed well with the high depressing ability of the MSC.


Introduction
As to flotation of iron ores, much attention is attached to the reverse flotation as a significant commercial separation process using polysaccharide as the depressant for iron minerals and amine as the collector for silica [1,2].Starch and its derivatives are widely used for depressing iron minerals in flotation due to their widespread source and low cost.In principle, starch usually adsorbs onto iron minerals via its active groups forming hydrophilic films, producing its depressing effect on the iron minerals [3].Furthermore, Xia et al. [4] reported that hydrogen bonding adsorption is considered as a universal adsorption model for starch in the depressing process of the reverse flotation.
There are two main types of starch; amylopectin and amylose.The amylopectin starch usually produces strong depression on the flotation [5,6], and specially exhibits better depressing action on iron minerals.However, starch as the depressant for fine iron minerals is consumed too much due to high specific surface areas of fines.In order to strengthen the adsorption of starch on iron minerals and reduce its consumption in flotation, starch has been modified through different techniques [7,8], such as various chemical, physical, and compound modifications, etc.Among them, the chemical modification is one of the most widely used modification methods, and so are their modified products, such as dextrin, carboxyl methyl starch, the oxidized starch, and phosphate ester starch.These modified starches have been widely reported only for laboratory studies, but industrially caustic starch has been widely applied in the reverse flotation of iron ore [9][10][11][12].In fact, the causticization technique, on one hand, is to prepare the caustic starch by conditioning the starch with some alkali solution [13,14]; on the other hand, mixtures of carboxylic acids were found in the caustic starch [15].So besides the hydroxyl groups, the existence of active carboxylic groups could further facilitate the adsorption of starch onto iron minerals and metallic hydroxide colloids concerned in this study.
There are various active groups in caustic starch.Therefore, some new techniques derived from caustic starch could be introduced into the reverse flotation for iron ores.Yue and Wu [16] recently claimed a marked technique called as "magnetic seeding depression (MSD)" for fine flotation, i.e., adding organic depressant (such as caustic starch) and magnetic seeds and applying a low field intensity pre-magnetization for depressing target minerals in the reverse flotation.This technique was reported to have a strong depressing ability in flotation of hematite ore slimes via the chemical interactions between the magnetic seeds and caustic starch, along with the magnetic interactions between the magnetic seeds and minerals, might be also named as a compound depressor (magnetic starch).In view of this, Wu [17,18] patented a new series of depressants based on the caustic starch composed of metallic hydroxide colloids and starch, known as the metallic-starch complex (MSC) solutions.As a type of nano-sized colloid, MSC synthesized by mixing relevant metallic ionic solutions with the caustic starch solution, could be used as the flotation depressant for iron minerals, producing efficient depressing ability on target minerals with a relatively low consumption of starch.In this study, the flotation of hematite ore in the presence of the metallic-starch complex (MSC) solution was investigated and the mechanism of the strong depression was studied via various measurements.

Materials
The sample (86.34% less than 74 µm) used for flotation tests and adsorption analysis was obtained from an iron ore mine in Shandong province, China, and contained 51.55% Fe (Total), 69.06% hematite, and 19.35% SiO 2 respectively.Pure hematite (containing 98.02% hematite) with an average size of 17.11 µm was obtained from an iron ore mine by high-intensity magnetic separation and gravity separation, being mostly used for the mechanism analysis.
Caustic starch was conditioned with a ratio of 4 parts starch (potato starch, commercial product) to 1 part sodium hydroxide by using deionized water and boiling the mixture for about 20 min while stirring in the atmosphere.The solution, so-called "caustic starch", was prepared as a 0.02 g/mL concentration (pH 13.27) for use.In flotation the dodecylamine (DDA, CH 3 (CH 2 ) 11 NH 2 > 99.7% purity) was prepared into a solution of 0.05 g/mL concentration.The DDA solution (used as the collector) with a 1:1 mole ratio of dodecylamine to acetic acid was conditioned in the deionized water by stirring for certain time.
Metallic-starch complex (MSC) solution [17,18] was synthesized by mixing the 0.02 g/mL caustic starch solution mentioned above with relevant metallic ionic solution (such as Fe 3+ , Zn 2+ , Pb 2+ and Mg 2+ ions), using corresponding soluble salts of FeCl   O, respectively.Then, the mixture conditioned with a ratio of 1 part soluble salt to 2 parts starch was maintained at 20 • C and pH 13.27 while stirring for about 20 min.Therefore, the starch in the MSC solution can be calculated as a 0.013 g/mL concentration here.Finally, the suspension (a nano-sized colloid, as confirmed in Table 1) with good dispersion was obtained for use.

Reverse Cationic Flotation Tests
For each test sample, 180 g hematite ore sample was dispersed with tap water and conditioned for 3 min in a 0.5 L flotation cell with the pulp of 28.13% solids by weight, and stirred for 5 min after adding moderate depressant.Following the depressant (using caustic starch or the MSC here), collector of dodecylamine (DDA) was introduced into the pulp and conditioned for 3 min.Then, the reverse flotation test was carried out.Finally, the target mineral hematite was depressed as a sink product, and the flotation recovery was calculated from the assaying results.

Total Organic Carbon (TOC) Analyses for Adsorption
In order to determine the amount of starch adsorption onto the particles, the supernatant solutions after conditioning the pulp with the reagents for some time according to the flotation tests were further centrifuged by a general laboratory centrifuge equipment.Then, a 25 mL aliquot of the supernatant in the centrifuge tube was taken for TOC analysis.Finally, the adsorption amount was calculated according to the residual and initial carbon concentration in the solution, as presented in Equation ( 1) for starch and Equation (2) for DDA, respectively.
where Γ represents the adsorption amount (mg/g), C is or C iD is the initial concentration (mg/L) of the starch (432 mg/L) or DDA (225 mg/L) added in the suspension, C OS or C OD is the concentration (mg/L) of the initial starch (2 × 10 4 mg/L) or DDA (5 × 10 4 mg/L) solution, C TS or C TD is related to the TOC analysis value (mg/L) of the centrifugal supernatant after the conditioning with the starch or DDA, C CS or C DDA (mg/L) is regarded as the TOC analysis value of the initial starch or DDA solution, M (g/L) refers to the concentration of hematite ore sample (actual value is about 360 g/L).

Adsorption Behaviour of the Metallic-Starch Complex (MSC) on Minerals
The adsorption behaviour study of the metallic-starch complex (MSC) on mica surface was scanned by a Multimode SPM Atomic Force Microscope (AFM) via the Tapping Mode, combined with the Contact Mode.Prior to the measurements, a 120 mg/L concentration of the MSC solution was prepared firstly, and then a fresh mica plate was placed in the solution for 30 min.Finally, the mica plate conditioned with the MSC was blow-dried slightly by the nitrogen and measured by the AFM.

Zeta Potential Measurements
Zeta potentials of hematite and the hematite in the presence of the MSC were measured using a Coulter Delsa-440SX zeta potential analyzer (Brookhaven Corporation, Long Island, NY, USA).To prepare samples for analyses, 0.03 g pure hematite (less than 5 µm) was dispersed in a 50 mL 10 −3 mol/L KCl solution by an ultrasonic cleaner, and then stirred at room temperature for 2 min.Then, the reagents were added to the suspension.The mixed suspension was conditioned for 20 min for pH adjustment using HCl or NaOH.Finally, the equilibrium pH was recorded, and a small aliquot of the supernatant in the suspension was transferred to the sample cell of the analyzer for zeta potential measurements, and the average potential values were recorded.In addition, the MSC depressant itself with its concentration of 0.013 g/mL was also analyzed for zeta potentials after pH adjustment.

Fourier Transform Infrared Spectroscopic (FTIR) and X-ray Diffraction (XRD) Studies
To study the adsorption characteristics of the MSC and hematite-MSC, the FTIR analysis of the samples was measured via the transmission method using an IRAffinity-1 spectrometer (Shimadzu Corporation, Kyoto, Japan).Firstly, the pure hematite (−2 µm) was conditioned with the MSC solution in a thermostatic shaker for 20 min at 25 • C.Then, a small part of the suspension was collected for centrifugation, and the precipitate was dried at 55 • C using a vacuum drying oven, and was used for the FTIR analysis.In addition, to understand the characteristics of the MSC, the X-ray diffraction (XRD) studies along with the FTIR measurements of the MSC were performed by crystallizing the MSC solution directly at 55 • C, and then the crystal was ground to less than 5 µm for measurements.

Characterization of the Metallic-Starch Complex (MSC)
Based on the preparation method of the MSC, it can be inferred that metallic ions (Fe 3+ , Zn 2+ , Pb 2+ and Mg 2+ ) could be transformed into corresponding hydrophilic metallic hydroxides and hydroxyl complexes under the strong alkali condition (pH > 13).In order to characterize the MSC, X-ray diffraction, FTIR, turbidity analysis, and nano-particle size testing techniques were used to understand the properties of metallic starch complexes (MSC).
Figure 1 shows the XRD spectra of the MSC and caustic starch.It can be seen that the caustic starch presents an amorphous state.In the Fe 3+ -starch spectrum the diffraction peaks nearing 26.78 • and 55.95 • can be attributed to the characteristic of β-FeOOH [19], indicating the presence of β-FeOOH crystal structure in the Fe 3+ -starch.Then, in the spectrum of Pb 2+ -starch, the characteristic diffraction peak of (PbCO 3 ) 2 •Pb(OH) 2 and the peak of Pb 2 O 3 were observed at 34.18 • , 26.78 • and 55.95 • , respectively, and these might be due to the decomposition of Pb(OH) 2 and its reaction with CO 2 during the crystallization of the Pb 2+ -starch.However, there are no characteristic peaks of Zn(OH) 2 found in the Zn 2+ -starch spectrum; only two characteristic peaks at 36.25 • and 36.53 • of ZnO were observed.Finally, it was found in the Mg 2+ -starch spectrum, the bands around 38.04 • and 58.76 • can be assigned as the characteristics of Mg(OH) 2 , and MgCO 3 was confirmed at 33.15 • and 46.53 • .These suggested that some metal oxides or carbonates were created during the crystallization of the MSC, indirectly reflecting the possible presence of metallic hydroxides or hydroxyl complexes in the MSC.crystallizing the MSC solution directly at 55 °C, and then the crystal was ground to less than 5 µm for measurements.

Characterization of the Metallic-Starch Complex (MSC)
Based on the preparation method of the MSC, it can be inferred that metallic ions (Fe 3+ , Zn 2+ , Pb 2+ and Mg 2+ ) could be transformed into corresponding hydrophilic metallic hydroxides and hydroxyl complexes under the strong alkali condition (pH > 13).In order to characterize the MSC, X-ray diffraction, FTIR, turbidity analysis, and nano-particle size testing techniques were used to understand the properties of metallic starch complexes (MSC).
Figure 1 shows the XRD spectra of the MSC and caustic starch.It can be seen that the caustic starch presents an amorphous state.In the Fe 3+ -starch spectrum the diffraction peaks nearing 26.78° and 55.95° can be attributed to the characteristic of β-FeOOH [19], indicating the presence of β-FeOOH crystal structure in the Fe 3+ -starch.Then, in the spectrum of Pb 2+ -starch, the characteristic diffraction peak of (PbCO3)2•Pb(OH)2 and the peak of Pb2O3 were observed at 34.18°, 26.78° and 55.95°, respectively, and these might be due to the decomposition of Pb(OH)2 and its reaction with CO2 during the crystallization of the Pb 2+ -starch.However, there are no characteristic peaks of Zn(OH)2 found in the Zn 2+ -starch spectrum; only two characteristic peaks at 36.25°and 36.53° of ZnO were observed.Finally, it was found in the Mg 2+ -starch spectrum, the bands around 38.04° and 58.76° can be assigned as the characteristics of Mg(OH)2, and MgCO3 was confirmed at 33.15° and 46.53°.These suggested that some metal oxides or carbonates were created during the crystallization of the MSC, indirectly reflecting the possible presence of metallic hydroxides or hydroxyl complexes in the MSC. Figure 2 presents the FTIR result of the Fe 3+ -starch.It can be inferred that peaks at 1645 cm −1 and 1016 cm −1 can be assigned as the C=O stretching vibration and the O-H bending vibration, respectively, and the bands around 1160 cm −1 and 1081 cm −1 are attributed to the C-O stretching vibration, demonstrating the characteristics of starch.Then, the peak of Fe-O stretching vibration [10], which was found at 905 cm −1 , might be due to the adsorption band of β-FeOOH [20].Meanwhile, in contrast to the FTIR spectrum of Fe(OH)3 colloids seen in Figure 2, it was found that the Fe(OH)3 could not represent the characteristic component of the Fe 3+ -starch.These highlighted the presence of the hydrophilic metallic hydroxide (β-FeOOH) which agreed with the XRD results in Figure 1.[10], which was found at 905 cm −1 , might be due to the adsorption band of β-FeOOH [20].Meanwhile, in contrast to the FTIR spectrum of Fe(OH) 3 colloids seen in Figure 2, it was found that the Fe(OH) 3 could not represent the characteristic component of the Fe 3+ -starch.These highlighted the presence of the hydrophilic metallic hydroxide (β-FeOOH) which agreed with the XRD results in Figure 1.       1, MSC exhibits a larger size than the caustic starch, and the size (1-1000 nm) order of them could be given as follows: Mg 2+ -starch > Zn 2+ -starch > Pb 2+ -starch > Fe 3+ -starch > caustic starch.Meanwhile, the low turbidity of the MSC reveals a high degree of dispersion as a stable solution (or colloid).1, MSC exhibits a larger size than the caustic starch, and the size (1-1000 nm) order of them could be given as follows: Mg 2+ -starch > Zn 2+ -starch > Pb 2+ -starch > Fe 3+ -starch > caustic starch.Meanwhile, the low turbidity of the MSC reveals a high degree of dispersion as a stable solution (or colloid).Based on the analyses mentioned above, a molecular model could be proposed as follows.To take the Fe 3+ -starch as an example, starch molecules adsorbed initially on the colloid nucleus (β-FeOOH), resulting in a stable "compound molecule" composed of the nucleus and covering of hydrophilic metallic hydroxyl complexes, together with the starch molecules.The colloid nucleus exhibited a low concentration of FeO + ions on its surface at low alkali pH, and then grew into a larger nucleus at high alkali pH.Therefore, some OH-and starch molecules would adsorb into the stern layer of the colloid nucleus, forming a "large starch molecule", surprisingly leading to a particular adsorption effect on iron particles with the aid of the bridging adsorption of the starch and the H-bonding adsorption of the hydrophilic metallic hydroxyl complexes.The proposed model of the MSC (Fe 3+ -starch) is given in Figure 4.

Reverse Cationic Flotation Tests
The effects of the metallic-starch complex (MSC) on the flotation performance of hematite ore were investigated at 625 g/t DDA, and the results are seen in Figure 5 and Table 2.
Figure 5 and Table 2 indicated that the flotation recovery of iron minerals increased with the increasing depressant dosage, but the iron recovery of depressant MSC was obviously higher than the caustic starch while adding the same concentration of starch.The flotation recovery using MSC as the depressant was slightly better than that using the same dosage of caustic starch, demonstrating the depressing ability of MSC (Fe 3+ , Zn 2+ , Pb 2+ and Mg 2+ ) on the iron minerals were higher than the caustic starch, and amongst them, the order of depressing ability was summarized as: Zn 2+ -starch > Pb 2+ -starch > Fe 3+ -starch > Mg 2+ -starch > caustic starch.In addition, it was also found that the Fe 3+ -starch displayed the best flotation selectivity among the MSC depressors.

Adsorption Amount of Reagents onto Iron Minerals in Flotation
Measurements of the adsorption amount of depressant and collector onto mineral particles in flotation pulp were carried out, and the results are presented in Table 3.  3 shows that the MSC adsorbed more on the particles than the caustic starch while slightly reducing the absorption of the collector (DDA), and among them, the Fe 3+ -starch exhibited a high adsorption of starch and relatively low adsorption of DDA.It can be also inferred that the adsorption abilities of the MSC agreed well with the flotation results in Table 2. Therefore, based on the adsorption analysis, it was confirmed that the MSC produced a high depressing ability through increasing the adsorption amount of starch on iron minerals and slightly reducing the absorption of the collector.

Adsorption Characteristics of the MSC onto Mica
Figure 6 shows the adsorption behaviour of various MSC on mica surface.It can be seen from Figure 6a that the adsorption effect of the caustic starch was especially weak on the mica surface with a sparse adsorption layer of only 5 nm.However, the Fe 3+ -starch exhibits up to 50 nm thick and a uniform adsorption layer in Figure 6b.In addition, Figure 6c shows the adsorption behaviour of Zn 2+starch onto mica with a moderate adsorption of 10-15 nm thickness, and in Figure 6d,e both the Pb 2+starch and Mg 2+ -starch display the adsorption coverage with about 10 nm thickness on the mica surface.

Adsorption Amount of Reagents onto Iron Minerals in Flotation
Measurements of the adsorption amount of depressant and collector onto mineral particles in flotation pulp were carried out, and the results are presented in Table 3. Table 3 shows that the MSC adsorbed more on the particles than the caustic starch while slightly reducing the absorption of the collector (DDA), and among them, the Fe 3+ -starch exhibited a high adsorption of starch and relatively low adsorption of DDA.It can be also inferred that the adsorption abilities of the MSC agreed well with the flotation results in Table 2. Therefore, based on the adsorption analysis, it was confirmed that the MSC produced a high depressing ability through increasing the adsorption amount of starch on iron minerals and slightly reducing the absorption of the collector.

Adsorption Characteristics of the MSC onto Mica
Figure 6 shows the adsorption behaviour of various MSC on mica surface.It can be seen from Figure 6a that the adsorption effect of the caustic starch was especially weak on the mica surface with a sparse adsorption layer of only 5 nm.However, the Fe 3+ -starch exhibits up to 50 nm thick and a uniform adsorption layer in Figure 6b.In addition, Figure 6c shows the adsorption behaviour of Zn 2+ -starch onto mica with a moderate adsorption of 10-15 nm thickness, and in Figure 6d,e both the Pb 2+ -starch and Mg 2+ -starch display the adsorption coverage with about 10 nm thickness on the mica surface.It could be demonstrated that all the depressants of the MSC created a higher adsorption thickness on the minerals than the caustic starch, and especially the Fe 3+ -starch displayed a thicker and smoother adsorption coverage than the other MSC.Therefore, the adsorption difference of the MSC from the traditional caustic starch could partly explain the flotation depressing gap between the two.It could be demonstrated that all the depressants of the MSC created a higher adsorption thickness on the minerals than the caustic starch, and especially the Fe 3+ -starch displayed a thicker and smoother adsorption coverage than the other MSC.Therefore, the adsorption difference of the MSC from the traditional caustic starch could partly explain the flotation depressing gap between the two.

Zeta Potential Measurements
Zeta potential measurements of the MSC and hematite in the presence of the MSC were carried out, and the results are shown in Figures 7 and 8, respectively.
As shown in Figure 7, both the MSC and caustic starch were negatively charged at neutral and alkali pH, but the MSC presents a weaker electronegativity than the caustic starch at the same pH value, and amongst the results of the MSC, the Fe 3+ -starch exhibits the lowest negative charge while the Zn 2+ -starch displays the largest negative charge.Therefore, it can be also revealed that the MSC (especially the Fe 3+ -starch) could adsorb onto iron minerals more easily than the caustic starch while in some cases iron minerals were negatively charged.Figure 8 found that the iso-electric point (iep) of hematite is around pH 6.5 and the hematite has a negative potential at neutral and alkali pH.Meanwhile, the absolute value of hematite potential was raised after adding a certain concentration of caustic starch, however, was weaker by using the Fe 3+ -starch.In this case, therefore, the adsorption of Fe 3+ -starch on hematite could facilitate agglomeration of particles more easily than the caustic starch, resulting in a good flotation effect.

Zeta Potential Measurements
Zeta potential measurements of the MSC and hematite in the presence of the MSC were carried out, and the results are shown in Figures 7 and 8, respectively.
As shown in Figure 7, both the MSC and caustic starch were negatively charged at neutral and alkali pH, but the MSC presents a weaker electronegativity than the caustic starch at the same pH value, and amongst the results of the MSC, the Fe 3+ -starch exhibits the lowest negative charge while the Zn 2+ -starch displays the largest negative charge.Therefore, it can be also revealed that the MSC (especially the Fe 3+ -starch) could adsorb onto iron minerals more easily than the caustic starch while in some cases iron minerals were negatively charged.Figure 8 found that the iso-electric point (iep) of hematite is around pH 6.5 and the hematite has a negative potential at neutral and alkali pH.Meanwhile, the absolute value of hematite potential was raised after adding a certain concentration of caustic starch, however, was weaker by using the Fe 3+ -starch.In this case, therefore, the adsorption of Fe 3+ -starch on hematite could facilitate agglomeration of particles more easily than the caustic starch, resulting in a good flotation effect.

Zeta Potential Measurements
Zeta potential measurements of the MSC and hematite in the presence of the MSC were carried out, and the results are shown in Figures 7 and 8, respectively.
As shown in Figure 7, both the MSC and caustic starch were negatively charged at neutral and alkali pH, but the MSC presents a weaker electronegativity than the caustic starch at the same pH value, and amongst the results of the MSC, the Fe 3+ -starch exhibits the lowest negative charge while the Zn 2+ -starch displays the largest negative charge.Therefore, it can be also revealed that the MSC (especially the Fe 3+ -starch) could adsorb onto iron minerals more easily than the caustic starch while in some cases iron minerals were negatively charged.Figure 8 found that the iso-electric point (iep) of hematite is around pH 6.5 and the hematite has a negative potential at neutral and alkali pH.Meanwhile, the absolute value of hematite potential was raised after adding a certain concentration of caustic starch, however, was weaker by using the Fe 3+ -starch.In this case, therefore, the adsorption of Fe 3+ -starch on hematite could facilitate agglomeration of particles more easily than the caustic starch, resulting in a good flotation effect.3.6.FTIR Spectra of the Hematite Conditioned with the MSC (Fe 3+ -Starch) Figure 9 shows the FTIR spectra of hematite in the presence of the MSC (Fe 3+ -starch).It can be observed in the spectrum of hematite conditioned with the Fe 3+ -starch that the adsorption peak around 1031 cm −1 is due to the C-O stretching and C-OH bending vibration, and the small adsorption at 1070 cm −1 can be attributed to the C-H bending vibration, and then the COO − asymmetric and symmetric stretching bands [10] are also found nearing 1625 cm −1 and 1404 cm −1 .The band at 3420 cm −1 can be considered as the stretching vibration of O-H group, suggesting the presence of hydrogen adsorption on the hematite.In addition, the adsorption bands around 561 cm −1 and 467 cm −1 are shifted to 538 cm −1 and 457 cm −1 , respectively, indicating the hematite-starch interaction.Therefore, the Fe 3+ -starch absorbed onto the hematite through the hydrogen bonding adsorption and chemisorption, however, the adsorption characteristic of β-FeOOH in that spectrum was not found at 905 cm −1 probably due to its low concentration in the mixture of the hematite-Fe 3+ starch.Figure 9 shows the FTIR spectra of hematite in the presence of the MSC (Fe 3+ -starch).It can be observed in the spectrum of hematite conditioned with the Fe 3+ -starch that the adsorption peak around 1031 cm −1 is due to the C-O stretching and C-OH bending vibration, and the small adsorption at 1070 cm −1 can be attributed to the C-H bending vibration, and then the COO − asymmetric and symmetric stretching bands [10] are also found nearing 1625 cm −1 and 1404 cm −1 .The band at 3420 cm −1 can be considered as the stretching vibration of O-H group, suggesting the presence of hydrogen adsorption on the hematite.In addition, the adsorption bands around 561 cm −1 and 467 cm −1 are shifted to 538 cm −1 and 457 cm −1 , respectively, indicating the hematite-starch interaction.Therefore, the Fe 3+ -starch absorbed onto the hematite through the hydrogen bonding adsorption and chemisorption, however, the adsorption characteristic of β-FeOOH in that spectrum was not found at 905 cm −1 probably due to its low concentration in the mixture of the hematite-Fe 3+ starch.

Conclusions
The MSC is a type of nano-sized colloidal complex which is configured by hydrophilic metallic hydroxide as the colloidal nucleus on which starch and hydroxyl complex are adsorbed, resulting in a larger molecule than starch itself.Amongst the MSC colloids, the Fe 3+ -starch presented its specific characteristics using β-FeOOH as the colloid nucleus while the other MSC colloid nuclei are synthesized by the corresponding metallic hydroxides (such as Pb(OH)2, Zn(OH)2 and Mg(OH)2).
MSC produced higher depressing ability on the flotation of iron ores than the caustic starch, and different types of the MSC showed some different depressing ability as follows: Zn 2+ -starch > Pb 2+starch > Fe 3+ -starch > Mg 2+ -starch > caustic starch, and the Fe 3+ -starch displayed the best flotation selectivity among the MSC depressors.
The high depressing ability of the MSC arose from increasing the adsorption density of starch on iron minerals and slightly reducing the absorption of the collector (DDA).All the MSC depressants created a thicker adsorption layer on the minerals than the caustic starch, and especially the adsorption of the Fe 3+ -starch displayed a thicker and smoother adsorption layer than the other MSC depressants.The strong adsorption ability of the MSC lies in the fact that the MSC exhibited a weaker electronegativity than the caustic starch, therefore leading to a better adsorption result of the starch onto iron minerals.In addition, the absolute value of hematite potential was raised after adding a certain concentration of caustic starch but it was, however, lowered by using the Fe 3+ -starch.

Conclusions
The MSC is a type of nano-sized colloidal complex which is configured by hydrophilic metallic hydroxide as the colloidal nucleus on which starch and hydroxyl complex are adsorbed, resulting in a larger molecule than starch itself.Amongst the MSC colloids, the Fe 3+ -starch presented its specific characteristics using β-FeOOH as the colloid nucleus while the other MSC colloid nuclei are synthesized by the corresponding metallic hydroxides (such as Pb(OH) 2 , Zn(OH) 2 and Mg(OH) 2 ).
MSC produced higher depressing ability on the flotation of iron ores than the caustic starch, and different types of the MSC showed some different depressing ability as follows: Zn 2+ -starch > Pb 2+ -starch > Fe 3+ -starch > Mg 2+ -starch > caustic starch, and the Fe 3+ -starch displayed the best flotation selectivity among the MSC depressors.
The high depressing ability of the MSC arose from increasing the adsorption density of starch on iron minerals and slightly reducing the absorption of the collector (DDA).All the MSC depressants created a thicker adsorption layer on the minerals than the caustic starch, and especially the adsorption of the Fe 3+ -starch displayed a thicker and smoother adsorption layer than the other MSC depressants.The strong adsorption ability of the MSC lies in the fact that the MSC exhibited a weaker electronegativity than the caustic starch, therefore leading to a better adsorption result of the starch onto iron minerals.In addition, the absolute value of hematite potential was raised after adding a certain concentration of caustic starch but it was, however, lowered by using the Fe 3+ -starch.

Figure 2
Figure2presents the FTIR result of the Fe 3+ -starch.It can be inferred that peaks at 1645 cm −1 and 1016 cm −1 can be assigned as the C=O stretching vibration and the O-H bending vibration, respectively, and the bands around 1160 cm −1 and 1081 cm −1 are attributed to the C-O stretching vibration, demonstrating the characteristics of starch.Then, the peak of Fe-O stretching vibration[10], which was found at 905 cm −1 , might be due to the adsorption band of β-FeOOH[20].Meanwhile, in contrast to the FTIR spectrum of Fe(OH) 3 colloids seen in Figure2, it was found that the Fe(OH) 3 could not represent the characteristic component of the Fe 3+ -starch.These highlighted the presence of the hydrophilic metallic hydroxide (β-FeOOH) which agreed with the XRD results in Figure1.

Figure 3 11 Figure 2 .
Figure 3 shows the FTIR spectra of the MSC.It is seen from the spectrum of Zn 2+ -starch that peaks of 475 cm −1 and 406 cm −1 can be attributed to the adsorption band of Zn-O [21], and bending vibrations of the hydroxyl of Zn(OH) 2 were found around the peak 1087 cm −1 , 1037 cm −1 and 768 cm −1 .Then, in the spectrum of Pb 2+ -starch the band nearing the 1382 cm −1 is the O-H bending vibration of the Pb(OH) 2 , and the stretching vibration of Pb-O can be also observed at 461 cm −1 .As shown in the Mg 2+ -starch spectrum, peaks of 565 cm −1 and 447 cm −1 can be considered as the adsorption band of Mg-O.Due to the high alkali pH of the MSC preparation, hydrophilic metallic hydroxides (such as Fe(OH) 3 or β-FeOOH, Zn(OH) 2 , Pb(OH) 2 and Mg(OH) 2 ) could be dissolved into corresponding hydrophilic metallic hydroxyl complexes on their surfaces (such as [Fe(OH) 4 ] − , [Zn(OH) 4 ] 2− , [Pb(OH) 4 ] 2− and [Mg(OH) 4 ] 2− ).

Figure 3
Figure 3 shows the FTIR spectra of the MSC.It is seen from the spectrum of Zn 2+ -starch that peaks of 475 cm −1 and 406 cm −1 can be attributed to the adsorption band of Zn-O [21], and bending vibrations of the hydroxyl of Zn(OH)2 were found around the peak 1087 cm −1 , 1037 cm −1 and 768 cm −1 .Then, in the spectrum of Pb 2+ -starch the band nearing the 1382 cm −1 is the O-H bending vibration of the Pb(OH)2, and the stretching vibration of Pb-O can be also observed at 461 cm −1 .As shown in the Mg 2+ -starch spectrum, peaks of 565 cm −1 and 447 cm −1 can be considered as the adsorption band of Mg-O.Due to the high alkali pH of the MSC preparation, hydrophilic metallic hydroxides (such as Fe(OH)3 or β-FeOOH, Zn(OH)2, Pb(OH)2 and Mg(OH)2) could be dissolved into corresponding hydrophilic metallic hydroxyl complexes on their surfaces (such as [Fe(OH)4] − , [Zn(OH)4] 2− , [Pb(OH)4] 2− and [Mg(OH)4] 2− ).

Figure 4 .
Figure 4.The proposed molecular model of the MSC (such as the Fe 3+ -starch).

Figure 5 .
Figure 5.Effect of depressant dosage on the floatation recovery at pH 7.5 (DDA 625 g/t).

Figure 5 .
Figure 5.Effect of depressant dosage on the floatation recovery at pH 7.5 (DDA 625 g/t).

Figure 7 .
Figure 7. Zeta potential of various depressants (0.013 g/mL) as a function of pH.

Figure 8 .
Figure 8. Zeta potential of hematite in the presence of the Fe 3+ -starch as a function of pH.

Figure 7 .
Figure 7. Zeta potential of various depressants (0.013 g/mL) as a function of pH.

Figure 7 .
Figure 7. Zeta potential of various depressants (0.013 g/mL) as a function of pH.

Figure 8 .
Figure 8. Zeta potential of hematite in the presence of the Fe 3+ -starch as a function of pH.Figure 8. Zeta potential of hematite in the presence of the Fe 3+ -starch as a function of pH.

Figure 8 .
Figure 8. Zeta potential of hematite in the presence of the Fe 3+ -starch as a function of pH.Figure 8. Zeta potential of hematite in the presence of the Fe 3+ -starch as a function of pH.

Table 1
listed the turbidity and size of the MSC.As shown in Table

Table 1
listed the turbidity and size of the MSC.As shown in Table

Table 1 .
Turbidity and average size of the MSC at pH 13.27 (NTU: Nephelometric Turbidity Unit).
Mass Recovery/% Grade Total Fe/%Recovery of Total Fe/%