Geochemistry and Mineralogy of the Clay-Type Ni-Laterite Deposit of San Felipe (Camagüey, Cuba)

: The Ni-laterite deposit at the San Felipe plateau, located 30 km northwest of Camagüey, in central Cuba, is the best example of a clay-type deposit in the Caribbean region. San Felipe resulted from the weathering of mantle peridotites of the Cretaceous Camagüey ophiolites. In this study, a geochemical and mineralogical characterization of two proﬁles (83 and 84) from the San Felipe deposit has been performed by XRF, ICP-MS, quantitative XRPD, oriented aggregate mount XRD, SEM, FE-SEM, and EMPA. Core 83, with a length of 23 m and drilled in the central part of the plateau, presents a notable concentration of cryptocrystalline quartz fragments and a rather poor content of NiO, averaging 0.87 wt.%. Core 84, which is 12 m long and drilled at the border of the plateau, lacks silica fragments and presents a higher NiO content, averaging 1.79 wt.%. The smectite structural formulae reveal that they evolve from trioctahedral to dioctahedral towards the top of the laterite proﬁles. Quantitative XRD analyses indicate that smectite is a dominant Ni-bearing phase, accompanied by serpentine and minor chlorite. Serpentine, as smectite, is enriched in the less soluble elements Fe 3+ , Al, and Ni towards the top of the proﬁles. Core 83 seems to have been affected by collapses and replenishments, whereas core 84 may have remained undisturbed.

Ni-laterites represent 70% of the world's Ni reserves and 60% of the world's current production [6,7].These deposits develop in humid climates during periods of low tectonic activity and in areas of moderate relief [1].There are many factors that may control the specific structure of each lateritic profile [8][9][10][11][12][13].However, the general structure of the profile is determined by the mobility of the different elements that are released by the hydrolysis of primary (and secondary) minerals.This structure consists broadly of a silicate-bearing saprolite horizon near the ultramafic protolith, topped by an oxide zone, separated by the so-called magnesium discontinuity [14].There are different classifications of nickel laterites depending on the morphology, lithology of the bedrock, degree of weathering, etc. [8,15]; although the most used one establishes three types of deposits according to the mineralogy of the dominant ore [16].The main hosts of Ni are iron oxyhydroxides, Minerals 2023, 13, 1281 2 of 23 concentrated in the oxide zone, in the oxide-type Ni-laterites; Ni-serpentine and garnierite found in the saprolite horizon of hydrous Mg silicate-type Ni-laterites; and smectites in clay-type Ni-laterites.A particularity of clay-type Ni-laterite deposits is that the Ni-bearing smectites are concentrated in a transition zone between the saprolite horizon and the oxide zone [16].
The San Felipe lateritic nickel deposit (Cuba) represents the best example of a clay-type Ni-laterite deposit in the Caribbean region, with current resources of 250 Mt at 1.43% Ni, 0.05% Co [26].Unfortunately, limited data on the San Felipe deposit exist and are mostly in Spanish [27][28][29][30][31]. Hence, in this work, the geochemistry and mineralogy of two Ni-laterite profiles of the San Felipe deposit have been revisited, placing special emphasis on the abundance, textures, and mineral chemistry of Ni-bearing phyllosilicates.

Geological Setting
The San Felipe deposit is located on the San Felipe plateau (in Spanish, Meseta de San Felipe), an erosional remnant near Camagüey city, with a total extension of 50 km 2 , a slight inclination from SSE to NNW, and with elevations between 140 and 190 masl.The San Felipe deposit is located at the north of the province of Camagüey, 30 km to the NW of the city of Camagüey, and 70 km SW of the city of Nuevitas (Figure 1a,b) [27][28][29][30][31].The current nickel resource of the San Felipe deposit is 250 Mt at 1.43% Ni and 0.05% Co [27].
The San Felipe weathering profile is developed on the serpentinized peridotite of the Camagüey ophiolitic massif (COM).This massif is part of the so-called Northern Cuban Ophiolitic Belt [32] and has been dated as early Cretaceous [33].These ultramafic bodies represent slices of oceanic lithosphere obducted onto the North American continental margin in the Latest Cretaceous to Late Eocene time during the collision between the volcanic arc of the Caribbean with Jurassic-Cretaceous passive margins (Figure 1c) [32,34].
Camagüey peridotites are essentially made up of mantle tectonites with subordinate gabbro sills and dykes.Mantle peridotites mainly consist of clinopyroxene-rich harzburgite, harzburgite, and minor dunite.Uplift exposed the peridotite bodies to laterization at the beginning of the Miocene [35].
dark red and yellowish-ocher colors (Figure 2a-d), with discrete centimeter-to metersized ferricrete and silica blocks (Figure 2e,f).In general, the weathering profile in San Felipe includes the following, from the bottom to the top: (i) ophiolitic peridotite parent rock; (ii) saprolite; (iii) clay zone (smectite > serpentine); (iv) ferruginous clay zone (Fe oxyhydroxides > smectite); (v) oxide zone (Figure 2b); (vi) ferricrete (Figure 2c,d) with free silica concretions [28].The latter is a characteristic feature of the San Felipe laterite profile (Figure 2e,f) [30,31].The San Felipe plateau was explored by the Asociación Económica Internacional Geominera S.A. and San Felipe Mining Ltd., in grids ranging from 1000 × 1000 m to 12.5 × 12.5 m in areas of special interest.The present study is based on two representative cores (named 83 and 84, Figure 1b).Since cores 83 and 84 represent a continuous sampling of the corresponding laterite profiles, they are going to be referred to as cores and profiles in this work equally.The textural characteristics of the hand samples are illustrated in Figure 3, and the distribution and thickness of the different units identified along the profiles are displayed in Figure 4. Core 83 was drilled in the central part of the plateau (Figure 1b), is 24 m in length, and can be divided into three horizons, from top to bottom [38]: (i) reddish oxide zone (1 m thick); (ii) reddish brown ferruginous saprolite (14 m); (iii) dark, greenish- The San Felipe plateau was explored by the Asociación Económica Internacional Geominera S.A. and San Felipe Mining Ltd., in grids ranging from 1000 × 1000 m to 12.5 × 12.5 m in areas of special interest.The present study is based on two representative cores (named 83 and 84, Figure 1b).Since cores 83 and 84 represent a continuous sampling of the corresponding laterite profiles, they are going to be referred to as cores and profiles in this work equally.The textural characteristics of the hand samples are illustrated in Figure 3, and the distribution and thickness of the different units identified along the profiles are displayed in Figure 4. Core 83 was drilled in the central part of the plateau (Figure 1b), is 24 m in length, and can be divided into three horizons, from top to bottom [38]: (i) reddish oxide zone (1 m thick); (ii) reddish brown ferruginous saprolite (14 m); (iii) dark, greenishbrown saprolite (9 m).Core 84 was drilled at the border of the plateau (Figure 1b), is 12 m in length, and consists of four horizons: (i) oxide zone (1 m); (ii) ferruginous saprolite (1 m); (iii) saprolite (8 m); and (iv) green, slightly weathered peridotite (2 m).The bedrock consists of a serpentinized clinopyroxene-rich peridotite, locally intruded by gabbros, but it was not sampled in either of the cores.As observed in Figure 3a,b, samples from higher levels are more porous and crumblier and contain goethitized nodules.Downward in the profile, samples become more compact (Figure 3a-c), and fractures with a green infilling are observed (Figure 3d,e).The ferruginous saprolite in profile 83 (Figure 3f) presents fragments of cryptocrystalline quartz aggregates.In core 84, samples from the saprolite at a depth of 7 m display fractured and porous fragments of the parent rock, surrounded and filled by brown-black Fe oxyhydroxide grains (Figure 3g).At the bottom, the slight weathering on serpentinized peridotite (sample 84-12) provides a dark green to the rock (Figure 3h).consists of a serpentinized clinopyroxene-rich peridotite, locally intruded by gabbros, but it was not sampled in either of the cores.As observed in Figure 3a,b, samples from higher levels are more porous and crumblier and contain goethitized nodules.Downward in the profile, samples become more compact (Figure 3a-c), and fractures with a green infilling are observed (Figure 3d,e).The ferruginous saprolite in profile 83 (Figure 3f) presents fragments of cryptocrystalline quartz aggregates.In core 84, samples from the saprolite at a depth of 7 m display fractured and porous fragments of the parent rock, surrounded and filled by brown-black Fe oxyhydroxide grains (Figure 3g).At the bottom, the slight weathering on serpentinized peridotite (sample 84-12) provides a dark green to the rock (Figure 3h).

Analytical Methods
Bulk-rock geochemical analyses on all samples (9 samples from core 83 and 12 samples from core 84) were performed at the Centro de Instrumentación Científica of the Universidad de Granada (CIC-UGR, Granada, Spain).Major element concentrations were obtained by X-ray fluorescence (XRF) spectrometry on glass beads using a Philips PV1404 spectrometer.Precision was better than ±1.5% for a concentration of 10 wt.%.Further details on the analytical technique can be found in [39].
Random powder X-ray diffraction (XRPD) and oriented aggregate mount X-ray diffraction (XRD, (air dry, ethylene glycol, and heated to 550 • C) analyses on all samples were obtained at Centres Científics i Tecnològics of the Universitat de Barcelona (CCiT-UB, Barcelona, Spain), in a PANalytical X'Pert PRO MPD Alpha1 powder diffractometer in Bragg-Brentano θ/2θ geometry of 240 mm of radius, nickel filtered Cu Kα1 radiation (λ = 1.5406Å), 45 kV, and 40 mA.The samples were scanned from 4 to 100 • (2θ) with a step size of 0.017 • and measuring time of 150 s per step, using an X'Celerator detector (active length = 2.122 • ).Mineral identification was facilitated by X'Pert Highscore search-match software using the powder diffraction database of the International Centre for Diffraction Data (ICDD).For the estimation of the relative amounts between identified mineral phases, the quantitative Rietveld analysis method [40] with the software Topas V4.2 [41] was used.
All the samples were embedded in epoxy resin, prepared as thin sections, and polished using non-aqueous fluids to prevent damage to mineral phases.The mineralogy and microtextural features of the thin sections were first examined with a Nikon Eclipse LV100 POL optical microscope (OM).The sections were later carbon coated and studied with an environmental scanning electron microscope (ESEM) Quanta 200 FEI, XTE 325/D8395, coupled with an energy dispersive X-ray spectrometer (EDS), and a JEOL JSM-7001F field emission SEM (FE-SEM), both equipped with secondary (SE) and backscattered electron (BSE) detectors, under 20 kV, at the CCiT-UB.

Major Elements Geochemistry
The major element compositions of both profiles and loss on ignition (LOI) data are given in Supplementary Material Table S1 and in Figure 4a,b as a function of depth.
The composition in terms of SiO 2 and Al 2 O 3 is similar in both profiles, with a decrease in SiO 2 and MgO, and an increase in Al 2 O 3 and Fe 2 O 3 to the top.The SiO 2 content in profile 83 is 45.4 wt.% at the base and 8.8 wt.% at the oxide horizon, with an anomalous abrupt increase to 84.2 wt.% at 15 m depth that is not observed in profile 84, where SiO 2 ranges from 44.5 to 32.2 wt.%.Aluminum ranges from 2.7 at the saprolite horizon to 13.0 wt.% Al 2 O 3 in profile 83 and 1.2 to 7.7 wt.% in profile 84.Iron is more abundant in profile 83 and varies from 33.6 wt.% to 63.3 wt.% Fe 2 O 3 , reaching maximum values at the oxide zone and the ferruginous saprolite, with remarkable contents in the saprolite and an abrupt decrease at 15 m depth (8.9 wt.%).The curves for SiO 2 and Fe 2 O 3 in profile 83 are almost symmetrical, indicating a strong negative correlation between them.In profile 84, Fe 2 O 3 increases continuously between 11.9 wt.% and 32 wt.% from the base to the top.Magnesium is more abundant in profile 84, from 29.9 wt.% MgO at the base to 4.8 wt.% at the top, and from 15.7 to 0.2 wt.% in profile 83.In core 84 there is an important increase in NiO at 6 m deep (3.6 wt.%).Nickel varies from 0.33 wt.% to 0.91 wt.% in profile 84 and from 0.44 wt.% to 0.83 wt.% in 83.Cobalt is below 0.05 wt.% CoO in core 83 and up to 0.18 wt.% CoO in core 84.The LOI presents an opposite behavior in each core, increasing towards the top in profile 83 (8.6 to 11.3 wt.%) with an abrupt decrease at 15 m (2.3 wt.%), and decreasing towards the top in profile 84 (10 to 5.2 wt.%).

Petrography
The base of core 84 is formed by a slightly weathered, serpentinized peridotite that does not preserve most of the primary mantle mineralogy.Despite that, under the OM some of the primary textures can be observed; olivine and pyroxene have been almost completely substituted by phyllosilicates and Fe oxides during serpentinization (Figure 5).Euhedral to subhedral sections of pyroxene grains of 1 mm in length have been altered to serpentine group minerals (lizardite and chrysotile) along cleavage planes, with thin, brown goethite discontinuous intergrowths (Figure 5a).There are fractures crosscutting the grains replaced by serpentine (Figure 5a,b).Pseudomorphs or voids left by olivine grains of about 0.2 mm in diameter are surrounded by minerals of the serpentine group (lizardite and chrysotile) and Fe oxide (magnetite/maghemite) small grains.Serpentine is regularly associated with micrometric-sized grains of magnetite distributed along fractures (Figure 5c).Cores of olivine grains are replaced by microcrystalline aggregates of needle-or platelet-shaped smectite (hereafter incipient smectite), which exhibit second-order interference colors (Figure 5c,d).
The original texture of the bedrock in the saprolite and the ferruginous saprolite is lost in both profiles (from 23 to 1 m depth in core 83 and from 9 to 1 m in core 84).This part of the profile is more porous and presents foliated and bent, green smectite crystals of more than 1 mm in length that leave elongated voids due to their cleavage.These crystals are the result of an almost complete substitution of the primary minerals, mainly pyroxene, by a secondary mineral of the smectite group (hereafter type I smectite), and in some areas by irregular phyllosilicate grains that appear dark red due to the presence of iron oxyhydroxides (sample 84-08, Figure 5e).Chlorite appears as a vein bridging between smectite grains (Figure 5f).Some samples of saprolite in profile 83 (15 m) have slightly different mineralogy, with irregular brown accumulations of Fe oxyhydroxides and slightly deformed angular fragments of botryoidal silica aggregates, of approximately 2 × 0.2 mm (Figure 5g).This texture may suggest that these fragments come from a silicified vein that collapsed.In the ferruginous saprolite, irregular green deformed grains of phyllosilicates (lizardite and type II smectite) up to 0.2 mm in length are surrounded by irregular brown Fe oxyhydroxide aggregates (sample 83-4, Figure 5h).
SEM images of a weathered peridotite sample reveal the texture of fractured, pseudomorphed olivine grains of about 1 mm in size wrapped by layers of serpentine and smectite or kerolite-type minerals with different average Z values (Figure 6a).Dissolution voids in the olivine cores are partially filled by disordered aggregates of incipient smectite platelets and Fe oxides (magnetite/maghemite) (Figure 6b).Original orthopyroxenes hosting clinopyroxene exsolution lamellae evolve to smectite at different rates, being the clinopyroxene exsolutions more quickly substituted (to incipient smectite) (Figure 6c).In addition, abundant Cr-spinel grains are present associated with pyroxene and may occur as euhedral octahedral crystals, anhedral crystals, or as inclusions in former pyroxene (Figure 6d).In the saprolite of core 84, needles and platelets of type I smectite have been observed (Figure 6e).In the porous ferruginous saprolite, bent tabular grains of serpentine (lizardite) contain cores of type II smectite (Figure 6f).Iron oxides occur as inclusions in serpentine or within fractures crosscutting serpentine in sample 83-22 (Figure 6g).Cr-spinel can also be found as fractured, isolated, and euhedral crystals substituted by Fe oxides (Figure 6h).
part of the profile is more porous and presents foliated and bent, green smectite crystals of more than 1 mm in length that leave elongated voids due to their cleavage.These crystals are the result of an almost complete substitution of the primary minerals, mainly pyroxene, by a secondary mineral of the smectite group (hereafter type I smectite), and in some areas by irregular phyllosilicate grains that appear dark red due to the presence of iron oxyhydroxides (sample 84-08, Figure 5e).Chlorite appears as a vein bridging between smectite grains (Figure 5f).Some samples of saprolite in profile 83 (15 m) have slightly different mineralogy, with irregular brown accumulations of Fe oxyhydroxides and slightly deformed angular fragments of botryoidal silica aggregates, of approximately 2 × 0.2 mm (Figure 5g).This texture may suggest that these fragments come from a silicified vein that collapsed.In the ferruginous saprolite, irregular green deformed grains of phyllosilicates (lizardite and type II smectite) up to 0.2 mm in length are surrounded by irregular brown Fe oxyhydroxide aggregates (sample 83-4, Figure 5h).

Mineral Chemistry
Our results show that type I smectites (found in the saprolite of core 84, Figure 5e) and type II smectites (in both cores 83 and 84, Figure 5f) display distinct compositions (Supplementary Material Table S2, Figure 7).
The average chemical composition of type I smectite in sample 84-09 (Figure 6), in the transition between the weathered peridotite and the saprolite horizon, is 43 [38] and formed as a substitution of olivine and pyroxene.
Serpentine in San Felipe can be divided, according to their Ni content, into low-Ni (socalled serpentine I) and Ni-enriched (serpentine II).The average composition of serpentine II grains in sample 84-7 (Figure 8d and Supplementary Material Table S3 S3, Figure 9).

Structure Characterization of Minerals by X-ray Diffraction (XRD)
The mineral phases identified in cores 83 and 84 and their relative amounts as a function of depth are given in Supplementary Material Table S4, and Figure 11 displays the XRPD of selected samples.The minerals identified are smectite, dehydrated or collapsed smectite (with a talc-like or kerolite-like structure), serpentine (lizardite and chrysotile), chlorite, quartz, hematite, goethite, maghemite, and Cr-spinel.As discussed later, quantification of nanometric-sized, hydrated phyllosilicates and, in particular, smectite and kerolite-like structures by Rietveld profile analysis is problematic [59][60][61].In sample 83-25, smectite presents an intense, broad, symmetric peak at 14.7 Å, and a kerolite faint wide reflection at 9.6 Å (Figure 8).However, at higher angles, both phases present almost coincident broad asymmetric hk diffraction bands, which are a typical feature of turbostratic structures [62].Accordingly, smectite and kerolite have been quantified together due to the similarity of their XRPD patterns.Whenever the smectite broad 14.7 Å peak is important, we will refer to possible mixtures of smectite/kerolite as "smectite".
In profile 83, smectite decreases from the base to the top (83.3 and 24.3 wt.%, respectively), and so does chlorite (4.3 at the base to 3.0 wt.% near the top).In contrast, lizardite decreases (0.3 wt.% at 25 m and 0.6 wt.% at 1 m).Profile 84 is dominated by smectite (74.0 to 17.3 wt.%) and serpentine (lizardite plus chrysotile) (24.6 wt.% at the bottom to 2.3 wt.% at the top).Near the middle of profile 83 (at 16 m depth), a highly silicified level appears, with more than 50 wt.%quartz.In core 84, quartz is less important, with only 18.2 wt.% at

Structure Characterization of Minerals by X-ray Diffraction (XRD)
The mineral phases identified in cores 83 and 84 and their relative amounts as a function of depth are given in Supplementary Material Table S4, and Figure 11 displays the XRPD of selected samples.The minerals identified are smectite, dehydrated or collapsed smectite (with a talc-like or kerolite-like structure), serpentine (lizardite and chrysotile), chlorite, quartz, hematite, goethite, maghemite, and Cr-spinel.As discussed later, quantification of nanometric-sized, hydrated phyllosilicates and, in particular, smectite and kerolite-like structures by Rietveld profile analysis is problematic [59][60][61].In sample 83-25, smectite presents an intense, broad, symmetric peak at 14.7 Å, and a kerolite faint wide reflection at 9.6 Å (Figure 8).However, at higher angles, both phases present almost coincident broad asymmetric hk diffraction bands, which are a typical feature of turbostratic structures [62].Accordingly, smectite and kerolite have been quantified together due to the similarity of their XRPD patterns.Whenever the smectite broad 14.7 Å peak is important, we will refer to possible mixtures of smectite/kerolite as "smectite".
hematite increase towards the top.Near the surface, the total amount of goethite and hematite is similar in both profiles (69.3 and 60.3 wt.%), but the percentage of goethite in core 83 doubles that of core 84.In Figure 12, the variation of the major mineral phases is represented as a function of depth.It is worth noting that smectite is always dominant along both profiles (Supplementary Material Table S4).In order to get further evidence on the presence of smectite, XRD of oriented aggregate mounts have been obtained for a sample of core 83 (83-7) and another of core 84 (84-12) (Figure 11a* and Figure 11c*, respectively).In sample 83-7, the symmetrical peak at d 001 = 14.7 Å corresponds to pure smectite with two water layers [63,64].After heating at 540 • C, the d 001 collapses to 9.9 Å.With ethylene glycol (EG), d 001 = 14.7 expands to 17.3 Å as symmetrical peaks, indicating a uniform swelling of almost all the layers without mixing with the non-swelling talc/kerolite layers [59] (Figure 11b).In sample 84-12, after heating at 540 • C, the d 001 collapses to 9.6 Å.With EG, d 001 = 14.3 expands to 17.0 Å as a symmetrical peak (Figure 12).

Degree of Weathering
The geochemical analyses (Figure 3) agree with the XRPD mineralogical composition (Supplementary Material Table S4, Figure 10).The SiO2 wt.% decreases in the two profiles in the ferruginous saprolite but in profile 83 there is an abrupt increase at 15 m deep that corresponds to the occurrence of cryptocrystalline quartz millimetric to centimetric fragments (Figure 5g).This interruption in the typical regular succession of horizons explains the observed differences between profiles 83 and 84 at this depth.The increase in silica is accompanied by a reduction of Al2O3, Fe2O3, MgO, NiO, and LOI (Figure 4a,b).
The ultramafic index of alteration (UMIA) is defined as an attempt to quantify and visualize the degree of weathering of an ultramafic rock (e.g., peridotites) [2]: The UMIA is different in the saprolite and ferruginous saprolite of the two cores.Profile 84 presents a regular succession of horizons characteristic of this type of laterite: oxide zone (UMIA = 51), ferruginous saprolite (UMIA = 39), saprolite (UMIA = 22 to 40), and slightly weathered serpentinized bedrock (UMIA = 15).The oxide zone is underdeveloped in the two cores, and the ferruginous saprolite horizon (UMIA = 41 to 60) is more developed in core 83 with an UMIA from 30 to 40.The saprolite horizons are similar in In profile 83, smectite decreases from the base to the top (83.3 and 24.3 wt.%, respectively), and so does chlorite (4.3 at the base to 3.0 wt.% near the top).In contrast, lizardite decreases (0.3 wt.% at 25 m and 0.6 wt.% at 1 m).Profile 84 is dominated by smectite (74.0 to 17.3 wt.%) and serpentine (lizardite plus chrysotile) (24.6 wt.% at the bottom to 2.3 wt.% at the top).Near the middle of profile 83 (at 16 m depth), a highly silicified level appears, with more than 50 wt.%quartz.In core 84, quartz is less important, with only 18.2 wt.% at the top.Magnetite/maghemite decreases from the base to the top, whereas goethite and hematite increase towards the top.Near the surface, the total amount of goethite and hematite is similar in both profiles (69.3 and 60.3 wt.%), but the percentage of goethite in core 83 doubles that of core 84.In Figure 12, the variation of the major mineral phases is represented as a function of depth.It is worth noting that smectite is always dominant along both profiles (Supplementary Material Table S4).

Degree of Weathering
The geochemical analyses (Figure 3) agree with the XRPD mineralogical composition (Supplementary Material Table S4, Figure 10).The SiO 2 wt.% decreases in the two profiles in the ferruginous saprolite but in profile 83 there is an abrupt increase at 15 m deep that corresponds to the occurrence of cryptocrystalline quartz millimetric to centimetric fragments (Figure 5g).This interruption in the typical regular succession of horizons explains the observed differences between profiles 83 and 84 at this depth.The increase in silica is accompanied by a reduction of Al 2 O 3 , Fe 2 O 3 , MgO, NiO, and LOI (Figure 4a,b).
The ultramafic index of alteration (UMIA) is defined as an attempt to quantify and visualize the degree of weathering of an ultramafic rock (e.g., peridotites) [2]: The UMIA is different in the saprolite and ferruginous saprolite of the two cores.Profile 84 presents a regular succession of horizons characteristic of this type of laterite: oxide zone (UMIA = 51), ferruginous saprolite (UMIA = 39), saprolite (UMIA = 22 to 40), and slightly weathered serpentinized bedrock (UMIA = 15).The oxide zone is underdeveloped in the two cores, and the ferruginous saprolite horizon (UMIA = 41 to 60) is more developed in core 83 with an UMIA from 30 to 40.The saprolite horizons are similar in both profiles, but the content in NiO is higher in 84.It must be noted that the total thickness of the saprolite horizon in core 83 is unknown.There are several factors that may lead to these differences, i.e., topography, position of the water table, drainage, local variations in the nature of the protolith, and degree of serpentinization.

Trioctahedral vs. Dioctahedral Smectites
Type I smectite, from the saprolite horizon, is trioctahedral in character (Supplementary Material Table S2) with a ratio between tetrahedral and octahedral cations of 1.26, near the ideal value of 1.33, and an octahedral occupancy of 2.99, where Mg is dominant.Its composition is intermediate between a saponite and nontronite and presents two types of textures: as random curved platelets filling cores of dissolved olivine (Figure 6b), and as pseudomorphs of pyroxene (Figure 6c).The octahedral occupation of Ni is <0.2.
Type II smectite is dioctahedral, close to nontronite, with a tetrahedral/octahedral ratio equal to 1.92 and an octahedral occupancy of 2.08, where Fe 3+ is dominant (Supplementary Material Table S2).This smectite appears in the ferruginous saprolite, very often as pseudomorphs of type II serpentine (Figure 6f).The occupancy of Ni is under 0.14.It appears that, towards the top, smectites become more stable by increasing their dioctahedral character.All smectites are very deficient in interlaminar cations (Ca and Na), suggesting that they could be mixed with kerolite.Smectites in samples with less goethite (and more magnetite/maghemite) (Supplementary Material Table S4) have higher Ni contents, which attain their maximum occupancy in the structure in the central part of the saprolite in core 84 (samples 84-7,6,5) (Figure 4b).The compositional variation of the smectites of San Felipe is similar to those of Murrin Murrin, described in [65].Similarly, a transition towards the top from a trioctahedral to a more dioctahedral coincides with the description of different weathering profiles developed in ultramafic rocks [24,65,66].

Type I Serpentine vs. Type II Serpentine
Two types of serpentine can also be distinguished.Type I, with low Ni and with excellent crystallinity, only appears surrounding pseudomorphed olivine grains in sample 84-12 (Figure 6b).The structural formula calculated by TEM in lizardite particles from this sample is (Mg 2.69 Fe 0.15 Ni 0.01 Si 2.02 O 5 (OH) 4 ) [38].Type II is a different generation of serpentine, less crystalline and with higher Ni contents (Supplementary Material Table S3), which coexists spatially with type II smectite in both profiles.The mean structural formula for type II serpentine in sample 84-6, (Mg 1.97 Fe 0.30 Ni 0.14 Al 0.13 )Si 2.09 O 5 (OH) 4 , can be considered a solid solution of the three end-members lizardite, Fe 2 SiO 5 (OH) 4 , and népouite, the latter two components being less soluble and stabilizing the serpentine as pore water becomes more acidic and oxidizing.As with smectites, Fe 3+ in serpentines increases towards the top.Type II serpentine may be the result of topotactic reactions that incorporate Ni and Fe in type I serpentine.For a complete discussion about the solubility and stability of Mg-Fe-Ni-serpentines in laterites, see [45].
Serpentine in profiles 83 and 84 includes the crystalline form of lizardite, which is dominant, together with less chrysotile in core 84.Most lizardite in the weathered peridotite is well crystallized, showing narrow diffraction peaks (Figure 11c).The mean crystallite size calculated in the refinement of the PXRD is estimated to be around 40 nm.In addition, a small incipient less crystalline fraction of lizardite with a crystallite size of 8 nm is also observed.

XRPD Interpretation of Smectite (vs. Kerolite-Type Structures)
The quantification of mineral phases by XRPD raises several relevant issues regarding the distribution of Ni among the different phyllosilicates present in the samples.The phyllosilicates sensu lato encountered in XRPD profiles are smectite, a kerolite-type structure, serpentine (lizardite plus chrysotile), and chlorite.The identification and quantification of the latter two through XRPD is simple since both phases are well crystallized.However, identifying and estimating the amount of smectite and/or a kerolite-type structure is more problematic because part of their diffractograms would coincide.Previous works [59,63] have shown that kerolite, and its Ni equivalent pimelite, occurs generally in association with weathered ultramafic rocks as coatings or vein infillings at the bottom of weathering profiles in association with serpentine.The authors of [23] have found that smectite and kerolite were almost always intimately associated with Ni-laterites resulting from the weathering of pyroxenites.Kerolite is often a ubiquitous poorly crystalline phase present in saprolites that can be associated either with a smectite or talc.Provided the lack of reliable published crystal structures of trioctahedral and dioctahedral smectites, they can only be included with precaution in the calculation of a powder diffraction file.On the contrary, the kerolite profile can be fitted well using the crystal structure of talc, as shown in Figure 11.As a result, it cannot be ascertained by XRPD which contribution to the turbostratic profile corresponds to smectite and which to kerolite, or even to a modified/dehydrated smectite, which could be an artifact produced during the powdering of the samples.The relative amount of smectite can be estimated by the 001 reflection, which is more important in the bottom of 83 than in 84.It is worth noting that the encountered smectites have a very low content of the interlaminar cations Na + and Ca 2+ , so their composition is close to a 2:1 dioctahedral or trioctahedral phyllosilicate.In particular, in the saprolite horizon of core 84, type I smectites with low Fe content approximate the composition of a talc-like structure.

Mineral Variations and Weathering Process across the Lateritic Profiles
Olivine and pyroxene relicts are absent in both profiles.The bulk composition of sample 84-12 (Supplementary Material Table S1) allows an approximate estimation of the mineral composition of the parent rock before serpentinization (and alteration of pyroxene).Assuming that only a small amount of Mg has been lost by the dissolution of a small amount of olivine, the Si/(Mg + Fe) molar ratio obtained from XRF is compatible with a peridotite-rich in orthopyroxene (~60% molar).Complete serpentinization of olivine would consume an equivalent amount of orthopyroxene (in molar units), leaving an important fraction of total pyroxene (~46% molar).Accordingly, the parent rock can be classified as an orthopyroxene-rich harzburgite.This remnant pyroxene is the base for the formation of new hydrated phases (smectite, kerolite).As weathering proceeds, part of the initial (hydrothermal, oceanic) serpentine (type I serpentine) will change its composition, incorporating Fe and Ni and becoming less soluble, while the remainder of serpentine will be dissolved incongruently, leaving some silica retained [45].This silica is needed for the formation of smectite and possibly chlorite.In profile 84, Mg is lost progressively, from the bottom to the top, and the Mg discontinuity between the saprolite horizon and the oxide zone is less sharp compared with other lateritic profiles worldwide [20,67].From the bottom to the top, the profile is enriched in the less soluble elements Fe, Al, and Cr.Excess silica forms quartz, while Fe forms goethite, hematite, and maghemite.Gibbsite has not been observed so it is concluded that Al has been incorporated in the iron oxides and oxyhydroxides.Indeed, goethite at the top of 83 and 84 contains a 10% mole fraction of the diaspore AlOOH component.In hematite from the same horizons, the mole fraction of corundum is only 5%.
It is worth noting that interstratified Ni clays have not been identified in San Felipe, unlike in Western Australia.According to the authors of [24], these interstratified clays formed post-laterization, during the onset of arid climate conditions in Australia.Therefore, there is no evidence of this in San Felipe.
Profile 84 follows a regular model of the formation of Ni-laterites in moderately tropical humid climates with marked dry seasons (1500 mm rainfall and 27 • C), after exposition to the surface for some million years [1,8,12].Initial weathering of serpentinized ultramafic rocks dissolves part of type I serpentine and incipient smectite pseudomorphing pyroxene, leaching Mg and, to a lesser extent, Si, downwards.Magnetite is oxidized to maghemite or to goethite.The latter is able to retain Ni somehow so that this element is not leached immediately [68].Goethite is the main mineral in the oxide zone.It may contain up to 2.7 wt.% NiO [31].Serpentine and smectite incorporate Fe 3+ and Ni that substitute Mg in the octahedral positions of both minerals.In this process, the more soluble Mg hydrous silicate component is substituted by the less soluble, which incorporates more Fe 3+ and Ni, so that the more soluble (more Mg, less Fe 3+ and Ni) appears below the less soluble in the profile.The rate at which the Ni retained initially by goethite is liberated, compared with the rate of its capture by the new hydrous silicates formed downwards, (incipient smectite → smectite I → smectite II; serpentine I → serpentine II) determines the content of Ni along the entire profile.
The bottom of profile 84 is poor in NiO (Supplementary Material Table S1, 0.33 wt.%, sample 84-12), and similar to the Ni content in peridotites [20].Supergene enrichment has not yet taken place significantly, with serpentines being formed in pre-weathering conditions.In the saprolite horizon, 85% of Ni is contained in type I smectite, and only 15% in serpentine.Serpentine (Supplementary Material Table S3) is enriched in Ni with respect to the same mineral at the base of the profile; however, its amount decreases towards the top, so that its contribution to nickel content near the top is only about 5 wt.%.Sample 84-12 represents the slightly weathered, serpentinized peridotite that, nevertheless, has been deeply altered in hydrothermal (oceanic) conditions prior to weathering.Olivine and pyroxene have completely been transformed to serpentine and smectite and/or kerolite before weathering.The initial transformation of enstatite to smectite is favored by the crystallographic similarities and the chain structure of the former, along its cleavage and exsolution planes [23,65], but needs some afford of silica, which possibly comes from the incongruent dissolution of part of the olivine.
The anomalous increase in serpentine and magnetite/maghemite or goethite near the top in both profiles (samples 83-6 and 84-4) may be due to floating blocks of bedrock that have been frequently detected by GPR (ground-penetrating radar) in the San Felipe formation [31].This is corroborated by correlation coefficients between serpentine and magnetite/maghemite or goethite for profiles 83 and 84, of 0.4 and 0.6, respectively.
It is worth noting that profile 84, from the border of the plateau, would represent an undisturbed profile that corresponds to the stationary development of regular horizons in the given lithologic and climatic conditions, and active drainage.On the contrary, profile 83, from the center of the plateau, presents fragmented microcrystalline quartz vein infillings and displays evidence of reworking along the profile.This would be a result of complex, not well-understood episodes of precipitation of silica-forming crusts, the collapse of part of the profile, and further replenishment downwards produced by active tectonics during the Pliocene [31,69].

Comparison of Smectites from Lateritic Profiles Worldwide
Supplementary Material Table S5 displays selected structural formulae of Ni-bearing smectites from Ni-laterite profiles worldwide.There are many differences between smectites based on: (i) the total layer charge and the distribution of this charge between the octahedral and the tetrahedral sheets; (ii) the Ni, Mg, and Fe content in the octahedral position; (iii) the origin, formed after olivine, or (ortho-and clino-) pyroxene or lizardite.These differences can be explained by the position of smectites in the lateritic profiles, and above all, the parent rock, topography, and climate.
The Ni-smectite from the pyroxenite of Niquelândia (Brazil) [65] is the richest in Ni (2.14 hafu and 2.71 cations in octahedral position), and the other two with remarkable Ni contents are those of Tagaung (Myanmar), and Falcondo (Dominican Republic) [25,55]: the sum of the octahedral cations being 1.8 and 1.75 hafu, and 2.71 or 3.06 cations in the octahedral position, respectively (Supplementary Material Table S5), confirming the trioctahedral character.Another smectite with dominant Ni in the octahedral position (1.03 hafu) is the one from the lower saprolite of Tagaung [55], but in this case, the sum of the octahedral cations is 2.43 (intermediate between trioctahedral and dioctahedral).Iron in the octahedral position is dominant in six smectites, two from Myanmar, three from Western Australia, and one from Cuba [38,52,55], the sum of the octahedral cations being between 2.01 and 2.27 hafu (Supplementary Material Table S5), confirming the dioctahedral character and a slight octahedral over-occupancy.Finally, Mg is the main octahedral cation in five smectites, two from the Western Ivory Coast [50], two from Western Australia [24,52], and two from Cuba [38].Four of them yield an octahedral cation sum between 3.06 and 2.86 hafu (trioctahedral character), and the other one is 2.26 hafu (dioctahedral character) (Supplementary Material Table S5).The smectite with the highest Mg in the octahedral position (1.82 hafu, 3.06 total occupancy, trioctahedral) is from serpentinized dunite and formed after olivine.
The highest Al is 0.71 hafu in the tetrahedral position and 0.25 Al hafu in the octahedral position in the trioctahedral smectite in the transition layer in the Western Ivory Coast [50].Iron is present in five samples in the tetrahedral position, three of them are the richest in Ni in the octahedral position (Brazil, Myanmar, Dominican Republic) [25,55,65].

Conclusions
The original mineral composition of the bedrock in the San Felipe Ni-laterite deposit is estimated to have a molar ratio between enstatite and forsterite of about 3.This mineral composition greatly influences the mineral evolution during weathering as well as the degree of supergene enrichment in Ni.
Smectite and serpentine incorporate Fe 3+ , Al, and Ni.For smectites, this represents a transformation from trioctahedral to dioctahedral character.Even if serpentine doubles the NiO content of smectite (~3.2 and ~1.5 wt.%, respectively), smectite is much more abundant in the saprolite, so this mineral contains about 80% of the total Ni, the remainder being located in serpentine.
Interlaminar cation content in smectites is very low, suggesting that part of the X-ray turbostratic profile observed is in fact an intermediate structure between kerolite and a collapsed smectite.
Profile 84 displays a regular succession of horizons of an ideal Ni-laterite profile.This regular succession is disrupted in profile 83 by a concentration of silica, which probably reveals a complex succession of events of collapse and replenishing of the area where the laterite was developed.
Finally, considering the Ni content, the abundance and nature of the ore (smectite and serpentine), and the current resources, the San Felipe deposit could be targeted for Ni, similar to other large Ni-laterite deposits in the Caribbean, such as Moa Bay, Cerro Matoso, and Falcondo.

Figure 1 .
Figure 1.(a) Location of the Camagüey ophiolite Massif in central Cuba.(b) Geographic location of cores 83 and 84 (yellow stars) in the San Felipe Ni-Co deposit in Camagüey Province, Cuba.Hillshaded DEM is based on the SRTM 30 m model [36].Contour lines represent elevations with 50 m intervals.Physiographic features are based on the naturalearthdata.comdatabase [37].Coordinate Reference System: EPSG:4326-WGS 84.(c) Simplified geological map of the study area indicating the San Felipe deposit [31].

Figure 1 .
Figure 1.(a) Location of the Camagüey ophiolite Massif in central Cuba.(b) Geographic location of cores 83 and 84 (yellow stars) in the San Felipe Ni-Co deposit in Camagüey Province, Cuba.Hillshaded DEM is based on the SRTM 30 m model [36].Contour lines represent elevations with 50 m intervals.Physiographic features are based on the naturalearthdata.comdatabase [37].Coordinate Reference System: EPSG:4326-WGS 84.(c) Simplified geological map of the study area indicating the San Felipe deposit [31].

Figure 2 .
Figure 2. Photos of the San Felipe Ni-laterite plateau.(a) General view at the top of the plateau, the material outcropping is of dark red color and is characterized by sparse, low vegetation.(b) Ocher to dark brown goethite and hematite concretion.(c,d) Centimeter-to meter-sized red blocks.(e) Amorphous silica or microcrystalline quartz decimeter-sized nodules, their internal translucent to opaque white appearance is shown in (f).

Figure 2 .
Figure 2. Photos of the San Felipe Ni-laterite plateau.(a) General view at the top of the plateau, the material outcropping is of dark red color and is characterized by sparse, low vegetation.(b) Ocher to dark brown goethite and hematite concretion.(c,d) Centimeter-to meter-sized red blocks.(e) Amorphous silica or microcrystalline quartz decimeter-sized nodules, their internal translucent to opaque white appearance is shown in (f).

Figure 3 .
Figure 3. (a) Photos of the samples from core 83 (sample depth in yellow).(b) Photos of samples from core 84 (sample depth in yellow).(c-h) Photos of hand specimens embedded in epoxy resin of the two studied cores: (c) sample 83-01 from the oxide zone; (d) sample 83-04 from the ferruginous saprolite; (e) sample 83-10 from the ferruginous saprolite, including green infillings in fractures; (f) sample 83-15 with cryptocrystalline quartz, from the ferruginous saprolite; (g) sample 84-07 from the saprolite; (h) sample 84-12 from the slightly weathered serpentinized peridotite.The scale for the six images is the same as in (a).The sample names are composed of the code of the core (83-or 84-) and a number that indicates the depth of the sample (e.g., "83-01" refers to the sample collected at 1 m from core 83).

Figure 3 .
Figure 3. (a) Photos of the samples from core 83 (sample depth in yellow).(b) Photos of samples from core 84 (sample depth in yellow).(c-h) Photos of hand specimens embedded in epoxy resin of the two studied cores: (c) sample 83-01 from the oxide zone; (d) sample 83-04 from the ferruginous saprolite; (e) sample 83-10 from the ferruginous saprolite, including green infillings in fractures; (f) sample 83-15 with cryptocrystalline quartz, from the ferruginous saprolite; (g) sample 84-07 from the saprolite; (h) sample 84-12 from the slightly weathered serpentinized peridotite.The scale for the six images is the same as in (a).The sample names are composed of the code of the core (83-or 84-) and a number that indicates the depth of the sample (e.g., "83-01" refers to the sample collected at 1 m from core 83).

Figure 5 .
Figure 5. Optical photomicrographs taken with plane polarized light (a,c,e,g,h) and crossed polars (b,d,f) of the characteristic textures of the main mineralogy in the San Felipe Ni-laterites: (a,b) py-

Figure 10 .
Figure 10.BSE photomicrograph (top left) and Si, Mg, Fe, Ni, and Al X-ray elemental maps obtained by EMPA of a type I smectite grain from sample 84-09 (transition between the serpentinized peridotite and the saprolite).

Figure 10 .
Figure 10.BSE photomicrograph (top left) and Si, Mg, Fe, Ni, and Al X-ray elemental maps obtained by EMPA of a type I smectite grain from sample 84-09 (transition between the serpentinized peridotite and the saprolite).

Figure 11 .
Figure 11.(a) XRPD refinement of sample 83-7 (ferruginous saprolite horizon): Rwp (numerical figure of merit quantifying the quality of the fit) = 3.3.Legend: blue = experimental pattern, red = calculated pattern, black = difference between experimental and calculated pattern, and orange = calculated pattern for goethite.At the bottom, the Bragg reflections for each mineral phase are shown.

Figure 11 .
Figure 11.(a) XRPD refinement of sample 83-7 (ferruginous saprolite horizon): Rwp (numerical figure of merit quantifying the quality of the fit) = 3.3.Legend: blue = experimental pattern, red = calculated pattern, black = difference between experimental and calculated pattern, and orange = calculated pattern for goethite.At the bottom, the Bragg reflections for each mineral phase are shown.(a*) XRD of oriented aggregate mounts of the same sample since 2θ degrees.Legend: black = untreated sample at room temperature, blue = treated with ETG, and red = heated to 540 • C. (b) XRPD refinement of sample 83-25 (saprolite horizon): Rwp = 4.5.Legend: black = experimental pattern, red = calculated pattern, gray = difference between the experimental and the calculated pattern, and green = calculated pattern for a talc-like structure (kerolite).At the bottom, the Bragg reflections for each mineral phase are shown.(b) XRPD refinement of sample 83-7 (ferruginous saprolite horizon): Rwp = 3.3.Legend: blue = experimental pattern, red = calculated pattern, black = difference between experimental and calculated pattern, and orange = calculated pattern for goethite.At the bottom, the Bragg reflections for each mineral phase are shown.(c) XRPD refinement of sample 84-12 (weathered peridotite): Rwp = 6.9, legend as in (a).(c*) XRD of oriented aggregate mounts of sample 84-12.Legend: red = untreated sample at room temperature, blue = treated with ETG, and green = heated to 540 • C.
) XRD of oriented aggregate mounts of the same sample since 2θ degrees.Legend: black = untreated sample at room temperature, blue = treated with ETG, and red = heated to 540 °C.(b) XRPD refinement of sample 83-25 (saprolite horizon): Rwp = 4.5.Legend: black = experimental pattern, red = calculated pattern, gray = difference between the experimental and the calculated pattern, and green = calculated pattern for a talc-like structure (kerolite).At the bottom, the Bragg reflections for each mineral phase are shown.(b) XRPD refinement of sample 83-7 (ferruginous saprolite horizon): Rwp = 3.3.Legend: blue = experimental pattern, red = calculated pattern, black = difference between experimental and calculated pattern, and orange = calculated pattern for goethite.At the bottom, the Bragg reflections for each mineral phase are shown.(c) XRPD refinement of sample 84-12 (weathered peridotite): Rwp = 6.9, legend as in (a).(c*) XRD of oriented aggregate mounts of sample 84-12.Legend: red = untreated sample at room temperature, blue = treated with ETG, and green = heated to 540 °C.