Improving the Copper-Molybdenum Ores Flotation Technology Using a Combined Collecting Agent

: The search for effective reagents for the flotation of non-ferrous metals from mineral raw materials is an actual problem. The article discusses the results of research on improving the technology of processing copper–molybdenum ores using a combined collector emulsion. The object of research was copper–molybdenum ore containing 0.43% copper and 0.0089% molybdenum. Copper minerals are represented by chalcopyrite 1.2% and chalcocite 0.015%, while covellite is present in a much smaller amount. The main mineral of molybdenum is molybdenite. The cycle of collective copper–molybdenum flotation includes the main flotation, control flotation, and three re-cleanings of concentrate. In the basic mode, the collective Cu–Mo concentrate was produced with the copper content of 16.25% with an extraction of 77.79% and with the molybdenum content of 0.45% with an extraction of 79.38%. Reaflot, thionocarbamate, and butyl xanthate were used in a ratio of 1:3:15 to prepare a combined collector agent. In order to produce the combined collector emulsion, the best degree of dispersion, which amounted to 99.5% of particles with a size of − 3.6 μm, was chosen. During the Cu–Mo ore flotation using an optimally dispersed microemulsion of the combined collector agent, a collective Cu–Mo concentrate was obtained with a copper content of 18.2% with an extraction of 83.58%, and with a molybdenum content of 0.49% with an extraction of 88.46%. The use of a combined collector agent increases the extraction of copper into the collective Cu–Mo concentrate by 5.79%, while the extraction of molybdenum increases by 9.08%.


Introduction
An increase in the efficiency of processing finely disseminated sulfide ores can be achieved through the use of improved reagent flotation modes, reagent processing, and new design solutions [1][2][3][4][5].The improvement of reagent regimes is achieved using new selective flotation reagents, their combination, ultrasonic treatment of reagents, and new designs of flotation equipment.
The search for effective reagents for the flotation of non-ferrous metals from mineral raw materials is an actual problem.Based on the regulation of the water-repellent ability and surface activity, a collector agent of copper and precious metals, sample 225-5, was obtained, which is more efficient than the industrially used dialkyldithiophosphate reagent [6,7].Sample 225-5 is a reagent modeled on a mixture of dialkyldithiophosphate with an extended hydrocarbon radical length and hydrophobizing component.
In the scientific research [8,9], the efficient use of phosphorus-bearing collector "PS" for the flotation of sulfide copper ores is shown.The crushing of the ore was about 60% of the class −0.074 mm.The efficiency of the flotation was controlled by the recovery of copper in the concentrate.At a consumption of the reagent "PS" 25 g/t, lime 0.75 kg/t, and frothing reagent T-92 85 g/t, the extraction of copper into the concentrate increases by 0.87%.
Scientists synthesized complexes of monohydroxyamide and monohydrazide of 2-ethyl-hexenylsuccinic acid with nickel and copper [10][11][12][13][14].The obtained reagents were tested on copper-nickel ore from the Pechenga ore deposits with a content of 0.49% Ni and 0.21% Cu.The use of the synthesized complex instead of the used aerofloat agent made it possible to obtain a collective copper-nickel concentrate with a nickel content of 7.5% with a recovery of 43.98%, and 4.3% copper with a recovery of 58.81%.The obtained results from the use of a complex of monohydroxyamide and 2-ethyl-hexenylsuccinic acid monohydrazide in the flotation of sulfide ores indicate the prospects for their application.
Under the conditions of using non-ionic collectors, the known methods for determining their residual concentration are ineffective.The developed spectral technique provides measurement of the concentration of a nonionic collector-allyl ester of amylxanthogenic acid in the aqueous phase of the pulp of copper-molybdenum flotation.The technique was applied to calculate the optimal grinding size of copper-molybdenum ore at the Erdenet factory.This made it possible to correct the value of the optimal content of the finished size class and, at the same time, to increase the extraction of copper and molybdenum into the concentrate by 0.8%-1.3%[15,16].
An increase in the extraction of useful components from sulfide ores can be achieved using a combination of various collectors [17][18][19][20].The optimal ratio of butyl xanthate and isobutyl dithiophosphate in a mixture with thionocarbamate was determined to increase the flotation rate of non-ferrous metals [21,22].Increasing the proportion of butyl xanthate in any combination increases the flotation rate of all monominerals.
Scientists are conducting research on the creation of new dialkyldithiophosphates.It is found that the higher aerofloats C 10 -C 16 have the ability to reduce the surface tension at the liquid-gas interface, similarly to strong surfactants, and that aerofloat agents, starting from nonyl (C 9 ), are characterized by a slow establishment of equilibrium at the liquid-gas interface, especially at low flotation concentrations [23][24][25][26].
The main problems of copper-containing ore processing are: the low copper content in ore, the high content of slurry particles (up to 40% of the class size smaller than 10 microns), finding copper minerals in the form of ultrafine aggregates, and the absence of highly effective selective reagents.Therefore, this raw material is the most difficult with respect to extraction of nonferrous metal sulfides.For the solution of a problem application of new selective flotation reagents, their combination, ultrasonic processing of reagents, and new designs of flotation equipment are possible [25,27].
The difficulties of copper-molybdenum ores beneficiation include the need for the very fine grinding of beneficiation products, insufficient efficiency in separating sulfide minerals from rock minerals, and the need to use complex technological modes for separating sulfide minerals.Therefore, the problem of finding new technological methods and schemes for the copper-molybdenum ores beneficiation is an urgent one [28,29].
The main indicators of the flotation process-extraction and selectivity concentrate-when using collectors depend on the specificity of their interaction at the interface's solid-liquid (s-l) and liquid-gas (l-g).In this regard, researchers are focused on studying the influence of these factors and the mechanism of action of the collectors.The hydrophobizing action of collectors, including dialkyldithiophosphate, depends on the strength of the chemical bond, the "functional group of the reagent-mineral surface", and on the length and structure (hydrocarbon chain of normal and isostructure) of the radical.
Thus, research on forming more selective reagents and collectors than xanthates and dithiophosphates was performed at the Gintsvetmet Institute.A number of S-substituted dialkyldithiocarbamates have been synthesized.S-cyanoethyl, N and N-diethyldithiocarbamate (DECE), produced by the interaction of sodium diethyldithiocarbamate and acrylonitrile, have been recognized as the most promising for the flotation of copper-molybdenum and polymetallic ores.
Dialkyldithiophosphates forming weaker complexes with heavy metal cations (Cu, Ni, Zn, Mo, Fe, etc.) in comparison with xanthogenates are characterized by a greater difference with them in the strength of complexes with heavy metal cations, which provides a greater selectivity of dialkyldithiophosphates action both in the separation of nonferrous metal sulfides and in the separation of iron sulfides from them [21,24,25].The higher surface activity of dialkyldithiophosphates at the interface l-g as compared to xanthogenates promotes the formation of small air bubbles and increases the flotation capability of fine particles.
Determining the effect of a combined collector on the extraction of copper and molybdenum (Cu-Mo) during the flotation of copper-molybdenum ores is the purpose of this work.
Technological equipment was also used.The original ore was crushed on a jaw crusher (DMD160/100) to a coarseness of less than 2.5 mm at Bishkek Experimental and Experimental Plant of Geological Exploration Equipment.Then the ore was crushed in a ball mill (40ML-000PS) to a particle size of 94% of the class of less than 74 µm.Dispersive analysis of the crushed ore was carried out on a photometric sedimentometer (FSKh-6K).Flotation was carried out on a laboratory flotation machine with 0.5, 0.75, 1.0 and 1.5 L chambers.The collective copper-molybdenum flotation cycle included basic flotation, control flotation and three concentrate purifications.The crushed ore in the form of a pulp with a density of 30%-35% solid was stirred in a flotation machine with flotation agents for a certain agitation time.The rotor speed was 1150 revolutions per minute.Then, at an air supply of 3.1 L per minute, the flotation of the ore was carried out.An emulsion of the combined reagent was prepared on the ultrasonic device UZDN-A1200T.The distribution of the reagent particles after dispersion was studied using a laser particle analyzer (Winner2000E).A vibrating micromill, the "pulverisette O" from FRITISCH, was used to prepare samples of ore and enrichment products for chemical analysis.

Results and Discussion
The work on improving the copper-molybdenum (Cu-Mo) ore flotation technology from the Kazakhstan deposit using a combined collector agent was performed.The mineralogical analysis showed that the ore contains the minerals molybdenite, pyrite, chalcopyrite, chalcocite, quartz, albite and a number of less significant minerals.
The main copper minerals are chalcopyrite −1.2% and chalcocite −0.015%, with covellite present in a much smaller amount.The main mineral of molybdenum is molybdenite −0.012%.Sulfide minerals of pyrite are present in amounts up to 0.5%.
According to the X-ray phase analysis, the content of the rock-forming minerals is 96% and is represented by quartz, albite, clinochlore, feldspar, chlorite, potassium microplagioclase and sericite.
Chalcopyrite is the main copper mineral, presented as irregular grains, interspersed in pyrite and gangue minerals (Figure 1a).The size of the chalcopyrite in the original ore is 0.001-1.5 mm.Mostly there are minerals of medium and small dissemination.Large, medium, small and micro-sized grains are interspersed extremely unevenly.Chalcopyrite is closely associated with pyrite and is often located along the internal cracks and intergranular spaces of pyrite (Figure 1b), forming a complex interspersed relationship.
Molybdenite is interspersed in quartz in the form of single crystals or their aggregates (Figure 2).The molybdenite impregnation is 0.003-0.3mm.
The degree of disclosure of chalcopyrite and pyrite in the studied ore sample was determined under a microscope.The ore grinding size was 65%, 75% and 85% of the class less than 74 µm.The degree of disclosure of chalcopyrite and pyrite in the original ore at different grinding sizes is presented in Table 1.When grinding the ore to 85% of the −0.074 mm class, the degree of disclosure of chalcopyrite and pyrite is 78% and 92%, respectively.The phase analysis of copper showed that copper is represented by 95.6% chalcopyrite, 2% chalcocite and covelline, and 2.4% in the form of copper oxides.Molybdenum in the studied ore sample is represented by 96% molybdenite and 4.0% in the form of oxide.
On the JXA-8230 electron probe microanalyzer from JEOL (Figure 3), the presence of chalcopyrite was established.The copper content at the point of electronic charge is 32.12%.The dispersion analysis was carried out on a photometric sedimentometer (FSH-6K) with crushed ore of up to 90% of the class less than 74 µm (Figure 4).
From Figure 4, it follows that the largest part of the finely crushed ore consists of the size classes 15-20 and 60-70 µm.
The sieve method was used to perform a granulometric analysis of the ore with the determination of the content of copper and molybdenum by size class (Table 2).When the ore grinding size is 80-81% of the class less than 71 µm, most of the copper and molybdenum is distributed into classes larger than 50 µm and less than 20 µm.For example, the size class +50 µm contains 29.1% copper and 38% molybdenum, while the −20 µm class contains 44.8% copper and 37.7% molybdenum.
The scheme for conducting test experiments on bulk Cu-Mo flotation is shown in Figure 5.The scheme included the main collective, control Cu-Mo flotation and three cleaning operations of the bulk Cu-Mo concentrate.Lime was added to the grinding of the ore to create the pH of the medium.Sodium sulfide was used to sulfidize the oxidized minerals.
According to the specified reagent regime in Figure 5, a collective Cu-Mo concentrate was obtained with a copper content of 16.25% and a molybdenum content of 0.45%, with an extraction of 77.79% and 79.38%, respectively.The obtained collective copper-molybdenum concentrate was analyzed by wave-dispersive microanalysis.This analysis showed the presence in the concentrate of the main mass of chalcopyrite, a small amount of secondary copper minerals and the presence of molybdenite (Figure 6a,b).In order to improve the technological performance of the flotation, test experiments were carried out on the flotation enrichment of the Cu-Mo ore using a combined reagent emulsion.The combined flotation agent is a mixture of sodium butyl xanthate, thionocarbamate and reaflot in an optimally selected ratio of 1:3:15.It was fed into the flotation process in the form of an emulsion produced in an ultrasonic disperser.
When using a combination of collectors in flotation, the mechanism of their interaction with the surface of minerals is determined by the characteristics of the surface of the minerals and the activity of each component of the collector.During dispersion, in addition to microbubbles, a microemulsion is formed, which, upon collision with slimy mineral particles, spreads and hydrophobizes their surface, improving the flotation process.Microbubbles, in turn, are much easier to attach to such hydrophobized surfaces of slimy particles.
The higher surface activity of the combined reagent at the liquid-gas interface compared to xantogenates promotes the formation of small air bubbles and increases the floatability of fine particles.
Studies on determining the dependence of the dispersion degree of the microemulsion of the base reagent sodium butyl xanthate and the combined flotation reagent on the degree of extraction of the slimy particles of copper and molybdenum during the mineral raw materials flotation were performed.The reagent dispersion time was 1, 2 and 3 min.The distribution of reagent particles after dispersion was studied on a Winner2000E laser particle analyzer, which is a laser diffraction particle size analyzer operating on the scattering principle.It is used to accurately determine the particle size distribution from 0.1 µm to 300 µm, with high sensitivity of the annular arrangement of photodetectors, which significantly increases the accuracy and repeatability of the measurements, with adjustable ultrasonic mixing and ultrasonic dispersion of the built-in liquid dispersion system.The research results showed that when dispersing sodium butyl xanthate for 1 min, the particles with a size of less than 7.5 µm amount to 88.149%.When dispersing sodium butyl xanthate for 2 min, the particles with a size of less than 8.9 µm amount to 87.41%.When dispersing sodium butyl xanthate for 3 min, particles with size less than 8.6 microns amount to 91.032%.The measurement results show that the dispersion of butyl xanthate does not lead to a significant change in the particle distribution.
However, dixanthogen microemulsion particles are also formed during the oxidation of butyl xanthate, which improves the flotation process.Dispersion is more necessary to obtain a microemulsion of sparingly soluble reagents, in particular thionocarbamates and reaflot (Figures 7 and 8).In the combined reagent without dispersion, particles with a size of less than 54 µm amount to 97.22%.
At the optimal dispersion time of the combined collector agents of 2 min, 99.6% are particles with a size of less than 3.7 µm.
Table 3 shows the results of the flotation of the Cu-Mo ore with a dispersed microemulsion of a combined collector agent at different dispersion times.During the Cu-Mo ore flotation using an optimally dispersed microemulsion of the combined collector agent, a collective Cu-Mo concentrate was obtained with a copper content of 18.2% with an extraction of 83.58%, and with a molybdenum content of 0.49% with an extraction of 88.46%.The dispersion of the combined collector agent makes it possible to increase the copper extraction into the collective Cu-Mo concentrate by 2.9%, and molybdenum by 3.62%.The copper extraction into the Cu-Mo concentrate increases by 5.79% and molybdenum by 9.08% with the use of butyl sodium xanthate compared with the basic mode.The use of dispersion of the microemulsion of the combined collector agent also makes it possible to reduce its consumption in flotation by 10%.The consumption of the combined collector agent after dispersion is 108 g/t in the main collective Cu-Mo flotation and 54 g/t in the control flotation.
The dependence of the degree of dispersion of the microemulsion of the combined collector agent on the extraction of slimy copper particles was determined.For this, a dispersion analysis of the base flotation and flotation tailings was carried out using a dispersed reagent microemulsion.Table 4 shows the results of the analysis of dispersion.
The use of a dispersed microemulsion makes it possible to increase the recovery of slimy copper particles in the Cu-Mo concentrate.The loss of copper in the final tailings of the control flotation in the basic mode in the size class −20 + 0 microns is 39.9%.The flotation tailings obtained using the combined collector microemulsion contain 29.8% copper in the −20 + 0 µm size class.The content of copper sludge particles in the flotation tailings is reduced by about 10% when using a combined collector agent.

Conclusions
A reagent flotation mode using a combined collector agent, which is a mixture of reaflot, thionocarbamate and butyl xanthate in a ratio of 1:3:15, was worked out on a sample of Cu-Mo ore.The optimum degree of dispersion of the combined agent was 99.6% of the particles smaller than 3.7 µm.
Studies comparing the results with the base collector sodium butyl xanthate were also conducted.In the basic mode, a collective Cu-Mo concentrate was produced with a copper content of 16.25% with an extraction of 77.79%, and with a molybdenum content of 0.45% with an extraction of 79.38%.
With the use of a combined collector agent, a collective Cu-Mo concentrate was produced with a copper content of 18.2% with an extraction of 83.58%, and with a molybdenum content of 0.49% with an extraction of 88.46%.
The extraction of copper into Cu-Mo concentrate increases by 5.79% and molybdenum by 9.08% with the use of butyl sodium xanthate compared with the basic regime.
The use of a dispersed microemulsion also makes it possible to increase the degree of extraction of slimy copper particles into a Cu-Mo concentrate.The content of copper-containing sludge particles in the flotation tailings is reduced by 10.09% when using a combined collector agent.

Figure 1 .
Figure 1.(a) Chalcopyrite.Yellow-independently in the form of xenomorphic grains; light yellow-in association with pyrite; black-gray-interspersed in vein minerals.Reflection is 260×.(b) Chalcopyrite.Yellow-in pyrite cracks; light yellow-in the form of thin veins.Reflection is 260×.

Table 1 .
Degree of chalcopyrite and pyrite release in the original ore at different grinding sizes.In intergrowths with pyrite and rock-forming minerals % 40.0 28.0 22.0 Pyrite Free, % 80.0 88.6 92.0In intergrowths with pyrite and rock-forming minerals % 20.0 11.4 8.0

Figure 5 .
Figure 5. Scheme of collective copper-molybdenum ore flotation.Int.pr is the abbreviation of Intermediate product.

Figure 7 .
Figure 7. Distribution of particles in the combined collector agent without dispersion.

Figure 8 .
Figure 8. Distribution of particles in the combined collector agent after dispersion.

Table 2 .
Distribution of copper and molybdenum by size class.

Table 3 .
Results of Cu-Mo ore flotation with a combined collector agent at different dispersion times.

Table 4 .
Results of dispersion analysis of flotation tailings.