Effect of Sodium Metabisulfite on Selective Flotation of Chalcopyrite and Molybdenite

Sodium metabisulfite (MBS) was used in this study for selective flotation of chalcopyrite and molybdenite. Microflotation tests of single and mixed minerals were performed to assess the floatability of chalcopyrite and molybdenite. The results of microflotation of single minerals showed that MBS treatment significantly depressed the floatability of chalcopyrite and slightly reduced the floatability of molybdenite. The results of microflotation of mixed minerals demonstrated that the MBS treatment could be used as a selective chalcopyrite depressant in the selective flotation of chalcopyrite and molybdenite. Furthermore, the addition of diesel oil or kerosene could significantly improve the separation efficiency of selective flotation of chalcopyrite and molybdenite using MBS treatment. A mechanism based on X-ray photoelectron spectroscopy analysis results is proposed in this study to explain the selective depressing effect of MBS on the flotation of chalcopyrite and molybdenite.


Introduction
Molybdenum minerals are often associated with copper sulfide minerals [1]. It is estimated that about 50% of the world's molybdenum production comes from copper and molybdenum (Cu-Mo) ores as a by-product [2,3]. Both copper and molybdenum are important materials in various fields; therefore, the separation of both copper and molybdenum minerals is important. Furthermore, molybdenum minerals play a very important role in making the Cu-Mo processing plant economically viable [4].
On the other hand, Castro et al. [31] showed that sodium metabisulfite has been used to replace lime as a pyrite depressant in the rougher flotation stage of Cu-Mo-Fe ores in Chile. Therefore, it might be more efficient to use sodium metabisulfite for the selective Cu-Mo flotation stage. Chen et al. [32] studied the effect of sodium metabisulfite on the floatability of molybdenite in fresh water and seawater. They reported that sodium metabisulfite exhibited a depressing effect on the recovery of molybdenite in fresh water. However, the effect of sodium metabisulfite on the depression of chalcopyrite in the selective Cu-Mo flotation has been not reported.
The main objective of this study is to investigate the effect of sodium metabisulfite (MBS) on the floatability of chalcopyrite and molybdenite. Furthermore, this work investigated the possibility of using MBS for selective flotation of chalcopyrite and molybdenite. In addition, X-ray photoelectron spectroscopy analysis was performed to assess the effect of MBS on the chemical state on the surface of chalcopyrite and molybdenite.

Materials
A high-purity crystal sample of chalcopyrite (Acari Mine, Arequipa, Peru) and molybdenite powder sample supplied by Sumitomo Metal Mining Co., Ltd. (Tokyo, Japan) were used in this study. The chalcopyrite sample was crushed and then hand sorted to minimize the impurity. The chalcopyrite was ground using an agate mortar and pestle, and then dry screened (passing 38 µm screener) prior to all tests. The mean particle sizes of chalcopyrite and molybdenite were 16.1 µm and 10.6 µm, respectively. The chemical and mineralogical compositions of chalcopyrite and molybdenite were measured using X-ray fluorescence (XRF, ZSX Primus 2, Rigaku, Tokyo, Japan) and X-ray diffraction (XRD, Ultima 4, Rigaku, Tokyo, Japan). The chemical and mineralogical analysis results of chalcopyrite and molybdenite are presented in Table 1 and Figure 1, respectively.
Analytical grade sodium metabisulfite (MBS) was employed as a copper depressant in this study. Analytical grade potassium hydroxide (KOH) and hydrochloric acid (HCl) were used as pH modifiers. Industrial grade kerosene and diesel oil were used as collectors. Industrial grade pine oil was used as a frother. All employed reagents were supplied by Wako Chemical Industries, Ltd. (Tokyo, Japan), except for the diesel oil, which was provided by a gas station (ENEOS Co., Ltd., Tokyo, Japan). Millipore (Direct-Q, Merck, Tokyo, Japan) ultra-pure water with a resistivity of 18.2 MΩ.cm was used in all experiments.  Analytical grade sodium metabisulfite (MBS) was employed as a copper depressant in this study. Analytical grade potassium hydroxide (KOH) and hydrochloric acid (HCl) were used as pH modifiers. Industrial grade kerosene and diesel oil were used as collectors. Industrial grade pine oil was used as a frother. All employed reagents were supplied by Wako Chemical Industries, Ltd. (Tokyo, Japan), except for the diesel oil, which was provided by a gas station (ENEOS Co., Ltd., Tokyo, Japan). Millipore (Direct-Q, Merck, Japan) ultra-pure water with a resistivity of 18.2 MΩ.cm was used in all experiments.

Microflotation Test
The flotation tests were carried out using single and mixed minerals of chalcopyrite and molybdenite. The mixing ratio was 50% chalcopyrite and 50% molybdenite. The mineral powders (0.6 g) were added to 180 mL of ultra-pure water. The solution pH was controlled at pH 9 for 2 min, and MBS treatment was carried out by adding MBS powder into the suspension. The MBS treatment was performed for 5 min. The MBS concentration varied from 0 mM to 5 mM. Pine oil (0.13 mM) was added to the suspension. The conditioning time for the pine oil was 2 min. To improve the flotation selectivity, a certain amount of emulsified diesel oil or kerosene was employed as collectors. These collectors were added before the addition of MBS powder. The diesel oil or kerosene was emulsified in a homogenizer (HG-200 Homogenizer, AS ONE, Tokyo, Japan) at 20,000 rpm for 30 s. The conditioning time for diesel oil or kerosene was 3 min. The suspension pH was controlled at pH 9 throughout the conditioning process by the addition of KOH or HCl.
The flotation tests were performed by transferring the suspension solution to a Partridge-Smith microflotation device [18]. Flotation was conducted by injecting nitrogen gas through a glass frit at a flow rate of 20 mL/min for 6 min. The float and tailing fractions were collected separately. These fractions were dried in an oven at 110 °C for 12 h and then weighed. The flotation tests were repeated twice, and the average value of recovery of each mineral is reported in this work.
The recovery of the mineral in the flotation of a single mineral system was calculated using Equation (1), where mfloat and msink are the mass of the mineral in the float and sink fractions, respectively. Meanwhile, the recovery of chalcopyrite and molybdenite in the flotation of mixed minerals system was calculated based on the assumption that copper and molybdenum belong to chalcopyrite and molybdenite, respectively. The froth and tailing fractions were analyzed by XRF, and the analysis results were used to calculate the recovery of each mineral using Equation (1). Newton efficiency (η) was calculated using

Microflotation Test
The flotation tests were carried out using single and mixed minerals of chalcopyrite and molybdenite. The mixing ratio was 50% chalcopyrite and 50% molybdenite. The mineral powders (0.6 g) were added to 180 mL of ultra-pure water. The solution pH was controlled at pH 9 for 2 min, and MBS treatment was carried out by adding MBS powder into the suspension. The MBS treatment was performed for 5 min. The MBS concentration varied from 0 mM to 5 mM. Pine oil (0.13 mM) was added to the suspension. The conditioning time for the pine oil was 2 min. To improve the flotation selectivity, a certain amount of emulsified diesel oil or kerosene was employed as collectors. These collectors were added before the addition of MBS powder. The diesel oil or kerosene was emulsified in a homogenizer (HG-200 Homogenizer, AS ONE, Tokyo, Japan) at 20,000 rpm for 30 s. The conditioning time for diesel oil or kerosene was 3 min. The suspension pH was controlled at pH 9 throughout the conditioning process by the addition of KOH or HCl.
The flotation tests were performed by transferring the suspension solution to a Partridge-Smith microflotation device [18]. Flotation was conducted by injecting nitrogen gas through a glass frit at a flow rate of 20 mL/min for 6 min. The float and tailing fractions were collected separately. These fractions were dried in an oven at 110 • C for 12 h and then weighed. The flotation tests were repeated twice, and the average value of recovery of each mineral is reported in this work.
The recovery of the mineral in the flotation of a single mineral system was calculated using Equation (1), where m float and m sink are the mass of the mineral in the float and sink fractions, respectively. Meanwhile, the recovery of chalcopyrite and molybdenite in the flotation of mixed minerals system was calculated based on the assumption that copper and molybdenum belong to chalcopyrite and molybdenite, respectively. The froth and tailing fractions were analyzed by XRF, and the analysis results were used to calculate the recovery of each mineral using Equation (1). Newton efficiency (η) was calculated using Equation (2), where R c is the recovery of molybdenite in the froth and R t is the recovery of chalcopyrite in the tailing.

X-ray Photoelectron Spectroscopy (XPS)
X-ray photoelectron spectroscopic analysis was performed to characterize the mineral surface before and after the treatment. The mineral powders (0.1 g) were suspended in 30 mL ultra-pure water. The pH was then adjusted to pH 9. Afterward, the suspension was treated with or without 5 mM MBS for 5 min at pH 9. After the treatment, the mineral sample was filtered, freeze-dried, and stored under a vacuum bag to minimize oxidation. XPS analysis was then carried out using an AXIS-ULTRA (Shimadzu-Kratos Co., Ltd., Manchester, UK) with an Al Kα X-ray source operated at 5 mA and 15 kV. The charge neutralizer was enabled during the analysis. The pressure in the analyzer chamber was 3.1 × 10 −7 torr. A survey scan and elemental region scan were performed to extract information on the oxidation states of chemical species on the mineral surface. The collected spectra were analyzed using Casa XPS software (Ver. 2.3.16). Shirley background corrections [33] were used throughout the analyses for carbon (C) 1s, oxygen (O) 1s, iron (Fe) 2p, sulfur (S) 2p, copper (Cu) 2p, and molybdenum (Mo) 3d spectra. The Gaussian-Lorentzian (GL) function was used to deconvolute the spectra. The binding energy was calibrated based on C 1s at a binding energy of 284.6 eV [15,25].

Microflotation of Single Mineral
Effects of MBS treatment on the flotation recovery of chalcopyrite and molybdenite in the single mineral system are presented in Figure 2. It should be noted that the microflotation tests were performed in the absence of a collector. The recovery of chalcopyrite significantly decreased from 65% in the absence of MBS to 15% after being treated in 0.5 mM MBS. The recovery of chalcopyrite gradually decreased with increasing concentration of MBS. The recovery of chalcopyrite was 5% after being treated in 5 mM MBS. These microflotation results indicate that the MBS treatment exhibited a strong depressing effect on the floatability of chalcopyrite. On the other hand, the addition of 0.5 mM MBS had an insignificant effect on the recovery of molybdenite. However, the addition of a higher concentration of MBS could reduce the recovery of molybdenite. For instance, the recovery of molybdenite slightly decreased from 67% to 55% after being treated in 5 mM MBS. A similar depressing effect of MBS on the floatability of molybdenite in deionized (DI) water has been reported by Chen et al. [32]. Although these microflotation results indicate that MBS treatment slightly depressed the floatability of molybdenite, the depressing effect was less significant compared to that on the floatability of chalcopyrite. In addition, the microflotation results presented in Figure 2 show that MBS treatment has potential as a selective copper depressant in the selective flotation of Cu-Mo.

XPS Analysis
XPS analysis was performed to explain the flotation results presented in Figure 2 by evaluating the oxidation states of chemical species on the surface of chalcopyrite and molybdenite before and after the MBS treatment. Figure 3 shows the X-ray photoelectron spectra of Cu 2p, S 2p, Fe 2p, and O 1s of chalcopyrite. recovery of molybdenite. However, the addition of a higher concentration of MBS could reduce the recovery of molybdenite. For instance, the recovery of molybdenite slightly decreased from 67% to 55% after being treated in 5 mM MBS. A similar depressing effect of MBS on the floatability of molybdenite in deionized (DI) water has been reported by Chen et al. [32]. Although these microflotation results indicate that MBS treatment slightly depressed the floatability of molybdenite, the depressing effect was less significant compared to that on the floatability of chalcopyrite. In addition, the microflotation results presented in Figure 2 show that MBS treatment has potential as a selective copper depressant in the selective flotation of Cu-Mo.

XPS Analysis
XPS analysis was performed to explain the flotation results presented in Figure 2 by evaluating the oxidation states of chemical species on the surface of chalcopyrite and molybdenite before and after the MBS treatment. Figure 3 shows the X-ray photoelectron spectra of Cu 2p, S 2p, Fe 2p, and O 1s of chalcopyrite.   Two Gaussian-Lorentzian (GL) functions could best fit the Cu 2p spectrum of chalcopyrite at pH 9 ( Figure 3A). The first GL function shows a peak centered at ca. 931.8 eV, which is in agreement with the Cu(I) of chalcopyrite [34]. The second GL function shows a peak centered at higher binding energy (i.e., 934.2 eV). This peak is attributed to the Cu(II) of Cu(OH) 2 [35]. The presence of Cu(II) is confirmed by the formation of a weak satellite peak located at binding energy 940-945 eV. The presence of Cu(II) on the chalcopyrite surface indicates that the chalcopyrite surface was slightly oxidized at pH 9 in the absence of MBS. In addition, the surface oxidation of chalcopyrite at pH 9 is confirmed by the Fe 2p spectrum. The deconvolution of Fe 2p spectrum of chalcopyrite at pH 9 shown in Figure 3B indicates that in addition to the Fe of chalcopyrite located at 707.4 eV [36], the chalcopyrite surface was covered by FeOOH and Fe 2 O 3 , as indicated by the peaks located at 710.6 eV and 711.0 eV, respectively [37]. The deconvolution of S 2p spectrum of chalcopyrite at pH 9 ( Figure 3C) indicates various peaks located at ca. 160.7 eV, 162.0 eV, and 163.8 eV. These peaks are attributed to chalcopyrite, disulfide (S 2 2− ), and polysulfide (S n 2− ), respectively [36]. The presence of oxide and hydroxide on the chalcopyrite surface is confirmed by the peak located at 529.9 eV [37] and 531.5 eV [38] in the O 1s spectrum of chalcopyrite at pH 9 ( Figure 3D). In addition, there is an indication of the presence of adsorbed water on the surface of chalcopyrite, as shown by the peak located at 533.4 eV [39] in Figure 3D.
The MBS treatment reduced the Cu(II) to Cu(I) on the chalcopyrite surface, as indicated by the absence of Cu(II) species in the Cu 2p spectrum of chalcopyrite ( Figure 3A). Only the Cu 2p peak of chalcopyrite was observed after the surface was treated in 5 mM MBS. The Fe 2p spectrum in Figure 3B shows that the MBS treatment significantly improved the peak intensity of FeOOH and formed a new peak located at 713.1 eV. This new peak is attributed to Fe 2 (SO 4 ) 3 [37]. The formation of sulfate species is confirmed by the appearance of a new peak located at 167.9 eV in the S 2p spectrum in Figure 3C and a new peak located at 532.2 eV in the O 1s spectrum in Figure 3D [36,37]. This sulfate species might be formed as a result of the reaction between MBS and dissolved oxygen in the water, as shown by Equations (3) and (4). Figure 4 presents the X-ray photoelectron spectra of Mo 3d, S 2p, and O 1s of molybdenite. The Mo 3d spectra of the molybdenite surface ( Figure 4A) were best fitted with three GL functions. The 3d 5/2 peaks located at ca. 229.5 eV, 229.7 eV, and 232.2 eV are attributed to molybdenum bulk (Mo(IV)) of molybdenite [40], Mo (IV) of molybdenum dioxide (MoO 2 ) [41], and Mo(VI) of molybdenum trioxide (MoO 3 ) [42], respectively. The S 2p spectrum of molybdenite shown in Figure 4B indicates a doublet peak with S 2p 3/2 peaks located at 162.3 eV, which is attributed to the monosulfide of molybdenite [19,43]. Figure 4C shows the O 1s spectra of molybdenite. The presence of molybdenum dioxide and molybdenum trioxide is confirmed by the O 1s peaks located at 530.3 eV [44] and 531.4 eV [45], respectively. In addition, there are other peaks located at 532.3 eV and 533.7 eV, which are attributed to the hydroxide of the organic contaminants [30] and adsorbed water (H 2 O) [39], respectively. Similar spectra of Mo 3d, S 2p, and O 1s of molybdenite were obtained after the molybdenite was treated in 5 mM MBS at pH 9. In addition, unlike the formation of sulfate species on the S 2p of chalcopyrite after being treated in 5 mM MBS at pH 9, there was no sulfate formation in the S 2p spectra of molybdenite.

Proposed Mechanism
Based on the XPS analysis results, a mechanism can be proposed to explain the depressing effect of MBS on the floatability of chalcopyrite. The MBS treatment mainly produces sulfate species as a reaction product when in contact with the dissolved oxygen in water (Equations (3) and (4)). This sulfate species covered the chalcopyrite surface, forming hydrophilic Fe 2 (SO 4 ) 3 species on the surface. Furthermore, the MBS treatment improved the intensity of hydrophilic FeOOH and  Similar spectra of Mo 3d, S 2p, and O 1s of molybdenite were obtained after the molybdenite was treated in 5 mM MBS at pH 9. In addition, unlike the formation of sulfate species on the S 2p of chalcopyrite after being treated in 5 mM MBS at pH 9, there was no sulfate formation in the S 2p spectra of molybdenite.

Proposed Mechanism
Based on the XPS analysis results, a mechanism can be proposed to explain the depressing effect of MBS on the floatability of chalcopyrite. The MBS treatment mainly produces sulfate species as a reaction product when in contact with the dissolved oxygen in water (Equations (3) and (4)). This sulfate species covered the chalcopyrite surface, forming hydrophilic Fe2(SO4)3 species on the surface. Furthermore, the MBS treatment improved the intensity of hydrophilic FeOOH and Fe2O3 species on the chalcopyrite surface. The presence of these various hydrophilic species on the surface depresses the floatability of chalcopyrite.
The XPS results of molybdenite indicate that the MBS had an insignificant effect on the binding energy of chemical species on the surface of molybdenite. However, the flotation results indicate that MBS treatment exhibited a slightly depressing effect on the  The XPS results of molybdenite indicate that the MBS had an insignificant effect on the binding energy of chemical species on the surface of molybdenite. However, the flotation results indicate that MBS treatment exhibited a slightly depressing effect on the floatability of molybdenite. This difference in XPS and flotation results could be caused by the crystal structure of molybdenite. The crystal structure of molybdenite shows two types of surfaces: (1) non-polar faces formed by the scission of S-S bonds and (2) polar edges generated by the rupture of strong covalent Mo-S bonds. Based on these bonding types, the faces are hydrophobic and the edges are hydrophilic [46]. These edges might be vulnerable to the MBS treatment than the faces as shown by Chen et al. [32]. They reported that the MBS treatment showed an insignificant effect in the spectra of molybdenite faces, however, it formed sulfate and sulfite species in the S 2p spectra of molybdenite edges after being treated in 1 mM MBS in DI water.
In this study, the molybdenite fine powder was used for flotation tests and XPS analysis, which has a higher edges-to-faces ratio, thus the depressing effect of MBS on the floatability of molybdenite became more apparent. Furthermore, the molybdenite powder used for XPS analysis in this study was not differentiated between the faces and edges of molybdenite, thus the XPS analysis could not identify the effect of MBS treatment on the molybdenite edges. However, the presence of sulfate and sulfite species on the molybdenite edges, as reported by Chen et al. [32], could explain the slightly depressing effect of MBS on the floatability of molybdenite presented in this study.

Microflotation of Mixed Minerals
The microflotation results of a single mineral, presented in Figure 2, show the possibility of using MBS treatment for selective separation of molybdenite and chalcopyrite. Therefore, the microflotation tests were performed using mixed chalcopyrite and molybdenite. Figure 5 shows the effects of MBS treatment on the recovery of chalcopyrite and molybdenite in the mixed minerals system. As expected, the microflotation results of mixed chalcopyrite and molybdenite show a similar trend as shown in the microflotation of a single mineral (Figure 2). The MBS treatment exhibited a strong depressing effect on the recovery of chalcopyrite and slightly reduced the recovery of molybdenite. Furthermore, the depressing effect increased with an increase in the concentration of MBS.
The Newton efficiency is presented in Figure 5 to assess the selectivity of the MBS treatment on the separation of chalcopyrite and molybdenite using flotation. The Newton efficiency increased from 25% before the MBS treatment to 43% after the addition of 0.5 mM MBS. The Newton efficiency reached a maximum value (48%) after the addition of 1 mM MBS and then slightly decreased to 46% after the addition of 5 mM MBS owing to the decreasing recovery of molybdenite. These Newton efficiency results demonstrate that the MBS treatment could be used as a selective depressant of chalcopyrite in the selective flotation of chalcopyrite and molybdenite.
Emulsified kerosene and diesel oil were used as collectors to improve the separation selectivity of chalcopyrite and molybdenite in the flotation of mixed minerals using MBS treatment. These non-polar oil collectors were selected because they are known as selective collectors for molybdenite, owing to a higher affinity on the molybdenite non-polar faces [2,[47][48][49][50]. In these flotation tests, the concentration of MBS was fixed at 1 mM. This concentration was selected based on the maximum Newton efficiency shown in Figure 5. Figure 6 shows the effect of emulsified diesel oil and kerosene on the recovery of mixed chalcopyrite and molybdenite after being treated in 1 mM MBS at pH 9. The addition of various concentrations of emulsified diesel oil and kerosene significantly improved the recovery of molybdenite compared to that of chalcopyrite. For instance, the recovery of molybdenite significantly increased from 52% to 82% after the addition of 100 mg/L diesel oil, while the recovery of chalcopyrite slightly increased from 7% to 13% under a similar condition. These results can be attributed to the selective adsorption of diesel oil and kerosene on the molybdenite surface, which was less affected by the MBS treatment than the chalcopyrite surface, as shown by the XPS analysis and flotation results. In addition, Suyantara et al. [48,51] showed that the molybdenite surface became more hydrophobic after the addition of emulsified kerosene, thus molybdenite became more floatable compared to that of chalcopyrite.  Figure 6 demonstrates that emulsified diesel oil was more effective to improve the recovery of molybdenite compared to that of emulsified kerosene. For instance, the recovery of molybdenite improved from 52% to 82% after the addition of 100 mg/L emulsified diesel oil, while the recovery of molybdenite increased from 52% to 73% after the addition of 100 mg/L emulsified kerosene. Diesel oil has a better dispersion capability in water (i.e., forming finer and homogeneous emulsion) than kerosene [52]; thus, it is more effectively adsorbed on the molybdenite surface. Figure 6A indicates that the recovery of molybdenite reached an optimum condition after the addition of 100 mg/L emulsified diesel oil. The addition of a higher concentration (i.e., 200 mg/L) of emulsified diesel oil slightly reduced the recovery of molybdenite. One of the possible reasons for this phenomenon is the addition of excess emulsified diesel oil caused excessive agglomeration of molybdenite particles, causing the molybdenite particle to become too heavy to be carried by the nitrogen bubbles to the froth zone. On the other hand, this phenomenon was not observed if emulsified kerosene was used as a collector ( Figure 6B). The maximum recovery of molybdenite was observed after the addition of 200 mg/L emulsified kerosene.
The recovery of chalcopyrite slightly increased with an increase in the concentration of emulsified diesel oil and kerosene ( Figure 6). This phenomenon can be caused by the physical adsorption of diesel oil and kerosene on the surface of chalcopyrite, owing to the presence of sulfur species on the slightly oxidized chalcopyrite, as shown from the XPS results. A similar phenomenon has been reported in previous studies [48,53]. In addition, this phenomenon might be caused by the interaction between molybdenite and chalcopyrite (i.e., heterocoagulation and entrapment of chalcopyrite), which requires further investigation. Indeed, Hornn et al. [54] showed that emulsified kerosene can be used to agglomerate the fine particle chalcopyrite, improving its floatability in the agglomeration-flotation. Table 2 confirms the effectiveness of MBS treatment as a selective depressant of chalcopyrite in the selective flotation of chalcopyrite and molybdenite with the addition of diesel oil and kerosene. In the absence of MBS treatment, the recoveries of chalcopyrite were 30.8% and 43.3% with the addition of 100 mg/L diesel oil and 200 mg/L kerosene, respectively. Meanwhile, the addition of diesel oil and kerosene significantly improved the recoveries of molybdenite, from 61.1% in the absence of collector to 88.0% and 89.5% with the addition of 100 mg/L diesel oil and 200 mg/L kerosene, respectively. With the addition of 1 mM MBS, the recovery of chalcopyrite significantly depressed to 13.7% and 19.1% under similar conditions. On the other hand, the recovery of molybdenite slightly decreased after the MBS treatment.  Figure 7 shows the Newton efficiency of flotation of mixed chalcopyrite and molybdenite after being treated in various concentrations of emulsified diesel oil and kerosene in 1 mM MBS at pH 9. The Newton efficiency gradually increased with an increase in the concentration of emulsified diesel oil and kerosene. The Newton efficiency reached a maximum value of 70% after the addition of 100 mg/L diesel oil in 1 mM MBS at pH 9. Under a similar concentration, the addition of emulsified kerosene results in lower Newton efficiency (i.e., 60%). Meanwhile, the Newton efficiency reached a maximum value of 62% after the addition of 200 mg/L emulsified kerosene in 1 mM MBS at pH 9. This result indicates that emulsified diesel oil is more effective in improving the selectivity of flotation of chalcopyrite and molybdenite compared to kerosene. As discussed previously, diesel has a higher effectivity owing to it having a better dispersion capability in water than kerosene. Nevertheless, both emulsified diesel oil and kerosene could significantly improve the separation selectivity of selective flotation of chalcopyrite and molybdenite using MBS treatment.

Conclusions
In this study, the effects of MBS treatment on the floatability of chalcopyrite and molybdenite were investigated. The microflotation results of a single mineral show that MBS treatment exhibited a strong depressing effect on the floatability of chalcopyrite and slightly depressed the floatability of molybdenite. The XPS analysis results indicated that the strong depressing effect of MBS on the floatability of chalcopyrite is caused by the formation of hydrophilic species (i.e., sulfate, Fe 2 (SO 4 ) 3 , FeOOH, and Fe 2 O 3 ) on the surface. On the other hand, MBS treatment showed an insignificant effect on the chemical species on the molybdenite surface.
The microflotation of mixed minerals showed that MBS treatment could be used as a selective depressant of chalcopyrite in the selective flotation of chalcopyrite and molybdenite. Furthermore, the addition of diesel oil or kerosene as a molybdenite collector could significantly improve the separation selectivity (i.e., Newton efficiency) of flotation of chalcopyrite and molybdenite using MBS treatment. The addition of diesel oil could effectively improve the Newton efficiency compared to that of kerosene.