Di ﬀ erent Insights into Silicate Rectorite Modiﬁcation and Its Role in Removal of Heavy Metal Ions from Wastewater

: In the ﬁeld of water management, the separation of metal contaminants from wastewater is very important and challenging. This study systematically investigated the e ﬀ ect and underlying mechanism of silicate rectorite (REC) on the removal of heavy metal ions (Cr(VI) and Pb(II)) from wastewater. The adsorption and removal capacity of REC was further improved by its novel modiﬁcation with ferric chloride hexahydrate. Compared to natural REC, the modiﬁed rectorite (Fe-REC) showed comparatively superior adsorption e ﬃ ciency for both Cr(VI) and Pb(II) due to the chemisorption of Fe 3 + on the REC surface as its oxidation state (Fe–O, Fe–OH, Fe–OOH). Adsorption on Cr(VI) attributed to the reaction between iron hydroxy complexes (FeOH 2 + , Fe(OH) 2 + and Fe(OH) 3 (aq)) and Cr(VI) species (HCrO 4 − and CrO 42 − ) in the aqueous solution. This reaction was perfectly consistent with the binding energy shifts in O 1s and Fe 2p species, as reﬂected by XPS analysis. While, the existence of –Al–OH and –Si–OH in silicate REC slurry reacted with PbOH + colloids produced from lead ions hydrolysis to promote Pb(II) adsorption. Zeta potential after modiﬁcation and removal occurred to shift positively or negatively to testify the adsorption of Fe 3 + and heavy metal ions. Freundlich and Langmuir isotherms conformed adsorption process for Cr(VI) and Pb(II), respectively.


Introduction
A long-standing problem, heavy metal ions contaminations from wastewater, is being in dire need of a solution to be solved thoroughly due to their biological accumulation and higher toxicity even at minute concentrations. Generally, the majority of these pollutants cannot degrade by themselves, such as hexavalent chromium Cr(VI) and divalent lead Pb(II). Hexavalent chromium is a kind of strong oxidant and highly soluble heavy metal with carcinogenic, mutagenic and teratogenic substance for human [1,2]. Based on its long-term impact, Cr(VI) has been listed as the first-class A toxic pollutant by the U.S. Environmental Protection Agency [3]. While Pb(II) acts as one of the most harmful heavy metals [4], plumbism by accumulation in human body can result in damages in brain, nervous, metabolic and reproductive system, even trigger sickness or death [5,6]. The bulk of these contaminations as effluents are discharged from several industries, including mining, batteries, textiles, metal plating, etc. [7].
Currently, more and more techniques have been developed and utilized for the removal of heavy metals from the aqueous environments, such as adsorption, electrochemistry, precipitation reaction, membrane filtration and biosorption processes [8,9]. Among these, the adsorption is an effective Damao Chemical Reagent Factory China (Tianjin, China) were used to control the pH through glass dropper bottles to eliminate the influence of the volume change of slurry. Different drops of HCl (3%, volume concentration) or NaOH (5%, mass concentration) were added to control the pH to the desired value. Ultrapure water was used throughout the study.

Rectorite Modification
Rectorite modification was conducted in a constant temperature oscillator with leaching as the main method. A certain amount of rectorite sample was added in the freshly prepared modifier Fe 3+ solution with a certain concentration, followed by the agitation with a constant temperature oscillator of 180 r/min speed under 30 °C. The modified rectorite sample (Fe-REC) was collected by the centrifugation, then washed several times with de-ionized water to remove the residual modifier and dried in a vacuum oven at 85 °C for 6 h.

Heavy Metal Ions Adsorption Test
The residual metal concentration of rectorite pulp after the adsorption process was determined by inductively coupled plasma spectrometer (ICP; Spectro, Kleve, Germany). During the measurements, the temperature was kept at 25 °C. The samples used in this adsorption test were prepared in the following order: at first, the modified sample Fe-REC was mixed simulated wastewater of 30 mg/L Cr(Ⅵ) and 40 mg/L Pb(II), respectively. Two kinds of mixtures were then shaken in the constant temperature oscillator for a while (10-70 min) to make the heavy metal ions adsorbed by Fe-REC efficiently. In the subsequent step, the liquid fraction that separated from the slurry was analyzed for the adsorption measurements. The procedure of modification and adsorption is provided in Figure 2. At last, the adsorbed amounts (represented by Γ) of Cr(Ⅵ) and Pb(II) by modified rectorite surface were calculated by using following equation: Where Γ is the adsorbed amount of heavy metal ions; C0 and C are the initial and residual concentrations (mg/L), respectively; Ferric chloride hexahydrate (FeCl 3 ·6H 2 O) was used for the modification of rectorite. Potassium dichromate (K 2 Cr 2 O 7 ) and lead nitrate (Pb(NO 3 ) 2 ) of chemical purity were used as simulated wastewater sources of the pollution respectively. In addition, HCl and NaOH of analytical grade from Damao Chemical Reagent Factory China (Tianjin, China) were used to control the pH through glass dropper bottles to eliminate the influence of the volume change of slurry. Different drops of HCl (3%, volume concentration) or NaOH (5%, mass concentration) were added to control the pH to the desired value. Ultrapure water was used throughout the study.

Rectorite Modification
Rectorite modification was conducted in a constant temperature oscillator with leaching as the main method. A certain amount of rectorite sample was added in the freshly prepared modifier Fe 3+ solution with a certain concentration, followed by the agitation with a constant temperature oscillator of 180 r/min speed under 30 • C. The modified rectorite sample (Fe-REC) was collected by the centrifugation, then washed several times with de-ionized water to remove the residual modifier and dried in a vacuum oven at 85 • C for 6 h.

Heavy Metal Ions Adsorption Test
The residual metal concentration of rectorite pulp after the adsorption process was determined by inductively coupled plasma spectrometer (ICP; Spectro, Kleve, Germany). During the measurements, the temperature was kept at 25 • C. The samples used in this adsorption test were prepared in the following order: at first, the modified sample Fe-REC was mixed simulated wastewater of 30 mg/L Cr(VI) and 40 mg/L Pb(II), respectively. Two kinds of mixtures were then shaken in the constant temperature oscillator for a while (10-70 min) to make the heavy metal ions adsorbed by Fe-REC efficiently. In the subsequent step, the liquid fraction that separated from the slurry was analyzed for the adsorption measurements. The procedure of modification and adsorption is provided in Figure 2. At last, the adsorbed amounts (represented by Γ) of Cr(VI) and Pb(II) by modified rectorite surface were calculated by using following equation: where Γ is the adsorbed amount of heavy metal ions; C 0 and C are the initial and residual concentrations (mg/L), respectively; Minerals 2020, 10, x FOR PEER REVIEW 4 of 17

Zeta Potential Test
Zeta potential measurements were conducted by a Coulter Delsa 440sx Zeta potential analyzer (Beckman Coulter, Beea, CA, USA) equipped with a rectangular electrophoresis cell. For the measurements, mineral samples were ground to -2 µm and the suspension was prepared by adding 40 mg of mineral samples to 80 mL desired solutions containing 1 mmol/L KNO3 as supporting electrolytes. Then, the suspension was conditioned by a magnetic stirring for 6 min to ensure adequate dispersion of the fine mineral particles. After settling for 10 min, the supernatant of the dilute fine particle suspension was taken for the zeta potential measurements.

XPS Analysis
X-ray Photoelectron Spectroscopy (XPS) with K-Alpha + (Thermo fisher Scientific, Waltham, MA, USA) was applied to analyze the composition and chemical state of the elements on the mineral surface before and after its modification and adsorption in order to characterize if the modifier Fe 3+ and the heavy metal ions Cr(Ⅵ) and Pb(II) were adsorbed effectively. The vacuum in the analysis room was kept at about 2 × 10 -7 mba and the X-ray source was monochromatic Al Ka at the energy of 72 W with 400 µm. Additionally, the scanning mode was decided as CAE. The energy step size of survey spectra and high-resolution spectra were 1.00 eV and 0.1 eV, respectively and their pass energy was set at 100 eV and 30 eV, respectively. All binding energies were calibrated using a characteristic C1s carbon peak (C1s = 284.7 eV). The sample was filtered and washed repeatedly with ultrapure water for washing away the weak physical adhesion of the reagent on the mineral surface. Afterwards, it was dried in a vacuum oven and then used for testing.

Description of Solution Chemistry Calculations
It is rather necessary to comprehend the occurrence state and physicochemical behavior of metal ions in the slurry. The adsorption of modifier Fe 3+ and heavy metal ions Cr(Ⅵ) and Pb(II) on the rectorite surface related to their dissolved state and hydrolyzed components to a degree. As a result, the solution compositions of Fe 3+ , Cr(Ⅵ) and Pb(II) were calculated to understand the mechanism of modification and adsorption. Metal ions can be hydrolyzed in the aqueous solution to form different

Zeta Potential Test
Zeta potential measurements were conducted by a Coulter Delsa 440sx Zeta potential analyzer (Beckman Coulter, Beea, CA, USA) equipped with a rectangular electrophoresis cell. For the measurements, mineral samples were ground to -2 µm and the suspension was prepared by adding 40 mg of mineral samples to 80 mL desired solutions containing 1 mmol/L KNO 3 as supporting electrolytes. Then, the suspension was conditioned by a magnetic stirring for 6 min to ensure adequate dispersion of the fine mineral particles. After settling for 10 min, the supernatant of the dilute fine particle suspension was taken for the zeta potential measurements.

XPS Analysis
X-ray Photoelectron Spectroscopy (XPS) with K-Alpha + (Thermo fisher Scientific, Waltham, MA, USA) was applied to analyze the composition and chemical state of the elements on the mineral surface before and after its modification and adsorption in order to characterize if the modifier Fe 3+ and the heavy metal ions Cr(VI) and Pb(II) were adsorbed effectively. The vacuum in the analysis room was kept at about 2 × 10 −7 mba and the X-ray source was monochromatic Al Ka at the energy of 72 W with 400 µm. Additionally, the scanning mode was decided as CAE. The energy step size of survey spectra and high-resolution spectra were 1.00 eV and 0.1 eV, respectively and their pass energy was set at 100 eV and 30 eV, respectively. All binding energies were calibrated using a characteristic C1s carbon peak (C1s = 284.7 eV). The sample was filtered and washed repeatedly with ultrapure water for washing away the weak physical adhesion of the reagent on the mineral surface. Afterwards, it was dried in a vacuum oven and then used for testing.

Description of Solution Chemistry Calculations
It is rather necessary to comprehend the occurrence state and physicochemical behavior of metal ions in the slurry. The adsorption of modifier Fe 3+ and heavy metal ions Cr(VI) and Pb(II) on the rectorite surface related to their dissolved state and hydrolyzed components to a degree. As a result, the solution compositions of Fe 3+ , Cr(VI) and Pb(II) were calculated to understand the mechanism of modification and adsorption. Metal ions can be hydrolyzed in the aqueous solution to form different hydroxy complexes. At this time, the concentration of each component can be calculated from the equilibrium relationship in the aqueous solution.
The species distribution of Fe 3+ in solutions was influenced by its pH and the initial concentration simultaneously. Homogeneous and heterogeneous systems were named before and after the precipitation reactions occurred, which were affected by the pH of solution. Different systems had different computing methods. In homogeneous ferric chloride solution system, the equilibrium reaction formulas and corresponding reaction coefficient were as follows [25]: The initial concentration of Fe 3+ and its side reaction coefficients were recorded as C Fe and α Fe 3+ , respectively, then: Subsequently, the species distribution of each component in homogeneous system was: In heterogeneous system, the species distribution of each component was: Fe(OH)

Modification of Rectorite
Different influencing factors were studied in Figure 3 to obtain the Fe-REC smoothly, such as the time of modification and the concentrations of Fe 3+ ions and pulp. Modification results were evaluated by the ability of modified rectorite to adsorb Cr(VI) ion in the solutions. As shown in Figure 3a, Fe 3+ concentration had important effects on the adsorption rate of Cr(VI). The Cr(VI) adsorption rate increased rapidly with the increasing Fe 3+ concentration up to 0.1 mol/L and then tended towards equilibrium with a further increase in doses of Fe 3+ . The optimum adsorption rate (about 89%) was obtained at the 0.1 mol/L Fe 3+ concentration. When it comes to the effect of pulp concentration in Figure 3b, the Cr(VI) adsorption rate increased slowly when the pulp concentration ranged from 50 to 300 g/L. As can be noted, there was a minor decrease in the Cr(VI) adsorption rate by increasing the pulp concentration from 200 to 300 g/L. Namely, the higher the pulp concentration, the slower the growth rate. Consequently, 200 g/L was defined as optimal pulp concentration value for REC modification. If REC was modified for a longer time (shown in Figure 3c), less and less Cr(VI) ions were adsorbed on the REC surface making the adsorption rate deteriorated evidently. Affected by modified time, the highest adsorption rate of 88.94% appeared at 3 h, which would be utilized as the fabrication time of Fe-REC. Overall, different factors had different effects on the modification results with the following sequence: Fe 3+ concentration > pulp concentration > modification time. In other words, the concentration of Fe 3+ had the greatest impact on the modification results while the modified time was the minimum.

Adsorption Studies
After the successful modification and obtaining Fe-REC, its adsorption performance on Cr(Ⅵ) and Pb(II) were investigated in the Figure 4 systematically. Figure 4a reflected the effect of pH on Cr(Ⅵ) and Pb(II) adsorption with REC and Fe-REC, respectively. As can be seen, the adsorption ability of Fe-REC was much better than that of the natural REC for both Cr(Ⅵ) and Pb(II), indicating that the Fe 3+ modification greatly contributed to its adsorption capacity. For Cr(Ⅵ) ions, the adsorption rate with Fe-REC declined significantly from acidic environment to basic, while there was almost no fluctuation with natural REC where the adsorption rate stabled at 55% approximately. If the mineral was modified by Fe 3+ , the natural pH of slurry was kept at 5 where the adsorption rate had approached 90%. Even though the pH of slurry was adjusted extremely acidic, the disparity to its natural pH was negligible. Hence there is no need to adjust the pulp pH for the sake of simplified experimental procedure. Compared with the Cr(Ⅵ) adsorption, there was an obvious difference in acidic and basic pulp for Pb(II) adsorption, in which the adsorption rate in basic pH was rather higher than that of the acidic no matter REC or Fe-REC. The main reason for this result was that in the presence of OH -, Pb(II) ions would react with OHto form Pb(OH)2 precipitate making it no significance for Pb(II) adsorption under alkaline environment. Like Cr(Ⅵ) adsorption, the optimum pH for Pb(II) adsorption was also fixed at its natural value. Figure 4 showed the effect of pulp concentration on the adsorption of Cr(Ⅵ) and Pb(II). Similar to Figure 4a, there was an evident phenomenon that the adsorption rate of Fe-REC was much higher than that of REC for simulated wastewater. For Cr(Ⅵ), the higher the pulp concentration, the higher adsorption rate of Fe-REC. When the pulp concentration rose to 70 g/L, the adsorption rate maintained stable gradually if it continued to increase. However, for Pb(II), only 40 g/L of pulp concentration was required for its excellent adsorption. By comparing Cr(Ⅵ) and Pb(II), the adsorption rate of Pb(II) was far better than that of Cr(Ⅵ), which could attribute to the larger ionic volume of Cr2O7 2-than that of Pb 2+ , not conducive to accommodate pollutants by the interlayer of rectorite and causing the lower adsorption rate finally.
The effect of adsorption time was presented in Figure 4c. Although the adsorption rate of Cr(Ⅵ) with REC was raised by increasing time, the results were much worse than Fe-REC. When the time

Adsorption Studies
After the successful modification and obtaining Fe-REC, its adsorption performance on Cr(VI) and Pb(II) were investigated in the Figure 4 systematically. Figure 4a reflected the effect of pH on Cr(VI) and Pb(II) adsorption with REC and Fe-REC, respectively. As can be seen, the adsorption ability of Fe-REC was much better than that of the natural REC for both Cr(VI) and Pb(II), indicating that the Fe 3+ modification greatly contributed to its adsorption capacity. For Cr(VI) ions, the adsorption rate with Fe-REC declined significantly from acidic environment to basic, while there was almost no fluctuation with natural REC where the adsorption rate stabled at 55% approximately. If the mineral was modified by Fe 3+ , the natural pH of slurry was kept at 5 where the adsorption rate had approached 90%. Even though the pH of slurry was adjusted extremely acidic, the disparity to its natural pH was negligible. Hence there is no need to adjust the pulp pH for the sake of simplified experimental procedure. Compared with the Cr(VI) adsorption, there was an obvious difference in acidic and basic pulp for Pb(II) adsorption, in which the adsorption rate in basic pH was rather higher than that of the acidic no matter REC or Fe-REC. The main reason for this result was that in the presence of OH -, Pb(II) ions would react with OHto form Pb(OH) 2 precipitate making it no significance for Pb(II) adsorption under alkaline environment. Like Cr(VI) adsorption, the optimum pH for Pb(II) adsorption was also fixed at its natural value. Figure 4 showed the effect of pulp concentration on the adsorption of Cr(VI) and Pb(II). Similar to Figure 4a, there was an evident phenomenon that the adsorption rate of Fe-REC was much higher than that of REC for simulated wastewater. For Cr(VI), the higher the pulp concentration, the higher adsorption rate of Fe-REC. When the pulp concentration rose to 70 g/L, the adsorption rate maintained stable gradually if it continued to increase. However, for Pb(II), only 40 g/L of pulp concentration was required for its excellent adsorption. By comparing Cr(VI) and Pb(II), the adsorption rate of Pb(II) was far better than that of Cr(VI), which could attribute to the larger ionic volume of Cr 2 O 7 2− than that of Pb 2+ , not conducive to accommodate pollutants by the interlayer of rectorite and causing the lower adsorption rate finally. The effect of adsorption time was presented in Figure 4c. Although the adsorption rate of Cr(VI) with REC was raised by increasing time, the results were much worse than Fe-REC. When the time was defined at 30 min, the adsorption with Fe-REC was close to saturation, about 92.43%. For Pb(II), the adsorption rate had a slight downward trend after 50 min and remained steady between 30 to 50 min. Thus, 30 min was chosen as the optimum time for the pollutant adsorption.   Figure 5 depicted the trend of rectorite zeta potential before and after its modification and adsorption with metal ions. Consistent with previous studies [26], the negative IEP (isoelectric point) value for the pure rectorite was -12.1 mV without any addition of reagents, indicating that zeta potential test was reliable. As shown in Figure 5, the potential on the REC surface decreased with the increasing pH and when the pH was 3.08, the potential was -0.25 mV, which was close to its PZC (point of zero charge). It could be concluded that the negative charge on the rectorite surface was almost neutralized. However, when the pulp was changed to more basic, the increasing high concentration of OH-made the potential more and more negative. When the REC was modified, namely Fe-REC, the zeta potentials exhibited a positive shift within the investigated pH range, which suggested that the positive Fe 3+ ions were apparently adsorbed to balance a portion of negative charge on the mineral surface. Similar to the tendency of REC, zeta potential of Fe-REC was still dropped with pH and at the natural pH, the value of potential was -2.21 mV, increased by 9.89 mV than that of REC, illustrating that the adsorption of Fe 3+ on rectorite surface had brought greater changes in potential. According to Figure 5, there was an obvious negative shift after negative Cr(Ⅵ) ions was adsorbed by Fe-REC and the natural potential reduced to -33.2 mV from -2.21 mV. This explained Cr(Ⅵ) was indeed adsorbed on Fe-REC surface, resulting in the change of potential. When the  Figure 5 depicted the trend of rectorite zeta potential before and after its modification and adsorption with metal ions. Consistent with previous studies [26], the negative IEP (isoelectric point) value for the pure rectorite was -12.1 mV without any addition of reagents, indicating that zeta potential test was reliable. As shown in Figure 5, the potential on the REC surface decreased with the increasing pH and when the pH was 3.08, the potential was -0.25 mV, which was close to its PZC (point of zero charge). It could be concluded that the negative charge on the rectorite surface was almost neutralized. However, when the pulp was changed to more basic, the increasing high concentration of OH-made the potential more and more negative. When the REC was modified, namely Fe-REC, the zeta potentials exhibited a positive shift within the investigated pH range, which suggested that the positive Fe 3+ ions were apparently adsorbed to balance a portion of negative charge on the mineral surface. Similar to the tendency of REC, zeta potential of Fe-REC was still dropped with pH and at the natural pH, the value of potential was -2.21 mV, increased by 9.89 mV than that of REC, illustrating that the adsorption of Fe 3+ on rectorite surface had brought greater changes in potential. According to Figure 5, there was an obvious negative shift after negative Cr(VI) ions was adsorbed by Fe-REC and the natural potential reduced to -33.2 mV from -2.21 mV. This explained Cr(VI) was indeed adsorbed on Fe-REC surface, resulting in the change of potential. When the positive Pb(II) ions were adsorbed on the Fe-REC surface, the zeta potential shifted positively, which illustrated some positive Pb(II) ions were adsorbed successfully, corresponding to its theoretical phenomena. . Figure 5. Zeta potential of rectorite before and after modification and adsorption.

XPS Analysis
Based on the chemical species on minerals surface and the distinctive binding energies of the inner electrons in each element, XPS analysis was performed to authenticate the interaction mechanism between the minerals and reagents [27]. The detailed values of atomic relative concentrations and binding energy of various components on the REC surface before and after some treatments are explained in this section. Table 2 illustrated that comparing REC with Fe-REC, it was visible for Fe 3+ to be adsorbed on the REC surface where the atomic relative concentration was about 1.38% causing the content of other mineral elements to decrease at the same time. This adsorption of Fe 3+ perfectly coincided with the result of zeta potential in Figure 5, in which it was specifically because of the Fe 3+ adsorption, making the potential on the REC surface shifted positively. Equally, 0.94% of Cr(Ⅵ) and 1.09% of Pb(II) occurred on the Fe-REC surface, respectively, after the treatment of adsorption by modified rectorite. Moreover, the adsorbed amount of Pb(II) was a little more than that of Cr(Ⅵ), agreeing with their adsorption tests in section 3.3 where the adsorption capacity on Pb(II) was better than that of Cr(Ⅵ).

XPS Analysis
Based on the chemical species on minerals surface and the distinctive binding energies of the inner electrons in each element, XPS analysis was performed to authenticate the interaction mechanism between the minerals and reagents [27]. The detailed values of atomic relative concentrations and binding energy of various components on the REC surface before and after some treatments are explained in this section. Table 2 illustrated that comparing REC with Fe-REC, it was visible for Fe 3+ to be adsorbed on the REC surface where the atomic relative concentration was about 1.38% causing the content of other mineral elements to decrease at the same time. This adsorption of Fe 3+ perfectly coincided with the result of zeta potential in Figure 5, in which it was specifically because of the Fe 3+ adsorption, making the potential on the REC surface shifted positively. Equally, 0.94% of Cr(VI) and 1.09% of Pb(II) occurred on the Fe-REC surface, respectively, after the treatment of adsorption by modified rectorite. Moreover, the adsorbed amount of Pb(II) was a little more than that of Cr(VI), agreeing with their adsorption tests in Section 3.3 where the adsorption capacity on Pb(II) was better than that of Cr(VI). The binding energy and its shift on the REC surface treated by modification and adsorption were depicted in Table 3. The shifts in binding energy of the studied elements mainly revealed that the Minerals 2020, 10, 176 9 of 16 reaction between Al species and Si species and their adsorption changed their chemical surrounding on REC surface. After the modification of REC, the shift of binding energy in O 1s was 0.37 eV, exceeding the measurement error range of 0.2 eV [28]. This shift meant the state of oxygen had undergone a chemical change during the adsorption of ferric chloride on the REC surface, indicating that the adsorption process of Fe 3+ was chemisorption. For the shift between Fe-REC and Fe-REC-Cr(VI), -0.87eV of O 1s and -1.23eV of Fe 2p drew attention easily to manifest oxygen and iron elements changed chemically during the Cr(VI) adsorption. However, for Fe-REC-Pb(II), except oxygen and iron elements, the binding energy in the silicate mineral elements of Al and Si also changed greatly with 0.81 eV and 0.33 eV, respectively. These findings demonstrated that it was chemisorption that occurred during the adsorptions of Cr(VI) and Pb(II).  Figure 6 showed XPS survey spectra of rectorite after modification and adsorption. From this figure, the emergence of Na and Ca elements was mainly due to interlayer cations of Na+ and Ca 2+ in the mica or montmorillonite unit layer [14]. When the REC was modified by Fe 3+ , significant characteristic peaks of Fe 2p appeared in XPS survey spectra, reflecting that the modifier Fe 3+ had a strong adsorption on the surface of REC. As a comparison, we could not detect any weak peaks of Cr(VI) and Pb(II) appeared on the Fe-REC surface after their adsorption. This may result from only a trace of chromium and lead elements adsorbed on Fe-REC surface was covered up by miscellaneous peaks easily owing to 1% detection accuracy of XPS. However, the adsorption of Cr(VI) and Pb(II) was demonstrated in Tables 2 and 3.   Figure 6. XPS survey spectra of rectorite before after modification and adsorption.
The high-resolution XPS spectra of Fe 2p in modified rectorite were shown in Figure 7 was reliable on account of better fitting results between raw intensity and peak sum. The main Fe 2p doublets peak of Fe 2p3/2 and Fe 2p1/2 appeared at 710.12 eV and 723.94 eV, respectively. The peaks at 714.85 eV and 730.49 eV were attributed to the satellite of Fe 2p3/2 and Fe 2p1/2. These main peaks of Fe 2p were assigned to the oxidation state of Fe(III) [29][30][31], which further demonstrated the formation of Fe-O, Fe-OH and Fe-OOH on the Fe-REC surface. This conclusion explained why the binding energy of oxygen element changed dramatically during the modification of REC in Table 3. The high-resolution XPS spectra of Fe 2p in modified rectorite were shown in Figure 7 was reliable on account of better fitting results between raw intensity and peak sum. The main Fe 2p doublets peak of Fe 2p3/2 and Fe 2p1/2 appeared at 710.12 eV and 723.94 eV, respectively. The peaks at 714.85 eV and 730.49 eV were attributed to the satellite of Fe 2p3/2 and Fe 2p1/2. These main peaks of Fe 2p were assigned to the oxidation state of Fe(III) [29][30][31], which further demonstrated the formation of Fe-O, Fe-OH and Fe-OOH on the Fe-REC surface. This conclusion explained why the binding energy of oxygen element changed dramatically during the modification of REC in Table 3. Binding energy (eV) Figure 6. XPS survey spectra of rectorite before after modification and adsorption.
The high-resolution XPS spectra of Fe 2p in modified rectorite were shown in Figure 7 was reliable on account of better fitting results between raw intensity and peak sum. The main Fe 2p doublets peak of Fe 2p3/2 and Fe 2p1/2 appeared at 710.12 eV and 723.94 eV, respectively. The peaks at 714.85 eV and 730.49 eV were attributed to the satellite of Fe 2p3/2 and Fe 2p1/2. These main peaks of Fe 2p were assigned to the oxidation state of Fe(III) [29][30][31], which further demonstrated the formation of Fe-O, Fe-OH and Fe-OOH on the Fe-REC surface. This conclusion explained why the binding energy of oxygen element changed dramatically during the modification of REC in Table 3.

Solution Chemistry Calculations
The hydroxyl complexation of Fe 3+ in solution mainly exhibits in Table 4 [31]. According to the Equations (3)-(7) and (8)- (13), the species distribution of each component in the ferric chloride solution (0.1 mol/L) in different systems could be calculated and the result was shown in Figure 8. Table 4. Equilibrium reaction and corresponding coefficients of different ions.

Reactions Reaction Constants
Fe(III) (17) Cr(VI) (23) Similar computing methods can also be applied in the species distribution of Cr(VI) and Pb(II), and both of their equilibrium reaction formulas and corresponding reaction coefficients were displayed in Table 4 [32,33]. Based on Table 4, the species distributions of 2.72 × 10 −4 mol/L Cr(VI) and 0.91 × 10 −4 mol/L Pb(II) were described in Figures 9 and 10. From Figure 8, the forms of Fe 3+ in solution were mainly iron hydroxy complexes owing to 4-5 pH in the slurry solution, consisting of FeOH 2+ , Fe(OH) 2 + and Fe(OH) 3 (aq). At the same time, the main species distribution of 2.72 × 10 −4 mol/L Cr(VI) in Figure 9 in the same pH range were HCrO 4 − and CrO 4 2− . Under this circumstance, the iron hydroxy complex (FeOH 2+ , Fe(OH) 2 + and Fe(OH) 3 (aq)) would react with HCrO 4 − and CrO 4 2− to promote the Cr(VI) adsorption on the Fe-REC surface according to the following equation [34]: Minerals 2020, 10, x; doi: FOR PEER REVIEW www.mdpi.com/journal/minerals Similar computing methods can also be applied in the species distribution of Cr(Ⅵ) and Pb(II), and both of their equilibrium reaction formulas and corresponding reaction coefficients were displayed in Table 4 [32,33]. Based on Table 4, the species distributions of 2.72 × 10 -4 mol/L Cr(Ⅵ) and 0.91 × 10 -4 mol/L Pb(II) were described in Figures 9 and 10. From Figure 8, the forms of Fe 3+ in solution were mainly iron hydroxy complexes owing to 4-5 pH in the slurry solution, consisting of FeOH 2+ , Fe(OH)2 + and Fe(OH)3(aq). At the same time, the main species distribution of 2.72 × 10 -4 mol/L Cr(Ⅵ) in Figure 9 in the same pH range were HCrO4 -and CrO4 2-. Under this circumstance, the iron hydroxy complex (FeOH 2+ , Fe(OH)2 + and Fe(OH)3(aq)) would react with HCrO4 -and CrO4 2-to promote the Cr(Ⅵ) adsorption on the Fe-REC surface according to the following equation [34]: Therefore, this explained why the binding energy of Fe and Cr elements happened to change over 0.2 eV during the Cr(Ⅵ) adsorption in XPS analysis (shown in Table 3).  Illustrated by Figure 10, the species distribution of 0.91 × 10 -4 mol/L lead ions solution were primarily Pb 2+ and PbOH + for pH ranging from 4 to 5. Owing to the existence of -Al-OH and -Si-OH of silicate rectorite in the slurry, these groups would react with the main species of Pb(II) as below [35]: where SOH represents -Al-OH and -Si-OH; SOdenotes forms of SOH losing H + . As a result, the adsorption mechanism of Pb(II) on the Fe-REC surface was as followed. The solid-liquid interface induced the hydrolysis of Pb to generate the PbOH + colloid with a positive charge, which would interact with negatively charged aluminosilicate to ultimately improve the Pb(II) adsorption, accordant with the results in XPS analysis (Table 3) where the binding energy of aluminum and silicon elements varied greatly during the process of Pb(II) adsorption. In this Therefore, this explained why the binding energy of Fe and Cr elements happened to change over 0.2 eV during the Cr(VI) adsorption in XPS analysis (shown in Table 3).
Illustrated by Figure 10, the species distribution of 0.91 × 10 −4 mol/L lead ions solution were primarily Pb 2+ and PbOH + for pH ranging from 4 to 5. Owing to the existence of -Al-OH and -Si-OH of silicate rectorite in the slurry, these groups would react with the main species of Pb(II) as below [35]: where SOH represents -Al-OH and -Si-OH; SOdenotes forms of SOH losing H + . As a result, the adsorption mechanism of Pb(II) on the Fe-REC surface was as followed. The solid-liquid interface induced the hydrolysis of Pb to generate the PbOH + colloid with a positive charge, which would interact with negatively charged aluminosilicate to ultimately improve the Pb(II) adsorption, accordant with the results in XPS analysis (Table 3) where the binding energy of aluminum and silicon elements varied greatly during the process of Pb(II) adsorption. In this scenario, the role of Fe 3+ was to weaken interlayer bond force to enhance the Pb(II) adsorption.
Minerals 2020, 10, x; doi: FOR PEER REVIEW www.mdpi.com/journal/minerals primarily Pb 2+ and PbOH + for pH ranging from 4 to 5. Owing to the existence of -Al-OH and -Si-OH of silicate rectorite in the slurry, these groups would react with the main species of Pb(II) as below [35]: where SOH represents -Al-OH and -Si-OH; SOdenotes forms of SOH losing H + . As a result, the adsorption mechanism of Pb(II) on the Fe-REC surface was as followed. The solid-liquid interface induced the hydrolysis of Pb to generate the PbOH + colloid with a positive charge, which would interact with negatively charged aluminosilicate to ultimately improve the Pb(II) adsorption, accordant with the results in XPS analysis (Table 3) where the binding energy of aluminum and silicon elements varied greatly during the process of Pb(II) adsorption. In this scenario, the role of Fe 3+ was to weaken interlayer bond force to enhance the Pb(II) adsorption.

Adsorption Isotherms
In aqueous solution, Langmuir and Freundlich models are usually used for the adsorption isotherms of heavy metal ions. What Langmuir isotherm assumes is the monolayer adsorption onto a uniform solid surface with no transmigration of adsorbate on the plane surface [36]. The isotherm is represented by [37] C e q e = C e q m + 1 K L q m (27) where C e is equilibrium concentration, mg/L; q e is equilibrium adsorption capacity, mg/g; q m is maximum adsorption capacity, mg/g; K L is adsorption energy, L/g; The linear plot of specific adsorption (C e /q e ) against the equilibrium concentration (C e ) shows that the adsorption obeys the Langmuir model. Values of q m and the constant K L can be acquired from the slope and interception of the plot, respectively. Freundlich is applied as an empirical model in which the isotherm is represented by [38] log q e = logK F + 1 n logC e (28) where adsorption capacity K F and adsorption intensity n are parameters that depend on the adsorbate and adsorbent, determined from the plot of logq e versus logC e . On the basis of the above Equations (27)-(28), Langmuir and Freundlich isotherms for Cr(VI) and Pb(II) adsorption are provided in Figures 11 and 12, respectively. In addition, their constants and correlation coefficients (R 2 ) are presented in Table 5. When it comes to Cr(VI) adsorption, the result of Freundlich isotherm (R 2 = 0.9908) was superior to that of Langmuir (R 2 = 0.9618), indicating that the isothermal adsorption of Cr(VI) was more compatible with Freundlich model. There is the reference to prove that if the n value in Freundlich model ranges from 1 to 10, the adsorption process will be effective [39]. Thus, the Cr(VI) adsorption process on the Fe-REC surface happened effectively (n = 3.2146). For Pb(II) adsorption, it was more consistent with Langmuir isotherm (R 2 = 0.9959) by comparing two kinds of models and the maximum adsorption capacity of Pb(II) was 1.3509 mg/g. On the basis of the above Equations (27)-(28), Langmuir and Freundlich isotherms for Cr(Ⅵ) and Pb(II) adsorption are provided in Figures 11 and 12, respectively. In addition, their constants and correlation coefficients (R 2 ) are presented in Table5. When it comes to Cr(Ⅵ) adsorption, the result of Freundlich isotherm (R 2 = 0.9908) was superior to that of Langmuir (R 2 = 0.9618), indicating that the isothermal adsorption of Cr(Ⅵ) was more compatible with Freundlich model. There is the reference to prove that if the n value in Freundlich model ranges from 1 to 10, the adsorption process will be effective [39]. Thus, the Cr(Ⅵ) adsorption process on the Fe-REC surface happened effectively (n = 3.2146). For Pb(II) adsorption, it was more consistent with Langmuir isotherm (R 2 = 0.9959) by comparing two kinds of models and the maximum adsorption capacity of Pb(II) was 1.3509 mg/g. Table 5. Isotherm parameters for Cr(Ⅵ) and Pb(II) adsorption by Fe-REC.    The model of modification and adsorption was shown in Figure 13 where some cations (Na + , K + and Ca 2+ ) were distributed on the surface of layered rectorite. When ferric chloride hexahydrate was added into the pulp, Fe 3+ would be adsorbed on the REC surface as its oxidation state (Fe-O), which can be proved by the significant characteristic peaks of Fe 2p appeared in XPS survey spectra. Since the interlayer bond force of rectorite was weakened, more produced vacancy promoted the Pb(II) adsorption significantly. In addition, the reactions between PbOH + and -AlOH or -SiOH also contributed to its adsorption capacity tremendously. The Cr(VI) adsorption process resulted from its main species in aqueous solution reacted with the Fe-O (FeOH 2+ , Fe(OH)2 + and Fe(OH)3(aq)) on the REC surface. Therefore, rectorite modification with Fe(III) can improve the removal of heavy metal ions distinctly. The model of modification and adsorption was shown in Figure 13 where some cations (Na + , K + and Ca 2+ ) were distributed on the surface of layered rectorite. When ferric chloride hexahydrate was added into the pulp, Fe 3+ would be adsorbed on the REC surface as its oxidation state (Fe-O), which can be proved by the significant characteristic peaks of Fe 2p appeared in XPS survey spectra. Since the interlayer bond force of rectorite was weakened, more produced vacancy promoted the Pb(II) adsorption significantly. In addition, the reactions between PbOH + and -AlOH or -SiOH also contributed to its adsorption capacity tremendously. The Cr(VI) adsorption process resulted from its main species in aqueous solution reacted with the Fe-O (FeOH 2+ , Fe(OH) 2 + and Fe(OH) 3 (aq)) on the REC surface. Therefore, rectorite modification with Fe(III) can improve the removal of heavy metal ions distinctly.

Metals Ions
Minerals 2020, 10, x; doi: FOR PEER REVIEW www.mdpi.com/journal/minerals the interlayer bond force of rectorite was weakened, more produced vacancy promoted the Pb(II) adsorption significantly. In addition, the reactions between PbOH + and -AlOH or -SiOH also contributed to its adsorption capacity tremendously. The Cr(VI) adsorption process resulted from its main species in aqueous solution reacted with the Fe-O (FeOH 2+ , Fe(OH)2 + and Fe(OH)3(aq)) on the REC surface. Therefore, rectorite modification with Fe(III) can improve the removal of heavy metal ions distinctly.

Conclusions
This investigation showed that the novel modifier Fe 3+ chemisorption on the REC surface improved its adsorption capacity for Cr(VI) and Pb(II). For Fe-REC, the potential exhibited a positive shift within the studied pH range. In the XPS survey spectra, significant characteristic peaks of Fe 2p appeared, which was the oxidation state of Fe(III) (Fe-O, Fe-OH, Fe-OOH) formed on the Fe-REC surface.
The Cr(VI) adsorption mechanism was mainly due to the reaction between the iron hydroxy complex of modifier (FeOH 2+ , Fe(OH)2 + and Fe(OH)3(aq)) and the major components of hexavalent chromium solution (HCrO4 -and CrO4 2-) to promote its adsorption behavior. From zeta potential results, there was an obvious negative shift after Cr(VI) ions was adsorbed by Fe-REC and the natural potential reduced to -33.2 mV from -2.21 mV. In XPS analysis, the binding energy of O 1s and Fe 2p changed a lot. This resulted in chemical changes of oxygen and iron elements during its adsorption. This adsorption process was consisted with Freundlich isotherm.

Conclusions
This investigation showed that the novel modifier Fe 3+ chemisorption on the REC surface improved its adsorption capacity for Cr(VI) and Pb(II). For Fe-REC, the potential exhibited a positive shift within the studied pH range. In the XPS survey spectra, significant characteristic peaks of Fe 2p appeared, which was the oxidation state of Fe(III) (Fe-O, Fe-OH, Fe-OOH) formed on the Fe-REC surface.
The Cr(VI) adsorption mechanism was mainly due to the reaction between the iron hydroxy complex of modifier (FeOH 2+ , Fe(OH) 2 + and Fe(OH) 3 (aq)) and the major components of hexavalent chromium solution (HCrO 4 − and CrO 4 2− ) to promote its adsorption behavior. From zeta potential results, there was an obvious negative shift after Cr(VI) ions was adsorbed by Fe-REC and the natural potential reduced to -33.2 mV from -2.21 mV. In XPS analysis, the binding energy of O 1s and Fe 2p changed a lot. This resulted in chemical changes of oxygen and iron elements during its adsorption. This adsorption process was consisted with Freundlich isotherm. While for Pb(II), there was PbOH + colloid appeared due to the lead ions hydrolysis induced by the solid liquid interface. It would react with the groups of -Al-OH and -Si-OH in silicate REC slurry, profiting Pb(II) adsorption. Zeta potential shifted positively after Pb(II) adsorption, corresponding to its theoretical phenomena. In XPS analysis, binding energy in silicate elements of Al and Si changed greatly (0.81 eV and 0.33 eV) to explain its adsorption mechanism. The Pb(II) adsorption was more accordant with Langmuir isotherm and its maximum adsorption capacity was 1.3509 mg/g.