Mineralogical and Leaching Characteristics of Altered Ilmenite Beach Placer Sands

In order to have a good understanding of the treatment process and improvement on the market value of ilmenite beach placer sands, knowledge of its mineral composition and phase distribution is fundamental. In this study, a combination of characterization techniques including high-resolution scanning electron microscopy (HR-SEM), high-resolution transmission electron (HR-TEM) microscope, and X-ray diffraction (XRD) techniques was used to understand the mineralogical characteristics of ilmenite beach placer sands obtained from Richards Bay, South Africa. The mineral phase constituents of the ilmenite beach placer sands were studied before pre-oxidation and additive leaching in a chloride environment. During observations using XRD and HR-SEM, the ilmenite beach placer sands exhibited signature rhombohedral crystal form and crescentic pits with evidence of alteration phases. The characterized pre-oxidized ilmenite showed the presence of a ferric oxide film deposit of the particles. The leaching characteristics of both raw and pre-oxidized ilmenite was studied in the presence of additives. The leaching efficiency of the pre-oxidized ilmenite in the presence of additives increased by 20% at atmospheric conditions. The characterized residues show the improved amenability of pre-oxidized leach in chloride media. The formation of new phases containing pseudo-rutile indicated crystallographic disintegration by the movement of atoms during dissolution. Some particles retained the crescentic pit and the subangular grain structure; however, the phase changes were observed at the grain boundaries and grain edges. The leached residue’s EDS results still indicated the presence of pseudo-rutile and some minor unreacted oxides such as SiO2, Al2O3, and other trace metals. The trace metals impurities present in the as-received ilmenite were reduced by 80% in the final residue after the leaching.


Introduction
Synthetic rutile production from ilmenite has gained momentum with increasing demand in pigment production, ceramics, coverings, and pharmaceutical applications [1,2]. With the scarcity of natural rutile, ilmenite and its alteration products have become a significant source of synthetic rutile and the titanium final product. Given the lucrative properties of titanium and titanium-based products, the rise in exploiting the heavy mineral sands is high. More than half of the global reserves of ilmenite are situated in both South Africa and Australia [3,4]. Ilmenite is mined from altered igneous rocks. These beach placer sands are extracted from the nearby dunes by dredging and gravity concentration

Mineralogical Studies on the Ilmenite Beach Placer Sands
The ilmenite samples used in this study were ilmenite beach placer sands collected from Richards Bay Minerals in South Africa. The particle size distribution of the sands was determined using the Malvern particle size analyzer and confirmed by the standard laboratory Tyler series sieves as both methods determine the cut size. The X-ray fluorescence spectrometry technique was used to determine the ilmenite sands' chemical composition, while the phases within the sand were identified using the X-Ray diffractometer technique using the PANalytical Empyrean Powder X-ray diffraction. The morphologies and the backscattered electrons of the sand were observed using a Jeol HR-SEM (model JSM 7600F, JEOL, Akishima, Japan), and the elemental compositions were mapped using energy dispersive spectrometry (EDS) techniques.

Pre-Oxidation and Leaching Studies
The ilmenite was pre-oxidized by heating the material to 817 • C in a muffle furnace in the presence of oxygen. The ramping furnace rate was 100 • C/h. The pre-oxidized ilmenite sands were air-cooled to Minerals 2020, 10, 1022 3 of 18 room temperature. The PANalytical Empyrean powder X-ray diffraction determined the phase analyses, and the morphology of the pre-oxidized ilmenite was observed using a Jeol HR-SEM (high-resolution scanning microscope) (model JSM 7600F). The Jeol HR-TEM (high resolution-transmission microscope) was used to determine the crystallographic structure of the material. Figure 1 shows a schematic overview of the leaching process. Ilmenite was leached using a 500 mL reactor placed on a heated plate. A mechanical stirrer with a maximum speed of 450 rpm was used to keep the slurry suspended during the experiment. De-ionized (DI) water was used to make up the slurry, and anhydrous hydrochloric acid was dosed to regulate the pH of the solution. The leaching was carried out at atmospheric pressure varying parameters such as temperature, acid concentration, agitation, solid to liquid ratio, and the residence time. The pH meter with a temperature gauge was used to measure both temperature and the pH. Magnesium sulfate was introduced at varying volumes and concentrations as a catalyst. Metallic iron was also introduced to the solution as a reducing agent. The pregnant leach solution was sampled intermittently at 30 min intervals for the duration of the leaching cycle. For statistical viability, the tests were repeated three times. Ammonium difluoride (NH 4 HF 4 ) was used as an additive because of its ability to attack the glassy silica component that forms during leaching.
Minerals 2020, 10, x FOR PEER REVIEW 3 of 20 SEM (high-resolution scanning microscope) (model JSM 7600F). The Jeol HR-TEM (high resolutiontransmission microscope) was used to determine the crystallographic structure of the material. Figure 1 shows a schematic overview of the leaching process. Ilmenite was leached using a 500 mL reactor placed on a heated plate. A mechanical stirrer with a maximum speed of 450 rpm was used to keep the slurry suspended during the experiment. De-ionized (DI) water was used to make up the slurry, and anhydrous hydrochloric acid was dosed to regulate the pH of the solution. The leaching was carried out at atmospheric pressure varying parameters such as temperature, acid concentration, agitation, solid to liquid ratio, and the residence time. The pH meter with a temperature gauge was used to measure both temperature and the pH. Magnesium sulfate was introduced at varying volumes and concentrations as a catalyst. Metallic iron was also introduced to the solution as a reducing agent. The pregnant leach solution was sampled intermittently at 30 min intervals for the duration of the leaching cycle. For statistical viability, the tests were repeated three times. Ammonium difluoride (NH4HF4) was used as an additive because of its ability to attack the glassy silica component that forms during leaching.
The leaching efficiency is calculated based on the amount of iron and impurities removed from ilmenite. The pregnant leach solution was characterized using ICP-OES (inductively coupled plasmaoptical emission spectrometry). The residue was characterized using a Jeol HR-SEM (model JSM 7600F) and Jeol HR-TEM. Equation (1) shows the reaction involved during leaching.

Mineralogy of As-Received Ilmenite
In Figure 2, the particle size distribution means that a particle size (d50) of 136 µm was observed. The diffraction patterns of each particle size range of the as-received ilmenite are shown in Figure 3. The background peaks and peak position in the diffractogram showed ilmenite (FeTiO3), rutile (TiO2), The leaching efficiency is calculated based on the amount of iron and impurities removed from ilmenite. The pregnant leach solution was characterized using ICP-OES (inductively coupled plasma-optical emission spectrometry). The residue was characterized using a Jeol HR-SEM (model JSM 7600F) and Jeol HR-TEM. Equation (1) shows the reaction involved during leaching.

Mineralogy of As-Received Ilmenite
In Figure 2, the particle size distribution means that a particle size (d50) of 136 µm was observed. The diffraction patterns of each particle size range of the as-received ilmenite are shown in Figure 3. The background peaks and peak position in the diffractogram showed ilmenite (FeTiO 3 ), rutile (TiO 2 ), and silica (SiO 2 ) as the major mineral phases in both finer and coarse fractions. The lower-sized fractions (−106, −75-micrometer size) showed the (Fe 2 )SiO 4 iron-silicate phase. The silicate phase in ilmenite deposits hosts impurity inclusions as it is the major gangue mineral phase. In line with XRD results, the chemical composition of as-received ilmenite material shown in Table 1  and silica (SiO2) as the major mineral phases in both finer and coarse fractions. The lower-sized fractions (−106, −75-micrometer size) showed the (Fe2)SiO4 iron-silicate phase. The silicate phase in ilmenite deposits hosts impurity inclusions as it is the major gangue mineral phase. In line with XRD results, the chemical composition of as-received ilmenite material shown in Table 1 comprises 48.23% Fe2O3 and 42.93% TiO2. The results showed that SiO2 (2.94%), Al2O3 (1.71%), and MnO (1.11%) represent the gangue minerals; however, the crystalline structure of MnO and Al2O3 could not be detected by XRD as they were below the detection limit. Other associated gangue materials were observed as traces <1%. The presence of Al2O3 and SiO2 further suggested that there was an alteration of the ilmenite mineralogical structure. The alumina and silica enrichment facilitates impurity inclusions within the structure post-deposition.     . Diffractometer patterns of as-received ilmenite samples at different particle size (µm) ranges with black (−75 µm) red(+75 µm) blue (+106 µm) green (+150 µm) pink (before sieving).
The particle size and shape identification by high-resolution scanning electron microscope (HR-SEM) analysis is shown in Figure 4. At lower magnification (×100), the observed embedded micrographs show an elongated shape feature of ilmenite. Ilmenite crystalline structure is rhombohedral as per the observation; the particle size ranges from 50-200 µm. The tiny grooves (pits) and veins observed at higher magnification (×500, ×1000) suggest the migration of atoms from the crystalline structural lattice further confirms mineralogical alteration of the material. The abrasion and cracks observed are a result of the particle to particle impact and collision during transportation from the sea bed. . Diffractometer patterns of as-received ilmenite samples at different particle size (µm) ranges with black (−75 µm) red (+75 µm) blue (+106 µm) green (+150 µm) pink (before sieving).
The particle size and shape identification by high-resolution scanning electron microscope (HR-SEM) analysis is shown in Figure 4. At lower magnification (×100), the observed embedded micrographs show an elongated shape feature of ilmenite. Ilmenite crystalline structure is rhombohedral as per the observation; the particle size ranges from 50-200 µm. The tiny grooves (pits) and veins observed at higher magnification (×500, ×1000) suggest the migration of atoms from the crystalline structural lattice further confirms mineralogical alteration of the material. The abrasion and cracks observed are a result of the particle to particle impact and collision during transportation from the sea bed. The cross-sectioned particle micrograph ( Figure 5) shows the pits protruding through the minerals structure. The suggested atoms migration is evident as there are spots that show darker colors than the original structure. The migration leaves pits allowing impurity atoms to deposit on the empty sites. The backscattering electron micrographs ( Figure 6) shows the different minerals' phases within the ilmenite structure. Using the elemental mapping technique (Figure 7), the ilmenite phase is concentrated on the grey colored phase, silica (dark black) and alumina (light grey) are inter-deposited within the ilmenite grain on the pits.
Similar to the XRD and XRF results, the EDS elemental mapping micrographs (Figure 7) show the presence of impurity inclusion within the ilmenite structure, confirming the assertion of the material mineralogical orientation has been altered. According to Buick and Dunlop [22], ilmenites have corundum structures with oxygen anions in the hexagonal tightly packed lattice and Fe and Ti cations occupying two-thirds of the interstices. Typically the ilmenite alterations and deposits in the Richards Bay area have chemical compositions containing a wide range of elements (Ca 2+ , Mn 2+ , Fe 3+ ), which can substitute the Fe 2+ in the lattice structure [23]. The manganese substitutions in the weathering transformation phase (pseudorutile) occur in the range of 0.6-1%, which is similar to what is observed in the chemical composition of this material [24]. The cross-sectioned particle micrograph ( Figure 5) shows the pits protruding through the minerals structure. The suggested atoms migration is evident as there are spots that show darker colors than the original structure. The migration leaves pits allowing impurity atoms to deposit on the empty sites. The backscattering electron micrographs ( Figure 6) shows the different minerals' phases within the ilmenite structure. Using the elemental mapping technique (Figure 7), the ilmenite phase is concentrated on the grey colored phase, silica (dark black) and alumina (light grey) are interdeposited within the ilmenite grain on the pits.   The cross-sectioned particle micrograph ( Figure 5) shows the pits protruding through the minerals structure. The suggested atoms migration is evident as there are spots that show darker colors than the original structure. The migration leaves pits allowing impurity atoms to deposit on the empty sites. The backscattering electron micrographs ( Figure 6) shows the different minerals' phases within the ilmenite structure. Using the elemental mapping technique (Figure 7), the ilmenite phase is concentrated on the grey colored phase, silica (dark black) and alumina (light grey) are interdeposited within the ilmenite grain on the pits.  . Backscattered electron micrograph of as-received ilmenite (a) charged particle (b) crosssectioned particle.
Similar to the XRD and XRF results, the EDS elemental mapping micrographs ( Figure 7) show the presence of impurity inclusion within the ilmenite structure, confirming the assertion of the material mineralogical orientation has been altered. According to Buick and Dunlop [22], ilmenites have corundum structures with oxygen anions in the hexagonal tightly packed lattice and Fe and Ti cations occupying two-thirds of the interstices. Typically the ilmenite alterations and deposits in the Richards Bay area have chemical compositions containing a wide range of elements (Ca 2+ , Mn 2+ , Fe 3+ ), which can substitute the Fe 2+ in the lattice structure [23]. The manganese substitutions in the weathering transformation phase (pseudorutile) occur in the range of 0.6-1%, which is similar to what is observed in the chemical composition of this material [24]. Backscattered electron micrograph of as-received ilmenite (a) charged particle (b) cross-sectioned particle. Changes in the mineralogical orientation of deposits create new dynamics in the structure's amenability to leaching. The impurity amounts shown in Figures 6 and 7 determine the weathering and process's extent, which affects the quality and recoverability of ilmenite.
The TEM micrographs (Figure 8) of the as-received ilmenite indicated the ilmenite deposit's polycrystalline nature. The latticed-spacing of the ilmenite shown in Figure 8 is 0.3740 nm. The mineral is in plate form with spiky and cracked morphology. The cracks observed penetrate deeper in the particle to the 250 nm size range. Due to the visible cracks, the particle has been altered, alteration of individual particles occurs along the rims and cracks as iron is readily displaced from Changes in the mineralogical orientation of deposits create new dynamics in the structure's amenability to leaching. The impurity amounts shown in Figures 6 and 7 determine the weathering and process's extent, which affects the quality and recoverability of ilmenite.
The TEM micrographs (Figure 8) of the as-received ilmenite indicated the ilmenite deposit's polycrystalline nature. The latticed-spacing of the ilmenite shown in Figure 8 is 0.3740 nm. The mineral is in plate form with spiky and cracked morphology. The cracks observed penetrate deeper in the particle to the 250 nm size range. Due to the visible cracks, the particle has been altered, alteration of individual particles occurs along the rims and cracks as iron is readily displaced from the lattice.

Pre-Oxidized Ilmenite Mineralogy
The pre-oxidized ilmenite micrographs ( Figure 9) show the ferric oxide phase's presence emanating from the oxidation process. The gradual formation of the Fe2O3·2TiO2 intermediate phase (Equation (2)) can be observed at a temperature of 800 °C. The relatively smooth and homogeneous surface morphology with eccentric pits (Figure 9) allows the Fe2O3 content of the intermediate phase to further break down to ferric oxide, which is amenable to leaching. McConville and Lee [25] reported the breaking down of the pseudo rutile at temperatures between 600 °C and 900 °C to form hematite and rutile due to diffusion during prolonged heating promoting the breakdown from the primary ilmenite particles changing the surface morphology of the particles creating a porous structure on the surfaces. The formation of the porous structure would favor the diffusion of the lixiviant during leaching. Figure 9. Pre-oxidized ilmenite backscattered electron micrographs at different magnification.

Leaching Characteristics
It is well established that the additives and reductants significantly affect the leaching efficiency of ilmenite from the electrochemical results. The response of as-received and pre-oxidized ilmenite

Pre-Oxidized Ilmenite Mineralogy
The pre-oxidized ilmenite micrographs ( Figure 9) show the ferric oxide phase's presence emanating from the oxidation process. The gradual formation of the Fe 2 O 3 ·2TiO 2 intermediate phase (Equation (2)) can be observed at a temperature of 800 • C. The relatively smooth and homogeneous surface morphology with eccentric pits (Figure 9) allows the Fe 2 O 3 content of the intermediate phase to further break down to ferric oxide, which is amenable to leaching. McConville and Lee [25] reported the breaking down of the pseudo rutile at temperatures between 600 • C and 900 • C to form hematite and rutile due to diffusion during prolonged heating promoting the breakdown from the primary ilmenite particles changing the surface morphology of the particles creating a porous structure on the surfaces. The formation of the porous structure would favor the diffusion of the lixiviant during leaching.

Leaching Characteristics
It is well established that the additives and reductants significantly affect the leaching efficiency of ilmenite from the electrochemical results. The response of as-received and pre-oxidized ilmenite to additive and reductive leaching was studied in a series of test works performed at atmospheric conditions. Figure 10 shows the leaching efficiency of ilmenite over time. It can be observed that when only metallic iron is added to the solution, the leaching efficiency of ilmenite is the lowest for both as-received and pre-oxidized samples. The NH 4 HF 4 substantially increased the as-received ilmenite leaching efficiency. The active HF component etches the passivation layer formed during leaching allowing interface reaction to continue increasing the dissolution rate of ilmenite. It can be noted that the pre-oxidized ilmenite response to leaching supersedes that of the as-received ilmenite at atmospheric conditions. In the same Figure 10, the leaching efficiency of the pre-oxidized ilmenite for all additives increased compared to the as-received ilmenite. The porous structure attained during the pre-oxidation step favors the solid-liquid interaction process during the ilmenite leaching process.
The micropores enhance the mass transfer rate of leaching reagents through the ferric oxide layer promoting the dissolution reaction. Therefore, this validates the assertion by Liu and Xiang [26] that the exposure of hematite through pre-oxidation promotes dissolution and untreated ilmenite has low reactivity to HCl. Mahamoud et al. [19] reported that the addition of metallic iron reduces the dissolved Fe 3+ to Fe 2+ and significantly improves the iron dissolution rate.
The pre-oxidized ilmenite micrographs (Figure 9) show the ferric oxide phase's presence emanating from the oxidation process. The gradual formation of the Fe2O3·2TiO2 intermediate phase (Equation (2)) can be observed at a temperature of 800 °C. The relatively smooth and homogeneous surface morphology with eccentric pits (Figure 9) allows the Fe2O3 content of the intermediate phase to further break down to ferric oxide, which is amenable to leaching. McConville and Lee [25] reported the breaking down of the pseudo rutile at temperatures between 600 °C and 900 °C to form hematite and rutile due to diffusion during prolonged heating promoting the breakdown from the primary ilmenite particles changing the surface morphology of the particles creating a porous structure on the surfaces. The formation of the porous structure would favor the diffusion of the lixiviant during leaching.

Leaching Characteristics
It is well established that the additives and reductants significantly affect the leaching efficiency of ilmenite from the electrochemical results. The response of as-received and pre-oxidized ilmenite to additive and reductive leaching was studied in a series of test works performed at atmospheric conditions. Figure 10 shows the leaching efficiency of ilmenite over time. It can be observed that when only metallic iron is added to the solution, the leaching efficiency of ilmenite is the lowest for both as-received and pre-oxidized samples. The NH4HF4 substantially increased the as-received ilmenite leaching efficiency. The active HF component etches the passivation layer formed during leaching allowing interface reaction to continue increasing the dissolution rate of ilmenite. It can be noted that the pre-oxidized ilmenite response to leaching supersedes that of the as-received ilmenite at atmospheric conditions. In the same Figure 10, the leaching efficiency of the pre-oxidized ilmenite for all additives increased compared to the as-received ilmenite. The porous structure attained during the pre-oxidation step favors the solid-liquid interaction process during the ilmenite leaching process. The micropores enhance the mass transfer rate of leaching reagents through the ferric oxide layer promoting the dissolution reaction. Therefore, this validates the assertion by Liu and Xiang [26] that the exposure of hematite through pre-oxidation promotes dissolution and untreated ilmenite has low reactivity to HCl. Mahamoud et al. [19] reported that the addition of metallic iron reduces the dissolved Fe 3+ to Fe 2+ and significantly improves the iron dissolution rate. The effect of temperature on ilmenite's leaching efficiency was investigated at 9.6 M, HCL in the presence of NH4HF4, and metallic iron. From the results presented in Figure 11, it can be noted that the increase in temperature increased the leaching efficiency of ilmenite. Moreover, the pre-oxidized sample had the highest leaching efficiency at all temperatures. The operational temperature was kept at 90 °C to avoid the formation of HF and HCL vapors at higher temperatures.

Effect of Temperature on the Leaching Efficiency of Ilmenite
The effect of temperature on ilmenite's leaching efficiency was investigated at 9.6 M, HCL in the presence of NH 4 HF 4 , and metallic iron. From the results presented in Figure 11, it can be noted that the increase in temperature increased the leaching efficiency of ilmenite. Moreover, the pre-oxidized sample had the highest leaching efficiency at all temperatures. The operational temperature was kept at 90 • C to avoid the formation of HF and HCL vapors at higher temperatures.
Minerals 2020, 10, x FOR PEER REVIEW 11 of 20 Figure 11. The effect of temperature on the leaching efficiency of as-received and pre-oxidized ilmenite, when using NH4HF4 and Fe as additives in chloride media.

The Behavior of Impurities during Leaching
Manganese, alumina, and silica form part of the crystalline structure of ilmenite coexisting as intra and inter impurities. In application, these impurities affect the quality of the final product. While maintaining the same leaching conditions, the behavior of the impurities was observed. Figure 12 presents the leaching characteristics of impurities associated with ilmenite. It can be observed that alumina had the highest leaching efficiency, which can be attributed to alumina's deposition characteristics. When observing the ilmenite crystal structure ( Figures 5-7), the alumina deposited on the intra part of the crystallographic structure, making it easy to be leached out. Figure 11. The effect of temperature on the leaching efficiency of as-received and pre-oxidized ilmenite, when using NH 4 HF 4 and Fe as additives in chloride media.

The Behavior of Impurities during Leaching
Manganese, alumina, and silica form part of the crystalline structure of ilmenite coexisting as intra and inter impurities. In application, these impurities affect the quality of the final product. While maintaining the same leaching conditions, the behavior of the impurities was observed. Figure 12 presents the leaching characteristics of impurities associated with ilmenite. It can be observed that alumina had the highest leaching efficiency, which can be attributed to alumina's deposition characteristics. When observing the ilmenite crystal structure ( Figures 5-7), the alumina deposited on the intra part of the crystallographic structure, making it easy to be leached out.
In the case of manganese, it was optimally leached to lower levels. The manganese grains are embedded within the ilmenite crystalline structure during alteration hence limiting complete extraction. Silica has the lowest extraction rate as it has larger grains embedded within the structure. Figure 13 shows the mineral phase constitution of the as-received ilmenite leached at the optimum condition at different time intervals from 45 min to 1 h 30 min, at 90 • C. Compared with Figure 3 (as-received ilmenite XRD diffractogram), the x-ray diffractograms of the residue samples were studied after each leaching time interval. New diffraction peaks appeared after a 45-min leach indicating surfacing rutile peaks as ilmenite dissolution occurs. Intermediate phases transformed into rutile; however, most unreacted ilmenite peak intensity is visible in the material. In the case of manganese, it was optimally leached to lower levels. The manganese grains are embedded within the ilmenite crystalline structure during alteration hence limiting complete extraction. Silica has the lowest extraction rate as it has larger grains embedded within the structure. Figure 13 shows the mineral phase constitution of the as-received ilmenite leached at the optimum condition at different time intervals from 45 min to 1 h 30 min, at 90 °C. Compared with Figure 3 (as-received ilmenite XRD diffractogram), the x-ray diffractograms of the residue samples were studied after each leaching time interval. New diffraction peaks appeared after a 45-min leach indicating surfacing rutile peaks as ilmenite dissolution occurs. Intermediate phases transformed into rutile; however, most unreacted ilmenite peak intensity is visible in the material.  Figure 14 shows the phase constitution of the pre-oxidized ilmenite during leaching at different temperatures. It can be observed that ilmenite peaked at high intensity at lower temperatures (25 and 45 °C). It can be attributed to the low iron dissolution rates at lower temperatures. At 90 °C, there are high-intensity peaks of the rutile phase, confirming that iron dissolution increases with an increase in temperature. When comparing the pre-oxidized ilmenite with the as-received material, the rutile peaks are more intense in the pre-oxidized sample than the as-received material. The rutile phase dominance in pre-oxidized material is attributed to the ferric oxide layer, which leaches faster, leaving the rutile phase exposed.  Figure 14 shows the phase constitution of the pre-oxidized ilmenite during leaching at different temperatures. It can be observed that ilmenite peaked at high intensity at lower temperatures (25 and 45 • C). It can be attributed to the low iron dissolution rates at lower temperatures. At 90 • C, there are high-intensity peaks of the rutile phase, confirming that iron dissolution increases with an increase in temperature. When comparing the pre-oxidized ilmenite with the as-received material, the rutile peaks are more intense in the pre-oxidized sample than the as-received material. The rutile phase dominance in pre-oxidized material is attributed to the ferric oxide layer, which leaches faster, leaving the rutile phase exposed. Figure 14 shows the phase constitution of the pre-oxidized ilmenite during leaching at different temperatures. It can be observed that ilmenite peaked at high intensity at lower temperatures (25 and 45 °C). It can be attributed to the low iron dissolution rates at lower temperatures. At 90 °C, there are high-intensity peaks of the rutile phase, confirming that iron dissolution increases with an increase in temperature. When comparing the pre-oxidized ilmenite with the as-received material, the rutile peaks are more intense in the pre-oxidized sample than the as-received material. The rutile phase dominance in pre-oxidized material is attributed to the ferric oxide layer, which leaches faster, leaving the rutile phase exposed.   Figure 15 shows the phase pattern of the pre-oxidized ilmenite leached in the presence of ammonium additives. It can be observed that at 25 • C there is a higher peak ilmenite peak intensity with few picks of TiO 2 and nitrogen. The peak intensity for ilmenite reduces as temperature increases; there are phase changes as the overlap between sulfur, TiO 2 , and ilmenite observed when leaching was conducted at 45 • C. At 90 • C, a precise observation of the dominant TiO 2 phase constitution confirms the assertion that the pre-oxidized ilmenite leached successfully in the presence of ammonium. When contrasting with the XRD pattern for the leached as-received ilmenite, pre-oxidized leached without additives, the additive leach shows a significant increase in the TiO 2 as temperature increases. To have a fully comprehensive understanding of how the crystallographic orientation was affected by leaching, a further mineralogical investigation was required.

Mineralogical Characterization of Leaching Residue Using SEM
Therefore, the residue was analyzed using a high-resolution scanning electron microscope (SEM) to determine the surface morphology and mineralogical orientation of the residue at each interval for both standard and additive leaching. Figure 16 shows the electron micrographs of the optimally leached ilmenite at different temperature intervals. The morphology of the residues after leaching at 25 • C observed (Figure 16a) showed no deposition or surface film build up during the leaching test, indicating that there was minimal dissolution that occurred. When observing Figure 16b,c, precipitation or a surface film can be observed, with a thicker layer observed on Figure 16c, it confirms that there is indeed a higher dissolution rate that occurs at high temperatures. The film on the particles shows distinct character, but there is no crystal disorientation; however, the fine particle cluster formation or deposition observed as the mineral build-up is targeted explicitly at the rough edges of the mineral surface. The surface layer is also thicker at the grooves, attributed to deposition and polymerization of titanium on the ridges during the leaching of iron from the crystal lattice.
confirms the assertion that the pre-oxidized ilmenite leached successfully in the presence of ammonium. When contrasting with the XRD pattern for the leached as-received ilmenite, preoxidized leached without additives, the additive leach shows a significant increase in the TiO2 as temperature increases. To have a fully comprehensive understanding of how the crystallographic orientation was affected by leaching, a further mineralogical investigation was required.

Mineralogical Characterization of Leaching Residue Using SEM
Therefore, the residue was analyzed using a high-resolution scanning electron microscope (SEM) to determine the surface morphology and mineralogical orientation of the residue at each interval for both standard and additive leaching. Figure 16 shows the electron micrographs of the optimally leached ilmenite at different temperature intervals. The morphology of the residues after leaching at 25 °C observed (Figure 16a) showed no deposition or surface film build up during the leaching test, indicating that there was minimal dissolution that occurred. When observing Figure  16b,c, precipitation or a surface film can be observed, with a thicker layer observed on Figure 16c, it confirms that there is indeed a higher dissolution rate that occurs at high temperatures. The film on the particles shows distinct character, but there is no crystal disorientation; however, the fine particle cluster formation or deposition observed as the mineral build-up is targeted explicitly at the rough edges of the mineral surface. The surface layer is also thicker at the grooves, attributed to deposition and polymerization of titanium on the ridges during the leaching of iron from the crystal lattice.  Figure 17 shows the electron micrographs of the pre-oxidized ilmenite leaching residues in the presence of reducing agent and ammonium additives. When observing the microstructures, it can be deduced that the ilmenite crystallographic structure was broken down during leaching. When comparing the micrographs in Figures 16 and 17, it is evident that the dissolution kinetics of the iron were altered by the presence of a reducing agent, in this case, metallic iron. Sasikumar, Srikanth [27] also observed that iron alters the iron titania bond's chemical composition, making it unstable and amenable to dissolution by hydrochloric acid. Figure 17a,b the particles show partial dissolution under microscopy at similar magnification and lower temperatures. It can be observed that the particle disintegration started at the edges of the particle, which is the area where the ferric oxide layer was deposited. The removal of iron and other  Figure 17 shows the electron micrographs of the pre-oxidized ilmenite leaching residues in the presence of reducing agent and ammonium additives. When observing the microstructures, it can be deduced that the ilmenite crystallographic structure was broken down during leaching. When comparing the micrographs in Figures 16 and 17, it is evident that the dissolution kinetics of the iron were altered by the presence of a reducing agent, in this case, metallic iron. Sasikumar, Srikanth [27] also observed that iron alters the iron titania bond's chemical composition, making it unstable and amenable to dissolution by hydrochloric acid.  Figure 18 shows the TEM leached residue's TEM micrographs for the pre-oxidized ilmenite leached in the presence of reductant and ammonium salt. The micrograph ( Figure 18) observed showed the amorphous and partly polycrystalline nature of the residue. As shown in Figure 18, the latticed-spacing difference is due to the mineral phase transformation to titania. The crystallographic disintegration of ilmenite particles is due to the migration of iron and impurity mineral atoms to the solution. As per the observation, it can be deduced that the amorphous part in the ilmenite crystal represents the disintegrated area shown in Figure 17. The polycrystalline area represents the unreacted part of the ilmenite particle. It can be observed that the amorphous area is predominantly on the edges of the crystal, which confirms the assertion  Figure 17a,b the particles show partial dissolution under microscopy at similar magnification and lower temperatures. It can be observed that the particle disintegration started at the edges of the particle, which is the area where the ferric oxide layer was deposited. The removal of iron and other base metal from the lattice also creates gaps in the crystal lattice resulting in line grooves. At higher temperatures (Figure 17c), the particle shows evident disintegration of the crystalline structure because of the high dissolution rate of iron and associated impurities.
In comparison with the leached as-received ilmenite sample in Figure 16, it can be deduced that the pre-oxidation enhanced the leaching efficiency of ilmenite. In Figure 16, there is no evident sign of particle breakdown, as in contrast to the evident disintegration of the euclic bond shown in Figure 17. To further understand the nature of the crystallographic disorientation, a closer look at the single leached particle through TEM was instigated. Figure 18 shows the TEM leached residue's TEM micrographs for the pre-oxidized ilmenite leached in the presence of reductant and ammonium salt. The micrograph ( Figure 18) observed showed the amorphous and partly polycrystalline nature of the residue. As shown in Figure 18, the latticed-spacing difference is due to the mineral phase transformation to titania. The crystallographic disintegration of ilmenite particles is due to the migration of iron and impurity mineral atoms to the solution. As per the observation, it can be deduced that the amorphous part in the ilmenite crystal represents the disintegrated area shown in Figure 17.
leached in the presence of reductant and ammonium salt. The micrograph ( Figure 18) observed showed the amorphous and partly polycrystalline nature of the residue. As shown in Figure 18, the latticed-spacing difference is due to the mineral phase transformation to titania. The crystallographic disintegration of ilmenite particles is due to the migration of iron and impurity mineral atoms to the solution. As per the observation, it can be deduced that the amorphous part in the ilmenite crystal represents the disintegrated area shown in Figure 17. The polycrystalline area represents the unreacted part of the ilmenite particle. It can be observed that the amorphous area is predominantly on the edges of the crystal, which confirms the assertion that during pre-oxidation, the ferric oxide, which is amenable to leaching, is moved to the periphery The polycrystalline area represents the unreacted part of the ilmenite particle. It can be observed that the amorphous area is predominantly on the edges of the crystal, which confirms the assertion that during pre-oxidation, the ferric oxide, which is amenable to leaching, is moved to the periphery of the ilmenite particle. Therefore, during leaching, the edges are disintegrated to form the amorphous phase. Figure 19 shows the micrograph of the leach residue crystals. It can be observed that the various ilmenite residue crystals are in the plate-like structure. The crystal orientation exhibits a similar orientation of the flat plate-like structure, which has a spiky orientation. The flat plate structure is attributed to the rhombohedral nature of the ilmenite crystals. It can be deduced from the origin of the deposit where during transportation of the ilmenite minerals, the collision of the particles caused cracks hence the spiky orientation.
Minerals 2020, 10, x FOR PEER REVIEW 17 of 20 of the ilmenite particle. Therefore, during leaching, the edges are disintegrated to form the amorphous phase. Figure 19 shows the micrograph of the leach residue crystals. It can be observed that the various ilmenite residue crystals are in the plate-like structure. The crystal orientation exhibits a similar orientation of the flat plate-like structure, which has a spiky orientation. The flat plate structure is attributed to the rhombohedral nature of the ilmenite crystals. It can be deduced from the origin of the deposit where during transportation of the ilmenite minerals, the collision of the particles caused cracks hence the spiky orientation.  In Figure 21, after 20 min, the manganese peaks were eliminated with low iron intensity peaks and chloride peaks from the leach solution. In comparison with the mapping in Figure 20, the leach residue decreases iron peaks as the leaching retention time increases. The final residues (Figure 22) confirm the assertion that there is a decrease in the intensity of the iron peaks; similarly, there is also the elimination of manganese, aluminum in the crystalline structure. The magnesium and silica impurity peaks are very low in intensity, suggesting that the ICP-OES results confirm a significant reduction in their concentration.  In Figure 21, after 20 min, the manganese peaks were eliminated with low iron intensity peaks and chloride peaks from the leach solution. In comparison with the mapping in Figure 20, the leach residue decreases iron peaks as the leaching retention time increases. The final residues ( Figure 22) confirm the assertion that there is a decrease in the intensity of the iron peaks; similarly, there is also the elimination of manganese, aluminum in the crystalline structure. The magnesium and silica impurity peaks are very low in intensity, suggesting that the ICP-OES results confirm a significant reduction in their concentration.

Conclusions
The pre-oxidation of the altered ilmenite beach placer sands provides a unique opportunity to transform the sands' mineralogical characteristics. By comparing the initial impurity characteristics of the as-received ilmenite beach sands, it is evident that the pre-oxidation increased the amenability of the sands to chloride leach. The shredded and disarranged surface orientation of the ilmenite increased the iron dissolution rate. The ilmenite mineral phase was converted to pseudo-rutile at intermediate time intervals, as the retention time increases the final mineral phase transformation to rutile. During the dissolution of iron, there is a change in d-spacing, the polycrystalline structure to amorphous.

Conclusions
The pre-oxidation of the altered ilmenite beach placer sands provides a unique opportunity to transform the sands' mineralogical characteristics. By comparing the initial impurity characteristics of the as-received ilmenite beach sands, it is evident that the pre-oxidation increased the amenability of the sands to chloride leach. The shredded and disarranged surface orientation of the ilmenite increased the iron dissolution rate. The ilmenite mineral phase was converted to pseudo-rutile at intermediate time intervals, as the retention time increases the final mineral phase transformation to rutile. During the dissolution of iron, there is a change in d-spacing, the polycrystalline structure to amorphous.

Conclusions
The pre-oxidation of the altered ilmenite beach placer sands provides a unique opportunity to transform the sands' mineralogical characteristics. By comparing the initial impurity characteristics of the as-received ilmenite beach sands, it is evident that the pre-oxidation increased the amenability of the sands to chloride leach. The shredded and disarranged surface orientation of the ilmenite increased the iron dissolution rate. The ilmenite mineral phase was converted to pseudo-rutile at intermediate time intervals, as the retention time increases the final mineral phase transformation to rutile. During the dissolution of iron, there is a change in d-spacing, the polycrystalline structure to amorphous.