High Gravity-Enhanced Direct Air Capture: A Leap Forward in CO 2 Adsorption Technology

: Given the global pressure of climate change and ecological equilibrium, there is an urgent need to develop effective carbon dioxide (CO 2 ) capture technology. Due to its comprehensiveness and ﬂexibility, Direct Air Capture (DAC) technology has emerged as a vital supplement to traditional emission reduction methods. This study aims to innovate Direct Air Capture (DAC) technology by utilizing the ultrasonic impregnation method to load Tetraethylenepentamine (TEPA) onto alumina (Al 2 O 3 ) as the adsorbent. Furthermore, high gravity adsorption technology is integrated to significantly enhance the efﬁciency of DAC. Characterization tests, including BET, FTIR, TG, XRD, and SEM-EDS, conﬁrm the structural stability and high capture capacity of the adsorbent. Additionally, this study demonstrates the rapid and efﬁcient capture of CO 2 from the air using TEPA-Al 2 O 3 adsor-bent under high gravity conditions for the ﬁrst time. Under optimal conditions with TEPA loading at 15.06%, a high gravity factor of 2.67, and a gas ﬂow rate of 30 L/min, TEPA-Al 2 O 3 achieves a CO 2 adsorption capacity of 48.5 mg/g in RAB, which is an improvement of 15.56 mg/g compared to traditional ﬁxed-bed technology. Moreover, it reaches adsorption saturation faster under high gravity conditions, exhibiting a signiﬁcantly higher adsorption rate compared to traditional ﬁxed-bed systems. Furthermore, the adsorption process better conforms to the Avrami model. Steam stripping regeneration is utilized to regenerate the adsorbent, demonstrating excellent regeneration performance and stable adsorption capacity, thereby proving its feasibility and economic beneﬁts as a DAC technology.


Introduction
Addressing the escalating severity of global warming and ecological imbalance, the drastic reduction of CO 2 emissions has become a critical worldwide imperative [1].Although traditional greenhouse gas mitigation methods have shown some effectiveness, they are typically limited to specific emission points and are less effective in addressing widely dispersed emission sources and the CO 2 historically accumulated in the atmosphere [2].Direct Air Capture (DAC) technology emerges as a versatile negative emissions technology [3] that can augment these methods, offering a more holistic and adaptable approach to the problem [4][5][6].
Within the global strategy to combat climate change, Direct Air Capture (DAC) technology stands out as particularly important and offers a unique pathway to achieve carbon neutrality.DAC technology operates independently of the CO 2 emission sources, allowing it to be deployed anywhere in the world without being constrained by geographical location or emission intensity [7].Additionally, DAC technology can capture CO 2 emissions that are challenging to mitigate through other methods, such as those from the transportation and agriculture sectors.Therefore, DAC technology is an essential component of achieving long-term global climate goals.
Adsorption technology is used in different energy systems [8,9], with high selectivity for CO 2 , and can be operated at room temperature and pressure, which has significant advantages over other technologies such as liquid solvent absorption or membrane separation in terms of feasibility and energy efficiency of technical implementation.
However, despite the promising prospects of DAC technology, its commercial viability is hindered by the low mass transfer efficiency resulting from capturing extremely low concentrations of CO 2 in the atmosphere (400 ppm) [10].This difficulty in capturing DAC technology due to low mass transfer efficiency underscores the significance of selecting appropriate carbon dioxide capture materials and capture equipment.High gravity technology, an innovative process intensification technique, employs centrifugal forces from rotation to simulate a high gravity environment and boost mass transfer.Widely applied in fields such as absorption [11], distillation [12], liquid-liquid extraction and reaction [13], dust removal [14], nanomaterial fabrication [15], and adsorption [16,17].High gravity adsorption, utilizing a rotating packed bed for an expanded gas-solid interface and rapid renewal, represents an advancement in this field.In order to further improve the efficiency of DAC technology, this study innovatively adopts the combination of high gravity adsorption technology.This study has adopted high gravity adsorption to enhance DAC's efficiency, where the increased rotational speeds in a high gravity adsorption bed markedly improve the adsorbent's interaction with CO 2 [16,18,19].
The selection of appropriate adsorbents is crucial for advancing DAC technology [10,20].Optimal adsorbents exhibit high selectivity and adsorption capacity, robust regenerative capabilities, and cost-effectiveness.Amine-functionalized adsorption technologies are notable for their low energy and equipment costs, as well as their high selectivity [4,[21][22][23].Tetraethylenepentamine (TEPA), with its amine-dense structure, has demonstrated superior ultra-dilute CO 2 absorption rates [24][25][26].Notably, Salestan et al. observed a 63% increase in CO 2 adsorption selectivity when TEPA was grafted onto MIL-101 [27].These findings underscore TEPA's efficacy as an amine agent, bolstering its adsorption performance based on raw materials.Consequently, this study selected TEPA as the adsorbent due to its aminerich structure and impressive CO 2 capture capacity.TEPA's ability to capture CO 2 with low energy input and its operational stability across various temperatures and pressures make it an ideal choice.To maximize TEPA's performance, ultrasonic impregnation is used to load it onto alumina with a high specific surface area, providing a stable physical framework and ensuring thermal and mechanical stability during CO 2 capture.
As shown in Figure 1, CO 2 in the air is captured by the adsorbent, and the adsorbent, after the completion of the capture, is regenerated by water vapor, and the regenerated adsorbent is used again for CO 2 capture, and the pure CO 2 is stored.
This study comprehensively evaluates the TEPA-Al 2 O 3 adsorbent within a high gravity adsorption bed through carefully designed experiments.The TEPA-Al 2 O 3 adsorbent was synthesized using ultrasonic impregnation and extensively characterized by BET, FT-IR, XRD, TGA, and SEM-EDS to determine its structural characteristics and properties.It was then used in conjunction with high gravity adsorption technology to assess its CO 2 adsorption performance from the air, examining the effects of various operational parameters on TEPA-Al 2 O 3 's efficacy.To deepen our understanding of the CO 2 adsorption mechanism, kinetic models were applied to systematically analyze the process within the high gravity adsorption bed.Interpreting the model parameters and the fitting results enabled an in-depth study of the physical and chemical phenomena occurring during adsorption, thus elucidating the operating principles of the high gravity adsorption bed.This study aims to provide an economically efficient DAC solution by innovatively combining adsorbents with high gravity apparatus.This work aims to introduce a novel instrument for global climate governance, assist in achieving carbon neutrality objectives, and emphasize the importance of technological innovation in climate change mitigation strategies.This study comprehensively evaluates the TEPA-Al2O3 adsorbent within a high gravity adsorption bed through carefully designed experiments.The TEPA-Al2O3 adsorbent was synthesized using ultrasonic impregnation and extensively characterized by BET, FT-IR, XRD, TGA, and SEM-EDS to determine its structural characteristics and properties.It was then used in conjunction with high gravity adsorption technology to assess its CO2 adsorption performance from the air, examining the effects of various operational parameters on TEPA-Al2O3's efficacy.To deepen our understanding of the CO2 adsorption mechanism, kinetic models were applied to systematically analyze the process within the high gravity adsorption bed.Interpreting the model parameters and the fitting results enabled an in-depth study of the physical and chemical phenomena occurring during adsorption, thus elucidating the operating principles of the high gravity adsorption bed.This study aims to provide an economically efficient DAC solution by innovatively combining adsorbents with high gravity apparatus.This work aims to introduce a novel instrument for global climate governance, assist in achieving carbon neutrality objectives, and emphasize the importance of technological innovation in climate change mitigation strategies.

Experimental Materials
Aluminum oxide (Al2O3) with a particle size of 2 mm was acquired from Shandong Guanghui New Materials Co., Ltd (Shandong, China).Analytical-grade anhydrous ethanol was sourced from Tianjin Tianli Chemical Reagent Co., Ltd(Tianjin, China).Tetraethylenepentamine (TEPA) was supplied by Shanghai Macklin Biochemical Co., Ltd(Shanghai, China).Deionized water used for washing was obtained from an in-house purification system.

Synthesis of TEPA-Al2O3
Initially, the aluminum oxide was washed three times with deionized water to prepare it for subsequent use.After washing, the Al2O3 was dried in an oven and stored in a glass container.Secondly, TEPAaethanol solutions with concentrations of 100, 150, 200, 250, and 300 mg•mL −1 were prepared in beakers containing anhydrous ethanol, with thorough stirring to achieve uniform dispersion.The TEPA-ethanol solution was then transferred to another beaker in the required proportion, and an appropriate amount of the

Experimental Materials
Aluminum oxide (Al 2 O 3 ) with a particle size of 2 mm was acquired from Shandong Guanghui New Materials Co., Ltd.(Shandong, China).Analytical-grade anhydrous ethanol was sourced from Tianjin Tianli Chemical Reagent Co., Ltd.(Tianjin, China).Tetraethylenepentamine (TEPA) was supplied by Shanghai Macklin Biochemical Co., Ltd.(Shanghai, China).Deionized water used for washing was obtained from an in-house purification system.

Synthesis of TEPA-Al 2 O 3
Initially, the aluminum oxide was washed three times with deionized water to prepare it for subsequent use.After washing, the Al 2 O 3 was dried in an oven and stored in a glass container.Secondly, TEPAaethanol solutions with concentrations of 100, 150, 200, 250, and 300 mg•mL −1 were prepared in beakers containing anhydrous ethanol, with thorough stirring to achieve uniform dispersion.The TEPA-ethanol solution was then transferred to another beaker in the required proportion, and an appropriate amount of the aluminum oxide carrier was added.This mixture was treated in an ultrasonicator for 4 h to allow for the uniform diffusion of TEPA molecules into the pores of the carrier.After ultrasonic treatment, the carrier impregnated with TEPA was separated from the solution by filtration and washed at least three times with anhydrous ethanol to remove any unbound TEPA.Finally, the treated sample was dried in an apparatus set at 353.15 K to remove any residual solvent.The dried sample was then stored in a glass container, ready for use.

Characterization of TEPA-Al 2 O 3
The pore structure characteristics of the composite material, including its specific surface area, average pore diameter, and total pore volume, were evaluated using lowtemperature nitrogen adsorption/desorption experiments conducted on a Micromeritics ASAP 2010 system (Norcross, GA, USA).
Functional groups on the surface of the composite material were identified using a NICOQ380 FTIR spectrometer (Waltham, MA, USA).FTIR spectra were recorded in the wavenumber range of 500-4000 cm −1 to identify characteristic functional groups present on the material's surface.The adsorbent's mass changes across a range of temperatures were detected using a Setaram Labsys evo thermogravimetric analyzer (Origin: Bavarian Asia, Germany, Model: STA449F3 Jupiter).During this process, the N 2 flow rate was set at 50 mL•min −1 , the heating rate was 10 • C•min −1 , and the temperature testing range was set from 30 to 1000 • C. The thermal stability of the alumina carrier and the TEPA-alumina composite material, as well as the proportion of polyethyleneimine in the composite material, were assessed by analyzing the TGA and DTG curves plotted.
Wide-angle X-ray diffraction (XRD) patterns ranging from 5 • to 85 • were obtained using a D/max-Rb powder X-ray diffractometer with a Cu Kα radiation source (λ = 0.15406 nm) and a scanning speed of 8 • /min.
Surface morphologies of carriers with different surface properties and their composite materials were analyzed using a JSM-7900F Scanning Electron Microscope (Showima City, Tokyo, Japan), yielding high-definition SEM-EDS images.

Adsorption Experiments
As shown in Figure 2, 20.0 g of previously prepared TEPA-Al 2 O 3 is packed into the Rotating Adsorption Bed (RAB) to capture CO 2 from the air, with its structural parameters presented in Table 1.Air is drawn through the fan and flows through the flowmeter before entering the high gravity adsorption bed.After the adsorption process is complete, CO 2 is captured on the adsorbent, and the purified air exits the system.Throughout the entire adsorption process, a portable CO 2 detector (model: NK-500A, origin: Xi'an, China) is used to monitor the CO 2 volume concentration at the RAB outlet in real-time.The research utilizes a high gravity rotational packed bed for adsorption, where s adsorbent particles serve as the packing material within the rotating bed, conducting adsorption process in a high gravity environment.To compare rotational packed bed different sizes and rotational speeds, the intensity of the high gravity field can be re sented by the dimensionless high gravity factor according to research methods in ch cal engineering.The dimensionless high gravity factor (β) is defined as the ratio of inertial acceleration (centrifugal acceleration) G to the gravitational acceleration g ( m/s²).Its expression can be simplified as follows: where N is the rotating speed (r•min −1 ), and r is the radius of the rotor (m).In our st the corresponding values of N and β are shown in Table 2.
Table 2.The relationship between rotational speed and high gravity factor in the rotating adsorp  The research utilizes a high gravity rotational packed bed for adsorption, where solid adsorbent particles serve as the packing material within the rotating bed, conducting the adsorption process in a high gravity environment.To compare rotational packed beds of different sizes and rotational speeds, the intensity of the high gravity field can be represented by the dimensionless high gravity factor according to research methods in chemical engineering.The dimensionless high gravity factor (β) is defined as the ratio of the inertial acceleration (centrifugal acceleration) G to the gravitational acceleration g (9.81 m/s 2 ).Its expression can be simplified as follows: where N is the rotating speed (r•min −1 ), and r is the radius of the rotor (m).In our study, the corresponding values of N and β are shown in Table 2.The adsorption capacity (q t ) can be calculated using Equation (2).For comparison, control experiments were also conducted in a fixed bed of the same size as the RAB, under the same reaction conditions as in the RAB experiments.All experiments were performed in triplicate, and the average values were taken to minimize measurement errors.
where q t is the adsorption capacity (mg•g −1 ), Q is the gas flow rate (L•min −1 ), m is the mass of the adsorbent (g), c 0 and c t are the inlet and outlet CO 2 volume concentrations (%), V m is the molar volume of gas (22.4 L•mol −1 ), and M CO 2 is the molar mass of CO 2 (44 g•mol −1 ).The regeneration of the adsorbent was conducted using steam stripping.The CO 2saturated adsorbent was dispersed in a glass container and then contacted with saturated steam at a flow rate of 1.2 g•min −1 and a temperature of 103 • C for 30 min to regenerate the adsorbent.The steam stripping regeneration was repeated multiple times to evaluate the regeneration efficiency and adsorption capacity of the adsorbent.The porosity characteristics of both Al 2 O 3 and its TEPA-impregnated counterparts were thoroughly examined using N 2 adsorption-desorption measurements.Table 3 shows Pore structural properties of Al 2 O 3 and TEPA-Al 2 O 3 .Notably, both materials exhibited Type IV adsorption isotherms [28] accompanied by distinctive H3 hysteresis loops (Figure 3), indicative of their mesoporous nature.As the relative pressure increased, the adsorption capacities of the materials showed incremental growth until reaching saturation, while desorption occurred at a gradual pace, highlighting stable adsorption properties and the presence of specific pore sizes and structures within the porous materials.The appearance of the hysteresis loop at a relative pressure (P/P0) around 0.40 suggested the existence of smaller mesopores within the materials.Upon impregnation with TEPA, noticeable alterations in surface area were observed.Initially, at lower TEPA concentrations, there was a slight increase in surface area, likely due to TEPA occupying smaller voids or surface defects, thereby enhancing the effective surface area of the material.However, as the concentration of TEPA increased, a plateau or minor decline in surface area was observed.This phenomenon can be attributed to the aggregation of TEPA molecules at higher concentrations, which tend to accumulate on the surface, thereby masking active sites and potentially leading to the occlusion or narrowing of minute pores.As a result, there might be a reduction in pore volume or a slight constriction of pore diameters.were thoroughly examined using N2 adsorption-desorption measurements.Table 3 shows Pore structural properties of Al2O3 and TEPA-Al2O3.Notably, both materials exhibited Type IV adsorption isotherms [28] accompanied by distinctive H3 hysteresis loops (Figure 3), indicative of their mesoporous nature.As the relative pressure increased, the adsorption capacities of the materials showed incremental growth until reaching saturation, while desorption occurred at a gradual pace, highlighting stable adsorption properties and the presence of specific pore sizes and structures within the porous materials.The appearance of the hysteresis loop at a relative pressure (P/P0) around 0.40 suggested the existence of smaller mesopores within the materials.Upon impregnation with TEPA, noticeable alterations in surface area were observed.Initially, at lower TEPA concentrations, there was a slight increase in surface area, likely due to TEPA occupying smaller voids or surface defects, thereby enhancing the effective surface area of the material.However, as the concentration of TEPA increased, a plateau or minor decline in surface area was observed.This phenomenon can be attributed to the aggregation of TEPA molecules at higher concentrations, which tend to accumulate on the surface, thereby masking active sites and potentially leading to the occlusion or narrowing of minute pores.As a result, there might be a reduction in pore volume or a slight constriction of pore diameters.

Fourier Transform Infrared Spectroscopy (FT-IR)
Figure 4 displays the infrared absorption spectra obtained for both Al 2 O 3 and TEPA-Al 2 O 3 samples.In the IR spectrum of TEPA-modified alumina, several distinct absorption peaks are clearly evident.The peak observed at 1065 cm −1 is tentatively attributed to the vibrations of hydroxyl groups associated with the alumina surface, indicating Al-OH vibrational modes.Similarly, the absorption peak at 1110 cm −1 is typically associated with C-N stretching vibrations, likely originating from the presence of amine groups in the TEPA molecule [26].Another notable absorption peak at 1315 cm −1 is likely due to the bending vibrations of the C-H bonds [29].Moreover, the peak observed at 1569 cm −1 may be ascribed to either the bending vibrations of N-H or the stretching vibrations of amides and carboxylic acids [29], Moreover, the peak observed at 1569 cm −1 may be ascribed to either the bending vibrations of N-H or the stretching vibrations of amides and carboxylic acids [30].Furthermore, the peak observed at 3777 cm −1 possibly corresponds to the vibrations of the amine groups (N-H) [29], indicating the presence of amine functionalities in the TEPA structure.The identification and assignment of these absorption peaks suggest an interaction between TEPA and the alumina surface, potentially accompanied by chemical transformations during the modification procedure.and carboxylic acids [29], Moreover, the peak observed at 1569 cm − ¹ may be ascribed to either the bending vibrations of N-H or the stretching vibrations of amides and carboxylic acids [30].Furthermore, the peak observed at 3777 cm − ¹ possibly corresponds to the vibrations of the amine groups (N-H) [29], indicating the presence of amine functionalities in the TEPA structure.The identification and assignment of these absorption peaks suggest an interaction between TEPA and the alumina surface, potentially accompanied by chemical transformations during the modification procedure.Additionally, the presence of distinct spike-like peaks in the XRD diffractogram may be attributed to the polycrystalline nature of the alumina microspheres used in the study [31].Additionally, the presence of distinct spike-like peaks in the XRD diffractogram may be attributed to the polycrystalline nature of the alumina microspheres used in the study [31].

Thermal Gravimetric Analysis (TGA)
As depicted in Figure 6, the thermal behavior of both Al2O3 and TEPA-Al2O3 across a specified temperature range is illustrated.Notably, the TEPA-loaded alumina begins to exhibit weight loss at approximately 100 °C.However, the thermal stability of the novel adsorbents, prepared with varying concentrations of impregnation solution, does not show significant differences.Within the temperature range of 30 °C to 1000 °C, Al2O3 demonstrates only a minimal loss in mass.All adsorbents display a noticeable and consistent weight loss from 0 to 100 °C, primarily attributed to the desorption of water ad-

Impact of Rotating Adsorption Bed (RAB) Operational Parameters on the Adsorption Performance of TEPA-Al2O3
Using the quantity of CO2 adsorption as the evaluation metric, this study explores the impact of different TEPA loading amounts, varying factors of high gravity, as well as distinct inlet gas flow rates on the CO2 adsorption performance of TEPA-Al2O3 from air.
3.2.1.The Effect of TEPA Loading on CO2 Capture from Air At 25 °C, by keeping the inlet gas flow rate constant at 30 L/min and the high gravity factor at 1.5, the impact of varying TEPA concentrations on the absorption of CO2 from the air by amine-modified adsorbents was investigated, with results illustrated in the accom-

Impact of Rotating Adsorption Bed (RAB) Operational Parameters on the Adsorption Performance of TEPA-Al 2 O 3
Using the quantity of CO 2 adsorption as the evaluation metric, this study explores the impact of different TEPA loading amounts, varying factors of high gravity, as well as distinct inlet gas flow rates on the CO 2 adsorption performance of TEPA-Al 2 O 3 from air.

The Effect of TEPA Loading on CO 2 Capture from Air
At 25 • C, by keeping the inlet gas flow rate constant at 30 L/min and the high gravity factor at 1.5, the impact of varying TEPA concentrations on the absorption of CO 2 from the air by amine-modified adsorbents was investigated, with results illustrated in the accompanying Figure 8.The results indicate a significant variation in CO 2 adsorption capacity in response to changes in TEPA loading.The Al 2 O 3 without TEPA loading exhibited an adsorption capacity of only 2.2 mg/g.As the TEPA concentration increased, the adsorption capacity also gradually improved, with 4-TEPA-Al 2 O 3 reaching a maximum value of 48.5 mg/g.This enhancement is attributed to the increased number of active sites available for interaction due to higher TEPA loadings, which increases the adsorbent surface affinity for CO 2 .Furthermore, the experiments revealed that the time to reach adsorption saturation varied with TEPA concentration.Within a certain range, the time required to achieve adsorption saturation first increased and then decreased with rising TEPA loadings.This trend may reflect variations in adsorption rates at different TEPA loadings, suggesting an optimal CO 2 adsorption rate at specific TEPA concentrations.Notably, among the various TEPA-Al 2 O 3 adsorbents studied, 4-TEPA-Al 2 O 3 demonstrated the highest CO 2 adsorption capacity (reaching 48.5 mg/g) and was thus selected for subsequent experimentation.

The Impact of the High gravity Factor on CO2 Capture from Air
Figure 9 illustrates the influence of the high gravity factor on the CO2 adsorption performance of amine-modified adsorbents.It is evident that as the high gravity factor gradually increases, there is a corresponding enhancement in the adsorption capacity.Initially, the adsorption capacity shows an upward trend with the increasing high gravity factor.This is attributed to the fact that a higher gravity factor promotes more frequent collisions between gas molecules and the adsorbent surface, thus accelerating the adsorption rate.Within the range of experimental parameters, an increase in adsorption capacity is observed, although the rate of increase remains moderate.As the high gravity factor is further elevated, it continues to augment the collision rate between gas molecules and the adsorbent surface.This enhancement in collision frequency further accelerates the adsorption rate, consequently shortening the time required to reach adsorption saturation.The findings highlight the significant role of the high gravity factor in influencing the kinetics of CO2 adsorption.By facilitating more efficient mass transfer and enhancing the interaction between gas molecules and the adsorbent surface, higher gravity factors contribute to improved adsorption performance.

The Impact of the High gravity Factor on CO 2 Capture from Air
Figure 9 illustrates the influence of the high gravity factor on the CO 2 adsorption performance of amine-modified adsorbents.It is evident that as the high gravity factor gradually increases, there is a corresponding enhancement in the adsorption capacity.Initially, the adsorption capacity shows an upward trend with the increasing high gravity factor.This is attributed to the fact that a higher gravity factor promotes more frequent collisions between gas molecules and the adsorbent surface, thus accelerating the adsorption rate.Within the range of experimental parameters, an increase in adsorption capacity is observed, although the rate of increase remains moderate.As the high gravity factor is further elevated, it continues to augment the collision rate between gas molecules and the adsorbent surface.This enhancement in collision frequency further accelerates the adsorption rate, consequently shortening the time required to reach adsorption saturation.The findings highlight the significant role of the high gravity factor in influencing the kinetics of CO 2 adsorption.By facilitating more efficient mass transfer and enhancing the interaction between gas molecules and the adsorbent surface, higher gravity factors contribute to improved adsorption performance.Although higher high gravity factors assist in increasing the frequency of collisions, adverse flow phenomena may lead to a reduced rate of adsorption.An excessively high high gravity factor might cause uneven movement of gas molecules within the packed bed, potentially leading to channeling effects.Under such circumstances, a portion of the CO2 may bypass the adsorbent surface and pass directly through the bed without sufficient contact, resulting in a decreased adsorption rate.From the graph, it is evident that TEPA-Al2O3 reaches adsorption saturation within 70 min at a high gravity factor of 4.17, which has been selected for use in subsequent studies.

The Effect of Inlet Air Flow Rate on the Capture of CO2 from Air
Based on the experimental outcomes, under the condition of a high gravity factor of 4.17, the impact of varying gas flow rates on the adsorption of carbon dioxide from the air using 4-TEPA-Al2O3 was investigated, with the results depicted in the accompanying figure 10.At lower flow rates (10 L/min and 15 L/min), the adsorption capacity approached saturation within 200 min but did not achieve a saturated state.Under these two flow rate conditions, the duration for the adsorbent to reach saturation was extended.However, as the gas flow rate was further increased, the adsorption capacity reached the same saturation level of 48.4 mg•g −1 , and the time required to achieve saturation gradually decreased.At a flow rate of 25 L/min, adsorption saturation was attained around 80 min.This trend may suggest that the gas flow rate exerts a significant influence on the adsorption kinetics.At low flow rates, the adsorbent has ample time to interact with CO2, hence achieving a relatively high adsorption capacity even at reduced flow rates.Conversely, with increased gas flow rates, the residence time of the gas on the adsorbent surface diminishes, resulting in a greater volume of gas contacting the adsorbent per unit time, yet the number of available adsorption sites on the surface remains unchanged.Consequently, at higher flow rates, the rate of adsorption is quicker, and the time to reach the same level of adsorption capacity is shorter, ultimately converging to the same adsorption quantity.Although higher high gravity factors assist in increasing the frequency of collisions, adverse flow phenomena may lead to a reduced rate of adsorption.An excessively high high gravity factor might cause uneven movement of gas molecules within the packed bed, potentially leading to channeling effects.Under such circumstances, a portion of the CO 2 may bypass the adsorbent surface and pass directly through the bed without sufficient contact, resulting in a decreased adsorption rate.From the graph, it is evident that TEPA-Al 2 O 3 reaches adsorption saturation within 70 min at a high gravity factor of 4.17, which has been selected for use in subsequent studies.

The Effect of Inlet Air Flow Rate on the Capture of CO 2 from Air
Based on the experimental outcomes, under the condition of a high gravity factor of 4.17, the impact of varying gas flow rates on the adsorption of carbon dioxide from the air using 4-TEPA-Al 2 O 3 was investigated, with the results depicted in the accompanying Figure 10.At lower flow rates (10 L/min and 15 L/min), the adsorption capacity approached saturation within 200 min but did not achieve a saturated state.Under these two flow rate conditions, the duration for the adsorbent to reach saturation was extended.However, as the gas flow rate was further increased, the adsorption capacity reached the same saturation level of 48.4 mg•g −1 , and the time required to achieve saturation gradually decreased.At a flow rate of 25 L/min, adsorption saturation was attained around 80 min.This trend may suggest that the gas flow rate exerts a significant influence on the adsorption kinetics.At low flow rates, the adsorbent has ample time to interact with CO 2 , hence achieving a relatively high adsorption capacity even at reduced flow rates.Conversely, with increased gas flow rates, the residence time of the gas on the adsorbent surface diminishes, resulting in a greater volume of gas contacting the adsorbent per unit time, yet the number of available adsorption sites on the surface remains unchanged.Consequently, at higher flow rates, the rate of adsorption is quicker, and the time to reach the same level of adsorption capacity is shorter, ultimately converging to the same adsorption quantity.

Kinetic Analysis of CO2 Adsorption from Air by Amine-Modified Adsorbents
For amine-modified adsorbents tasked with capturing CO2 from the air, the adsorption performance is influenced not only by the physicochemical properties of the adsorbent itself but also by the rate of adsorption.The adsorption rate is a critical factor affecting the efficiency of CO2 uptake from the air by adsorbents and can provide essential engineering parameters for the practical application of these materials.Consequently, studying the adsorption kinetics and rates is key to exploring the process and mechanism of CO2 adsorption from the air.Currently, numerous adsorption kinetic models are available to investigate the rate of gas adsorption reactions on the surface of porous solids.In this paper, three models are employed to analyze the kinetics of CO2 adsorption onto aminemodified adsorbents: Lagergren's pseudo-first-order model, Ho's pseudo-second-order model, and the Avrami fractional-order kinetics model.These models were selected because they are more apt to describe the CO2 adsorption process on amine-modified materials, where the adsorption rate is limited by the kinetics of surface reactions [32].

Lagergren's Pseudo-First-Order Adsorption Kinetics Model
The Lagergren pseudo-first-order kinetic model is commonly utilized to determine whether the adsorption reaction follows a physisorption mechanism.This model is straightforward and particularly suitable for adsorption processes where surface adsorption predominates.It postulates that at adsorption equilibrium, the interaction between the gas and the solid surface is reversible, and the adsorption rate is directly proportional to the difference between the equilibrium adsorption capacity and the quantity of adsorbate at time t.The model has been widely applied in the analysis of dynamic adsorption data and in the design of adsorption processes.Its formula is expressed as follows: Integrating Equation (2) yields Equation (3): where  is the adsorption capacity at time t (mg/g);  is the equilibrium adsorption capacity (mg/g);  is the rate constant of the pseudo-first-order model (min −1 ); t is the adsorption time (min).

Kinetic Analysis of CO 2 Adsorption from Air by Amine-Modified Adsorbents
For amine-modified adsorbents tasked with capturing CO 2 from the air, the adsorption performance is influenced not only by the physicochemical properties of the adsorbent itself but also by the rate of adsorption.The adsorption rate is a critical factor affecting the efficiency of CO 2 uptake from the air by adsorbents and can provide essential engineering parameters for the practical application of these materials.Consequently, studying the adsorption kinetics and rates is key to exploring the process and mechanism of CO 2 adsorption from the air.Currently, numerous adsorption kinetic models are available to investigate the rate of gas adsorption reactions on the surface of porous solids.In this paper, three models are employed to analyze the kinetics of CO 2 adsorption onto amine-modified adsorbents: Lagergren's pseudo-first-order model, Ho's pseudo-second-order model, and the Avrami fractional-order kinetics model.These models were selected because they are more apt to describe the CO 2 adsorption process on amine-modified materials, where the adsorption rate is limited by the kinetics of surface reactions [32].

Lagergren's Pseudo-First-Order Adsorption Kinetics Model
The Lagergren pseudo-first-order kinetic model is commonly utilized to determine whether the adsorption reaction follows a physisorption mechanism.This model is straightforward and particularly suitable for adsorption processes where surface adsorption predominates.It postulates that at adsorption equilibrium, the interaction between the gas and the solid surface is reversible, and the adsorption rate is directly proportional to the difference between the equilibrium adsorption capacity and the quantity of adsorbate at time t.The model has been widely applied in the analysis of dynamic adsorption data and in the design of adsorption processes.Its formula is expressed as follows: Integrating Equation (2) yields Equation (3): where q t is the adsorption capacity at time t (mg/g); q e is the equilibrium adsorption capacity (mg/g); k 1 is the rate constant of the pseudo-first-order model (min −1 ); t is the adsorption time (min).

Ho's Pseudo-Second-Order Adsorption Kinetics Model
The Ho pseudo-second-order kinetic model assumes that the rate of adsorption is related to the availability of active sites on the surface of the adsorbent and is primarily applicable to chemisorption mechanisms.This model can more comprehensively describe the adsorption mechanism, providing a preliminary assessment and rate characterization of the adsorption process.It is suitable for the adsorption processes of most porous adsorbents.Its expression is as follows: Integrating Equation ( 4) results in Equation ( 5): (6) where q t is the adsorption capacity at time t (mg/g); q e is the equilibrium adsorption capacity (mg/g); k 2 is the rate constant for pseudo-second-order adsorption (g•mg −1 •min −1 ); t is the adsorption time (min).

Avrami's Fractional-Order Kinetics Model
The pseudo-first-order and pseudo-second-order kinetic models are used to describe the physical and chemical adsorption mechanisms of adsorption reactions.Nevertheless, adsorption behavior frequently results from the combined effects of physical and chemical adsorption processes.The Avrami fractional-order kinetic model, initially developed for simulating crystallization and particle nucleation processes, is now also adopted to study the dynamic adsorption behaviors of amine-modified adsorbents [33].This model is adept at depicting the concurrent contribution of both physical and chemical adsorption in the adsorption mechanism.Its mathematical representation is given by: Upon integrating Equation ( 6), we obtain Equation (7): where q t is the adsorption capacity at time t (mg/g); q e is the equilibrium adsorption capacity (mg/g); k a represents the adsorption rate constant (min −1 ); t is the adsorption time (min).
In this study, a Rotating Adsorption Bed was employed as the adsorption apparatus, utilizing amine-modified adsorbents to directly capture CO 2 from the air.Unlike conventional fixed beds, the adsorbent within the RAB is in a state of disordered rolling due to the action of centrifugal force, allowing for omnidirectional contact between the adsorbent and air rather than merely flowing upwards from the bottom of the adsorption layer.Based on this unique mode of contact, further performance evaluations revealed significant differences between the RAB and traditional fixed beds under a flow rate (Q) of 20 L/min and a dimensionless high gravity parameter (β) of 4.17, with specific results depicted in Figure 11.Table 4 shows the principal parameters for the kinetics model fitting of CO2 adsorption from air on TEPA-Al 2 O 3 .
the RAB indicates high-ior adsorption performance.To address this phenomenon, three different kinetic models were utilized for fitting and analysis.These models demonstrated varying degrees of suitability in predicting the adsorption behavior of TEPA-Al2O3 for CO2.Among them, the pseudo-first-order and pseudosecond-order kinetic models were somewhat inaccurate in certain respects.Especially in the early stages of adsorption, the pseudo-first-order model overestimated the amount of CO2 adsorbed, while in the stages approaching equilibrium, the predicted values of the model deviated from the actual values.In contrast, the Avrami model exhibited the best fit for the adsorption data, with the predicted adsorption capacity closely matching the experimental values and correlation coefficients (R 2 ) of 0.999 and 0.997 in the fixed bed and Rotating Adsorption Bed (RAB), respectively.This indicates the simultaneous occurrence of physical and chemical adsorption in the process.Furthermore, the adsorption rate constants obtained from the fitting of the three models suggest that the adsorption rate in the high centrifugal bed is significantly higher than that in the solid bed.This advantage is attributed to the continuous dynamic renewal of the adsorption medium under high centrifugal forces, promoting a more efficient renewal of the gas-solid interface, thereby accelerating the adsorption process.

Regeneration of Amine-Modified Adsorbents
The continuous reuse of adsorbent materials is a practice in line with ecological sustainability principles, contributing to waste reduction, raw material savings, and decreased energy consumption, which aligns with the objectives of environmental protection and sustainable development strategies.Under the optimal conditions identified in

The Pseudo-First-Order Model
The Pseudo-Second-Order Model Avrami's Fractional-Order Kinetics Model The adsorption mechanism of CO 2 in air can be divided into two stages: rapid adsorption during the initial phase and a subsequent slow approach to equilibrium.In the initial phase, the abundance of active sites on the surface of the amine-modified material allows for quick adsorption of CO 2 , exhibiting a near-linear relationship with time.As these active sites become increasingly occupied, the rate of adsorption decreases due to the necessity for CO 2 to diffuse into deeper pores.Furthermore, it is evident from the graph that in the RAB, the adsorbent reaches saturation in a shorter time with a larger adsorption capacity.Compared to the traditional fixed bed method, the adsorption capacity in the RAB increased by 15.56 mg/g.The steeper slope of the adsorption curve within the RAB indicates high-ior adsorption performance.To address this phenomenon, three different kinetic models were utilized for fitting and analysis.
These models demonstrated varying degrees of suitability in predicting the adsorption behavior of TEPA-Al 2 O 3 for CO 2 .Among them, the pseudo-first-order and pseudo-secondorder kinetic models were somewhat inaccurate in certain respects.Especially in the early stages of adsorption, the pseudo-first-order model overestimated the amount of CO 2 adsorbed, while in the stages approaching equilibrium, the predicted values of the model deviated from the actual values.In contrast, the Avrami model exhibited the best fit for the adsorption data, with the predicted adsorption capacity closely matching the experimental values and correlation coefficients (R 2 ) of 0.999 and 0.997 in the fixed bed and Rotating Adsorption Bed (RAB), respectively.This indicates the simultaneous occurrence of physical and chemical adsorption in the process.Furthermore, the adsorption rate constants obtained from the fitting of the three models suggest that the adsorption rate in the high centrifugal bed is significantly higher than that in the solid bed.This advantage is attributed to the continuous dynamic renewal of the adsorption medium under high centrifugal forces, promoting a more efficient renewal of the gas-solid interface, thereby accelerating the adsorption process.

Regeneration of Amine-Modified Adsorbents
The continuous reuse of adsorbent materials is a practice in line with ecological sustainability principles, contributing to waste reduction, raw material savings, and decreased energy consumption, which aligns with the objectives of environmental protection and sustainable development strategies.Under the optimal conditions identified in previous research, we applied steam stripping technology to reactivate the amine-modified adsorbent materials and recorded the regeneration effects.Figure 12 demonstrates that after several regeneration cycles, the adsorbent still exhibited a high CO 2 capture capacity (40.32 mg•g −1 ), with only a slight performance decay.These results highlight the superior regenerative potential and enduring stability of the adsorbent material.The steam regeneration process can periodically refresh the activity of the adsorbent material, removing the attached carbon dioxide and enabling the material's cyclic reapplication.By economically regenerating the adsorbent, we not only efficiently recover and recycle valuable adsorptive resources but also save on energy expenses.This practice of resource recycling is greatly beneficial for environmental protection and the advancement of sustainability, as well as for reducing economic costs and enhancing overall economic value.
previous research, we applied steam stripping technology to reactivate the amine-modified adsorbent materials and recorded the regeneration effects.Figure 12 demonstrates that after several regeneration cycles, the adsorbent still exhibited a high CO2 capture capacity (40.32 mg•g −1 ), with only a slight performance decay.These results highlight the superior regenerative potential and enduring stability of the adsorbent material.The steam regeneration process can periodically refresh the activity of the adsorbent material, removing the attached carbon dioxide and enabling the materialʹs cyclic reapplication.By economically regenerating the adsorbent, we not only efficiently recover and recycle valuable adsorptive resources but also save on energy expenses.This practice of resource recycling is greatly beneficial for environmental protection and the advancement of sustainability, as well as for reducing economic costs and enhancing overall economic value.
Conversely, Table 5 meticulously documents the CO2 adsorption performance of different amine-modified adsorbents in the atmosphere.The adsorbent used in this study exhibited higher adsorption capacity compared to most other materials in the control group.This emphasizes the potential of our research in capturing atmospheric CO2.Subsequent cyclic testing has revealed that these adsorbents maintain excellent stability, high recovery, and adsorption efficiencies over repeated use, which are crucial for sustainable operation in practical applications.Furthermore, the relatively low amine loading levels utilized in this work imply not only a more economical use of raw materials during production but also potential reductions in energy consumption and operational costs during the adsorbent regeneration process.Lower amine loading may also reduce corrosion issues and operational risks, thereby contributing to the extended lifespan of the equipment and reduced maintenance costs.This cost-benefit analysis underscores the potential economic advantages of our study for industrial applications, providing a positive outlook for future commercialization processes.Conversely, Table 5 meticulously documents the CO 2 adsorption performance of different amine-modified adsorbents in the atmosphere.The adsorbent used in this study exhibited higher adsorption capacity compared to most other materials in the control group.This emphasizes the potential of our research in capturing atmospheric CO 2 .Subsequent cyclic testing has revealed that these adsorbents maintain excellent stability, high recovery, and adsorption efficiencies over repeated use, which are crucial for sustainable operation in practical applications.Furthermore, the relatively low amine loading levels utilized in this work imply not only a more economical use of raw materials during production but also potential reductions in energy consumption and operational costs during the adsorbent regeneration process.Lower amine loading may also reduce corrosion issues and operational risks, thereby contributing to the extended lifespan of the equipment and reduced maintenance costs.This cost-benefit analysis underscores the potential economic advantages of our study for industrial applications, providing a positive outlook for future commercialization processes.

Conclusions
In this study, a novel amine-functionalized adsorbent, TEPA-Al 2 O 3 , with efficient CO 2 adsorption performance, was successfully prepared using the ultrasonic impregnation method.Structural and performance characterizations confirmed the uniform distribution of TEPA on the Al 2 O 3 support and the excellent specific surface area, pore size, and pore volume of the formed adsorbent.
This work innovatively combined the supergravity adsorption technique to determine the optimal operating conditions for the adsorbent.Under these conditions, TEPA-Al 2 O 3 exhibited a maximum saturated adsorption capacity of 48.5 mg/g and a higher adsorption rate constant compared to traditional fixed-bed systems.These findings demonstrate the advantages of the supergravity adsorption technique in improving the rate of the adsorption process.Furthermore, our adsorbent showed significant stability during repeated use and regeneration processes, maintaining an adsorption capacity of 40.32 mg/g even after 10 regeneration cycles.This result highlights not only the good durability of the adsorbent but also its potential value in practical applications, especially in achieving sustainable direct air capture technologies.
Based on this study, we anticipate future research to further develop, including exploring the applicability of the ultrasonic impregnation method to prepare other types of adsorbents, investigating CO 2 adsorption under a wider range of temperature, humidity, and other conditions in a supergravity field, optimizing the production process of TEPA-Al 2 O 3 to enhance its performance, and evaluating its practicality in different industrial application scenarios.Additionally, the development of new low-energy regeneration strategies will be an important direction for further research to reduce operational costs and improve the overall sustainability of the system.

Figure 1 .
Figure 1.The cycle of amine-modified adsorbents absorbing CO2 in air.

Figure 1 .
Figure 1.The cycle of amine-modified adsorbents absorbing CO 2 in air.

Figure 4 .
Figure 4. Infrared spectra of Al2O3 and TEPA-Al2O3.3.1.3.X-ray Diffraction Analysis (XRD) As depicted in Figure 5, the XRD patterns for Al2O3 and TEPA-Al2O3 are shown.The diffraction peaks for both samples are primarily observed at 2θ values of 19.46°, 28.24°, 31.93°,37.61°, 45.83°, 60.86°, and 67.26°.The positions of these peaks are consistent with the characteristic peaks of γ-Al2O3 (JCPDS No. 10-0425, JCPDS No. 34-0493), indicating that the alumina retains its Al2O3 crystalline structure post-TEPA loading.A comparison of the XRD patterns before and after impregnation reveals identical characteristic peak positions, suggesting that the crystal structure has not undergone fundamental changes.Additionally, the presence of distinct spike-like peaks in the XRD diffractogram may be attributed to the polycrystalline nature of the alumina microspheres used in the study[31].

Figure 4 .
Figure 4. Infrared spectra of Al 2 O 3 and TEPA-Al 2 O 3 .3.1.3.X-ray Diffraction Analysis (XRD) As depicted in Figure 5, the XRD patterns for Al 2 O 3 and TEPA-Al 2 O 3 are shown.The diffraction peaks for both samples are primarily observed at 2θ values of 19.46 • , 28.24 • , 31.93 • , 37.61 • , 45.83 • , 60.86 • , and 67.26 • .The positions of these peaks are consistent with the characteristic peaks of γ-Al 2 O 3 (JCPDS No. 10-0425, JCPDS No. 34-0493), indicating that the alumina retains its Al 2 O 3 crystalline structure post-TEPA loading.A comparison of the XRD patterns before and after impregnation reveals identical characteristic peak positions, suggesting that the crystal structure has not undergone fundamental changes.Additionally, the presence of distinct spike-like peaks in the XRD diffractogram may be attributed to the polycrystalline nature of the alumina microspheres used in the study[31].

Figure 5 . 20 Figure 6 .
Figure 5.The curve of XRD of Al 2 O 3 and TEPA-Al 2 O 3 .3.1.4.Thermal Gravimetric Analysis (TGA)As depicted in Figure6, the thermal behavior of both Al 2 O 3 and TEPA-Al 2 O 3 across a specified temperature range is illustrated.Notably, the TEPA-loaded alumina begins to exhibit weight loss at approximately 100 • C.However, the thermal stability of the novel

Figure 6 . 20 Figure 7 .
Figure 6.The curve of TG and DTG of Al 2 O 3 and TEPA-Al 2 O 3 in the temperature range of 30~1000 • C. 3.1.5.Scanning Electron Microscope and Energy Dispersive Spectrometer Analysis (SEM-EDS) SEM-EDS characterization was conducted on Al 2 O 3 before and after amine loading to examine the surface morphology and elemental distribution, as depicted in Figure 7. Panels (a) and (b) showcase the SEM images of Al 2 O 3 and TEPA-Al 2 O 3 , respectively, revealing that the alumina possesses a layered structure with abundant folds [31], providing ample space for the insertion of TEPA.The surface of TEPA-Al 2 O 3 is covered with a multitude of uniformly distributed fine particles, indicating an even loading of TEPA onto the alumina surface.Energy-dispersive X-ray spectroscopy (EDS) spectra for both Al 2 O 3 and TEPA-Al 2 O 3 are displayed in panels (c) and (e), respectively.These spectra clearly demonstrate an enriched and homogenized distribution of nitrogen (N) in the adsorbent subsequent to TEPA loading.Panel (d) illustrates the elemental distribution for Al 2 O 3 , and upon approximate estimation, the relative percentage contents for C, O, and Al elements are approximately 43.02%, 39.01%, and 17.97%, respectively.Following the loading of TEPA onto the adsorbent, in addition to C, O, and Al, the presence of the N element is also detected, with an estimated relative percentage content of approximately 7.35%.These results collectively indicate that TEPA has been uniformly loaded onto the surface of Al 2 O 3 .

Atmosphere 2024 ,
15,  x FOR PEER REVIEW 11 of 20 trend may reflect variations in adsorption rates at different TEPA loadings, suggesting an optimal CO2 adsorption rate at specific TEPA concentrations.Notably, among the various TEPA-Al2O3 adsorbents studied, 4-TEPA-Al2O3 demonstrated the highest CO2 adsorption capacity (reaching 48.5 mg/g) and was thus selected for subsequent experimentation.

Figure 8 .
Figure 8.The influence of TEPA impregnation solution concentration on the CO2 adsorption performance of amine-modified adsorbents.

Figure 8 .
Figure 8.The influence of TEPA impregnation solution concentration on the CO 2 adsorption performance of amine-modified adsorbents.

Figure 9 .
Figure 9.The impact of the high gravity factor on the CO2 adsorption performance of amine-modified adsorbents.

Figure 9 .
Figure 9.The impact of the high gravity factor on the CO 2 adsorption performance of amine-modified adsorbents.

Figure 10 .
Figure 10.The impact of gas flow rate on the CO2 adsorption performance of amine-modified adsorbents.

Figure 10 .
Figure 10.The impact of gas flow rate on the CO 2 adsorption performance of amine-modified adsorbents.

Figure 11 .
Figure 11.The comparison of kinetic model results and experimental CO2 adsorption amounts for 4-TEPA-Al2O3 in the Rotating Adsorption Bed (RAB) and fixed bed.

Figure 11 .
Figure 11.The comparison of kinetic model results and experimental CO 2 adsorption amounts for 4-TEPA-Al 2 O 3 in the Rotating Adsorption Bed (RAB) and fixed bed.

Table 4 .
The principal parameters for the kinetics model fitting of CO 2 adsorption from air on TEPA-Al 2 O 3 .

Table 1 .
Structural parameters of rotating packed bed.

Table 2 .
The relationship between rotational speed and high gravity factor in the rotating adsorption bed.

m 2 /g) a V pore (cm 3 /g ) b d (nm) c Amine Loading (%) d
a BET surface area; b Total pore volume; c Average pore size; d The actual value from TGA.

Table 4 .
The principal parameters for the kinetics model fitting of CO2 adsorption from air on TEPA-Al2O3.

Table 5 .
Comparison of adsorbents of CO2 in some literature and this work.

Table 5 .
Comparison of adsorbents of CO 2 in some literature and this work.MCF, silica mesocellular foam; b PAA, Synthesis of Poly(allylamine); c PEIBr, branched PEI. a