Recent Developments in Understanding Biochar’s Physical–Chemistry

: Biochar is a porous material obtained by biomass thermal degradation in oxygen-starved conditions. It is nowadays applied in many ﬁelds. For instance, it is used to synthesize new materials for environmental remediation, catalysis, animal feeding, adsorbent for smells, etc. In the last decades, biochar has been applied also to soils due to its beneﬁcial effects on soil structure, pH, soil organic carbon content, and stability, and, therefore, soil fertility. In addition, this carbonaceous material shows high chemical stability. Once applied to soil it maintains its nature for centuries. Consequently, it can be considered a sink to store atmospheric carbon dioxide in soils, thereby mitigating the effects of global climatic changes. The literature contains plenty of papers dealing with biochar’s environmental effects. However, a discrepancy exists between studies dealing with biochar applications and those dealing with the physical-chemistry behind biochar behavior. On the one hand, the impression is that most of the papers where biochar is tested in soils are based on trial-and-error procedures. Sometimes these give positive results, sometimes not. Consequently, it appears that the scientiﬁc world is divided into two factions: either supporters or detractors. On the other hand, studies dealing with biochar’s physical-chemistry do not appear helpful in settling the factions’ problem. This review paper aims at collecting all the information on physical-chemistry of biochar and to use it to explain biochar’s role in different ﬁelds of application.


Introduction
Global climate change (GCC) is the most important challenge mankind is facing in the modern era. The whole scientific community agrees that the main cause of GCC are greenhouse gases (e.g., carbon dioxide, methane, and various nitrous oxides) which have atmospheric concentrations that depends not only on natural Earth emissions (e.g., biomass decay and burning, oceans, volcanos, earthquakes) but also, and mainly, on anthropic activities such as agriculture, deforestation, and burning of fossil fuels [1].
To account for the effects of global climate change on living systems, the term "environmental sustainability" has become keyword for scientists and politicians. It intends to maintain environmental resources, thereby making them available for future generations [2]. To this aim, one of the strategies applied to contrast GCC effects is to limit the impact of anthropic activities on the environment, thus reducing the consumption  To understand why biochar/charcoal/char is very helpful in reducing the effects of global warming, one has to consider that carbonaceous plant metabolites produced by photosynthesis return back to CO 2 when plant materials are allowed to decompose ( Figure 2A). However, if plant residues are thermally degraded in oxygen-starved conditions, up to 60% of the original plant C can be transformed into biochar/charcoal/char ( Figure 2B). Mineralization of this carbonaceous material back to CO 2 is extremely slow when it is used to improve soil quality. For this reason, it provides a pathway for temporary CO 2 subtraction from the global C cycle and reduces the concentration of carbon dioxide in the atmosphere [34].
Agronomy 2021, 11, x FOR PEER REVIEW 3 of 42 To understand why biochar/charcoal/char is very helpful in reducing the effects of global warming, one has to consider that carbonaceous plant metabolites produced by photosynthesis return back to CO2 when plant materials are allowed to decompose (Figure 2A). However, if plant residues are thermally degraded in oxygen-starved conditions, up to 60% of the original plant C can be transformed into biochar/charcoal/char ( Figure  2B). Mineralization of this carbonaceous material back to CO2 is extremely slow when it is used to improve soil quality. For this reason, it provides a pathway for temporary CO2 subtraction from the global C cycle and reduces the concentration of carbon dioxide in the atmosphere [34].
controlled by sustainability standards, their use for biochar production may pose serious problems for biodiversity protection, wildlife habitats, soil protection, and water production, thereby limiting the eco-sustainability of biochar applications. On the other hand, the definition by Lehmann and coworkers [9,43,44] is only oriented towards agronomic uses. In fact, it does not consider production methodologies, and it does not include the very important greenhouse gas reduction property.
It is not possible to provide a single general definition for sustainability. It depends on the field where it is applied. As an example, sustainability is the ability to manage "a resource for maximum continuing production, consistent with the maintenance of a constantly renewable stock" when it deals with biological resources [2]. In agriculture, sustainability is "the ability of a system to maintain productivity in spite of a major disturbance" [2]. In the energy field, the term is associated with the "transition from a global energy system based on consuming depletable fossil fuels to a sustainable system based on non-depletable fuels" [2]. When dealing with ecology, sustainability refers to the conservation of the micro-and macroenvironments where flora and fauna can survive [2]. All these sustainability concepts must be fulfilled in order to produce a biochar which is environmentally sustainable. To this aim, the European Biochar Foundation [48] substantially changed the definition by Lehman and co-workers [48]: "Biochar is a porous, carbonaceous material that is produced by pyrolysis of plant biomasses and is applied in such a way that the contained carbon remains stored as a longterm C sink or replaces fossil carbon in industrial manufacturing. It is not made to be burnt for energy generation".
According to this more general definition, the only biomasses that can be used for biochar production are those obtained by fast growing plants, plant residues from certified forestry management, agricultural residues, and organic wastes from urban areas [28]. Moreover, the European Biochar Certificate (EBC) definition accounts also for all the possible uses of biochar as a new material such as its application in paper and cellulose industry, for advanced building materials, electronics, 3D printing, decontamination, such as in water and sewage treatment, mining, air filtration, textile industry, and animal farming [49]. Table 1 reports the types of biomasses which can be used to produce biochar according to the EBC [48]. Table 1. Types of biomasses to be used for the production of biochar according to the European Biochar Certificate [48].

Origin Feedstock
Local waste collection services with waste separation Biodegradable waste, biodegradable waste with kitchen waste, biodegradable waste with kitchen waste and leftovers In the aforementioned structure, hetero-atoms, such as O, N, P, and S, are predominantly incorporated within the aromatic rings, thereby contributing to the complex surface chemistry and reactivity of biochar [50].
The chemical nature of biochar induces to think that environmental release of polycyclic aromatic hydrocarbons (PAHs, persistent pollutants formed during pyrolysis) may occur [3,52,53]. Based on this assumption, they put forward the precautionary principle and limit biochar field applications. However, in the last decade, many papers appeared in the literature, all dealing with the high environmental stability of biochar when it is applied to soils [3,40,[52][53][54][55][56][57][58][59][60][61][62][63]. In particular, Rombolà et al. [55] reported not only that the concentration of total PAHs remains below the maximum acceptable concentration established in many European countries, but also that their concentration decreases within five years after the application of biochar to soils. However, it is noteworthy that Rombolà's Example of biochar structure intended as a stacked crystalline graphene sheets and randomly ordered amorphous aromatic structures (this figure has been reproduced from Reference [51]).
In the aforementioned structure, hetero-atoms, such as O, N, P, and S, are predominantly incorporated within the aromatic rings, thereby contributing to the complex surface chemistry and reactivity of biochar [50].
The chemical nature of biochar induces to think that environmental release of polycyclic aromatic hydrocarbons (PAHs, persistent pollutants formed during pyrolysis) may occur [3,52,53]. Based on this assumption, they put forward the precautionary principle and limit biochar field applications. However, in the last decade, many papers appeared in the literature, all dealing with the high environmental stability of biochar when it is applied to soils [3,40,[52][53][54][55][56][57][58][59][60][61][62][63]. In particular, Rombolà et al. [55] reported not only that the concentration of total PAHs remains below the maximum acceptable concentration established in many European countries, but also that their concentration decreases within five years after the application of biochar to soils. However, it is noteworthy that Rombolà's paper [53] poses a serious methodological problem. It is not clear whether PAH reduction following biochar application is due either to leaching or to PAH decomposition. The former may still be a risk because of possible accumulation in groundwater and food magnification. Polycyclic aromatic hydrocarbons decomposition occurs mainly through fragmentation. Over the long term, most of the biochar nanoparticles leach out. Although these are not toxic, at present, it is not possible to exclude any groundwater contamination risks [64]. Regardless of the possible mechanisms related to PAH reduction in soils after biochar application, the European Biochar Foundation established a PAH threshold of  [48], which is far below the background contamination. In addition, as reported by Conte et al. [28]: "Biochar shows a very good adsorption potential for hydrophobic materials [ . . . ]. For this reason, the USEPA suggests charcoal as the best available technology for the treatment of hydrophobic contamination. [ . . . ] the concern about possible dioxin content in biochars is overstated. On the one hand, the amount of dioxins in biochars that have been analyzed to date was very low [ . . . ]. On the other hand, any dioxins present are strongly bound to biochar, thereby being unavailable for plant nutrition and to the food chain [ . . . ]".
In other words, biochar adsorbs more environmental PAHs and other hydrophobic pollutants than it releases. Table 2 reports the main characteristics to produce a biochar which follows the EBC guidelines. According to what has been reported above, the answer to the question regarding biochar's risk to health can only be that biochar is not risky provided that it is produced and used according to the recommendations from the European Biochar Foundation [48].

Aim of This Work
Biochar research received a great deal of interest in the last decade and its role in many different applications has been clarified. However, the understanding of biochar behavior seems more empirical than relying on a well-structured theoretical framework. For this reason, we intend to discuss the most recent literature to provide a general and critical overview of the newest findings on biochar's physical chemistry, thereby highlighting all the main information useful to disclose the molecular mechanisms of biochar functioning. Due to its multivalent characteristics, we will focus not only on the mechanisms of biochar applied to soils, but also on its role in environmental remediation.

Making Biochar: A Brief Summary of the Main Production Methodologies
Notwithstanding that the focus of this review paper is not on biochar production, a brief summary of simple techniques used to obtain the aforementioned material is given. The idea is to provide an easy tool for inexperienced readers who want to approach biochar science. The production methods listed here are not exhaustive of the whole range of techniques used to obtain biochar; therefore, readers are recommended to consult the publications in references [44,65,66] for wider and more detailed information.
The different techniques applied for biochar production provide materials with typical characteristics, making them reliable for many specific uses [49]. As an example, when only small amounts of biochar are needed for lab studies, the lab-muffle-furnace method can be applied (Appendix A). This home-made, quick procedure to transform any kind of biomass is affected by the researcher's awareness and by the impossibility of correctly controlling all the production parameters (e.g., atmosphere composition, quenching methodology). Therefore, a reliable approach to the lab-muffle-furnace method would be for the same researcher to undertake the production of biochar for the entire research group. This is the only way to obtain a carbonaceous material with repeatable characteristics.
A valid alternative to obtain biochars with reproducible chemical-physical properties is the use of lab-pyrolizers (Appendix B). These are designed to adjust the pyrolyzing atmosphere and quenching procedures. Depending on the pyrolizer characteristics, the amount of biochar that is produced can be in the order of tens of grams, which is at least ten times more than the amount obtained by the lab-muffle-furnace method. Being highly reproducible, the advantages of the use of lab-pyrolizers rely on the fact that the obtained biochar can be used for the production of new materials such as electrodes [67], sorbent for specific pollutants [68], or even for medicine [49].
The hydrothermal carbonization (Appendix C) is usually applied to retrieve biochars (which in this case are referred to as hydrochars) having very good fertilizing characteristics [69,70]. This is mainly due to the presence of residual polysaccharide and polypeptide units that are not thermally decomposed by the mild temperature conditions used during the process [71].
When larger amounts of material are needed for agricultural purposes, the Kon-Tiki kiln can be a useful tool for biochar production (Appendix D). This method allows control of the quenching procedure, whereas no control of the pyrolysis temperature is achieved. The biochar obtained by this home-made procedure appeared to be very effective in increasing pumpkin production [72].
In Appendix E, the industrial thermochemical carbonization (also referred to as gasification) is briefly summarized. The method is thought to produce syn-gas which can be applied for energy production, while biochar is obtained as a low-cost by-product [6]. The latter can be applied to achieve different aims such as agricultural purposes [16], environmental remediation, electrical energy storage, electrochemical sensors, and catalysis [73].

The Effect of Feedstock Nature
The nature of the biomass used for biochar production appears to play a major role in addressing its chemical-physical properties [28]. Different feedstocks show different composition in terms of cellulose, hemicellulose, lignin as well as inorganic components [21,74]. These differences result in a different biomass behavior during the thermal degradation described in the previous paragraph [74,75]. In particular, hemicellulose is the first to undergo decomposition at a temperature ranging between 200 and 260 • C, while cellulose breaks down at 240-350 • C and lignin at 280-500 • C [74]. The pyrolysis mechanism of hemicelluloses starts with a depolymerization producing oligosaccharides. Therefore, xylan chain cleavage and molecular rearrangement produces a xylopyranose. The xylopyranose is further degraded to small molecular weight compounds such as furfural and fragments containing two or three carbon atoms. As for the hemicellulose, also cellulose is first depolymerized into oligosaccharides. Then the glucosidic bonds of the oligosaccharides are broken to produce D-glucopyranose. The intramolecular rearrangement of D-glucopyranose produces levoglucosan. The latter further decomposes to form small molecular weight compounds. Pyrolysis of lignin generates phenolic compounds such as guaiacol-like, phenol-like, syringol-like, and catechol-like systems [74].
The relative abundances of the biomass components described above effect reactivity and yield, thereby affecting the ratios between the volatile products (e.g., bio-oil and gas) and the biochar [74][75][76]. For instance, biomasses with a low content of lignin, minerals, and nitrogen are used to produce bio-oil and fuel-gas. Conversely, feedstock containing larger amounts of lignin are mainly applied to achieve biochar [8]. As a rule of thumb, the biochars produced from woods have low ash and high carbon contents, whereas the thermal degradation of herbaceous biomasses, biosolids and manures result in biochars with low carbon content and larger amounts of ashes, nitrogen, phosphorus, potassium, and sulphur [44,77].
Besides their chemical nature, the biomasses used for biochar production affect also its porosity and, therefore, its adsorptive properties [44,78]. During the thermal degradation, the loss of volatile organic compounds results in a volume reduction. Consequently, the arising mineral and carbon skeleton retain the rudimentary feedstock porosity and structure. The residual cellular structures of botanical origin that are present and identifiable in biochars contribute to the majority of the biochar macro-porosity [44]. This is confirmed by microscopic investigations showing the presence of aligned honeycomb-like groups of pores ( Figure 4). The latter ones are due to the carbonaceous skeleton arising from the biological capillary structure of the raw material. Finally, the large-sized pores serve as a feeder to lower-dimension pores [44]. and nitrogen are used to produce bio-oil and fuel-gas. Conversely, feedstock containing larger amounts of lignin are mainly applied to achieve biochar [8]. As a rule of thumb, the biochars produced from woods have low ash and high carbon contents, whereas the thermal degradation of herbaceous biomasses, biosolids and manures result in biochars with low carbon content and larger amounts of ashes, nitrogen, phosphorus, potassium, and sulphur [44,77].
Besides their chemical nature, the biomasses used for biochar production affect also its porosity and, therefore, its adsorptive properties [44,78]. During the thermal degradation, the loss of volatile organic compounds results in a volume reduction. Consequently, the arising mineral and carbon skeleton retain the rudimentary feedstock porosity and structure. The residual cellular structures of botanical origin that are present and identifiable in biochars contribute to the majority of the biochar macro-porosity [44]. This is confirmed by microscopic investigations showing the presence of aligned honeycomb-like groups of pores ( Figure 4). The latter ones are due to the carbonaceous skeleton arising from the biological capillary structure of the raw material. Finally, the large-sized pores serve as a feeder to lower-dimension pores [44].
The number of inorganic components in the feedstock also plays an important role in determining the physical structure of biochar. Depending on the applied processing conditions (outlined below), ash fusion or sintering may dramatically change the physical and structural composition of biochar. The number of inorganic components in the feedstock also plays an important role in determining the physical structure of biochar. Depending on the applied processing conditions (outlined below), ash fusion or sintering may dramatically change the physical and structural composition of biochar.

The Biomass Pretreatment
The chemical-physical biochar characteristics depend not only on the feedstock's nature but also on the pretreatments to which it was subjected. Pretreatments are usually applied to facilitate thermal degradation. The hierarchical and recalcitrant nature of biomasses (due to the intricate structure where cellulose, hemicellulose, and lignin are rigidly associated through non-covalent bonds and covalent cross-linkages) prevent any easy disruption, thereby causing undesirable energy expenditure when biomass thermal degradation is used for energy production (e.g., gasification). The advantages of biomass pretreatments are also related to the formation of solid by-products with specific properties enabling their use in wastewater treatments, air cleaning, soil remediation, and catalytic purposes to facilitate energy production [8,76,[79][80][81][82][83]. In particular, washing biomass prior to pyrolysis with either acidic or basic solutions may remove up to 70% of the initial minerals contained in the feedstock [79,84,85]. However, the use of dilute acid and hot water results in a slight decomposition of hemicellulose. Conversely, the application of dilute alkali disrupts lignin structure and solubilizes hemicellulose. As a consequence, the thermal degradation applied after the acid/base treatment achieves a higher yield in liquids (tar) and gases at the expense of the solid residue [79,84,85]. The latter, when obtained after biomass treatment with a 1:1 (v:v) HNO 3 /H 2 O 2 solution, appears to have enhanced adsorption capacity for cadmium from high concentration solutions as compared to biochars obtained from non-pretreated biomasses [86]. This difference can be explained assuming that the treatment favors biochar mesoporosity.
The three dimensional structure of the biomass can also be altered by the use of ionic liquids (ILs) [79]. These are poorly coordinated melted salts made by at least one large organic ion (possibly with a delocalized charge) with a relatively low reticular energy [87]. When biomass is placed in an ionic liquid, the H-bond net is broken by the interactions with the IL cation and anion moieties ( Figure 5), thereby providing a material that can be better used for energy purposes (i.e., high yield in biofuels rather than biochar) [79]. However, when the biomass is first heated in concentrated sulphuric acid then treated with IL, a functionalized IL-biochar is obtained. The latter is successfully applied as a catalyst in cellulose dissolution for biofuel production [88,89].
honeycomb-like group of pores, due to the cellular structure of the feedstock, are clearly visible (unpublished results from the group of P.C.).

The Biomass Pretreatment
The chemical-physical biochar characteristics depend not only on the feedstock's nature but also on the pretreatments to which it was subjected. Pretreatments are usually applied to facilitate thermal degradation. The hierarchical and recalcitrant nature of biomasses (due to the intricate structure where cellulose, hemicellulose, and lignin are rigidly associated through non-covalent bonds and covalent cross-linkages) prevent any easy disruption, thereby causing undesirable energy expenditure when biomass thermal degradation is used for energy production (e.g., gasification). The advantages of biomass pretreatments are also related to the formation of solid by-products with specific properties enabling their use in wastewater treatments, air cleaning, soil remediation, and catalytic purposes to facilitate energy production [8,76,[79][80][81][82][83]. In particular, washing biomass prior to pyrolysis with either acidic or basic solutions may remove up to 70% of the initial minerals contained in the feedstock [79,84,85]. However, the use of dilute acid and hot water results in a slight decomposition of hemicellulose. Conversely, the application of dilute alkali disrupts lignin structure and solubilizes hemicellulose. As a consequence, the thermal degradation applied after the acid/base treatment achieves a higher yield in liquids (tar) and gases at the expense of the solid residue [79,84,85]. The latter, when obtained after biomass treatment with a 1:1 (v:v) HNO3/H2O2 solution, appears to have enhanced adsorption capacity for cadmium from high concentration solutions as compared to biochars obtained from non-pretreated biomasses [86]. This difference can be explained assuming that the treatment favors biochar mesoporosity.
The three dimensional structure of the biomass can also be altered by the use of ionic liquids (ILs) [79]. These are poorly coordinated melted salts made by at least one large organic ion (possibly with a delocalized charge) with a relatively low reticular energy [87]. When biomass is placed in an ionic liquid, the H-bond net is broken by the interactions with the IL cation and anion moieties ( Figure 5), thereby providing a material that can be better used for energy purposes (i.e., high yield in biofuels rather than biochar) [79]. However, when the biomass is first heated in concentrated sulphuric acid then treated with IL, a functionalized IL-biochar is obtained. The latter is successfully applied as a catalyst in cellulose dissolution for biofuel production [88,89]. Biochar characteristics can be modified also by treating biomasses with metals, e.g., Mg, Fe, Ca, and Al (usually as nitrogen-containing or chloride salts or by electrodeposition) prior to the thermal degradation [80]. The role of the metals is to enhance biochar adsorption properties, thereby making it a good material for environmental remediation [80]. Enhancement of the biochar's adsorptive capacity following this treatment can be explained by the Lewis acid-like behavior of the metals added to biomasses prior to the pyrolysis.
Other biomass pretreatments are: (i) the electrospinning of a cellulose acetate solution with subsequent deacetylation and pyrolysis in order to produce carbon fibers to be applied for the production of electrodes [90]; (ii) the low-temperature pre-carbonization combined with KOH chemical activation in order to retrieve tubular nanomaterials to be applied for the achievement of super-capacitors [91]; (iii) the addition of (NH 4 ) 2 HPO 4 before carbonization in order to increase biochar porosity, cross-linking, and availability of nitrogen and phosphorous [91]. A complete review of biomass pretreatments for the achievement of biochars for the production of new materials is reported in Bi et al. [27].

The Influence of the Pyrolysis Conditions
The experimental conditions applied during the biomass thermal treatments (e.g., temperature and atmosphere) greatly affect biochar characteristics and properties. Therefore, biochar value in terms of its performance for its possible application (e.g., agriculture, soil carbon sequestration, catalyst) is strongly dependent on how pyrolysis is conducted. In the following sub-sections, the most important effects of pyrolysis conditions on biochar characteristics are reviewed.

Temperature Effect on the Amount of Carbon in Biochars
Pyrolysis temperature significantly influences the final biochar structural and physicochemical properties. This is due to the release of volatiles and the formation and volatilization of intermediate melts [77,[92][93][94]. Many studies indicate that the higher the temperature, the larger is the biochar carbon-content since loss of nitrogen, hydrogen, and oxygen are recorded [77,[92][93][94][95]. The biochars produced at low temperature (<350 • C) reveal a carbon content below 60% (w/w), while as the temperature increases in the range 400-500 • C, the carbon-content increases to 60-80% (w/w). For temperatures as high as 500 • C, the carbon content reaches values larger than 80% (w/w). However, the latter case is valid mostly for wood-derived biochar [44]. When animal residues (e.g., manure) are used, the carbon content reveals an opposite trend [96,97]. This is explained by the effect of the large amount of ashes present in the biomasses from animal origin [97].

Temperature Effect on the Chemical Nature of Biochar Components
Besides the changes of carbon content in biochars, also the chemical nature of the biochar organic components varies with temperature. With increasing temperatures, the amount of alkyl carbons decreases, and aromatic residues increases [44,98,99] (Figure 6). From approximately 250-450 • C, the amount of alkyl and aromatic moieties increases, while if the temperature reaches ≥500 • C, the resulting biochar is made by highly recalcitrant forms of organic matter, i.e., poly-condensed aromatic hydrocarbons ( Figure 6). Therefore, the biochars produced at high temperatures (≥500 • C) are chemically more stable and more resistant to microbial and abiotic degradations than those obtained at lower temperatures.

Temperature Effect on Biochar Ash Content
Temperature increase also results in a decreased amount of the final solid product, with a concomitant increase in the ash content due to the naturally occurring inorganic components in all biomasses [92][93][94]. As an example, the biochar produced from chicken manure revealed an ash content increasing from 40% to 60%, as the temperature rose from 300 • C to 600 • C [77]; the ash content in the biochar from apple tree branches varied 6-9% as the temperature rose from 300 • C to 600 • C [93]; the biochar obtained from pine sawdust evidenced an increase of the ash content from 1% to 2% by increasing the pyrolysis temperature from 350 • C to 750 • C [94]; the ash content in a biochar obtained from pea straw increased from 15% to 24% as the temperature rose from 350 • C to 750 • C [94]; the biochar from coconut flesh waste showed an ash content varying from 5% to 8% as the temperature was changed from 350 • C to 600 • C [95]. These findings can be explained by considering that the higher the temperature, the larger is the amount of volatile organic compounds (VOCs) produced during the pyrolysis, thereby leading to an amount of solid biochar smaller than that obtained at lower temperatures.

Temperature Effect on Biochar Surface Properties
The progressively larger amount of volatile organic components released from the feedstock with rising temperatures is responsible for the reduction of the surface functional groups which, in turn, cause the adsorption properties of biochars [39,[100][101][102][103]. According to Chun et al. [100], low-temperature biochars (that is, those obtained at 300-400 • C) revealed an amount of polar groups (e.g., -OH, -COOH, -C=O etc.) larger than those obtained at temperatures above 500 • C. Because of this, Uchimiya et al. [15,104] reported that biochars obtained at temperatures ≥500 • C revealed a lower capacity to trap heavy metals. Furthermore, the reduction of the adsorption capacity is due also to the biochar's physical structure as the temperature increases [44,[104][105][106]. In particular, the release of the volatile organic components generates pore structures similar to those of the biomass cells (see above). Pore volume and average pore size (i.e., the porosity) increase as the temperature rises up to approximately 500 • C. Above this temperature, pore coalescence and ash melting occur, thereby resulting in a reduction of the porosity [91,107,108]. Figure 7 schematically summarizes pore formation during biomass thermal degradation. The leftmost side of the figure represents the honeycomb-like cells in the biomass prior to the pyrolysis. As the temperature increases to 500 • C, the volatilization of the organic components produces holes as schematized in the central part of Figure 7. Finally, above 500 • C, the high pressure generated by salt melting, together with the production of progressively larger amounts of VOCs, provokes disruption of cell walls and pore coalescence (at the rightmost side of Figure 7), thereby allowing reduction of biochar surface area and capacity to retain organic and inorganic pollutants [107].
Agronomy 2021, 11, x FOR PEER REVIEW 12 of 42 the high pressure generated by salt melting, together with the production of progressively larger amounts of VOCs, provokes disruption of cell walls and pore coalescence (at the rightmost side of Figure 7), thereby allowing reduction of biochar surface area and capacity to retain organic and inorganic pollutants [107].

Effect of Pyrolysis Heating Rate and Holding Time
Three modes to perform pyrolysis can be recognized. As reported in Table 3, they differ for the heating rate, that is the ramp applied to reach the pyrolysis temperature, and the holding time, that is the time during which the heating temperature is maintained [109,110].
Fast pyrolysis is carried out by applying very high heating rates (that is in the order of hundreds of degrees Celsius per seconds, °C s −1 ) and a very short holding time (<2 s) ( Table 3). Under the aforementioned conditions, the heating rate is so rapid that the biomass reaches the pyrolysis temperature before any thermal decomposition starts [111]. This mode is applied to obtain high yields of bio-oils that come from the condensation of the volatile organic compounds generated by the biomass heating [112]. Bio oils-mainly composed of 20-25% water, 20-25% water-insoluble-lignin, 25-30% organic acids, 5-12% non-polar hydrocarbons, 5-10% sugars and 10-25% other oxygenated compounds [21]are used for the production of electrical energy. If the aim of fast pyrolysis is to produce a maximum quantity of bio-oils compared to biochar and syngas, usually conditions need to be accounted for: fine particle size of the biomass to be pyrolyzed (<1 mm), careful control of the final temperature (around 450-550 °C), heating rate > 200 °C s −1 , short hot vapor residence time (around 2 s), and rapid cooling of the vapors [111][112][113]. When the fast pyrolysis is conducted at a temperature ranging between 700 °C and 1000 °C, hydrogen gas is produced in addition to bio-oils [114]. The conventional or mid pyrolysis is conducted by applying a heating rate of approximately 20 °C s −1 and a pyrolysis temperature usually not above 600 °C held from a few

Effect of Pyrolysis Heating Rate and Holding Time
Three modes to perform pyrolysis can be recognized. As reported in Table 3, they differ for the heating rate, that is the ramp applied to reach the pyrolysis temperature, and the holding time, that is the time during which the heating temperature is maintained [109,110].  35 35 Fast pyrolysis is carried out by applying very high heating rates (that is in the order of hundreds of degrees Celsius per seconds, • C s −1 ) and a very short holding time (<2 s) ( Table 3). Under the aforementioned conditions, the heating rate is so rapid that the biomass reaches the pyrolysis temperature before any thermal decomposition starts [111]. This mode is applied to obtain high yields of bio-oils that come from the condensation of the volatile organic compounds generated by the biomass heating [112]. Bio oils-mainly composed of 20-25% water, 20-25% water-insoluble-lignin, 25-30% organic acids, 5-12% non-polar hydrocarbons, 5-10% sugars and 10-25% other oxygenated compounds [21]-are used for the production of electrical energy. If the aim of fast pyrolysis is to produce a maximum quantity of bio-oils compared to biochar and syngas, usually conditions need to be accounted for: fine particle size of the biomass to be pyrolyzed (<1 mm), careful control of the final temperature (around 450-550 • C), heating rate > 200 • C s −1 , short hot vapor residence time (around 2 s), and rapid cooling of the vapors [111][112][113]. When the fast pyrolysis is conducted at a temperature ranging between 700 • C and 1000 • C, hydrogen gas is produced in addition to bio-oils [114].
The conventional or mid pyrolysis is conducted by applying a heating rate of approximately 20 • C s −1 and a pyrolysis temperature usually not above 600 • C held from a few minutes up to a few hours (Table 3) [21,112,115]. This mode is applied to obtain a better biochar yield compared to the fast pyrolysis.
The slow pyrolysis mode-the oldest one, used for thousands of years to produce biochar for agricultural purposes [21,44,112]-is conducted by applying very low heating rates, low to moderate temperatures (around 400 • C) and long reaction times (up to days) ( Table 3). The long holding time ensures the conversion of condensable vapors into biochar and non-condensable gases. Unlike fast pyrolysis, the slow one does not necessarily need a fine feedstock particle size (smaller than 1 mm). In fact, raw materials that are not available as powders or fine particles are usually used [116]. Slow/conventional and fast pyrolysis generate different solid bio-carbon products, even when the same raw biomass materials are used. The most significant differences include the evolution of the specific surface area resulting from the development of a porous structure during the pyrolysis process, and the average pore size and pore size distribution [27].

Effect of the Pyrolysis' Atmosphere
Apart from temperature, heating, and holding times, also the atmosphere used during the thermal degradation influences the yield of the pyrolysis products and the biochar chemical-physical characteristics. As an example, Guizani et al. [117] reported that an atmosphere of carbon dioxide applied during the pyrolysis was responsible for the lower biochar yield as compared to the pyrolysis conducted under an N 2 atmosphere. This was explained by suggesting that carbon dioxide can hinder tar polymerization according to Equation (1) (tar polymerization is one of the secondary reactions contributing to biochar formation), can react with methane and hydrogen according to Equations (2) and (3) (thus altering syngas composition), and may favor biochar degradation via the Boudouard reaction described in Equation (4) [117]: Guizani et al. [117] also reported that the biochar produced in a CO 2 atmosphere has larger surface area and lower H/C and O/C ratios than those produced in an N 2 atmosphere.
These characteristics have been related to the better adsorption properties for organic and inorganic contaminants as compared to the same materials obtained in an N 2 atmosphere [118]. The ameliorated adsorption properties of the biochars obtained in a CO 2 atmosphere may also suggest a better nutrient exchange ability when they are applied to soils as amendments. However, no studies have been found to confirm such an expectation.
The results from Guizani et al. [117] have been confirmed by Fan et al. [118], Valdés et al. [119], and Luo et al. [120], whereas only partially by Molenda [121]. In particular, the latter reported that "biocarbon obtained in an atmosphere of carbon dioxide is characterized by a higher proportion of oxygen compared to the product produced in a nitrogen atmosphere". The differences among these studies lay in the different pyrolysis modes used to perform the CO 2 -driven thermal degradations. Fast pyrolysis was applied in Guizani et al. [117], Fan et al. [118], Valdés et al. [119], and Luo et al. [120], whereas slow pyrolysis followed by slow biochar cooling to room temperature was used in Molenda [121]. It is conceivable that the slow pyrolysis conditions may have avoided removal of the oxygenated functional groups (revealed by means of the infrared spectroscopy) laying on the surface of the biomass feedstock.
An alternative to carbon dioxide and/or nitrogen atmosphere is the application of an ammonia atmosphere. When NH 3 is used to drive thermal degradation of biomasses, nitrogen-enriched biochars are obtained. They can be used either as plant fertilizers or useful activated carbon in materials science (e.g., electronic, optic or transmission applications) [122][123][124]. Ammonia leads to the formation of pyridinic-, pyrrolic-, quaternary-N and pyridine-N-oxide groups.
N-activated biochars can be also obtained via the application of an atmosphere made by a mixture of carbon dioxide and ammonia. The results by Xiong et al. [125] and Zhang et al. [126] showed that five different chemical pathways can conceivably occur on the biomass surface during the thermal degradation ( Figure 8). In pathway 1, the alcoholic moieties can react with ammonia generating primary amines. The latter can combine with carbon dioxide to provide N-alkyl ammonium salts and N-alkil carbamates. Pathway 2 shows that, in the presence of ammonia, ether moieties are transformed to secondary amines. The latter combine with carbon dioxide to produce N,N-dialkyl ammonium salts and N,N-dialkyl carbamates. Primary and secondary amines (coming from Pathways 1 and 2, respectively) can react with each other in the presence of carbon dioxide to produce N-alkyl ammonium salts and N,N-dialkyl carbamates (Pathway 3). The N-alkyl carbamates from Pathway 1 may rearrange with water expulsion to produce isocianates (Pathway 4). Finally, the N-alkyl carbamates from Pathway 1 and the N,N-dialkyl ammonium salts from Pathway 2 can condense to form N-alkyl, N',N'-dialkyl urea derivatives (Pathway 5).
The simultaneous presence of all the aforementioned moieties obtained by the chemical transformations of the biomass surfaces appear to be responsible for the very high carbon dioxide affinity of the produced biochars [125,126]. This may suggest that the CO 2 /NH 3obtained biochars can have different effects when applied to soils. On the one hand, they can work as nitrogen suppliers to plant nutrition. On the other hand, they can trap atmospheric CO 2 in soils, thereby contributing to the mitigation of global climatic change.
An alternative to carbon dioxide and/or nitrogen atmosphere is the application of an ammonia atmosphere. When NH3 is used to drive thermal degradation of biomasses, nitrogen-enriched biochars are obtained. They can be used either as plant fertilizers or useful activated carbon in materials science (e.g., electronic, optic or transmission applications) [122][123][124]. Ammonia leads to the formation of pyridinic-, pyrrolic-, quaternary-N and pyridine-N-oxide groups.
N-activated biochars can be also obtained via the application of an atmosphere made by a mixture of carbon dioxide and ammonia. The results by Xiong et al. [125] and Zhang et al. [126] showed that five different chemical pathways can conceivably occur on the biomass surface during the thermal degradation ( Figure 8). In pathway 1, the alcoholic moieties can react with ammonia generating primary amines. The latter can combine with carbon dioxide to provide N-alkyl ammonium salts and N-alkil carbamates. Pathway 2 shows that, in the presence of ammonia, ether moieties are transformed to secondary amines. The latter combine with carbon dioxide to produce N,N-dialkyl ammonium salts and N,N-dialkyl carbamates. Primary and secondary amines (coming from Pathways 1 and 2, respectively) can react with each other in the presence of carbon dioxide to produce N-alkyl ammonium salts and N,N-dialkyl carbamates (Pathway 3). The N-alkyl carbamates from Pathway 1 may rearrange with water expulsion to produce isocianates (Pathway 4). Finally, the N-alkyl carbamates from Pathway 1 and the N,N-dialkyl ammonium salts from Pathway 2 can condense to form N-alkyl, N',N'-dialkyl urea derivatives (Pathway 5). The simultaneous presence of all the aforementioned moieties obtained by the chemical transformations of the biomass surfaces appear to be responsible for the very high carbon dioxide affinity of the produced biochars [125,126]. This may suggest that the CO2/NH3-obtained biochars can have different effects when applied to soils. On the one hand, they can work as nitrogen suppliers to plant nutrition. On the other hand, they can trap atmospheric CO2 in soils, thereby contributing to the mitigation of global climatic change. Figure 8. Chemical pathways involved in the changes of biomass surface chemistry during the pyrolysis in CO 2 /NH 3 atmosphere. All the reactions described here do not account for the stoichiometry. The scheme has been re-elaborated from references [125,126].
Besides the effects on the biochar surface chemistry, the CO 2 /NH 3 atmosphere also affects pore formation and size [125,126]. Figure 9 shows that the atmosphere made solely by carbon dioxide first improves pore volume and surface area as the temperature is raised up to a value of around 700 • C. Above 800 • C, pore collapse occurs. Therefore, pore volume and surface area reduction are observed. As the thermal degradation is carried out in an ammonia atmosphere, pore clogging with reduction of porosity and surface area is observed up to a temperature of around 600 • C. As the temperature increases, the N-containing groups (generated by the reactions between ammonia and the walls of the biomass pores) are degraded. At the same time, pore collapse occurs. When the CO 2 /NH 3 mixture is used as pyrolysis atmosphere, a synergic effect of both gases is observed. While carbon dioxide allows pore volume and surface area improvement, ammonia reacts with the pore walls, thereby forming a kind of glue-like layer which improves the adsorption properties of the biochar as compared to the materials obtained either in pure CO 2 or NH 3 atmospheres. As the temperature is raised above the value of around 800 • C, pore collapse and degradation of N-containing groups occurs [125,126]. pyrolysis in CO2/NH3 atmosphere. All the reactions described here do not account for the stoichiometry. The scheme has been re-elaborated from references [125,126].
Besides the effects on the biochar surface chemistry, the CO2/NH3 atmosphere also affects pore formation and size [125,126]. Figure 9 shows that the atmosphere made solely by carbon dioxide first improves pore volume and surface area as the temperature is raised up to a value of around 700 °C. Above 800 °C, pore collapse occurs. Therefore, pore volume and surface area reduction are observed. As the thermal degradation is carried out in an ammonia atmosphere, pore clogging with reduction of porosity and surface area is observed up to a temperature of around 600 °C. As the temperature increases, the Ncontaining groups (generated by the reactions between ammonia and the walls of the biomass pores) are degraded. At the same time, pore collapse occurs. When the CO2/NH3 mixture is used as pyrolysis atmosphere, a synergic effect of both gases is observed. While carbon dioxide allows pore volume and surface area improvement, ammonia reacts with the pore walls, thereby forming a kind of glue-like layer which improves the adsorption properties of the biochar as compared to the materials obtained either in pure CO2 or NH3 atmospheres. As the temperature is raised above the value of around 800 °C, pore collapse and degradation of N-containing groups occurs [125,126]. . Scheme of pore formation in CO2, NH3, and CO2/NH3 atmospheres. The grey color indicates the formation of a "glue"-like layer made by N-containing groups. The scheme has been elaborated from References [125,126].
The amount of oxygen-containing surface functional groups with the aim to produce biochar having a high affinity for metal ions and, therefore, being possibly applied for wastewater treatments, has been obtained by means of application of air steam under mild temperature conditions (that is temperatures ~ 300 °C) [127]. The mild temperatures are needed to prevent biomass burn-off while oxygen-functionalization occurs ( Figure 10). The advantage of this oxygen-rich carbonaceous material is related also to its high cationic exchange capacity [127] which makes it potentially a useful soil fertilizer. Figure 9. Scheme of pore formation in CO 2 , NH 3 , and CO 2 /NH 3 atmospheres. The grey color indicates the formation of a "glue"-like layer made by N-containing groups. The scheme has been elaborated from References [125,126].
The amount of oxygen-containing surface functional groups with the aim to produce biochar having a high affinity for metal ions and, therefore, being possibly applied for wastewater treatments, has been obtained by means of application of air steam under mild temperature conditions (that is temperatures~300 • C) [127]. The mild temperatures are needed to prevent biomass burn-off while oxygen-functionalization occurs ( Figure 10). The advantage of this oxygen-rich carbonaceous material is related also to its high cationic exchange capacity [127] which makes it potentially a useful soil fertilizer. ment of plastic waste disposal. Plastic pollution is one of the main environmental problems humans are currently facing [134]. Although the biochar yield is lower than in the absence of co-pyrolyzing materials, the solid carbonaceous products resulting from copyrolysis appear more efficient in adsorbing organic and inorganic pollutants than the biochar from non-co-pyrolyzed biomasses [130][131][132][133]135]. Moreover, Brebu et al. [136] also found that the co-pyrolyzed biochar reveals higher calorific values compared to pyrolysis of biomasses alone.

Post-Pyrolysis Chemical and Physical Biochar Functionalization
The properties of biochar can be modulated after pyrolysis, thus providing new materials to be used in very different and often not even connected fields. As an example, He et al. [137] and Liu et al. [138] report a persulfate post pyrolysis treatment of biochars produced at different temperatures. Biochars activate either formation of radical sulfate (• SO 4 − ) or active oxygen (• OH − ) which are the main agents responsible for the degradation of the organic pollutants in biochar treated soils and water.
An innovative, costless, and highly efficient way to produce a biochar with surface areas larger than 120%, compared with the typical surface areas in carbonaceous materials from slow pyrolysis, is the hydrodynamic cavitation [139]. Cavitation is a physical phenomenon occurring when a liquid surrounding a solid material is accelerated. Flow acceleration decreases liquid pressure on the surface of the solid system, thereby provoking the formation of bubbles. Once the bubbles collapse, high-pressure waves are formed, and new pores are generated on the surface of the biochar (Figure 11), leading to an improvement of its surface area. The advantage of the hydrodynamic cavitation in designing new

Effect of Co-Pyrolysis
The term co-pyrolysis refers to a process where two or more different feedstock are used to produce materials with a wide range of applications. As an example, co-pyrolysis is applied to obtain sustainable bio-fuels, when biomasses are mixed with coal [128,129] or some types of plastics [130][131][132][133]. The presence of the co-pyrolysis materials allows yield efficiency in the production of bio-oils, thereby leading to the conclusion that co-pyrolysis may satisfy two different types of needs. On one hand, it can provide liquid materials that can be applied as biofuels, thus reducing the use of fossil fuels, and contributing to the mitigation of the global climatic changes. On the other hand, it allows a better management of plastic waste disposal. Plastic pollution is one of the main environmental problems humans are currently facing [134]. Although the biochar yield is lower than in the absence of co-pyrolyzing materials, the solid carbonaceous products resulting from co-pyrolysis appear more efficient in adsorbing organic and inorganic pollutants than the biochar from non-co-pyrolyzed biomasses [130][131][132][133]135]. Moreover, Brebu et al. [136] also found that the co-pyrolyzed biochar reveals higher calorific values compared to pyrolysis of biomasses alone.

Post-Pyrolysis Chemical and Physical Biochar Functionalization
The properties of biochar can be modulated after pyrolysis, thus providing new materials to be used in very different and often not even connected fields. As an example, He et al. [137] and Liu et al. [138] report a persulfate post pyrolysis treatment of biochars produced at different temperatures. Biochars activate either formation of radical sulfate (·SO − 4 ) or active oxygen (·OH − ) which are the main agents responsible for the degradation of the organic pollutants in biochar treated soils and water.
An innovative, costless, and highly efficient way to produce a biochar with surface areas larger than 120%, compared with the typical surface areas in carbonaceous materials from slow pyrolysis, is the hydrodynamic cavitation [139]. Cavitation is a physical phenomenon occurring when a liquid surrounding a solid material is accelerated. Flow acceleration decreases liquid pressure on the surface of the solid system, thereby provoking the formation of bubbles. Once the bubbles collapse, high-pressure waves are formed, and new pores are generated on the surface of the biochar (Figure 11), leading to an improvement of its surface area. The advantage of the hydrodynamic cavitation in designing new types of biochars is its possible integration with other consolidated methods, such as hydrothermal carbonization and chemical activation, possibly leading to effective synergism [139].
When metal-containing solutions are soaked in biochars, new composites are obtained [80]. The presence of the metals allows enhancement of biochar's surface adsorption features. As an example, hydrophilic biochars have been prepared with zero-valent iron nanoparticles in order to be applied in environmental remediation to remove organic [140][141][142] and inorganic [143] contaminants. Finally, ball milling has been shown to increase the external surface areas of low temperature biochars, while for higher temperature biochars with relatively low surface area, ball milling appeared to increase both external and internal surface areas [144]. Regardless of the temperature-driven biochar production, ball-milled biochars showed high affinity for metal ions via formation of metalπ interactions with the graphitic biochar structure. Figure 11. Scheme of the hydrodynamic cavitation method with a pump directing the water flow towards the biochar.

Innovative Functionalization Strategies
As outlined above, biochar can be conceivably considered a new generation material that can have many different uses and applications. In the following subsections, we discuss the most recent developments in biochar functionalization, and the innovative strategies which are able to make biochar even more versatile than expected by the studies we analyzed so far.

Magnetic Biochars
As reported above, many biochars have been tested for their ability in environmental remediation. However, when applied to soils and water, these materials are difficult to remove. Therefore, new strategies have been developed to functionalize biochars with magnetic nanoparticles such as Fe2O3, FeOOH, and Fe3O4 [145]. The resulting carbonaceous materials can then be removed through the application of a magnetic field. Two different pathways can be used to make biochars magnetic. In particular, either pyrolysis or hydrothermal carbonization can be applied on the biomass feedstock treated with ironcontaining solutions in alkaline conditions [145]. Alternatively, the magnetic nanoparticles can be synthesized in the presence of the biochar, thereby being deposited directly on its surface [146]. In all cases the reactions occurring in the system follow the co-precipitation scheme reported in Equations (5)-(9) [147][148][149][150]: Figure 11. Scheme of the hydrodynamic cavitation method with a pump directing the water flow towards the biochar.
When metal-containing solutions are soaked in biochars, new composites are obtained [80]. The presence of the metals allows enhancement of biochar's surface adsorption features. As an example, hydrophilic biochars have been prepared with zero-valent iron nanoparticles in order to be applied in environmental remediation to remove organic [140][141][142] and inorganic [143] contaminants. Finally, ball milling has been shown to increase the external surface areas of low temperature biochars, while for higher temperature biochars with relatively low surface area, ball milling appeared to increase both external and internal surface areas [144]. Regardless of the temperature-driven biochar production, ball-milled biochars showed high affinity for metal ions via formation of metal-π interactions with the graphitic biochar structure.

Innovative Functionalization Strategies
As outlined above, biochar can be conceivably considered a new generation material that can have many different uses and applications. In the following subsections, we discuss the most recent developments in biochar functionalization, and the innovative strategies which are able to make biochar even more versatile than expected by the studies we analyzed so far.

Magnetic Biochars
As reported above, many biochars have been tested for their ability in environmental remediation. However, when applied to soils and water, these materials are difficult to remove. Therefore, new strategies have been developed to functionalize biochars with magnetic nanoparticles such as Fe 2 O 3 , FeOOH, and Fe 3 O 4 [145]. The resulting carbonaceous materials can then be removed through the application of a magnetic field. Two different pathways can be used to make biochars magnetic. In particular, either pyrolysis or hydrothermal carbonization can be applied on the biomass feedstock treated with iron-containing solutions in alkaline conditions [145]. Alternatively, the magnetic nanoparticles can be synthesized in the presence of the biochar, thereby being deposited directly on its surface [146]. In all cases the reactions occurring in the system follow the co-precipitation scheme reported in Equations (5)-(9) [147][148][149][150]: The conditions used to produce magnetic biochars can lead not only to materials easily removable from soils and water, but also with improved physicochemical properties (that is surface area and porosity) that enable better sorption capacity for organic and inorganic contaminants as compared to non-functionalized biochars [141,145,146].

The Plasticized Biochars
Among the different attempts to find novel uses for biochar or to improve its chemicalphysical properties, plasticization appears to be the new frontier. Based on the synthetic procedures to obtain nanocomposites made by the combination of epoxy resin and multiwalled carbon nanotubes [151], Giorcelli et al. [152] mixed biochar with a low viscosity epoxy resin and a hardener in order to obtain a composite that showed elasticity increment for biochar amounts <2% (w w −1 ). Conversely, as the amount of biochar increased over 2%, the composite revealed higher ductility. This may suggest that biochar-based plastics can be applied to the production of a wide number of products according to the particular property needed (elasticity or ductility). Composites with enhanced dynamic viscoelasticity, creep resistance, and stress relaxation were also obtained by melt mixing, then extruding a rice husk biochar added with high-density polyethylene [153]. When the extrusion is performed on the mixture made by biochar and polyethylene added with wood flour and other additives (such as Mg(OH) 2 or Al(OH) 3 ), the resulting plastic also shows interesting flame retardant characteristics [154].

The Co-Composted Biochar
Multiple nutrient deficiencies due to the fact of soil fertility depletion in many areas of the planet are emerging as the major constraint to the sustainability of agriculture on a global scale. Therefore, biochar has been considered a useful amendment to improving soil quality. Biochar can affect soil structure, thereby influencing water retention and nutrient availability [16], while it can be a source of several plant nutrients once it is functionalized as in the case, for example, of Kon-Tiki kiln quenching by cow urine [72]. With the aim to produce new generation and more efficient fertilizers, biochar is also used as an additive to produce compost. The latter is an organic material obtained via a procedure referred to as composting which, in turn, consists in the microbial breakdown of organic material into simpler components used to fertilize soils [155]. When composting is done by mixing organic wastes with biochar, a co-composted material with very high capacity to capture and release nitrate is obtained [17]. Moreover, enhancement of cation exchange capacity is observed [156], while a reduction of potentially harmful chemicals is achieved during composting [157]. The co-composted biochar allows the enhancement of crop production [17,156,158,159].

The Physical Chemistry of Biochar Functioning
As evidenced in the paragraphs above, biochar is a heterogeneous carbonaceous material which can have multiple uses. A very explicative review concerning biochar multiple applications is given in Schmidt and Wilson [49]. However, the molecular mechanisms behind the different biochar uses are not well clarified yet. In this paragraph a summary of the molecular mechanisms of biochar functioning is given.

The Thermodynamics of Biochar Adsorption/Desorption: A Novel Elaboration of the Freundlich Isotherm
Let us indicate as A, a generic compound solubilized in a liquid solvent. When a porous system is present, the following equilibrium can be written: In the chemical Equation (10), A l is the equilibrium liquid phase generic compound, while A s is the same material adsorbed on the porous surface when the equilibrium is Here, q s , expressed in mol kg −1 , represents the amount at equilibrium of the sorbed compound (in moles) per unit of biochar mass (in kg), C w is the equilibrium molar concentration of A l , K F , and N are the Freundlich constant and the linearity parameter, respectively.
Pignatello and co-workers [160][161][162] reported that Equation (11) poorly fits the adsorption data, especially when aromatic organic pollutants are accounted for. This is because biochar surface chemistry and physics changes according to all the conditions previously described. In particular, the adsorption process is affected by: -Cavity effects (cav): these refer to the structural organization of solvent molecules (e.g., water) at the solid-liquid interface, thereby accounting also for the transport of the solvated solute towards the point of the surface where it will be adsorbed [163,164]; -Dispersion forces (disp): These are better known as London dispersion forces. They are involved in the adsorption of a solute via induced dipole interactions; -Dipole-dipole interactions (dip) due to the presence of permanent dipoles. They account for the solute-solvent, solute-solute, solvent-substrate, and solute-substrate interactions; -H-bonds (H-b): As for dip, these account for solvent-solute, solute-solute, substratesolvent, and substrate-solute interactions; -π−π interactions (π−π): As for dip and H-b, these are also involved in solute-solute, solute-solvent, substrate-solvent, and substrate-solute interactions.
For this reason, they re-elaborated the Freundlich isotherm by accounting for all those effects and calculated the Gibbs free energy involved in the sorption process in Equation (10) as: Here, the subscript s stands for "substrate" (i.e., the porous system such as biochar), while w stands for "water". Since the latter has been recognized as the most relevant environmental solvent, from now on all the equations will refer to the adsorption processes from water systems.
The Gibbs free energy in (12) refers to the process of the removal of the solute A from water (let us indicate the solute-water interaction as [A·w]) and to its inclusion on the substrate surface (let us indicate the substrate-solute interaction with [A·s]) according to Equations (13) and (14). The latter two equations summed together give Equation (15), which is formally the same as Equation (10): [A·w] [A·s] (15) Due to the non-ideality of the conditions, the excess free energy (G ex ) must be accounted for [155]. Therefore, Equation (12) can be re-arranged as in (16): The first term in brackets on the right side of Equation (16) represents the hydrophobic effect involved in the removal of the solute from water and its transfer to the substrate surface. It can be indicated as ∆G  attractive forces, which are ultimately electrostatic in nature. It can be indicated as G elect s,A . Therefore, Equation (16) can be re-written as: Let us now indicate with s 0 a generic solvent to put in contact with the aqueous solution containing A. The Gibbs free energy for the partition equilibrium can be written as in (18): We can assume a linear correlation between ∆G where a and b are two solute concentration dependent empirical parameters. By combining Equations (17)- (19), Equation (20) is obtained: Keeping into account the direct correlation between the Gibbs free energy and the equilibrium constant, Equation (20) can be re-arranged as in (21): where K s−w,A is the equilibrium constant for the adsorption of the solute A on a substrate such as biochar; K s 0 −w,A is the partition constant of the solute A between water and an organic solvent (e.g., it can be the octanol-water constant, K ow ); E = G elect s,A −aG elect s 0 ,A RT is the electrostatic contribution to the adsorption on the substrate; b 1 = b RT . Assuming that K s−w,A = q s C w , and re-arranging Equation (21), it is possible to write: Equation (22) simplifies to (23) when the adsorption of the generic A compound is affected only by hydrophobic interactions with the substrate: The Freundlich constant modified according to this model can be written as in (24): The larger the K * value, the stronger the interaction between the generic compound A and the biochar. The modified Freundlich model reported above allows us to understand the different contributions (i.e., hydrophobic, and electrostatic) involved in the interactions between a pollutant and a biochar. For this reason, it can be very helpful in addressing biochar production according to the chemical nature of the pollutant to be removed. However, for the sake of completeness, it must be noticed that this model was applied only to hydrophobic pollutants whose electrostatic contribution to the interaction with biochar was negligible [160][161][162]. For this reason, more studies are needed to validate the strength of this model.

The Kinetics of Biochar Adsorption/Desorption
The reaction rate for the equilibrium described in Equation (10) is defined as the amount of adsorbate disappearing from the solution in the time unit as it is adsorbed on biochar [165]. According to Tong et al. [166], Equation (25) must be accounted for the time dependence of biochar adsorption: Here, Q is the amount (in moles) of adsorbate per mass unit (in kg) of biochar; Q e is the amount of adsorbate in solution when the sorption equilibrium is achieved (it can be expressed in moles per kilograms of solvent); x is the reaction order (it can have any value ≥ 0); k x is referred to as kinetic constant. The latter is used as the experimental parameter to establish the affinity between adsorbate and adsorbent. The larger the k x value, the higher the adsorbate-adsorbent affinity.
The order of reaction is experimentally established upon integration of Equation (25) and determines the dependence of the reaction rate on the concentration of the reactants. Assuming x = 1, 2, 3 after integration and rearrangement, Equation (25) can be re-written as in (26)-(28), respectively: Noticeably, for any x = 1 (i.e., the order of reaction can assume also non-integer values), and the general solution of Equation (25) can be written as: In all the previous equations, Q t is the amount of adsorbate per mass unit of biochar at time t, while k 1 , k 2 , and k 3 are the first-, second-, and third-order kinetic constants, respectively. Due to the complexity of the biochar adsorption phenomena (see below), these kinetics are also referred to as kinetics of pseudo-first, pseudo-second, and pseudothird order, respectively [166][167][168][169][170][171][172]. Figure 12 reports the shape of Equations (26)-(28) which must be experimentally accounted for to establish if the adsorption follows one of the mentioned kinetic laws. Figure 12A shows how the fitting of the experimental data points should appear if the pseudo-first order kinetics applies. Conversely, Figure 12B,C report the linear correlation to be applied when the pseudo-second and pseudo-third order kinetics are valid.
Pseudo second-order kinetics appeared to best describe the adsorption uptake rate of a dye on biochar surface from rice husk [173], of Pb(II) and Cd(II) on the surface of a magnetic biochar obtained by functionalizing costless pine bark wastes with CoFe 2 O 4 [174], and of Cu(II) and tetracycline on a Fe/Zn-doped sawdust biochar [175]. Interestingly, a study from Reguyal et al. [176] showed that the kinetics of biochar absorption is also affected by adsorbate concentration. It was reported that the pseudo-second order kinetic model best described the experimental data at low sulfamethoxazole concentrations (between 1 and 5.1 mg L −1 ), while the pseudo-first order best applied to the kinetic data when sulfamethoxazole concentration was as high as 20.5 mg L −1 [176]. However, it must be noticed that in recent kinetic studies, the terms pseudo first-and pseudo second-orders have been replaced by the term "partition coefficient" which better accounts for the biochar behavior in removing pollutants from environmental compartments [177][178][179][180]. these kinetics are also referred to as kinetics of pseudo-first, pseudo-second, and pseudo-third order, respectively [166][167][168][169][170][171][172]. Figure 12 reports the shape of Equations (26)-(28) which must be experimentally accounted for to establish if the adsorption follows one of the mentioned kinetic laws. Figure  12A shows how the fitting of the experimental data points should appear if the pseudofirst order kinetics applies. Conversely, Figure 12B,C report the linear correlation to be applied when the pseudo-second and pseudo-third order kinetics are valid.  The third-order kinetic model is rarely applied in biochar chemistry. However, Zahedifar and Moosavi [181] reported that it was unsuitable to explain the Zn desorption mechanisms from biochar-amended calcareous soils, while Tian et al. [182] showed that the third-order kinetics can be efficaciously used to describe the mechanisms of the CO 2 gasification of Miscanthus-derived-biochar at different processing conditions.

The Meaning of the Reaction Order and the Langmuir Isotherm from Kinetic Considerations
The reaction order is often related to the molecularity of a reaction. The term "molecularity" refers to the number of reactant molecules binding together to form, within the ratelimiting step of the reaction, an "activated complex" that affords the reaction products [165]. Accordingly, a first-order reaction is a reaction for which only one molecule among the different reactants is involved in the activated complex formation. However, when two molecules are needed to form the collision complex, the reaction can be referred to as second order. According to Laidler and Glasstone [165], reactions occurring on the surface of a solid-phase system, such as a catalyst, can be also considered as third-order reactions. In fact, the collision complex is made by all the reactants interacting with the surface of the catalyst. It must be recognized that the relationship between the order of a reaction and the molecularity is only a simplification. However, this can help in developing a simplistic adsorption theory such as the one elaborated by Langmuir at the beginning of the 20th century [183][184][185].
Let us indicate with the letter B the biochar, with the letter A the system that can be adsorbed on biochar, and with B 1 the A-B complex containing a molar amount of adsorbate which interacts with the biochar surface. We can write the equilibrium reported in (30): where the left-to-right reaction is the adsorption of A on B, thereby providing B 1 , while the right-to-left reaction is the desorption of A from the B surface. Let us also assume: Based on these constraints, it is possible to consider the relationship (31) as descriptive for the steady-state condition:  (29) given by k e = k d /k i and the fraction of biochar sites covered by the adsorbate given by ϑ A = [B 1 ]/[B 0 ], it is straightforward to obtain Equation (32) which is the simplest form for the Langmuir adsorption isotherm. Figure 13A reports the simulations of the Langmuir Equation (32) by using different k e values. When k e is raised up to 1, the trend changes from the quasi-linear behavior observed for low k e values (i.e., k e = 0.025) to the L-shaped one. Equation (32) is unreliable in fitting S-shaped experimental data. This is certainly due to the limits of the approach based on the ideal conditions (I) to (IV) indicated above. In fact, the ideal (I) to (IV) conditions are valid only for monodentate adsorbents in dilute solutions, while the biochar surface must be completely flattened. The latter condition is never a real situation.  Figure 13A reports the simulations of the Langmuir Equation (32) by using different k e values. When k e is raised up to 1, the trend changes from the quasi-linear behavior observed for low k e values (i.e., k e = 0.025) to the L-shaped one. Equation (32) is unreliable in fitting S-shaped experimental data. This is certainly due to the limits of the approach based on the ideal conditions (I) to (IV) indicated above. In fact, the ideal (I) to (IV) conditions are valid only for monodentate adsorbents in dilute solutions, while the biochar surface must be completely flattened. The latter condition is never a real situation. A modified Langmuir isotherm to account for non-ideal conditions is given in Equation (33) [186]: where X is an empirical parameter related to the effects of the adsorbate concentration. Equation (33) appears to be a good alternative to the model depicted in Equation (31) when S-shaped trends are acquired ( Figure 13B). A slightly modified version of Equation (33) is referred to as the Sips equation [187,188], which can be written in the form (34): Equation (34) has the advantage that the K e values are always expressed as L mol −1 , irrespective of the value for X. Moreover, it reduces to the Freundlich equation for 1 ≫ (K e [A]) X . It is worth noting that Equation (34) has never been used in the evaluation of biochar adsorption properties. Therefore, it is desirable that in the future its suitability for the analysis of biochar characteristics is studied. A modified Langmuir isotherm to account for non-ideal conditions is given in Equation (33) [186]: where X is an empirical parameter related to the effects of the adsorbate concentration. Equation (33) appears to be a good alternative to the model depicted in Equation (31) when S-shaped trends are acquired ( Figure 13B). A slightly modified version of Equation (33) is referred to as the Sips equation [187,188], which can be written in the form (34): Equation (34) has the advantage that the K e values are always expressed as L mol −1 , irrespective of the value for X. Moreover, it reduces to the Freundlich equation for 1 (K e [A]) X . It is worth noting that Equation (34) has never been used in the evaluation of biochar ad-sorption properties. Therefore, it is desirable that in the future its suitability for the analysis of biochar characteristics is studied.
Notwithstanding the aforementioned limitations, the Langmuir model reported in Equation (31) showed a suitability to explain the competitive adsorption of different antibiotics on bamboo-derived biochar, whereas Freundlich isotherm was more reliable in modelling absorption of single antibiotics on the same biochar [189]. Similar results regarding the reliability of the Langmuir isotherm given in Equation (31) were obtained by Zhou et al. [175] who studied the adsorption mechanisms of Cu(II) on a Fe/Zn-doped-biochar.
As a general remark, special attention must be paid when one considers studies concerning the use of the Langmuir models. In most of the published papers, volumetric concentrations of adsorbate are commonly used without any theoretical background. Conversely, the concentration units must be mol L −1 . This comes from thermodynamic considerations [190]. In fact, Liu [190] showed that incorrect and unreasonable ∆G 0 values can be calculated when non-molar units are applied. As a consequence, misunderstanding of the adsorption/desorption mechanisms can occur [190].

The Dynamics of Water and Nutrients in Biochar Pore System
In the previous paragraphs, the traditional thermodynamic and kinetic approaches have been discussed to explain how experimental data can be handled to understand how strongly an adsorbate is bound to biochar and which possible molecular mechanisms can be involved in the adsorbate-biochar interactions. However, a quite innovative dynamic approach can be used to understand the nature of the adsorbate-biochar interface interactions. This is based on the evaluation of fast field cycling (FFC) NMR relaxometry investigations [163,164].
Fast field cycling NMR relaxometry has been specifically designed for the measurement of the longitudinal relaxation times (T 1 ) of NMR observable spin nuclei [163,164,191,192]. T 1 is a measure of the time needed for the recovery of the longitudinal component of the magnetization along the z-axis [193]. Its value is influenced by: "fluctuating local magnetic or electrical fields generated by (i) nuclear dipoles, (ii) unpaired electrons, (iii) electric charges interacting with nuclear quadrupole moments for > 1/2 spin nuclei, (iv) anisotropy of the chemical shielding tensor, and (v) fluctuating scalar coupling interactions and molecular rotations. It is recognized that molecular motions are the primary factors affecting the aforementioned fluctuations. For this reason, the measurement of longitudinal relaxation time (or longitudinal relaxation rate, R 1 , that is the inverse of T 1 ) can be related to molecular dynamics. In particular, FFC NMR relaxometry allows evaluating motion frequencies ranging from ≈10 5 to ≈10 8 Hz. These are the typical motion frequencies for aqueous systems in natural porous media" [194].
It is widely recognized that the molecular dynamics investigated by the T 1 value measurements of liquid systems, such as water, in biochar pores is affected by the interactions with the porous boundaries [163,164,[191][192][193][194][195][196]. Namely, the smaller the pore size, the more constrained water molecules are. Conversely, when pore sizes increase, water molecules become more mobile. For this reason, according to pore size distribution, three different water types can be recognized: (i) strongly bound water in micropores; (ii) weakly bound water in mesopores; (iii) bulk water in macropores [163].
Following variable temperature FFC NMR relaxometry experiments [22], it was shown that water molecules can interact with pore boundaries by the inner-sphere mechanism, thereby suggesting that water molecules penetrate into biochar pores and adhere to the surface by formation of weak bonds such as non-conventional H-bonds (e.g., the OH-π bonding described in References [197,198]), Van der Waals interactions, and coordination linkages (Figure 14). The latter are Lewis acid-base interactions occurring when the electron-rich oxygen in water approaches the metal ions situated on the biochar surface. ducing fertility of the upper soil horizons. The time spent by water (and hence watersolvated nutrients) either on the biochar surface (surface-time) or in the bulk (bulk-time) can be measured by FFC NMR relaxometry [195]. The relationship between the surfaceand the bulk-times was used to define the biochar wettability [195], which is affected by the chemistry of the biochar surface. The latter, in turn, depends on all the experimental conditions reported above for the preparation. Figure 14. Different possible bindings between water molecules and biochar. Water can interact with biochar's surface by OH-π bonding, Van der Waals interactions, and coordination linkages. The latter occur when the electron-rich oxygen in water lays in the proximity of a metal ion (dark grey outgrowths). The blue spheres represent a solvated cation (e.g., ammonium).
Having clarified the molecular mechanisms involved in the water/nutrient dynamics inside the biochar pore system, it is intuitive to understand why biochar application to soils increases water retention [16,[202][203][204][205], thereby ameliorating physiological plant responses to drought stresses [206], enhancing plant defense mechanisms [207], and increasing soil microbial biodiversity [208,209]. For further information about the advantages and disadvantages of biochar applications, see Das et al. [210].

The Mechanisms of Entrapment and Decomposition of Pollutants in Biochar
In Section 3.4., a post-pyrolysis biochar functionalization with persulfate was described. It was pointed out that persulfate activates biochar surface via formation either of radical sulfate (• SO 4 − ) or hydroxyl radical (• OH − ). When the persulfate-activated biochar traps pollutants, a reaction such as that described in Figure 15 for the degradation of bisphenol A, occurs [138]. Namely, this pollutant (also known as 2,2'-bis-(4-hydroxyphenil)propane) is firstly oxidized to 2-(4-hydroxyphenil)-2'-(3,4-dihydroxyphenil)-propane. Then a homolytic split occurs, generating hydroxyphenyl and 2-(3,4-dihydroxyphenyl)- Figure 14. Different possible bindings between water molecules and biochar. Water can interact with biochar's surface by OH-π bonding, Van der Waals interactions, and coordination linkages. The latter occur when the electron-rich oxygen in water lays in the proximity of a metal ion (dark grey outgrowths). The blue spheres represent a solvated cation (e.g., ammonium).
It is worth noting that the water molecules in biochar pores belong also to the hydration spheres of solutes which may work as plant nutrients ( Figure 14) [199,200]. In other words, some plant nutrients are captured in biochar thanks to water-mediated interactions and can be released into the soil solution when it is used as soil amendment [17][18][19].
Given that the nature of the aforementioned interactions is transient, it is possible to state that the movement of nutrients in the biochar pore system can occur via two different mechanisms [201]. Firstly, water molecules diffuse horizontally on the biochar surface. This allows nutrients to be dragged towards plant roots. Secondly, each water molecule can "hop" from the biochar surface over a longer distance, while it is replaced by another molecule. This allows nutrients to be leached towards deeper soil horizons, thereby reducing fertility of the upper soil horizons. The time spent by water (and hence watersolvated nutrients) either on the biochar surface (surface-time) or in the bulk (bulk-time) can be measured by FFC NMR relaxometry [195]. The relationship between the surfaceand the bulk-times was used to define the biochar wettability [195], which is affected by the chemistry of the biochar surface. The latter, in turn, depends on all the experimental conditions reported above for the preparation.
Having clarified the molecular mechanisms involved in the water/nutrient dynamics inside the biochar pore system, it is intuitive to understand why biochar application to soils increases water retention [16,[202][203][204][205], thereby ameliorating physiological plant responses to drought stresses [206], enhancing plant defense mechanisms [207], and increasing soil microbial biodiversity [208,209]. For further information about the advantages and disadvantages of biochar applications, see Das et al. [210].

The Mechanisms of Entrapment and Decomposition of Pollutants in Biochar
In Section 3.4., a post-pyrolysis biochar functionalization with persulfate was described. It was pointed out that persulfate activates biochar surface via formation either of radical sulfate (·SO − 4 ) or hydroxyl radical (·OH − ). When the persulfate-activated biochar traps pollutants, a reaction such as that described in Figure 15 for the degradation of bisphenol A, occurs [138]. Namely, this pollutant (also known as 2,2 -bis-(4-hydroxyphenil)propane) is firstly oxidized to 2-(4-hydroxyphenil)-2 -(3,4-dihydroxyphenil)-propane. Then a homolytic split occurs, generating hydroxyphenyl and 2-(3,4-dihydroxyphenyl)-propane radicals. Both are subjected to a series of not well-defined oxidations which result in the formation of carbon dioxide and water [138]. able to reduce selenate (SeO 4 − ) to selenite (SeO 3 − ) and then to selenide (Se 2− ) via metallic selenium (Se) by redox reactions that can be schematized as follows: 2Se + C + 2H 2 O → 2Se 2− + CO 2 + 4H + (37) Figure 15. Example of degradation of a pollutant (bisphenol A) on the surface of a persulfate activated biochar. The reaction scheme has been re-elaborated with permission from Reference [138].
In reactions (35) to (37), C represents the biochar which is oxidized to carbon dioxide. However, biochar oxidation can also be limited to a surface functionalization with formation of oxidized groups, thereby making the carbonaceous material more hydrophilic. While selenium-containing pollutants are immobilized by the alteration of their oxidation Figure 15. Example of degradation of a pollutant (bisphenol A) on the surface of a persulfate activated biochar. The reaction scheme has been re-elaborated with permission from Reference [138].
When the biochar is obtained by co-pyrolysis with polyethylene terephthalate (Section 3.3.7), a material very efficient in removing/entrapping organic and inorganic pollutants is obtained [135]. In particular, Oh and Seo [135] reported that this type of biochar is able to reduce selenate (SeO − 4 ) to selenite (SeO − 3 ) and then to selenide (Se 2− ) via metallic selenium (Se) by redox reactions that can be schematized as follows: In reactions (35) to (37), C represents the biochar which is oxidized to carbon dioxide. However, biochar oxidation can also be limited to a surface functionalization with formation of oxidized groups, thereby making the carbonaceous material more hydrophilic. While selenium-containing pollutants are immobilized by the alteration of their oxidation state, a pollutant such as chromate (CrO 2− 4 ) is trapped via a mechanism involving electrostatic interactions [135]. Experimental results [135] suggest that the presence of polyethylene-terephthalate (Section 3.5.2.) as co-pyrolyzing material allows formation of a biochar where the graphitic-like layer may reveal domains with low electron density. Hence, the electron-rich chromate anions can be hooked in the electronic "holes", thus allowing formation of stable complexes which can be easily removed and disposed of in landfills. Conversely, when heavy metals (Me n+ ), such as Pb 2+ , are present in the environment, a C π − Me n+ mechanism must be invoked. In this case, the electron-rich aromatic systems of the graphitic-like biochar moieties (i.e., C π ) can "hook" the electron-poor metal cations [135]. However, Paz-Ferreiro et al. [211] report that the mechanisms for heavy metal entrapment in biochar are also due to the presence of surface oxygenated/nitrogenated functions, which can "hook" the metals via their lone-pair electrons. For this reason, the same authors state that biochar is suitable for soil phytoremediation projects because it allows reduction of heavy metals leachability and bioavailability. As already discussed in Section 3.3.6., biochar affinity for metal ions can be beneficial for water treatment. Surface complexation was found to be the main mechanism in Pb 2+ removal from contaminated water in lab-scale flow-through column tests [212], where biochar potential as an active component in permeable reactive barriers for groundwater treatment was assessed.
Aromatic pollutants, such as 2,4-dichlorophenol (DCP) and triazines, may interact with the biochar via weak C π − C π interactions [137,162], which were also described in Conte et al. [213] to explain the increased retention of polycyclic aromatic hydrocarbons in soils induced by treatment with humic substances. As nitro-groups are bound to the benzene ring, such as in the case of the 2,4-dinitrotoluene, the biochar C π systems can trap the aforementioned pollutant via interactions with the π systems of the nitrogroups [135]. Different mechanisms were accounted for to explain the immobilization of polyfluorinated organic compounds on biochar surfaces [200]. In particular, a cooling agent used in scientific instruments commercially known as Galden ® -IUPAC name is oxidized poly(1,1,2,3,3,3-hexafluoroprop-1-ene)-with formula CF 3 − (OCF(CF 3 )CF 2 ) n − (OCF 2 ) m − OCF 3 and an average molecular weight of 610 Da, can be adsorbed on biochar's surface by (i) charge transfer bond with biochar metal impurities; (ii) H-bonds with biochar surface hydrophilic groups; (iii) Van der Waals interactions with the biochar C-skeleton; (iv) outer-sphere interactions where water molecules bridge the Galden ® with the electronpoor biochar metal impurities. Biochar can also trap anionic pollutants such as fluoride (F − ) in groundwater [214]. In this case, the presence of biochar surface cation impurities is considered responsible for F − electrostatic entrapment. However, the effect of these impurities reduces as pH increases. In fact, Zhou et al. [214] observed that the higher the pH, the lower the amount of fluoride retained on the biochar surface. This can be explained by the progressive deprotonation of the surface acidic functional groups which allow negative charge to increase and electrostatic repulsions. In addition, when magnetic biochars are applied for groundwater remediation, the presence of paramagnetic systems modifies biochar z-potential, thus allowing enhancement of the capacity of magnetic biochar surfaces to attract fluoride ions [214].

Conclusions
This paper aimed for a critical evaluation of the main literature dealing with the physical chemistry of biochar. As stated in the introduction, the number of studies on biochar applications in many fields is increasing tremendously. While concordance about biochar peculiarities exists in all the chemistry sectors where this system is seen as the base for the synthesis of many different materials (e.g., filters, electrodes) [215], debate regarding biochar's usefulness in environmental applications is ongoing [28]. The latter is due to the fact that in many studies, biochar is used prior to any detailed chemical and physical evaluation of its properties and analysis of its environmental impact [216].
Summarizing the purpose of this paper in a very few words, it is a guide to answer the key question on how I intend to use the biochar.
We have reached an awareness about biochar complexity. This paper highlights that a great deal is known about the basis of biochar chemistry and physics, although the answers that have been reported here represent the starting point for new questions.
Certainly, one should be aware that biochars made from different feedstocks can have very different chemical properties, even if the same process is applied to produce them. However, not only feedstock choice but also biomass pre-functionalization, the correct production method, and biochar post-functionalization can be considered key points for biochar uses. Accordingly, papers where any conclusion (either positive or negative) regarding biochar is achieved without any deep chemical-physical investigation are not acceptable anymore. Moreover, the reading of the oldest papers where no physical-chemical analyses are reported should be contextualized and conclusions revisited by reproducing the same data after performing the correct investigations to understand the "why and how" behind those conclusions.
Author Contributions: All the authors equally contributed to this paper. All authors have read and agreed to the published version of the manuscript.
Funding: This research received no external funding.

Informed Consent Statement: Not applicable.
Data Availability Statement: Not applicable.

Conflicts of Interest:
The authors declare no conflict of interest.

Appendix A. The Lab-Muffle-Furnace Method
When only a few grams of biochar are needed either for the purpose of chemicalphysical characterization or in vitro experiments to test biochar effects on seed germination and plant growth; a lab production can be achieved by using the system reported in Figure A1 [77]. Namely, a small amount of an air-dried biomass is weighed in a Pyrex flask and placed into a muffle furnace with a cap not-hermetically closed on it. This can be obtained by placing an aluminum foil straw between the cap and the Pyrex flask opening. Muffle furnace temperature is then slowly raised until the desired value is reached. Temperature increase must be slow to avoid rapid gas release and sample blow-up. Initially, residual air is still present in the system. As the reaction starts, oxygen is consumed, the air flows away from the small aperture and cannot re-enter the flask due to the high operating temperature. Once this occurs, the thermal degradation proceeds under anoxic conditions. The limit of this method is not only the very low amount of biochar that can be obtained, but also the impossibility of controlling the quenching procedure. Moreover, the temperature is manually ramped, unless the lab muffle furnace is provided with an automatic temperature ramp controller.  Figure A1. Lab-muffle-furnace biochar production. A few grams of air-dried biomass are placed in a Pyrex flask. The temperature is slowly raised to the desired value. Initially, the oxygen-containing air is still in the flask. Once the oxygen is consumed and the gas flows out from the container, the pyrolysis starts.

Appendix B. The Lab Pyrolizer
The biochar obtained by lab-furnace method (Appendix A) cannot be used for the production of new materials such as electrodes [67], sorbent for specific pollutants [68], or medicine [49]. In these cases, reproducible chemical-physical properties must be achieved by controlling all the pyrolysis conditions. Therefore, a different production approach must be utilized [67,68,217]. Figure A2 shows a typical lab pyrolizer made from a computer-controlled muffle furnace and a refractory tube where the biomass sample placed in a quartz container is positioned. The refractory tube is connected to an inert gas bottle. The inert gas fulfills two functions. Firstly, it removes the oxygen-containing air from the refractory tube, thereby allowing a pyrolysis with a yield larger than that from the lab muffle furnace methods (Appendix A). Secondly, the inert gas works as a carrier to remove the volatile pyrolysis by-products which are expelled towards the fume cupboard. The computer control allows to program the temperature ramp, the pyrolysis temperature, and the pyrolysis duration. The advantage of the lab pyrolizer reported in Figure A2 is the possibility of a scaling up for industrial purposes [217], while the limit can be the consumption of huge amounts of expensive inert gases. Figure A1. Lab-muffle-furnace biochar production. A few grams of air-dried biomass are placed in a Pyrex flask. The temperature is slowly raised to the desired value. Initially, the oxygen-containing air is still in the flask. Once the oxygen is consumed and the gas flows out from the container, the pyrolysis starts.

Appendix B. The Lab Pyrolizer
The biochar obtained by lab-furnace method (Appendix A) cannot be used for the production of new materials such as electrodes [67], sorbent for specific pollutants [68], or medicine [49]. In these cases, reproducible chemical-physical properties must be achieved by controlling all the pyrolysis conditions. Therefore, a different production approach must be utilized [67,68,217]. Figure A2 shows a typical lab pyrolizer made from a computer-controlled muffle furnace and a refractory tube where the biomass sample placed in a quartz container is positioned. The refractory tube is connected to an inert gas bottle. The inert gas fulfills two functions. Firstly, it removes the oxygen-containing air from the refractory tube, thereby allowing a pyrolysis with a yield larger than that from the lab muffle furnace methods (Appendix A). Secondly, the inert gas works as a carrier to remove the volatile pyrolysis by-products which are expelled towards the fume cupboard. The computer control allows to program the temperature ramp, the pyrolysis temperature, and the pyrolysis duration. The advantage of the lab pyrolizer reported in Figure A2 is the possibility of a scaling up for industrial purposes [217], while the limit can be the consumption of huge amounts of expensive inert gases. Agronomy 2021, 11, x FOR PEER REVIEW 30 of 42 Figure A2. Lab pyrolizer. The muffle furnace is controlled by a computer which allows the programming and control of the temperature ramp to reach the pyrolysis temperature. An inert gas removes the air from the systems, thus allowing biomass thermal degradation with a larger yield than by the lab muffle furnace method. The reported scheme represents the one available in one of the authors' lab (PC).

Appendix C. The Hydrothermal Carbonization
Instead of the pyrolysis conducted as aforementioned, a newer way to produce biochar is the hydrothermal carbonization (HTC) ( Figure A3). It is performed in a reactor where the biomass, fully immersed in water, is heated at high pressure at a temperature between 150 °C and 350 °C [218]. Under these conditions, water causes the hydrolysis and cleavage of lignocellulose as well as the hydrolysis of all the organic systems present in the biomass [218]. An advantage of HTC is the consumption of a lower amount of thermal energy as compared to pyrolysis, while its limit is the impossibility to precisely control the operating pressure. The latter "depends on the steam pressure of water and gas development during feedstock decomposition" [218,219]. Usually, to distinguish between the biochar obtained by pyrolysis and that produced by HTC, this second is referred to as "hydrochar" [218]. Figure A2. Lab pyrolizer. The muffle furnace is controlled by a computer which allows the programming and control of the temperature ramp to reach the pyrolysis temperature. An inert gas removes the air from the systems, thus allowing biomass thermal degradation with a larger yield than by the lab muffle furnace method. The reported scheme represents the one available in one of the authors' lab (PC).

Appendix C. The Hydrothermal Carbonization
Instead of the pyrolysis conducted as aforementioned, a newer way to produce biochar is the hydrothermal carbonization (HTC) ( Figure A3). It is performed in a reactor where the biomass, fully immersed in water, is heated at high pressure at a temperature between 150 • C and 350 • C [218]. Under these conditions, water causes the hydrolysis and cleavage of lignocellulose as well as the hydrolysis of all the organic systems present in the biomass [218]. An advantage of HTC is the consumption of a lower amount of thermal energy as compared to pyrolysis, while its limit is the impossibility to precisely control the operating pressure. The latter "depends on the steam pressure of water and gas development during feedstock decomposition" [218,219]. Usually, to distinguish between the biochar obtained by pyrolysis and that produced by HTC, this second is referred to as "hydrochar" [218]. Agronomy 2021, 11, x FOR PEER REVIEW 31 of 42 Figure A3. Schematic representation of a reactor for the hydrothermal carbonization of biomasses.

Appendix D
As stated in the present study, biochar is obtained by the thermal degradation of biomasses in oxygen starved conditions. One of the most used and economic technologies for biochar achievement is the Kon-Tiki kiln depicted in Figure A4A, while the reactions occurring during biochar production are reported in Figure A4B [30,72].
The Kon Tiki kiln consists of a metallic cone where woody biomass, having the characteristics reported in Table 1, is placed and rested on a metallic grid. The thermal energy needed for the pyrolysis is provided by the flame produced by triggering biomass combustion. Once the burning starts, a series of different thermal events occur ( Figure A4B). As the temperature rises to 100 °C, biomass moisture is volatilized. Simultaneously wood combustion triggers, thereby producing carbon dioxide, ashes, and water vapor as well as an increase of thermal energy. As the temperature rises, the oxygen around the wood disperses and the production of oil vapors, pyrolysis gases (e.g., CO, H2, CH4), and biochar is obtained in a zone where a temperature of around 400 °C is reached. Oil vapors disperse and are degraded to hydrocarbons and tar in the zone of the flame where the temperature rises to around 600 °C. The soot deriving from these processes is decomposed in the zone where the temperature reaches around 1500 °C. Finally, the most distant part of the flame contains all the degradation products at a temperature of around 400 °C.
To prevent an over production of ashes with a biochar low yield, the reactions occurring in the Kon Tiki kiln can be quenched by using different methods. As an example, the quench can be achieved with water solutions (such as tap water or urine) or by smothering with a 5-10 cm thick layer of soil, sand, or manure [30,72]. Figure A3. Schematic representation of a reactor for the hydrothermal carbonization of biomasses.

Appendix D
As stated in the present study, biochar is obtained by the thermal degradation of biomasses in oxygen starved conditions. One of the most used and economic technologies for biochar achievement is the Kon-Tiki kiln depicted in Figure A4A, while the reactions occurring during biochar production are reported in Figure A4B [30,72].
The Kon Tiki kiln consists of a metallic cone where woody biomass, having the characteristics reported in Table 1, is placed and rested on a metallic grid. The thermal energy needed for the pyrolysis is provided by the flame produced by triggering biomass combustion. Once the burning starts, a series of different thermal events occur ( Figure A4B). As the temperature rises to 100 • C, biomass moisture is volatilized. Simultaneously wood combustion triggers, thereby producing carbon dioxide, ashes, and water vapor as well as an increase of thermal energy. As the temperature rises, the oxygen around the wood disperses and the production of oil vapors, pyrolysis gases (e.g., CO, H 2 , CH 4 ), and biochar is obtained in a zone where a temperature of around 400 • C is reached. Oil vapors disperse and are degraded to hydrocarbons and tar in the zone of the flame where the temperature rises to around 600 • C. The soot deriving from these processes is decomposed in the zone where the temperature reaches around 1500 • C. Finally, the most distant part of the flame contains all the degradation products at a temperature of around 400 • C.
To prevent an over production of ashes with a biochar low yield, the reactions occurring in the Kon Tiki kiln can be quenched by using different methods. As an example, the quench can be achieved with water solutions (such as tap water or urine) or by smothering with a 5-10 cm thick layer of soil, sand, or manure [30,72]. Soil, sand, and manure are applied on the upper part of the kiln and act by reducing the presence of the oxygen feeding the fire. This type of heating extinction is very slow and may produce a biochar rich in condensates and pollutants such as PAHs. The final carbonaceous product can certainly be good as fuel charcoal because condensates and PAHs burn well. However, it cannot be applied for agricultural purposes due to the possibility of groundwater contamination [30].
When water or an aqueous solution is used, the quenching can be achieved in two different ways. The liquid can be applied from the bottom. In this case a hot steam is generated when the solution gets in contact with the hot surface of the pyrolyzing material and two effects are obtained: (i) an increase of the biochar surface area, thereby improving its adsorption properties, (ii) the aqueous solution expels and reacts with the condensates from the pores of the biochar, thus preventing their possible contaminating effect [30,72]. If the quenching is done from the top of the kiln, the effect of the hot steam is not as efficient as previously described because the vapor phase cannot soak the whole system. As a consequence, a reduced surface area with a diminished adsorption potential is obtained [30,72]. The advantage of the Kon Tiki kiln is the huge amount of biochar that can be obtained, thereby fulfilling the need for field applications. The limitation is the impossibility of controlling all the pyrolysis conditions. This leads to biochars with chemical-physical properties which may differ case by case. Therefore, a precise analytical characterization is needed prior to any possible biochar field use.

Appendix E
Assuming that the conditions reported in Table 1 are fulfilled, the carbonaceous material obtained as a by-product of industrial thermochemical processes (i.e., gasification) can be also be referred to as "biochar" [99]. Gasification is used to produce a syngas which is in turn applied for energy purposes. The process has been detailed in De Pasquale et al. [99] and references therein. Briefly, the biomass is placed in a reactor where it is partially oxidized by heating at temperatures as high as 1200 °C. The syngas produced by the bio- Soil, sand, and manure are applied on the upper part of the kiln and act by reducing the presence of the oxygen feeding the fire. This type of heating extinction is very slow and may produce a biochar rich in condensates and pollutants such as PAHs. The final carbonaceous product can certainly be good as fuel charcoal because condensates and PAHs burn well. However, it cannot be applied for agricultural purposes due to the possibility of groundwater contamination [30].
When water or an aqueous solution is used, the quenching can be achieved in two different ways. The liquid can be applied from the bottom. In this case a hot steam is generated when the solution gets in contact with the hot surface of the pyrolyzing material and two effects are obtained: (i) an increase of the biochar surface area, thereby improving its adsorption properties, (ii) the aqueous solution expels and reacts with the condensates from the pores of the biochar, thus preventing their possible contaminating effect [30,72]. If the quenching is done from the top of the kiln, the effect of the hot steam is not as efficient as previously described because the vapor phase cannot soak the whole system. As a consequence, a reduced surface area with a diminished adsorption potential is obtained [30,72]. The advantage of the Kon Tiki kiln is the huge amount of biochar that can be obtained, thereby fulfilling the need for field applications. The limitation is the impossibility of controlling all the pyrolysis conditions. This leads to biochars with chemical-physical properties which may differ case by case. Therefore, a precise analytical characterization is needed prior to any possible biochar field use.

Appendix E
Assuming that the conditions reported in Table 1 are fulfilled, the carbonaceous material obtained as a by-product of industrial thermochemical processes (i.e., gasification) can be also be referred to as "biochar" [99]. Gasification is used to produce a syngas which is in turn applied for energy purposes. The process has been detailed in De Pasquale et al. [99] and references therein. Briefly, the biomass is placed in a reactor where it is partially oxidized by heating at temperatures as high as 1200 • C. The syngas produced by the biomass thermal degradation consists of a mixture of carbon monoxide, carbon dioxide, hydrogen, methane, and nitrogen. It can be used to power diesel-cycle endothermic engines to produce both electricity and heat or as a ready-to-use fuel. The total amount of thermal energy from these processes is ∆H = −203 MJ kmol −1 . However, biomasses contain not only carbon, hydrogen, and water but also nitrogen (which is converted to N x O y , NH 3 , and N 2 ), sulphur (converted to H 2 S), and chlorine (converted to HCl). The amount of nitrogenated, sulphurated, and chlorinated gases in syngas is negligible. Finally, the many inorganic components usually present in biomasses are collected as ashes together with the biochar ( Figure A5). The total amount of thermal energy from these processes is ΔH = −203 MJ kmol −1 . However, biomasses contain not only carbon, hydrogen, and water but also nitrogen (which is converted to NxOy, NH3, and N2), sulphur (converted to H2S), and chlorine (converted to HCl). The amount of nitrogenated, sulphurated, and chlorinated gases in syngas is negligible. Finally, the many inorganic components usually present in biomasses are collected as ashes together with the biochar ( Figure A5). Figure A5. The left side of the photo shows conifer wood residues. The right side shows the biochar obtained by the conifer biomass after industrial thermochemical carbonization (i.e., gasification). The conifer biochar showed here was analyzed in de Pasquale et al. [99]. The amount of ash resulted 80 ± 7 g kg −1 . Figure A5. The left side of the photo shows conifer wood residues. The right side shows the biochar obtained by the conifer biomass after industrial thermochemical carbonization (i.e., gasification). The conifer biochar showed here was analyzed in de Pasquale et al. [99]. The amount of ash resulted 80 ± 7 g kg −1 .