Catalyst System for Hydrogenation Catalysis Based on Multiarm Hyperbranched Polymer Templated Metal (Au, Pt, Pd, Cu) Nanoparticles

1
School of Chemistry and Chemical Engineering, Anyang Normal University, Anyang 455000, China
2
Henan Province Key Laboratory of New Optoelectronic Functional Materials, Anyang Normal University, Anyang 455000, China
*
Authors to whom correspondence should be addressed.
Polymers 2017, 9(9), 459; https://doi.org/10.3390/polym9090459
Submission received: 24 August 2017 / Revised: 14 September 2017 / Accepted: 15 September 2017 / Published: 19 September 2017

Abstract

:
With a hyperbranched poly(amidoamine) core and many water-soluble poly(ethylene glycol) monomethyl ether arms connected by pH-sensitive acylhydrazone bonds, multiarm hyperbranched polymer was used as nanoreactor and reductant to prepare metal nanoparticles endowed with intelligence and biocompatibility. The multiarm hyperbranched polymer encapsulated nanoparticles (NPs) showed excellent catalytic activity for hydrogenation, thus an excellent catalyst system for hydrogenation was established. The rate constants could reach as high as 3.48 L·s−1·m−2, which can be attributed to the lack of surface passivation afforded by the multiarm hyperbranched polymer.

Graphical Abstract

1. Introduction

Hyperbranched polymers are a kind of highly branched polymers with three-dimensional topological structures. They have many inner cavities and a large amount of terminal functional groups. Due to their unique molecular structures and facile synthesis route, hyperbranched polymers have received much attention and remarkable development has been made on their synthesis, characterization, and modification in the past decades [1,2,3,4]. This leads to an increasing interest on their application, such as molecular self-assembly [5,6,7,8,9,10,11,12], control-release of dyes [13,14,15,16,17,18], drug delivery [19,20,21], protein delivery [22,23], gene transfection [24,25,26,27,28], molecular imaging [29], nanoparticle (NP) encapsulation [30,31,32,33], and so on.
NP synthesis is one of the most important applications of hyperbranched polymers in recent years. With a three-dimensional globular architecture, numerous cavities, and plenty of peripheral functional groups [34,35,36], hyperbranched polymers are regarded as ideal stabilizers and nanoreactors/templates to prepare size-controlled semiconductors [37,38,39,40,41], metal nanoparticles (NPs) [42,43,44,45,46,47], metal nanodots [48,49], and metal oxide nanocrystals [25,26,50,51], etc. Until now, various hyperbranched polymers, not only the conventional covalent hyperbranched polymers but also supramolecular multiarm hyperbranched polymers [41,52] have been reported to prepare nanocrystals. By preparing nanocrystals within hyperbranched polymers, the environmental sensitivity and biocompatibility of polymers [53,54], and the optical, magnetic, and electrical properties of nanocrystals can be combined, endowing nanocrystals with intelligence and biocompatibility.
In this work, multiarm hyperbranched polymers were used as reductants, stabilizers, and nanoreactors to prepare metal (Au, Pt, Pd, Cu) NPs, resulting in an excellent catalyst system for hydrogenation catalysis. The multiarm hyperbranched polymer (HPAMAM-g-MPEG) has a hyperbranched poly(amido amine) (HPAMAM) core and many water-soluble poly(ethylene glycol) monomethyl ether (MPEG) arms connected by pH-sensitive acylhydrazone bonds. The multiarm hyperbranched polymers with acylhydrazone bonds have a better reduction ability and can reduce metal ions in one minute when compared with molecules with amine groups. More importantly, it is pH-responsive and consequently endows NPs prepared within it with pH-responsive properties. Here, HAuCl4 with different pH values was used to prepare Au NPs in order to investigate the influence of pH-sensitive acylhydrazone bonds on NP synthesis. The catalysis activities of metal (Au, Pt, Pd, Cu) NPs were characterized by p-nitrophenol (PNP) hydrogenation catalysis. Among them, Au prepared under under pH 4.0 and pH 6.7, Pt NPs, and Pd NPs show excellent catalysis activities for hydrogenation. Thus, an excellent catalyst system for hydrogenation catalysis based on multiarm hyperbranched polymer templated metal NPs was established.

2. Experimental

2.1. Materials

HAuCl4·3H2O (99.99%), H2PtCl6·6H2O (Pt 37.5%), K2PdCl4 (99.99%), CuSO4 (99.00%), and p-nitrophenol (PNP) were bought from Alfa Aesar (Lancashire, UK). HPAMAM-g-MPEG was from our lab. The ultrapure water with 18.2 MΩ·cm was used in all experiments.

2.2. Synthesis of Dynamic Hyperbranched Polymers with pH-Sensitive Acylhydrazone Bonds

2.2.1. Synthesis of Hyperbranched Poly(Amidoamine) (HPAMAM)

Hyperbranched poly(amidoamine) (HPAMAM) can be synthesized from commercially available AB and Cn types of monomers by one-pot polymerization via the coupled-monomer method [32]. 9.03 g (0.15 mol) ethylenediamine (EDA) in 28 mL methanol were put into a one-neck flask in an ice-salt bath, and then 25.83 g (0.3 mol) methyl acrylate (MA) was dropwise added to the flask under stirring. The mixture was stirred at room temperature for one week and then the flask was fixed onto a rotary evaporator to remove the methanol under the vacuum. After reacting for 1 h at 60 °C, 2 h at 100 °C, 2 h at 120 °C, and 2 h at 140 °C on the rotary evaporator in vacuum, a slightly yellow dope was obtained [32].
1H NMR (400 MHz, DMSO-d6, 298 K) δ: 2.10–2.30 (NH2), 2.30–2.90 (COCH2, NHCH2, NH2CH2), 2.91–3.30 (NCH2), 3.31–3.50 (NCH2), 3.51–3.62 (OCH3), 7.52, 7.97 (CONH).

2.2.2. Synthesis of Acylhydrazine Terminated HPAMAM (HPAMAM-NHNH2)

0.5 g HPAMAM were dissolved in 40 mL anhydrous ethanol and then 20 mL 85% hydrazine hydrate was added. The mixture was stirred and refluxed at 125 °C for 3 h. After rotatory evaporating at 70 °C for 1 h and further drying in vacuum at 70 °C for 48 h, HPAMAM with acylhydrazine terminals (HPAMAM-NHNH2) was gained.
1H NMR (400 MHz, DMSO-d6, 298 K) δ: 1.83–2.30 (NH2), 2.30–2.80 (COCH2, NHCH2, NH2CH2), 2.86–3.24 (NCH2), 3.27–3.50 (NCH2), 3.62–4.40 (CONHNH2), 7.56, 8.13 (CONHCH2), 9.09 (CONHNH2).

2.2.3. Synthesis of Multiarm Hyperbranched Polymers with pH-sensitive Acylhydrazone Bonds (HPAMAM-g-MPEG)

0.30 g HPAMAM-NHNH2 and 1.83 g para-substituted poly(ethylene glycol) monomethyl ether benzaldehyde (MPEG-C6H4CHO) were dissolved in anhydrous ethanol (50 mL). The ethanol solution was refluxed under N2 atmosphere for 24 h. After rotatory evaporating, the product was redispersed in dichloromethane (10 mL) and then drops were added to ice ether (200 mL). The resulting precipitate was dried under vacuum to obtain HPAMAM-g-MPEG.
1H NMR (400 MHz, DMSO-d6, 298 K) δ: 2.08–2.27 (NH2), 2.30–2.90 (COCH2, NHCH2, NH2CH2), 2.99–3.16 (NCH2), 3.23 (OCH3), 3.26–3.40 (NCH2), 3.44–4.22 (OCH2), 7.56, 8.13 (CONHCH2), 6.86–7.37 (Ar), 7.56–8.08 (CONHCH2), 8.63 (ArCH=N), 11.10–11.40 (CONHN=C) [38].

2.3. NP Synthesis within Multiarm Hyperbranched Polymer HPAMAM-g-MPEG

Typically, 7.5 mg HPAMAM-g-MPEG was dissolved in 3 mL ultrapure water and then 0.5 mL HAuCl4 (1.5 μmol) aqueous solution (pH value was adjusted to 2.9, 4.0 and 6.7 by 1 M NaOH for different samples, respectively) was added. After stirring for several minutes, claret-red Au NPs were obtained and abbreviated as Au/HPAMAM-g-MPEG. A similar procedure was done for Pt, Pd, and Cu NP synthesis except that the stirring time was all set as 48 h and HAuCl4 was replaced by equal amount of H2PtCl6, K2PdCl4 and CuSO4, respectively. For H2PtCl6 aqueous solution, the pH value was also adjusted to 6.7 by 1 M NaOH. UV-Vis spectra of Au, Cu, Pd, Pt nanoparticles synthesized within HPAMAM-g-MPEG can be seen in Figure S1.

2.4. PNP Hydrogenation Catalysis

The UV–Vis spectrophotometer was blanked with 2 mL of ultrapure water in a quartz cuvette and then 0.75 mL of 0.2 M NaBH4 and 0.25 mL of 600 μM PNP (pH = 12) aqueous solution were then added to the reaction cuvette. 150 μL of Au/HPAMAM-g-MPEG solution (pH = 11.0) was rapidly added into the reaction cuvette. Data were collected at a frequency of one per 1 second. The absorbance at 400 and 600 nm (for background correction) were used to calculate the kinetic rate constant by fitting to first-order integrated rate equations.

2.5. Measurements

Transmission electron microscopy (TEM) and elemental characterization were carried out on a JEOL 2010 microscope (JEOL, Tokyo, Japan) with an energy-dispersive X-ray spectrometer (JEOL, Tokyo, Japan) (EDS) at an accelerating voltage of 200 kV. UV–Vis spectra were recorded on a Varian Carry-50 UV–Vis spectrometer (JEOL, Tokyo, Japan).

3. Results and Discussion

Scheme 1a shows the chemical structure of HPAMAM-g-MPEG multiarm hyperbranched polymer used. HPAMAM-g-MPEG was constructed by combining acylhydrazine-modified hyperbranched poly(amidoamine) (HPAMAM-NHNH2) and para-substituted poly(ethylene glycol) monomethyl ether benzaldehyde (MPEG-C6H4CHO) by acylhydrazone bonds. The 1H NMR spectra of HPAMAM, HPAMAM-NHNH2 and HPAMAM-g-MPEG are shown in Figure 1. The signal at 3.58 ppm in Figure 1A corresponds to the methoxy terminals of HPAMAM, while it disappears in Figure 1B. This is because the methoxy terminals have been transformed into acylhydrazine after hydrazinolysis. After reacting with benzaldehyde-terminated MPEG, new proton signals at 8.63 and 11.10–11.40 ppm indicated the formation of acylhydrazone bonds, as shown in Figure 1C. HPAMAM-g-MPEG, a multiarm hyperbranched polymer with pH-sensitive acylhydrazone bonds, has great potential in synthesizing pH-responsive NPs, nanodots, etc. Here, HPAMAM-g-MPEG was used to prepare Au, Pt, Pd, and Cu NPs, as shown in Scheme 1b. The reversible performance of HPAMAM-g-MPEG can be seen in Figure S2. HPAMAM-g-MPEG firstly sequestered HAuCl4 (or H2PtCl6, or K2PdCl4 or CuSO4), and then reduced the metal ions into corresponding metal NPs by acylhydrazone bonds and amines, as shown in Scheme 1a,b.
Take HAuCl4 as an example, HPAMAM-g-MPEG can reduce all the HAuCl4 into Au NPs in two minutes, which was much quicker than other hyperbranched polymers with amines such as HPAMAM. We used HPAMAM-g-MPEG to reduce HAuCl4 with different values (pH 2.9, pH 4.0 and pH 6.7). Under pH 2.9 and pH 4.0, HPAMAM-g-MPEG can be cleaved into MPEG-CHO and HPAMAM-NHNH2, and metal NP/HPAMAM-NHNH2 would be formed, as shown in Scheme 1b. UV–Vis spectra were used to monitor the reduction rate. For the samples using HAuCl4 with pH 2.9 or pH 4.0 or pH 6.7, data were collected every 6 s, 12 s, and 3 min, respectively. The reduce time were 1.6, 3.4, and 92 min, respectively, as seen in Figure 2. As we know that acylhydrazone bonds in HPAMAM-g-MPEG can be cleaved into acylhydrazine and aldehyde groups under acid conditions (pH ≤ 5), while acylhydrazine have extraordinary strong reducing capacity, consequently, HAuCl4 aqueous solution with pH value lower than five can be reduced more quickly than that with high pH value.
The morphology of Au NPs synthesized was characterized by TEM, as shown in Figure 3. The sizes of Au NPs synthesized under different pH of HAuCl4 (pH 2.9, pH 4.0, and pH 6.7) are 17.8 ± 6.6, 15.7 ± 2.0, and 5.3 ± 2.0 nm, respectively. Au NPs synthesized under pH 2.9 have a large size and wide size-distribution. This is because acylhydrazone bonds of HPAMAM-g-MPEG change into acylhydrazine groups, which could reduce HAuCl4 immediately and the resulting NPs cannot be well stabilized anymore. Au NPs synthesized under pH 4.0 have a low size-distribution when compared with that under pH 2.9 due to the lower cleavage rate of acylhydrazone bonds as compared to that under pH 2.9. Whereas, Au NPs synthesized under pH 6.7 have a rather smaller size when compared with that synthesized under other pH conditions. Under pH 6.7, acylhydrazone bonds remain stable and could reduce HAuCl4 gently. HPAMAM-g-MPEG not only acts as stabilizer but also as a reducing agent, resulting a small size and narrow size-distribution of Au NPs.
Metal NPs have significant potential as catalysts due to their high surface area and their size and shape-dependent catalytic activities. Here, the catalytic activities of Au NPs with various sizes were evaluated for PNP hydrogenation catalysis, as shown in Scheme 1c. The PNP, with a yellow color under alkaline conditions, is often reduced slowly into colorless p-aminophenol (PAP) by NaBH4. However, the reduction can be accelerated greatly in the presence of catalyst. The UV–Vis spectra were monitored every second, as shown in Figure 4a. The absorbance at 400 nm (peak of PNP) decreased, accompanied with an increase of 310 nm (peak of PAP). The PNP hydrogenation catalysis can also be evidenced by the color change from yellow to colorless. The kinetic rate constants were analyzed according to the first-order rate law [55,56,57,58,59,60]. The absorbance at 400 nm was subtracted from absorbance at 600 nm to correct for background absorption. By plotting the natural log of the corrected absorbance at 400 nm against time, and fitting the steepest part of the curve into a line, the slope, which is considered as the rate constant, can be obtained. The rate constants kapp for Au NPs synthesized under different pH values (pH 2.9, pH 4.0, pH 6.7) of HAuCl4 were 0.065, 0.277 and 0.309 s−1, respectively. The trend is consistent with the surface area of Au NPs. Au NPs prepared under pH 6.7 had the smallest diameter accompanying the largest surface area when compared with Au NPs prepared under other pH conditions, resulting in the highest rate constants kapp (s−1). When the rate constants were normalized to the surface area per unit volume, the rate constants k1 were 0.92, 3.48, and 1.31 L·s−1·m−2, respectively. For the calculation of the hydrogenation rate constants kapp and k1 can be seen in Figure S3. For the volume, all of the catalysis experiments had the same volume. This means that the rate constants k1 is inversely proportional to the surface area of NPs, resulting in the biggest rate constants k1 for Au NPs prepared under pH 4 as compared to other Au NPs. Different from the G4 or G6 PAMAM dendrimers that have steric crowding problems at the periphery, HPAMAM-g-MPEG has a small HPAMAM core and several MPEG arms, so small molecules such as PNP can penetrate the MPEG shell and access the surfaces of small NPs more easily. That is why metal NPs synthesized within HPAMAM-g-MPEG have high rate constants. Detail information on the size of HPAMAM and HPAMAM-g-MPEG measured by DLS can be seen in Figure S4.
As reported in many papers [55,56,57,58,59,60], Pt and Pd NPs have also been shown to be very efficient catalysts for hydrogenation and Heck reactions. Consequently, dynamic HPAMAM-g-MPEG was also used as reductant and nanoreactor to prepare Pt, Pd, and Cu NPs. The TEM images of Pt, Pd, and Cu NPs are shown in Figure 5. The average diameter of Pt, Pd, and Cu NPs are 3.7, 5.9, and 4.2 nm, respectively.
The catalytic activities of Pt, Pd, and Cu NPs synthesized within HPAMAM-g-MPEG were also evaluated by PNP hydrogenation catalysis, as shown in Figure 6. The rate constants kapp for Pt, Pd, and Cu NPs were 0.397, 0.341, 0.148 s−1, respectively. After being normalized to the surface area per unit volume, the rate constants k1 were 1.86, 1.32, and 0.72 L·s−1·m−2, respectively. From the rate constant, we can see that Pt and Pd NPs have better catalysis activities as compared with that of Cu NPs. As reported in many papers [55,56,57,58,59,60], noble Pt and Pd NPs are commonly used as catalysts for catalytic hydrogenation, Heck reaction and Suzuki-coupling reaction, and always have good catalysis activities. For Cu NPs, their undesirable catalysis behavior can be attributed to their ease oxidation property. Information on catalysis rate constants of NPs has been summarized in Table S1.

4. Conclusions

In this paper, size-controlled Au NPs were prepared within multiarm hyperbranched polymer HPAMAM-g-MPEG under different pH of HAuCl4. HPAMAM-g-MPEG, not only was used as reductant to reduce metal ions, but also can be used as nanoreactors and stabilizers to prepare metal NPs. Systematic investigation of the effect of NP size and the pH value of HAuCl4 on the catalytic activity of the resulting Au NPs was performed. The rate constants k1 for Au NPs prepared under 4.0 of HAuCl4 could reach as high as 3.48 L·s−1·m−2 for the reduction of PNP. We suppose that this is because the HPAMAM-NHNH2 generated from the cleavage of HPAMAM-g-MPEG under acid conditions has high reducing compatibility and low steric crowding problems at the periphery. Pt, Pd, and Cu NPs were also synthesized within multiarm hyperbranched HPAMAM-g-MPEG, and also proved to be highly active catalysts for the hydrogenation reaction. For Pt NPs, the rate constants k1 was as high as 1.86 L·s−1·m−2 for the reduction of PNP. The results presented here demonstrate the utility of multiarm hyperbranched polymer as nanoreactor for preparing novel metal NPs and their excellent catalytic properties. The metal NP/HPAMAM-g-MPEG nanocomposites would be very promising catalysts in many conditions.

Supplementary Materials

The following are available online at www.mdpi.com/2073-4360/9/9/459/s1.

Acknowledgments

This work is supported by the Joint Fund for Fostering Talents of National Natural Science Foundation of China and Henan Province (U1204213), the National Natural Science Foundation of China (21304001, 21403006), the Program for International S & T Cooperation Projects of Henan Province (162102410001), the Program for Science&Technology Innovation Talents in Universities of Henan Province (14HASTIT013) and Foundation for University Young Key Teacher by Henan Province (2014GGJS-107).

Author Contributions

Yunfeng Shi, Lixin Liu and Junjie Wang conceived and designed the experiments. Fengyue Zhang, Mengyuan Niu, Yanzhu Zhao, Yifan Fan, Yanping Liang, Mei Liu and Zhenzhu Zhang did the experiments. Yunfeng Shi wrote the paper.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Caminade, A.M.; Yan, D.; Smith, D.K. Dendrimers and hyperbranched polymers. Chem. Soc. Rev. 2015, 44, 3870–3873. [Google Scholar] [CrossRef] [PubMed]
  2. Gao, C.; Yan, D. Hyperbranched polymers: From synthesis to applications. Prog. Polym. Sci. 2004, 29, 183–275. [Google Scholar] [CrossRef]
  3. Marco, F.; Vögtle, F. Dendrimers From Design to Application. Angew. Chem. Int. Ed. 1999, 38, 884–905. [Google Scholar]
  4. Zheng, Y.; Li, S.; Weng, Z.; Gao, C. Hyperbranched polymers: Advances from synthesis to applications. Chem. Soc. Rev. 2015, 44, 4091–4130. [Google Scholar] [CrossRef] [PubMed]
  5. Jiang, W.; Zhou, Y.; Yan, D. Hyperbranched polymer vesicles: From self-assembly, characterization, mechanisms, and properties to applications. Chem. Soc. Rev. 2015, 44, 3874–3889. [Google Scholar] [CrossRef] [PubMed]
  6. Jin, H.; Huang, W.; Zhu, X.; Zhou, Y.; Yan, D. Biocompatible or biodegradable hyperbranched polymers: From self-assembly to cytomimetic applications. Chem. Soc. Rev. 2012, 41, 5986–5997. [Google Scholar] [CrossRef] [PubMed]
  7. Liu, C.; Gao, C.; Yan, D. Honeycomb-patterned photoluminescent films fabricated by self-assembly of hyperbranched polymers. Angew. Chem. Int. Ed. 2007, 46, 4128–4131. [Google Scholar] [CrossRef] [PubMed]
  8. Liu, Y.; Yu, C.; Jin, H.; Jiang, B.; Zhu, X.; Zhou, Y.; Lu, Z.; Yan, D. A supramolecular Janus hyperbranched polymer and its photoresponsive self-assembly of vesicles with narrow size distribution. J. Am. Chem. Soc. 2013, 135, 4765–4770. [Google Scholar] [CrossRef] [PubMed]
  9. Tian, W.; Li, X.; Wang, J. Supramolecular hyperbranched polymers. Chem. Commun. 2017, 53, 2531–2542. [Google Scholar] [CrossRef] [PubMed]
  10. Yan, D.; Zhou, Y.; Hou, J. Supramolecular self-assembly of macroscopic tubes. Science 2004, 303, 65–67. [Google Scholar] [CrossRef] [PubMed]
  11. Zhou, Y.; Huang, W.; Liu, J.; Zhu, X.; Yan, D. Self-assembly of hyperbranched polymers and its biomedical applications. Adv. Mater. 2010, 22, 4567–4590. [Google Scholar] [CrossRef] [PubMed]
  12. Zhou, Y.; Yan, D. Supramolecular self-assembly of amphiphilic hyperbranched polymers at all scales and dimensions: Progress, characteristics and perspectives. Chem. Commun. 2009, 10, 1172–1188. [Google Scholar] [CrossRef] [PubMed]
  13. Sunder, A.; Kramer, M.; Hanselmann, R.; Mulhaupt, R.; Frey, H. Molecular nanocapsules based on amphiphilic hyperbranched polyglycerols. Angew. Chem. Int. Ed. 1999, 38, 3552–3555. [Google Scholar] [CrossRef]
  14. Kramer, M.; Stumbe, J.F.; Turk, H.; Krause, S.; Komp, A.; Delineau, L.; Prokhorova, S.; Kautz, H.; Haag, R. pH-responsive molecular nanocarriers based on dendritic core-shell architectures. Angew. Chem. Int. Ed. 2002, 41, 4252–4256. [Google Scholar] [CrossRef]
  15. Liu, C.; Gao, C.; Yan, D. Synergistic Supramolecular Encapsulation of Amphiphilic Hyperbranched Polymer to Dyes. Macromolecules 2006, 39, 8102–8111. [Google Scholar] [CrossRef]
  16. Wilms, D.; Stiriba, S.E.; Frey, H. Hyperbranched polyglycerols: From the controlled synthesis of biocompatible polyether polyols to multipurpose applications. Acc. Chem. Res. 2010, 43, 129–141. [Google Scholar] [CrossRef] [PubMed]
  17. Kurniasih, I.N.; Keilitz, J.; Haag, R. Dendritic nanocarriers based on hyperbranched polymers. Chem. Soc. Rev. 2015, 44, 4145–4164. [Google Scholar] [CrossRef] [PubMed]
  18. Shi, Y.F.; Wang, J.J.; Yuan, B.Q.; Lv, B.J.; Hou, X.Y.; Yang, X.Y.; Qin, Z.L.; Jia, S.; Lu, D.D.; Du, J.M.; et al. pH-Responsive nanocarriers based on dynamic covalent hyperbranched polymers. Sci. Adv. Mater. 2015, 7, 2486–2491. [Google Scholar] [CrossRef]
  19. Chen, S.; Zhang, X.Z.; Cheng, S.X.; Zhuo, R.X.; Gu, Z.W. Functionalized amphiphilic hyperbranched polymers for targeted drug delivery. Biomacromolecules 2008, 9, 2578–2585. [Google Scholar] [CrossRef] [PubMed]
  20. Paleos, C.M.; Tsiourvas, D.; Sideratou, Z.; Tziveleka, L.A. Drug delivery using multifunctional dendrimers and hyperbranched polymers. Expert Opin. Drug Deliv. 2010, 7, 1387–1398. [Google Scholar] [CrossRef] [PubMed]
  21. Wang, X.; Tang, J.; Sui, M.; Wang, X.; Xu, J.; Shen, Y. Degradable water soluble hyperbranched polymers for drug delivery. J. Control. Release 2011, 152, e76–e78. [Google Scholar] [CrossRef] [PubMed]
  22. Dong, R.; Zhou, Y.; Zhu, X. Supramolecular dendritic polymers: From synthesis to applications. Acc. Chem. Res. 2014, 47, 2006–2016. [Google Scholar] [CrossRef] [PubMed]
  23. Wurm, F.; Klos, J.; Räder, H.J.; Frey, H. Synthesis and noncovalent protein conjugation of linear-hyperbranched PEG-poly(glycerol) α,ωn-telechelics. J. Am. Chem. Soc. 2009, 131, 7954–7955. [Google Scholar] [CrossRef] [PubMed]
  24. Hemmati, M.; Najafi, F.; Shirkoohi, R.; Moghimi, H.R.; Zarebkohan, A.; Kazemi, B. Synthesis of a novel PEGDGA-coated hPAMAM complex as an efficient and biocompatible gene delivery vector: An in vitro and in vivo study. Drug Deliv. 2016, 23, 2956–2969. [Google Scholar] [CrossRef] [PubMed]
  25. Shi, Y.; Du, J.; Zhou, L.; Li, X.; Zhou, Y.; Li, L.; Zang, X.; Zhang, X.; Pan, F.; Zhang, H.; et al. Size-controlled preparation of magnetic iron oxidenanocrystals within hyperbranched polymers and their magnetofection in vitro. J. Mater. Chem. 2012, 22, 355–360. [Google Scholar] [CrossRef]
  26. Shi, Y.; Zhou, L.; Wang, R.; Pang, Y.; Xiao, W.; Li, H.; Su, Y.; Wang, X.; Zhu, B.; Zhu, X.; et al. In situ preparation of magnetic nonviral gene vectors and magnetofection in vitro. Nanotechnology 2010, 21, 115103. [Google Scholar] [CrossRef] [PubMed]
  27. Martello, F.; Piest, M.; Engbersen, J.F.; Ferruti, P. Effects of branched or linear architecture of bioreducible poly(amido amine)s on their in vitro gene delivery properties. J. Control. Release 2012, 164, 372–379. [Google Scholar] [CrossRef] [PubMed]
  28. Ahmed, M.; Narain, R. Cell line dependent uptake and transfection efficiencies of PEI-anionic glycopolymer systems. Biomaterials 2013, 34, 4368–4376. [Google Scholar] [CrossRef] [PubMed]
  29. Munnemann, K.; Kolzer, M.; Blakey, I.; Whittaker, A.K.; Thurecht, K.J. Hyperbranched polymers for molecular imaging: Designing polymers for parahydrogen induced polarisation (PHIP). Chem. Commun. 2012, 48, 1583–1585. [Google Scholar] [CrossRef] [PubMed]
  30. Duan, H.; Nie, S. Etching colloidal gold nanocrystals with hyperbranched and multivalent polymers: A new route to fluorescent and water-soluble atomic clusters. J. Am. Chem. Soc. 2007, 129, 2412–2413. [Google Scholar] [CrossRef] [PubMed]
  31. Mashhadi Malekzadeh, A.; Ramazani, A.; Tabatabaei Rezaei, S.J.; Niknejad, H. Design and construction of multifunctional hyperbranched polymers coated magnetite nanoparticles for both targeting magnetic resonance imaging and cancer therapy. J. Colloid Interface Sci. 2017, 490, 64–73. [Google Scholar] [CrossRef] [PubMed]
  32. Shi, Y.; Tu, C.; Zhu, Q.; Qian, H.; Ren, J.; Liu, C.; Zhu, X.; Yan, D.; Kong, E.S.; He, P. Self-assembly of CdTe nanocrystals at the water/oil interface by amphiphilic hyperbranched polymers. Nanotechnology 2008, 19, 445609. [Google Scholar] [CrossRef] [PubMed]
  33. Yang, H.Y.; Jang, M.S.; Gao, G.H.; Lee, J.H.; Lee, D.S. pH-Responsive biodegradable polymeric micelles with anchors to interface magnetic nanoparticles for MR imaging in detection of cerebral ischemic area. Nanoscale 2016, 8, 12588–12598. [Google Scholar] [CrossRef] [PubMed]
  34. Bakhshi, H.; Agarwal, S. Hyperbranched polyesters as biodegradable and antibacterial additives. J. Mater. Chem. B 2017, 5, 6827–6834. [Google Scholar] [CrossRef]
  35. Wang, S.; Chen, Y. pH-responsive, lysine-based, hyperbranched polymers mimicking endosomolytic cell-penetrating peptides for efficient intracellular delivery. Chem. Mater. 2017, 29, 5806–5815. [Google Scholar] [CrossRef]
  36. Huang, W.; Smarsly, E.; Han, J.; Bender, M.; Seehafer, K.; Wacker, I.; Schroder, R.R.; Bunz, U.H. Truxene-based hyperbranched conjugated polymers: Fluorescent micelles detect explosives in water. ACS Appl. Mater. Interfaces 2017, 9, 3068–3074. [Google Scholar] [CrossRef] [PubMed]
  37. Fan, Y.; Cai, Y.; Liu, H.; Chen, Y. CdS quantum dots capped with hyperbranched graft copolymers: Role of hyperbranched shell in fluorescence and selective mercury-sensing. Sens. Actuators B 2017, 251, 171–179. [Google Scholar] [CrossRef]
  38. Shi, Y.; Wang, Z.; Weng, X.; Zhou, L.; Yuan, B.; Deng, J.; Yang, H.; Wu, H.; Du, W.; Du, J.; et al. Preparation of highly fluorescent and ph responsive CdTe quantum dots within dynamic covalent hyperbranched polymers and their in vitro application as fluorescence probe. Sci. Adv. Mater. 2015, 7, 615–622. [Google Scholar] [CrossRef]
  39. Shi, Y.F.; Liu, L.; Pang, H.; Zhou, H.L.; Zhang, G.Q.; Ou, Y.Y.; Zhang, X.Y.; Du, J.M.; Xiao, W.C. Facile preparation of highly luminescent CdTe quantum dots within hyperbranched poly(amidoamine)s and their application in bio-imaging. Nanoscale Res. Lett. 2014, 9, 115. [Google Scholar] [CrossRef] [PubMed]
  40. Richter, T.V.; Schuler, F.; Thomann, R.; Mulhaupt, R.; Ludwigs, S. Nanocomposites of size-tunable ZnO-nanoparticles and amphiphilic hyperbranched polymers. Macromol. Rapid Commun. 2009, 30, 579–583. [Google Scholar] [CrossRef] [PubMed]
  41. Shi, Y.; Tu, C.; Wang, R.; Wu, J.; Zhu, X.; Yan, D. Preparation of CdS nanocrystals within supramolecular self-assembled nanoreactors and their phase transfer behavior. Langmuir 2008, 24, 11955–11958. [Google Scholar] [CrossRef] [PubMed]
  42. Hu, D.; Jin, S.; Shi, Y.; Wang, X.; Graff, R.W.; Liu, W.; Zhu, M.; Gao, H. Preparation of hyperstar polymers with encapsulated Au25(SR)18 clusters as recyclable catalysts for nitrophenol reduction. Nanoscale 2017, 9, 3629–3636. [Google Scholar] [CrossRef] [PubMed]
  43. Huang, X.; Zheng, S.; Kim, I. Hyperbranched polymers and dendrimers as templates for organic/inorganic hybrid nanomaterials. J. Nanosci. Nanotechnol. 2014, 14, 1631–1646. [Google Scholar] [CrossRef] [PubMed]
  44. Hu, X.; Zhou, L.; Gao, C. Hyperbranched polymers meet colloid nanocrystals: A promising avenue to multifunctional, robust nanohybrids. Colloid Polym. Sci. 2011, 289, 1299–1320. [Google Scholar] [CrossRef]
  45. Zhou, L.; Gao, C.; Hu, X.; Xu, W. General avenue to multifunctional aqueous nanocrystals stabilized by hyperbranched polyglycerol. Chem. Mater. 2011, 23, 1461–1470. [Google Scholar] [CrossRef]
  46. Morikawa, M.; Kim, K.; Kinoshita, H.; Yasui, K.; Kasai, Y.; Kimizuka, N. Aqueous nanospheres self-assembled from hyperbranched polymers and silver ions: Molecular inclusion and photoreduction characteristics. Macromolecules 2010, 43, 8971–8976. [Google Scholar] [CrossRef]
  47. Shi, Y.; Xia, N.; Lv, C.; Xing, Z.; Guo, F.; Ding, T.; Zhang, N.; Zhao, H.; Wang, H.; Zhang, G.; et al. In situ preparation of Au or Ag nanoparticles in the presence of hyperbranched poly(amidoamine)s with hydrophobic end-groups as nanoreactors and reductants. Polym. Composite. 2013, 34, 526–530. [Google Scholar] [CrossRef]
  48. Shi, Y.; Zhao, J.; Zhou, L.; Li, T.; Liu, M.; Liu, L. Blue-emitting and amphibious metal (Cu, Ni, Pt, Pd) nanodots prepared within supramolecular polymeric micellesfor cellular imaging applications. RSC Adv. 2016, 6, 59497–59501. [Google Scholar] [CrossRef]
  49. Shi, Y.; Li, S.; Zhou, Y.; Zhai, Q.; Hu, M.; Cai, F.; Du, J.; Liang, J.; Zhu, X. Facile preparation of luminescent and intelligent gold nanodots based on supramolecular self-assembly. Nanotechnology 2012, 23, 485603. [Google Scholar] [CrossRef] [PubMed]
  50. Shi, Y.; Huang, D.; Zhou, L.; Weng, X.; Cai, F.; Lv, B.; Hou, X.; Li, H.; Zhao, J.; Ma, F.; et al. In situ preparation of size-controlled iron oxide nanocrystals using double-hydrophilic multiarm hyperbranched polymers as nanoreactors and their magnetofection. Sci. Adv. Mater. 2015, 7, 219–226. [Google Scholar] [CrossRef]
  51. Das, P.; Nikhil, R.J. Highly colloidally stable hyperbranched polyglycerol grafted red fluorescent silicon nanoparticle as bioimaging probe. ACS Appl. Mater. Interfaces 2014, 6, 4301–4309. [Google Scholar] [CrossRef] [PubMed]
  52. Zhu, L.; Shi, Y.; Tu, C.; Wang, R.; Pang, Y.; Qiu, F.; Zhu, X.; Yan, D.; He, L.; Jin, C.; et al. Construction and application of a pH-sensitive nanoreactor via a double-hydrophilic multiarm hyperbranched polymer. Langmuir 2010, 26, 8875–8881. [Google Scholar] [CrossRef] [PubMed]
  53. Khabibullin, A.; Mastan, E.; Matyjaszewski, K.; Zhu, S. Surface-initiated atom transfer radical polymerization. Adv. Polym. Sci. 2016, 270, 29–76. [Google Scholar]
  54. Chmielarz, P.; Yan, J.; Krys, P.; Wang, Y.; Wang, Z.; Bockstaller, M.R.; Matyjaszewski, K. Synthesis of nanoparticle copolymer brushes via surface-initiated seATRP. Macromolecules 2017, 50, 4151–4159. [Google Scholar] [CrossRef]
  55. Carino, E.V.; Knecht, M.R.; Crooks, R.M. Quantitative analysis of the stability of Pd dendrimer-encapsulated nanoparticles. Langmuir 2009, 25, 10279–10284. [Google Scholar] [CrossRef] [PubMed]
  56. Rahim, E.H.; Kamounah, F.S.; Frederiksen, J.; Christensen, J.B. Heck reactions catalyzed by PAMAM-dendrimer encapsulated Pd(0) nanoparticles. Nano Lett. 2001, 1, 499–501. [Google Scholar] [CrossRef]
  57. Garcia-Martinez, J.C.; Lezutekong, R.; Crooks, R.M. Dendrimer-encapsulated Pd nanoparticles as aqueous, room-temperature catalysts for the stille reaction. J. Am. Chem. Soc. 2005, 127, 5097–5103. [Google Scholar] [CrossRef] [PubMed]
  58. Johnson, J.A.; Makis, J.J.; Marvin, K.A.; Rodenbuschand, S.E.; Stevenson, K.J. Size-dependent hydrogenation of p-nitrophenol with Pd nanoparticles synthesized with poly(amido)amine dendrimer templates. J. Phys. Chem. C 2013, 117, 22644–22651. [Google Scholar] [CrossRef]
  59. Herves, P.; Perez-Lorenzo, M.; Liz-Marzan, L.M.; Dzubiella, J.; Lu, Y.; Ballauff, M. Catalysis by metallic nanoparticles in aqueous solution: Model reactions. Chem. Soc. Rev. 2012, 41, 5577–5587. [Google Scholar] [CrossRef] [PubMed]
  60. Pozun, Z.D.; Rodenbusch, S.E.; Keller, E.; Tran, K.; Tang, W.; Stevenson, K.J.; Henkelman, G. A systematic investigation of p-nitrophenol reduction by bimetallic dendrimer encapsulated nanoparticles. J. Phys. Chem. C 2013, 117, 7598–7604. [Google Scholar] [CrossRef] [PubMed]
Scheme 1. Illustration for the synthesis of Au, Pt, Pd, and Cu nanoparticles (NPs) within dynamic hyperbranched polymers HPAMAM-g-MPEG (a,b) and PNP hydrogenation via sodium borohydride in the presence of the metal catalyst (c).
Scheme 1. Illustration for the synthesis of Au, Pt, Pd, and Cu nanoparticles (NPs) within dynamic hyperbranched polymers HPAMAM-g-MPEG (a,b) and PNP hydrogenation via sodium borohydride in the presence of the metal catalyst (c).
Polymers 09 00459 sch001
Figure 1. 1H NMR spectra of (A) HPAMAM; (B) HPAMAM-NHNH2; and, (C) HPAMAM-g-MPEG (400 MHz, in DMSO-d6, 298 K).
Figure 1. 1H NMR spectra of (A) HPAMAM; (B) HPAMAM-NHNH2; and, (C) HPAMAM-g-MPEG (400 MHz, in DMSO-d6, 298 K).
Polymers 09 00459 g001
Figure 2. UV–Vis spectra of Au/HPAMAM-g-MPEG nanocomposites synthesized under different pH of HAuCl4 ((a) pH 2.9; (b) pH 4.0; and, (c) pH 6.7)).
Figure 2. UV–Vis spectra of Au/HPAMAM-g-MPEG nanocomposites synthesized under different pH of HAuCl4 ((a) pH 2.9; (b) pH 4.0; and, (c) pH 6.7)).
Polymers 09 00459 g002
Figure 3. Transmission electron microscopy (TEM) images of Au NPs synthesized under different pH values of HAuCl4 ((a) pH 2.9; (b) pH 4.0; (c) pH 6.7) and energy-dispersive X-ray spectrometer (EDS) of Au NPs synthesized under pH 6.7 of HAuCl4 (d).
Figure 3. Transmission electron microscopy (TEM) images of Au NPs synthesized under different pH values of HAuCl4 ((a) pH 2.9; (b) pH 4.0; (c) pH 6.7) and energy-dispersive X-ray spectrometer (EDS) of Au NPs synthesized under pH 6.7 of HAuCl4 (d).
Polymers 09 00459 g003
Figure 4. Reduction of p-nitrophenol (PNP) catalyzed by various Au NPs. (a), (c) and (e) show the UV–Vis spectra with arrows indicating the decreasing absorbance at 400 nm (peak of PNP) and the increasing absorbance at 310 nm (peak of PAP). (b), (d) and (f) show the plots of the natural log of corrected absorbance at 400 nm against time. (a,b) correspond to Au NPs synthesized at pH 2.9. (c,d) correspond to Au NPs synthesized at pH 4.0. (e,f) correspond to Au NPs synthesized at pH 6.7.
Figure 4. Reduction of p-nitrophenol (PNP) catalyzed by various Au NPs. (a), (c) and (e) show the UV–Vis spectra with arrows indicating the decreasing absorbance at 400 nm (peak of PNP) and the increasing absorbance at 310 nm (peak of PAP). (b), (d) and (f) show the plots of the natural log of corrected absorbance at 400 nm against time. (a,b) correspond to Au NPs synthesized at pH 2.9. (c,d) correspond to Au NPs synthesized at pH 4.0. (e,f) correspond to Au NPs synthesized at pH 6.7.
Polymers 09 00459 g004
Figure 5. TEM images of Pt (a), Pd (b), and Cu (c) NPs synthesized within the multiarm hyperbranched polymer (HPAMAM-g-MPEG).
Figure 5. TEM images of Pt (a), Pd (b), and Cu (c) NPs synthesized within the multiarm hyperbranched polymer (HPAMAM-g-MPEG).
Polymers 09 00459 g005
Figure 6. Reduction of PNP catalyzed by Pt (a,b), Pd (c,d), and Cu (e,f) NPs. (a,c,e) show the UV–Vis spectra with arrows indicating the decreasing absorbance at 400 nm (peak of PNP) and the increasing absorbance at 310 nm (peak of PAP). (b,d,f) show the plots of the natural log of corrected absorbance at 400 nm against time.
Figure 6. Reduction of PNP catalyzed by Pt (a,b), Pd (c,d), and Cu (e,f) NPs. (a,c,e) show the UV–Vis spectra with arrows indicating the decreasing absorbance at 400 nm (peak of PNP) and the increasing absorbance at 310 nm (peak of PAP). (b,d,f) show the plots of the natural log of corrected absorbance at 400 nm against time.
Polymers 09 00459 g006

Share and Cite

MDPI and ACS Style

Shi, Y.; Liu, L.; Zhang, F.; Niu, M.; Zhao, Y.; Fan, Y.; Liang, Y.; Liu, M.; Zhang, Z.; Wang, J. Catalyst System for Hydrogenation Catalysis Based on Multiarm Hyperbranched Polymer Templated Metal (Au, Pt, Pd, Cu) Nanoparticles. Polymers 2017, 9, 459. https://doi.org/10.3390/polym9090459

AMA Style

Shi Y, Liu L, Zhang F, Niu M, Zhao Y, Fan Y, Liang Y, Liu M, Zhang Z, Wang J. Catalyst System for Hydrogenation Catalysis Based on Multiarm Hyperbranched Polymer Templated Metal (Au, Pt, Pd, Cu) Nanoparticles. Polymers. 2017; 9(9):459. https://doi.org/10.3390/polym9090459

Chicago/Turabian Style

Shi, Yunfeng, Lixin Liu, Fengyue Zhang, Mengyuan Niu, Yanzhu Zhao, Yifan Fan, Yanping Liang, Mei Liu, Zhenzhu Zhang, and Junjie Wang. 2017. "Catalyst System for Hydrogenation Catalysis Based on Multiarm Hyperbranched Polymer Templated Metal (Au, Pt, Pd, Cu) Nanoparticles" Polymers 9, no. 9: 459. https://doi.org/10.3390/polym9090459

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop