The Development and Performance of Knitted Cool Fabric Based on Ultra-High Molecular Weight Polyethylene

In order to withstand high-temperature environments, ultra-high molecular weight polyethylene (UHMWPE) fibers with cooling properties are being increasingly used in personal thermal management textiles during the summer. However, there is relatively little research on its combination with knitting. In this paper, we combine UHMWPE fiber and knitting structure to investigate the impact of varying UHMWPE fiber content and different knitting structures on the heat and humidity comfort as well as the cooling properties of fabrics. For this purpose, five kinds of different proportions of UHMWPE and polyamide yarn preparation, as well as five kinds of knitted tissue structures based on woven tissue were designed to weave 25 knitted fabrics. The air permeability, moisture permeability, moisture absorption and humidity conduction, thermal property, and contact cool feeling property of the fabrics were tested. Then, orthogonal analysis and correlation analysis were used to statistically evaluate the properties of the fabrics statistically. The results show that as the UHMWPE content increases, the air permeability, heat conductivity, and contact cool feeling property of the fabrics improve. The moisture permeability, moisture absorption and humidity conductivity of fabrics containing UHMWPE are superior to those containing only polyamide. The air permeability, moisture permeability, and thermal conductivity of the fabrics formed by the tuck plating organization are superior to those of the flat needle plating and float wire plating organization. The fabric formed by 2 separate 2 float wire organization has the best moisture absorption, humidity conduction, contact cool feeling property.


Introduction
Recently, with the continuous intensification of the greenhouse effect, the ambient temperature in summer has become hotter, and the utilization rate of refrigeration equipment has soared.However, the energy consumption and heat generated by refrigeration equipment contributes to the greenhouse effect, creating a vicious cycle [1].The application of cool fabrics can alleviate this phenomenon to a certain extent.Cool fabric, quite literally, is the type of fabric that creates a cooling sensation when it comes into contact with the skin.When in direct contact with human skin, this material can quickly absorb and conduct sweat on the skin's surface, and rapidly dissipate the heat generated by the body's hot environment, keeping the skin dry and cool upon contact.It can keep you cool and comfortable for a long time and plays a role in regulating the microclimate on the surface of human skin [2,3].Cool feeling fabrics can be divided into passive heat dissipation textiles, active cooling textiles, temperature and moisture responsive textiles from the principle of development [4,5].
At present, there are mainly three methods to realize the coolness of fabrics, namely, the application of the fiber with coolness itself or the physicochemical modification of coolness fiber, the fabric structure design, and finishing of fabrics with coolness additives [6,7].Common fibers to achieve fabric coolness [8] include fibers with high thermal conductivity Polymers 2024, 16, 325 2 of 18 when spinning, such as jade powder, mica powder and other fibers with high thermal conductivity minerals [9][10][11], as well as fibers with shaped cross sections designed by melt spinning [12][13][14].In terms of organizational structure, fabrics primarily achieve cooling through pore heat dissipation and water conduction heat dissipation.The lower the interweaving of yarn in the tissue unit of the fabrics, the higher the porosity, the better the permeability and heat performance of the fabrics [15].Under the same conditions, the smaller the tightness and thickness of the fabric, the better the cooling performance [16].The looped knitted fabric has better air permeability and dynamic cooling than the floating knitted fabric [17].The post-finishing of cooling additives [18] is a method used to add additives containing menthol, xylitol, and other functions of moisture absorption and heat absorption in the process of fabric finishing, so that the fabric has a cool feeling.However, when using the cool aid to arrange the fabric, the durability of the cool fabric cannot be guaranteed, and the process is relatively complex.Thus, the application of cool fibers and the design of the structure are the best ways to achieve the cool feeling of fabrics.
Most of the existing research on cool fabrics focuses on adding high thermal conductivity substances into the spinning stock solution or changing the shape of spinneret holes during spinning to produce fibers with high thermal conductivity or irregular cross sections, so as to prepare cool fabrics [19,20].However, this method is not only complex and challenging to implement, but also the inclusion of high thermal conductivity substances will diminish the mechanical properties of the fiber and compromise the durability of the fabric.In addition, fibers with high hygroscopic properties are used to prepare cool fabrics [21].However, such fabrics have limited cold contact, and may cause a stuffy feeling after a long time.The ultra-high molecular weight polyethylene (UHMWPE) fiber does not require the addition of high thermal conductivity minerals or the design of irregular cross sections during the spinning process.Its high thermal conductivity, high infrared transmittance, and smooth surface accelerate the conduction of heat and water, achieving a cooling effect [22,23].This process does not alter the original performance of the fiber, making it a superior material for weaving cool fabric.Knitted fabrics are superior to woven fabrics in terms of flexibility, ductility, and breathability.However, there is relatively little research on combining UHMWPE with knitting technology.
In this paper, we utilized UHMWPE filament with high thermal conductivity, combined with polyamide filament and polyamide/spandex covered yarn, to prepare five types of yarns with varying UHMWPE content.Additionally, we designed and wove 25 different fabrics using five different knitting structures based on the plating stitch.The aim of this study was to examine the impact of varying UHMWPE content and different fabric structures on the thermal and wet-related properties of fabrics, with the goal of facilitating the development of cooling fabrics.

The Materials
Ultra-high molecular weight polyethylene (UHMWPE) fiber, also known as highstrength and high-modulus polyethylene fiber, has good chemical stability, cut resistance, hydrophobicity, and coolness.It is mostly used in medical, industrial, and national defense sectors.However, due to ongoing advancements in industrial technology, UHMWPE is increasingly finding applications in the textile industry [24].Studies have found that the thermal conductivity of common fibers ranges from 0.042 to 0.337 W/(m• • C), as shown in Table 1.In contrast, the thermal conductivity of UHMWPE fiber ranges from 0.3 to 0.5 W/(m• • C), demonstrating excellent thermal conductivity [25].The fabric developed with this fiber has excellent cooling properties.Studies have found that it is possible to interweav UHMWPE fiber with other functional fibers [26,27].Three types of yarn were selected for fabric knitting: 8.33 tex UHMWPE filament, 7.78 tex polyamide filament, and 8.89 tex polyamide/spandex covered yarn (consisting of 5.56 tex polyamide clad with 3.33 tex spandex).

Fabric Structure Design and Preparation
The varying fabric structures not only impact the surface characteristics of the fabric, such as smoothness and pore size, but also influence the intrinsic properties of the fabric, such as thermal and moisture comfort, at a deeper level.

Fabric Structure Design and Preparation
The varying fabric structures not only impact the surface characteristics of the fa such as smoothness and pore size, but also influence the intrinsic properties of the fa such as thermal and moisture comfort, at a deeper level.

Fabric Structure Design and Preparation
The varying fabric structures not only impact the surface characteristics of the fabr such as smoothness and pore size, but also influence the intrinsic properties of the fab such as thermal and moisture comfort, at a deeper level.The Saint-toni SM8-TOP2 MP2 seamless underwear machine is utilized for fabric knitting.This equipment has a machine number of E28 needles/inch and a total of 1344 needles.It is equipped with an 8-way yarn feeding system, with each way having 8 yarn nozzles and 2 needle selectors [28][29][30].The physical pictures of the fabrics woven using the five knitting structures mentioned above are shown in Figure 3.
The Saint-toni SM8-TOP2 MP2 seamless underwear machine is utilized for fab knitting.This equipment has a machine number of E28 needles/inch and a total of 13 needles.It is equipped with an 8-way yarn feeding system, with each way having 8 ya nozzles and 2 needle selectors [28][29][30].The physical pictures of the fabrics woven usi the five knitting structures mentioned above are shown in Figure 3.To comprehensively assess the performance of UHMWPE fabric, we select UHMWPE filament and polyamide filament as the raw materials for the upper yarn, a polyamide/spandex covered yarn for the ground yarn.By altering the number of ya feeding routes for the two types of upper yarn, five different upper yarn configuratio have been designed for fabric knitting.These configurations are as follows: 8U0N, wh all upper yarns from the 1st to the 8th are UHMWPE filament; 6U2N, where except for upper yarn of the 1st and 3rd routes, the upper yarn of the other 6 routes are UHMW filament; 4U4N, where the 4 odd-numbered upper yarns are polyamide filament, and 4 even-numbered upper yarns are UHMWPE filament; 2U6N, where except for the upp yarns of the 2nd and 4th routes, which are UHMWPE filament, the upper yarns of other 6 routes are polyamide filament; 0U8N, where all upper yarns from the 1st to 8th are polyamide filament.In the preparation of these five yarns, the proportion UHMWPE filament in the upper yarn (PU) was determined to be 100%, 75%, 50%, 25 and 0%.The factors and levels of the samples are presented in Table 2.The properties fabrics were compared and analyzed primarily based on two factors: upper yarn config ration and organizational structure.The study comprehensively considered 5 levels of u per yarn configuration and 5 levels of organizational structure, resulting in the weavi of 25 groups of experimental samples (5 × 5 = 25).The basic specifications of the samp are presented in Table 3.To comprehensively assess the performance of UHMWPE fabric, we selected UHMWPE filament and polyamide filament as the raw materials for the upper yarn, and polyamide/spandex covered yarn for the ground yarn.By altering the number of yarn feeding routes for the two types of upper yarn, five different upper yarn configurations have been designed for fabric knitting.These configurations are as follows: 8U0N, where all upper yarns from the 1st to the 8th are UHMWPE filament; 6U2N, where except for the upper yarn of the 1st and 3rd routes, the upper yarn of the other 6 routes are UHMWPE filament; 4U4N, where the 4 odd-numbered upper yarns are polyamide filament, and the 4 even-numbered upper yarns are UHMWPE filament; 2U6N, where except for the upper yarns of the 2nd and 4th routes, which are UHMWPE filament, the upper yarns of the other 6 routes are polyamide filament; 0U8N, where all upper yarns from the 1st to the 8th are polyamide filament.In the preparation of these five yarns, the proportion of UHMWPE filament in the upper yarn (P U ) was determined to be 100%, 75%, 50%, 25%, and 0%.The factors and levels of the samples are presented in Table 2.The properties of fabrics were compared and analyzed primarily based on two factors: upper yarn configuration and organizational structure.The study comprehensively considered 5 levels of upper yarn configuration and 5 levels of organizational structure, resulting in the weaving of 25 groups of experimental samples (5 × 5 = 25).The basic specifications of the samples are presented in Table 3.

Air Permeability
The air permeability of a fabric refers to the ability of air to pass vertically through a specified test area of the fabric under a specific pressure difference within a given unit of time [31,32].According to GB/T 5453-1997 "Textiles-Determination of the permeability of fabrics to air" [33], the air permeability of the fabric was tested using the YG461E-III automatic air permeability meter from Ningbo Textile Instrument Factory (Ningbo, China).The test result was measured by the air permeability ratio (Q), with higher ratios indicating better air permeability.The test pressure difference set during the testing process is 100 Pa, Polymers 2024, 16, 325 5 of 18 with a test area of 20 cm 2 .Ten different sections of each fabric are selected to measure its air permeability, and the average value is calculated for each section.

Moisture Permeability
The moisture permeability of fabric, also known as water vapor permeability, refers to the fabric's ability to allow water vapor to pass through, specifically the fabric's permeability to gaseous water [34].According to GB/T 12704.1-2009"Textiles-Test method for watervapor transmission of fabrics-Part 1: Desiccant method" [35], the moisture permeability of the fabric was tested using the YG601H-II type computerized fabric permeability meter from Ningbo Textile Instrument Factory (Ningbo, China).The test result was measured by the moisture permeability ratio (WVT).The calculation formula is Formula (1).The higher the value, the greater the moisture permeability.Prepare three round samples of each fabric with a diameter of approximately 7 cm, and then average the results.
where: WVT represents the moisture permeability ratio of the sample, measured in [g•(m 2 •24 h) −1 ]; ∆m is the difference between two weighing masses of the same test assembly, measured in grams; S denotes the effective experimental area of the sample, with a value of 0.00283 m 2 for this experiment; t stands for the test time, measured in hours.

Moisture Absorption and Humidity Conduction
The moisture absorption property of the fabric refers to its ability to absorb liquid water, while the humidity conduction property of the fabric pertains to its ability to conduct liquid water [36].According to GB/T 21655.2-2009"Textiles-Evaluation of absorption and quick-drying Part 2: Method for moisture management tests", [37] the Q290 liquid moisture management analyzer (Standard Group (Hong Kong) Limited, China) is used to test the fabric's wetting time (upper T1, lower T2), absorption speed (upper A1, lower A2), and accumulative one-way transport capacity (O) to collectively characterize the moisture absorption and humidity conduction of the fabric.Before the test, a NaCl solution with a mass concentration of 9 g/L should be prepared to simulate human sweat.After preparing the instrument, five square samples measuring 8 cm × 8 cm of each fabric are tested sequentially.During the test, the fabric is positioned with the skin side facing up, and the average value is then recorded.

Thermal Property
The thermal conductivity of fabrics, also known as heat transfer, refers to the ability of fabrics to conduct heat [38].According to GB/T 11048-2008 "Textiles-Physiological effects-Measurement of thermal and water-vapor resistance under steady-state conditions", [39] the thermal properties of fabrics were tested using the YG606G thermal resistance and wet resistance tester manufactured by Ningbo Textile Instrument Factory (Ningbo, China).The test results were measured using three indexes: thermal resistance (R t ), warmth retention ratio (W t ), and heat transfer coefficient (K t ).The lower the thermal resistance and the higher the warmth retention ratio, the better the heat transfer coefficient, and thus the better the heat transfer properties of the fabric.Prepare three square samples of 35 cm × 35 cm for each type of fabric.After the machine has been preheated, place the samples on the test board one by one for testing (with the skin side of the fabric facing the test board, i.e., the skin side facing downward), and then calculate the average value.

Contact Cool Feeling Property
The contact cool feeling property of fabric refers to the phenomenon where the skin comes into contact with fabric that is cooler than the skin's temperature.This results in rapid heat exchange from the skin surface to the fabric, causing an instantaneous drop in skin surface temperature.This change is then relayed to the brain through the thermosensitive nerve endings in the skin, creating a sensation of coolness [40].According to GB/T 35263-2017 "Textiles-Testing and Evaluation for Instant Contact Cool Feeling", [41] the contact cool feeling property of the fabric was tested using the MB291 Fabric Cooling Performance Tester (Quanzhou Meibang Instrument, Quanzhou, China).The test result was measured by the contact cool feeling coefficient q max .The higher the contact cold feeling coefficient, the more intense the sensation of coolness the skin experiences from the fabric.Five square samples, each measuring 20 cm × 20 cm, of each fabric were prepared and tested sequentially, and the results were averaged.

Results and Discussion
The study investigated the air permeability, moisture permeability, moisture absorption and humidity conduction, thermal property and contact cool feeling property of 25 types of knitted fabrics.The performance test results are presented in Table 4.The standard deviation values for each test result are shown in Table 5.It can be seen from Table 5 that the data of each performance index are more reliable.Orthogonal test analysis and correlation analysis were conducted on the test results to investigate the impact of various upper yarn configurations and organizational structures on fabric properties, as well as the factors influencing these properties.

Air Permeability
The air permeability of fabric is influenced by various factors, with yarn type and structure being the primary ones [42].The orthogonal test results for the air permeability test in Table 4 are presented in Table 6.It can be observed that the R-value of factor A is smaller than that of factor B, indicating that the fabric structure has a greater impact on the sample's air permeability.This may be because the impact of the inter-yarn porosity on the air permeability of the fabric is slightly greater than that of the inter-fiber porosity.In addition, it can also be observed that achieving the best weaving scheme for fabric air permeability is A 1 B 4 .Note: K i represents the mean of the sum of experimental results for this factor at level i, and is used to calculate the R-value, where i is 1,2, . .., 5; The R-value is the range value, which is the largest K i minus the smallest K i , and is used to rank the primary and secondary factors.
To more intuitively study the influence of the two factors and five levels of the design on the air permeability of the sample, the relationship diagram in Figure 4 was created by plotting the level of each factor on the horizontal axis and the average air permeability (K i value) of the fabric under each factor level on the vertical axis.It can be observed from the figure that the influence of each level in the upper yarn configuration of factor A on the air permeability of the fabrics is ranked as follows: A 1 > A 2 > A 3 > A 4 > A 5 .This indicates that as the proportion of UHMWPE filament in the upper yarn decreases, the air permeability ratio of the fabric also decreases, leading to a deterioration in air permeability.This may be due to the fact that as the proportion of UHMWPE filament decreases and the proportion of polyamide filament increases within the same structure, the mass per unit area and thickness of the fabric increase.Consequently, the passage of air through the fabric decreases and extends, leading to a reduction in air permeability.The order of influence degree of each level in the organizational structure of factor B on the air permeability of the fabrics is as follows: B 4 > B 2 > B 1 > B 3 > B 5 .This indicates that the air permeability of the fabric formed by the tuck plating organization is the best, followed by the flat needle plating organization, and the float wire plating organization is the worst.This may be because under the preparation of the same yarn, the mass per unit area of the fabric formed by the tuck plating organization is smaller than that of the fabric formed by the flat needle plating organization and the float wire plating organization.Additionally, the tuck plating organization can create a hole effect on the fabric surface, allowing air to pass through more easily, resulting in better air permeability.
According to the orthogonal analysis results above, the primary factor influencing the air permeability of the fabric is its structure.Different structures will exhibit distinct variations in mass per unit area and thickness.The correlation analysis between air permeability and the specification parameters of the fabrics was conducted, and the results are shown in Table 7.It can be seen that the air permeability of the fabrics is highly correlated with the mass per unit area and thickness of the fabric (0.8 < |r| ≤ 1).This correlation is negative, indicating that fabrics with smaller mass per unit area and thinner thickness have greater air permeability and better air permeability.There was a weak positive correlation between the proportion of UHMWPE filament in the upper yarn configuration (0.3 < |r| ≤ 0.5), and the fabric's air permeability.A larger proportion of UHMWPE filament in the upper yarn configuration was associated with better air permeability.According to the orthogonal analysis results above, the pri the air permeability of the fabric is its structure.Different structu variations in mass per unit area and thickness.The correlation a meability and the specification parameters of the fabrics was con are shown in Table 7.It can be seen that the air permeability of th lated with the mass per unit area and thickness of the fabric (0.8 < is negative, indicating that fabrics with smaller mass per unit are have greater air permeability and better air permeability.There w relation between the proportion of UHMWPE filament in the u (0.3 < |r| ≤ 0.5), and the fabric's air permeability.A larger propo ment in the upper yarn configuration was associated with better

Moisture Permeability
The primary factors influencing the moisture permeability characteristics, yarn characteristics, and fabric structure character nal test results for the moisture permeability test in Table 4 are pr be seen that the upper yarn configuration of the fabric had a si

Moisture Permeability
The primary factors influencing the moisture permeability of fabrics include fiber characteristics, yarn characteristics, and fabric structure characteristics [43].The orthogonal test results for the moisture permeability test in Table 4 are presented in Table 8.It can be seen that the upper yarn configuration of the fabric had a significant impact on the moisture permeability of the sample.In addition, it can also be seen from the table that the optimal weaving scheme to achieve the best fabric moisture permeability is A 3 B 4 .To intuitively study the influence of two factors and five levels on the moisture permeability of the sample, the factor level is taken as the x-axis, and the average permeability of the fabric under the factor level (K i value) as the y-axis.The relationship diagram of each factor level and average moisture permeability is shown in Figure 5.It can be observed from the figure that the influence of each level in the upper yarn configuration of factor A on the moisture permeability of the fabrics is ranked as follows: A 3 > A 4 > A 2 > A 1 > A 5 .This indicates that the moisture permeability of the fabric is optimal when the ratio of the number of yarn routes between the UHMWPE filament and the polyamide filament in the upper yarn configuration is equal.This is because, under the same structure, the polyamide fiber has better moisture absorption than UHMWPE, and the fabric containing polyamide fiber has better moisture permeability than pure UHMWPE fabric.However, due to the continuous absorption of moisture by the polyamide fiber, the fiber will expand, causing the gap between the fibers to become smaller, Polymers 2024, 16, 325 10 of 18 resulting in poor moisture permeability of pure polyamide fabric.The order of influence of each level in the organizational structure of factor B on the moisture permeability of the fabrics is as follows: B 4 > B 2 > B 1 > B 3 > B 5 .This indicates that the moisture permeability of the fabric formed by the tuck plating organization is better, while the float wire plating organization is the worst.This is because, under the same yarn preparation, the fabric formed by the tuck plating organization has a larger aperture, resulting in a larger specific surface area, more water transfer channels, and better moisture permeability.
due to the continuous absorption of moisture by the polyamide fib causing the gap between the fibers to become smaller, resulting i ability of pure polyamide fabric.The order of influence of each le structure of factor B on the moisture permeability of the fabrics is B3 > B5.This indicates that the moisture permeability of the fabric ing organization is better, while the float wire plating organizat because, under the same yarn preparation, the fabric formed by zation has a larger aperture, resulting in a larger specific surface a channels, and better moisture permeability.According to the orthogonal analysis results above, a corre ducted between the fabric's moisture permeability and its spec well as other performance indicators.The results are presented in the moisture permeability of the fabrics is significantly correlated and air permeability of the fabrics (0.5 < |r| ≤ 0.8) and has a low co ness (0.3 < |r| ≤ 0.5).It shows that fabric with a low quality per permeability has relatively good moisture permeability.There wa the proportion of UHMWPE filament in the upper yarn configura  According to the orthogonal analysis results above, a correlation analysis was conducted between the fabric's moisture permeability and its specification parameters, as well as other performance indicators.The results are presented in Table 9.It is evident that the moisture permeability of the fabrics is significantly correlated with the surface density and air permeability of the fabrics (0.5 < |r| ≤ 0.8) and has a low correlation with the thickness (0.3 < |r| ≤ 0.5).It shows that fabric with a low quality per unit area and good air permeability has relatively good moisture permeability.There was no correlation between the proportion of UHMWPE filament in the upper yarn configuration (0 < |r| ≤ 0.3).

Moisture Absorption and Humidity Conduction
The factors that primarily affect the moisture absorption and humidity conduction of fabrics include the hydrophilicity of fibers and the fabric structure [44][45][46].The shorter the soaking time, the higher the water absorption rate and the greater the one-way transfer index, leading to improved moisture absorption and humidity conduction of the fabric.According to the evaluation method outlined in GB/T 21655.2-2009for assessing the moisture absorption of the fabric in Table 4, it is evident that all 25 fabrics exhibit excellent moisture absorption.When the UHMWPE fiber content exceeds that of the polyamide, the moisture conductivity of the fabrics is improved.The orthogonal test was conducted following the standardization of the test results for the positive indicators (soaking time) and negative indicators (water absorption rate and one-way transfer index) of the fabrics in Table 4.The analysis results are presented in Table 10.The comprehensive hygroscopic moisture guide index C (the sum of data after standardized processing of A1, A2, T1, T2, and O) was used to comprehensively represent the moisture absorption and humidity conduction of the fabric.It can be observed that A 2 B 5 is the optimal weaving pattern for enhancing the fabric's moisture absorption and humidity conduction.To intuitively study the influence of two factors and five levels on the moisture absorption and humidity conduction of the sample, each factor level was used as the horizontal coordinate, and the average comprehensive hygroscopic moisture guide index of the fabric under the factor level (K i value) as the ordinate.The relationship diagram of each factor level and the average comprehensive hygroscopic moisture guide index is shown in Figure 6.The figure illustrates the varying degrees of influence of each level in the upper yarn configuration of factor A on the moisture absorption and humidity conduction of the fabrics.The ranking is as follows: A 2 > A 3 > A 4 > A 5 > A 1 .This indicates that when the proportion of UHMWPE filament in the upper yarn configuration is 75%, the fabric exhibits the best moisture absorption and humidity conduction.Conversely, when the upper yarn is entirely polyamide, the fabric demonstrates the worst moisture absorption and humidity conduction.This is because the UHMWPE filament has poor moisture absorption properties, while the polyamide fiber has better moisture absorption properties.When the upper yarn contains UHMWPE, the fabric can form a structure with one side being hydrophobic and the other side being hydrophilic, achieving a unidirectional moisture absorption and humidity conduction effect.However, when the upper yarn is filled with UHMWPE filament, water is not easily absorbed.Conversely, when the upper yarn contains a significant amount of polyamide, the water is not easily conducted after absorption, thus preventing the achievement of effective unidirectional moisture absorption and humidity conduction.The order of influence of each level in the organizational structure of factor B on the moisture absorption and humidity conduction of the fabrics is as follows: B 5 > B 4 > B 2 > B 3 > B 1 .This indicates that the moisture absorption and humidity conductivity of the fabric formed by the 2 separate 2 float wire organization is better, while the flat needle plating organization is the worst.This may be because the fabric formed by the 2 separate 2 float wire organization is denser, with more interweaving points, and has more water absorption and conduction channels, resulting in better moisture absorption and humidity conductivity.
According to the orthogonal analysis results above, a correlation analysis was conducted between the comprehensive hygroscopic moisture guide index C of the fabric and the fabric specification parameters, as well as other performance indexes.The results are presented in Table 11.It is evident that the comprehensive hygroscopic moisture conductivity index C of fabric exhibits a significant positive correlation (0.5 < |r| ≤ 0.8) with the moisture permeability of the fabric.more water absorption and conduction channels, resulting in bett and humidity conductivity.According to the orthogonal analysis results above, a corre ducted between the comprehensive hygroscopic moisture guide i the fabric specification parameters, as well as other performance presented in Table 11.It is evident that the comprehensive hygro tivity index C of fabric exhibits a significant positive correlation moisture permeability of the fabric.

Thermal Property
The properties of fibers (thermal conductivity) and fabric st area and thickness, etc.) are the main factors that affect the therm [47].The orthogonal test results for the thermal property test in Table 12.It is evident that the arrangement of the upper yarn in th impact on the thermal properties of the sample.In addition, as th warmth retention ratio decrease, the heat transfer coefficient inc thermal performance of the sample.Therefore, the best weaving

Thermal Property
The properties of fibers (thermal conductivity) and fabric structures (mass per unit area and thickness, etc.) are the main factors that affect the thermal properties of fabrics [47].The orthogonal test results for the thermal property test in Table 4 are presented in Table 12.It is evident that the arrangement of the upper yarn in the fabric had a significant impact on the thermal properties of the sample.In addition, as the thermal resistance and warmth retention ratio decrease, the heat transfer coefficient increases, leading to better thermal performance of the sample.Therefore, the best weaving scheme to achieve the desired thermal properties of the fabric is A 1 B 4 .
Table 12.Results of orthogonal test on thermal properties of fabrics.

The best level of factors
For the thermal conductivity of the sample, the smaller the value of thermal resistance and warmth retention ratio, the larger the value of heat transfer coefficient, the better the thermal conductivity.Therefore, the best factor level of the thermal properties of the sample is A 1 B 4 To intuitively study the influence of the two factors and five levels of the design on the thermal properties of the sample, each factor level was used as the horizontal coordinate.The average thermal resistance, average warmth retention ratio, and average heat transfer coefficient of the fabric at each factor level (K i value) were used as the longitudinal coordinates.Subsequently, the parameter relationship diagram of each factor level and average thermal properties was drawn, as shown in Figure 7.It can be observed from the figure that the influence of each level in the upper yarn configuration of factor A on the heat transfer coefficient of the fabric is ranked as follows: A 1 > A 2 > A 3 > A 4 > A 5 .The influence on thermal resistance and warmth retention ratio of fabrics is opposite to the heat transfer coefficient.The results indicated that as the proportion of UHMWPE filament in the upper yarn configuration increased, the thermal resistance and warmth retention ratio of the fabric decreased, the heat transfer coefficient increased, and the thermal conductivity improved.This is because, under the same organizational structure, UHMWPE filament has a higher thermal conductivity than polyamide filament.By increasing the proportion of UHMWPE filament, the fabric thickness decreases, enhancing heat transfer ability, shortening the heat transfer path, and improving the fabric's thermal conductivity.The order of influence of each level in the organizational structure of factor B on the heat transfer coefficient of the fabrics is as follows: B 4 > B 2 > B 1 > B 3 > B 5 .The degree of influence on thermal resistance and warmth retention ratio of fabrics is opposite to the heat transfer coefficient.The thermal conductivity of the fabric formed by the tuck plating technique is the highest, followed by the flat needle plating organization, and the float wire plating organization is the lowest.This is because, under the same yarn preparation, the fabric formed by the tuck plating organization is thinner, has more open space, and allows heat to pass through more easily than the fabric formed by the other two types of organizational structures.
nate.The average thermal resistance, average warmth retention ratio, and average heat transfer coefficient of the fabric at each factor level ( i K value) were used as the longitu- dinal coordinates.Subsequently, the parameter relationship diagram of each factor level and average thermal properties was drawn, as shown in Figure 7.It can be observed from the figure that the influence of each level in the upper yarn configuration of factor A on the heat transfer coefficient of the fabric is ranked as follows: A1 > A2 > A3 > A4 > A5.The influence on thermal resistance and warmth retention ratio of fabrics is opposite to the heat transfer coefficient.The results indicated that as the proportion of UHMWPE filament in the upper yarn configuration increased, the thermal resistance and warmth retention ratio of the fabric decreased, the heat transfer coefficient increased, and the thermal conductivity improved.This is because, under the same organizational structure, UHMWPE filament has a higher thermal conductivity than polyamide filament.By increasing the proportion of UHMWPE filament, the fabric thickness decreases, enhancing heat transfer ability, shortening the heat transfer path, and improving the fabric's thermal conductivity.The order of influence of each level in the organizational structure of factor B on the heat transfer coefficient of the fabrics is as follows: B4 > B2 > B1 > B3 > B5.The degree of influence on thermal resistance and warmth retention ratio of fabrics is opposite to the heat transfer coefficient.The thermal conductivity of the fabric formed by the tuck plating technique is the highest, followed by the flat needle plating organization, and the float wire plating organization is the lowest.This is because, under the same yarn preparation, the fabric formed by the tuck plating organization is thinner, has more open space, and allows heat to pass through more easily than the fabric formed by the other two types of organizational structures.According to the orthogonal analysis results above, the thermal resistance, warmth retention ratio, and heat transfer coefficient of the fabric were found to be correlated with the mass per unit area, fabric thickness, the proportion of UHMWPE filament in the upper yarn configuration, air permeability, and moisture permeability, respectively.These results are presented in Table 13.It is evident that the thermal resistance, warmth retention ratio of the fabric, mass per unit area, thickness, the proportion of UHMWPE filament in the upper yarn configuration, and air permeability all exhibit significant correlation (0.5 < |r| ≤ 0.8) or high correlation (0.8 < |r| ≤ 1).They are positively correlated with the mass per unit area and thickness, and negatively correlated with the proportion of UHMWPE filament in the upper yarn configuration and air permeability.The greater the mass per According to the orthogonal analysis results above, the thermal resistance, warmth retention ratio, and heat transfer coefficient of the fabric were found to be correlated with the mass per unit area, fabric thickness, the proportion of UHMWPE filament in the upper yarn configuration, air permeability, and moisture permeability, respectively.These results are presented in Table 13.It is evident that the thermal resistance, warmth retention ratio of the fabric, mass per unit area, thickness, the proportion of UHMWPE filament in the upper yarn configuration, and air permeability all exhibit significant correlation (0.5 < |r| ≤ 0.8) or high correlation (0.8 < |r| ≤ 1).They are positively correlated with the mass per unit area and thickness, and negatively correlated with the proportion of UHMWPE filament in the upper yarn configuration and air permeability.The greater the mass per unit area and thickness of the UHMWPE filament in the upper yarn configuration, the lower the air permeability of the fabric.This results in higher thermal resistance, better warmth retention, and improved thermal insulation performance.The heat transfer coefficient of the fabric showed a significant correlation (0.5 < |r| ≤ 0.8) or high correlation (0.8 < |r| ≤ 1) with the mass per unit area, thickness, the proportion of UHMWPE filament in the upper yarn configuration, and air permeability.It was negatively correlated with the mass per unit area and thickness, and positively correlated with the proportion of UHMWPE filament in the upper yarn configuration.The results indicated that the fabric with a smaller mass per unit area, thinner thickness, a larger proportion of UHMWPE filament in the upper yarn configuration, and higher air permeability exhibited a higher heat transfer coefficient and better diathermy.

Contact Cool Feeling Property
There are numerous factors that affect the contact cool feeling property of fabrics, including fiber materials, fabric structure, and more [48].According to GB/T 35263-2017, if the contact cooling coefficient (q max ) of the fabric is 0.15 or higher, the fabric exhibits good contact cooling sensitivity.From Table 4 we can see that the contact cooling coefficient (q max ) of all 25 designed samples exceeds 0.15, indicating that the contact cooling sensitivity of all samples is good.The orthogonal test results for the contact cool feeling property test in Table 4 are presented in Table 14.It can be seen that the upper yarn configuration of the fabric had a significant impact on the sample's contact cool feeling property.In addition, it can also be seen from the table that the best weaving scheme to achieve the cool feeling property by making the fabric contact is A 1 B 5 .In order to study the influence of the two factors and five levels of the design on the contact cool feeling property of the sample in a more intuitive manner, each factor level was used as the horizontal coordinate.The average contact cool feeling coefficient (K i value) of the fabric under each factor level was used as the longitudinal coordinate.A relationship diagram between the level of each factor and the average contact cool feeling coefficient was then drawn, as shown in Figure 8.The figure illustrates the varying degrees of influence of each level in the upper yarn configuration of factor A on the contact cool feeling coefficient of the fabrics, with the ranking as follows: A 1 > A 2 > A 3 > A 4 > A 5 .This indicates that as the proportion of UHMWPE filament in the upper yarn decreases, the contact cool feeling coefficient of the fabric also decreases, leading to a deterioration in the contact cool feeling property.This is because, under the same organizational structure, the thermal conductivity of UHMWPE fiber is higher than that of polyamide.The higher the UHMWPE fiber content, the greater the thermal conductivity of the fabric and the stronger the sensation of coolness.The influence degree of each level in the organizational structure of factor B on the contact cool feeling coefficient of the fabrics is as follows: B 5 > B 1 > B 3 > B 2 > B 4 .This indicates that the contact cool feeling property of the fabric formed by the float wire plating organization and the flat needle plating organization weave is better than that of the tuck plating organization.The contact area between the fabric and the skin is larger when using the float wire plating and flat needle plating techniques compared to the tuck plating organization under the same yarn preparation.This results in a stronger feeling of coolness due to increased heat conduction channels.
B5 > B1 > B3 > B2 > B4.This indicates that the contact cool feelin formed by the float wire plating organization and the flat nee weave is better than that of the tuck plating organization.The c fabric and the skin is larger when using the float wire plating and niques compared to the tuck plating organization under the sam results in a stronger feeling of coolness due to increased heat con  Based on the orthogonal analysis results above, a correlation between the fabric's contact cool feeling coefficient and its spec other performance indicators, as presented in Table 15.It is evid feeling coefficient of the fabric shows no correlation (0 < |r| ≤ 0.3 area, thickness, air permeability, moisture permeability, and com moisture guide index of the fabric.However, it is highly correlate proportion of UHMWPE filament in the upper yarn configuratio positive.It is indicated that the fabric with a higher proportion o the upper yarn configuration exhibits a larger contact cool feeli contact cool feeling properties.There is a low positive correlation the heat transfer coefficient of the fabric and the contact cool feelin that fabrics with a higher heat transfer coefficient provide a bette  Based on the orthogonal analysis results above, a correlation analysis was conducted between the fabric's contact cool feeling coefficient and its specification parameters and other performance indicators, as presented in Table 15.It is evident that the contact cool feeling coefficient of the fabric shows no correlation (0 < |r| ≤ 0.3) with the mass per unit area, thickness, air permeability, moisture permeability, and comprehensive hygroscopic moisture guide index of the fabric.However, it is highly correlated (0.8 < |r| ≤ 1) with the proportion of UHMWPE filament in the upper yarn configuration, and the correlation is positive.It is indicated that the fabric with a higher proportion of UHMWPE filament in the upper yarn configuration exhibits a larger contact cool feeling coefficient and better contact cool feeling properties.There is a low positive correlation (0.3 < |r| ≤ 0.5) between the heat transfer coefficient of the fabric and the contact cool feeling coefficient, suggesting that fabrics with a higher heat transfer coefficient provide a better cool feeling.

Conclusions
To investigate the impact of UHMWPE fiber content and knitting structure on the heat and humidity comfort and contact cool feeling property of fabrics, five types of upper yarns with varying proportions were designed using UHMWPE filament and polyamide filament.The UHMWPE fiber proportions were 100%, 75%, 50%, 25%, and 0%, respectively.There are five types of knitting structures based on the plating stitch, including flat needle plating, single needle single column set circle with added yarn, 1 separate 1 float wire, double needle and double column set circle with added yarn, and 2 separate 2 float wire.
These structures can produce 25 different types of knitted fabrics on the machine.The air permeability, moisture permeability, moisture absorption and humidity conduction, thermal property, and contact cool feeling property of the fabrics were investigated using orthogonal analysis and correlation analysis.The results indicate that for the same yarn configuration, the samples exhibit good air permeability, moisture permeability, and heat conductivity.Additionally, the samples with a higher proportion of UHMWPE filament in the veil demonstrate better moisture absorption and contact sensitivity.In the case of the same UHMWPE and polyamide composition, the added tissue shows improved moisture permeability and moisture absorption, as well as enhanced air permeability and contact conductivity with a higher proportion of UHMWPE filament in the veil.In general, the knitted fabric made by using UHMWPE fiber in a reasonable manner exhibits excellent heat and humidity comfort performance, offering a new way for the development of cool and comfortable fabrics.
Five different organizational structures were designed based on the knitting fabric: flat needle plating organization (a), single needle single column set circle add yarn organization (b), 1 separate 1 float wire organization (c), double needle and double column set circle to add yarn organization (d), and 2 separate 2 float wire organization (e).The structural design diagram is depicted in Figure 1.The diagram of the coil structure is shown in Figure 2.
Five different organizati structures were designed based on the knitting fabric: flat needle plating organization single needle single column set circle add yarn organization (b), 1 separate 1 float organization (c), double needle and double column set circle to add yarn organization and 2 separate 2 float wire organization (e).The structural design diagram is depicte Figure 1.The diagram of the coil structure is shown in Figure 2.

Figure 1 .Figure 2 .
Figure 1.Fabric structure design diagrams; (a) flat needle plating organization; (b) single n single column set circle add yarn organization; (c) 1 separate 1 float wire organization; (d) do needle and double column set circle to add yarn organization; (e) 2 separate 2 float wire orga tion.

Figure 1 .
Figure 1.Fabric structure design diagrams; (a) flat needle plating organization; (b) single needle single column set circle add yarn organization; (c) 1 separate 1 float wire organization; (d) double needle and double column set circle to add yarn organization; (e) 2 separate 2 float wire organization.
Five different organizatio structures were designed based on the knitting fabric: flat needle plating organization ( single needle single column set circle add yarn organization (b), 1 separate 1 float w organization (c), double needle and double column set circle to add yarn organization ( and 2 separate 2 float wire organization (e).The structural design diagram is depicted Figure 1.The diagram of the coil structure is shown in Figure 2.

Figure 1 .
Figure 1.Fabric structure design diagrams; (a) flat needle plating organization; (b) single nee single column set circle add yarn organization; (c) 1 separate 1 float wire organization; (d) dou needle and double column set circle to add yarn organization; (e) 2 separate 2 float wire organi tion.

Figure 2 .
Figure 2. Fabric coil structure diagrams; (a) flat needle plating organization; (b) single needle sin column set circle add yarn organization; (c) 1 separate 1 float wire organization; (d) double nee and double column set circle to add yarn organization; (e) 2 separate 2 float wire organization.T light blue lines represent the upper yarn of each add yarn organization, and the light green li represent the ground yarn of each add yarn organization.

Figure 2 .
Figure 2. Fabric coil structure diagrams; (a) flat needle plating organization; (b) single needle single column set circle add yarn organization; (c) 1 separate 1 float wire organization; (d) double needle and double column set circle to add yarn organization; (e) 2 separate 2 float wire organization.The light blue lines represent the upper yarn of each add yarn organization, and the light green lines represent the ground yarn of each add yarn organization.

Figure 3 .
Figure 3. Fabric physical pictures; (a) flat needle plating organization; (b) single needle single c umn set circle add yarn organization; (c) 1 separate 1 float wire organization; (d) double needle a double column set circle to add yarn organization; (e) 2 separate 2 float wire organization.

Figure 3 .
Figure 3. Fabric physical pictures; (a) flat needle plating organization; (b) single needle single column set circle add yarn organization; (c) 1 separate 1 float wire organization; (d) double needle and double column set circle to add yarn organization; (e) 2 separate 2 float wire organization.
tuck plating organization can create a hole effect on the fabric surf through more easily, resulting in better air permeability.

Figure 4 .
Figure 4.The relationship between the level of each factor and the aver sample.

Figure 4 .
Figure 4.The relationship between the level of each factor and the average air permeability of the sample.

Figure 5 .
Figure 5.The relationship between the level of each factor and the aver of the sample.

Figure 5 .
Figure 5.The relationship between the level of each factor and the average moisture permeability of the sample.

Figure 6 .
Figure 6.The relationship of each factor level and the average comprehen guide index.

Figure 6 .
Figure 6.The relationship of each factor level and the average comprehensive hygroscopic moisture guide index.

Figure 7 .
Figure 7. Figure of the relationship between the level of each factor and the average thermal resistance, warmth retention ratio and heat transfer coefficient of the sample.

Figure 7 .
Figure 7. Figure of the relationship between the level of each factor and the average thermal resistance, warmth retention ratio and heat transfer coefficient of the sample.

Figure 8 .
Figure 8. Figure of the relationship between the level of each factor an feeling coefficient of the sample.
Figure 8. Figure of the relationship between the level of each factor an feeling coefficient of the sample.

Figure 8 .
Figure 8. Figure of the relationship between the level of each factor and the average contact cool feeling coefficient of the sample.

Table 1 .
Thermal conductivity of common fibers.

Table 1 .
Thermal conductivity of common fibers.

Table 2 .
Factor-level table of experimental samples.

Table 2 .
Factor-level table of experimental samples.

Table 3 .
Basic specification parameters of the experimental samples.

Table 4 .
Performance test results of the experimental samples.

Table 5 .
Standard deviation values of the various performance test results of the fabrics.

Table 6 .
Analysis results of orthogonal test of fabric air permeability.

Table 7 .
The correlation between fabric air permeability and fabric specification parameters.

Table 8 .
Analysis results of fabric moisture permeability orthogonal test.

Table 9 .
Correlation between fabric moisture permeability and fabric sp other performance indicators.

Table 9 .
Correlation between fabric moisture permeability and fabric specification parameters and other performance indicators.

Table 10 .
Analysis results of orthogonal test of fabric moisture absorption.

Table 11 .
The correlation between comprehensive hygroscopic moisture fabric specifications and other performance indexes.

Table 11 .
The correlation between comprehensive hygroscopic moisture guide index of fabrics and fabric specifications and other performance indexes.

Table 13 .
The correlation of fabric thermal properties with fabric specifications and other properties.

Table 14 .
Results of orthogonal test of fabric contact cool feeling property.

Table 15 .
The correlation of fabric contact cool feeling coefficient with fab properties.

Table 15 .
The correlation of fabric contact cool feeling coefficient with fabric specifications and other properties.