In Situ Synthesis of CsPbX3/Polyacrylonitrile Nanofibers with Water-Stability and Color-Tunability for Anti-Counterfeiting and LEDs

Inorganic CsPbX3 (X = Cl, Br, I) perovskite quantum dots (PQDs) have attracted widespread attention due to their excellent optical properties and extensive application prospects. However, their inherent structural instability significantly hinders their practical application despite their outstanding optical performance. To enhance stability, an in situ electrospinning strategy was used to synthesize CsPbX3/polyacrylonitrile composite nanofibers. By optimizing process parameters (e.g., halide ratio, electrospinning voltage, and heat treatment temperature), all-inorganic CsPbX3 PQDs have been successfully grown in a polyacrylonitrile (PAN) matrix. During the electrospinning process, the rapid solidification of electrospun fibers not only effectively constrained the formation of large-sized PQDs but also provided effective physical protection for PQDs, resulting in the improvement in the water stability of PQDs by minimizing external environmental interference. Even after storage in water for over 100 days, the PQDs maintained approximately 93.5% of their photoluminescence intensity. Through the adjustment of halogen elements, the as-obtained composite nanofibers exhibited color-tunable luminescence in the visible light region, and based on this, a series of multicolor anti-counterfeiting patterns were fabricated. Additionally, benefiting from the excellent water stability and optical performance, the CsPbBr3/PAN composite film was combined with red-emitting K2SiF6:Mn4+ (KSF) on a blue LED (460 nm), producing a stable and efficient WLED device with a color temperature of around 6000 K and CIE coordinates of (0.318, 0.322). These results provide a general approach to synthesizing PQDs/polymer nanocomposites with excellent water stability and multicolor emission, thereby promoting their practical applications in multifunctional optoelectronic devices and advanced anti-counterfeiting.


Introduction
Recently, inorganic cesium lead halide perovskite quantum dots (PQDs) with the molecular formula CsPbX 3 (X = Cl, Br, I) have undergone extensive research as promising next-generation optoelectronic materials due to their high photoluminescent quantum yield (PLQY), color-tunable luminescence, narrow emission bands and so on [1][2][3][4].They have gained significant attention in applications such as anti-counterfeiting, photocatalysis, bioimaging, displays and lighting [5,6].However, the instability of PQDs can be attributed to the lower formation energy and ionic character of chemical bonds, which render them highly sensitive to environmental factors (e.g., water, temperature or radiation), greatly limiting their practical applications in optoelectronics [7][8][9].To enhance the stability Polymers 2024, 16, 1568 2 of 13 of PQDs, a series of encapsulation strategies, including PQDs/mesoporous silica [10], PQDs/metal-organic frameworks [11] and PQDs/glass composites [12], have been proposed.However, the synthesis and processing processes of these methods are complex and cumbersome, including mesoporous template synthesis, sol-gel preparation, sintering, etc., and are not suitable for large-scale fabrication.Electrospinning technology has garnered significant attention in recent years.In addition to its application in preparing basic films, it has been demonstrated as a simple and high-throughput process for producing polymer nanofibers with enhanced crystallinity [13,14].Additionally, electrospun nanofibers can serve as effective substrates for functional materials such as metal nanoparticles and quantum dots.The spatially confined effect of electrospun nanofibers can effectively enhance the stability of quantum dots and suppress the occurrence of aggregation phenomena [15], making it a feasible technique for manufacturing perovskite nanofiber films.For example, Fan's group utilized a one-step emulsion electrospinning method to produce organicinorganic hybrid perovskite nanocrystals/polymer nanofibers, exhibiting excellent stability even in humid conditions (>60%) and underwater [16].Similarly, Chen's group employed electrospinning in the one-step fabrication of uniform luminescent nanofibers based on a perovskite core-shell structure, with the perovskite and polymer serving as the core and shell, respectively.These nanofibers retained 50% of their initial luminescent intensity after immersion in water for 48 h [17].The aforementioned similar studies have indeed enhanced the stability of PQDs to some extent.However, their long-term stability in water fails to meet the requirements for underwater background applications.
In this study, the selection of polyacrylonitrile (PAN) as the polymer matrix is due to its excellent weather resistance, UV resistance and good water/thermal stability [18][19][20].Furthermore, polymer fibers also have the advantages of having a high surface specific surface area, adjustable diameter and uniform topography [15,21].Hence, CsPbX 3 /PAN composite nanofibers have been successfully synthesized via an in situ electrospinning method, aiming to achieve the protection and preservation of CsPbX 3 PQDs.Furthermore, a systematic investigation was conducted on the influence of electrospinning parameters (e.g., applied voltage, halide ratio and heat treatment temperature) on the morphology, optical properties and chemical stability of CsPbX 3 /PAN composite nanofibers.The advantage of this process lies in the rapid stretching and solidification of PAN nanofibers during the electrospinning process, which effectively restricts the generation of large-sized PQDs and provides strong protection for CsPbX 3 PQDs inside PAN polymers.Thus, the electrospun CsPbBr 3 /PAN composite film maintained long-term high stability in water, retaining over 93.5% of the photoluminescence intensity for more than 100 days.In addition, the composite fiber film exhibited excellent multicolor luminescence (a tunable emission spectrum from blue to red and high color purity) by adjusting the proportion of the halogen element.Considering the outstanding stability and luminescence performance, combined with the simple and efficient electrospinning process that integrated CsPbX 3 PQDs with PAN nanofibers, a novel composite film material was formed.This significantly enhances the water and thermal stability of PQDs and provides new approaches and methods for their practical applications in advanced anti-counterfeiting and white LEDs.

Preparation of PQDs/PAN Nanofibers
Typically, 0.5 mmol of PbX 2 and 0.5 mmol of CsX (X = Br, I) were dissolved in 10 mL of DMF.Then, 1.0 g of PAN was added into the above mixture under stirring.To dissolve PbCl 2 and CsCl, 5 mL of DMSO and 5 mL of DMF were used to prepare a precursor solution.The synthesis of various PQDs/PAN composite nanofibers was accomplished via a uniaxial electrospinning technique.A stainless-steel needle with a size of 20 G was employed during the electrospinning process.A total volume of 10 mL of precursor spinning solution was delivered using an electric pump at a rate of 2 mL/h.A fixed voltage of 15 kV was applied, with the needle positioned 15 cm away from the receiving substrate.The electrospinning process lasted for 2.5 h.Finally, the CsPbX 3 /PAN composite nanofibers were dried in an oven at 60 • C for 1 h to eliminate any residual organic solvents.

Fabrication of WLED
Then, 0.1 g of K 2 SiF 6 :Mn 4+ (KSF) phosphor powder was thoroughly blended with 5 g of organosilica gel and continuously stirred for 3 h.The resulting solution mixture was carefully applied onto a blue LED chip (λ = 460 nm), which was covered with a dried CsPbBr 3 /PAN composite film.The assembly underwent curing at 80 • C for 5 h.

Characterizations
X-ray diffraction patterns of samples were collected by using an X-ray diffractometer (XRD, Ultima IV, Rigaku, Tokyo, Japan).Scanning electron microscopy (SEM) was performed on a JSM-7600F (JEOL, Tokyo, Japan) electron microscope.Transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM) images were taken on a JEM-2100F (JEOL, Tokyo, Japan) transmission electron microscope equipped with an X-ray spectrometer detector.The fluorescence distribution was confirmed by a Leica LSM-710 (Zeiss, Oberkochen, Germany) laser scanning confocal microscope (LSCM).UV-vis absorption spectra were recorded by a PE Lambda-950 UV-vis-NIR spectrophotometer (PerkinElmer, Waltham, MA, USA).The photoluminescence (PL) spectra and decay lifetimes were measured on an Edinburgh FLS980 fluorescence spectrometer (Edinburgh, Edinburgh, UK).The luminescent photographs were taken by a Canon EDS 70D digital camera (Canon, Tokyo, Japan).

Results and Discussions
Figure 1a depicts a schematic illustration of the one-step uniaxial electrospinning process.Inside the syringe, a PAN mixed solution containing CsX and PbX 2 (X = Cl, Br, I) in varying proportions is injected.Subsequently, the mixed precursor solution is continuously ejected through a spinning needle (be applied with a fixed voltage) with a diameter of 0.51 mm (20 G specification).Simultaneously, a fixed negative voltage is applied to the receiving substrate to provide traction to the spinning solution, stretching it into nanofibers during solidification.Within this process (Figure 1b), the nanofibers act as miniature nanoreactors, where the crystallization of perovskite quantum dots occurs along with polymer solidification [21], and the rapid solidification of PAN during electrospinning imposes a constraint effect on quantum dots, suppressing their rapid growth in the absence of other ligands [22].At the same time, the high voltage and large specific surface area of the nanofibers promote the rapid evaporation of DMF in a very short time [23].In this process, the needle makes a reciprocating motion from left to right, and by adjusting the ratio between different halogens (Cl, Br, I), large-area, regular, multicomponent PQD nanofiber films can be prepared (Figure 1c-g).These CsPbX 3 /PAN composite nanofibers exhibit excellent foldability, allowing arbitrary folding and cutting, demonstrating significant potential in wearable displays and other flexible luminescent devices.
exhibit excellent foldability, allowing arbitrary folding and cutting, demonstrating significant potential in wearable displays and other flexible luminescent devices.Firstly, the comprehensive morphological characterization of pure PAN and CsP-bBr3/PAN composite nanofibers has been investigated, as shown in Figure 2. The pure PAN nanofibers exhibit uniform thickness and a smooth surface, with an average diameter of approximately 480 nm (Figure 2a,b).As illustrated in Figure 2c,d, the average diameters of CsPbBr3/PAN (CsBr:PbBr2 is 1:1) composite nanofibers are around 350 ± 50 nm, indicating that these are finer fibers compared to pure PAN nanofibers.This is due to the addition of PQDS, which affects the arrangement and accumulation of pan molecules during fiber formation.And this results in a reduction in fiber diameter.Additionally, it can be observed that the surface of the nanofibers becomes slightly rougher, which may be attributed to residues of CsBr and PbBr2.Furthermore, the elemental mapping of the as− obtained composite nanofibers is provided in Figure 2e.From the figure, it is evident that the distribution of C, Pb and Br elements can be clearly observed along the as−obtained nanofibers.This confirms that PQDs are able to successfully grow inside nanofibers.Laser confocal fluorescence microscopy was then utilized for the random testing of CsP-bBr3/PAN composite nanofibers (Figure 2f,g).The images show the distribution and physical dimensions of electrospun fibers under bright−field conditions and actual fluorescence images under 385 nm excitation.Merging the images under bright−field and fluorescence conditions reveals that all fibers in CsPbBr3/PAN electrospun fibers exhibit clear and uniform fluorescence.Finally, an XRD characterization test was conducted on CsP-bBr3/PAN composite nanofibers to further investigate their specific structures and compositions.As seen in Figure 2h, the characteristic diffraction peaks of CsPbBr3/PAN composite nanofibers align with the standard X−ray diffraction pattern of CsPbBr3 (PDF#18−0364) and PAN (PDF#48−2119), where the diffraction angles 2θ = 15.2°,21.54° and 30.72° correspond to the (100), ( 110) and ( 200) crystal planes of the CsPbBr3 perovskite cubic phase.These angles match well with the standard CsPbBr3 cubic phase, and no other impurity phases are observed.The above comprehensive characterization analysis validates the feasibility of the in situ synthesis of PQDs nanofibers via electrospinning.Firstly, the comprehensive morphological characterization of pure PAN and CsPbBr 3 /PAN composite nanofibers has been investigated, as shown in Figure 2. The pure PAN nanofibers exhibit uniform thickness and a smooth surface, with an average diameter of approximately 480 nm (Figure 2a,b).As illustrated in Figure 2c,d, the average diameters of CsPbBr 3 /PAN (CsBr:PbBr 2 is 1:1) composite nanofibers are around 350 ± 50 nm, indicating that these are finer fibers compared to pure PAN nanofibers.This is due to the addition of PQDS, which affects the arrangement and accumulation of pan molecules during fiber formation.And this results in a reduction in fiber diameter.Additionally, it can be observed that the surface of the nanofibers becomes slightly rougher, which may be attributed to residues of CsBr and PbBr 2 .Furthermore, the elemental mapping of the as-obtained composite nanofibers is provided in Figure 2e.From the figure, it is evident that the distribution of C, Pb and Br elements can be clearly observed along the as-obtained nanofibers.This confirms that PQDs are able to successfully grow inside nanofibers.Laser confocal fluorescence microscopy was then utilized for the random testing of CsPbBr 3 /PAN composite nanofibers (Figure 2f  Next, PL properties and chemical stability are displayed in Figure 3. Figure 3a illustrates the UV−vis absorption spectra and PL spectra of the CsPbBr3/PAN composite nanofibers.The UV-visible absorption peak of this green film extends to around 525 nm, and it exhibits a PL peak at 512 nm with Full Width at Half Maximum (FWHM) of 24 nm.The inset in Figure 3a shows the actual emission photograph of the CsPbBr3/PAN composite film under 365 nm UV excitation, vividly showcasing its bright and pure green fluorescence.Afterwards, the influence of adjustments in the CsBr/PbBr2 ratio and applied voltage on the optical properties of PQDs/PAN composite nanofibers was investigated, employing CsPbBr3/PAN as a representative example.CsPbBr3/PAN composite nanofibers with different CsBr/PbBr2 ratios were prepared under a voltage of 14 KV.As depicted in Figure 3b,variations in the CsBr/PbBr2 ratio results in corresponding changes in the PL peak.As the CsBr/PbBr2 ratio increases, the PL peaks are located at 514 nm, 511 nm, 512 nm, 506 nm and 518 nm, with corresponding FWHM values of 22 nm, 28 nm, 24 nm, 22 nm and 43 nm, respectively.Moreover, both an excessively high and low CsBr/PbBr2 ratio can lead to a weakening of the PL intensity of sample.Additionally, under the condition where CsBr:PbBr2 = 1:1, the variation in the PL intensity of CsPbBr3/PAN composite nanofibers with different voltages is illustrated in Figure 3c.The PL intensity at 14 KV is twice that at 13 and 15 KV.However, with a further increase in voltage, the PL intensity begins to decrease.This is due to the intensified confinement growth effects in the nanofibers.At higher voltages, the polymer nanofibers solidify more rapidly, resulting in reduced growth time for PQDs within the nanofibers.This constrains the in situ growth of PQDs, leading to smaller particle sizes or limited crystallization.In order to achieve optimized process parameters, a systematic study was carried out on the halide ratios and applied voltages (Figures S1 and S2).From the comparison of emission spectra and PL intensity among various systems, it can be observed that when the CsBr:PbBr2 is 1:1 and 3:2, composite nanofibers prepared under specific voltages exhibit the generation of spurious emission peaks.When the ratio is 4:1, the PL intensity of samples prepared at different voltages is relatively weak.Comprehensively taking into account its optical performance, the optimal process parameters are determined to be voltage, 14 KV; CsBr:PbBr2 = 2:3.Next, PL properties and chemical stability are displayed in Figure 3. Figure 3a illustrates the UV-vis absorption spectra and PL spectra of the CsPbBr 3 /PAN composite nanofibers.The UV-visible absorption peak of this green film extends to around 525 nm, and it exhibits a PL peak at 512 nm with Full Width at Half Maximum (FWHM) of 24 nm.The inset in Figure 3a shows the actual emission photograph of the CsPbBr 3 /PAN composite film under 365 nm UV excitation, vividly showcasing its bright and pure green fluorescence.Afterwards, the influence of adjustments in the CsBr/PbBr 2 ratio and applied voltage on the optical properties of PQDs/PAN composite nanofibers was investigated, employing CsPbBr 3 /PAN as a representative example.CsPbBr 3 /PAN composite nanofibers with different CsBr/PbBr 2 ratios were prepared under a voltage of 14 KV.As depicted in Figure 3b, variations in the CsBr/PbBr 2 ratio results in corresponding changes in the PL peak.As the CsBr/PbBr 2 ratio increases, the PL peaks are located at 514 nm, 511 nm, 512 nm, 506 nm and 518 nm, with corresponding FWHM values of 22 nm, 28 nm, 24 nm, 22 nm and 43 nm, respectively.Moreover, both an excessively high and low CsBr/PbBr 2 ratio can lead to a weakening of the PL intensity of sample.Additionally, under the condition where CsBr:PbBr 2 = 1:1, the variation in the PL intensity of CsPbBr 3 /PAN composite nanofibers with different voltages is illustrated in Figure 3c.The PL intensity at 14 KV is twice that at 13 and 15 KV.However, with a further increase in voltage, the PL intensity begins to decrease.This is due to the intensified confinement growth effects in the nanofibers.At higher voltages, the polymer nanofibers solidify more rapidly, resulting in reduced growth time for PQDs within the nanofibers.This constrains the in situ growth of PQDs, leading to smaller particle sizes or limited crystallization.In order to achieve optimized process parameters, a systematic study was carried out on the halide ratios and applied voltages (Figures S1 and S2).From the comparison of emission spectra and PL intensity among various systems, it can be observed that when the CsBr:PbBr 2 is 1:1 and 3:2, composite nanofibers prepared under specific voltages exhibit the generation of spurious emission peaks.When the ratio is 4:1, the PL intensity of samples prepared at different voltages is relatively weak.Comprehensively taking into account its optical performance, the optimal process parameters are determined to be voltage, 14 KV; CsBr:PbBr 2 = 2:3.Under optimal ratios and voltage conditions, chemical stability assessments were performed on the prepared CsPbBr3/PAN composite film.As observed in Figure 3d, with increasing temperature, the PL intensity of the prepared sample gradually decreases and quenches at 423 K, owing to the thermal quenching phenomenon.At elevated temperatures, the heightened exciton dissociation fosters direct interactions between electrons and phonons, thereby inducing fluorescence quenching.It is noteworthy that the PL emission peak position and FWHM remain essentially unchanged in the temperature range of 303-383 K (Figure S3), which ensures the color purity of the sample at high temperatures.This also reflects the superb optical performance of the CsPbBr3/PAN composite nanofibers.Finally, long−term observations and tests were conducted on the stability and PL intensity decay of the CsPbBr3/PAN composite film in water (completely immersed, with periodic water replenishment).Due to the encapsulation of PQDs within the polymeric matrix, the PL intensity of the CsPbBr3/PAN composite film does not exhibit a significant decline for over 100 days (Figure 3e).Combining Figure 3f,g, the position and FWHM of its PL peak remain essentially unchanged.Under 365 nm excitation, the film continues to exhibit bright green fluorescence in water over an extended period.Consequently, polymeric nanofibers prepared through uniaxial electrospinning demonstrate exceptional encapsulation protection for in situ synthesized PQDs within the fibers.
Given the excellent optical performance and chemical stability of CsPbBr3/PAN composite nanofibers, a mature electrospinning process strategy was employed to expand the preparation of PQDs/PAN composite nanofibers with different halogens, followed by a series of characterization tests.From Figure 4a-d, it can be seen that the nanofibers doped with four different halide elements exhibit uniform thickness.However, with the varying conductivity of the spinning solutions caused by different halide ions, there are significant differences in the average diameter of the nanofibers.The diameters of CsPbCl3/PAN, CsP-bBr1.5Cl1.5/PAN,CsPbBr1.5I1.5/PAN and CsPbI3/PAN composite nanofibers are approxi- Under optimal ratios and voltage conditions, chemical stability assessments were performed on the prepared CsPbBr 3 /PAN composite film.As observed in Figure 3d, with increasing temperature, the PL intensity of the prepared sample gradually decreases and quenches at 423 K, owing to the thermal quenching phenomenon.At elevated temperatures, the heightened exciton dissociation fosters direct interactions between electrons and phonons, thereby inducing fluorescence quenching.It is noteworthy that the PL emission peak position and FWHM remain essentially unchanged in the temperature range of 303-383 K (Figure S3), which ensures the color purity of the sample at high temperatures.This also reflects the superb optical performance of the CsPbBr 3 /PAN composite nanofibers.Finally, long-term observations and tests were conducted on the stability and PL intensity decay of the CsPbBr 3 /PAN composite film in water (completely immersed, with periodic water replenishment).Due to the encapsulation of PQDs within the polymeric matrix, the PL intensity of the CsPbBr 3 /PAN composite film does not exhibit a significant decline for over 100 days (Figure 3e).Combining Figure 3f,g, the position and FWHM of its PL peak remain essentially unchanged.Under 365 nm excitation, the film continues to exhibit bright green fluorescence in water over an extended period.Consequently, polymeric nanofibers prepared through uniaxial electrospinning demonstrate exceptional encapsulation protection for in situ synthesized PQDs within the fibers.
Given the excellent optical performance and chemical stability of CsPbBr 3 /PAN composite nanofibers, a mature electrospinning process strategy was employed to expand the preparation of PQDs/PAN composite nanofibers with different halogens, followed by a series of characterization tests.From Figure 4a-d, it can be seen that the nanofibers doped with four different halide elements exhibit uniform thickness.However, with the varying conductivity of the spinning solutions caused by different halide ions, there are significant differences in the average diameter of the nanofibers.The diameters of CsPbCl 3 /PAN, CsPbBr 1.5 Cl 1.5 /PAN, CsPbBr 1.5 I 1.5 /PAN and CsPbI 3 /PAN composite nanofibers are approximately 400~800 nm; 200~300 nm; 100~200 nm; and 600~1000 nm, respectively.The specific structures and compositions of them are illustrated in Figure 4e.As Cl − and I − gradually substitute for Br − , changes in lattice size and interplanar spacing lead to a gradual shift in the overall characteristic peaks of the samples [24].Notably, when preparing CsPbI 3 /PAN composite nanofibers following the same procedure, the fluorescence emission spectrum appears chaotic (Figure S4a).To address this issue, annealing treatment was conducted.From Figure S4b, a significant enhancement in the red light emission peak is observed at an annealing temperature of 100 • C, and a single PL characteristic peak is achieved at 120 • C (Figure S4c).The effectiveness of this method is further demonstrated by comparing the actual luminescence images before and after annealing in Figure S4d-f.Building upon this, random site tests were conducted on the CsPbI 3 /PAN composite nanofibers treated at 120 • C by using LSCM (Figure S4g).Nanofibers exhibit bright and clear red fluorescence, which similarly confirms the effectiveness of the annealing treatment.The above phenomenon is caused by the short reaction time, leading to the immature crystallization of CsPbI 3 PQDs within freshly prepared nanofibers [25].XRD comparative analysis in Figure 4e confirms that the characteristic diffraction peaks of CsPbI 3 /PAN align with the standard diffraction pattern of the orthorhombic crystal structure (PDF#74-1970).This affirms the large-scale formation of CsPbI 3 PQDs within nanofibers.
Polymers 2024, 16, x FOR PEER REVIEW 7 of 13 structures and compositions of them are illustrated in Figure 4e.As Cl − and I − gradually substitute for Br − , changes in lattice size and interplanar spacing lead to a gradual shift in the overall characteristic peaks of the samples [24].Notably, when preparing CsPbI3/PAN composite nanofibers following the same procedure, the fluorescence emission spectrum appears chaotic (Figure S4a).To address this issue, annealing treatment was conducted.
From Figure S4b, a significant enhancement in the red light emission peak is observed at an annealing temperature of 100 °C, and a single PL characteristic peak is achieved at 120 °C (Figure S4c).The effectiveness of this method is further demonstrated by comparing the actual luminescence images before and after annealing in Figure S4d-f.Building upon this, random site tests were conducted on the CsPbI3/PAN composite nanofibers treated at 120 °C by using LSCM (Figure S4g).Nanofibers exhibit bright and clear red fluorescence, which similarly confirms the effectiveness of the annealing treatment.The above phenomenon is caused by the short reaction time, leading to the immature crystallization of CsPbI3 PQDs within freshly prepared nanofibers [25].XRD comparative analysis in  The UV−vis absorption spectra of the four multicolor CsPbX3/PAN composite nanofibers are shown in Figure 5.The purple CsPbCl3/PAN composite nanofiber (Figure 5a) exhibits a PL peak at 418 nm and a UV-visible absorption peak at 410 nm.The blue CsP-bBr1.5Cl1.5/PANcomposite nanofiber (Figure 5b) shows a PL peak at 454 nm and a UVvisible absorption peak at 448 nm.The orange CsPbBr1.5I1.5/PANcomposite nanofiber (Figure 5c) displays a PL peak at 534 nm and a UV-visible absorption peak at 472 nm.Lastly, the red CsPbI3/PAN composite nanofibers (Figure 5d) reveals a PL peak at 671 nm and a UV-visible absorption peak at 415 nm.By comparing the UV−vis absorption spectra of composite nanofibers composed of four different halogens, it can be observed that as the halide composition changes from Cl − to I − , the CsPbX3/PAN composite nanofibers exhibit higher absorbance in the ultraviolet and visible spectral regions [26].Subsequently, thermal stability tests were conducted on the four aforementioned composite nanofiber films.The results indicated that samples doped with halogen element iodine exhibit excellent thermal stability (Figure S5).The UV-vis absorption spectra of the four multicolor CsPbX 3 /PAN composite nanofibers are shown in Figure 5.The purple CsPbCl 3 /PAN composite nanofiber (Figure 5a) exhibits a PL peak at 418 nm and a UV-visible absorption peak at 410 nm.The blue CsPbBr 1.5 Cl 1.5 /PAN composite nanofiber (Figure 5b) shows a PL peak at 454 nm and a UV-visible absorption peak at 448 nm.The orange CsPbBr 1.5 I 1.5 /PAN composite nanofiber (Figure 5c) displays a PL peak at 534 nm and a UV-visible absorption peak at 472 nm.Lastly, the red CsPbI 3 /PAN composite nanofibers (Figure 5d) reveals a PL peak at 671 nm and a UV-visible absorption peak at 415 nm.By comparing the UV-vis absorption spectra of composite nanofibers composed of four different halogens, it can be observed that as the halide composition changes from Cl − to I − , the CsPbX 3 /PAN composite nanofibers exhibit higher absorbance in the ultraviolet and visible spectral regions [26].Subsequently, thermal stability tests were conducted on the four aforementioned composite nanofiber films.The results indicated that samples doped with halogen element iodine exhibit excellent thermal stability (Figure S5). Figure 6a illustrates the photoluminescence (PL) spectra of all CsPbX3/PAN compo site nanofibers, and their emitting wavelengths range from 418 to 671 nm.Unlike tradi tional cadmium−based QDs, the emission color of which is adjusted via the quantum size effect, the CsPbX3/PAN composite nanofibers show the flexible tunability of emission color via simply modifying the PQD compositions.Figure 6b presents corresponding ac tual luminescent photographs under 365 nm ultraviolet excitation, displaying vivid and vibrant colors.Later, time−resolved single−photon counting spectroscopy was employed From Figure 6c, it can be observed that the average PL lifetime of composite nanofibers prepared with halide elements Br and Cl doping is smaller than that of PQD nanofiber films doped with Br and Cl.(Table S1).This behavior aligns with PL decay patterns o PQDs reported in the literature [27][28][29].As the halide atom radius increases at the X site (Cl − = 1.81 Å, Br − = 1.96Å, I − = 2.20 Å), it leads to the enlargement of the bandgap of PQDs thereby increasing the carrier recombination rate.On the other hand, different halide ele ments can induce changes in the band structure of PQDs, which may affect the formation and recombination rate of electron-hole pairs, consequently influencing the fluorescence lifetime [27].The luminescent films of PQD nanofibers prepared by electrospinning differ significantly from traditional lanthanide−doped phosphors.CsPbX3/PAN composite nan ofibers, with their narrow FWHM and tunable emission, can generate saturated, sin gle−color luminescence [30][31][32].The CIE coordinates, as shown in Figure 6d, illustrate the broad color gamut of these CsPbX3 PQDs (Table S2).Considering the excellent micolor emission properties and exceptional stability of the electrospun composite films, these samples hold great promise for multicolored optoelectronic applications in aquatic envi ronments in applications of counterfeit prevention and LEDs. Figure 6a illustrates the photoluminescence (PL) spectra of all CsPbX 3 /PAN composite nanofibers, and their emitting wavelengths range from 418 to 671 nm.Unlike traditional cadmium-based QDs, the emission color of which is adjusted via the quantum size effect, the CsPbX 3 /PAN composite nanofibers show the flexible tunability of emission color via simply modifying the PQD compositions.Figure 6b presents corresponding actual luminescent photographs under 365 nm ultraviolet excitation, displaying vivid and vibrant colors.Later, time-resolved single-photon counting spectroscopy was employed.From Figure 6c, it can be observed that the average PL lifetime of composite nanofibers prepared with halide elements Br and Cl doping is smaller than that of PQD nanofiber films doped with Br and Cl.(Table S1).This behavior aligns with PL decay patterns of PQDs reported in the literature [27][28][29].As the halide atom radius increases at the X site (Cl − = 1.81 Å, Br − = 1.96Å, I − = 2.20 Å), it leads to the enlargement of the bandgap of PQDs, thereby increasing the carrier recombination rate.On the other hand, different halide elements can induce changes in the band structure of PQDs, which may affect the formation and recombination rate of electron-hole pairs, consequently influencing the fluorescence lifetime [27].The luminescent films of PQD nanofibers prepared by electrospinning differ significantly from traditional lanthanidedoped phosphors.CsPbX 3 /PAN composite nanofibers, with their narrow FWHM and tunable emission, can generate saturated, single-color luminescence [30][31][32].The CIE coordinates, as shown in Figure 6d, illustrate the broad color gamut of these CsPbX 3 PQDs (Table S2).Considering the excellent micolor emission properties and exceptional stability of the electrospun composite films, these samples hold great promise for multicolored optoelectronic applications in aquatic environments in applications of counterfeit prevention and LEDs.On the one hand, electrospinning offers the advantage of producing large−area, highly stable fluorescent nanofiber films; on the other hand, the flexibility (Figure 7d,e) of the nanofibers themselves allows for arbitrary cutting and assembling into any desired pattern, which renders them suitable for applications in anti−counterfeiting and WLED [33,34].Thus, leveraging the foldability of nanofiber films attempts to cut multicolor CsPbX3/PAN composite films into different patterns (Figure 7). Figure 7a-c  On the one hand, electrospinning offers the advantage of producing large-area, highly stable fluorescent nanofiber films; on the other hand, the flexibility (Figure 7d,e) of the nanofibers themselves allows for arbitrary cutting and assembling into any desired pattern, which renders them suitable for applications in anti-counterfeiting and WLED [33,34].Thus, leveraging the foldability of nanofiber films attempts to cut multicolor CsPbX 3 /PAN composite films into different patterns (Figure 7). Figure 7a-c The excellent display performance implies potential applications in the field of multicolor anti-counterfeiting.This utilization of electrospun nanofiber films showcases promise for future advancements in multifunctional materials for security and display technologies.
Benefiting from the exceptional PL performance and good long-term stability of CsPbX 3 /PAN composite nanofibers, white light-emitting diodes (WLEDs) were successfully fabricated using CsPbBr 3 /PAN composite film and red-emitting KSF phosphors.Figure 8a illustrates the operational principles of the WLED, wherein a blue light-emitting diode (LED) emitting at a wavelength of 460 nm is selected as the excitation light source.The KSF and CsPbBr 3 /PAN composite film are combined and overlaid onto the LED.Following this, they are encapsulated and cured with organic adhesive, which results in a simplified WLED device [35].Performance testing of the prepared WLED under a 20 mA drive current, as shown in Figure 8b, reveals distinct emission peaks in the blue, green and red spectral ranges.The inset presents actual emission photographs of the WLED device, providing a clear depiction of its ability to emit bright, pure white light.Finally, based on Figure 8c, the WLED device exhibits CIE coordinates of (0.318, 0.322), placing it within the white light region with a color temperature of approximately 6000 K [36].Taking into account the chemical stability of the CsPbBr 3 /PAN composite film, it shows significant potential in light-emitting devices.Benefiting from the exceptional PL performance and good long−term stability of CsPbX3/PAN composite nanofibers, white light−emitting diodes (WLEDs) were successfully fabricated using CsPbBr3/PAN composite film and red−emitting KSF phosphors.Figure 8a illustrates the operational principles of the WLED, wherein a blue light−emitting diode (LED) emitting at a wavelength of 460 nm is selected as the excitation light source.The KSF and CsPbBr3/PAN composite film are combined and overlaid onto the LED.Following this, they are encapsulated and cured with organic adhesive, which results in a simplified WLED device [35].Performance testing of the prepared WLED under a 20 mA drive current, as shown in Figure 8b, reveals distinct emission peaks in the blue, green and red spectral ranges.The inset presents actual emission photographs of the WLED device, providing a clear depiction of its ability to emit bright, pure white light.Finally, based on Figure 8c, the WLED device exhibits CIE coordinates of (0.318, 0.322), placing it within the white light region with a color temperature of approximately 6000 K [36].Taking into account the chemical stability of the CsPbBr3/PAN composite film, it shows significant potential in light−emitting devices.Benefiting from the exceptional PL performance and good long−term stability o CsPbX3/PAN composite nanofibers, white light−emitting diodes (WLEDs) were success fully fabricated using CsPbBr3/PAN composite film and red−emitting KSF phosphors Figure 8a illustrates the operational principles of the WLED, wherein a blue light−emitting diode (LED) emitting at a wavelength of 460 nm is selected as the excitation light source The KSF and CsPbBr3/PAN composite film are combined and overlaid onto the LED.Fol lowing this, they are encapsulated and cured with organic adhesive, which results in a simplified WLED device [35].Performance testing of the prepared WLED under a 20 mA drive current, as shown in Figure 8b, reveals distinct emission peaks in the blue, green and red spectral ranges.The inset presents actual emission photographs of the WLED de vice, providing a clear depiction of its ability to emit bright, pure white light.Finally based on Figure 8c, the WLED device exhibits CIE coordinates of (0.318, 0.322), placing i within the white light region with a color temperature of approximately 6000 K [36].Tak ing into account the chemical stability of the CsPbBr3/PAN composite film, it shows sig nificant potential in light−emitting devices.

Conclusions
In summary, we employed an electrospinning in situ synthesis strategy to fabricate visible-light tunable CsPbX 3 (X = Cl, Br, I)/PAN composite nanofibers with emitting wavelengths ranging from 418 to 671 nm.Through process optimization, specific parameters were set as follows: voltage: 14 KV; CsBr:PbBr 2 = 2:3.The CsPbBr 3 /PAN nanofiber film exhibited good stability in water resistance tests.This remarkable stability is attributed to the effective encapsulation of PQDs by the polymeric matrix, which isolates them from the detrimental effects of oxygen and moisture.Even after immersion in water for over 100 days, the film maintained approximately 93.5% of its PL intensity.Building upon this, doping various halogen elements endowed it with multicolor luminescent properties.Combined with the flexibility of the composite films themselves, they can be fabricated into various shapes and multicolored anti-counterfeiting patterns.Furthermore, leveraging the narrow FWHM and tunable emission characteristics of CsPbX 3 /PAN (X = Cl, Br, I) composite nanofibers, we successfully prepared a bright white light-emitting diode (WLED) with CIE coordinates of (0.318, 0.322) and a color temperature of around 6000 K under blue LED excitation.These results not only provide a unique approach for the synthesis of PQDs but also advance their practical applications in optoelectronic lighting and display technologies.
,g).The images show the distribution and physical dimensions of electrospun fibers under bright-field conditions and actual fluorescence images under 385 nm excitation.Merging the images under bright-field and fluorescence conditions reveals that all fibers in CsPbBr 3 /PAN electrospun fibers exhibit clear and uniform fluorescence.Finally, an XRD characterization test was conducted on CsPbBr 3 /PAN composite nanofibers to further investigate their specific structures and compositions.As seen in Figure 2h, the characteristic diffraction peaks of CsPbBr 3 /PAN composite nanofibers align with the standard X-ray diffraction pattern of CsPbBr 3 (PDF#18-0364) and PAN (PDF#48-2119), where the diffraction angles 2θ = 15.2 • , 21.54 • and 30.72 • correspond to the (100), (110) and (200) crystal planes of the CsPbBr 3 perovskite cubic phase.These angles match well with the standard CsPbBr 3 cubic phase, and no other impurity phases are observed.The above comprehensive characterization analysis validates the feasibility of the in situ synthesis of PQDs nanofibers via electrospinning.Polymers 2024, 16, 1568 5 of 13 Polymers 2024, 16, x FOR PEER REVIEW 5 of 13
Figure 4e confirms that the characteristic diffraction peaks of CsPbI3/PAN align with the standard diffraction pattern of the orthorhombic crystal structure (PDF#74−1970).This affirms the large−scale formation of CsPbI3 PQDs within nanofibers.
, respectively, show fluorescent patterns (a school badge and the letters NJFU) composed of individual multicolor CsPbX3/PAN composite films created by cutting and assembling CsPbX3/PAN composite films with various compositions under UV excitation (λ = 365 nm) in dark conditions.The excellent display performance implies potential applications in the field of multicolor anti−counterfeiting.This utilization of electrospun nanofiber films showcases promise for future advancements in multifunctional materials for security and display technologies.
, respectively, show fluorescent patterns (a school badge and the letters NJFU) composed of individual multicolor CsPbX 3 /PAN composite films created by cutting and assembling CsPbX 3 /PAN composite films with various compositions under UV excitation (λ = 365 nm) in dark conditions.

Polymers 2024 , 13 Figure 7 .
Figure 7. (a-c) Demonstration of the application of a multicolor fluorescent patterns for anti−counterfeiting. (d,e) Flexibility on display.

Figure 7 .
Figure 7. (a-c) Demonstration of the application of a multicolor fluorescent patterns for anticounterfeiting.(d,e) Flexibility on display.

Figure 7 .
Figure 7. (a-c) Demonstration of the application of a multicolor fluorescent patterns for anti−coun terfeiting.(d,e) Flexibility on display.

Figure 8 .
Figure 8.(a) Simplified structure of WLED.(b) EL spectrum (inset shows a digital camera image of the working WLED).(c) CIE coordinate and color gamut of WLED.