High-Performance Photoinitiating Systems for LED-Induced Photopolymerization

Currently, increasing attention has been focused on light-emitting diodes (LEDs)-induced photopolymerization. The common LEDs (e.g., LED at 365 nm and LED at 405 nm) possess narrow emission bands. Due to their light absorption properties, most commercial photoinitiators are sensitive to UV light and cannot be optimally activated under visible LED irradiation. Although many photoinitiators have been designed for LED-induced free radical polymerization and cationic polymerization, there is still the issue of the mating between photoinitiators and LEDs. Therefore, the development of novel photoinitiators, which could be applied under LED irradiation, is significant. Many photoinitiating systems have been reported in the past decade. In this review, some recently developed photoinitiators used in LED-induced photopolymerization, mainly in the past 5 years, are summarized and categorized as Type Ⅰ photoinitiators, Type Ⅱ photoinitiators, and dye-based photoinitiating systems. In addition, their light absorption properties and photoinitiation efficiencies are discussed.

Photoinduced polymerization is a chain reaction. Photoinitiators (PIs) can generate active species (free radicals, cations, etc.) under light irradiation to initiate the polymerization of monomers, so a PI has a crucial influence on polymerization rates and final function conversions (FC) for monomers. A photoinitiating system (PIS) can be composed of a PI or PI/additive. Free radical photopolymerization (FRP) can be initiated by generated free radicals. It should be mentioned that FRP is normally inhibited by oxygen, which can quench the primary initiating and propagating radicals. Cationic photopolymerization (CP) is normally sensitive to the presence of moisture [22,23]. Some essential characteristics, including desirable light absorption properties, high photochemical activity, good solubility, and low toxicity, are the important evaluation standard for PIs [24][25][26][27].
Traditional UV light sources (i.e., a mercury lamp) demonstrate many drawbacks, such as short service life, slow switching times, sometimes long heat-up times, and high energy consumption, compared to modern light-emitting diode (LED) light sources. In addition, significant heat generation by broadband illumination of a mercury lamp can affect the surface properties of products, and the ozone release in operation is harmful to the human body [28][29][30][31]. The inherent disadvantages of UV light sources hinder the development of

Triphenylamine-Based Photoinitiators
Triphenylamine is widely employed for the design of new PIs due to its excellent electron-donating ability. Chemical modification is usually carried out with various groups to obtain extended conjugation. The chemical structures of triphenylamine-based PIs mentioned in this review are given in Table 2. Han et al. [62] synthesized a blue-greenlight-sensitive PI CDM2 based on the triphenylamine-curcumin structure. The combination of triphenylamine and curcumin units made it show strong absorption in the blue and green light regions. The introduction of triphenylamine on both sides of the CMD2 reduced the energy gap, which contributed to the red-shifted absorption band. It was very interesting that the maximum absorption wavelength (λmax) of CDM2 in tetrahydrofuran was 467 nm, which was suitable for long-wavelength irradiation sources. As a result, the CDM2/iodonium salt system demonstrated good initiation efficiency, and the function conversions of diglycidyl ether of bisphenol A could reach up to 56% and 46% under blue LED or green LED, respectively.

Triphenylamine-Based Photoinitiators
Triphenylamine is widely employed for the design of new PIs due to its excellent electron-donating ability. Chemical modification is usually carried out with various groups to obtain extended conjugation. The chemical structures of triphenylamine-based PIs mentioned in this review are given in Table 2. Han et al. [62] synthesized a blue-greenlight-sensitive PI CDM2 based on the triphenylamine-curcumin structure. The combination of triphenylamine and curcumin units made it show strong absorption in the blue and green light regions. The introduction of triphenylamine on both sides of the CMD2 reduced the energy gap, which contributed to the red-shifted absorption band. It was very interesting that the maximum absorption wavelength (λmax) of CDM2 in tetrahydrofuran was 467 nm, which was suitable for long-wavelength irradiation sources. As a result, the CDM2/iodonium salt system demonstrated good initiation efficiency, and the function conversions of diglycidyl ether of bisphenol A could reach up to 56% and 46% under blue LED or green LED, respectively.

Triphenylamine-Based Photoinitiators
Triphenylamine is widely employed for the design of new PIs due to its excellent electron-donating ability. Chemical modification is usually carried out with various groups to obtain extended conjugation. The chemical structures of triphenylamine-based PIs mentioned in this review are given in Table 2. Han et al. [62] synthesized a blue-greenlight-sensitive PI CDM2 based on the triphenylamine-curcumin structure. The combination of triphenylamine and curcumin units made it show strong absorption in the blue and green light regions. The introduction of triphenylamine on both sides of the CMD2 reduced the energy gap, which contributed to the red-shifted absorption band. It was very interesting that the maximum absorption wavelength (λmax) of CDM2 in tetrahydrofuran was 467 nm, which was suitable for long-wavelength irradiation sources. As a result, the CDM2/iodonium salt system demonstrated good initiation efficiency, and the function conversions of diglycidyl ether of bisphenol A could reach up to 56% and 46% under blue LED or green LED, respectively.

.2. Triphenylamine-Based Photoinitiators
Triphenylamine is widely employed for the design of new PIs due to its excellent electron-donating ability. Chemical modification is usually carried out with various groups to obtain extended conjugation. The chemical structures of triphenylamine-based PIs mentioned in this review are given in Table 2. Han et al. [62] synthesized a blue-greenlight-sensitive PI CDM2 based on the triphenylamine-curcumin structure. The combination of triphenylamine and curcumin units made it show strong absorption in the blue and green light regions. The introduction of triphenylamine on both sides of the CMD2 reduced the energy gap, which contributed to the red-shifted absorption band. It was very interesting that the maximum absorption wavelength (λ max ) of CDM2 in tetrahydrofuran was 467 nm, which was suitable for long-wavelength irradiation sources. As a result, the CDM2/iodonium salt system demonstrated good initiation efficiency, and the function conversions of diglycidyl ether of bisphenol A could reach up to 56% and 46% under blue LED or green LED, respectively.
Two triphenylamine derivatives, Dye3 and Dye4, were designed as PIs by Abdallah et al. [63]. The molar extinction coefficients at 405 nm (ε 405nm ) were 4110 M −1 cm −1 and 4740 M −1 cm −1 for Dye3 and Dye4. They were efficient in initiating the CP of EPOX using LED at 405 nm, especially the epoxy function conversion was 66% for Dye3/Iod system. Good performances were shown in FRP of TMPTA for Dye/Iod/NPG PISs, and function conversions were 59% and 57% for Dye3 and Dye4 systems, respectively. The photolysis and fluorescence quenching processes indicated that the reactions for dyes and Iod were effective. Indeed, the electron-donating ability of the triphenylamine core allowed for effective electron transfer reactions.
Three triphenylamine-based hexaarylbiimidazole derivatives (HABI1, HABI2, HABI3) were synthesized by Li [64]. They exhibit favorable absorption bands from 360 nm to 420 nm. The maximum absorption wavelengths (λ max ) of HABI1-3 were 383, 385, and 384 nm, respectively. The performance of HABIs was evaluated by differential scanning photocalorimetry (photo-DSC) under a UV lamp (250-450 nm) and LED lamp (380-750 nm), respectively. The favorable values of free energy changes proved to have good electron transfer ability for the HABIs/NPG systems. The final function conversions of TMPTA for the HABI1/NPG system were 80% and 58% upon exposure to UV and LED light, respectively. High conversions demonstrated that the HABI1/NPG system could be applied under both UV and LED irradiation sources.
Jin et al. [65] proposed a conjugated sulfonium-based triphenylamine derivative (PI-PAG) as PI in CP. Triarylsulfonium salts are widely used as cationic PI due to the generation of strong protic acids and thermal stability. However, the absorption peaks of most commercial triarylsulfonium salts are below 300 nm, so they cannot be applied under longerwavelength LEDs, such as LED at 365 and 405 nm. To extend the light absorption band, the sulfonium salt moiety was associated with a long-wavelength triphenylamine chromophore in PI-PAG to form a π-conjugated structure. Interestingly, PI-PAG had good light absorption properties (λ max = 381 nm, ε 365nm = 19,200 M −1 cm −1 , ε 405nm = 14,900 M −1 cm −1 ). The photoinitiation ability of PI-PAG (1 wt%) in CP was evaluated upon exposure to 365, 385, and 405 nm LEDs. The final function conversion for EPOX at 5 min was 52.3% for PI-PAG alone using a LED at 365 nm. When Iod1 was added as a co-initiator, the final function conversion of EPOX reached 82% for PI-PAG/Iod1 (1%/3%, w/w). In addition, the CP of other monomers, such as cyclohexene oxide and Triethyleneglycol divinyl ether (DVE-3), was also investigated. For PI-PAG (0.5 wt%) alone, the polymerization of DVE-3 was observed. Furthermore, PI-PAG/Iod1 (0.5%/2%, w/w) had a good performance. Final function conversions of DVE-3 were 90.65% and 90.3% using LED at 365 and 405 nm, respectively.
A photochemical mechanism of PI-PAG was investigated by photolysis and electron spin resonance-spin trapping (ESR-ST) experiments. The S−C bond could break under irradiation; then, the generated sulfur cation radicals further reacted with hydrogen donors to produce the active initiation species H + for CP. The PI-PAG/Iod1 system could also generate cations through an electron transfer reaction. Due to its good performance, PI-PAG successfully initiated the polymerization under chemiluminescence irradiation; the associated chemical mechanisms are presented in detail in [66]. The light emission at 430 nm was generated through chemical reaction. The CP of cyclohexene oxide was observed in the presence of PI-PAG under the emitted light. These results indicated that the design strategy of π-conjugated sulfonium salts was effective.

Naphthalimide-Based Photoinitiators
Naphthalimide derivatives are widely used as PIs due to their good stability and ease of synthesis. Additionally, the absorption properties from 400 nm to 600 nm of naphthalimide derivatives can be adjusted by different chemical groups [67][68][69][70]. The chemical structures of naphthalimide-based PIs mentioned in this review are presented in Table 3. A series of naphthalimide derivatives NDP1−NDP7 were proposed as PIs upon LED at 405 nm exposure [71]. The λ max of NDP3 and NDP5 were located below 350 nm. Others demonstrated good light absorption properties because of nitro withdrawing substituent in the naphthalene moiety. Their maximum absorption wavelengths were all located in the range of 417 to 440 nm. The CP of epoxides was evaluated. NDP1/Iod1 and NDP3/Iod1 systems demonstrated low efficiency (FC < 30%) upon exposure to LED at 405 nm. Interestingly, high epoxy function conversions of EPOX 59%, 62% and 63% were obtained in the presence of NDP2/Iod1, NDP4/Iod1, and NDP6/Iod1 systems, respectively, at 800 s. NDP2, NDP4 and NDP6 also exhibit good cationic initiation ability under LED at 455 nm irradiation. The polymerization of TMPTA was evaluated using NDPs/Iod1 and NDPs/Iod1/NVK systems. An excellent performance was observed for NDP2/Iod1 (FC = 52%), NDP2/Iod1/NVK (FC = 63%), NDP4/Iod1 (FC = 52%) and NDP4/Iod1/NVK (FC = 58%). The amino or alkylamino groups contributed to the good light absorption for NDP2, NDP4, and NDP6 structures, which allowed for favorable efficiency in polymerization experiments. to produce the active initiation species H + for CP. The PI-PAG/Iod1 system could also generate cations through an electron transfer reaction. Due to its good performance, PI-PAG successfully initiated the polymerization under chemiluminescence irradiation; the associated chemical mechanisms are presented in detail in [66]. The light emission at ~430 nm was generated through chemical reaction. The CP of cyclohexene oxide was observed in the presence of PI-PAG under the emitted light. These results indicated that the design strategy of π-conjugated sulfonium salts was effective. Four naphthalimide derivatives, NDA1-NDA4 with amino or alkylthio substituents, were designed by Xiao et al. [72]. The maximum absorption wavelengths of NDA1, NDA2, NDA3, and NDA4 in acetonitrile are 416 nm, 431 nm, 387 nm, and 439 nm, respectively. Compared to others, the NDA3 exhibited a blue-shifted absorption, which could be attributed to the alkylthio substituent in a naphthalimide skeleton. Steady-state photolysis experiments of NDAs/Iod1 systems exhibit high photochemical reactivity, and favorable electron transfer reaction processes was found. Moreover, the generated phenyl radicals following the NDA2/Iod1 electron transfer reaction were detected in ESR-ST experiments. These naphthalimide derivatives demonstrated good performance in CP, and the epoxy function conversions were all higher than 58% for NDA1/Iod1, NDA2/Iod1, and NDA3/Iod1 systems upon exposure to LED at 405 and 455 nm.
Yu et al. [73] prepared six naphthalimide aryl sulfide derivatives, NAS1-NAS6, and their maximum absorption wavelengths were 389 nm, 385 nm, 340 nm, 387 nm, 391 nm, and 395 nm, respectively. Due to the electron-withdrawing substituents (acetyl, nitro, and fluoro group), blue-shifted absorption was found for NAS2, NAS3, and NAS4, compared to NAS1. The values of free energy changes ∆G for NASs/Iod1 systems were negative, which ensured favorable electron transfer. The CP of the epoxy monomer was carried out for NASs/Iod1 systems using LED at 405 nm. The NAS6/Iod1 system exhibited the best initiation performance, and the epoxy function conversion was 56%. In addition, the C(aryl)-S bond could dissociate to produce active radicals. For different structures, the cleavage of C-S bonds in different positions resulted in the difference in photoinitiation ability. The function conversion of HDDA for NAS6 (0.5 wt%) reached up to 83% upon LED exposure at 405 nm. The electron-rich radicals with isopropyl and methyl groups generated by NAS6 could induce the polymerization of acrylate easily [74]. These naphthalimide aryl sulfide derivatives had high stability under sunlight and demonstrated potential application in the photocuring field.
A PI named Naphth-Iod was designed by Zivic et al. [75]. The λ max of Naphth-Iod was 340 nm, and the absorption band reached up to 390 nm. The CP of EPOX was carried out under LED at 365 nm irradiation. Final epoxy conversions were 40% and 43% in the presence of 1 wt% and 2 wt% Naphth-Iod, respectively, at 800 s. The CP of triethyleneglycol divinyl ether was also carried out on a BaF2 pellet in laminate, and a high vinyl ether function conversion 90% was obtained within 100 s upon exposure to LED at 365 nm at room temperature. In addition, Naphth-Iod could also be used in FRP. The acrylate function conversion of 2,2-bis-[4-(methacryloxy-2-hydroxy-propoxy)-phenyl]-propane (Bis-GMA) and triethylene glycol dimethacrylate (TEGDMA) blend (70/30) was 93% using 2 wt% Naphth-Iod. High-function conversions demonstrated that Naphth-Iod could be used as a versatile PI in CP and FRP. For the photolysis experiment, the absorbance of PI decreased upon exposure to LED at 365 nm. Moreover, the phenyl radical was detected in spin-trapping ESR experiments. Based on these results, a mechanism was proposed. The C-I bond broke to produce a phenyl radical for FRP, and the cation was generated for CP through an in-cage process. In addition, the singlet and triplet excited states energy were higher than the bond dissociation energy (C-I), which was in agreement with the favorable cleavage process.     NDP3 λ max~3 34 ε max~1 3,100 [71] itiators.  [71] itiators.

Coumarine-Based Photoinitiators
Coumarin derivatives are widely applied in many fields, such as fluorescent bio labels and organic light-emitting diodes. Through chemical modification, a wide variety of electronic, photochemical and photophysical properties can be obtained for coumarin derivatives [76]. Therefore, coumarin is a good scaffold to use in the design of PIs. The chemical structures of coumarin-based PIs mentioned in this review are shown in Table 4. Two coumarin derivatives (CoumA and CoumB) were designed by Abdallah et al. [77]. Good light absorption (CoumA: λmax = 421 nm; CoumB: λmax = 405 nm) ensured the availability of LED at 405 nm. The polymerization of EPOX (25 μm) in the air was studied using LED at 405 nm. A fast polymerization rate and high epoxy function conversion (FC = 80%) were found for the CoumA/Iod system. However, no polymerization of EPOX was observed for the CoumB/Iod system in the same condition. The acrylate function conversions of TMPTA were 81% and 93% for the CoumA/Iod/NPG and CoumB/Iod/NPG systems. Efficient interactions between coumarins and Iod were observed. Indeed, coumarin derivatives as photoredox catalysts were efficient when amine was used as an electron donor and iodonium salt as an electron acceptor. In addition, water-soluble CoumB was also used for hydrogel synthesis. Finally, free radical polymerization in 3D printing was successfully proved due to the high performance of CoumA and CoumB. NAS5 λ max~3 91 ε 405nm~1 2,600 [73] NAS4 λmax ~ 387 ε405 nm ~ 12,800 [73] NAS5 λmax ~ 391 ε405 nm ~ 12,600 [73] NAS6 λmax ~ 395 ε405 nm ~ 11,700 [73] Naphth-Iod

Coumarine-Based Photoinitiators
Coumarin derivatives are widely applied in many fields, such as fluorescent bio labels and organic light-emitting diodes. Through chemical modification, a wide variety of electronic, photochemical and photophysical properties can be obtained for coumarin derivatives [76]. Therefore, coumarin is a good scaffold to use in the design of PIs. The chemical structures of coumarin-based PIs mentioned in this review are shown in Table 4. Two coumarin derivatives (CoumA and CoumB) were designed by Abdallah et al. [77]. Good light absorption (CoumA: λmax = 421 nm; CoumB: λmax = 405 nm) ensured the availability of LED at 405 nm. The polymerization of EPOX (25 μm) in the air was studied using LED at 405 nm. A fast polymerization rate and high epoxy function conversion (FC = 80%) were found for the CoumA/Iod system. However, no polymerization of EPOX was observed for the CoumB/Iod system in the same condition. The acrylate function conversions of TMPTA were 81% and 93% for the CoumA/Iod/NPG and CoumB/Iod/NPG systems. Efficient interactions between coumarins and Iod were observed. Indeed, coumarin derivatives as photoredox catalysts were efficient when amine was used as an electron donor and iodonium salt as an electron acceptor. In addition, water-soluble CoumB was also used for hydrogel synthesis. Finally, free radical polymerization in 3D printing was successfully proved due to the high performance of CoumA and CoumB.

Coumarine-Based Photoinitiators
Coumarin derivatives are widely applied in many fields, such as fluorescent bio labels and organic light-emitting diodes. Through chemical modification, a wide variety of electronic, photochemical and photophysical properties can be obtained for coumarin derivatives [76]. Therefore, coumarin is a good scaffold to use in the design of PIs. The chemical structures of coumarin-based PIs mentioned in this review are shown in Table 4. Two coumarin derivatives (CoumA and CoumB) were designed by Abdallah et al. [77]. Good light absorption (CoumA: λmax = 421 nm; CoumB: λmax = 405 nm) ensured the availability of LED at 405 nm. The polymerization of EPOX (25 μm) in the air was studied using LED at 405 nm. A fast polymerization rate and high epoxy function conversion (FC = 80%) were found for the CoumA/Iod system. However, no polymerization of EPOX was observed for the CoumB/Iod system in the same condition. The acrylate function conversions of TMPTA were 81% and 93% for the CoumA/Iod/NPG and CoumB/Iod/NPG systems. Efficient interactions between coumarins and Iod were observed. Indeed, coumarin derivatives as photoredox catalysts were efficient when amine was used as an electron donor and iodonium salt as an electron acceptor. In addition, water-soluble CoumB was also used for hydrogel synthesis. Finally, free radical polymerization in 3D printing was successfully proved due to the high performance of CoumA and CoumB.

Coumarine-Based Photoinitiators
Coumarin derivatives are widely applied in many fields, such as fluorescent bio labels and organic light-emitting diodes. Through chemical modification, a wide variety of electronic, photochemical and photophysical properties can be obtained for coumarin derivatives [76]. Therefore, coumarin is a good scaffold to use in the design of PIs. The chemical structures of coumarin-based PIs mentioned in this review are shown in Table 4. Two coumarin derivatives (CoumA and CoumB) were designed by Abdallah et al. [77]. Good light absorption (CoumA: λ max = 421 nm; CoumB: λ max = 405 nm) ensured the availability of LED at 405 nm. The polymerization of EPOX (25 µm) in the air was studied using LED at 405 nm. A fast polymerization rate and high epoxy function conversion (FC = 80%) were found for the CoumA/Iod system. However, no polymerization of EPOX was observed for the CoumB/Iod system in the same condition. The acrylate function conversions of TMPTA were 81% and 93% for the CoumA/Iod/NPG and CoumB/Iod/NPG systems. Efficient interactions between coumarins and Iod were observed. Indeed, coumarin derivatives as photoredox catalysts were efficient when amine was used as an electron donor and iodonium salt as an electron acceptor. In addition, water-soluble CoumB was also used for hydrogel synthesis. Finally, free radical polymerization in 3D printing was successfully proved due to the high performance of CoumA and CoumB.
Some derivatives bearing an iodonium salt moiety were designed as efficient onecomponent PIs by Topa et al. [78]. Their maximum absorption wavelengths were 350 nm. The polymerization of EPOX was evaluated using coumarin derivatives alone under air. 7M-P demonstrated the best initiation ability among them, and the epoxy function conversions were 58% and 53% using LED at 365 and 405 nm, respectively. Due to the good performance of coumarin-based PIs in CP and FRP, 3D-printed objects were fabricated successfully using TMPTA/EPOX blends. In steady-state photolysis experiments, the absorbance of coumarin derivatives at maximum absorption wavelength decreased obviously under LED at 365 and 405 nm irradiation. According to laser flash photolysis (LFP) experiments, the iodonium salts dissociated by homolytic or heterolytic cleavage of carbon-iodine bond. The BDE of coumarin moiety-iodine was higher than that of I-Ph-R bond. It indicated the cleavage in I-Ph-R moiety was more favorable. In addition, the aryl radicals were detected by spin-trapping ESR experiments. Based on the above results, a cleavage mechanism was proposed.

Chalcone-Based Photoinitiators
Chalcone is a natural scaffold that has been found in numerous plants. Chalcones have been applied in many fields, including organogels and organic photovoltaics [79].

Chalcone-Based Photoinitiators
Chalcone is a natural scaffold that has been found in numerous plants. Chalcones have been applied in many fields, including organogels and organic photovoltaics [79].

Chalcone-Based Photoinitiators
Chalcone is a natural scaffold that has been found in numerous plants. Chalcones have been applied in many fields, including organogels and organic photovoltaics [79]. Interestingly, chalcones can be synthesized directly by condensation of an aldehyde with acetophenone [80,81]. Markedly, chalcones also undergo a competing [2+2] photodimerization, which can be employed for photocrosslinking. Therefore, as an environmentfriendly and available dye, chalcone has been employed to design bioinspired PIs in recent years [82][83][84]. The chemical structures of chalcone-based PIs mentioned in this review are shown in Table 5.
A series of bis-chalcone compounds were proposed by Chen et al. [86]. These bischalcone compounds exhibit favorable absorption. High ε 405nm for Bis-chalcone 5 and Bis-chalcone9 were observed. The FRP of PEG-acrylate monomer in laminate (~20 µm) was evaluated using bis-chalcone/Iod/EDB systems upon exposure to LED at 405 nm. The structures Bis-chalcone 5, 7, and 9 exhibited good initiation ability, and the acrylate function conversions were 62%, 95%, and 91%, respectively. Due to the high photoactivity, 3D-printed objects were successfully fabricated in laser write experiments (laser diode at 405 nm) using Bis-chalcone 5 and 9. In addition, other chalcone compounds were synthesized by Chen et al. [87,88]. These studies provide a powerful tool for designing the PISs used in LED photopolymerization. friendly and available dye, chalcone has been employed to design bioinspired PIs in recent years [82][83][84]. The chemical structures of chalcone-based PIs mentioned in this review are shown in Table 5.
A series of bis-chalcone compounds were proposed by Chen et al. [86]. These bischalcone compounds exhibit favorable absorption. High ε405 nm for Bis-chalcone 5 and Bis-chalcone9 were observed. The FRP of PEG-acrylate monomer in laminate (~20 μm) was evaluated using bis-chalcone/Iod/EDB systems upon exposure to LED at 405 nm. The structures Bis-chalcone 5, 7, and 9 exhibited good initiation ability, and the acrylate function conversions were 62%, 95%, and 91%, respectively. Due to the high photoactivity, 3Dprinted objects were successfully fabricated in laser write experiments (laser diode at 405 nm) using Bis-chalcone 5 and 9. In addition, other chalcone compounds were synthesized by Chen et al. [87,88]. These studies provide a powerful tool for designing the PISs used in LED photopolymerization. friendly and available dye, chalcone has been employed to design bioinspired PIs in recent years [82][83][84]. The chemical structures of chalcone-based PIs mentioned in this review are shown in Table 5.
A series of bis-chalcone compounds were proposed by Chen et al. [86]. These bischalcone compounds exhibit favorable absorption. High ε405 nm for Bis-chalcone 5 and Bis-chalcone9 were observed. The FRP of PEG-acrylate monomer in laminate (~20 μm) was evaluated using bis-chalcone/Iod/EDB systems upon exposure to LED at 405 nm. The structures Bis-chalcone 5, 7, and 9 exhibited good initiation ability, and the acrylate function conversions were 62%, 95%, and 91%, respectively. Due to the high photoactivity, 3Dprinted objects were successfully fabricated in laser write experiments (laser diode at 405 nm) using Bis-chalcone 5 and 9. In addition, other chalcone compounds were synthesized by Chen et al. [87,88]. These studies provide a powerful tool for designing the PISs used in LED photopolymerization.

Type II Photoinitiators
Many studies have focused on Type II PIs which can interact with hydrogen donors through H-abstraction reaction to generate two free radicals. Some ketone-type compounds, including benzophenone (BP), thioxanthone (TX), and camphorquinone (CQ), are widely used as Type II PIs. Tertiary amines and thiols are normally used as hydrogen donors due to their good reductant behavior [89,90]. After electron transfer and proton transfer, two free radicals are generated. Because of steric hindrance and delocalization of unpaired electrons, ketyl radicals from ketone compounds have no reactivity to double bonds [91]. The absorption for most traditional Type II PIs are mainly located in the UV region, so many efforts have been devoted to expanding the light absorption range of Type II PIs to match the near UV or visible LEDs. Introducing the Type II PI structures onto dye scaffolds to obtain π-conjugated structures is an effective method. The π-conjugated structure is expected to expand the absorption and achieve good H-abstraction ability. The obtained structures can be classified as dye-based PISs. However, compared to the general dye molecules, the obtained structures demonstrate a more obvious feature of Type II PI in the presence of hydrogen donors. Therefore, these structures are separately listed as Type II PIs in this review. Benzophenone and thioxanthone are the most commonly employed, and some published chemical structures are introduced in the following context.

Benzophenone Photoinitiators
As a traditional UV-sensitive PI, BP does not absorb light in longer wavelength regions (>380 nm). BP was modified widely to obtain better photoinitiation ability. Many groups, including amino, thioether, and oxime, were induced into the BP skeleton, and these BP derivatives demonstrated good efficiency under UV light or halogen lamp [92][93][94][95][96][97][98][99][100][101][102]. Herein, the BP derivatives proposed in recent years are mainly summarized. The chemical structures of benzophenone PIs mentioned in this review are presented in Table 6.
A Type II PI (Py_BP) based on the BP group linked to a pyrene moiety was designed by Tehfe et al. [103]. The maximum absorption wavelength of Py_BP was 348 nm, and high values of ε 348nm = 26,000 M −1 cm −1 , and ε 405nm = 1400 M −1 cm −1 were found. The FRP of TMPTA was carried out upon halogen lamp exposure (λ > 300 nm), and no polymerization was found for BP/amine system. The function conversion of TMPTA reached up to 35% using Py_BP/N-methyldiethanolamine (MDEA) (1%/4%, wt%/wt%) system. Indeed, the good light absorption properties and H-abstraction ability allowed an effective Type II behavior for Py_BP. A good polymerization profile (FC = 55% at 800 s) was also observed in the CP of EPOX upon halogen lamp exposure for Py_BP/Iod (0.5%/2%, wt%/wt%) system. All results indicated that Py_BP was a reactive PI for both FRP and CP. Another BP derivative (Py_BP5) with the coupling of BP and pyrene moieties was designed by Telitel et al. [104]. Py_BP5 had a hybrid structure where BP and pyrene were fused via a benzene ring. The maximum absorption wavelength of Py_BP5 was 395 nm. Compared to Py_BP, Py_BP5 had a red-shifted absorption wavelength which could be attributed to the strong molecular orbital coupling. Free radical polymerization was carried out under Xe-Hg lamp with a filter (λ > 340 nm) irradiation. The function conversion of 40% of TMPTA was obtained using Py_BP5/MDEA (1%/2%, wt%/wt%) system at t = 200 s. Indeed, combining BP with a light-absorbing moiety is a good method to improve the light absorption properties of BP derivatives, and it was also reported in other works [105].
Zhang et al. [106] connected the BP group with naphthalimide chromophore to design another Type II PI BPND. Good light absorption properties (λ max = 431 nm, ε 405nm = 15,700 M −1 cm −1 ) were obtained. In photolysis experiments, the absorbance of BPND at 431 nm decreased slowly during the irradiation at 405 nm, on account of the H-abstraction for two BPND molecules probably. The generated aminoalkyl radical was detected in spin-trapping ESR experiments. When Iod was added, fast bleaching was observed under irradiation. In FRP experiments, BPND alone could initiate the polymerization of TMPTA as one-component Type II PI. Interestingly, BPND/Iod system exhibit excellent and similar photoinitiation ability (55~57%) under LED at 405, 455 and 470 nm irradiation. High function conversions (56~70%) were also obtained in CP for EPOX in the presence of the BPND/Iod system. The high performance of BPND benefits from the good design of the molecular structure. In a word, the ketone-dye-based compounds demonstrate great potential in the design of PIs for LED photoinitiation.
Five visible light benzophenone-based PIs (BP1-BP5) were synthesized by Huang et al. [107]. In these structures, BP was incorporated into different arylamin moieties. The UV absorption spectra of BPs were investigated in a dichloromethane solution. Compared to BP, BP derivatives exhibit red-shifted absorption, and λ max of them were all located in a range of 360 to 375 nm. Due to the good absorption properties and the BP moiety, these PIs were expected to act as efficient visible Type II PIs in FRP. The photolysis of BPs/triethylamine (TEA) systems were studied under 365 nm light irradiation. The absorption band at~360 nm decreased; meanwhile, an increasing peak at~290 nm was observed. The FRP of TMPTA under a UV lamp was evaluated by photo-DSC in the presence of BPs/TEA systems. The reference BP/TEA system demonstrated the best performance among them. No polymerization was observed for BP3/EDB system. The polymerization of TMPTA was also evaluated under white light LED irradiation (380-750 nm). High function conversions of TMPTA were found for BP-1/TEA and BP/TEA systems, respectively. Indeed, good light absorption properties ensured the efficient photoinitiation ability for BP-1 as a Type II PI.
Three compounds named C-DBP, P-DBP and T-DBP were designed as PIs for LED photopolymerization by Jia et al. [108]. These chemical structures incorporated benzophenone as an electron acceptor and carbazole/phenothiazine/triphenylamine as an electron donor. Considering the photo-isomerization of the double bond, the triple bond is a desired π-linker for D-π-A structures to extend the conjugated structures. These PIs had favorable absorption bands in the region of 300 to 450 nm. The FRP of tripropylene glycol diacrylate (TPGDA) were carried out upon exposure to LED at 405 nm using DBP/triethanolamine (TEOA) system. It was interesting that C-DBP/TEOA (0.25%/2%, w/w) exhiexhibitedd photoinitiation ability and the acrylate function conversion reached up to 95%, while P-DBP and T-DBP systems demonstrated poor performance in polymerization experiments. In fluorescence and nanosecond transient absorption experiments, C-DBP demonstrated both BP-like features, contributing to good H-abstraction ability. Thus, C-DBP had good performance in free radical photopolymerization.
A benzophenone derivative named BPN was designed by Xue et al. [109]. BPN had strong adsorption in the range of 320~500 nm (ε 405nm = 42,400 M −1 cm −1 ), indicating BPN could be used as visible light PI under LED illumination. It was interesting that the polymerization of the TPGDA blends were observed at LED at 405 nm without any additional co-initiator. The acrylate function conversion was 80% at 80 s in the presence of 0.5 wt% BPN. It was attributed to dimethyl amine moiety in the structure. Interestingly, the faster polymerization rate and higher function conversion (90%) were obtained using BPN/TEOA system. BPN demonstrated the same performance as benchmark ITX in polymerization experiments. Fast photolysis was observed for BPN alone upon exposure to LED at 405 nm. The reason was that an H-abstraction reaction occurred between benzophenone and amine groups in two BPN molecules. In addition, the absorption of BPN declined fast in the presence of TEOA. Indeed, the H-abstraction reaction mainly occurred in BPN/TEOA bimolecular system. In spin-trapping ESR experiments, the generated BPN (-H) radical and TEOA (-H) radical were detected, which verified the H-abstraction reaction in unimolecular and bimolecular systems, respectively. Because of its high performance, BPN has great potential to be used in photoinitiation.
A series of benzophenone-carbazole compounds (BPC-BPC4) was investigated by Liu et al. [110,111]. Interestingly, the benzoyl substituent is connected with carbazole to generate a benzophenone moiety. The benzophenone-carbazole structure demonstrates the feature of the Type II photoinitiator (PI). Good absorption in the UV region was found (ε max = 18,600 M −1 cm −1 , λ max = 342 nm) for BPC and the value of ε 365nm was favorable. Therefore, their photoinitiation performances of them were studied using a LED at 365 nm.
Benzophenone-carbazole PIs could initiate the polymerization of monomers alone. In addition, better performances were found for two-component systems (FC = 60% for BPC/EDB system; FC = 63% for BPC/Iod system). Besides, these PIs demonstrated favorable performance in cationic polymerization of EPOX (FC = 46% for BPC/Iod system).

Thioxanthone Photoinitiators
Thioxanthone (TX) is another efficient Type II PI, and the TX derivatives are widely used in FRP and CP. Compared to BP, TX exhibits a longer absorption wavelength in the range of 300-400 nm, so TX derivatives are in a class of potential visible light PIs [114][115][116]. As known, the commercial isopropylthioxanthone (ITX) is widely used as a benchmark Type II PI. The chemical structures of thioxanthone PIs mentioned in this review are given in Table 7.
A thioxanthone-carbazole derivative (TX-C) was synthesized by Yilmaz et al. [117][118][119]. TX moiety was in conjunction with carbazole chromophore to obtain light absorption in the visible range. TX-C demonstrated good absorption at a longer wavelength range (400-500 nm), where TX was almost transparent. Indeed, the extended conjugation of TX and carbazole moieties contributed to the longer absorption wavelength. The λ max was 434 nm for TX-C, and a high molar extinction coefficient was found (ε 434nm = 2010 M −1 cm −1 ). In the steady-state photolysis experiments, the absorbance at 434 nm of TX-C decreased. It indicated that an H-abstraction reaction occurred between TX and the amine group in the carbazole moiety. Therefore, TX-C could be used as a one-component Type II PI without an additional hydrogen donor. The initiation ability of PI was evaluated upon exposure to visible light (430-490 nm). There is no polymerization of monomers in the presence of the TX/amine system due to the poor absorption property of TX in the visible range. As expected, TX-C could initiate the polymerization of methyl methacrylate (MMA) alone. The excited state TX-C reacted with the ground state TX-C to generate carbazoyl radical, which was active in the polymerization of MMA. When the amine (hydrogen donor) was added, TX-C/amine system demonstrated a faster polymerization rate than one-component TX-C. Indeed, in the presence of amine, H-abstraction occurred easily between TX-C and amine. In summary, TX-C was an excellent visible Type II PI and had many targeted applications.
A thioxanthone-anthracene PI (TX-A) was synthesized by Balta et al. [120,121]. The maximum absorption wavelength of TX-A was 368 nm and the absorption band extended to 450 nm. In photolysis experiments, the absorption band of the anthracene moiety almost disappeared with the consumption of TX-A, while the absorption of thioxanthone moiety at 380 nm was still observed. TX-A was used as a PI for the FRP of MMA. It was strange that higher function conversions were found in the presence of TX-A under air, compared to TX-A/amine system. In addition, no polymerization was found under nitrogen. Based on the photolysis and polymerization experiments, the conclusions could be obtained that TX moiety did not likely participate in the H-abstraction reaction, and oxygen played an important role in polymerization. As known, when the triplet oxygen (ground state molecular oxygen) is quenched, singlet oxygen will produce through energy transfer. In an air-saturated TX-A solution, the generation of singlet oxygen was confirmed by the NIR luminescence spectrum. Therefore, singlet oxygen could react with anthracene moiety to generate endoperoxide. Then endoperoxide decomposed into radicals that were active for monomers. The chemical mechanism of TX-A is helpful in overcoming oxygen inhibition in FRP processes [122,123].
A PI named TX-NPG was designed by Tar et al. [124]. TX-NPG exhibit good light absorption in the region of 300-600 nm in N,N-dimethylformamide. Favorable molar extinction coefficients at 392 nm (ε 392nm = 1670 M −1 cm −1 ) and 583 nm (ε 583nm = 440 M −1 cm −1 ) were observed. The red-shifted band (~583 nm) disappeared when triethylamine was added to the solution, which could be attributed to the intramolecular or intermolecular hydrogen bond in TX-NPG solution. This peculiar absorption was also reported in other TX derivatives, such as thioxanthone carboxylic acid and sodium fluorenecarboxylatethioxanthone [115,125]. Favorable absorption properties made TX-NPG attractive as a visible PI. TX-NPG was investigated as a Type II PI in the photopolymerization experiments under irradiation with 392, 473, 532, and 635 nm. In the presence of TX-NPG alone, the function conversions of acrylate monomers under irradiation at 392, 473, 532, and 635 nm were 63%, 21%, 24% and 14%, respectively. This was attributed to the H-abstraction reaction in a one-component system. The addition of MDEA as a hydrogen donor contributed to the H-abstraction reaction, and higher final function conversions were obtained. The performance of TX-NPG demonstrated the possibility of its use under panchromatic irradiation. In addition, several TX derivatives bearing abstractable hydrogen sites (amine group) were also designed as one-component PIs [126][127][128].
To explore the relationships between structure and efficiency, the singlet and triplet states of TX derivatives were detected. The results showed that a thioxanthone triplet state was found in TX-2CBZ and ITX structures, and the lifetime were about 1.0 µs and 5.8 µs, respectively. TX-2CBZ demonstrated strong H-abstraction ability due to the TX moiety in structure, while no significant H-abstraction was observed for TX-2DPA and TX-2PTZ. It could possibly be ascribed to the internal conversion as a deactivation pathway of the excited state, which resulted in the slow reaction with EDB. The TX-2CBZ/Iod system also exhibited good performance in the CP of EPOX (FC = 59%). In the 3D-printing experiments, the pattern was successfully fabricated using a three-component TX-2CBZ/Iod/EDB system with TMPTA/EPOX blend. The PI TX-2CBZ, which had a similar performance to ITX, was applied in 3D printing [130]. structure, while no significant H-abstraction was observed for TX-2DPA and TX-2PTZ. It could possibly be ascribed to the internal conversion as a deactivation pathway of the excited state, which resulted in the slow reaction with EDB. The TX-2CBZ/Iod system also exhibited good performance in the CP of EPOX (FC = 59%). In the 3D-printing experiments, the pattern was successfully fabricated using a three-component TX-2CBZ/Iod/EDB system with TMPTA/EPOX blend. The PI TX-2CBZ, which had a similar performance to ITX, was applied in 3D printing [130]. TX λ max~3 80 ε max~5 300 [131] structure, while no significant H-abstraction was observed for TX-2DPA and TX-2PTZ. It could possibly be ascribed to the internal conversion as a deactivation pathway of the excited state, which resulted in the slow reaction with EDB. The TX-2CBZ/Iod system also exhibited good performance in the CP of EPOX (FC = 59%). In the 3D-printing experiments, the pattern was successfully fabricated using a three-component TX-2CBZ/Iod/EDB system with TMPTA/EPOX blend. The PI TX-2CBZ, which had a similar performance to ITX, was applied in 3D printing [130]. ITX λ max~3 86 ε max~6 500 ε 395nm~3 900 [132] could possibly be ascribed to the internal conversion as a deactivation pathway of the excited state, which resulted in the slow reaction with EDB. The TX-2CBZ/Iod system also exhibited good performance in the CP of EPOX (FC = 59%). In the 3D-printing experiments, the pattern was successfully fabricated using a three-component TX-2CBZ/Iod/EDB system with TMPTA/EPOX blend. The PI TX-2CBZ, which had a similar performance to ITX, was applied in 3D printing [130]. TX-C λ max~4 34 ε max~2 010 [118,119] could possibly be ascribed to the internal conversion as a deactivation pathway of the excited state, which resulted in the slow reaction with EDB. The TX-2CBZ/Iod system also exhibited good performance in the CP of EPOX (FC = 59%). In the 3D-printing experiments, the pattern was successfully fabricated using a three-component TX-2CBZ/Iod/EDB system with TMPTA/EPOX blend. The PI TX-2CBZ, which had a similar performance to ITX, was applied in 3D printing [130].

Type Ⅰ Photoinitiators
Type Ⅰ PIs are used widely in industry and research laboratories. Oxime esters, acylphosphine oxides, and amino ketones are commonly used in photopolymerization.

Type Ⅰ Photoinitiators
Type Ⅰ PIs are used widely in industry and research laboratories. Oxime esters, acylphosphine oxides, and amino ketones are commonly used in photopolymerization.

Type Ⅰ Photoinitiators
Type Ⅰ PIs are used widely in industry and research laboratories. Oxime esters, acylphosphine oxides, and amino ketones are commonly used in photopolymerization.

Type I Photoinitiators
Type I PIs are used widely in industry and research laboratories. Oxime esters, acylphosphine oxides, and amino ketones are commonly used in photopolymerization. However, except for several commercial PIs, such as diphenyl(2,4,6-trimethylbenzoyl) phosphine oxide (TPO) and 1-benzyl-1-(dimethylamino)propyl 4-morpholinophenyl ketone (369), most of Type I PIs do not absorb light above 400 nm. Therefore, it is important to improve the absorption ability of Type I PIs to match the emission spectra of longwavelength LEDs. Herein, oxime esters and acylphosphine oxides are mainly summarized in this review.

Oxime Ester Photoinitiators
Oxime esters have been investigated widely as Type I PIs due to their high photoactivity [133,134]. Commercial oxime esters, OXE 01 and OXE 02, have been used to successfully produce thin films in color filter resists [135]. Under irradiation, the N−O bond in the oxime ester structure can break to produce iminyl and acyloxy radicals. The decarboxylation reaction occurs in the acyloxy radical to produce CO 2 and in another active radical that can induce free radical polymerization. As the OXE 01 and OXE 02 can absorb UV light only, they perform poorly under visible light. Therefore, the design of novel oxime esters which can be used under visible LEDs is important. The chemical structures of oxime ester PIs mentioned in this review are shown in Table 8. Due to the different structures and substituents, the presented oxime esters exhibited very different light absorption properties, as shown in their maximal absorption wavelengths (λ max in Table 8).
A series of oxime ester PIs based on the coumarin chromophore were synthesized by Li et al. [136]. They were designed to study the substituent and electronic effects. These PIs exhibited strong absorption, and the λ max of O-3 and O-4 were 436 nm (ε 436nm = 41,690 M −1 cm −1 ) and 433 nm (ε 433nm = 7680 M −1 cm −1 ), respectively. Compared to O-4, O-3 demonstrated a dramatically increased molar extinction coefficient, which could be ascribed to the substitution position of the oxime-ester moiety. Stronger absorption of O-3 could be ascribed to the planar conformation and increased degree of conjugation [137]. The λ max of O-3F and O-3O were all 436 nm. The photoinitiation ability of the PIs was investigated under a LED at 450 nm. O-3 demonstrated the best performance among them due to its strong absorption. Interestingly, both high-thiol and vinyl doublebond conversions were found using O-3 in thiol-based click polymerization. O-3 exhibit photobleaching property, and the curing depth was 2.6 mm within 10 min irradiation upon exposure to LED at 450 nm (200 mW/cm 2 ). Indeed, the colorless photoreaction products allowed the light to penetrate deeper into the formulation. In addition, some oxime ester PIs based on coumarin chromophores were investigated and applied in 3D printing [138,139].
Hammoud et al. [140] designed some oxime esters based on the coumarin scaffold. All the chemical structures exhibited favorable molar extinction coefficients at 405 nm (i.e., OXE-D: ε 405nm = 22,500 M −1 cm −1 ; OXE-J: ε 405nm = 25,000 M −1 cm −1 ). The Type I photoinitiation behaviors of the oxime esters were investigated upon exposure to LED at 405 nm in the FRP of TMPTA. OXE-J and OXE-D exhibited better initiation performances than the others, and the function conversions of TMPTA were 72% and 73%, respectively. According to computational calculations, the enthalpy value of the decarboxylation reaction and the cleavage process for the N-O bond was energetically favorable for OXE-D. In addition, the highest spin density of the methyl radical contributed to the good reactivity of OXE-D in polymerization experiments. Finally, a 3D-printed object was successfully obtained using an OXE-D/Iod system in acrylate monomers.
Two arylaminocarbazole oxime ester PIs (OXE1 and OXE2) were designed by Ma et al. [141]. In addition to Type I PIs, OXE1 and OXE2 could also play the role of photosensitizer in multicomponent systems. OXE1 and OXE2 had wide absorption ranges at 200~450 nm. Under irradiation at 405 nm, the absorbance of OXE1 and OXE2 decreased to a certain extent. The results indicated the generation of stable photolysis products. When iodonium salt was added, the photolysis rate of the OXE1/iodonium salt system was faster than that of OXE1 alone. It suggested that the interaction of OXE1/iodonium salt was quick and efficient. The favorable values of free energy changes for OXE1/iodonium salt and OXE2/iodonium salt systems were obtained. In addition, the phenyl radical was detected in OXE1/iodonium salt system by spin-trapping ESR experiments. The FRP of TPGDA was studied upon exposure to the laser diode at 405 nm. TPGDA polymerized because of the oxime ester moiety in these structures. Higher function conversions were found using OXEs/iodonium salt (0.2%/1%, w/w). The photoinitiation performance was in line with the results of photolysis and the ESR experiments. The polymerization of epichlorohydrin was evaluated using OXEs/iodonium salt systems, and favorable function conversions were obtained. Indeed, the OXEs/iodonium salt systems could generate cations through electron transfer reactions to induce epoxide ring-opening polymerization. In conclusion, the arylaminocarbazole oxime esters broaden the application of oxime esters in visible light photopolymerization.
Ding et al. [142] designed two oxime esters named E-FBOXEs. The FRP of TPGDA was investigated upon exposure to LED at 395 nm. High function conversions of 81% and 80% were obtained using E-FBOXE-Me and E-FBOXE-ph, respectively. Interestingly, photochromism of the polymers prepared by E-FBOXEs was found under heating. After polymerization, a brown PTPGDA film was obtained using E-FBOXE-Me. The brown turned colorless when the film was heated at 50 • C. The photochromic mechanism was investigated by ESR and FTIR spectra. The results demonstrated that the N−O bond in E-FBOXE-Me molecules underwent cleavage under LED at 395 nm irradiation. Then, under heating, the generated acetoxy and colorful iminyl radicals could recombine to generate neutral E-FBOXE-Me structures. This special photochemical mechanism of E-FBOXEs makes it possible to design photochromic materials.
Four oxime esters based on carbazole-coumarin fused subunit were designed by Zhou et al. [143]. All the oxime esters exhibit similar absorption spectra with the maximum absorption wavelength λ max = 374 nm. The absorbance of OXE-EM decreased gradually under LED at 365 nm irradiation. Meanwhile, this process was also monitored through 1 H NMR. The results demonstrated the dissociation of the N-O bond. In addition, methyl radical was detected in spin-trapping ESR experiments. The FRP of TMPTA was evaluated by Photo-DSC. Under LED at 365, 385 and 405 nm irradiation, the photoinitiation ability of the oxime esters followed the order OXE-EM > OXE-IM > OXE-EP > OXE-IP. It was interesting that these PIs demonstrated better performance under LED at 405 nm than LED at 365 nm, although the molar extinction coefficients at 365 nm were higher. When irradiated at 365 or 405 nm, the photolysis behavior of OXE-EM was similar. A wavelengthdependent photopolymerization mechanism was proposed in this work. In addition, stilbene-based, phenyl thienyl thioether-based, and bicarbazole-based oxime ester PIs were also reported by Jin's group [144][145][146].

Acylphosphine Oxide Photoinitiators
Acylphosphine oxides are another class of Type Ⅰ PI. They are widely used in many fields due to their high efficiency and good photobleaching. As the absorption of most

Acylphosphine Oxide Photoinitiators
Acylphosphine oxides are another class of Type Ⅰ PI. They are widely used in many fields due to their high efficiency and good photobleaching. As the absorption of most

Acylphosphine Oxide Photoinitiators
Acylphosphine oxides are another class of Type I PI. They are widely used in many fields due to their high efficiency and good photobleaching. As the absorption of most acylphosphine oxide PIs is located in the UV range, it is important to broaden their absorption of them in the visible range to match the emission spectra of LEDs. The chemical structures of acylphosphine oxide PIs mentioned in this review are shown in Table 9.
A series of acylphosphine oxide compounds were proposed by Dietlin et al. [149]. Before synthesis, molecular modeling was used to select the potentially reactive compounds. The maximum absorption wavelength was computed to match the selected LEDs. The energy of the triplet state (E T ), as well as the bond dissociation energy (BDE), were computed to explore whether the cleavage of the bond was energetically favorable (⊗H < 0). The spin density on the radical center was computed to ensure the efficient addition of the double bond; 7 molecules were selected from 86 molecules based on favorable calculated parameters. The molar extinction coefficients at 395 nm of acylphosphine oxide compounds (except ADPO-6 and ADPO-7) were higher than that of TPO-L. The FRP of TMPTA was performed under LED at 395 nm irradiation using (1 wt%). All the photoinitiators (except ADPO-5) demonstrated higher final function conversions than commercial TPO-L and BAPO. Although ADPO-5 had good absorption properties, the cleavage of the bond took place with difficulty. The rational design of acylphosphine oxide compounds is helpful in selecting an efficient PI to use in LED photopolymerization.
An acylphosphine oxide PI 4-(diethylamino)benzoyldiphenylphosphine oxide (DEAPO) was designed and synthesized by Xie et al. [150]. Compared to TPO (λ max = 380 nm), a red-shifted maximum absorption wavelength was obtained for DEAPO (λ max = 386 nm). Interestingly, the absorption band of DEAPO extended to 440 nm and high molar extinction coefficients of DEAPO was obtained (ε 385nm = 43,800 M −1 cm −1 ; ε 420nm = 5950 M −1 cm −1 ). The good absorption property was ascribed to the diethyl amino moiety in the DEAPO structure (prolonging the conjugation system). DEAPO was evaluated as a Type I PI with TMPTA. Upon exposure to LED at 385 nm, the function conversion of the DEAPO system (FC = 68.7%) was higher than the TPO system (FC = 58.2%). In addition, the DEAPO system (FC = 64.3%) demonstrated better performance than the TPO system (FC = 47.1%) under LED at 420 nm irradiation. Indeed, good absorption properties for DEAPO allowed the efficient initiation ability under LEDs. The results demonstrated that DEAPO has the potential to be applied in the field of dental materials or food packaging.
Two carbazolyl-based acylphosphine oxide compounds (ETPO and ALPO) were synthesized by Wu et al. [151]. Favorable molar extinction coefficients were observed for ETPO (ε 405nm = 2270 M −1 cm −1 ) and ALPO (ε 405nm = 1300 M −1 cm −1 ), which could be attributed to the large rigid plane and the strong conjugate system in carbazole moiety. In steady-state photolysis experiments, the absorbance peak of ETPO and ALPO decreased dramatically under LED at 395 nm irradiation, which exhibit high photoactivity for the two compounds. The FRP of TMPTA (~40 µm) was studied upon exposure to LED at 405 nm. Acrylate function conversions for monomers were 44.7%, 75.7%, and 56.7% using ETPO, ALPO and TPO (1 wt%), respectively. Due to the bad solubility in monomers, the efficiency of ETPO in TMPTA was low. ALPO demonstrated better performance than TPO due to its high photoactivity and good absorption properties. ALPO can be used as a visible PI in many fields.

Other Type I photoinitiators
An acylstannane-based PI tetrakis(2,4,6-trimethylbenzoyl)stannane (see Table 10) was designed for visible light photopolymerization [152]. Acylstannanes could show Type I PIs features like those in acylgermanes [153][154][155]. The absorption band of this acylstannane can extend to 550 nm. In steady-state photolysis, fast photobleaching was observed for the acylstannane (1 × 10 −3 mol/L in acetonitrile) with a LED at 460 nm (1 W/cm 2 ) after 3 min. It was attributed to the cleavage of the Sn-CO bond. The photoinitiation ability was studied under LED at 460 and LED at 522 nm. Upon exposure to a LED at 460 nm, tetrakis(2,4,6-trimethylbenzoyl)stannane demonstrated a similar performance with Ivocerin ® , and high acrylate conversion was found. In addition, the acylstannane still showed high reactivity under LED at 522 nm. Interesting, favorable curing depths were obtained in the presence of this acylstannane-based PI. In prospect, it can be applied in many industrial fields.

Other Type I photoinitiators
An acylstannane-based PI tetrakis(2,4,6-trimethylbenzoyl)stannane (see Table 10) was designed for visible light photopolymerization [152]. Acylstannanes could show Type I PIs features like those in acylgermanes [153][154][155]. The absorption band of this acylstannane can extend to 550 nm. In steady-state photolysis, fast photobleaching was observed for the acylstannane (1 × 10 −3 mol/L in acetonitrile) with a LED at 460 nm (1 W/cm 2 ) after 3 min. It was attributed to the cleavage of the Sn-CO bond. The photoinitiation ability was studied under LED at 460 and LED at 522 nm. Upon exposure to a LED at 460 nm, tetrakis(2,4,6trimethylbenzoyl)stannane demonstrated a similar performance with Ivocerin ® , and high acrylate conversion was found. In addition, the acylstannane still showed high reactivity under LED at 522 nm. Interesting, favorable curing depths were obtained in the presence of this acylstannane-based PI. In prospect, it can be applied in many industrial fields.
Some N-hydroxynaphthalimide ester derivatives (namely NPIE1-NPIE9, see Table 10) are proposed as Type I PIs [156]. They demonstrated good light absorption properties, such as ε 405nm (NPIE1) = 15,000 M −1 cm −1 and ε 405nm (NPIE2) = 14,400 M −1 cm −1 . Interestingly, these PIs demonstrated a favorable performance for the FRP of the monomers. NPIE1 (FC = 68%) demonstrated better performance than benchmark structure TPO (FC = 66%) in polymerization experiments of TMPTA. A decarboxylation process was discovered for these structures. The mechanisms N-hydroxynaphthalimide ester derivatives were investigated using a computational procedure, steady-state photolysis, and fluorescence approaches. Finally, the cleavage mechanism (N−O bond) of the Type I PI was proposed.

Conclusions and Perspectives
In the past few years, photoinitiators for LED photopolymerization have received increasing attention. An increasing number of organic dyes have been used in photoinitiating systems due to their good light absorption properties. Many chemical structures demonstrate good performance in FRP and CP under LED irradiation. The modification for traditional Type I and Type II photoinitiators have also been carried out frequently to

Conclusions and Perspectives
In the past few years, photoinitiators for LED photopolymerization have received increasing attention. An increasing number of organic dyes have been used in photoinitiating systems due to their good light absorption properties. Many chemical structures demonstrate good performance in FRP and CP under LED irradiation. The modification for traditional Type I and Type II photoinitiators have also been carried out frequently to NPIE9 λ max~3 97 ε max~1 4,900 ε 405nm~1 4,000 [156]

Conclusions and Perspectives
In the past few years, photoinitiators for LED photopolymerization have received increasing attention. An increasing number of organic dyes have been used in photoinitiating systems due to their good light absorption properties. Many chemical structures demonstrate good performance in FRP and CP under LED irradiation. The modification for traditional Type I and Type II photoinitiators have also been carried out frequently to expand the range of their applications. For the development of photoinitiators, besides light absorption properties, synthesis procedures, toxicity, and cost should also be taken into account. All the presented PIs remain on the lab scale even if industrial development can be considered. In the future, more efforts should be devoted to addressing biocompatibility, which can provide significant opportunities for photoinitiators in the field of biomaterials and biomedicine. In addition, it is also desirable and crucial to resolving the yellow coloration induced by some photoinitiators during the photopolymerization. Some scaffolds with photo-bleaching characteristics are a potential option for the design of photoinitiators with a favorable curing depth.
Author Contributions: Conceptualization, all authors; validation, all authors; resources, J.L. and P.X.; writing-original draft, S.L.; writing-review and editing, all authors; supervision, J.L. and P.X.; project administration, J.L. and P.X.; funding acquisition, P.X. and J.L. All authors have read and agreed to the published version of the manuscript.

Institutional Review Board Statement: Not applicable.
Informed Consent Statement: Not applicable.

Data Availability Statement:
The data presented in this study are available on request from the corresponding author.

Conflicts of Interest:
The authors declare no conflict of interest.