Effect of the Application of a Coating Native Potato Starch/Nopal Mucilage/Pectin on Physicochemical and Physiological Properties during Storage of Fuerte and Hass Avocado (Persea americana)

The avocado fruit is an agro-industrial product with high export demand in Peru due to its sensory and nutritional qualities, which can be affected during storage. The study aimed to evaluate the effect of the application of a coating formulated with potato starch (Solanum tuberosum ssp andigena), nopal mucilage (Opuntia ficus indica), and pectin on the physicochemical and physiological properties during the storage of Fuerte and Hass avocados. Samples were taken in their harvest state from the plantation in “Occobamba”, which is cultivated by the Avocado Producers Association in Chincheros, Apurímac, Peru. Physicochemical properties (titratable acidity, pH, total soluble solids) and physiological properties (weight loss, firmness, and color L* a* b*) were determined during 20 days of storage at 20 °C. The elaborated films present high transparency and low aw values. In the coated avocado of the Hass and Fuerte varieties, acidity and total soluble solids decreased significantly (p-value < 0.05) during the storage time. Weight loss and firmness of coated fruits decrease to a lesser extent. Luminosity L*, color index, and color variation showed better attributes for the coated samples. The use of coatings made with potato starch, nopal mucilage, and pectin allows the physicochemical and physiological properties of avocado fruits to be maintained for a longer time during storage.


Vegetal Material
The avocado fruits (Persea americana) of the Hass and Fuerte varieties in the state of harvest maturity with uniform pigmentation and without physical and biological damage were collected from the fields in "Ocobamba" of the Avocado Producers Association. With the coordinates: Latitude −13.483056 • and Longitude −73.561111 • at 3032 m altitude, from the Province of Chincheros, Apurímac, Peru.
The emulsions were prepared by adding the components (Table 1), taking as reference the formulations proposed by Choque-Quispe et al. [34], in the following order: potato starch solution (PS), nopal mucilage solution (NM), and citrus pectin grade 65 (PC) (Spectrum, New Brunswick, Canada), under continuous stirring until complete homogenization, then heated to 70 • C, and glycerol (G) (99.5%, Scharlau, Barcelona, Spain) under continuous agitation. The emulsion was allowed to cool in the environment until its application to the avocado fruits.

Determination of Transparency and Water Activity of Coatings
The emulsions were molded on glass plates at room temperature for 24 h, obtaining coating films. The films were conditioned in a quartz vial with a rectangular side, and the transmittance was read at 600 nm in a Thermo Fisher UV-Vis spectrophotometer, model Genesys 150 (Madison, WI, USA) [35]. Transparency was reported as the ratio between transmittance and thickness (nm/mm).

IR Analysis of the Coating
Tablets were prepared with 0.1% KBr (grade IR, Darmstadt, Germany). The readings were made in transmission mode in the FTIR spectrometer (Fourier transform infrared spectroscopy), Thermo Fisher, Nicolet IS50 model (Waltham, MA, USA), in a range of 4000 to 400 cm −1 with a resolution of 4 cm −1 .

Thermal Analysis of the Coating
The thermal transition properties of the coatings were analyzed through a differential scanning calorimeter (DSC), TA Instruments brand, model DSC2500 (Waters TM, New Castle, DE, USA), under a nitrogen atmosphere (50 mL/min). Samples were sealed in an aluminum pan and scanned from 20 to 200 • C at a heating rate of 5 • C/min. The equipment was stabilized through a baseline run at analysis conditions for 1 h.
A thermogravimetric analysis (TGA) was applied to know the thermal stability of the coating. The samples were loaded in alumina crucibles, and taken to a TA Instruments brand equipment, model TGA550 (Waters TM, New Castle, DE, USA), in the range of 20 to 200 • C, heating rate of 10 • C/min, and nitrogen supply of 50 mL/min.

Coating Application
The emulsion was applied to avocado fruits of the Hass and Fuerte varieties through a conventional atomizer, verifying that the entire surface was covered, and it was allowed to dry at room temperature. Likewise, fruits without coating were considered as control of both varieties.

Determination of Physicochemical Properties
The titratable acidity of the pulp was determined as a percentage of citric acid, the pH, and total soluble solids of the coated avocado samples every two days, for 20 days at 20 • C of storage, according to the methodologies proposed by the AOAC [40].

Determination of Physiological Properties
Weight loss during storage was determined and expressed as a percent weight difference. Fruit firmness was measured in different parts of the fruit using a penetrometer [41].
The color characteristics of avocado peel during storage were measured using the Kónica-Minolta colorimeter, model CR-5 (Japan), luminosity L* was determined (0 = black and 100 = white), chroma a* (+a = red, −a = green), chroma b* (+b = yellow and −b = blue). The measurements were taken at previously defined points, and the average of the values was recorded [28,42].
Likewise, the color index (CI*) (Equation (1)) was determined, which allows color to be expressed in a single numerical data [43], whose interpretation is as follows:

•
If CI* −40 to −20, colors range from blue-violet to deep green.

•
If CI* −20 to −2, colors range from deep green to yellowish-green.

•
If CI* +2 to +20, colors range from pale yellow to deep orange.

•
If CI* +20 to +40, colors range from deep orange to deep red.
In the same way, the color difference (∆E*) was calculated with respect to the control sample (Equation (2)) [35].

Statistical Analysis
A randomized complete block design was applied, and data were collected in triplicate and analyzed by two-factor ANOVA and Tukey's multiple comparison at 5% significance through Statistica V12 software, demo mode.

Coating Characteristics
Film transparency is a very important sensory aspect during fruit coating [13,45]. Transmittance values of around 81% were reported for the elaborated coatings (p-value > 0.05) ( Table 2). Values above 90% are considered transparent [35,46], suggesting that the films prepared could be considered suitable for avocado coating, whose transparency values are 6.939 and 7.332 nm/mm, being slightly higher for formulation F2 (p-value < 0.05). Where: x , arithmetic mean; SD, standard deviation; CV, coefficient of variability.
The water activity (a w ) allows us to indirectly know the hygroscopic capacity of the films due to the presence of active receptor sites for water molecules on their surface. In the same way, it allows to take criteria of microbiological aspects [42,47,48]. It was observed that the film with formulation F2 reported a w 0.404 ± 0.05 slightly lower than F1 (p-value < 0.05), that is, it would retain less water due to the lower presence of hydrophilic groups, preventing the water diffusion due to the film barrier [13,49,50], this would be due to the lower presence of pectin in the formulation.
IR analysis revealed high-intensity peaks around 3350 cm −1 , being higher for the F2 film ( Figure 1). This is attributed to the presence of hydroxyl groups of carbohydrates and gums (basis of the structure of starch, nopal mucilage, and pectin) [37][38][39], which would allow it to retain higher moisture content. The spectrum around 2930 cm −1 is due to the stretching vibration of the carbohydrate methyl group. A small peak around 1640 cm −1 shows the presence of water adsorbed on the film, being slightly higher in F2, which confirms its ability to retain water on its surface, making it a slightly permeable material. Peaks around 1415, 1038, and 922 cm −1 evidence the presence of carboxyl, carbonyl, and methyl groups from polysaccharides and carbohydrates [34,37,39,50].

Transparency
(nm/mm) 6.939 ± 0.276 3.971 7.332 ± 0 Where: ̅ , arithmetic mean; SD, standard deviation; CV, coefficient of v The water activity (aw) allows us to indirectly know the hy films due to the presence of active receptor sites for water mole the same way, it allows to take criteria of microbiological aspe served that the film with formulation F2 reported aw 0.404 ± 0.05 value < 0.05), that is, it would retain less water due to the lower groups, preventing the water diffusion due to the film barrier due to the lower presence of pectin in the formulation.
IR analysis revealed high-intensity peaks around 3350 cm −1 film ( Figure 1). This is attributed to the presence of hydroxyl grou gums (basis of the structure of starch, nopal mucilage, and pect allow it to retain higher moisture content. The spectrum around stretching vibration of the carbohydrate methyl group. A smal shows the presence of water adsorbed on the film, being slightly firms its ability to retain water on its surface, making it a slig Peaks around 1415, 1038, and 922 cm −1 evidence the presence of methyl groups from polysaccharides and carbohydrates [34,37,3  The coatings must have good flexibility, and this is achiev plasticizers such as glycerin. The low values of the glass trans high flexibility, such as those found in the elaborated polymers around 29 °C (Figure 2a), with endothermic peaks and similar b they have the same glycerol content [49]. In the same way, i The coatings must have good flexibility, and this is achieved with the addition of plasticizers such as glycerin. The low values of the glass transition temperatures show high flexibility, such as those found in the elaborated polymers (F1 and F2), with values around 29 • C (Figure 2a), with endothermic peaks and similar behavior. This is because they have the same glycerol content [49]. In the same way, it was observed that the gelatinization temperature was around 159.4 • C for both polymers, although, with a slightly higher gelatinization enthalpy for F1 (11.14 J/g). This is due to the higher content of pectin, which presents a greater number of branches in its structure than starch [34,37,49]. [34,37,49].
The TGA study showed that both F1 and F2 polymers retain moisture at around °C, which means an average mass loss of 13.6% (Figure 2b). Likewise, it was observed about 94.4% of the material used as a coating in the avocado is organic matter, so it ca considered a biodegradable material, and this behavior is similar for polymers of thi ture [20,34,35,37].

Acidity
Acidity is slightly higher for the coated and control of the Hass variety, while fo Fuerte variety, it reported 5.88, 4.71, and 4.94 for the control, F1, and F2, respectively ble 3). It was observed that the reported acidity for the Hass variety during storage wa decreased for the control sample (Figure 3a), while the F1 coating it was higher. In same way, a considerable decrease was observed between days 6 to 12 for F1 and F spectively. For the Fuerte variety, a similar decrease occurred in the control and co samples, although a strong drop occurred around day 6 ( Figure 3c). This behavior is acteristic of fruits and vegetables due to the metabolic rate and coincides with the b ning of maturation and sugar accumulation [51].
The fact of acidity decrease is due to the activity of dehydrogenases, which be as substrates for the synthesis of new products during maturation, generating hi The TGA study showed that both F1 and F2 polymers retain moisture at around 110 • C, which means an average mass loss of 13.6% ( Figure 2b). Likewise, it was observed that about 94.4% of the material used as a coating in the avocado is organic matter, so it can be considered a biodegradable material, and this behavior is similar for polymers of this nature [20,34,35,37].

Acidity
Acidity is slightly higher for the coated and control of the Hass variety, while for the Fuerte variety, it reported 5.88, 4.71, and 4.94 for the control, F1, and F2, respectively (Table 3). Where: x , arithmetic mean; SD, standard deviation; CV, coefficient of variability. * p-value per treatment, ** p-value per treatment comparison, *** p-value per day of maturation within treatments, **** For n = 3.
It was observed that the reported acidity for the Hass variety during storage was less decreased for the control sample (Figure 3a), while the F1 coating it was higher. In the same way, a considerable decrease was observed between days 6 to 12 for F1 and F2, respectively. For the Fuerte variety, a similar decrease occurred in the control and coated samples, although a strong drop occurred around day 6 ( Figure 3c). This behavior is characteristic of fruits and vegetables due to the metabolic rate and coincides with the beginning of maturation and sugar accumulation [51].
sugar content and volatile substances, which give better sensory characteristics to co avocados [2,52].
The addition of potato starch in the formulation of the coating allows the redu of avocado acidity for both varieties (Figure 3b,d), due to the fact that it would achi greater impermeable capacity to gases and humidity.

pH
It was observed that the pH values for the two varieties showed significant varia during the maturation time (p-value < 0.05) (Figure 4a,c). However, the mean val slightly similar for the coated samples of both varieties (Table 4), indicating that the ing allows for the preservation of the pH of the fruits, this being a usual behavio coated avocado [1,53]. This behavior is due to the fact that during the maturation stage, the pH incr due to the development of acidic substances, and once the maximum point of matur is reached, these tend to decrease due to the fact that they are consumed in the meta The fact of acidity decrease is due to the activity of dehydrogenases, which behave as substrates for the synthesis of new products during maturation, generating higher sugar content and volatile substances, which give better sensory characteristics to coated avocados [2,52].
The addition of potato starch in the formulation of the coating allows the reduction of avocado acidity for both varieties (Figure 3b,d), due to the fact that it would achieve a greater impermeable capacity to gases and humidity.

pH
It was observed that the pH values for the two varieties showed significant variations during the maturation time (p-value < 0.05) (Figure 4a,c). However, the mean value is slightly similar for the coated samples of both varieties (Table 4), indicating that the coating allows for the preservation of the pH of the fruits, this being a usual behavior for coated avocado [1,53]. This behavior is due to the fact that during the maturation stage, the pH increases due to the development of acidic substances, and once the maximum point of maturation is reached, these tend to decrease due to the fact that they are consumed in the metabolic processes. They also act as precursors of volatile substances in avocado, so the pH tends to neutrality [41,54].
On the other hand, increasing the addition of potato starch in the formulation of the coatings allows the pH of the avocado fruits of the two varieties to increase slightly (Figure 4b,d).

Soluble Solids
Regarding soluble solids, the Hass variety showed a higher value on days 4 to 10 (Figure 5a), and the control sample showed the opposite behavior (p-value < 0.05), with values around 7.0 • Brix (Table 5), which is characteristic of the Hass variety [1,38]. processes. They also act as precursors of volatile substances in avocado, so the pH tends to neutrality [41,54].
On the other hand, increasing the addition of potato starch in the formulation of the coatings allows the pH of the avocado fruits of the two varieties to increase slightly ( Figure  4b,d).

Soluble Solids
Regarding soluble solids, the Hass variety showed a higher value on days 4 to 10 (Figure 5a), and the control sample showed the opposite behavior (p-value < 0.05), with values around 7.0 °Brix (Table 5), which is characteristic of the Hass variety [1,38]. Where: ̅ , arithmetic mean; SD, standard deviation; CV, coefficient of variability. * p-value per treatment, ** p-value per treatment comparison, *** p-value per day of maturation within treatments, **** For n = 3.  Where: x , arithmetic mean; SD, standard deviation; CV, coefficient of variability. * p-value per treatment, ** p-value per treatment comparison, *** p-value per day of maturation within treatments, **** For n = 3. Regarding the Fuerte variety, the coated samples showed similar behavior during the storage time (p-value = 0.928), decreasing the soluble solids rapidly during the first 8 days of storage, and thereafter there is a slight variation reaching values around 4 °Brix (Figure 5c). In fact, the F2 coating shows lower values of soluble solids. This is due to the plasticizing effect of starch (Figure 5b,d), which prevents water loss, which favors maturation, increasing the concentration of sugars due to the phenomenon of respiration of this  Where: x , arithmetic mean; SD, standard deviation; CV, coefficient of variability. * p-value per treatment, ** p-value per treatment comparison, *** p-value per day of maturation within treatments, **** For n = 3.
Regarding the Fuerte variety, the coated samples showed similar behavior during the storage time (p-value = 0.928), decreasing the soluble solids rapidly during the first 8 days of storage, and thereafter there is a slight variation reaching values around 4 • Brix (Figure 5c). In fact, the F2 coating shows lower values of soluble solids. This is due to the plasticizing effect of starch (Figure 5b,d), which prevents water loss, which favors maturation, increasing the concentration of sugars due to the phenomenon of respiration of this climacteric fruit [54,55].
The variation of soluble solids in avocado fruit would be involved in the enzymatic activity of alpha and beta-amylase, which hydrolyze starches to simple sugars [32]. The Hass variety would present a higher carbohydrate content because the soluble solids increase between days 4 and 10 (Figure 5a), while the Fuerte variety does not show this behavior. On the contrary, it decreases, confirming the higher matter fat content [53].

Avocado Weight Loss
During storage, the weight of coated and control avocado fruits decreased significantly for both varieties (p-value < 0.05). The F2 formulation reported less loss, 5.19% and 3.79% for the Hass and Fuerte varieties, respectively (Table 6). Weight loss in both varieties manifests itself in an increasing way until day 14. Although the first two days are slower (Figure 6a,c). Where: x , arithmetic mean; SD, standard deviation; CV, coefficient of variability. * p-value per treatment, ** p-value per treatment comparison, *** p-value per day of maturation within treatments, **** For n = 3.
Likewise, it was observed that the increase in starch in the formulations does not considerably influence the weight loss for both coated varieties (Figure 6b,d). This indicates that the starch offers good impermeability to water, offering a better barrier. ment, ** p-value per treatment comparison, *** p-value per day of maturation within treatm For n = 3.
Likewise, it was observed that the increase in starch in the formulations considerably influence the weight loss for both coated varieties (Figure 6b,d). T cates that the starch offers good impermeability to water, offering a better barrie Weight loss during storage is mainly due to moisture loss, which is due to t vapor pressure gradient between the fruit and the environment as well as cellular and physiological processes in the fruit [15,18,35,38]. However, this loss can be through the use of barriers such as films, which would prevent transpiration, an change of gases in the fruit with the environment [18,52], although they could be by the environmental temperature and relative humidity [28,56].
Weight loss becomes an economic loss, which considerably affects produc keters, and exporters, reaching, in many cases, up to 60% of the total weight, an accompanied by the loss of sensory quality [23,57,58]. Weight loss during storage is mainly due to moisture loss, which is due to the water vapor pressure gradient between the fruit and the environment as well as cellular activity, and physiological processes in the fruit [15,18,35,38]. However, this loss can be lessened through the use of barriers such as films, which would prevent transpiration, and the exchange of gases in the fruit with the environment [18,52], although they could be affected by the environmental temperature and relative humidity [28,56].
Weight loss becomes an economic loss, which considerably affects producers, marketers, and exporters, reaching, in many cases, up to 60% of the total weight, and this is accompanied by the loss of sensory quality [23,57,58].

Avocado Color
It was observed that the luminosity L*, for the control decreases considerably (p-value < 0.05), with a tendency to gray. In the coated samples, F1 and F2, there was less of a decrease reported at day 20 (Table 7). This would be due to the fact that the coating gives greater brightness to the fruits.
Chroma a* for the Fuerte variety increased with a similar trend for the control and the coated varieties (Table 7), acquiring a greater shade of dark green during storage time, while chroma b* decreased slightly for the control sample.
As for the Hass variety, L* decreases considerably for the control sample after 20 days of storage to values of 6.00, while for F1 and F2 it decreased from 29.80 to 9.10 and from 29.70 to 7.47 ( Table 8). The chroma a* increases for the control sample from −15.77 to 1.63. In the same way, it occurs for the coated samples, that is, a considerable change from green to a red trend. Where: x , arithmetic mean; SD, standard deviation; CV, coefficient of variability. * Different letters indicate significant difference, evaluated through Tukey's test at 5% significance.
Negative a* values indicate a green tonality trend, and it is associated with the presence of chlorophyll b (3-methyl group). An increase in this parameter would indicate degradation due to enzymatic action, producing phytol and chlorophyllide [10,30,59,60]. This is manifested in both varieties, although with greater emphasis on the Hass variety (Tables 7 and 8). This is a characteristic behavior for this coated and natural variety [26,28,35,36,52,61].
Chroma b* decreases considerably for both varieties, control and coated, and is associated with the presence of chlorophyll A with a blue tonality (3-formyl group), and at storage this tonality is attenuated [27,59,61]. At the same time, carotenoid pigments are synthesized and degraded, giving the fruit that dark coloration [18,62,63].
On the other hand, the color index (CI*) provides insight into the overall color trend [43]. Values between −20.0 to −2.0 indicate a trend from deep green to yellowishgreen. During storage, the Fuerte variety showed a tendency to dark green, and it was more pronounced from day 10, being higher for the control sample, which indicates that the coatings allow for the maintenance of the intense green color, which is characteristic of the Fuerte variety. Regarding the Hass variety, it was observed that CI* increases from negative to positive values, from intense green to intense red (CI* > 20) (Table 8). This tonality is characteristic of the Hass variety in its state of maturity. Where: x , arithmetic mean; SD, standard deviation; CV, coefficient of variability. * Different letters indicate significant difference, evaluated through Tukey's test at 5% significance.
In Figure 7a,b, a break in the curve is observed, which occurs approximately at 10 days for both varieties. This point would refer to the climacteric peak, where the fruit is completely mature [2,36]. However, coated fruits show less tendency to mature because the coating offers a barrier to the transfer of oxygen to the fruit, reducing metabolism and, consequently, CO 2 production as well as reducing oxidation reactions at the cellular level. [18,23,56,61]. On the other hand, the color index (CI*) provides insight into the overall color trend [43]. Values between −20.0 to −2.0 indicate a trend from deep green to yellowish-green During storage, the Fuerte variety showed a tendency to dark green, and it was mor pronounced from day 10, being higher for the control sample, which indicates that th coatings allow for the maintenance of the intense green color, which is characteristic o the Fuerte variety. Regarding the Hass variety, it was observed that CI* increases from negative to positive values, from intense green to intense red (CI* > 20) (Table 8). Thi tonality is characteristic of the Hass variety in its state of maturity.
In Figure 7a,b, a break in the curve is observed, which occurs approximately at 1 days for both varieties. This point would refer to the climacteric peak, where the fruit i completely mature [2,36]. However, coated fruits show less tendency to mature becaus the coating offers a barrier to the transfer of oxygen to the fruit, reducing metabolism and consequently, CO2 production as well as reducing oxidation reactions at the cellular leve [18,23,56,61]. Regarding color variation (ΔE*), values greater than 3 are classified as very differen compared to the initial sample. It was observed that the Hass and Fuerte varieties coate with F2 reported values of ΔE* < 3, for days 2 and 4 (Tables 7 and 8), and thereafter i increased, although with less intensity for the samples coated with F2, which suggests tha Regarding color variation (∆E*), values greater than 3 are classified as very different compared to the initial sample. It was observed that the Hass and Fuerte varieties coated with F2 reported values of ∆E* < 3, for days 2 and 4 (Tables 7 and 8), and thereafter it increased, although with less intensity for the samples coated with F2, which suggests that this coating presents better protection against fruit color deterioration. However, the fruits of the Hass variety acquire reddish tones while the Fuerte variety tends towards a dark green tone (Figure 8a,b).

Fruit Firmness
Firmness showed a significant decrease (p-value < 0.05) during storage time ( 9). As for the Fuerte variety, significant differences were observed between treatmen value < 0.05) at 20 days of storage, with the control sample reporting less firmness kgf/cm 2 ), and slightly higher for the samples coated with F2. (0.70 kgf/cm 2 ). While, f Hass variety, it was observed that the control sample presented firmness of 0.50 kg and for the samples coated with F2 it was 2.80 kgf/cm 2 (p-value < 0.05). Table 9. Firmness (kgf/cm 2 ) of control and coated avocados.

Fruit Firmness
Firmness showed a significant decrease (p-value < 0.05) during storage time ( Table 9). As for the Fuerte variety, significant differences were observed between treatments (p-value < 0.05) at 20 days of storage, with the control sample reporting less firmness (0.30 kg f /cm 2 ), and slightly higher for the samples coated with F2. (0.70 kg f /cm 2 ). While, for the Hass variety, it was observed that the control sample presented firmness of 0.50 kg f /cm 2 , and for the samples coated with F2 it was 2.80 kg f /cm 2 (p-value < 0.05). Where: x , arithmetic mean; SD, standard deviation; CV, coefficient of variability. * p-value per treatment, ** p-value per treatment comparison, *** p-value per day of maturation within treatments, **** For n = 3.
The beginning of the considerable decrease in firmness was around day 8, for both varieties (Figure 9a,b), which suggests that the samples reached full maturity, which is the climacteric peak [36,64]. From day 18 onwards for the Hass variety, and day 14 for the Fuerte variety, firmness stabilizes with minimum values being lower for the control samples.
The beginning of the considerable decrease in firmness was around day 8, for varieties (Figure 9a,b), which suggests that the samples reached full maturity, which climacteric peak [36,64]. From day 18 onwards for the Hass variety, and day 14 fo Fuerte variety, firmness stabilizes with minimum values being lower for the control ples. This would be because the coatings allow for delayed degradation of protopectin more soluble compounds, such as pectic acid and sugars, due to depolymerization of tins by enzymatic action. Although, these are limited by the lack of oxygen due t barrier action of the polymer [28,54,55,65,66]. In addition, another aspect is the low w loss of the coated fruits, which allows better firmness to be maintained [38,67], and behavior is characteristic of samples coated with polymers [18,23,26,31,35,38,52,61,68

Conclusions
Films made from native potato starch, nopal mucilage, and pectin showed high t parency and low aw values. Regarding the coated avocado of the Hass and Fuerte vari it was observed that the acidity and the total soluble solids decreased significantl value < 0.05), although the pH did not vary considerably during the storage time. Re to weight loss and firmness, it was observed that they decreased to a lesser magnitud both varieties. Regarding the luminosity L*, color index, and color variation, better a utes were observed for the coated samples of both varieties during 20 days of storage use of coatings formulated with potato starch and nopal mucilage allows for the ma nance of the physicochemical and physiological properties of avocado fruits of the and Fuerte varieties for a longer time in storage.  This would be because the coatings allow for delayed degradation of protopectin into more soluble compounds, such as pectic acid and sugars, due to depolymerization of pectins by enzymatic action. Although, these are limited by the lack of oxygen due to the barrier action of the polymer [28,54,55,65,66]. In addition, another aspect is the low water loss of the coated fruits, which allows better firmness to be maintained [38,67], and this behavior is characteristic of samples coated with polymers [18,23,26,31,35,38,52,61,68].

Conclusions
Films made from native potato starch, nopal mucilage, and pectin showed high transparency and low a w values. Regarding the coated avocado of the Hass and Fuerte varieties, it was observed that the acidity and the total soluble solids decreased significantly (p-value < 0.05), although the pH did not vary considerably during the storage time. Related to weight loss and firmness, it was observed that they decreased to a lesser magnitude for both varieties. Regarding the luminosity L*, color index, and color variation, better attributes were observed for the coated samples of both varieties during 20 days of storage. The use of coatings formulated with potato starch and nopal mucilage allows for the maintenance of the physicochemical and physiological properties of avocado fruits of the Hass and Fuerte varieties for a longer time in storage.