Biodegradable Polymer Composites for Electrophysiological Signal Sensing

Electrophysiological signals are collected to characterize human health and applied in various fields, such as medicine, engineering, and pharmaceuticals. Studies of electrophysiological signals have focused on accurate signal acquisition, real-time monitoring, and signal interpretation. Furthermore, the development of electronic devices consisting of biodegradable and biocompatible materials has been attracting attention over the last decade. In this regard, this review presents a timely overview of electrophysiological signals collected with biodegradable polymer electrodes. Candidate polymers that can constitute biodegradable polymer electrodes are systemically classified by their essential properties for collecting electrophysiological signals. Moreover, electrophysiological signals, such as electrocardiograms, electromyograms, and electroencephalograms subdivided with human organs, are discussed. In addition, the evaluation of the biodegradability of various electrodes with an electrophysiology signal collection purpose is comprehensively revisited.

Concerning electrophysiological technology, the most emphasized technical element is the skin-contact electrode, which determines the quality of the bio-signal detection: noise level, signal-to-noise ratio (SNR), and operational stability [16,17]. Skin-contact electrodes are classified into wet-type electrodes [18][19][20] and dry-type electrodes [21][22][23]. The conventional and commercial electrode type is the wet-type electrode, and as a representative example, pre-gelled Ag/AgCl wet-type skin-contact electrodes are extensively used [24,25]. However, the above-mentioned wet-type electrodes suffer from a disadvantage, in that the measurement time is short. The wettability of the wet-type electrodes varies as a function of time, and their conductivity and adhesion to the skin are reduced, which significantly disturbs continuous and long-term detection from an operational stability perspective. Meanwhile, dry-type skin-contact electrodes avoid the issue of a short measurement period. A representative example of a dry-type skin-contact electrode is metal nanofilms, having excellent conductivity and measurement stability [26,27]. However, metal nanofilms still have the limitations of low skin adhesion ability and vulnerability to mechanical stress. As To reach a conductivity similar to metallic conductors, CPMs have typically needed to be doped or ordered into a high crystalline phase. Oxidation or reduction of CPMs for negative or positive polarons/bipolarons in the polymer chain are utilized. For instance, the removal of π-bond electrons from the conjugated backbone generates radical cation defects (known as polarons) and delocalizes the remaining electrons in the π -orbitals, which allows the electrons to move freely along the chain. The formation of a positively charged polymer backbone involves the incorporation of dopant anions, which have the effect of maintaining the electrostatic balance of the positive charge (Figure 1c). Positively charged structures provide p-doping, and negatively charged structures provide n-doping [52]. The delocalization of these polarons/bipolarons along the polymeric backbone improves the conductivity of CPMs. For instance, PAc generally exhibits a conductivity of 10 −5 S cm −1 , but its conductivity can be further improved to the level of 10 2 to 10 3 S cm −1 through appropriate doping. In the case of PPy, a representative CPMs, it has an extremely low conductivity, similar to insulators in an undoped state, but by adding halogenic dopant materials during the synthetic process, the conductivity of PPy increases drastically to 10 −3 S cm −1 [52]. Poly (3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS), which is the most widely used CPM commercially, is a good example of utilizing the ability to control the conductivity according to doping level. The conductivity of PEDOT:PSS can reach up to 4600 S cm −1 , and that it has availability for conductivity improvement not only through the synthesis process, but also via post-treatments, is an attractive point.
have been developed (Figure 1a) and studied regarding their physical and chemical characteristics. As shown in Figure 1a,b, CPMs have a Pi (π)-conjugated system, consisting of irregular single and double bonds along the polymer chain [50], in their molecular structures. The conductivity of CPMs originates from the above-mentioned conjugated carbon chains containing highly delocalized, polarized, and electron-dense π bonds [50,51]. To reach a conductivity similar to metallic conductors, CPMs have typically needed to be doped or ordered into a high crystalline phase. Oxidation or reduction of CPMs for negative or positive polarons/bipolarons in the polymer chain are utilized. For instance, the removal of π-bond electrons from the conjugated backbone generates radical cation defects (known as polarons) and delocalizes the remaining electrons in the πorbitals, which allows the electrons to move freely along the chain. The formation of a positively charged polymer backbone involves the incorporation of dopant anions, which have the effect of maintaining the electrostatic balance of the positive charge (Figure 1c). Positively charged structures provide p-doping, and negatively charged structures provide n-doping [52]. The delocalization of these polarons/bipolarons along the polymeric backbone improves the conductivity of CPMs. For instance, PAc generally exhibits a conductivity of 10 −5 S cm −1 , but its conductivity can be further improved to the level of 10 2 to 10 3 S cm −1 through appropriate doping. In the case of PPy, a representative CPMs, it has an extremely low conductivity, similar to insulators in an undoped state, but by adding halogenic dopant materials during the synthetic process, the conductivity of PPy increases drastically to 10 −3 S cm −1 [52]. Poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS), which is the most widely used CPM commercially, is a good example of utilizing the ability to control the conductivity according to doping level. The conductivity of PEDOT:PSS can reach up to 4600 S cm −1 , and that it has availability for conductivity improvement not only through the synthesis process, but also via posttreatments, is an attractive point. Although the conductivity of CPMs can be further improved by doping or increasing crystallinity, their natural characteristics, such as brittleness, non-biodegradability, and weak mechanical durability, limit their use as robust skin contact electrodes. As a strategy Although the conductivity of CPMs can be further improved by doping or increasing crystallinity, their natural characteristics, such as brittleness, non-biodegradability, and weak mechanical durability, limit their use as robust skin contact electrodes. As a strategy to overcome the mentioned issues, CPMs have been studied and developed in the form of composites blended with other functional matrices.

Biocompatible Adhesives
To obtain clear electrophysiological signals and reduce noise, a stable contact state between electrodes and the skin surface is one of the most important requirements. In general, the surface of the skin is known to be comprised of a protein called keratin [79,80]. Keratin has specific functional groups, such as hydroxyl (-OH), carboxyl (-COOH), thiol (-SH), and amine (-NH2) groups [79], and skin adhesion of the polymer composites can be obtained by inducing the interaction between these functional groups on the keratin surface. Among the various functional organic materials, catechol derivatives and glucose derivatives have been highlighted as biocompatible adhesives [81][82][83][84] (Figure 3a). For instance, dopamine, which was inspired by the mussel, exhibits excellent adhesive Biodegradation refers to the phenomenon that occurs through the activity of enzymes or chemical degradation by living organisms and their secretions [78]. During biodegradation, organic polymers are degraded into small molecular weight fragments that can ultimately be further converted into carbon dioxide and water. As mentioned above, the basic degradation mechanism is to divide macro molecular weight polymers into a smaller unit, and most BFMs have specific points where they are easily decomposed by hydrolysis and oxidation (Figure 2c). For instance, polymers containing ester bonds can be hydrolyzed under acidic or alkaline conditions. The specific moieties, such as ester, amide, thioester, imine, imide, anhydride, carbonate, urethane, and urea, are major unstable sites, where hydrolysis reactions occur. Degradation of polymers is also able to progress through oxidation of specific sites (moieties) in the polymer backbone or side chains. The common oxidizable groups, such as ether, amide, aldehyde, amine, phenol, allylic carbon, carbon alpha to aromatic, and carbon alpha to aliphatic, provide biodegradability to both synthesized and naturally-derived BFMs.

Biocompatible Adhesives
To obtain clear electrophysiological signals and reduce noise, a stable contact state between electrodes and the skin surface is one of the most important requirements. In general, the surface of the skin is known to be comprised of a protein called keratin [79,80]. Keratin has specific functional groups, such as hydroxyl (-OH), carboxyl (-COOH), thiol (-SH), and amine (-NH 2 ) groups [79], and skin adhesion of the polymer composites can be obtained by inducing the interaction between these functional groups on the keratin surface. Among the various functional organic materials, catechol derivatives and glucose derivatives have been highlighted as biocompatible adhesives [81][82][83][84] (Figure 3a). For instance, dopamine, which was inspired by the mussel, exhibits excellent adhesive properties for tissue repair, drug delivery, and skin contact patches, due to its catechol groups [85][86][87][88]. The catechol group consists of two hydroxyl groups and a phenolic group and this unique combination allows it to participate in various interfacial adhesions, such as hydrogen bonding, cation-pi interactions, and thiol reductions [86] (Figure 3b). In the case of glucose derivates, including dextran and starch, these contain a lot of hydroxyl groups in the monomer. The hydroxyl groups have multiple roles, providing bonding between monomers and adhesion to the keratin surface through hydrogen bonding.

Electrophysiological Signals
Electrophysiology is the study of electrical activity, by interpreting recorded electrical changes between cells and tissues. It is possible to diagnose diseases of the

Electrophysiological Signals
Electrophysiology is the study of electrical activity, by interpreting recorded electrical changes between cells and tissues. It is possible to diagnose diseases of the human body by recording changes in the electrical activity of core organs, such as the heart, brain, and muscles. The electrical activity extracted from the core organs could be applied for various purposes, including early disease diagnosis [89][90][91], artificial organs [92], and augmented reality [93]. The methods of collecting electrophysiological signals are classified into an invasive method and a non-invasive method. The invasive method has the advantage of being able to accurately collect a signal by implanting electrophysiological sensors into the human body. However, the toxicity of the implanted electrophysiological sensor may cause damage to the human body, and additional surgery is required to remove the nondecomposable electrophysiological sensor at the end of its lifespan. On the other hand, the non-invasive method has the advantage of easily collecting electrophysiological signals and a lower burden of surgery, due to attaching an electrophysiology sensor to the human skin. However, the signal of the targeted human organ is indirectly transmitted through the skin. Therefore, the measured electrophysiological signal is affected by the impedance of human skin. In addition, electrophysiological signals collected by the non-invasive method are sensitive to various external environmental factors, such as humidity, noise, and vibration. As a result, invasive and non-invasive electrophysiological sensors are needed with biocompatible and non-toxicity materials for human health. In addition, electrophysiological sensors based on toxic and non-decomposable substances could cause environmental pollution, due to an increase in the e-waste [94]. As such, the development of biodegradable material-based electro-physiological sensors is highly in demand. In this chapter, we report on biodegradable polymer electrodes for the measurement of electrocardiography (ECG), electrocardiography (EMG), and electroencephalography (EEG) ( Figure 4).

Electrocardiography
An ECG records the electrical activity produced by the heartbeat. ECG signal analysis is used to confirm a normal heart rate and for early diagnosis of various heart diseases, such as arrhythmias [95], myocardial infarction [96], and angina [97]. The ECG signals generated by a single heartbeat are classified in the following order: P-wave, QRS complex, and T-wave [98]. The P-wave and the QRS complex are generated by the atria depolarization and the depolarization of the ventricles, respectively. Finally, the T-wave occurs with the repolarization of the ventricles (Figure 5a).
In 2018, Seo et al. demonstrated an ECG sensor using calcium (Ca)-modified silk fibroin as an adhesion layer [99]. The reusable Ca-modified silk fibroin adhesive exhibited multifunctionalities, such as conductivity and water-degradability. When immersed in

Electrocardiography
An ECG records the electrical activity produced by the heartbeat. ECG signal analysis is used to confirm a normal heart rate and for early diagnosis of various heart diseases, such as arrhythmias [95], myocardial infarction [96], and angina [97]. The ECG signals generated by a single heartbeat are classified in the following order: P-wave, QRS complex, and T-wave [98]. The P-wave and the QRS complex are generated by the atria depolarization and the depolarization of the ventricles, respectively. Finally, the T-wave occurs with the repolarization of the ventricles (Figure 5a). In 2018, Seo et al. demonstrated an ECG sensor using calcium (Ca)-modified silk fibroin as an adhesion layer [99]. The reusable Ca-modified silk fibroin adhesive exhibited multifunctionalities, such as conductivity and water-degradability. When immersed in water, the peel strength of Ca-modified silk fibroin adhesive decreased to 1.2 N m −1 within 30 min and could be separated from the skin without any damage. To confirm the effect of the adhesive on ECG, they compared and analyzed the ECG waveforms collected by a commercial Ag/AgCl electrode and silk-adhesive-layer-based electrode. The commercial Ag/AgCl electrodes presented PQRST peaks with high noise levels and low signal amplification, due to weak adhesion and relatively high impedance (Figure 5b). In contrast, the electrodes with the Ca-modified silk adhesive presented lower noise levels and higher signal amplification than the Ag/AgCl electrodes, due to their low impedance and high adhesion properties (Figure 5c). In addition, the proposed silk-adhesive ECG electrode exhibited an undistorted ECG signal, despite the movement caused by the bending of the wrist (Figure 5d,e).
To fabricate a multifunctional hydrogel electrophysiology sensor, in 2021, Li et al. demonstrated a conductive hydrogel electrode, by blending MXene, poly(acrylic acid) (PAA), and amorphous calcium carbonate (ACC) to measure ECG signals [100]. In this work, Mxene, PAA, and ACC were used as conductive, biodegradable, and cross-linking components. The Ca ion of ACC interacts with the carboxylic group of PAA and -OH, -F, and -O groups at the surface of Mxene through metal chelation. With the supramolecular interaction between the components, the proposed MXene-PAA-ACC hydrogel exhibited strong self-healable, stretchable, and biodegradable characteristics. The proposed hydrogel electrode degrades within 65 days in phosphate-buffered saline (PBS) solution. The degradability of the MXene-PAA-ACC hydrogel originated from its chemical and structural characteristics. The surface-terminated functional groups of hydrophilic MXene nanosheets and the carboxyl groups of PPA increased the water penetration of MXene-PAA-ACC hydrogels. Furthermore, the hydrogel electrode has porous microstructures, to facilitate the penetration of water molecules in PBS (Figure 5f). Water molecules penetrating the gel swell the MXene-PAA-ACC hydrogels by intercalating between the MXene nanosheets or binding to the hydrophilic PAA. As the cross-linking between components gradually weakens due to swelling, the gel eventually decomposes. For ECG signal measurement, MXene-PAA-ACC hydrogel electrodes were attached to human arms and ankles (Figure 5g). Figure 5h shows the ECG waveform measured with the proposed electrode. The measured ECG exhibited the heart electrical activity of normal adults and distinguishable PQRST peaks.
Yuen et al. collected an ECG signal using polycarbonate (PC)-based ion gels and poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT: PSS) electrodes [71]. To achieve robust adhesivity and high conductivity, PCs were prepared using N-substituted cyclic carbonates. The designed PCs were synthesized thorough the ring-opening polymerization of polyethylene glycol (PEG), mono (8MC (6-methyl-1,6,6-dioxazocan-2one)), and bifunctional cyclic carbonates (bis 8MC (6,6 -(ethane-1,2-diyl)bis(1,3,6,-dioxazocan-2-one)). The reaction was initiated by the introduction of the primary alcohol group of PEG with the presence of an organic catalyst. Ionic liquids ([BMIm][Lac], 1-butyl-3-methylimidazolium chloride) were intercalated during the synthetic process to enhance the conductivity of the final gel electrode. The proposed PCs based ion gels are non-toxic and have good biodegradability in water. Owing to the large amounts of ester bonds in the PC chains, the hydrolysis reaction occurred at the ester moieties when gels were submerged in water. The polycarbonate-based ion gels were attached to the volunteer's forearm and elbow, to collect the ECG using a three-electrode method. The proposed gel electrode exhibited a clearer ECG signal sensing performance than the commercial Ag/AgCl electrode, due to a low impedance level.

Electromyography
EMG is a method that records the electrical activity derived from the contraction and relaxation of muscles. EMG waveforms are generated by action potentials during muscle contraction and stabilization states. The stronger the contraction of the muscle, the higher the action potential (Figure 6a). However, it is difficult to quantitatively determine the EMG signal because the composition and density of muscle tissue varies from individual to individual and the thickness of the skin is different. To overcome this issue, efforts have been made to decompose and interpret EMG signals (Figure 6b). The automatic decomposition EMG (ADEMG) method [101] and the algorithm of precision decomposition [102] are techniques for decomposing EMG signals. In the case of EMG signal quantification, frequency domain [103] and time domain [104,105] analysis have been used. In general, the collected EMG potentials are used for the diagnosis of muscle diseases. Furthermore, since the muscles are operated by nerves, EMG can be utilized for various neurological diagnoses, such as peripheral neuropathy [106] and trigeminal neuralgia [107].
In 2020, Xu et al. reported a cost-effective and disposable EMG sensor by patterning it on a paper substrate with graphite from a commercial 9B pencil [108]. The paper substrate was composed of porous cellulose, which can be easily dissolved in water through a hydrolysis reaction between monomers. The water-based degradation performance of the proposed device was easily controlled by the coating of Silbione RT Gel 4717 A/B. The additional Silbione coating provided the film with skin adhesion and waterproofing properties. The pencil-paper sensor was adapted to collect EMG signals from the forearm. The proposed EMG sensor exhibited stable and real-time EMG signal sensing performance under direct water injection and sweaty skin conditions. A method to improve sensing performance by utilizing structural changes was reported. In 2021, Won et al. collected EMG signals by fabricating a sensor consisting of PLA as a BFM and PEDOT: PSS as a CPM [109]. The proposed sensor was laser cut in a Y-shape, to accommodate a kirigami structure with increased stretchability and areal coverage. Figure 6c shows the design of the Y-shaped kirigami structure electrode, adjusting L and S variables to control the stretchable characteristics. Moreover, the W variable controls the area of the actual electrode. With the aforementioned structure, the proposed electrode exhibited stretchability in the diagonal direction (Figure 6d). Figure 6e shows the EMG potentials measured in the vicinity of the forearm flexor with the conventional Ag/AgCl gel electrode and the proposed electrode. A higher SNR value was achieved when using the proposed electrode for EMG measurement, due to an enlarged areal coverage. Owing to the usage of PLA, the proposed device has potential for water-degradability under acid or base conditions through the catalyzed hydrolysis reaction. The ester bonds of PLA can be easily broken down by the water molecules via random chain scission.
To manufacture an eco-friendly electrophysiological sensor that can be easily separated and with strong adhesion to the skin, in 2020, Zhang et al. demonstrated a transient epidermal electronic (TEE) sensor based on a genetically engineered plasticized copolymer (GEPC) for EMG monitoring [110]. The GEPC was prepared through modification of silk fibroin with resilin protein and plasticized with glycerol. In the composite gel, all components were interconnected by hydrogen bonding. The proposed TEE presents stepwise water-degradability, due to the interaction between water and its components (silk fibroin, resilin protein, and glycerol). Figure 6f shows a sequential schematic of the TEE degradation by water. Decomposition occurs when the TEE is immersed in water, but it retains its conductivity and adhesivity until this stage. During this process, the glycerol was extracted from the gel and the plasticizer was exchanged with water molecules. However, after heat-modulated dehydration, the gel lost its stretchable characteristics and easily broke down into small fragments, owing to the absence of a plasticizer.

Electroencephalography
EEG is a method that records the brain signals caused by the electrical activity of the nervous system. The locations of human scalp electrodes for EEG measurements are  [109] with permission from American Chemical Society); (e) EMG measurements for the proposed electrode and conventional electrode; (f) schematic of water-induced changes in GEPC substrate-based TEE electrodes (adapted from [110] with permission from the John Wiley and Sons).

Electroencephalography
EEG is a method that records the brain signals caused by the electrical activity of the nervous system. The locations of human scalp electrodes for EEG measurements are classified according to international standards. Figure 7a shows a map of human scalp electrode positions with a 10-20 system method. The electrode was labeled as frontal (F), temporal (T), parietal (P), occipital (O), and central (C), respectively. Additionally, the FTOPC abbreviation was followed by a number, to define the detailed position for the EEG measurement [111,112]. Since an EEG waveform measured in the human brain is visually confusing and difficult to analyze, the complex signal is generally interpreted with the frequency, using the power spectrum method (Figure 7b) [113,114]. First, the delta waves are vibrations below 4 Hz and appear in meditation or coma. The theta waves vibrate at 4~7 Hz and appear in the process of recalling memories or initiating sleep. The alpha wave appears at about 8~12 Hz and is the EEG in a stable state. The Beta waves that are generated in a state of arousal have a frequency of 13~25 Hz. Finally, the gamma waves that occur above 25 Hz are caused by a high wakefulness state and REM sleep.
In 2021, Nandi et al. demonstrated an EEG sensor based on bovine serum albumin (BSA) protein extracted from bovines [115]. The proposed polymer gel composite exhibited high proton-conductivity, owing to the hydrogen bond network between oxo-amino-acids functional groups in the protein and the water molecules. The proton-conducting polymer gel was prepared through the polymerization of reduced BSA (R-BSA). First, BSA was treated with trifluoroethanol, water, and 2-mercaptoethanol for reduction of BSA. After that, the R-BSAs were polymerized using ethylenediamine via reshuffling of the disulfide bonds of R-BSA. The prepared gel composite exhibited a 500% stretchability and a proton conductivity of about 5 mS cm -1 . Figure 7c shows the protease-based biodegradable characteristics of R-BSA films. Trypsin, which is a BSA digesting enzyme through a hydrolysis reaction, was added to tris-buffer solution (pH 7.4, 37 • C). A R-BSA film treated with trypsin for 40 h was degraded by about 80%. Figure 7d shows the collected EEG signals using a R-BSA-based electrophysiology sensor. Clear alpha waves and beta waves were successfully measured according to the closed and open states of the eyes.
To investigate the electrical activity of the cerebral cortex, in 2016, Yu et al. demonstrated EEG and electrocorticography (ECoG) sensors utilizing silicon nanomembranes (Si NMs) [116]. In the proposed sensor, Si NMs, PLGA, and SiO 2 were used as electrodes, substrates, and a passivation layer. The PLGA and SiO 2 dissolved within 4-6 weeks and 6 months under the condition of 37 • C biofluids, respectively. The dissolving mechanism of components including Si NMs, SiO 2 , and PLGA is a hydrolysis reaction. Si and SiO 2 can form ortho-silicic acid (Si(OH 4 )) under biofluid conditions. In the case of PLGA, the presence of a specific moiety (ester bond) of PLGA provides strong water degradability. The proposed sensor was attached to the cortex of the left hemisphere and the periosteum of an adult rat, to collect EEG and ECoG signals. The measured ECoG signal showed similar waveforms to the signal recorded by the commercial control electrode. In the case of EEG signals, reliable theta waves and sleep spindles were recorded through the proposed electrode based on in vivo sensing.
Meanwhile, Manouchehri et al. designed a conductive coating material to increase the biocompatibility of the electrode-tissue interface [117]. The proposed conductive coatings were prepared by adding oligoaniline to chitosan and epoxidizing the chitosan by reaction with epichlorohydrin. Figure 7e shows the degree of swelling and degradation according to the oligoaniline content of the conductive coatings. When the content of hydrophobic oligoaniline was decreased, the diffusion of water molecules inside the hydrogel was relatively increased and this accelerated the swelling rate. According to the increased diffusion of water molecules, the decomposition rate was promoted. During the swelling process, the cross-linking interaction between the amine group of chitosan and the carboxyl group of the oligoaniline began to be weakened by the water molecules, and as this process continued, the gel broke down into small pieces.

Biodegradability Evaluation of Polymers
Biodegradable polymer-material-based electrophysiological sensors are attracting attention due to the growing importance of environmental protection. The conventional electrophysiological sensors are manufactured based on toxic synthetic materials and non-degradable materials, to improve their functions. However, human health is threatened by the increase in e-wastes due to the high demand for electronic products. Recently, research on electrophysiological sensors using biodegradable polymers has been increasingly reported, to create a green environment. The biodegradability of a polymer is primarily due to the principle of releasing polymer-binding chains through various microorganisms, water, and biofluids. In addition, naturally extractable guar gum [18], gelatin [118], starch [119], and fabric [120,121] have been adopted for achieving green (d) EEG waveform of alpha and beta waves (adapted from [115] with permission from John Wiley and Sons); (e) swelling rate and degradation rate of conduct polymer coatings (adapted from [116] with permission from the Elsevier B.V.).

Biodegradability Evaluation of Polymers
Biodegradable polymer-material-based electrophysiological sensors are attracting attention due to the growing importance of environmental protection. The conventional electrophysiological sensors are manufactured based on toxic synthetic materials and nondegradable materials, to improve their functions. However, human health is threatened by the increase in e-wastes due to the high demand for electronic products. Recently, research on electrophysiological sensors using biodegradable polymers has been increasingly reported, to create a green environment. The biodegradability of a polymer is primarily due to the principle of releasing polymer-binding chains through various microorganisms, water, and biofluids. In addition, naturally extractable guar gum [18], gelatin [118], starch [119], and fabric [120,121] have been adopted for achieving green electrophysiological devices, by fabricating biodegradable polymers. Furthermore, research is underway to improve parameters such as the conductivity, biocompatibility, and stability of biodegradable polymers. In this chapter, we report the biodegradation results of electrophysiological sensors fabricated with biodegradable polymers.
To manufacture an eco-friendly biodegradable sensor, in 2018, Yi et al. demonstrated a Zn-based ECG and EMG sensor with strong biodegradability using galactomannan extracted from Leucaena leucocephala (L. leucocephala) as a substrate [122]. Both Zn and galactomannan exhibited a solvent-selective degradation, owing to the hydrolysis reaction. Galactomannan substrates are structurally stable in ethanol but decompose in water (Figure 8a). In addition, Zn electrodes were immersed in ethanol and distilled water to investigate the degradation characteristics of different solvents. Figure 8b shows a Zn electrode degraded by distilled water for 24 h. On the other hand, the Zn electrode was in a stable state in ethanol. As another representative study, in 2015, Hwang et al. measured EMG using biodegradable (poly(1,8-octanediol-co-citrate) (POC) as a substrate for an electrophysiology sensor [123]. The electrophysiology sensor was immersed in PBS solution (pH 10), to investigate its degradability (Figure 8c). As a result, the Mg electrode was degraded within a few hours, while SiO 2 and POC were slowly dissolved within a few weeks. The dissolution kinetics of the proposed sensor depend on the temperature, pH, and ionic concentration of the solution, which have parametric effects on hydrolysis.  Table 1 with a comparison with a commercial Ag/AgCl gel electrode.  For strong adhesion to the skin, in 2022, Meng et al. manufactured a dry film electrode with polypyrrole (Ppy), acid-modified silk fibroin (AM-SF), and cellulose nanocrystals (CNC) [124]. They modified the tyrosine side chain of the SF protein with the sulfonic acid groups and obtained an interlocking structure between the positively-charged Ppy and negatively-charged SF networks. In the proposed film, Ppy acts as a CPM, calcium (Ca)modified SF acts as an adhesive matrix, and CNC was used as a crosslinker, respectively. The degradation characteristic of Ppy@AM-SF/CNC film was investigated by immersing the film in PBS and protease XIV solutions (Figure 8d). Figure 8e shows a photograph of the degradable Ppy@AM-SF/CNC film in a Protease XIV condition at 37 • C. With the proposed conditions, the proposed film degraded into small fragments after 15 days through the catalytic proteolysis reaction of SF, owing to the Protease XIV enzyme.
Shao et al. demonstrated a hydrogel-based epidermal ECG sensor by combining cellulose nanofibers (CNF), polydopamine (PDA), and polyacrylamide (PAM) [125]. The proposed hydrogel has high ion-conductive, self-adhesive, and water-degradable characteristics. CNF, PDA, and PAM were cross-linked through hydrogen bonds between the functional groups of polymers. Additionally, ferric (Fe 3+ ) interacted with polymers via metal chelation and was introduced to promote the degradation of the hydrogel through the Fenton-like reaction. During the degradation process, hydrophilic amide groups of the PAM chains absorb a large number of water molecules, which gradually decompose the hydrogen bonds between the polymer matrix chains. The penetrated oxygen molecules from the atmosphere slacken the network structure and oxidized the catechol groups of the tris-catechol-ferric complexes. Through the above steps, the ferric was released from the complexes and could participate in the Fenton-like reactions by reduction to Fe 2+ . The ammonium persulfate added to the gel synthesis process was activated by the released Fe 2+ . The Fenton-like reaction was promoted through the production of oxidant SO 4− radical, and the generated radicals consequently reacted with hydroxyl ions in the solution. The above reaction produces hydroxyl radical, which has a high reactivity, and decomposes the remaining gel components into small organic molecules. To investigate the changes in molecular weight of hydrogels quantitatively, gel permeation chromatography (GPC) was performed, and the molecular weight was reduced by half during the 30-day degradation test period.
In Section 3, we systematically reviewed biodegradable polymeric composite electrodes, with various materials and degradation mechanisms. The detail bio-signal sensing performance parameters of the proposed composites are summarized in Table 1 with a comparison with a commercial Ag/AgCl gel electrode.

Future Perspectives and Challenges
The research results presented above prove that biodegradable polymer electrodes have the potential to be used as a key material in various medical fields in the future. For instance, since biocompatible polymer composites are non-toxic to the human body, they can be utilized for long-term bio-signal collection, and this technology is expected to greatly contribute to maintaining life-expectancies through continuous health monitoring. Preventative, predictive, and personalized management of diseases can be achieved through electrophysiological sensing systems being integrated with IoT technologies. Furthermore, the biodegradable characteristics of polymer composite electrodes could prevent environmental pollution by reducing e-waste. However, the following technical barriers should be overcome for further development of the technology of biodegradable polymer electrophysiological sensors.
(1) One of the applications of bio-signal sensing electrodes is collecting electrophysiological signals over long-term periods by attaching them to the human body. The currently commercialized system has difficulty in continuous monitoring, due to its weight and bulky system size, which restricts the free movement of the patient when it is attached to the body. To overcome the aforementioned issue, it is essential to reduce the weight and size of the measurement system. In terms of application in an integrated sensing system, bio-signal sensing electrodes should be arranged with other components. For this integration, a high-level patterning process is required, and the combinations of materials and processes needs to be further diversified. (2) The experimental conditions for biodegradation tests should be standardized. Most of biodegradable properties were investigated using a single specific solvent. To realize the full commercialization of biodegradable polymers, it is necessary to specifically characterize the biodegradable properties under various conditions, such as ambient humidity, solvent temperature, and acidity. (3) The biocompatibility of by-products generated during decomposition should be considered. The organic material itself used as an electrode has biocompatibility when in the form of a polymer, but by-products occurring in the decomposition reaction may be harmful. Therefore, to utilize biodegradable electrodes for practical applications, a sensor design that guarantees the non-toxicity of by-products is required. (4) The mechanical and chemical stability of polymer composites should be further improved. To continuously monitor electrophysiological signals with polymer composite electrodes, it is necessary to attach an epidermal sensor to the human body under daily. Therefore, composite film electrodes should guarantee sufficient resistance to variables that can occur in the conditions of daily life, such as sweat, movement, and pressure from external contact. For the practical utilization of electrodes, properties such as mechanical durability and adhesion of composites need to be further developed. (5) Controllable degradation kinetics of components are required for specific applications, such as implantable devices. In the above-mentioned approaches, the degradation rate needs to be programmed for the desired conditions. To meet the above requirements, the control of the dissolution or degradation behavior of BFMs and CPMs needs to be improved.
The future perspectives and challenges of the biodegradable polymer electrodes are summarized and illustrated with Figure 9.
Polymers 2022, 14, x FOR PEER REVIEW 17 of 22 (5) Controllable degradation kinetics of components are required for specific applications, such as implantable devices. In the above-mentioned approaches, the degradation rate needs to be programmed for the desired conditions. To meet the above requirements, the control of the dissolution or degradation behavior of BFMs and CPMs needs to be improved. The future perspectives and challenges of the biodegradable polymer electrodes are summarized and illustrated with Figure 9.

Conclusions and Outlooks
In this review, we summarized functional organic materials for biodegradable polymeric epidermal electrodes into conductive, frame, and adhesive categories. The specific characteristics of electrophysiological signals, including ECG, EMG, EEG, and previous attempts to collect them using biodegradable electrodes were reviewed, with detailed degradation mechanisms. As the revisited studies suggest, the feasibility of biodegradable polymers for versatile uses in various electrophysiological sensing devices is promising. Various polymer composites for both wet and dry type electrodes potentially satisfy conductive and functional electrode roles, as well as having high compatibility with the skin and body. The gel-type electrodes introduced in this review have advantages in terms of their ease of fabrication, high ionic conductivity, and robust mechanical properties. However, as mentioned in the introduction, the performance of gel-type electrodes is affected by environmental conditions. From this point of view, dry electrodes may be an ideal skin-contact electrode, but there are many obstacles to the

Conclusions and Outlooks
In this review, we summarized functional organic materials for biodegradable polymeric epidermal electrodes into conductive, frame, and adhesive categories. The specific characteristics of electrophysiological signals, including ECG, EMG, EEG, and previous attempts to collect them using biodegradable electrodes were reviewed, with detailed degradation mechanisms. As the revisited studies suggest, the feasibility of biodegradable polymers for versatile uses in various electrophysiological sensing devices is promising. Various polymer composites for both wet and dry type electrodes potentially satisfy conductive and functional electrode roles, as well as having high compatibility with the skin and body. The gel-type electrodes introduced in this review have advantages in terms of their ease of fabrication, high ionic conductivity, and robust mechanical properties. However, as mentioned in the introduction, the performance of gel-type electrodes is affected by environmental conditions. From this point of view, dry electrodes may be an ideal skin-contact electrode, but there are many obstacles to the implementation of dry film electrodes with excellent adhesion, mechanical stability, and conductivity. Owing to the aforementioned issues, studies on polymer composites to improve gel-type electrodes have been previously attempted. Despite the challenges, there have been many recent attempts to implement ideal dry-type epidermal electrodes with robust mechano-electrical characteristics. We believe that such comprehensive analyses and the various attempts will open up an opportunity for valuable uses in the next generation of wearable or implantable healthcare devices.