Core/Shell Pigments with Polyaniline Shell: Optical and Physical–Technical Properties

Core/shell pigments allow for the combination of the active anti-corrosion effect of the shell and the barrier effect of the core. This makes it possible to obtain anti-corrosion pigments, with a high—protective effect and low toxicity. Thus, the need for a comprehensive study of the properties of these pigments grows more urgent, before their application to paints and varnishes. The hiding power of core/shell pigments comes close to the one of pure polyaniline (PANi), when the PANi content in the pigment reaches 50 wt.%, with sulfuric and phosphoric acids used as dopants. This paper, also, shows that the blackness value of core/shell pigments with 10 wt.% PANi is around 35 and constant; for pure PANi, their blackness value is 40. When PANi content is 5 wt.%, kaolin-based pigment shows the lowest blackness, which happens due to a generally higher whiteness of kaolin. However, when the PANi content surpasses 10 wt.%, there seems to be no influence on the blackness of the core/shell pigments. The core/shell pigment with a 20 wt.% PANi is, optically, identical to a black-iron-oxide pigment. An increase in the PANi content of the core/shell pigment leads to an increase in the oil absorption of the samples. It was found that the dispersion process would be the most energy efficient for core/shell pigments, containing kaolin and talc as a core.


Introduction
Aniline-based dyes were first obtained in the 19th century [1]. Aniline blue, yellow, orange, black, and a wide range of other dyes were synthesized, in accordance with industry demands, by the end of the 19th century. Aniline-based-dye production led to the abandonment of scarce and expensive natural raw materials (indigo, madder, cochineal, Tyrian purple). Today, the «Colour Index» international pigment and dye classifier contains more than 150 aniline-based products as well as others based on derivatives. Dyes obtained using aniline can be divided into three groups [2,3]: Dyes made from aniline; Dyes that include other compounds, apart from aniline; Dyes based on intermediate products made from aniline.
However, aniline-based dyes possess bad substrate coverage, which does not allow them to be added to paints and varnishes as a pigment. Polyaniline (PANi), the product of aniline polymerization in the presence of various oxidizing agents, is an exception. PANi possesses poor solubility in most organic solvents, which limits its practical implementation. However, obtaining soluble PANi is still a top-level task for a lot of researchers all over the world. This fact made it possible to obtain PANi films with high conductivity and high mechanical properties [4][5][6][7]. For example, water-soluble PANi was synthesized in [4], by its

Materials and Methods
In total, 0.28 g of H 2 SO 4 and 0.25 g of aniline (Sigma-Aldrich, St. Louis, MO, USA) were dissolved into 50 g of water and stirred well with a magnetic stirrer, until the resulting aniline salt was completely dissolved. Then, 5 g of core pigment was added into the reaction mixture. After that, 50 mL of aqueous solution of ammonium persulfate (0.75 g of ammonium persulfate (Sigma-Aldrich)/49.25 g of water) was added, simultaneously, to the suspension, obtained under intensive stirring. The reaction mixture was stirred for 1 h and, then, left for 24 h. The resulted suspension was filtered and washed, first with 250 mL of acid solution used in the synthesis (1 mol/L) and, then, with acetone, until a clear filtrate was obtained. The core pigment obtained was dried at 60 • C for 12 h.
Inorganic fillers, such as kaolin (KaMin™ HG, KaMin LLC, Lawrenceville, GA, USA), talc (Talc-8, Ashirwad Minerals and Marbles), bentonite (BENTONE SD-1, Elementis Specialties, London, UK), and muscovite (Micro-Mica W1, New Enterprise Stone & Lime Co., Inc., New Enterprise, PA, USA), which could serve as new solid-phase nuclei during polymer formation, were also presented in the medium. The main properties of the used inorganic fillers are shown in Table 1. Sulfuric, phosphoric, and hydrochloric acids (all acids were purchased from Sigma-Aldrich and used as received or purified according to standard procedures) were used as PANi dopants. The PANi content in the core/shell pigment varied from 0 to 50 wt.%.
Optical micrographs were taken using a Biolam S12 (LOMO, Saint Petersburg, Russia) optical microscope. SEM micrographs were taken using a Zeiss SUPRA 40 (Carl Zeiss, Oberkochen, Germany) electron microscope. Fourier-transform infrared spectroscopy (FTIR) analysis of PANi salt powder and core/shell pigments was carried out in the range of 375-4000 cm −1 using BRUKER ALPHA (Bruker Optics, Billerica, MA, USA). Oil absorption of the samples was determined using [33]. Density was measured by pycnometry [34]. The hiding power of the core/shell pigments obtained was determined visually [35]. Color properties of core/shell pigments were obtained using a spectrophotometer Ci4200 (X-rite, Kentwood, MI, USA). The pigment blackness was measured according to [36,37]. The coloring ability of core pigments with PANi coating was determined as follows. The paste with a core/shell pigment to titanium dioxide ratio of 1:3 was prepared by grinding on the plate using a chime and spatula, until it became homogeneous. Then, this paint was used to make paint touches, with their reflection spectra being detected on a spectrophotometer (X-rite Ci4200). The p minimum value was determined for the test and control samples, in the short-wave area of the spectrum. The two-constant Kubelka-Munk theory function was calculated using the formula [34], where ρ is the minimum reflection index value for the determined wavelength. Black-iron-oxide pigment was used as the reference sample. Coloring ability I col (%) was calculated by: where F test and F cnt are Kubelka-Munk functions of test and control (iron oxide black) samples, respectively.
To determine pigment dispersibility, the pigment paste made, using a specific recipe, was dispersed in a bead mill. The recipe is: water prepack 7.5 g (consists of water, ethylene glycol, sodium tripolyphosphate, hydroxyethyl cellulose), pigment 5 g (0.83 g of PANicoated core/shell pigment and 4.17 g of titanium dioxide), and the pigment paste to beads ratio is 1:1. Approximately 0.5 mL of the paste were sampled after 5, 15, 25, 35, 50, and 65 min. A piece of thick paper was covered with the obtained paste, using a brush. The painting-touch size for spectrum detection was 50 mm × 50 mm. The reflection index of the hardened sample was registered on the spectrophotometer Ci4200 (X-rite, Kentwood, MI, USA), at the minimum of sample reflectivity. Using the obtained indices, Kubelka-Munk function values were calculated, and, then, t/F vs. t graph was plotted. After that, k d and F ∞ were calculated using the least squares method. k d was determined as a reciprocal of the length of the Y-axis line, cut with the obtained graph, while F ∞ was determined as a reciprocal of the slope [34].
Dispersion resistance value was calculated by the formula [34]: where F ∞ is the Kubelka-Munk function critical value, and k d is dispersion rate constant.

Results and Discussion
Based on the optical microscopy data, it can be seen that core/shell pigment is formed during the course of the synthesis (Figures 1-3). Individual PANi particles and colorless lamellar talc particles can be seen in the micrographs of the mechanical mixture of talc and PANi ( Figure 4). where F∞ is the Kubelka-Munk function critical value, and kd is dispersion rate constant.

Results and Discussion
Based on the optical microscopy data, it can be seen that core/shell pigment is formed during the course of the synthesis (Figures 1-3). Individual PANi particles and colorless lamellar talc particles can be seen in the micrographs of the mechanical mixture of talc and PANi (Figure 4).  where F∞ is the Kubelka-Munk function critical value, and kd is dispersion rate constant.

Results and Discussion
Based on the optical microscopy data, it can be seen that core/shell pigment is formed during the course of the synthesis (Figures 1-3). Individual PANi particles and colorless lamellar talc particles can be seen in the micrographs of the mechanical mixture of talc and PANi (Figure 4).       The pictures obtained using scanning electron microscopy, also, confirm the formation of core/shell pigments ( Figure 5).
(a) The pictures obtained using scanning electron microscopy, also, confirm the formation of core/shell pigments ( Figure 5).  The pictures obtained using scanning electron microscopy, also, confirm the formation of core/shell pigments ( Figure 5). The FTIR spectra of different core/shell pigments and PANi samples are shown in Figure S1 (Supplementary Materials). The absorption bands at 1478 cm −1 and 1560 cm −1 are assigned to benzenoid and quinoid ring vibration, respectively [38]. The absorption band characteristic of the conducting protonated form is found at about 1245 cm −1 . The absorption band at 1139 cm −1 is due to the in-plane bending vibration of C-H [39], while  The FTIR spectra of different core/shell pigments and PANi samples are shown in Figure S1 (Supplementary Materials). The absorption bands at 1478 cm −1 and 1560 cm −1 are assigned to benzenoid and quinoid ring vibration, respectively [38]. The absorption band characteristic of the conducting protonated form is found at about 1245 cm −1 . The absorption band at 1139 cm −1 is due to the in-plane bending vibration of C-H [39], while at 1305 cm −1 it is because of C-N stretching of the benzenoid ring of PANi [40]. The aromatic ring and out-of-plane C-H deformation vibrations manifest themselves in the region of 900-700 cm −1 . The FTIR spectra of core/shell pigments show a blue shift of the main absorption bands, compared to PANi. Besides, from absorption bands caused by PANi presence, there are a number of bands in the spectra of core pigments related to the core used in the study.    A change in the shell thickness, as well as the nature of PANi surface, leads to changes in color characteristics. The study established the influence of shell thickness and the nature of PANi surface on color properties. The graphs show that an increase in the doped PANi content raises the b* coordinate and lowers the a* coordinate. The core/shell pigment-color tone moves from a green area to a green-yellow area. The b* coordinate growth, with an increase in the PANi content for core/shell pigments, may be due to a large number of yellow-brown-colored aniline oligomers (Figure 8a-c). An inverse relationship is observed for core/shell pigment with undoped PANi coating: the a* coordinate rises and the b* coordinate declines with an increase in the PANi content ( Figure 3d). However, this happens because the core/shell pigment covered with undoped PANi is blue, and the mixture turns greener due to the color subtractivity. The angle of the color vector projection shows it clearly. A change in the shell thickness, as well as the nature of PANi surface, leads to changes in color characteristics. The study established the influence of shell thickness and the nature of PANi surface on color properties. The graphs show that an increase in the doped PANi content raises the b* coordinate and lowers the a* coordinate. The core/shell pigment-color tone moves from a green area to a green-yellow area. The b* coordinate growth, with an increase in the PANi content for core/shell pigments, may be due to a large number of yellow-brown-colored aniline oligomers (Figure 8a-c). An inverse relationship is observed for core/shell pigment with undoped PANi coating: the a* coordinate rises and the b* coordinate declines with an increase in the PANi content (Figure 3d). However, this happens because the core/shell pigment covered with undoped PANi is blue, and the mixture turns greener due to the color subtractivity. The angle of the color vector projection shows it clearly.
Hiding power is another important optical property of pigment. This property, for PANi-coated core/shell pigments, depends on the polymer content in the pigment only and has no relation to the doping acid used in the synthesis. Core/shell pigment hiding power grows with an increase in PANi content (Figure 9). It should be noted that the hiding power is comparable to that of pure PANi, even at a 50 wt.% of core/shell pigment content, with a shell of phosphoric-acid-doped PANi. Hiding power is another important optical property of pigment. This property, for PANi-coated core/shell pigments, depends on the polymer content in the pigment only and has no relation to the doping acid used in the synthesis. Core/shell pigment hiding power grows with an increase in PANi content (Figure 9). It should be noted that the hiding power is comparable to that of pure PANi, even at a 50 wt.% of core/shell pigment content, with a shell of phosphoric-acid-doped PANi.  The same relation can be seen for the core/shell pigment-coloring strength ( Figure 10)it rises along with the increase in PANi content.
The same relation can be seen for the core/shell pigment-coloring strength ( Figure  10)-it rises along with the increase in PANi content. The obtained core/shell pigments possess low color purity, so their application as green pigments is objectionable. However, high blackness may let it be applied as black pigments, since one of their important properties is blackness. Figure 11 shows that the blackness of core/shell pigments increases with the growth of PANi content. Moreover, the nature of the core used affects the blackness of core/shell pigments, only at low PANi content (~10 wt.%). So, a further increase in PANi content results in pigments that possess approximately equal blackness, regardless of the used core. The blackness of all core/shell pigments is slightly lower compared to PANi. Doping acid affects core/shell pigment blackness poorly, regardless of the PANi content. Figure 12 shows the core/shell pigment blackness vs. PANi content graph. The obtained core/shell pigments possess low color purity, so their application as green pigments is objectionable. However, high blackness may let it be applied as black pigments, since one of their important properties is blackness. Figure 11 shows that the blackness of core/shell pigments increases with the growth of PANi content. Moreover, the nature of the core used affects the blackness of core/shell pigments, only at low PANi content (~10 wt.%). So, a further increase in PANi content results in pigments that possess approximately equal blackness, regardless of the used core. The blackness of all core/shell pigments is slightly lower compared to PANi. Doping acid affects core/shell pigment blackness poorly, regardless of the PANi content. Figure 12 shows the core/shell pigment blackness vs. PANi content graph.
Despite the high absorption index, black pigments are, usually, diverse in their shade of black. Growth of PANi content in core/shell pigment causes a brown tint for almost all samples, due to the brown aniline oligomers in its content. Their mass is not high enough to count PANi in, but they have a high molecular weight, enough to remain undissolved in acetone while washing off the core/shell pigments. Table 2 shows the comparison of core/shell pigments, with the coating of PANi and common black pigments. the nature of the core used affects the blackness of core/shell pigments, only at low PANi content (~10 wt.%). So, a further increase in PANi content results in pigments that possess approximately equal blackness, regardless of the used core. The blackness of all core/shell pigments is slightly lower compared to PANi. Doping acid affects core/shell pigment blackness poorly, regardless of the PANi content. Figure 12 shows the core/shell pigment blackness vs. PANi content graph.  Despite the high absorption index, black pigments are, usually, diverse in their shade of black. Growth of PANi content in core/shell pigment causes a brown tint for almost all samples, due to the brown aniline oligomers in its content. Their mass is not high enough to count PANi in, but they have a high molecular weight, enough to remain undissolved in acetone while washing off the core/shell pigments. Table 2 shows the comparison of core/shell pigments, with the coating of PANi and common black pigments. It is clear from the table that the core/shell pigments obtained with a PANi shell (20 wt% and more) are similar to iron-black pigment, and an increase in PANi content results in an excess of all optical properties.
Anticorrosive features, also, stand out as an advantage of core/shell pigments. Being  It is clear from the table that the core/shell pigments obtained with a PANi shell (20 wt% and more) are similar to iron-black pigment, and an increase in PANi content results in an excess of all optical properties.
Anticorrosive features, also, stand out as an advantage of core/shell pigments. Being coated, they can possess a barrier effect, due to a lamellar and/or flaky-core shape. PANi presence, also, provides an active anticorrosive defense.
It is essential to know the physical-technical properties of the pigments, besides their optical properties, when it comes to developing polymer-material compositions. The type of doping acid, the PANi content in the core/shell pigment composition, and the core used during synthesis can influence the properties. One of the important indices defining the pigment content in filled material is oil absorption. The presence of a polymer shell increases the surface of the core/shell pigment. Figure 13 shows the oil absorption vs. PANi content in the core/shell pigment. Oil absorption for PANi is much higher, in comparison to the one for initial fillers. This is associated with a larger content of PANi, which has a higher oil absorption compared to the filler used as a core. This is associated with a larger specific surface area of PANi, and, therefore, a large amount of oil is required for wetting the powder (specific surface area core/shell pigment (20% of doped PANi, muscovite-based, H 2 SO 4 as a dopant, 3.1 m 2 /g); specific surface area core/shell pigment (50% of doped PANi, muscovite-based, H 2 SO 4 as a dopant, 9.1 m 2 /g)). Due to a rise in core/shell pigment specific surface area, an increase in PANi content leads to an increase in oil absorption. This holds for all doping agents used. However, for hydrochloric acid as a dopant, the function is a bit more complicated than that for sulfuric and phosphoric acids. PANi shell doping with hydrochloric acid results in the rise of oil absorption to a polymer content of 10 wt.%, and, then, it remains almost immobile up to 50 wt.%. That functional behavior may indicate a complete uniform overlap of the PANi core surface. A similar, anomalous behavior is observed for all core pigments, where hydrochloric acid was used as the PANi doping agent (Figure 14). PANi, muscovite-based, H2SO4 as a dopant, 9.1 m 2 /g)). Due to a rise in core/shell pigment specific surface area, an increase in PANi content leads to an increase in oil absorption. This holds for all doping agents used. However, for hydrochloric acid as a dopant, the function is a bit more complicated than that for sulfuric and phosphoric acids. PANi shell doping with hydrochloric acid results in the rise of oil absorption to a polymer content of 10 wt.%, and, then, it remains almost immobile up to 50 wt.%. That functional behavior may indicate a complete uniform overlap of the PANi core surface. A similar, anomalous behavior is observed for all core pigments, where hydrochloric acid was used as the PANi doping agent ( Figure 14).  For some samples, the extreme type of oil absorption vs. PANi content graph may be attributable to the fact that the maximum oil absorption is observed when the core surface is completely covered by the PANi shell. A further decrease in the function, with an increase in PANi content, occurs due to "secondary fouling" [41,42], which reduces the specific surface area of a core pigment particle.
The density of core/shell pigments heavily depends on the ratio of the inorganic core and organic shell. Furthermore, doping acid can influence the density of obtained pigments, since the producing PANi density changes in accordance with it. Figure 15 shows the effect of PANi content in the core/shell pigment on its density.  For some samples, the extreme type of oil absorption vs. PANi content graph may be attributable to the fact that the maximum oil absorption is observed when the core surface is completely covered by the PANi shell. A further decrease in the function, with an increase in PANi content, occurs due to "secondary fouling" [41,42], which reduces the specific surface area of a core pigment particle. The density of core/shell pigments heavily depends on the ratio of the inorganic core and organic shell. Furthermore, doping acid can influence the density of obtained pigments, since the producing PANi density changes in accordance with it. Figure 15 shows the effect of PANi content in the core/shell pigment on its density. It is clear that the growth of PANi content in core/shell pigment corresponds with density reduction. The reason for that is the lower density of PANi over the starting filler. Therefore, an increase in PANi content leads to a decrease in core/shell pigment density. PANI doping agent, used marginally, affects the core/shell pigment density. The same trends are observed for using other substrates as a core material.
Dispersibility is the other important pigment performance, for making filled materials. Table 3 shows the results of studying the core pigment dispersibility.
It can be seen that, regardless of PANi content, the dispersion rate constant is the highest for all core/shell pigments using hydrochloric acid as a dopant for PANi. The time to reach half of the Kubelka-Munk function limit value lies within 10 min, for most of the core pigments.
That characteristic can be arranged in the following order (Table 4), depending on the core used: muscovite > bentonite > talc > kaolin. So, kaolin-and talc-based core/shell pigment dispersing is the lower energy-intensive process.  It is clear that the growth of PANi content in core/shell pigment corresponds with density reduction. The reason for that is the lower density of PANi over the starting filler. Therefore, an increase in PANi content leads to a decrease in core/shell pigment density. PANI doping agent, used marginally, affects the core/shell pigment density. The same trends are observed for using other substrates as a core material.
Dispersibility is the other important pigment performance, for making filled materials. Table 3 shows the results of studying the core pigment dispersibility.
It can be seen that, regardless of PANi content, the dispersion rate constant is the highest for all core/shell pigments using hydrochloric acid as a dopant for PANi. The time to reach half of the Kubelka-Munk function limit value lies within 10 min, for most of the core pigments.
That characteristic can be arranged in the following order (Table 4), depending on the core used: muscovite > bentonite > talc > kaolin. So, kaolin-and talc-based core/shell pigment dispersing is the lower energy-intensive process.

Conclusions
It was shown that the hiding power of the obtained core/shell pigment samples increases with the increase in PANi content, regardless of the doping agent used. Their coloring strength, also, grows as the PANi content increases. Core/shell pigments with PANi shell doped with phosphoric acid possess the best coloring strength.
In addition, it was demonstrated that the core/shell pigment color shade shifts from a green area to a green-yellow area, with the PANi content increase. This was due to the high content of aniline oligomers. The core/shell pigment blackness depends directly on the PANi content.
It was established that a growth in PANi content leads to an increase in core/shell pigment oil absorption. This results from pigment-specific surface area expansion. It was found that core/shell pigment density reduces with the rise of PANi content, owing to the lower density of the conducting polymer particles.
The core/shell pigment dispersing was studied. It was shown that kaolin-and talcbased core/shell pigments, with PANi shell doped with sulfuric and hydrochloric acids, are well-dispersed.
It was established that core/shell pigments can be used as black pigments in the composition of paints and varnishes.