Patchy Micelles with a Crystalline Core: Self-Assembly Concepts, Properties, and Applications

Crystallization-driven self-assembly (CDSA) of block copolymers bearing one crystallizable block has emerged to be a powerful and highly relevant method for the production of one- and two-dimensional micellar assemblies with controlled length, shape, and corona chemistries. This gives access to a multitude of potential applications, from hierarchical self-assembly to complex superstructures, catalysis, sensing, nanomedicine, nanoelectronics, and surface functionalization. Related to these applications, patchy crystalline-core micelles, with their unique, nanometer-sized, alternating corona segmentation, are highly interesting, as this feature provides striking advantages concerning interfacial activity, functionalization, and confinement effects. Hence, this review aims to provide an overview of the current state of the art with respect to self-assembly concepts, properties, and applications of patchy micelles with crystalline cores formed by CDSA. We have also included a more general discussion on the CDSA process and highlight block-type co-micelles as a special type of patchy micelle, due to similarities of the corona structure if the size of the blocks is well below 100 nm.


Introduction
The solution self-assembly of block copolymers (BCPs) has paved the way to a vast number of micellar assemblies of various shapes (e.g. spheres, cylinders, vesicles, platelets, core-shell, core-shell-corona, and compartmentalized (core or corona) structures) and hierarchical superstructures, as well as hybrids with fascinating applications in drug delivery and release, as emulsifiers/blend compatibilizers, in nanoelectronics, as responsive materials (temperature, pH, light), templates for nanoparticles, in heterogeneous catalysis, etc. [1][2][3][4][5][6]. A key prerequisite for controlling/programming the solution self-assembly is the synthesis of well-defined diblock and triblock (linear, star-shaped, ABA-or ABC-type) copolymers via controlled or living polymerization techniques, such as living anionic polymerization, reversible addition−fragmentation chain transfer, nitroxide-mediated, and atom transfer radical polymerization [5][6][7][8][9]. In general, anisotropic polymer micelles can be divided into three main categories: multicompartment core micelles (MCMs), surface-compartmentalized micelles, and a combination of both [2]. MCMs are generally defined as micellar assemblies with a solvophilic corona and a microphase-separated solvophobic core. According to the suggestion of Laschewsky et al., a key feature of multicompartment micelles is that the various sub-domains in the micellar core feature substantially different properties to behave as separate compartments [10,11]. MCMs are commonly prepared via hierarchical self-assembly of suitable building blocks, which For the preparation of patchy micelles and polymersomes from amorphous BCPs, three main strategies can be applied: (i) self-assembly of ABC triblock terpolymers in selective solvents for the incompatible A and C blocks [42][43][44][45][46][47][48]; (ii) co-assembly of AB and CD diblock copolymers with selective interactions between the B and C blocks (e.g. hydrogen bonding, ionic interactions, solvophobic interactions) [49][50][51][52], resulting in patchy micelles with an insoluble mixed B/C core; and (iii) co-assembly of AB and BC diblock copolymers [53][54][55][56] where the B block forms the insoluble core. However, mostly spherical micelles or polymersomes with a patchy corona have been reported and only a few reports describe the preparation of one-dimensional (worm-like, cylindrical) assemblies with a patch-like compartmentalized corona, even though theoretical work on mixed polymer brushes predict their existence [57][58][59][60][61]. One of the rare but highly intriguing examples are PtBA-b-PCEMA-b-PGMA (poly(tert-butyl acrylate)-block-poly(2-cinnamoyloxyethyl methacrylate)-block-poly(glyceryl monomethacrylate)) and PnBA-b-PCEMA-b-PtBA (PnBA: poly(n-butyl acrylate)) triblock terpolymers [42,43,45]. For self-assembly, the triblock terpolymers were first dissolved in a good solvent for all blocks (CH2Cl2, CHCl3, or THF), followed by the addition of methanol (non-solvent for the middle block) to induce micelle formation. As an intermediate, cylindrical micelles with a patchy corona were formed first, with the PtBA blocks forming small circular patches in a corona mainly consisting of PGMA or PnBA. Upon further decreasing the solvent quality for the PtBA block (addition of MeOH), these cylinders can form double and triple helices via hierarchical self-assembly. This concept has also been applied to triblock terpolymers with a poly(2-hydroxyethyl methacrylate) middle block, having the potential for further modification by esterification of the pendant hydroxy functions [42]. Besides, crystallization- For the preparation of patchy micelles and polymersomes from amorphous BCPs, three main strategies can be applied: (i) self-assembly of ABC triblock terpolymers in selective solvents for the incompatible A and C blocks [42][43][44][45][46][47][48]; (ii) co-assembly of AB and CD diblock copolymers with selective interactions between the B and C blocks (e.g. hydrogen bonding, ionic interactions, solvophobic interactions) [49][50][51][52], resulting in patchy micelles with an insoluble mixed B/C core; and (iii) co-assembly of AB and BC diblock copolymers [53][54][55][56] where the B block forms the insoluble core. However, mostly spherical micelles or polymersomes with a patchy corona have been reported and only a few reports describe the preparation of one-dimensional (worm-like, cylindrical) assemblies with a patch-like compartmentalized corona, even though theoretical work on mixed polymer brushes predict their existence [57][58][59][60][61]. One of the rare but highly intriguing examples are PtBA-b-PCEMAb-PGMA (poly(tert-butyl acrylate)-block-poly(2-cinnamoyloxyethyl methacrylate)-blockpoly(glyceryl monomethacrylate)) and PnBA-b-PCEMA-b-PtBA (PnBA: poly(n-butyl acrylate)) triblock terpolymers [42,43,45]. For self-assembly, the triblock terpolymers were first dissolved in a good solvent for all blocks (CH 2 Cl 2 , CHCl 3 , or THF), followed by the addition of methanol (non-solvent for the middle block) to induce micelle formation. As an intermediate, cylindrical micelles with a patchy corona were formed first, with the PtBA blocks forming small circular patches in a corona mainly consisting of PGMA or PnBA. Upon further decreasing the solvent quality for the PtBA block (addition of MeOH), these cylinders can form double and triple helices via hierarchical self-assembly. This concept has also been applied to triblock terpolymers with a poly(2-hydroxyethyl methacrylate) middle block, having the potential for further modification by esterification of the pendant hydroxy functions [42]. Besides, crystallization-driven self-assembly (CDSA) is a highly versatile tool for the preparation of well-defined cylindrical micelles of controlled length and length distribution, and has proven as a valuable method for the preparation of patchy cylindrical micelles. This review will focus on the recent developments concerning self-assembly strategies for the production of crystalline-core micelles (CCMs) bearing a patchy corona, and will also address their unique properties and potential applications. As stated above, block co-micelles represent a special case of patchy micelles and thus, will be discussed only briefly. This is not only due to the usually larger size and sequential arrangement of surface compartments in the corona, in contrast to the more alternating arrangement in patchy cylindrical micelles (Figure 1b,c), but is also attributed to the substantially different self-assembly procedure. Block co-micelles are commonly prepared by sequential living CDSA of different diblock copolymers, whereas patchy micelles are formed by simultaneous CDSA of diblock copolymer mixtures or CDSA of ABC triblock terpolymers with crystallizable middle blocks. Hence, this review will be divided into four main sections, starting with a general consideration of CDSA. The second part gives a compact overview over self-assembly strategies used to form cylindrical and platelet-like block comicelles. The different self-assembly concepts for patchy micelles with crystalline cores will be reviewed in the third section, followed by a discussion on properties and applications of these interesting compartmentalized nanostructures.

Crystallization-Driven Self-Assembly (CDSA)
As pointed out in the introduction, the preparation of one-dimensional (1D) cylindrical (or worm-like) micelles with controlled dimensions, low-length dispersities, and tailored corona structures and functionalities still remains a challenge in the self-assembly of fully amorphous BCPs. Besides, the introduction of a crystallizable block, which adds an additional and strong driving force for micelle formation, has turned out to be a highly efficient route to solve these issues. Consequently, the self-assembly of such BCPs, bearing crystallizable blocks, is termed crystallization-driven self-assembly (CDSA) [1,62,63]. This field was pioneered by studies on poly(ferrocenyl dimethylsilane) (PFS)-containing BCPs and is gaining increasing importance for the preparation of well-defined 1D and two-dimensional (2D) assemblies, especially since the discovery of living CDSA ( Figure 2) [63][64][65][66][67]. Analogous to the living polymerization of monomers, CDSA can proceed in a living manner, employing small micellar fragments as seeds (Figure 2a: seeded growth) for the addition of unimers (molecularly dissolved BCPs with a crystallizable block). In this approach, the micellar seeds, also termed "stub-like" micelles, are produced by vigorous sonication of long, polydisperse cylindrical micelles prepared by conventional CDSA. Owing to its living nature, the length of the produced cylindrical micelles shows a linear dependence on the unimer/seed ratio employed, and length dispersities are very low (L w /L n typically well below 1.1; where L n is the number average and L w the weight average micelle length).
Living CDSA can also be realized by using spherical CCMs as seeds [68], by self-seeding [69][70][71] (Figure 2a), and even directly by polymerization-induced CDSA (Figure 2b) [72][73][74], i.e., via polymerization in the presence of seed micelles. The selfseeding approach also uses small micellar fragments that are heated in dispersion to a specific annealing temperature (T a ), where most of the crystalline core is molten/dissolved and only a very minor fraction of crystallites survive. These act as seeds in the subsequent CDSA upon cooling (Figure 2a: self-seeding), and the length of the micelles can be controlled by a proper choice of T a . If T a is too low, the crystalline cores will not melt/dissolve, and the length distribution of the employed micellar fragments remains unchanged. On the other hand, if T a is too high, the crystalline cores will melt/dissolve completely, and no crystallites will survive that could act as seeds. As a result, in between these two limiting cases, an increase in micelle length with increasing T a is observed, as the fraction of surviving crystallites (seeds) decreases with T a . This range of self-seeding temperatures can be very restricted, making length control difficult. Another drawback of these seed-based protocols is the low amount of cylindrical micelles that can be produced, as commonly rather dilute solutions have to be used. This can be overcome by the living polymerizationinduced CDSA approach, enabling the production of uniform cylindrical micelles with concentrations up to ca. 10-20% (w/w solids) within a few hours. In a recent report, it was shown that living CDSA can even be stimulated by light, utilizing the photo-induced cis-trans isomerization in oligo(p-phenylenevinylene) (OPV)-based BCPs [75].
3, x FOR PEER REVIEW 4 of 25 dilute solutions have to be used. This can be overcome by the living polymerization-induced CDSA approach, enabling the production of uniform cylindrical micelles with concentrations up to ca. 10-20% (w/w solids) within a few hours. In a recent report, it was shown that living CDSA can even be stimulated by light, utilizing the photo-induced cistrans isomerization in oligo(p-phenylenevinylene) (OPV)-based BCPs [75].
(a) Concepts for living CDSA, enabling the production of cylindrical micelles with defined length and narrow length distribution. Self-seeding employing seeds produced by thermal treatment of micelle fragments (top) and seeded growth using small micellar fragments ("stub"-like micelles) as seeds (bottom). (b) Living polymerization-induced CDSA (PI-CDSA) utilizing micellar seeds during anionic polymerization of the PFS block. After complete conversion, the reaction was quenched with 4-tert-butylphenol. (a) Reproduced from [76] with permission of the American Chemical Society (ACS).

Short Excursion on Block Co-Micelles
Block co-micelles represent a special type of patchy CCM, because of the sequential arrangement of surface compartments and the precisely adjustable size of the blocks, usually leading to larger corona segments than commonly observed for patchy CCMs. Analogous to the synthesis of BCPs, block co-micelles are produced by sequential living CDSA. The characteristic of this process is that the micelles' termini remain "active" after unimer addition is completed. Consequently, addition of a different type of unimer leads to the formation of a blocky structure (Figure 3a) [65,114]. This feature allows for precise control over the block length by adjusting the amount of added unimer. (a) Concepts for living CDSA, enabling the production of cylindrical micelles with defined length and narrow length distribution. Self-seeding employing seeds produced by thermal treatment of micelle fragments (top) and seeded growth using small micellar fragments ("stub"-like micelles) as seeds (bottom). (b) Living polymerization-induced CDSA (PI-CDSA) utilizing micellar seeds during anionic polymerization of the PFS block. After complete conversion, the reaction was quenched with 4-tert-butylphenol. (a) Reproduced from [76] with permission of the American Chemical Society (ACS).

Short Excursion on Block Co-Micelles
Block co-micelles represent a special type of patchy CCM, because of the sequential arrangement of surface compartments and the precisely adjustable size of the blocks, usually leading to larger corona segments than commonly observed for patchy CCMs. Analogous to the synthesis of BCPs, block co-micelles are produced by sequential living CDSA. The characteristic of this process is that the micelles' termini remain "active" after unimer addition is completed. Consequently, addition of a different type of unimer leads to the formation of a blocky structure (Figure 3a) [65,114]. This feature allows for precise control over the block length by adjusting the amount of added unimer. Polymers 2021, 13, x FOR PEER REVIEW 5 of 25  [79] with permission of the American Association for the Advancement of Science (AAAS), (b) reproduced from [67] with permission of the Royal Society of Chemistry (RSC), (c) reproduced from [105], and (d) reproduced from [68] with permission of ACS.
Similar to living polymerization techniques, in which the reactivity of the first monomer limits the choice of a second monomer, unimers need to fulfill certain requirements for successful co-crystallization. For example, the micellar cores need to be compatible for epitaxial crystallization, i.e., they should exhibit a similar crystal lattice spacing [115,116]. A common way to fulfill this prerequisite is the use of diblock copolymers bearing the same crystallizable block that induces homoepitaxial growth, as shown first for PFS-containing diblock copolymers to produce B-A-B triblock co-micelles [65]. Within this work, (c) Laser-scanning confocal microscopy image of solid-state, donor-acceptor, coaxial heterojunction nanowires based on B-A-B segmented nanofibers with a semi-crystalline PDHF core (depicted in blue) and a semi-crystalline P3EHT shell (depicted in red) in the outer corona blocks, taken with both blue (PDHF) and red (P3EHT) channels (scale bar: 10 µm). Blue emission from the central PDHF core, as well as red/orange emission from the outer P3EHT segments, due to Förster resonance energy transfer (FRET) were observed. (d) Schematic depiction of the formation of B-A-B triblock co-micelles with patchy outer corona blocks, starting from SES wCCMs as seed micelles and subsequent living CDSA of SEM unimers in THF (left) and corresponding TEM image of patchy block co-micelles (scale bar: 100 nm). (a) Reproduced from [79] with permission of the American Association for the Advancement of Science (AAAS), (b) reproduced from [67] with permission of the Royal Society of Chemistry (RSC), (c) reproduced from [105], and (d) reproduced from [68] with permission of ACS.
Similar to living polymerization techniques, in which the reactivity of the first monomer limits the choice of a second monomer, unimers need to fulfill certain requirements for successful co-crystallization. For example, the micellar cores need to be compatible for epitaxial crystallization, i.e., they should exhibit a similar crystal lattice spacing [115,116]. A common way to fulfill this prerequisite is the use of diblock copolymers bearing the same crystallizable block that induces homoepitaxial growth, as shown first for PFS-containing diblock copolymers to produce B-A-B triblock co-micelles [65]. Within this work, PFS-b-polyisoprene (PFS-b-PI) cylindrical micelles served as seeds for the nucleation of PFS-b-polymethylvinylsilane (PFS-b-PMVS) and PFS-b-polydimethylsiloxane (PFS-b-PDMS) unimers, respectively. For heteroepitaxial growth, different PFS-containing seed micelles were applied to induce CDSA of polyferrocenylgermane (PFG)-containing diblock copolymers [73,83,89]. The crystal lattice spacing of the two core-forming blocks only differs by about 6%, enabling the formation of tri-and pentablock co-micelles as well as 2D co-assemblies.
Living CDSA has opened the door to a huge variety of one dimensional, PFScontaining block co-micelles with tailored numbers, lengths, and composition of corona blocks [114,[117][118][119][120][121]. Centrosymmetric and non-centrosymmetric block co-micelles are accessible, and give rise to broad structural complexity [79]. In particular, the introduction of fluorescent corona blocks marks an important step in the development of block co-micelles, since this enables the formation of barcode and RGB micelles ( Figure 3b) [67,77,122]. Up to that point, the fabrication of cylindrical nanomaterials with precise, color-tunable compartments of predictable length and number was challenging. Moreover, it is possible to induce fluorescence in the semicrystalline core-forming block by replacing the PFS block by a poly(di-n-hexylfluorene) (PDHF) block [78]. B-A-B triblock co-micelles with PDHF core and P3HT outer corona blocks were found to show long-range exciton transport (>200 nm). Inducing secondary crystallization of a poly(3-(2'-hexylethyl)thiophene) (P3EHT) corona block even rendered solid-state donor-acceptor heterojunctions possible ( Figure 3c) [105]. These materials bear a high potential for applications in optoelectronics, device fabrication, and sensing [123].
The scope of complex micellar assemblies is further extended by hierarchical selfassembly, using block co-micelles as building blocks for the formation of 2D and threedimensional (3D) superstructures. There are different strategies to realize hierarchical assemblies-for example, coordination-driven co-assembly [129] or dialysis of amphiphilic block co-micelles against selective solvents, enabling highly efficient side-by-side or endto-end stacking (Figure 4a,b) [88,130,131], or spatially confined hydrogen-bonding interactions [132,133]. The latter opens access to numerous hierarchical 2D morphologies, such as "I"-shaped, cross, shish-kebab ( Figure 4c) or windmill-like ( Figure 4d) structures, by precisely tailored interactions between hydrogen donor and hydrogen acceptor units within the block co-micelles. However, not only the attractive interactions by hydrogen-bonding have to be taken into account, but also repulsive interactions caused by steric hindrance of the corona chains. To overcome this problem, tuning the length of the hydrogen acceptor blocks has proven to be a suitable solution, rendering 3D assemblies possible. It is noted that 2D platelet-like hierarchical superstructures, as well as more complex micelle architectures like double-and single-headed, spear-like micelles [90], scarf-like micelles [89], diamond-fiber hybrid structures [81], or platelets with various shapes (rectangular, quasihexagonal, and diamond platelet micelles) [82][83][84][85] are accessible.   [88] with permission of AAAS, (c) reproduced from [133] with permission of ACS, and (d) from [132] with permission of Springer Nature.

CDSA of Linear and Star-Shaped Triblock Terpolymers
The most widely used route toward crystalline-core patchy micelles is the CDSA of linear ABC triblock terpolymers with a crystallizable middle block (Table 1) [134]. In contrast to block co-micelles, where the sequential living CDSA of different diblock copolymers results in a block-type segmentation of the corona, the incompatibility of the coronaforming blocks is the driving force for corona segregation in CDSA of triblock terpolymers. This affects the average width of the patches and leads to an alternating, chessboard-like arrangement of the corona patches [135]. Worm-like CCMs (wCCMs) with a patchy corona were first reported in 2008 for triblock terpolymers with a semicrystalline PE middle block and two amorphous outer blocks, namely PS and PMMA (SEM) [93]. Since patchy, worm-like (or cylindrical) CCMs based on these triblock terpolymers have been intensively studied, the self-assembly mechanism will be elucidated in detail on this example. Windmill"-like supermicelles via living CDSA of a PFS-b-PtBA diblock copolymer from "cross" supermicelles (scale bar = 0.5 µm). The "cross" supermicelles featured an H-bond acceptor corona block (P2VP) at the termini, onto which short CCMs with H-bond donor corona blocks (PMVSOH) that served as seeds for the subsequent living CDSA of the PFS-b-PtBA diblock copolymer (color code identical to (c)) were immobilized. (a,b) reproduced from [88] with permission of AAAS, (c) reproduced from [133] with permission of ACS, and (d) from [132] with permission of Springer Nature.

CDSA of Linear and Star-Shaped Triblock Terpolymers
The most widely used route toward crystalline-core patchy micelles is the CDSA of linear ABC triblock terpolymers with a crystallizable middle block (Table 1) [134]. In contrast to block co-micelles, where the sequential living CDSA of different diblock copolymers results in a block-type segmentation of the corona, the incompatibility of the corona-forming blocks is the driving force for corona segregation in CDSA of triblock terpolymers. This affects the average width of the patches and leads to an alternating, chess-board-like arrangement of the corona patches [135]. Worm-like CCMs (wCCMs) with a patchy corona were first reported in 2008 for triblock terpolymers with a semicrystalline PE middle block and two amorphous outer blocks, namely PS and PMMA (SEM) [93]. Since patchy, worm-like (or cylindrical) CCMs based on these triblock terpolymers have been intensively studied, the self-assembly mechanism will be elucidated in detail on this example.
Initially, the SEM triblock terpolymers are placed in a good solvent for the amorphous blocks and heated above the melting temperature of the semicrystalline PE block in the given solvent (Figure 5a) [94]. Depending on the solvent quality for the PE middle block, different micelle morphologies are formed. In good solvents for the molten PE block (for example, THF or toluene), the triblock terpolymers are molecularly dissolved, i.e., unimers are formed. In bad solvents for PE (for example 1,4-dioxane), the molten PE block collapses, and spherical micelles with an amorphous (molten) PE core are observed. Cooling of the corresponding unimer solution (in good solvents) or dispersion of spherical micelles (bad solvents) results in the nucleation of PE crystallization. In good solvents, the nuclei are stable and able to initiate the bidirectional, 1D epitaxial growth of the remaining unimers to generate wCCMs. However, in bad solvents, the spherical shape of the micelles dictates the final morphology of the CCMs. Consequently, confined crystallization of PE in the respective micellar cores leads to the generation of spherical CCMs. In both cases, the micelle corona exhibits a patch-like, microphase-separated (patchy) structure, whereas for wCCMs the patchy structure of the corona is more pronounced (Figure 5b,c). For wCCMs, an almost alternating arrangement of the PS and PMMA patches in the corona can be deduced from transmission electron microscopy (TEM) [94], and was also confirmed by small-angle neutron scattering studies [135]. Table 1. Overview of self-assembly concepts for patchy micelles with a crystalline core.

Self-Assembly Concept
Employed BCPs Special Feature Reference

CDSA of triblock terpolymers
Linear triblock terpolymers Control over micelle morphology, length control through seeded growth, co-crystallization with PS-b-PE-b-PS [93,94,[134][135][136] PS-b-PE-b-PDxA 1 Functional groups for NP incorporation [137,138] PS-b-PFS-b-PMMA Control over patch size, co-crystallization with diblock co-polymers of varying PS and PMMA block lengths Length control through seeded growth [140] Star-shaped triblock terpolymers µ-SIF Seeded growth, block co-micelles with patchy µ-SIF outer blocks, and middle block based on PFS-b-PDMS [141] Non-covalent grafting on carbon nanotubes PS-b-PE-b-PMMA Temperature-stable patchy hybrid materials [142] Co-assembly of diblock copolymers A facile way to tailor the sizes of the PS and PMMA corona patches is random cocrystallization of an SEM triblock terpolymer with a corresponding SES triblock copolymer, bearing two PS end blocks [136]. A systematic increase of the SES fraction led to a decrease of the PMMA patch size (Figure 7a). Thus, this approach allows to tune the corona structure by a simple co-assembly without the need to synthesize new triblock terpolymers for each desired corona composition. Another efficient way to modify the corona patches is the introduction of functional groups via selective amidation of the PMMA block in SEM triblock terpolymers with different N,N-dialkylethylenediamines [137,138]. CDSA in THF led to patchy wCCMs, for which the patch size and shape could be tuned by varying the block length ratio of the corona blocks (Figure 7b,c) and selective solvent interactions. The functionalized, patchy corona enables an application of these wCCMs as templates for the incorporation of inorganic nanoparticles (NPs), which will be discussed in detail in Section 5.2.
Polymers 2021, 13, x FOR PEER REVIEW 9 of 25 can be deduced from transmission electron microscopy (TEM) [94], and was also confirmed by small-angle neutron scattering studies [135]. Figure 5. (a) Schematic representation of the proposed mechanism for the formation of patchy worm-like and spherical crystalline-core micelles (wCCMs and sCCMs, respectively) from SEM triblock terpolymers (PS blocks are represented in blue, PE in black, and PMMA in red). TEM images of (b) patchy S340E700M360 wCCMs prepared by CDSA in THF and subsequent annealing at 45 °C for 3 h, and (c) patchy S340E700M360 sCCMs formed in dimethylacetamide (subscripts denote the respective average degrees of polymerization, PS was selectively stained with RuO4 vapor and appears dark). Reproduced from [94] with permission of ACS.
A facile way to tailor the sizes of the PS and PMMA corona patches is random cocrystallization of an SEM triblock terpolymer with a corresponding SES triblock copolymer, bearing two PS end blocks [136]. A systematic increase of the SES fraction led to a decrease of the PMMA patch size (Figure 6a). Thus, this approach allows to tune the co- Figure 5. (a) Schematic representation of the proposed mechanism for the formation of patchy wormlike and spherical crystalline-core micelles (wCCMs and sCCMs, respectively) from SEM triblock terpolymers (PS blocks are represented in blue, PE in black, and PMMA in red). TEM images of (b) patchy S 340 E 700 M 360 wCCMs prepared by CDSA in THF and subsequent annealing at 45 • C for 3 h, and (c) patchy S 340 E 700 M 360 sCCMs formed in dimethylacetamide (subscripts denote the respective average degrees of polymerization, PS was selectively stained with RuO 4 vapor and appears dark). Reproduced from [94] with permission of ACS.
The patchy corona structure of SEM wCCMs can also be transferred to multiwalled carbon nanotubes (CNTs) by a non-covalent grafting approach that forms 1D patchy hybrids (Figure 7d) [142]. In contrast to CDSA, which is commonly used to obtain patchy wCCMs, these patchy hybrids were prepared by an ultrasound-assisted process. Here, the PE block selectively adsorbs onto the CNT surface, while the soluble PS and PMMA blocks form the patchy corona. The driving force for CNT functionalization is the high affinity of the PE block to the CNT surface, which was supported by the use of a SEM triblock terpolymer, which is not able to crystallize at room temperature, but successfully generates patchy CNT hybrids.
Different attempts were made to exchange the PE block with another crystallizable block in order to generate patchy wCCMs. Successful examples are triblock terpolymers of PS-b-PFS-b-PMMA, PS-b-PFS-b-PMVS, and PI-b-PFS-b-PMMA [139,140], as well as µ-ABC miktoarm star terpolymers with a crystallizable PFS block (Figure 6a) [141]. The PFS-containing triblock terpolymers were able to undergo a seeded growth protocol for living CDSA in different solvents to form patchy wCCMs of predictable length (Figure 6b). Remarkably, the living CDSA of all triblock terpolymers proceeded rather slowly compared to PFS-containing diblock copolymers, which was attributed to two effects: (i) the comparably high steric hindrance caused by the two corona blocks surrounding the core-forming block, and (ii) the choice of solvent, which did not sufficiently support the crystallization of PFS. For the PS-b-PFS-b-PMMA triblock terpolymers, the corona chain length (core to total corona block ratio) was varied, and co-crystallization of the resulting triblock terpolymers resulted in block co-micelles with a patchy corona. Interestingly, the different micelle blocks were still discernible by TEM analysis because of the different corona thicknesses (Figure 6c). the PE block to the CNT surface, which was supported by the use of a SEM triblock terpolymer, which is not able to crystallize at room temperature, but successfully generates patchy CNT hybrids. Different attempts were made to exchange the PE block with another crystallizable block in order to generate patchy wCCMs. Successful examples are triblock terpolymers of PS-b-PFS-b-PMMA, PS-b-PFS-b-PMVS, and PI-b-PFS-b-PMMA [140,141], as well as µ-ABC miktoarm star terpolymers with a crystallizable PFS block (Figure 7a) [142]. The PFS-containing triblock terpolymers were able to undergo a seeded growth protocol for living CDSA in different solvents to form patchy wCCMs of predictable length ( Figure  7b). Remarkably, the living CDSA of all triblock terpolymers proceeded rather slowly compared to PFS-containing diblock copolymers, which was attributed to two effects: (i) the comparably high steric hindrance caused by the two corona blocks surrounding the core-forming block, and (ii) the choice of solvent, which did not sufficiently support the crystallization of PFS. For the PS-b-PFS-b-PMMA triblock terpolymers, the corona chain length (core to total corona block ratio) was varied, and co-crystallization of the resulting triblock terpolymers resulted in block co-micelles with a patchy corona. Interestingly, the different micelle blocks were still discernible by TEM analysis because of the different corona thicknesses (Figure 7c).  rona patches is the introduction of functional groups via selective amidation of the PMMA block in SEM triblock terpolymers with different N,N-dialkylethylenediamines [137,138]. CDSA in THF led to patchy wCCMs, for which the patch size and shape could be tuned by varying the block length ratio of the corona blocks (Figure 6b,c) and selective solvent interactions. The functionalized, patchy corona enables an application of these wCCMs as templates for the incorporation of inorganic nanoparticles (NPs), which will be discussed in detail in Section 5.2. Figure 6. (a) Random co-crystallization of a SES triblock copolymer and a SEM triblock terpolymer, in order to tune the size of the corona patches. TEM images of patchy wCCMs obtained by co-crystallization of S380E880S390 with S340E700M360 in THF (subscripts denote the respective average degrees of polymerization), revealing a decreasing size of the bright-appearing PMMA corona patches with an increasing amount of S380E880S390 (scale bars: 100 nm). TEM images of patchy (b) S415E830DMA420 and (c) S660E1350DMA350 wCCMs (DMA: N,N-dimethylaminoethyl methacrylamide), as well as (d) 1D patchy hybrids with a CNT core and a patchy PS/PMMA corona prepared by ultrasound-assisted, non-covalent grafting of an SEM triblock terpolymer onto CNTs. For all samples, PS was selectively stained with RuO4 vapor and appears dark. (a) Reproduced from [136] with permission of Elsevier, (b,c) reprinted from [138] with permission of RSC, and (d) reproduced from [139] with permission of ACS.
The patchy corona structure of SEM wCCMs can also be transferred to multiwalled carbon nanotubes (CNTs) by a non-covalent grafting approach that forms 1D patchy hybrids (Figure 6d) [139]. In contrast to CDSA, which is commonly used to obtain patchy wCCMs, these patchy hybrids were prepared by an ultrasound-assisted process. Here, the PE block selectively adsorbs onto the CNT surface, while the soluble PS and PMMA blocks form the patchy corona. The driving force for CNT functionalization is the high affinity of  [136] with permission of Elsevier, (b,c) reprinted from [138] with permission of RSC, and (d) reproduced from [142] with permission of ACS.

Co-Assembly of Diblock Copolymers
The simultaneous co-assembly of PFS-based diblock copolymers represents an alternative way of producing patchy, cylindrical CCMs, next to the use of synthetically more demanding linear or star-shaped triblock terpolymers (Table 1). However, the corona patches of the resulting micelles are usually arranged in a blocky rather than an alternating manner. Consequently, the micelles produced with this approach represent a special case of patchy CCMs. The first example of these patchy block co-micelles was reported in 2014, and is based on the co-crystallization of linear and brush-type BCPs with a crystallizable PFS block [143]. Starting from a linear PFS-b-PMVS diblock copolymer, the PMVS corona block was alkylated via thiol-ene functionalization, in order to yield a brush-type BCP with pendant C18 alkyl chains. The brush-type BCPs showed poor crystallization behavior, due to the steric repulsion of the alkyl moieties. However, simultaneous co-crystallization with the linear BCP, applying cylindrical PFS-b-PDMS seed micelles, resulted in a gradual integration of the brush-type unimers. Hence, a patchy corona segmentation of the end blocks was observed for the produced B-A-B triblock co-micelles by TEM and atomic force microscopy (AFM) (Figure 8a).
case of patchy CCMs. The first example of these patchy block co-micelles was reported in 2014, and is based on the co-crystallization of linear and brush-type BCPs with a crystallizable PFS block [143]. Starting from a linear PFS-b-PMVS diblock copolymer, the PMVS corona block was alkylated via thiol-ene functionalization, in order to yield a brush-type BCP with pendant C18 alkyl chains. The brush-type BCPs showed poor crystallization behavior, due to the steric repulsion of the alkyl moieties. However, simultaneous cocrystallization with the linear BCP, applying cylindrical PFS-b-PDMS seed micelles, resulted in a gradual integration of the brush-type unimers. Hence, a patchy corona segmentation of the end blocks was observed for the produced B-A-B triblock co-micelles by TEM and atomic force microscopy (AFM) (Figure 8a). (a) Reprinted from [143], (b,c) reprinted from [145] with permission of ACS, and (d,e) reproduced from [80] with permission of RSC.
The preparation of patchy block co-micelles is not limited to sterically demanding coblocks, but can be induced by a strong difference in the Flory-Huggins interaction parameter between the corona-forming blocks [144]. Blends of PFS-b-PDMS with PFS-b-PMVS and PFS-b-PI, respectively, were co-crystallized, resulting in a blocky corona segmenta- (a) Reprinted from [143], (b,c) reprinted from [145] with permission of ACS, and (d,e) reproduced from [80] with permission of RSC.
The preparation of patchy block co-micelles is not limited to sterically demanding co-blocks, but can be induced by a strong difference in the Flory-Huggins interaction parameter between the corona-forming blocks [144]. Blends of PFS-b-PDMS with PFSb-PMVS and PFS-b-PI, respectively, were co-crystallized, resulting in a blocky corona segmentation. Staining with Karstedt's catalyst (selective for PI and PMVS) revealed the small corona patches and made two different patch arrangements visible (helical pattern and hemispherical shape). In a subsequent study, the competitive seeded-growth kinetics of the simultaneous co-crystallization of diblock copolymers bearing different corona blocks was investigated [145]. To this end, PFS-b-poly(2-vinylpyridine) (PFS-b-P2VP) was co-crystallized with two different PFS-b-poly(N-isopropyl acrylamide) (PFS-b-PNiPAM) diblock copolymers using short PFS-b-P2VP seed micelles. The length of the PFS block was similar in all used diblock copolymers, but the corona block length of the PFS-b-PNiPAM diblock copolymers differed, which affected the epitaxial growth rate of the PFS-b-PNiPAM unimers on the seed micelles. If this growth rate was comparable to that of the competing PFS-b-P2VP unimers, patchy micelles were observed (Figure 8b). If, on the other hand, the growth rates of the two competing diblock copolymers differed significantly, the formation of block co-micelles was preferred (Figure 8c). Additionally, the epitaxial growth rate of the PFS-b-P2VP diblock copolymers was manipulated by quaternization of the P2VP block, which generated a permanent positive charge within the corona chains. Co-crystallization with a PFS-b-PNiPAM diblock copolymer, which yielded a patchy structure with the non-quaternized PFS-b-P2VP, then led to a blocky arrangement of the patches, which could again be attributed to the differing epitaxial growth rates.
Beyond changes in the epitaxial growth rate by manipulation of the corona chains, the crystallization behavior of the PFS core block can also be altered [80]. A variation in the PFS block length affects the so-called critical dissolution temperature (T c ). This temperature describes the point at which the initial average micelle length doubles upon cooling. Heating a mixture of two different micelle fragments with similar T c values to an annealing temperature (T a ), and T a < T c results in separate micelle fragments. If T a is in the range of the T c of both micellar fragments, the micellar fragments dissolve partly, and tadpole-shaped fragments are observable. If T a > T c , self-seeding is taking place and the growth kinetics are dictated by the epitaxial growth rates of the two competing unimer types, i.e., a patchy morphology is observed for similar growth rates and a blocky arrangement of the patches results from dissimilar growth rates (Figure 8d). The selfseeding behavior changes if two diblock copolymers with different T c values are employed. If T a is raised above the T c of one of the diblock copolymers, but is still lower than the T c of the other diblock copolymer, the diblock copolymer with the lower T c will partly or almost fully dissolve and epitaxially grow from the remaining micelle seed fragments of both diblock copolymers. This results in either match stick-like micelles or block comicelles. If T a is increased well above the T c of both diblock copolymers, again the growth kinetics determine the final observable corona arrangement-i.e., for similar growth rates, a patchy segmentation is generated (Figure 8e). This concept can also be transferred to mixtures of PFS homopolymers and PFS-based BCPs [146]. Due to the higher T c of the PFS homopolymer, a certain fraction of PFS homopolymer crystal fragments will survive upon proper choice of T a ; these fragments then act as seeds upon subsequent cooling and annealing. This not only allows the production of cylindrical micelles of uniform length, but also of well-defined block co-micelles or patchy micelles employing a mixture of PFS with different PFS-based BCPs. An important feature of this approach with respect to applications is the comparably easy scale-up, enabling the production of uniform cylindrical micelles of controlled architecture up to concentrations of 10% (w/w solids) or more.

Interfacial Activity and Blend Compatibilization
The alternating, patch-like arrangement in the corona of worm-like (or cylindrical) patchy CCMs offers a high potential for a variety of applications. As was shown for amorphous Janus micelles, polymer particles exhibiting two opposing faces made of PS and PMMA (or poly(tert-butyl methacrylate)) serve as excellent particulate surfactants and compatibilizers in polymer blends [147][148][149][150][151][152][153][154][155][156][157][158]. This originates from the unique interfacial activity of these materials [38]. Patchy wCCMs were proven to show not only a superior interfacial activity compared to cylindrical micelles with a homogeneous PS corona, but also an identical interfacial activity compared to that of Janus micelles at a water-toluene interface (Figure 9a) [159]. Although Janus particles consist of only two clearly separated compartments (or faces), which facilitates the orientation at interfaces, the unique corona structure of patchy micelles is able to adapt to the requirements of the interface, i.e., the respective insoluble block will collapse and the soluble block will expand. Depending on the molecular weight of the corona-forming blocks and thus, the thickness of the corona, the interfacial activity could be tuned, and was shown to increase with thickness (at constant micelle length), which is in good agreement with theoretical predictions [160]. Interestingly, patchy SEM wCCMs can also be hierarchically assembled by a confinement process through emulsification in a toluene-in-water emulsion and subsequent evaporation of the solvents. This leads to microparticles with a highly ordered hexagonal close-packed lattice structure [161]. the interfacial activity could be tuned, and was shown to increase with thickness (at constant micelle length), which is in good agreement with theoretical predictions [160]. Interestingly, patchy SEM wCCMs can also be hierarchically assembled by a confinement process through emulsification in a toluene-in-water emulsion and subsequent evaporation of the solvents. This leads to microparticles with a highly ordered hexagonal close-packed lattice structure [161].  The excellent interfacial activity of patchy wCCMs can be harnessed for the efficient compatibilization of polymer blends, as reported for solvent-cast PS/PMMA (80/20 w/w) blends [162]. In this work, SEM triblock terpolymers were non-covalently grafted onto the surface of multiwalled CNTs, in order to obtain temperature-stable hybrid compatibilizers with a patchy PS/PMMA corona (patchy CNTs, Figure 7d). The performance of these hybrid compatibilizers was studied depending on their weight fraction, revealing that an increasing filler content considerably reduced the size of the PMMA droplets (minority component) in the blends down to 0.13 µm 2 for the blend with 9 wt.% patchy CNTs (Figure 9b,c). Remarkably, the obtained PMMA domain areas were significantly lower compared to that achieved by using Janus cylinders (L = 2.3 µm, biphasic PS/PMMA corona) as compatibilizers, resulting in domain areas of 10.2 µm 2 and 1.77 µm 2 for 5 wt.% and 10 wt.% Janus cylinders (PS/PMMA = 80/20 w/w), respectively [163]. In addition, the TEM image taken at higher magnification (inset of Figure 9b) shows that well-dispersed patchy CNTs are not only located at the PS/PMMA interface, but are also homogeneously distributed in the PS and PMMA phase. The homogeneous distribution of the patchy CNTs, together with their superior compatibilizing efficiency, can be again attributed to the unique feature of the patchy corona, being able to adapt to their surroundings (PS/PMMA interface, or neat PS and PMMA phases) by selective collapse/expansion of the corona blocks.

Nanoparticle Templates/Hybrids
Metal and metal oxide NPs are highly attractive materials for a multitude of applications, such as optics, medicine, electronics, or catalysis, originating from their unique optical properties and high surface-to-volume ratio [164][165][166][167][168][169][170][171]. However, the high surface area is an ambivalent feature, as it is useful, for example, in catalysis, but considerably limits the overall stability of NP dispersions, due to agglomeration and Ostwald ripening. Here, the stabilization of NPs with ligands has proven to be a convenient solution to overcome this substantial drawback [172][173][174][175]. Another highly efficient method is the use of micellar nanostructures to selectively embed the NPs within functional surface compartments, which not only act as ligands for the NPs, but also keep the NPs' surface accessible and inhibits agglomeration due to spatial separation [38,117,118,127,137,176,177].
In particular, patchy wCCMs, with their well-defined, alternating segmented coronas, have been shown to be versatile NP templates, and even allow the regio-selective incorporation of two different NP types, since the chemistry of the two corona-forming blocks can be tailored to the specific needs of the respective NP [137,138]. In order to obtain these binary-loaded hybrid materials, based on patchy PS-b-PE-b-poly(dimethylaminoethyl methacrylamide) (SEDMA) wCCMs, a two-step procedure for the selective decoration of the patches with NPs was developed (Figure 10a). In the first step, preformed, PS-stabilized gold NPs were mixed with a dispersion of the functional patchy wCCMs, followed by the addition of acetone as a selective solvent for the PDMA block, resulting in a collapse of the PS chains. Due to selective interactions of the PS corona block and the PS-stabilized gold NPs, the NPs were enclosed within the PS patches upon collapse of the PS chains. In the following step, preformed, acetate-stabilized zinc oxide NPs were incorporated in the functional patches by a ligand exchange method. Intrinsic staining provided by the inorganic NPs facilitated an examination of the resulting structures via TEM (Figure 10b,c). The different types of NPs are clearly discernible by their different diameters (D; D gold NP = 7.9 nm, D zinc oxide NP = 2.7 nm) and the contrast (heavy metals generate a higher contrast in TEM compared to transition metal oxides). Interestingly, despite the small size of the corona patches (<20 nm), it seems that more than one NP per patch is observable. This might be attributed to the extremely small size of the chosen inorganic NPs (<10 nm).
The selective functionalization of surface-compartmentalized polymeric micelles with inorganic NPs was also shown for PFS-containing triblock co-micelles, featuring a quaternized P2VP corona in the middle [117,118]. Through electrostatic interactions, the middle block was selectively loaded with mercaptoacetic acid-stabilized gold NPs, PbS quantum dots and dextran-magnetite NPs, demonstrating the versatility of block co-micelles as NP templates. Furthermore, NP hybrid materials with block co-micelles derived from co-assembly of diblock copolymers were reported. Here, the spatially confined incorporation of platinum NPs and CdSe quantum dots was enabled by selective interactions with functional corona patches [146,178].

Heterogeneous Catalysis
As mentioned in the previous section, an application of noble metal and metal oxide NPs in catalysis is highly desirable, because of the high catalytically active surface area of the employed NPs. However, ligands, which are needed for stabilization of the NPs, might inhibit the superior catalytic activity of the NPs by blocking the surface. Even for tailor-made ligands, this is a distinct drawback, since these materials are usually hard to recover after usage. A separation of the catalytically active species from the reaction medium is challenging and expensive. Immobilizing the catalytically active NPs on suitable supports (e.g., inorganic, polymeric) solves this problem of recoverability, while preserving the activity and accessibility of the NPs' surface [179][180][181][182][183][184][185]. Nonetheless, agglomeration of the inorganic NPs on the surface of the heterogeneous supports can occur if the NPs are insufficiently confined, resulting in a significant loss of activity over several consecutive catalysis cycles.

EER REVIEW
16 of 25 quantum dots and dextran-magnetite NPs, demonstrating the versatility of block co-micelles as NP templates. Furthermore, NP hybrid materials with block co-micelles derived from co-assembly of diblock copolymers were reported. Here, the spatially confined incorporation of platinum NPs and CdSe quantum dots was enabled by selective interactions with functional corona patches [146,178]. (c) Bright-field (left) and high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM, right) images, clearly revealing the binary loading with two different NP types. Reproduced and adapted from [138] with permission of RSC.

Heterogeneous Catalysis
As mentioned in the previous section, an application of noble metal and metal oxide NPs in catalysis is highly desirable, because of the high catalytically active surface area of the employed NPs. However, ligands, which are needed for stabilization of the NPs, might inhibit the superior catalytic activity of the NPs by blocking the surface. Even for tailor-made ligands, this is a distinct drawback, since these materials are usually hard to recover after usage. A separation of the catalytically active species from the reaction medium is challenging and expensive. Immobilizing the catalytically active NPs on suitable supports (e.g., inorganic, polymeric) solves this problem of recoverability, while preserving the activity and accessibility of the NPs' surface [179][180][181][182][183][184][185]. Nonetheless, agglomeration of the inorganic NPs on the surface of the heterogeneous supports can occur if the NPs are insufficiently confined, resulting in a significant loss of activity over several consecutive catalysis cycles.
The highly regular, alternating arrangement of the corona compartments in patchy wCCMs allows us to efficiently confine inorganic NPs. However, these micellar templates have to be immobilized on a solid support, which provides high accessibility of the reac- The highly regular, alternating arrangement of the corona compartments in patchy wCCMs allows us to efficiently confine inorganic NPs. However, these micellar templates have to be immobilized on a solid support, which provides high accessibility of the reactants to the catalytically active NPs and easy recovery in order to harness these structures for heterogeneous catalysis. This issue was overcome by coating different patchy PS-b-PEb-poly(dialkylaminoethyl methacrylamide) wCCMs onto the surface of PS nonwovens by means of coaxial electrospinning (Figure 11a,b) [186,187]. The resulting patchy nonwovens were loaded with gold NPs through a simple dip-coating process (Figure 11c), which was driven by a ligand exchange reaction. The hybrid nonwovens were successfully applied as catalysts for the alcoholysis of dimethylphenylsilane (Figure 11d) at room temperature, showing a comparable or even higher catalytic activity than other supports reported before [188][189][190][191][192][193]. Moreover, the employed patchy hybrid nonwovens were easily recoverable from the reaction medium and reusable in at least 10 consecutive catalysis cycles. at room temperature, showing a comparable or even higher catalytic activity than other supports reported before [188][189][190][191][192][193]. Moreover, the employed patchy hybrid nonwovens were easily recoverable from the reaction medium and reusable in at least 10 consecutive catalysis cycles. Figure 11. (a) Catalytically active, hybrid nonwovens prepared by a combination of bottom-up (CDSA) and top-down (coaxial electrospinning) approaches. In the first step, patchy nonwovens were prepared by decorating a PS nonwoven with functional, patchy PS-b-PE-b-poly(dialkylaminoethyl methacrylamide) wCCMs by coaxial electrospinning (PS patches are depicted in blue and the functional, tertiary amino group containing patches in red). Subsequently, the patchy nonwovens were loaded with citrate-stabilized Au NPs via a ligand exchange process (citrate against tertiary amino groups in functional patches). (b) Scanning electron microscopy images of a patchy nonwoven (based on S415E830DMA420 wCCMs) before and (c) after loading with Au NPs (back-scattered electron detector). (d) Au NP-catalyzed alcoholysis of dimethylphenylsilane in nbutanol. (e) Kinetics of the Au NP-catalyzed alcoholysis of dimethylphenylsilane in n-butanol, employing patchy hybrid nonwovens as catalysts (DiPA = poly(diisopropylaminoethyl methacrylamide). Reproduced from [186] with permission from RSC.
Since this system offers different possibilities to tune the catalytic activity, an indepth study on the influence of the patch size and chemistry on the reaction kinetics was conducted. Here, an extended first-order kinetics model was employed, which includes the induction periods observed in the catalytic alcoholysis of dimethylphenylsilane in nbutanol. This study revealed a strong dependence on the accessibility of the reactants to the gold NPs' surface, being mainly controlled by the swellability of the functional patches in n-butanol. The latter depends on both patch chemistry, i.e., poly(N,N-dimethylami- Figure 11. (a) Catalytically active, hybrid nonwovens prepared by a combination of bottom-up (CDSA) and top-down (coaxial electrospinning) approaches. In the first step, patchy nonwovens were prepared by decorating a PS nonwoven with functional, patchy PS-b-PE-b-poly(dialkylaminoethyl methacrylamide) wCCMs by coaxial electrospinning (PS patches are depicted in blue and the functional, tertiary amino group containing patches in red). Subsequently, the patchy nonwovens were loaded with citrate-stabilized Au NPs via a ligand exchange process (citrate against tertiary amino groups in functional patches). (b) Scanning electron microscopy images of a patchy nonwoven (based on S 415 E 830 DMA 420 wCCMs) before and (c) after loading with Au NPs (back-scattered electron detector). (d) Au NP-catalyzed alcoholysis of dimethylphenylsilane in n-butanol. (e) Kinetics of the Au NP-catalyzed alcoholysis of dimethylphenylsilane in n-butanol, employing patchy hybrid nonwovens as catalysts (DiPA = poly(diisopropylaminoethyl methacrylamide). Reproduced from [186] with permission from RSC.
Since this system offers different possibilities to tune the catalytic activity, an in-depth study on the influence of the patch size and chemistry on the reaction kinetics was conducted. Here, an extended first-order kinetics model was employed, which includes the induction periods observed in the catalytic alcoholysis of dimethylphenylsilane in n-butanol. This study revealed a strong dependence on the accessibility of the reactants to the gold NPs' surface, being mainly controlled by the swellability of the functional patches in n-butanol. The latter depends on both patch chemistry, i.e., poly(N,N-dimethylaminoethyl methacrylamide) (PDMA, more hydrophilic) vs. poly(N,N-diisopropylaminoethyl methacrylamide) (PDiPA, more hydrophobic) patches, as well as size. As a result, significantly longer induction (t ind ) and reaction (t R ) times were observed for the first catalysis cycles compared to the tenth cycles (Figure 11e). Nonwovens with more polar PDMA patches were the most efficient in NP stabilization (prevention of agglomeration), but showed a significantly lower t R in the first catalysis cycle, due to a strong interaction with the gold NPs' surface. Thus, precise tuning of the patch size and chemistry is needed to optimize the catalysts performance. However, the modular design of the patchy hybrid nonwovens enables a facile adaption to the needs of different catalysis systems-for example, by an exchange of the support material or by varying the type of NPs. Moreover, it is possible to render the functionalized patches thermo-responsive [194], which opens access to catalytic reactions regulated by an inherent temperature control.

Conclusions and Outlook
From a conceptual point of view, several strategies exist for the production of patchy micelles with crystalline cores, such as CDSA of triblock terpolymers with crystallizable middle blocks, miktoarm stars, or the co-assembly of diblock copolymers with a common crystallizable block but different corona-forming blocks. However, so far, patchy micelles have been reported only for BCPs with PE or PFS as crystallizable blocks, despite the fact that a large variety of crystallizable polymer blocks has already been utilized in CDSA. Here, ring-opening polymerization of lactones or lactides, in combination with controlled radical polymerization techniques, might be another promising alternative, as BCPs based on PCL or PLLA as crystallizable blocks are readily accessible. Moreover, PFS could be replaced by ruthenocene-based BCPs, which show a higher degree of crystallinity but are less studied for CDSA. Finally, patchy micelles could be derived from the simultaneous heteroepitaxial growth of two crystallizable di-or triblock copolymers bearing different core-and corona-forming blocks, inducing segmentation within the core as well as in the corona.
The alternating arrangement of the corona patches emerges as an excellent feature for the stabilization and confinement of metal and metal oxide nanoparticles, opening applications in heterogeneous catalysis. Yet this has been shown only for the gold nanoparticlecatalyzed alcoholysis of silanes, and it is anticipated that this concept can be transferred to other relevant catalytic processes like heterogeneous hydrogenation. By incorporating different nanoparticle types, even cascade reactions might be realizable. Most interestingly, the interfacial activity of patchy, worm-like (or cylindrical) micelles is equivalent to that of Janus micelles, the latter being, however, more difficult to produce. Thus, patchy micelles might be utilized in interfacial catalysis, as well as in the efficient stabilization of emulsions or compatibilization of polymer blends.