Review on the Accelerated and Low-Temperature Polymerization of Benzoxazine Resins: Addition Polymerizable Sustainable Polymers

Due to their outstanding and versatile properties, polybenzoxazines have quickly occupied a great niche of applications. Developing the ability to polymerize benzoxazine resin at lower temperatures than the current capability is essential in taking advantage of these exceptional properties and remains to be most challenging subject in the field. The current review is classified into several parts to achieve this goal. In this review, fundamentals on the synthesis and evolution of structure, which led to classification of PBz in different generations, are discussed. Classifications of PBzs are defined depending on building block as well as how structure is evolved and property obtained. Progress on the utility of biobased feedstocks from various bio-/waste-mass is also discussed and compared, wherever possible. The second part of review discusses the probable polymerization mechanism proposed for the ring-opening reactions. This is complementary to the third section, where the effect of catalysts/initiators has on triggering polymerization at low temperature is discussed extensively. The role of additional functionalities in influencing the temperature of polymerization is also discussed. There has been a shift in paradigm beyond the lowering of ring-opening polymerization (ROP) temperature and other areas of interest, such as adaptation of molecular functionality with simultaneous improvement of properties.


Introduction
Benzoxazine (Bz) monomer is typically synthesized via Mannich-like condensation of a phenolic and a primary amine derivative in the presence of formalin or paraformaldehyde to form 1,3-benzoxazines (e.g., 3,4-dihydro-3-methyl-2H-1,3-benzoxazine). Bz contains a heterocyclic six-membered ring in an irregular chair conformation with oxygen and nitrogen atoms at the 1-and 3-positions, respectively. The monomer undergoes cationic ringopening polymerization (ROP) to form polybenzoxazines (PBzs). Holly and Cope [1] first reported the synthesis of benzoxazine monomers, which was extended by Burke et al. [2,3] followed by Schreiber [4,5] and Higginbottom [6] to PBz resins. Ning and Ishida [7] reported the properties of PBzs in 1994. This led to an emergence of the PBz era. This class of polymers is an attractive alternative to many traditional thermosets, such as epoxies, phenol-formaldehyde, bismaleimides, cyanate ester resins, and even polyimides due to its excellent properties, rich design flexibility at the molecular level and competitive cost.
Since the discovery of PBzs, a large number of structural modifications have been considered to advance their applications. Due to their very complex structure and IU- Figure 1. Synthesis of Bz monomers (a) one-step synthesis of representative benzoxazine monomer using phenol (PH), aniline (a) and formaldehyde, (b) asymmetric benzoxazine [80] and (c) multi-step synthetic approach [81].
It must be noted that not all phenolic-OH groups may condense with amine and formaldehyde to form oxazine ring. Interestingly, a dimeric phenol with an amine bridge led to the formation of an asymmetric mono-oxazine inevitably instead of expected bisbenzoxazine as in Figure 1b. This unusual and inequivalence of phenolic-OH reactivity is due to the existence of a strong intramolecular H-bonding (bond length~0.18 nm) of one phenolic-OH with the >N-group, hampering its accessibility for ring-closure reaction [80].
Aside from highly reduced reactivity by intra-molecular hydrogen bond formation, lack of free o-position of phenolic structure can also prevent oxazine ring formation. Phenolic compounds, such as pyrogallol, 3-methoxycatechol, novolac, lignin, and tannin that contain some phenolic groups with no open o-position will remain as such rather than being involved in formation of oxazine. Such uncondensed OH groups will act as ring-opening initiators and/or catalysts and are known to shorten shelf life unless they are inactivated via intramolecular hydrogen bonding interactions or modified to chemical latent structures. In certain monomers, when some components interfere with the traditional mode, a three-step synthesis is found to be convenient in place of a one-step Mannich condensation reaction as shown in Figure 1c [81].
In general, the oxazine functionality number can be varied depending upon the nature of the starting materials and reaction conditions. The representative structures of mono-   [82,83].
As proposed by Burke and Ishida [2,119], formation of benzoxazine monomer (PH-a) in acidic conditions preferentially proceeds via iminium ion intermediate instead of the sequential reaction of aniline and resultant intermediate with formaldehyde molecules, as supported by ionization mass spectrometry (ESI-MS) with infrared multiple photon dissociation (IRMPD) spectroscopy [120]. Small ring strain in oxazine ring due to the presence of two heteroatoms, N and O, demands a modestly high temperature~140-240 • C to mediate  [152]. (b) Variation in tan δ of polybenzoxazines [152]. Copyright 2014. Reproduced with permission from American Chemical Society.
Incorporation of a rigid aromatic structure in the PBz backbone such as fluorenyl and naphthol resulted in an improvement in properties, especially thermal stability, high char yield, LOI, and flame-retardance [153][154][155][156][157]. Incorporation of fluorene moiety in the Bz monomer imparted photoluminescence and UV stabilization characteristics to the PBz [158].
Similarly to thermoplastics, properties of PBz framework are also affected by the chirality of the monomer [89,159]. The S-configuration origin PBz (S-tbtmpPH-pea) showed a slightly higher T g (31 • C) than the racemic (rac-tbtmpPH-pea) (19 • C) due to stereoregular arrangement of units in the polymer backbone [160]. However, these values are much lower than the reported values for mono-oxazine based resins, due to blocked oand ppositions with bulky t-butyl groups (Figure 9a). Recently Nagarjuna et al. [89] reported utility of chiral biobased isomannide sourced diamine (ima) to induce chirality in bisoxazine monomers. This resulted in an unusual multiplet oxazine 1 H NMR signals as compared to singlet signal, which are typically observed in traditional Bz monomers. The incorporation of rigid isomannide core resulted in fully biobased chiral PBz as illustrated in Figure 9b, a comparable T g to their petro-based aromatic diamine counterparts and a 2-fold higher adhesive strength than poly(BA-a) (Figure 9c). . Synthesis and ROP of chiral Bz monomers (a) S-tbtmpPH-pea and rac-tbtmpPH-pea mono-oxazine [160], (b) G-ima and C-ima bis-oxazine [89] and (c) lap shear strength (LSS) values of C-ima, G-ima and BA-a benzoxazine based thermosets at room temperature [89]. Copyright 2019. Reproduced with permission from American Chemical Society.
The position, nature, and number of oxazine rings affect the polymerization behavior and lead to various types of linkages in the resultant network. Figure 10 clearly shows a broad DSC exotherm in 3,5-xylidine (35x) based monomer, BA-35x, as compared to aniline based BA-a. This infers the existence of two polymerization reactions in BA-35x; the lower temperature exotherm is accounted for the ROP reaction, while the higher temperature shoulder corresponds to the side reactions such as formation of bisphenolic methylene linkages, arylamine Mannich bridge and methylene linked structures. Ishida and Sanders [142,161] supported existence of these linkages in BA-35x by FTIR spectroscopy. The structural variation of the polymer network is highly dependent on the nature of constituent phenol and amine and the additional functionalities present therein. BA-m and BA-a showed a significant effect on degree of polymerization and the crosslink density as investigated by 13 C solid-state NMR [162]. A substantial influence on the degradation behavior of resultant polybenzoxazines is observed. Secondary amines are detected at temperatures <400 • C while phenols are detected at temperatures >400 • C in aliphatic amine based polybenzoxazines. In the case of poly(BA-a) and poly(22PP-a) below 600 • C, the degradation behavior of Mannich base cleavage under an oxidative environment is influenced significantly by the nature of constituent phenols below 600 • C [163]. Table 1 clearly shows that both introduction and position of methyl substituent on arylamine influences growth and degradation behaviors of PBz bis-benzoxazines prepared with various amines [164], possess the processing window as BA-35x < BA-mt < BA-a. The T g were found to be consistent with the T p of the polymerization exotherms, suggesting a significant variation in structure dependent reactivity to form crosslinking networks. The T g of PBz based dimethyl substituted aniline (35x) is much higher at 243 • C than unsubstituted aniline of 168 • C [161,164]. Additionally, poly(BA-mt) and poly(BA-35x) display a delayed onset of thermal degradation (T 5% ) until around 350 • C, as compared to poly(BA-a). A regioselective control was found to improve the mechanical and thermal properties due to the occurrence of secondary crosslinking mechanism, leading to a predominance of thermally stable arylamine bridges [83,162,163]. Table 1. Thermal characterization of substituted polybenzoxazines [161].  Likewise in BA-35x, a very broad DSC polymerization exotherm comprised of several overlapped peaks was also observed in case of ethylenediamine (eda) based bisbenzoxazine monomers [137]. The two overlapped exotherm peaks of PH-eda are centered at temperatures that are atypically low for benzoxazines. This is attributed to the short ethylene linkage between the oxazine rings leading to steric hindrance or other structural interactions destabilizing the oxazine rings to affect polymerization at low temperatures [166]. A simultaneous occurrence of both polymerization and degradation is also reported in these structures. The highest temperature peak in these exotherms is ascribed to the degradation mechanism.
A significant influence of methyl-substituent in Bz polymerization is also reported. In case of BA-a, oMBA-a and oMBA-35x, the polymer network growth proceeded by only one dominant auto-catalytic process with the existence of either phenol Mannich or arylamine Mannich bridge structure. On the other hand, BA-35x shows simultaneous occurrence of both crosslinking reactions. The nature and presence of methyl substituent in Bz monomer profoundly controls the type of linkages in polymer structure, as illustrated in Figure 11 [83,165].
However, exhibiting multiple polymerization exotherms is not a common phenomenon in multi-functional benzoxazine monomers. Rather, multifunctional benzoxazines with possible multiple polymerization mechanisms often display a single exothermic peak. This seemingly a contradictory phenomenon was reported by Zhang et al. [167] and recently by Lyu et al. [139] Regio-isomers 5,5 -, 5,7 -, and 7,7 -based on 3-alkoxyphenol (methoxy, butoxy) and ddm, shown in Figure 12a, were purified to form single crystals to study the effect of benzoxazines with different reactivity within the same molecule. The DSC thermograms of individual isomers are shown in Figure 12b. Despite having 5-and 7-methoxy isomers in the same molecule, 5,7 -MOPH-ddm shows a symmetric and rather sharp exothermic peak at 226 • C, and this phenomenon is explained using the rate of reaction theory.  Besides classical linkages formed by oxazine ROP, formation of other types of crosslinks such as ester linkages due to copolymerization, [168] triazine ester/isocyanurate [169] are also reported. Introduction of such additional linkages in PBz is advantageous and found to increase T g of PBz. For instance, copolymerization of BA-a with 3,3 ,4,4 -benzophenonetetracarboxylic dianhydride (BTDA) enhanced T g to 263 • C. Nitrile based Bz monomers are prone to undergo phenolic group-mediated nucleophile triggering, which may form various nitrile-nitrile addition structures. These structures affect the crosslink density of the polymer network [170,171]. Figure 13a shows the synthesis of BA and 4-(3-aminophenoxy)phthalonitrile (appn) based phthalonitrile benzoxazine monomer. The nitrile groups form triazine and phthalocyanine structures, Figure 13b, in addition to oxazine ring-polymerization, thereby imparting a very high thermal stability (>400 • C) to poly(BA-appn). A simultaneous occurrence of oxazine ring-opening and triazine/phthalonitrile ring-forming reaction led to an improved mechanical performance, which is attributed to synergistic interactions between the polymer framework [172]. Curing kinetics of bisphthalonitrile Bz monomer was found to involve a free radical mechanism, where methine and methylene promote cyclization reactions of the cyano group [173].
Like nitrile, cyanate ester functionality also affects polymerization of benzoxazine functionality [174][175][176][177][178]. It was proposed that the phenolic hydroxyl group generated by benzoxazine ring-opening reaction reacts with the cyanate ester group to form iminocarbonate intermediate, which triggers cyclotrimerization of cyanate groups [174,175,179,180]. Further, it was proposed that the ring-opened oxazine rings insert into the triazine rings to form cyanurates and isocyanurates, which then probably further react with oxazine rings to form other structures [176]. Wang et al. [178] proposed the benzoxazine ring itself catalyzes both trimerization of cyanate ester and isomerization (cyanurate to isocyanurate) reactions upon heating. They showed the possibility of ROP for benzoxazine at 30 • C as evident from Figure 14i. This supported that the benzoxazine ring only induces the catalytic effect in trimerization of cyanate linkage as proposed in Figure 14ii. Ohashi et al. [181] proposed that the existence of cyanate ester functionality in the benzoxazine monomer affects its polymerization at a lower temperature than the benzoxazine/cyanate ester blends. Figure 14iii clearly supports the existence of multiple exotherms due to two different types of crosslinking processes in the DSC trace. They proposed the cyanate ester reaction promotes benzoxazine cationic ring-opening polymerization more efficiently when it is present in the benzoxazine structure itself. TGA thermogram, Figure 14iv, shows the improved thermal stability of PBz containing cyanate ester group. Besides cyanate ester crosslinking reactions, the high thermal stability is also attributed to the co-reaction of the resultant amine moiety to form additional crosslinks and thereby may prevent decomposition or evaporation of aniline component from PBz during heating.  [171] and (b) proposed nitrile groups based cyclic structures formed during polymerization [171]. Despite expected higher thermal properties of PBzs based on naphthol, use of nonfunctional naphthoxazines is somewhat limited due to evaporation of the naphthoxazine units prior to polymerization [183,184]. Naphthoxazines functionalized with cyanate ester, Figure 14v, revealed minimization of such mass losses as indicated by multiple exotherm maxima, to support cyanate ester trimerization along with ROP of Bz ring. Additionally, incorporation of cyanate ester functionality not only lowered the polymerization temperature but also led to a relatively higher stability than their aniline counterparts as shown in Table 2 [182]. Table 2. Thermal characterization of naphthoxazine and general benzoxazine [182]. A simultaneous trimerization and oxazine ROP is observed only in cases of 1NP-pcna and 2NP-pcna while o-substituted cyanate esters, 1NP-ocna and 2NP-ocna, showed multiple exothermic peaks with a lower exothermic temperature than p-substituted cyanate ester functional naphthoxazines.
Other reactive functionalities, such as propargyl [185][186][187], epoxide [188,189], oxyalcohol [190] and amino [191] groups, are also incorporated in benzoxazine structures to impart additional crosslinks or other related benefits due to ease of structural control at the molecular level. Interestingly, aldehyde-containing benzoxazine, upon modification to a Schiff base, enables its applicability to sequester metals ions [192].

Smart Benzoxazine Monomers
In addition to obvious reactivities of the additional substituent other than an oxazine ring as discussed in the previous section, there are certain structures or groups, which themselves do not possess ability to polymerize and yet can influence the rate or mechanism of oxazine polymerization. Such smart molecules can be quite useful as demonstrated in the following sections.
A unique class of o-amide functional Bzs was found to polymerize at much lower temperature than traditional Bz, without any help of initiator or catalyst. The presence of intramolecular H-bonding between an amide group and the adjacent oxazine ring acts as an internal trigger to stimulate ROP of oxazine ring at low temperature to form PBz with o-amide phenol functionalities. The T p of Bz with o-amide found to be lower than p-amide isomer by 47 • C supporting the catalyzing effect induced by neighboring amide functionality via a 5-membered intramolecular H-bonding interaction. With further treatment at higher temperature (>ROP temperature) during post-curing or any event of catching fire, intramolecular cyclization between the neighboring hydroxyl and amide groups occurs to form oxazole rings with the elimination of water. Such interconversion of PBzs to polybenzoxazole imparts a better set of thermal properties due to formation of a more stable polymeric network as shown in Figure 15.  [193]. Copyright 2012. Reproduced with permission from American Chemical Society.
Regiochemistry of oand p-amide substituents in Bz monomer containing pyridine ring affects the strength of intramolecular H-bonding interactions with the O in oxazine ring and N-H· · · N interaction with pyridine ring affecting polymerization characteristics and its conversion to PBO [194].
Similarly, o-imide functional Bz monomers are synthesized using the simplistic approach shown in Figure 16a via condensation reaction of 2-(2-hydroxyphenyl)isoindoline-1,3-dione (2,2-HPIO) with aniline (a) [195]. Benzoxazine resins with o-imide functionality revealed advantageous properties as compared with p-imide functional isomers. The crosslinked polybenzoxazine based on o-imide unit undergoes decarboxylation at high temperature to form a more thermally stable crosslinked polybenzoxazole (with T 5% = 505, Y c = 73%). This method allows elimination of the traditionally used expensive raw materials and harmful solvents for polybenzoxazole synthesis.
The polybenzoxazole thermosets based on the ortho-(amide-co-imide) functional benzoxazine monomers (BHPICA-a and BHPICA-ddm) are synthesized as shown in Figure 16e. As illustrated in Table 3, the attainment of very high T g and thermal stability of these polymers upon heating at high temperature (400 • C) is supported by the formation of thermally stable linkages. This strategy demonstrates an easier and promising synthetic route of such polymers which can be used for high performance demanding applications [198].
The presence of ortho-nitrile group functionality in ortho-phthalimide-functionalized benzoxazine monomer revealed exceptionally high thermal stability (T 5% = 550 • C) and high char yield value (70%). This is accounted to by the formation of highly crosslinked network, stemming from the occurrence of multiple polymerization reactions, namely, oxazine ROP, cyano cyclotrimerization and benzoxazole ring formation [199]. Benzoxazine monomers with atropisomerism [200][201][202][203] account for a more interesting set of properties than traditional benzoxazine structures. The formation of highly cross-linked networks through multiple polymerization behaviors in single-component resins is advantageous in terms of ease of processability and high performance properties of ortho-maleimide functional benzoxazines with additional crosslinking such as cyano or acetylene functionalities [203]. Table 3. Thermal characterization of o-(amide-co-imide) functional polybenzoxazines [198]. Obtained after heating at 300 • C a and 400 • C b for 1 h to assist cyclodehydration reaction; c T g values are reported from dynamic mechanical analysis.
A wide family of allyl functionalized benzoxazine monomers is shown in Figure 17a. Variation in position, number and hybrid structure of benzoxazine monomer is reported in the literature. Allyl groups were found to influence the polymerization behavior of Bz monomer [53,94,95,[204][205][206]. The higher rate of polymerization of N-allyl substituted benzoxazine (PH-ala) as compared to N-(n-propyl) benzoxazine is attributed to the neighboring group participation of allyl group to assist oxazine ring-opening reaction [53]. PH-ala showed two exotherms with T p at 207 and 260 • C that are associated with the thermal polymerization of the allyl group (attached to N) and formation of PBz, respectively. With an allyl group at the o-position, for o-allylphenol aniline (oALPH-a) monomer, a single exotherm T p at 263 • C is observed. Steric hindrance to polymerization is inferred from the observed low value of T g and poor thermal stability of poly(oALPH-a) [205]. Among difunctional allyl benzoxazines (oALPH-hda and oALPH-dds), sulfone bridged PBz showed relatively high thermal stability which is due to the significant difference in polarity of aliphatic and sulfoxide linkages [206]. The presence of inherent allyl groups in naturally occurring phenol, eugenol (E), was also explored for PBz. However, due to blocked oand p-positions, it revealed limited polymerizability. This can be overcome by synthesizing hybrid bis-Bz monomer using phenol and eugenol. It was found that a variation in phenol to eugenol ratio in polymer allowed tunability in T g ( Figure 17b) along with the renewable content [94]. Isoeugenol (IE) is a naturally occurring structural isomer to eugenol, which has a propenyl instead of allyl group at the p-position. This variation in the position of double bond in phenol made a lower T p value of IE-fa in comparison to E-fa. This suggested a prior involvement of double bonds to mediate ROP reaction of Bz monomer as the ring-opened phenolate ion is in conjugation with the alkenyl π bonds in IE-fa. A copolymerization of double bonds with oxazine is proposed as shown in Figure 17c [95]. Similarly, involvement of propenyl group in the crosslinking reactions was also noticed by Sha et al. [207].
Introduction of photoreactive functionalities, coumarin [208][209][210][211], chalcone [212], and bis-benzylidene as another smart feature in Bz monomer is reported. This created their capability for photodimerization [213,214] and exploration for self-healing applications. Kiskan and Yagci [209] utilized photoreactive coumarin functionality containing phenol, methyl substituted umbelliferone (MU), and p-toluidine (pt) based benzoxazine monomer, which upon irradiation at 300 nm underwent photodimerization via [2π + 2π] cycloaddition with alkenyl bonds as shown in Figure 18a. Like coumarin based Bz monomer, photosensitive bis-benzylidene linked Bz, BHPe-a (structure is shown in Figure 18b [213]) also undergoes [2π + 2π] cycloaddition to form cyclobutane ring-linked dimer. This allowed an increase in oxazine functionality and an extended monomer capability to undergo crosslinking reactions at the oxazine ring and double bonds. Figure 18c shows monitoring of dimerization reaction of monomer by UV-VIS. studies. A decrease in intensity at 365 nm due to π−π* absorption of a double bond of bis-benzylidene acetone, and increase in intensity at 280 nm due to δ−δ* absorption of newly formed cyclobutane ring with the irradiation time was observed.  [53,95,[204][205][206]. (b) Strategy to affect T g using hybrid bio-based monomer [94]. Copyright 2015. Reproduced with permission from Royal Society of Chemistry. (c) Probable mechanism of ring-opening polymerization in IE-fa Bz monomer [95].
Besides the capability for photo-induced dimerization, the coumarin as compared with non-coumarin containing monomers ( Figure 19a) showed a low T p for ROP reaction [210]. High stability of the ring opened phenoxide ion via extended resonance occurs in both U-a and MU-a. This resulted in a reduction in T p of PH-a from 261 • C to 220 • C (U-a) and 232 • C (MU-a) as illustrated in Figure 19b,c [210]. The methyl group in coumarin in MU-a indirectly affects the reactivity of oxazine by being less electrophilic, i.e., less electron-withdrawing in nature, and thus, it has lower stability and hence accounts for observed higher ROP temperature than U-a. Alagar et al. [214] extended copolymerization of chalcone benzoxazine with bismaleimides to improve thermal stability of polymers.  [208] and (b) bis-benzylidene containing benzoxazine monomers and their light mediated dimerization [213]. (c) UV absorption spectra of BHPe-a in DMAc at a concentration of 0.8 mg/40 mL after irradiation at 365 nm for various periods of time [213]. Copyright 2017. Reproduced with permission from American Chemical Society. As discussed previously, mono-oxazine functional monomers suffer from a few problems. They tend to evaporate significantly prior to polymerization and, upon polymerization, form small oligomers with molecular weight of several hundred to few thousands, despite their processing advantage of very low viscosity and ease of purification upon synthesis. Zhang et al. [215] reported the first example of AB-type benzoxazine monomer having maleimide and furan as the terminal functionalities of the monomer. They proposed that the Diels-Alder reaction takes place between the maleimide and furan below the polymerization temperature of oxazine to form small oligomers of several repeat units during melt processing. This approach maintains the advantage of very low viscosity mono-benzoxazine yet prevents evaporation of the monomer, as the increased molecular weight of the oligomer means it will not evaporate at the processing temperature as compared in Figure 20 for mono-oxazine benzoxazine monomers with and without Diels-Alder reacting pair. This further leads to a crosslinked polymer chain structure that exhibits good mechanical and thermal properties by reducing the number of dangling chain ends, a usual issue in mono-benzoxazine polymers. The main-chain type oligomers with several repeat units have been reported to offer good trade-off between processability and high thermal properties as discussed in Section 2.2. They exhibit high char yield, resulting in one of the smallest heat release capacities (HRC), 33.4 J/g.K, of all polymers. Certain monomers possess self-catalyzed cationic ring-opening polymerization for example, deoxybenzoinbased benzoxazine monomer [216]. Lowering the polymerization temperature reduces the chance of monomers to evaporate. Figure 20. Thermogravimetric analysis of HPMI-fa and PH-a, showing nearly complete prevention of the evaporation of the resin prior to polymerization [215]. Copyright 2019. Reproduced with permission from American Chemical Society.

Third Generation Benzoxazines
The third generation consists of reactive PBzs (with both thermoplastic/thermoset characteristics), namely, (i) main-chain type, where oxazine group is part of every chemical repeat unit of the oligomer chain; (ii) side-chain type based on thermoplastic backbone, where oxazine ring is part of the side chain of every chemical repeat unit; and (iii) telechelic, where oligomer of any polymer chain is terminated by reactive oxazine functionalities at each of the chain ends.
In general, mono-oxazine based PBzs containing several dangling-chain ends account for a lower thermal stability [131,[217][218][219][220]. This concept of the chain end of PBz being the cause of the lowest degradation temperature of multiple degradation scheme was first presented by Chernykh et al. [221].
The incorporation of benzoxazine moieties as repeating units into polymer main chains reduces the number of chain ends in the crosslinked polymers, thus providing an enhanced thermal stability. Therefore, if the mono-amine used as the raw material contains an additional reactivity either by having reactive substituent or added reactivity of the phenyl ring by regioselectivity, the thermal stability of the polymer was found to improve substantially [141]. This main-chain type architecture provides benefits of both thermoplastic and thermoset polymers. Advantages include both solution and melt processability, tunability in T g and production of self-supporting films, which further upon crosslinking improve thermal and mechanical strength [222][223][224]. The presence of additional functionalities other than oxazine is beneficial to modify properties, e.g., poly(benzoxazine-co-urea) [225], Figure 21a, showed attractive adhesion properties due to existence of polar linkages of both urea and ring-opened benzoxazine and ductile nature of the reactive polymeric chain precursor. The LSS value of poly(benzoxazine-co-urea) determined from plot Figure 21b was found to be 61 kg cm −2 , which is lower than poly(Cddm) [87] (79.0 kg cm −2 ). This could be attributed to a higher crosslinking density in the latter and existence of better adhesion properties of ring-opened oxazine structure vs urea linkages in the polymer framework. Cardanol based PBz resins revealed a great potential in many applications [117]. For instance, the adhesive strength of cardanol derived monomers was found to increase with the increase in number of benzoxazine rings in the monomer, as shown in Figure 21c [90]. This enhancement in LSS values is accounted to an interplay of the low viscosity of monomers and flexibility and crosslink density of the polymer.  Figure 22. The latter polymer, which is based on the crosslinking from o-position to the oxazine N, revealed a lower T o and a wider width of the tan δ peak suggesting the ROP occurs through the o-position to the O of oxazine led to better thermal properties than that through the o-position to the N of oxazine [226]. In summary, main chain type subclass polybenzoxazines provides benefits of an easy synthesis and processability without compromising thermal stability and mechanical property between the polymers obtained from monomeric and high molecular weight oligomeric oxazine precursors. Furthermore, additional reactive functionality other than oxazine ring provides capability to optimize the benefits of both thermoplastic and thermoset polymers. For example, additional functionalities modify the properties of the polymer such as tunability in T g , solubility in solvents, formation of self-supporting films and may provide opportunities to control over ductility and adhesive properties to name a few.
Selective introduction of benzoxazine moieties into polymer side chains and terminals [227], and the attachment of radically polymerizable groups such as methacryloyl group to Bz monomers [228,229], led to more variation in functional properties than those discussed above. Few representative structures are shown in Figure 23. Radically polymerizable functionalities in benzoxazine monomers were synthesized to incorporate the benzoxazine units within the side-chain of constituent repeat unit.  [228,229] and (b) TGA curve of methacryloyl-benzoxazine monomer [228]. Copyright 2011. Reproduced with permission from American Chemical Society.
Radically polymerizable groups bearing benzoxazine monomers first photopolymerize and are then followed by a thermally activated ROP reaction. However, polymerization of oxazine ring is not realized due to the limit of thermoplastic polymer degradation at a much lower temperature of 200 • C, as can be seen from TGA trace in Figure 23b [228,229]. Copolymerization of poly(PH-pva) (va, vinylaniline) with methyl methacrylate (MMA), and n-butyl acrylate (BuA) followed by polymerization led to the formation of a tough and flexible film, respectively [230]. The molecular weight of both homopolymer i.e., poly(PH-pva) and poly(vPH-a) (vPH, vinylphenol) was found to be relatively low, which is attributed to the steric hindrance of benzoxazine groups and can be affected by copolymerization with N-phenylmaleimide [231]. The polymer, poly(PH-pva), showed a higher stability (>400 • C), supporting the concept that control at molecular level is the key to guide properties.
Instead of polymerizing monomers containing benzoxazine units, another facile approach involves tethering of pre-synthesized monomers to the polymer backbone directly via potential and affordable chemistries [232] such as click [185,[233][234][235], esterification chemistry, and so on [229]. Representative examples are shown in Figure 24. Interestingly, in the aforementioned side-chain polymers, the benzoxazine units are grafted at a higher concentration. Sparse population of benzoxazine can also be possible by milder photochemical approaches. Temel et al. [236] synthesized a one-component type II photoinitiator based on the BOP-a benzoxazine monomer derived from benzophenone (BoP). This monomer revealed better light absorption characteristics than BoP alone. BoPa initiated free radical photopolymerization of MMA to form BoP-a tethered PMMA, showing a higher T g (135 • C) than neat PMMA (100-105 • C). Bai and Shi [237] reported a BoP based bisbenzoxazine photoinitiator revealed four times higher photopolymerization rate of acrylate monomers than BoP based system.
Telechelic structures are macromonomers containing non-reactive oligomeric chains in the structure with terminal oxazine groups. The low concentration of oxazine functionality allows for development of lightly crosslinked networks. However, they can be effective for copolymerization with other monomers and polymers. Several reactive thermoplastic telechelic architectures are reported with the variation in linking units from flexible to rigid linkages as shown in Figure 25, to tailor their properties [238]. Unfortunately, due to the dilution effect of the reactive oxazine rings, the T p might increase as compared with ordinary monomeric counterparts.

Smart Benzoxazines
Despite having outstanding performances, polybenzoxazoles (PBO), usage is still limited both by synthetic and fabrication challenges. Additionally, the stringent synthetic requirements, such as expensive and higher structural rigidity of raw materials as shown in Figure 26a, sensitive reaction conditions, and difficulty of completely eliminating the solvent used leads to aging of the properties. This demands exploration of alternative simpler and facile routes. Recently, a new class of benzoxazine monomers and mainchain type polymers that contain o-amide, o-imide, and o-amide-imide groups have been reported [56,195,198,241]. These benzoxazine resins undergo usual ROP to form crosslinked PBzs at temperatures lower than ordinary benzoxazine polymerization. Upon further heating the crosslinked polybenzoxazines, in situ structural transformation takes place that converts polybenzoxazine to PBO. Correlating this intermediate structure with the smart designing of the benzoxazine monomer, Agag et al. [193] first reported an easier synthetic route for PBO via polybenzoxazine through the process shown in Figure 26b. This synthetic aspect was further confirmed as only o-amide benzoxazine isomer account to PBO formation, but p-amide benzoxazine failed to undergo such intramolecular cyclization reaction, as illustrated in Figure 26c.  [193].
The work was further extended by Zhang et al. [241,242] where they reported formation of crosslinked PBO via poly(benzoxazine amic acid), poly(Bzaa), using o-benzoxazine chemistry as shown in Figure 27. Synthesis involved imidization to form crosslinked polyimide, (cPI) which upon further heating undergoes simultaneous decarboxylation and cyclization reaction to give crosslinked polybenzoxazole (cPBO).
The synthetic route was further simplified by the exclusion of amic acid intermediate via small molecule o-imide functional benzoxazines as a precursor for structural transformation to PBO. The polymer showed a very high thermal stability with T 5% of 505 • C and an extremely high char yield of 73% [195]. Interestingly, o-amide functional benzoxazine monomers are found to undergo ROP at a much lower temperature than both the p-isomer and non-amide-based control monomer. The o-isomer revealed a lower polymerization temperature than the p-isomer due to the more stable intramolecular 5-membered ring hydrogen bonding interaction that accelerates the ring-opening process [243]. The above polymers revealed an extraordinary low heat release capacity (HRC) further making them strong contenders to replace poly(ether imide) and other high performance polymers. In above-mentioned methodologies, the temperature required for conversion of oamide benzoxazines and o-imide benzoxazines into benzoxazole structure was found to be high,~300-400 • C, which led to difficulties during their fabrication. Zhang et al. overcame this difficulty by developing the endcapping trifluoro group. The incorporation of o-trifluoroacetamide in benzoxazine (oTFAPH-ddm) exhibits a low polymerization temperature compared to other reported o-amide benzoxazines due to higher acidity of amide hydrogen, Figure 28. Furthermore, a remarkably low temperature (260 • C) for interconversion to benzoxazole is observed. Additionally, existence of fluorine in PBO led to an attractive feature of low dielectric constant (2.42-2.19 within the frequency range of 1 Hz-1 MHz) in addition to high thermal stability and T g of 354 • C. Mahdy and Kuo [244] reported a direct synthetic route for the preparation of o-imide containing benzoxazine monomer by condensation of anhydride (NTCDA) with o-amino phenol (o-APH) to produce o-imide phenol (NDoPH) which was then condensed with paraformaldehyde and aniline to form o-imide benzoxazine as shown in Figure 29. The monomer revealed miscibility with poly(4-vinylphenol) due to hydrogen bonding between C=O and OH groups. Upon polymerization of the monomer, the extensive H-bonding between polybenzoxazine led to an improvement in T g , thermal stability, and char yields of the resultant polymer blends. Zhang et al. [245] reported the synthesis of side chain containing an o-imide functionality to norbornene functional benzoxazine ring as shown in Figure 30. This allowed the monomer to undergo ring-opening metathesis polymerization (ROMP) to form a new polynorbornene functionalized benzoxazine. However, its interconversion to substituted PBO is not reported due to limitations of thermal stability of poly(oHPNI-a) x main side as determined from the TGA curve in Figure 30b.

Oxazine Ring Substituted Benzoxazine
Both the synthesis of 1,3-benzoxazine monomer and polymer and their properties are widely reported in literature. Supplementarily, substitution in oxazine ring at 2-and/or 4-position as shown in Figure 31 presents an attractive structural design, especially in polymer chemistry [246,247]. The nomenclature adopted in such structures is an extension to earlier proposition of benzoxazine structures. For abbreviation of the ring substituted benzoxazine, the following nomenclature is proposed: abbreviated benzoxazine monomer name-[position of substitution in oxazine ring] abbreviated phenyl/alkyl in lower case characters. Thus, for example, PH-a with phenyl ring substitution at 2-position is represented as PH-a- [2]ph.
Ohashi et al. [247] first reported polymerization of phenyl substituted 1,3-benzoxazines. The substitution at 2-position is achieved via typical multi-step synthesis from salicylaldehyde involving condensation with benzaldehyde instead of formalin for ring closure reaction. The substitution in oxazine ring allowed a lower polymerization temperature than the general benzoxazines due to the resonance stabilization of iminium ion intermediate as shown in Figure 31b. However, polymerization of oxazine ring-substituted monomers is currently limited due to evaporation of lower molecular weight N-benzylideneaniline molecule as a byproduct accounting for a lower thermal stability of polymer. Alternatively, formation of ladder-type bisbenzoxazine PH-ppda- [2]ph lowered issues of volatilization, due to heavier and bulky nature of imine accounting for its entrapment in polymerization matrix and subsequent involvement in the polymerization reactions. Such losses can also be minimized to some extent by using catalyst mediated ROP at low temperature [248]. More recently, lack of the use of formaldehyde during the synthesis was emphasized as an environmentally friendly method by Travernier et al. [249].

Fused Ring Benzoxazines
Fused-ring benzoxazine structures contain a sandwiched oxazine ring between an aromatic ring and a cycloaliphatic ring 1-naphthol (1-NP) [250] or 2-naphthol (2-NP) [251,252]. This approach involves a two-step synthesis, firstly of cyclic imines and activated phenols reacted to form aminocycloalkylphenols by the Betti reaction [253]. Secondly, ring-closure reaction of amino derivative with formaldehyde as shown in Figure 32 is carried out [254]. The nomenclature follows numbering of the positions on the oxazine ring as in benzoxazine nomenclature. The aromatic portion contains numbers accompanied by the character "x" as abbreviation for the aromatic ring (b and n for benzene, and naphthalene, respectively) and finally the fused ring using alphabetic letters. For instance, 1-NP and formalin (f) based benzoxazine fused with 3,4-dihydro-2H-pyrrole (p) will be abbreviated as 1NP-p-f. Arza et al. [254] reported the polymerization of fused ring benzoxazine. These monomers show a much lower T p as compared to the conventional mono-oxazine monomers. This is due to high basicity of tertiary amines and van der Waals' strain in sandwiched oxazine ring geometry. Despite interesting structure, low temperature mass losses of polymers as shown in TGA trace Figure 32b demands exploration of alternative synthetic designs.

Acceleration of the Rate of Polymerization via Intermolecular Interaction
Benzoxazine monomers tend to undergo thermally accelerated ring-opening polymerization in the temperature range 160-220 • C. This temperature range varies with the structure, number of oxazine rings, regio-position, and most importantly, purity of the monomer. In general, mono-oxazine benzoxazines have a T p of ca. 250 • C. A low polymerization temperature is desired to improve processibility and compatibility with many other resins and substrates. Alternatively, physical blending of catalysts and initiators with the Bz monomer is one of the most efficient and economically viable approaches for the lowering of polymerization temperature [255][256][257][258][259].
Burke and co-workers [2,260] first reported the ring-opening reaction of Bz, indicating that aminoalkylation preferred to occur at the free o-position rather than at the free p-position of the phenol in the reaction of 1,3-dihydrobenzoxazine with a phenol. Riess et al. [261] also observed preference of o-substitution during the investigation of the kinetics of mono-functional benzoxazines in the presence of catalytic amounts of 2,4-di-tertbutylphenol. McDonagh and Smith [262] suggested existence of ring-chain tautomerism in protonated benzoxazine. Dunkers and Ishida [256] proposed cationic ROP mechanism of Bz monomers. It occurs by protonation of the oxygen/nitrogen atom in oxazine ring in formation of an iminium ion intermediate. This then undergoes several electrophilic aromatic substitution reactions to form the PBz framework. A simplified structure of this phenolic polymer representation is shown in Figure 33. The oxazine ring in the monomer with free o-position undergoes a cleavage reaction at O-CH 2 -N bond to form a polymer with a Mannich base phenoxy-type polybenzoxazine structure [255]. This then rearranges to a thermally stable Mannich type phenolic polymer structure upon heating. The Ishida group worked extensively in determining the thermally accelerated polymerization mechanism and supported ROP proceeds through cationic mechanisms [42,64,[263][264][265][266][267]. The plausible mechanism is shown in Figure 33. More recently Liu et al. [268] provided an experimental evidence to support the intrinsic ROP without an added initiator using a high purity monomer, PH-a.
The ring-opening polymerization is primarily guided by the strong Lewis basicity of both N and O atoms present in the oxazine ring. It was proposed that the acidic catalyst allows polymer network growth via cationic ring-opening reaction while basic catalyst proceeds by nucleophilic ring-opening reaction as illustrated in Figure 34 [268]. Wang and Ishida first reported the formation of arylether structure instead of traditional phenolic structure as the repeat unit of polybenzoxazine chains when the monomer was polymerized at low temperatures using catalysts [255]. Sudo et al. [269] then reported that this N,O-acetal structure (unit A) formed during polymerization of p-substituted monomer at lower temperatures in the presence of a catalyst and can undergo structural transformation to thermally stable phenolic structures (unit B) upon heating above 150 • C. The existence of different types of linkages in polymer structure is guided by temperature, and their extent in polymer architecture is quantified by NMR spectroscopy as shown in Figure 35. Additionally, the main chain rearrangement was prominent in the polymerizations of N-arylover N-alkyl-1,3-benzoxazines, while the latter favors the formation of Mannich-type structure polymers.
An understanding of the polymerization mechanism provides a strategy to utilize or design structures of catalysts/initiators. Done effectively, this provides insight into methods for the acceleration of polymerization. Besides structure of monomers, polymerization behavior is a combination of effects which are primarily guided by the amount, acidity, basicity and structural compatibility of the initiator/catalysts. It must also be noted that purity of monomer is essential as the presence of unconsumed reactants and oligomers initiate polymerization reaction, thereby affecting the rate and temperature required for polymerization. The purity of a benzoxazine monomer has been documented to have a dramatic effect on melting and polymerization behavior [270].

Ordinary Acids
Acidic initiators are usually preferred due to ease of availability and variable acidity to mediate cationic ROP. Acids protonate either the oxygen or the nitrogen atom of oxazine ring and thereby facilitate intermediate iminium ion formation. The former is preferred as the resultant iminium ion intermediate is relatively more stable, as shown in Figure 36    Ishida et al. [266] reported the use of phenols with a free o-position (BA, poly(phydroxystyrene), 2,2'-dihydroxybenzophenone and 2,6-di-tert-butyl-p-cresol), with mild and strong organic and mineral acids (acetic, adipic, sebacic, benzoic, sulfuric, p-toluenesulfonic, phosphoric acids) as catalysts for the ROP of Bz monomer. Adipic acid (6 mol%) was found to be the most effective and showed a 17% decrease in the curing parameters. PBzs obtained using strong carboxylic acids were inferior to those formed with weak carboxylic acids. The pK a of the acid appeared to control the interconversion of the reactive intermediate, aminomethyl ester and the iminium ion affecting crosslinking reactions. Figure 37 shows a faster decrease in the normalized areas of the characteristic oxazine ring vibrations at 1050 and 813 cm −1 in presence of p-cresol (pK a = 10.2) than sebacic acid (pK a = 4.7, 5.4), supporting that the former mediates faster oxazine ring-opening reaction [256]. The effect of phenol on the polymerization reaction and associated reaction pathways was explicitly understood using the reaction of 2,4-xylenol (2,4-XY) with 3-aryl substituted benzoxazine. The intermediate species formed were several inter-and intra-molecular rearranged products [272]. Bisphenol F acts as a better catalyst than BA which may be due to differential electron donating capability of methylene vs isopropylidene bridge in biphenols [273]. A very high loading (~40 wt%) of phenolic compound, cashew nut shell liquid (CNSL), in BA-a led to a decrease in both T p and ∆H from 216 • C and 246 J g −1 to 197 • C and 194 J g −1 [274]. Furthermore, the polymerization reaction proceeds in an autocatalytic manner due to the formation of ring-opened phenolic structures [266], which itself promotes the initiation reaction and induces a catalytic effect. For instance, resorcinolaniline (R-a) benzoxazine undergoes polymerization (T i 146 • C, T p 179 • C) at a much lower temperature as compared to PH-a [146]. This is accounted to the formation of two vs one phenolic -OH in ring-opened structure in R-a vs. PH-a.
The low percentage of phenols act as an initiator and affect both rate and the temperature required for ROP reaction. Hamerton et al. [275] reported that TDA (3,3-thiodipropionic acid, pK a = 4.11) is a superior initiator to 3,3-thiodiphenol due to its higher pK a value. TDA has a greater effect on the reduction of T o with simultaneous increase in crosslink density as reflected from a high T g value in the resultant polymer.
Natural renewable phenolic acids, cinnamic [102], ferulic [101], coumaric [101] and phloretic acids [104] besides their utility as a feedstock for the synthesis of benzoxazine monomer, were also used as catalyst to reduce the polymerization temperature of the polymerization reaction.

Thiols and Elemental Sulfur
Unlike phenols, thiophenols react with Bz monomers in a reversible manner at ambient temperature. Additionally, high miscibility, inexpensive cost, and stability towards moisture are encouraging towards their practical use. As compared to phenols, thiol compounds are more efficient at lower weight percent loading due to their active hydrogen donating ability. Gorodisher et al. [276] in 2011, reported addition reaction of thiols with Bz for adhesive application. They proposed a two-step Catalytic Opening of the Lateral Benzoxazine Rings by Thiols (COLBERT) mechanism as shown in Figure 38a. A first step involving protonation of the nitrogen atom of an oxazine ring by thiol was proposed. Subsequently, the thiolate ion attacks >CH 2 group between heteroatoms to enable oxazine ring-opening reaction. The overall process is similar to acid catalyzed nucleophilic addition and simultaneous ring-opening reaction of benzoxazines. Due to reversibility of the reaction, only small amounts of thiols reduce the polymerization temperature as shown in DSC thermograms in Figure 38b, and due to a continuous regeneration of active species, thiol and iminium ion, which then mediate polymerization reaction. The protonation of the N or O atom of an oxazine ring by thiol is considered a ratedetermining step as supported by catalytic, and inhibitory effect of acids, and bases on ROP of oxazine ring, respectively. It is observed that monomers sourced from aliphatic amines undergo a more rapid reaction with thiols than aromatic amines due to their more basic nature. The rate of reaction is strongly affected by the acidity of thiol and nature of solvent (protic vs aprotic). Kawaguchi et al. [277,278] investigated the reversible nature of polymerization-depolymerization reaction of pC-a with p-methoxythiophenol (pMOTPH) to form a ring-opened adduct as illustrated in Figure 39a. The yield of adduct is higher in polar solvents as compared to polar aprotic solvents, Figure 39b, which is due to stabilization of the polar zwitter ion/ammonium cation intermediate [277,279,280]. Besides monomer, main-chain type PBz was polymerized at room temperature with various thiols, namely, thiophenol, 2-ethanethiol and 1-butanthiol in CH 3 OH/CHCl 3 for 24 h. Successful incorporation of the thiol compounds to PBz was confirmed by spectral and molecular weight characterizations [279]. Urbaniak et al. [281] proposed that reversible ring-opening of 1,3-benzoxazine with thiols proceeds via an iminium ion intermediate rather than the cyclic six-membered transition state, as shown in Figure 40 [278]. p-Nitrothiophenol and thiophenol promotes a substantial increase in % conversion of monomer as can be seen from Figure 40b, which illustrates the strong influence of thiols with low pK a values. Their work emphasizes the relevance of the protonation step in the ring-opening reactions of benzoxazine with thiols in solvent/solvent-free conditions, allowing predominance of acidity over nucleophilicity [277,281]. Instead of external thiol addition, in situ generated thiol-functionalized benzoxazine monomer from reductive cleavage of a disulfide linked precursor monomer was trapped with epoxides to form substituted Bz structures as shown in Figure 41a. The newly formed monomer exhibited much higher tendency to polymerize than those without sulfide moiety, due to stabilization of intermediate via dipolar interactions including resonance stabilization, as illustrated in Figure 41b [280,282]. Beyazkilic et al. [283] and Narayanan et al. [284] successfully polymerized Bz monomer by simultaneous photoinduced thiol-ene and COLBERT reactions due to the presence of double bonds and oxazine rings. The oxazine ring-opening and allyl group polymerization in BA-ala vs thiol treated BA-ala were observed at~230 and~278 • C vs. 175 and 260 • C, respectively.
Besides thiol reagent, elemental sulfur (S) also acts as reactive reagent and was found to reduce the polymerization temperature of benzoxazine monomer [19,21,24,285,286]. Shukla et al. [21] demonstrated lowering of T p from 263 • C, in C-a monomer, to the copolymerization (C-a and S 8 ) reaction temperature of 185 • C. Figure 42a,b shows optical images of solventless copolymerization reaction at various stages and the possible mode of copolymerization mechanism, respectively. It was proposed that in situ generated polysulfane diradicals react with oxazine ring and double bonds to form poly(C-a-ran-S). The copolymers with sulfur demonstrated their utility as cathodic material in Li-S and Na-S battery [19,21,24,287]. Arza et al. [286] demonstrated an effect of amine basicity in Bz monomer during coreaction with S 8 at 120 • C. They found conversion of monomer to Schiff base in the presence of S 8 is lower for amines containing electron-withdrawing groups (nitro, trifluoromethyl) than electron-donating groups (methoxy) as shown in Figure 43. Arslan et al. [285] supported existence of radical chemistry and liberation of H 2 S gas during copolymerization of BA-ala with S 8 in presence of a radical scavenger. A sulfur radical transfer and coupling (SRTC) reaction was proposed by Lin and Liu [288], as illustrated in Figure 44. PH-a acted as a radical transfer agent for the preparation of copolymers with S 8 . The copolymers revealed superhydrophobicity (with water contact angle~140 • ) along with temperature mediated self-healing properties.

Brønsted Acids
Brønsted acids, especially p-toluenesulfonic acid (TsOH) [255,269,[289][290][291] are widely reported to accelerate oxazine ring-opening by the protonation of nitrogen and/or oxygen atoms followed by a transformation into the final reaction products. The percentage of N,O-acetal (unit A) and Mannich bridge (unit B) structures in polybenzoxazine are affected by TsOH mediated polymerization of pC-a [269]. The former linkages are prominent in the presence of 1 mol% TsOH and low temperature (150 • C). It is evident from Figure 45a,b, at 180 • C, both the monomer consumption and main chain rearrangement were significantly accelerated with the predominance of phenolic Mannich linkages.
An intramolecular approach involving covalently linked acidic functionalities (Ph-OH, -COOH) [11,256,292,293] within the Bz monomer provides several benefits. They catalyze the polymerization reaction by acting as source of protons and stabilize the ring-opened structures. Substitution of carboxylic group pto O atom of oxazine ring in benzoxazine ring assists stabilization of intermediate ion than when present at the pto N atom of oxazine ring. The carboxylic groups undergo decarboxylation during polymerization and enhance the crosslink density. Furthermore, evolution of CO 2 led to foaming of the resin, as shown in Figure 46 [11,111].  Hassan et al. [294] developed a low temperature curable reactive blend of BA-a with BA. The incorporation of BA serves a secondary function to increase the reactivity of the blend serving both as an initiator and as co-reactant. With an increase in BA content to 15 wt%, T p reduced from 245 to 215 • C, and T g from 162 to 147 • C. Beyond 15 wt%, BA incorporation led to a substantial decrease in thermal stability. This is accounted to by the existence of thermally labile BA rich dangling chains in the resultant polymer. Hemvichian and Ishida [295] reported primary decomposition product of PBz are mainly amine, benzene, phenol derivatives. The first mass loss at 150-200 • C is the degradation of BA branches or lightly crosslinked side chains in BA-a/BA polymer [206]. Addition of phenolic nucleophiles (1.5 equivalents), 2-methyl resorcinol (MR), hydroquinone (HQ), pyrogallol (PG) and 2,7-dihydroxynaphthalene (DHNP) to TPHB-a altered T p from 238 • C to 133, 118, 115 and 128 • C, respectively. TPHB-a/DHNP copolymer holds industrial importance due to both high thermal stability and a low processing temperature [145]. In addition to the intermolecular catalysis, an intramolecular approach has also been studied. Chen et al. [296] reported heating a mixture of derivative of Meldrum acid and BA-fa monomer assisted ROP. It is proposed that the decomposition of acid produces ketene first, which upon hydrolysis, is converted to carboxylic acid, affecting polymerization. [297] were found to not only accelerate the polymerization of BA-a due to acidic sulfonic groups (decreased T o and T p values of the BA-a by 39 and 16 • C, respectively) but also increase toughness of the resultant composite. Similarly, incorporation of phenolphthalein polyphosphazene microspheres in BA-a reduced polymerization temperature and led to flame retardance properties due to P and N synergistic effect [298].

Others
Photoinitiated cationic polymerization using diphenyliodonium (Ph 2 I + PF 6 − ) and triphenylsulfonium (Ph 3 S + PF 6 − ) salts led to the light induced generation of protons to form polybenzoxazine (72% conversion). A high monomer concentration (>0.5 mol L −1 ) resulted in oligomer formation, indicating predominance of chain transfer reactions. Besides protons, carbon-centered radicals generated by photolysis of DMPA are oxidized to the corresponding carbocations, which then induce the polymerization of the monomer [299]. Diphenyliodonium salts (ArI + X − ), reported as moderate initiators, are very effective photoinitiators due to their modest stability and low toxicity for cationic polymerization. In their presence, polymerization profiles of BA-a became broad and started at a much lower temperature (162 • C). An anion dependent effect is observed in the initiation activity of the photoinitiators salt. The polymerization proceeds in two steps: the first step involves generation of H + X − , and the second step is the initiation of acid-catalyzed ROP of benzoxazine monomer [300].
Filler-mediated catalysis is yet another approach that has attracted researchers in terms of catalysis and additional benefits such as microwave processing [301]. The acidic functionalities on the surface of montmorillonite (MMT) [191,302], polyhedral oligomeric silsesquioxane (POSS) [303], titania [304] and carbon fiber [305] induce a catalytic effect and lower the ROP of monomers.

Use of Catalysts
The lowering of polymerization temperature was mediated by addition of Lewis acid catalysts, [255,269,271,306,307] metal salts [52,259,308,309], metal organic frameworks [310,311], and nanoparticles [13,303,312,313], which catalyze ROP either due to the presence of empty orbitals or metal ions which have interactions with the lone pair of heteroatoms in oxazine ring and mediate ROP.
The nature of phenolic vs N,O-acetal polymer network structure is dependent on the nature of initiator. A labile proton initiator, such as phenol, results in phenolic structure while a non-labile proton initiator, such as Lewis acid, leads to N,O-acetal structure if polymerization proceeds at a modest temperature. The catalysts affect the polymerization reaction, which proceeds at a lower temperature than usually required, to form phenoxy structures with N,O-acetal linkages, which then undergoes thermal cleavage to form the corresponding phenoxide and iminium ion polymeric intermediates. Further electrophilic attack by a benzene ring on iminium ion species form phenolic Mannich-type rearranged structures, which are apparently more thermally stable, as illustrated in Figure 47. Occurrence of these linkages was first proposed by Wang and Ishida as discussed in next Section 3.2.1. and shown in Figure 48a [255].

Lewis Acids
Wang and Ishida [255] first reported Lewis acids such as PCl 5 , PCl 3 , POCl 3 , TiCl 4 , AlCl 3 and MeOTf mediated cationic ROP of benzoxazines to form N,O-acetyl linked polymer structure at room temperature, as shown in Figure 48a. The polymer yield obtained was highest in case of PCl 5 . With PCl 5 as an initiator, two different polymerization mechanisms competed during the polymer growth, depending on different methyl substitution positions in phenolic ring of the monomers. These mechanisms gave rise to both Mannich base phenoxy-type and phenolic-type polymers [267]. Later Sudo et al. [269] reported the low temperature favored arylether, N,O-acetal structure, a structure that is thermally unstable and can undergo structural transformation to the phenolic-type at an elevated temperature (>160 • C).
Even Lewis acid complexes such as BF 3 /H 2 O, PCl 5 , AlCl 3 , BF 3 ·OEt 2 , etc. [255,257,314] affect benzoxazine polymerization as they increase the basicity of water and indirectly promote the generation of free protons. This then protonates the oxazine ring, which will lead to ring-opening reaction to generate a carbocation. The resultant carbocation reacts by chain transfer reaction to the benzene ring of another benzoxazine molecule, leading to the formation of dimer and other higher oligomers. BF 3 ·OEt 2 was found to be effective in alcoholic solution under mild conditions, and polymerization proceeds through an intermediate hemiaminal ether, which led mainly to the formation of diphenylmethane bridges, Figure 48b, along with the classical Mannich-type in PBz [314]. Thermal behavior of the PBzs formed using Lewis acids complexes exhibits high T g and char yield due to the controlled polymerization conditions. The resultant polymer structure is more ordered as compared to the one obtained during thermal polymerization.
Metal centered compounds accelerate benzoxazine polymerization through the coordination of electron deficient site with the heteroatoms in the oxazine ring. The advantage of utilization of metal complex is due to the ease of tuning of their activity by combination of various metal with appropriate ligands or counter ions. Incorporation of metal simultaneously improves the properties of the resultant composite. Inopportunely, certain metal complexes are relatively intolerant towards moisture, which requires attention during their blending with the monomer, and sometimes the mechanical performance of the material may deteriorate with time. Low and Ishida [52] investigated an improvement in thermal stability of resin on addition of metal chlorides. Transition metal chlorides (~2 mol%) catalyzed polymerization while simultaneously improving the thermal stability and flame retardance characteristics. It appears metal complexes co-ordinate with the lower thermally stable defect structures generated during polymerization such as Schiff base and amide functional groups, thus forming more stable structures before char formation occurs.
Besides lowering of ROP temperature, Sudo et al. [259] studied 4th period transition metals (manganese, iron, cobalt and zinc) acetylacetonato (acac) complexes which allowed ease of processing too. Replacement of ligand from acac with a more electron deficient hexafluoro acac (F 6 -acac) ligand endowed increased Lewis acidity to the complex, and this resulted in an enhanced catalytic activity. Additionally, moisture-tolerance and high activity of F 6 -acac complexes, without their detrimental effect on thermal stability of the polymer, further favor its utility. For instance, acetylene functional benzoxazines undergo thermally activated polymerization where acetylene groups and oxazine rings polymerize simultaneously, releasing large quantities of heat with a sudden increase in viscosity in an extremely short time, affecting processability of pristine monomer. Nickel acetylacetonate hydrate/PPh 3 allowed controllable and mild polymerization conditions as they prepolymerize acetylene groups to polyacetylene Bz structures. Both T p and ∆H reduced from 247 • C and 879 J g −1 to 152 • C and 555 J g −1 , respectively, with enhanced thermal stability [316]. Addition of Fe(acac) 3 (~3.5 mol%) assisted completion of both ring-opening polymerization of oxazine and cyclotrimerization of the cyano group to triazine ring at 350 • C in CN-functionalized Bz [317].
ZnCl 2 is a more effective catalyst than AlCl 3 and PCl 5 for the polymerization, as the resultant polybenzoxazine obtained has a much higher char yield (by 19%) than typical phenolic Mannich type polybenzoxazine with similar T g value [306]. Besides the nature of metal centers in catalysts, ease of dispersion of catalysts, such as cerium nitrate, in the monomer is another key factor which govern their catalytic efficiency [309]. Zinc stearate (10 mol%) was found to be the most effective catalyst to lower the T o of ROP of bio-based C-a monomer from 242 • C to 169 • C [311]. Like zinc salts, zinc-based metal organic frameworks (MOF) led to lowering of E a of polymerization from 98 kJ/mol (neat resin) to 58 kJ/mol due to Lewis acidic nature of Zn 4 O nodes. It was suspected the voids between the MOF allowed swift seepage of monomer to access intrinsic Lewis Zn 4 O nodes catalytic centers. The polymer exhibited a relatively high thermal stability (T 5% = 416 • C) as compared to the pristine polymer (T 5% = 345 • C) [310].
The presence of empty d-orbitals or electron deficient centers in inorganic materials is prudential for ROP. Silica-and boron-modified polybenzoxazine hybrids demonstrated an enhanced thermal stability along with strong catalytic properties due to the Lewis acidic characteristics of Si and B atoms. Use of trisilanolphenyl POSS [318], phenylboronic acid (PBA) [319], 2-phenyl-1,3,2-benzenediolborane [320], poly(resorcinol phenylboronate) (PRB) [321], tris(pentafluorophenyl)borane [315] is also reported. Especially, with only 3 mol% addition of boron-based Lewis acid B(C 6 F 5 ) 3 , a significant increase in char yields (13%) over the pristine polymer is observed, Figure 48c. This is attributed to the high degree of crosslinking induced by the catalyst, coordination between boron (catalyst) and nitro-gen atoms (polybenzoxazine) that may delay the amine degradation in polybenzoxazine, and the usual mode contribution of boron and fluorine atoms induced flame retardation effect [315].

Amines
Agag et al. [322] reported involvement of amine in ROP reaction of benzoxazines. Figure 49a shows the synthetic scheme of monomer, and Figure 49b shows the DSC profile. The pAPH-ddm revealed multiple exothermic peaks both at a low temperature and at the similar temperature as amine protected pAPH-ddm monomer. This supports multistage consumption of the amine as co-reactant. The presence of amide linkage in NTCP functional pAPH-ddm has an effect in the reduction of polymerization temperature. Recently, Sun and coworkers [323] proposed a reaction mechanism of Bz with amines as shown in Figure 50. The ring-opening addition reaction of amine to benzoxazine and the subsequent progression of the reaction led to polymerization via cationic mechanism. The polymerization reaction mechanism involves a reversible reaction of the amine with benzoxazine to form the zwitter ionic intermediates with both phenolate and aminomethanaminium structures. Upon heating at elevated temperature, the aminomethanaminium moiety decomposes to an iminium ion and proceeds towards an electrophilic substitution reaction with the aromatic ring to form a stable aminomethylphenol structure. Amines act as the nucleophile and allow polymerization to proceed at a much milder temperatures (120-150 • C) with faster rates. The E a for polymerization reactions follows the basicity order of amine, arylamine > alicyclic amine > alkylamine. Primary, secondary and tertiary amines successfully assist ring opening reaction of mono-oxazine in polar solvents, and crosslinking reactions was realized in case of reaction of diamine with bis-benzoxazine at room temperature [324]. Addition of polypyrrole (PPy, 5 wt%) also mediates the ROP reaction, and T p value was significantly reduced for C-fa and BF-A, from 245 to 185 • C and 226 to 165 • C, respectively [325]. Imidazoles with and without the labile hydrogen are also reported as good catalysts [326][327][328][329][330].

Latent Catalysts
Mixing active initiators/catalysts with benzoxazines often initiates ROP at low temperature and increases the viscosity significantly during the storage, thus, reducing the shelf life for practical use. Latent catalysts are usually dormant and have minimum activity under normal conditions thereby eliminating storage issues [290,331]. The latent curing systems are usually pre-mixed formulations containing both monomer and hardening reagent, to allow ease of usage with controllable processing characteristics [332]. Generally, they are in form of salt and liberate the active components by an external trigger, which is usually heat [331,333]. Both the anionic (acid) and cationic (basic) species may be involved in the overall polymerization process. They can be organic, inorganic or both. Besides decreasing the polymerization temperature, they also affect the nature of linkages in resultant polymer. This results in variation of both thermal and mechanical properties from those of the pristine polymers [17,334]. Latent catalyst works based on the combined mechanisms. Typically, when the system temperature is raised to the reaction temperature, a heterogeneous latent catalyst undergoes a transition, such as melting, to become an active catalyst before the temperature reaches the polymerization temperature. Some homogeneous latent catalyst achieves time delay based on the non-linear kinetic activation.

Heterogeneous Latent Catalysts
These are solid catalysts and are nearly insoluble in monomer at room temperature. Their existence in different phase is mainly responsible for the suppression of their catalytic activity. However, they induce adverse effects on both fluidity and viscosity of the polymerizing reaction mixture. In this class, the catalysts reported are alkyltosylates (ROTs) [258,290,334], TsOH/amine (isopropanolamine or methylamine) [335], ammonium chloride [336], lithium iodide [307], etc.
Wang et al. [258] reported addition of methyl p-toluenesulfonate (MeOTs, 5 wt%) in BA-a resulted in a complex and broad DSC polymerization profile with multiple exothermic peaks at 144, 179 and 200 • C as compared to neat BA-a (T p 231 • C), shown in Figure 51a. These low temperature peaks are assigned to the polymerization reaction of BA-a by cationic initiation by MeOTs. Replacement of the counter ion from tosylate to triflate in methyl substituted initiator led to a significant increase in T g from 142 to 193 • C of the resultant polybenzoxazine inferring variation in the polymerization structure [255].
It is apparent from Figure 51b that the percentage conversion of monomer is nearly 100% in 3 h at 180 • C in presence of tert-BuOTs than the pristine monomer. The activity of TsOH is higher than ROTs, and the activity of ROTs varies with the nature of alkyl group. The alkyl p-toluenesulfonates acts as "thermally latent catalysts", and their susceptibility to dissociate at the elevated temperatures is highly dependent on its structure. The generated corresponding alkyl cations, TsOH and/or ROTs initiate polymerization reactions as illustrated in Figure 51c,d [290]. A dual system composed of TsOH and EMI (imidazole) effectively promotes the main chain rearrangement reaction from the initially formed N,O-acetal-type to Mannich-type linkage in the solid state [269]. Latent curing salt TsOH with amine catalyzes both polymerization and copolymerization reactions [335,337,338]. The bivalent amine (isopropanolamine, methylamine) was found to be more effective than the univalent amine (diethanolamine or diethylethanolamine). Addition of 10 mol% of latent catalyst to BA-a with bisphenol-A-based epoxy resin led to improvement in T g and flame resistance characteristics of the resultant copolymer. This is accounted by the enhanced crosslink density as both the released amine and acid induce both homo-and co-polymerization reactions [337]. It must be noted that the latent catalyst polymerizes epoxy resin and the resultant polymerization products further catalyzes Bz ring-opening reaction. Thus, it belongs to a secondary latent catalyst for Bz.
Similarly, in polymerization assisted by lithium iodide, lithium cation acts analogous to TsOH due to its very high affinity toward oxazine oxygen atom. Iodide ion serves a dual role, due to its good nucleophilic and leaving group properties [307]. A probable mechanism of LiI catalyzed polymerization is shown in Figure 52a. The obtained polymer mainly furnished phenolic CH 2 units with a high percentage of true phenolic CH 2 units. As a comparison, under similar conditions TsOH provided phenolic CH 2 units with more amounts of general phenolic CH 2 units, and EMI mainly afforded phenoxy CH 2 units, supporting the concept that LiI is a better catalyst to favor true phenolic linkages. Figure 52b,c represents time dependence percentage conversion and DSC polymerization profiles of monomers following the order NaI < EMI < TsOH < LiBr < LiBr/NaI ≈ LiI, confirming LiI is more effective and has nearly the same catalytic effect as LiBr + NaI.
Amine HX salts reduce the ROP temperature, and reduction is found to be both cation and counter-ion dependence and follows the order of I − > Br − > Cl − [331]. Recently, cyanuric chloride (2,4,6-trichloro-1,3,5-triazine, TCT) was used as a miscible latent catalyst; it remained dormant at RT and was activated due to moisture or nucleophile to form HCl and cyanuric acid, which then catalyzes the ROP reaction [339].

Homogeneous Latent Catalysts
A homogeneous liquid of benzoxazines with amines forms intermolecular latent curing system based on reaction equilibrium. This strategy differs fundamentally from the blocked hardeners proceeding to release active groups via thermal deprotection. The reversible reaction of Bz and amine acts as a latent curing system, forming a reaction equilibrium with the intermediate structures of low viscosity at room temperature for a long time as discussed in Section 3.2.2. An imbalance in reaction equilibrium is achieved by heating, leading to rapid increase in viscosity due to polymerization as shown in Figure 53a. The pristine polymer, poly (BF-a), showed a lower tensile strength of 44 MPa as compared to PBz (180 MPa) formed by co-reacting with amine, Figure 53b   In addition to intermolecularly associated compounds such as a salt or complex, intramolecularly associated compounds such as intra-molecular H-bonded material or zwitterions or intramolecular electronic effects also affect the ROP temperature. The stable intramolecular H-bonding interactions at low temperature between the phenolic -OH group with oxazine ring N-atom [333], or N-H of amide group with oxazine ring O atom [341], showed an enhanced shelf life due to inactive nature/unavailability of such acidic hydrogens. However, such hydrogen-bonded interactions are weakened or disrupted upon increasing the temperature leading to the formation of the free phenolic -OH groups inducing a latent catalytic effect on the polymerization reaction. Phenolic hydroxyl bearing naphthoxazines was found to be a latent catalyst for the ROP of simple 1,3-benzoxazines [342]. The presence of phenolic-OH sandwiched between the two oxazine rings in PG-fa monomer [343] and amide derivative of gallic acid-based main-chain benzoxazines revealed a latent effect [344]. Similarly, hydrogen-bonding between phenolic-OH and carbonyl motif in naturally occurring phenol, naringenin-based benzoxazine monomer, NA-fa, is accounted to have a latent effect and leads to a lower polymerization temperature,

Nanomaterials
Organic-inorganic nanocomposites could exhibit unexpected hybrid properties synergistically derived from two components that are dramatically different from their bulk counterparts. Further, due to their nano-size, nanocomposites feature an extensive array of interfacial interactions that can result in salient changes relative to their components properties. The surface of nanomaterials is usually modified to allow their ease of dispersion, reducing aggregation issues, and improve adhesion with the polybenzoxazine matrix. The surface carboxylic and hydroxyl groups on carbon nanotubes [312], core shell rubber (CSR) [345], and graphene oxide [346][347][348], graphene nanoplatelets [349] and metal-oxide nanoparticles (NPs) [13,313] reduce polymerization temperature of benzoxazine monomers with a reduction in E a . A higher T g and char yield is indicative of improvement in intermolecular interactions in the polymerization reaction. Improvement in adhesive strength of steel plates and initial low viscosity of C-a monomer is credited to the higher surface area and acceleration in ROP due to exposition of aluminum atoms on the surface of NPs [13]. Such dual nature of interaction among polybenzoxazine has been studied using inverse chromatography by Xu et al. [350]. A 5 wt% addition of capped iron oxide nanoparticles in benzoxazine monomer endows the benefits of substantial lowering of the polymerization temperature (from 207 • C to 143 • C) and enhancing maximum thermal stability (increase of 34 • C) which is attributed to the iron ions and capping agent. Surprisingly, in addition to the usual chemical linkages in the polybenzoxazine network, Monisha et al. [313] reported the existence of biphenyl linkages due to oxidative polymerization, as shown in Figure 54. Polymer nanocomposites revealed uniform dispersion of iron oxide nanoparticles with good magnetic saturation and superparamagnetic behavior.

Others
Yue et al. [351] investigated the catalytic potential of α-zirconium phosphate (α-ZrP, 3 wt%) and the resulting decrease in T p values of BA-a by 18 • C with concomitant increase in ∆H observed. The poly(BA-a)/α-ZrP composite showed improved thermal properties as exfoliated α-ZrP provided a physical barrier for the spread of flame by retarding the diffusion of both heat and degraded gaseous products.
Chen et al. [352] reported on the addition of a hyperbranched polymeric ionic liquid obtained via a thiol-ene click reaction. Thiol-ended hyperbranched polyesters and 1-allyl-3imethylimidazolium hexafluorophosphate to BA-a and epoxy blend lowers both gelation time and polymerization temperature with an improvement in mechanical strength of benzoxazine/epoxy thermosets, Figure 55 and Table 4. The toughening mechanism was attributed to the in situ reinforcing and toughening mechanisms [352].   Table 4. Thermal stability and degradation data from thermogravimetric analysis under nitrogen atmosphere [352]. Intermolecular H-bonding was found to influence both initiation and acceleration of ring-opening reaction [261]. H-bonding was also found to have negative influence and decelerate chain propagation reaction. The formation of benzoxazine dimer acts as a "self-selective reaction" due to reaction on only one site of phenol, owing to the existence of intramolecular hydrogen bonds as supported by XRD analysis, as illustrated in Figure 56a [80]. The asymmetric molecule thus formed deactivates the other phenolic-OH reactive site due to strong intramolecular hydrogen bond. A similar obstructive behavior due to intramolecular hydrogen bond leads to self-termination as shown in Figure 56b of ring-opening reaction of p-substituted benzoxazines is reported [132]. On the contrary, close vicinity of o-methylol group in PH-a assist ROP via inter-molecular H-bonding [353]. The H-bonding between the hydroxyl groups of polybenzoxazine influences physica crosslinks due to extension of intermolecular H-bonding with the polar functionalitie (carbonyl, ether, amine, hydroxyl) present in other polymers such as poly(ɛ-caprolactone (PCL) [354][355][356], poly(ethylene oxide), [357,358] chitosan (CS) [359][360][361][362], amino-cellulose [363] and polyurethane [364][365][366][367]. Although, the effect of OH groups on the polymeriza tion of -OH or -NH2 containing benzoxazine monomers, non-benzoxazine monomers and polymers is not explicitly stated. However, this intermolecular H-bonding between pola groups of polymers and oxazine ring catalyzes the ring-opening kinetics and is expected to typically reduce the polymerization exotherm temperature in DSC thermograms.
These intermolecular specific interactions influence the chain structure of main pol ymer backbone and affect microstructure morphology leading to variation in thermal and mechanical properties. A controlled nanoscale microphase separation is observed in a co polymer PBz and PCL. As shift in Tm value of PCL in blend to higher temperature sug gested development of physical crosslinks between the two, which hinders the transfer o heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single Tg which supports miscibility of the two in the melt state as shown in Figure 57a [356,368]. Figure  57b shows a segregation of PCL spherulitic morphologies and an effect on its growth rate is observed which confirms a reduction in their chain mobility and dilution of PCL do mains due to the interpenetrating PBz framework [369]. The polymer blends appeared to be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scale as supported by 13  -caprolactone) (PCL) [354][355][356], poly(ethylene oxide), [357,358] chitosan (CS) [359][360][361][362], amino-cellulose [363] and polyurethane [364][365][366][367]. Although, the effect of OH groups on the polymerization of -OH or -NH 2 containing benzoxazine monomers, non-benzoxazine monomers and polymers is not explicitly stated. However, this intermolecular H-bonding between polar groups of polymers and oxazine ring catalyzes the ring-opening kinetics and is expected to typically reduce the polymerization exotherm temperature in DSC thermograms.
These intermolecular specific interactions influence the chain structure of main polymer backbone and affect microstructure morphology leading to variation in thermal and mechanical properties. A controlled nanoscale microphase separation is observed in a copolymer PBz and PCL. As shift in T m value of PCL in blend to higher temperature suggested development of physical crosslinks between the two, which hinders the transfer of heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single T g which supports miscibility of the two in the melt state as shown in Figure 57a [356,368]. Figure 57b shows a segregation of PCL spherulitic morphologies and an effect on its growth rate is observed which confirms a reduction in their chain mobility and dilution of PCL domains due to the interpenetrating PBz framework [369]. The polymer blends appeared to be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scale as supported by 13 C CP/MAS NMR spectroscopic analyses [370]. Instead of physical blend, naphthoxazine functional PCL macromonomers were synthesized using NP-ea as the coinitiator for the stannous-2-ethylhexanoate catalyzed living ring-opening polymerization of tension of intermolecular H-bonding with the polar functionalities ne, hydroxyl) present in other polymers such as poly(ɛ-caprolactone) y(ethylene oxide), [357,358] chitosan (CS) [359][360][361][362], amino-cellulose ne [364][365][366][367]. Although, the effect of OH groups on the polymerizacontaining benzoxazine monomers, non-benzoxazine monomers and icitly stated. However, this intermolecular H-bonding between polar and oxazine ring catalyzes the ring-opening kinetics and is expected he polymerization exotherm temperature in DSC thermograms. cular specific interactions influence the chain structure of main polaffect microstructure morphology leading to variation in thermal and es. A controlled nanoscale microphase separation is observed in a co-L. As shift in Tm value of PCL in blend to higher temperature sugof physical crosslinks between the two, which hinders the transfer of e region of PCL [368]. PCL/PBz blends revealed a single Tg which of the two in the melt state as shown in Figure 57a [ [359][360][361][362], amino-cellulos [363] and polyurethane [364][365][366][367]. Although, the effect of OH groups on the polymeriza tion of -OH or -NH2 containing benzoxazine monomers, non-benzoxazine monomers and polymers is not explicitly stated. However, this intermolecular H-bonding between pola groups of polymers and oxazine ring catalyzes the ring-opening kinetics and is expected to typically reduce the polymerization exotherm temperature in DSC thermograms. These intermolecular specific interactions influence the chain structure of main pol ymer backbone and affect microstructure morphology leading to variation in thermal and mechanical properties. A controlled nanoscale microphase separation is observed in a co polymer PBz and PCL. As shift in Tm value of PCL in blend to higher temperature sug gested development of physical crosslinks between the two, which hinders the transfer o heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single Tg which supports miscibility of the two in the melt state as shown in Figure 57a [356,368]. Figur 57b shows a segregation of PCL spherulitic morphologies and an effect on its growth rat is observed which confirms a reduction in their chain mobility and dilution of PCL do mains due to the interpenetrating PBz framework [369]. The polymer blends appeared to be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scale as supported by 13 C CP/MAS NMR spectroscopic analyses [370]. Instead of physical blend, naphthoxa zine functional PCL macromonomers were synthesized using NP-ea as the coinitiator fo the stannous-2-ethylhexanoate catalyzed living ring-opening polymerization of ɛ-capro lactone [371]. The flame resistance of poly(benzoxazine-co-ε-caprolactam) nanocompo sites was improved by incorporation of cyclotriphosphazene fiber [372]. It is possible tha H-bonding interactions between the produced hydroxyl groups of the open-ring Mannich base of the propagating species and poly(ε-caprolactone) or poly(ε-caprolactam) chains a molecular level may influence the fundamental structural changes of the polybenzoxazin crosslinked networks [354]. The H-bonding between the hydroxyl groups of polybenzoxazine influences physical crosslinks due to extension of intermolecular H-bonding with the polar functionalities (carbonyl, ether, amine, hydroxyl) present in other polymers such as poly(ɛ-caprolactone) (PCL) [354][355][356], poly(ethylene oxide), [357,358] chitosan (CS) [359][360][361][362], amino-cellulose [363] and polyurethane [364][365][366][367]. Although, the effect of OH groups on the polymerization of -OH or -NH2 containing benzoxazine monomers, non-benzoxazine monomers and polymers is not explicitly stated. However, this intermolecular H-bonding between polar groups of polymers and oxazine ring catalyzes the ring-opening kinetics and is expected to typically reduce the polymerization exotherm temperature in DSC thermograms.
These intermolecular specific interactions influence the chain structure of main polymer backbone and affect microstructure morphology leading to variation in thermal and mechanical properties. A controlled nanoscale microphase separation is observed in a copolymer PBz and PCL. As shift in Tm value of PCL in blend to higher temperature suggested development of physical crosslinks between the two, which hinders the transfer of heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single Tg which supports miscibility of the two in the melt state as shown in Figure 57a [356,368]. Figure  57b shows a segregation of PCL spherulitic morphologies and an effect on its growth rate is observed which confirms a reduction in their chain mobility and dilution of PCL domains due to the interpenetrating PBz framework [369]. The polymer blends appeared to be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scale as supported by 13 C CP/MAS NMR spectroscopic analyses [370]. Instead of physical blend, naphthoxazine functional PCL macromonomers were synthesized using NP-ea as the coinitiator for the stannous-2-ethylhexanoate catalyzed living ring-opening polymerization of ɛ-caprolactone [371]. The flame resistance of poly(benzoxazine-co-ε-caprolactam) nanocomposites was improved by incorporation of cyclotriphosphazene fiber [372]. It is possible that H-bonding interactions between the produced hydroxyl groups of the open-ring Mannich base of the propagating species and poly(ε-caprolactone) or poly(ε-caprolactam) chains at molecular level may influence the fundamental structural changes of the polybenzoxazine crosslinked networks [354].
-caprolactone) or poly( based Bz [132]. The H-bonding between the hydroxyl groups of polybenzoxazine influ crosslinks due to extension of intermolecular H-bonding with the polar (carbonyl, ether, amine, hydroxyl) present in other polymers such as poly(ɛ (PCL) [354][355][356], poly(ethylene oxide), [357,358] chitosan (CS) [359][360][361][362], am [363] and polyurethane [364][365][366][367]. Although, the effect of OH groups on th tion of -OH or -NH2 containing benzoxazine monomers, non-benzoxazine m polymers is not explicitly stated. However, this intermolecular H-bonding groups of polymers and oxazine ring catalyzes the ring-opening kinetics a to typically reduce the polymerization exotherm temperature in DSC therm These intermolecular specific interactions influence the chain structur ymer backbone and affect microstructure morphology leading to variation i mechanical properties. A controlled nanoscale microphase separation is ob polymer PBz and PCL. As shift in Tm value of PCL in blend to higher tem gested development of physical crosslinks between the two, which hinders heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a si supports miscibility of the two in the melt state as shown in Figure 57a    Chitosan (CS)/PBz blends revealed lowering in the ROP due to catalytic effect of amine group of CS [359][360][361]. Additionally, synergistic hydrogen bonding interactions may have role in the chain propagation in ROP reaction. The ROP temperature of V-fa was reduced remarkably to 70 • C from 204 • C when blended with CS due to Schiff base formation [361]. A probable existence of physical and chemical crosslinks network is supported, as shown in Figure 58. Among naturally occurring amine sources, amino acids, dopamine and mussel-inspired catechol-derivatives hold great potential in benzoxazine chemistry. A few other animal sourced amine or phenolic compounds that were used for making benzoxazines are catechol [100], dopamine [114] and amino acids [100,373,374].

Participation of the Non-Oxazine Functional Group on the Polybenzoxazine Formation
The existence of certain functionalities participates in the polybenzoxazine formation. The aldehyde group in V-a monomer undergoes in situ oxidation to carboxylic acid during polymerization, Figure 59a. The so-formed carboxylic acid group, like in pHBA-a [96,293,375], assists acid mediated polymerization of V-a and undergoes decarboxylation upon further heating and thus provides additional crosslinking sites for the growth of polymer framework. Knoevenagel reaction [377,378] is a well-known synthetic method to form C=C group from dehydration reaction between aldehyde and methyl functionality. In HBAD-amp, electron-withdrawing character of -CHO group lowered the ROP temperature (T o reduced to 208 • C from 240 • C) to the one without it. Heating the resultant polymer to higher temperature suppressed the formation of styrylpyridine-containing polybenzoxazine. This leads to a remarkably enhanced thermal stability due to occurrence of the intra-or intermolecular Knoevenagel condensation reactions between benzaldehyde and methylpyridine groups as shown in Figure 59b, as indicated by FTIR studies [376].

Influence by Molecular Alignment or Packing
Introduction of Bz functionality in the side chain of polymer backbone imparted characteristic properties on the resultant molecules. Cationic ROP occurred at a lower temperature with a faster polymerization rate than ordinary benzoxazine resins in liquid crystalline (LC) benzoxazine resins [379]. Main-chain type linear benzoxaine polymers containing diacetylene and oxazine groups showed unusual polymerization behavior with the exotherm maximum below 200 • C and onset at 125 • C. It was suspected that the rigid diacetylene moieties in the polymer backbone favored local chain ordering beyond the melting temperature leading to lowered oxazine ring-opening polymerization temperature [380]. Faster polymerization (as low as ca. 110 • C) is observed even above the liquid crystal forming temperature. It is possible that the rigid chromophores maintain local order above the liquid crystal transition temperature, making it easier to polymerize. Birefringent polybenzoxazine film based on mono-oxazine structure was obtained; however, it suffers from dissolution issues due to low molecular weight of polymer [381]. Kawauchi et al. [382] reported with lower percentage conversion (~40%), the polymer film treated at 160 • C followed by cooling showed birefringence, indicating that regain of ordering at molecular level was due to reversibility in thermoresponsive phase transition, Figure 60a. The poly(BA-cab) exhibits a liquid crystalline phase after ROP of BA-cab at 240 • C. This may be due to the orderly stacking and arrangement of the mesogens favored by strong short-range interaction and availability of cholesterol-based mesogens in the side-chain rather than the backbone, as indicated from SAXS spectrum in Figure 60b. The crosslinked liquid crystalline PBz reveals a very high thermal conductivity [383].

Modification of Monomer Structures by Electron-Donating or -Withdrawing Groups
Structure of the mono-oxazine ring was shown to be a distorted semichair with ring strain. This strain, resulting from distorted molecular conformation, makes it possible for an oxazine ring to undergo ROP under favorable conditions. To affect ROP reaction, other than the electronegativity of oxazine ring (electron rich nitrogen and oxygen), free o-position of the benzene ring with respect to phenolic-OH was shown to be necessary towards thermal polymerization of monomer with or without catalyst in the temperature range 150-230 • C. In the presence of cationic initiator, propagation of polymerization reaction can proceed by reacting at unobstructed o-position of benzene ring to produce Mannich base phenolic type polymers. In this case, monomer propagates via formation of carbocation which is stabilized by intramolecular H-bonding and leads to high molecular weight polymer formation [267]. The conversion at maximum polymerization rate was found to be independent of the polymerization temperature. Study of the polymerization, especially kinetics of thermoset material, is necessary for determining its practical usage [384]. However, a comprehensive study of processing conditions and chemo-rheological behaviors, such as determination of time-temperature-transformation (TTT) diagram [385], has not yet been reported.
The purity, type, position, number and nature of substituents on the benzene ring of phenol and/or amine and oxazine ring, chemical reactants, catalyst used and the polymerization conditions influence ROP and, consequently, the structure of polymer [82,138,292,375]. With increase in purity of benzoxazine, polymerization temperature increases. Han et al. [121] provided an experimental evidence to support the intrinsic ROP without an added initiator using a high purity monomer, as shown in Figure 61. Unlike initiator driven polymerization where T p is expected to increase substantially towards zero initiator concentration, the T p observed approached an asymptotic value near zero initiator concentration, supporting the hypothesis that oxazine ring can undergo intrinsic self-initiating ring-opening polymerization. The presence of impurities or catalysts decreases the polymerization temperature but not necessarily required to initiate the polymerization. This phenomenon was termed as thermally accelerated polymerization. The electronic character of substituents has great influences on the kinetics of polymerization of monomer. Electron-withdrawing groups promote the thermally accelerated ROP with a reduction in E a by increasing the bond length and lowering the bond energy of C-O on an oxazine ring. Electron withdrawing groups at the p-position of both aromatic rings of PH-a, viz., nitro, formyl, chlorine and carboxylic, methacrylol, coumarin, etc., affect polymerization temperature [11,138,273,292,323].
With the increase in the electron-withdrawing nature of the substituents, the polymerization temperature decreases with the concomitant increase in ∆H values [97,210,228,375,386]. This effect is due to the generation of more acidic phenolic species as compared to unsubstituted monomer thereby increasing the catalytic activity. Furthermore, it is supported by reduced catalytic activity as indicated by an increase in the polymerization temperature of p-substituted photopolymerized methacrylol PH-a from 203 to 222 • C [228]. With -COOH, regardless of the position occupied, benzoxazine monomers were found to polymerize just after melting at much lower temperature. This behavior is attributed to the more pronounced effect that the acidic nature of the -COOH group has rather than its electronic effect. The -COOH catalyzes the reaction by increasing the concentration of oxonium species in the polymerizing medium. PH-a without any substitution showed T p exotherm at 262 • C. On substituting p-position of both phenol and aniline moiety with -COOH, -OH group T p decreased to 208 • C [11,292] as supported through polymerization kinetics and modelling studies. The opposite effect was observed when electron-withdrawing substituents were attached to the p-position of phenyl or aniline ring. A decrease in T p is observed when an electron-withdrawing group (NO 2 , Cl) is present at pto the phenyl ring while their presence at position pto aniline ring increases the T p . This effect is attributed to the destabilization of phenoxide ion by electron-withdrawing substituents at p-position of phenyl ring. In the case of electron donor substituents such as methoxy and methyl group, no notable effect on the rate of polymerization was observed irrespective of its presence in phenyl or aniline ring [138]. The only exception to this is the substitution by -OH/NH 2 group in phenyl ring [110,322]. The amine and ammonium groups were found to affect the occurrence of benzoxazine polymerization at low temperature [273,323,336,359,361,387]. The basicity of N atom affects the rate of oligomer formation and thus polymerization [140,388]. Surprisingly, presence of electron withdrawing acetylene-functional group in aniline at the m-position lowered the T p by 36 • C as compared to its structure without acetylene group [389]. Both PH-fa and BA-fa showed a decrease of 14 and 20 • C, respectively, in ROP temperature as compared to PH-a and BA-a supporting the suggested role played by amine component is correct. Furan ring of furfuryl amine undergoes electrophilic aromatic substitution reactions more readily than a benzene ring of aniline [130]. The presence of fluorine at the meta-position to phenol ring facilitated both polymerization and crosslinking reactions, which is accounted to its smaller size and electron withdrawing nature [390]. The existence of phenolic-OH [391][392][393][394][395], phenyl thioether and hydroxyl [104,282,396,397] moieties lowers the polymerization temperature. Besides DSC plots, polymerization of benzoxazines can even be monitored by time-conversion plots at variable temperature [282], where either the conversion of monomer or formation of polymer can be monitored by various techniques. It was found that processing at low temperature, followed by heating at high temperature, interconverts the nature of linkages, i.e., induces conversion of labile to thermally stable crosslinking of network, with improved thermal properties.
Similar results were obtained when bridging electron-withdrawing groups present in diamine 4,4 -diaminodiphenylmethane (ddm) and 4,4 -diaminodiphenylether (dde). The ddm based Bz showed 10 • C lower T o than dde based monomers. However, their counterparts containing methylol groups (named oMeOPH-dde and oMeOPH-ddm, respectively) at different positions plays a significant role in accelerating polymerization due to intramolecular assistance [398].
Similarly, even structural isomers in amine component with position of polar ether linkages (p-vs. m-), a prominence of electronic effects in polymerization temperature is obvious. A lowering in T o value with biphenyl ether linkage at pvs. m-position in diamine suggesting an interplay of electronic effects [399].
As compared to PH-ddm, no significant change in T p is observed when methyl groups are present on phenol (o/m/pC, PH, 2,4-DMPH) rather on amine (ddm) in bis-benzoxazine as shown in Figure 62a. However, oand p-blocked phenol based monomers showed a substantial increase in T p as evident from DSC trace in Figure 62b [167].
A variation in diamine component from aromatic to aliphatic also affected the polymerization temperature. Allen et al. [137] investigated the effect of aliphatic diamine chain length and relative position of methyl substituent in phenol ring in benzoxazine monomer. Methyl substitution in phenol decreased the reactivity of the monomer and caused the position of the polymerization exotherm to increase to higher temperatures, as can be seen from Figure 63. Polymerization of the o-substituted monomer is forced to proceed through less favorable p-position as indicated by high temperature required for polymerization.
Even the temperature required to thermally activate benzoxazine polymerization directly increases as a function of diamine chain length. The dilution of oxazine functionality with non-reactive functionalities such as alkyl, alkoxy or other inactive groups, increases the polymerization temperature [116,238].  The electronic effects from bridging groups in bisphenol [400] or diamine [399] effects on ring-forming and ring-opening reactions have been studied using the compounds shown in Figure 64a. In general, electron-withdrawing groups present in phenol affect the condensation reaction to form the monomer as they induce electronic effect which lowers the reactivity of phenolic-OH. On the contrary, presence of such groups in phenolic ring promotes thermally accelerated polymerization due to the stabilization of the ring opened intermediate ion. The electronic effect due to various bridging groups such as >C(CH 3 ) 2 , >CH 2 , >O, >CO, and >SO 2 in bisphenol-A was studied. A variation in position of ether linkage, pvs min the aromatic diamine found to lower the ROP temperature. Especially, stronger electron-withdrawing groups revealed predominance of arylamine methylene Mannich bridge structure in the polybenzoxazine network. Figure 64b shows that the value of T p varies in the order BA-a < BF-a < DHDPE-a < EDP-a < DHBoP-a < DHDPS-a as predicted by electron donating or withdrawing nature of bridging groups [400]. Compared with BA-a, the bis-benzoxazine containing Schiff base linkages forms aligned chain segments requiring higher energy to facilitate the polymerization due to π-π stacking. This restricts the motion of oxazine rings, leading to less involvement of oxazine rings in polymerization and, therefore, resulting in lower ∆H values [192]. Incorporation of rigid spacer units, trimethylphenyl indane and tetramethyl spirobiindane between the reactive benzoxazine units, leads to mobility restriction imposed on the reactive sites by the increasing viscosity of the polymerizing medium, affecting the polymerization rate [401]. The effect of intermolecular H-bonding between the urea linkages allowed close proximity of oxazine rings, which in turn, lead to accelerated polymerization at much lower temperature [225].
Introduction of fluorenyl unit as bridging group in bis-amine or bis-phenol similar to BA-a did not show noticeable effect in affecting ring-opening temperature, suggesting nonparticipation of such functionality electronically in affecting intermediate stability [154,157]. Interestingly, certain functionalities in the monomer such as diethylphosphonate groups undergoes thermal dissociation to form acidic phosphite groups which catalyze the ROP as reflected with lower value of E a [17].
Instead of introduction of functionalities in the phenol or amine group involved directly in the formation of benzoxazine ring, Bz ROP is also sensitive to when functionality is varied at the other positions. For instance, presence of electron withdrawing end-caps attached to the imide ring present at ortho-position to the phenol ring in Bz monomer also lower the polymerization temperature [202].

Design of Monomer Structure to Influence the Intermolecular Packing (Rigid Groups)
Over the time, to improve crosslinking density and hence T g of polybenzoxazine, monomers containing multiple oxazine rings are synthesized using multifunctional phenol/amine as a starting material. With each increase in the number of oxazine rings, polymerization temperature reduces substantially. This lowering in temperature is attributed to the presence of intramolecular cross-interaction between oxazine ring and aromatic hydrogens as indicated by the respective 1 H-1 H NOESY NMR spectra of benzoxazine monomers. Another advantage observed was the decrease in the weight loss during curing (from 90% to 2.4%) with increase in T g [147]. Introduction of the two oxazine functionality onto single benzene reduced the polymerization temperature by 62 • C. Incorporation of the third oxazine functionality was not much effective and ROP temperature was reduced only by 13 • C as its phenolic ring is completely substituted and has no free reactive position [144].
NTCDA was chosen to prepare indole-containing benzoxazine due to its rigid structure, which helped in decreasing the ring-opening temperature of dianhydride ring during its reaction with amines as shown in Figure 65 [244]. The conversion from polybenzoxazine to polybenzoxazole accompanies water or CO 2 formation when the precursor is o-amide or o-imide functional benzoxazine, respectively. While the amount of water produced is relatively small, it is nonetheless desirable to avoid small molecular compound formation in a short period to avoid potential void formation during processing. Taking advantage of different temperature for water and CO 2 formation of the o-amide and o-imide functional benzoxazines, Zhang et al. [197] synthesized an asymmetric bisoxazine molecule having both o-amide and o-imide groups as shown in Figure 66a. Indeed, the volatile formation at each transition nearly halved. The maxima of ROP of o-(amide-imide) Bz monomer (oAI-a) lies in between o-amide (oA-a) and o-imide (oI-a) Bz monomer, as evident from Figure 66b, exhibiting melting point at 125 • C, whereas o-imide monomer polymerized without melting resulted in low degree of crosslinking and low heat of polymerization, which is due to highest rigidity oI-a. Unexpectedly, it was found that o-(amide-imide) polybenzoxazine has the highest thermal stability. This class of polymers exhibit unusual thermomechanical properties in that G is nearly constant in a wide temperature range from room temperature to 400 • C.

Influence of Oxazine Ring-Opening by Intramolecular Interactions: Neighboring Group Effect and 5-or 6-Membered Ring H-Bonding
Neighboring group participation of hydroxyl group in ROP of oxazine ring in a substituted phenol-based vs. unsubstituted or suitably modified benzoxazine (control) has been studied [189,398,403]. Kiskan et al. [190,217] synthesized hydroxyethyl terminated ether chain-functional benzoxazine monomers and found a reduction in polymerization temperature as compared to traditional unfunctionalized benzoxazine monomer. Kudoh et al. [189] extended the mechanistic knowledge of the polymerization reaction to elaborate the role of the hydroxyethyl functionality in activating the ring-opening reaction of the N-(2hydroxyethyl)-1,3-benzoxazine monomer. N-(2-hydroxyethyl)-1,3-benzoxazine was found to polymerize at a much faster rate than non-polar structural analogue. This is accounted to the intramolecular reaction of hydroxyl groups with cationic moieties of the zwitterionic intermediate formed by the ring-opening reaction of benzoxazine and in situ generated a 5-membered cyclic N,O-acetal structure as illustrated in Figure 67a. Sudo et al. [404] reported utility of amino acid, namely, glycine and β-alanine as amine component (as a tetrabutylammonium salt) with p-cresol to form mono-oxazine monomer. The rate of polymerization is faster for glycine (with 100% conversion within 5 h at 120 • C) followed by alanine and then 2-aminoethanol followed by methylamine based benzoxazine. The reason attributed for such a fast polymerization rate is the neighboring group participation of carboxylate ion and the effect that polarity of the solvent and counter ion has. An increase in steric bulk to the substituent N-alkyl group of benzoxazine monomer led to a decrease in the polymerization rate [405]. This is accounted to the release of volatile N-alkylimine compound as a byproduct in bulk amount. Replacement of N-propyl to N-allyl functionality in benzoxazine exhibited a faster polymerization rate. This is again due to the stability imparted by the intramolecular interaction between the cationic species and the π-bond of the allyl group [406].  [197]. Copyright 2015. Reproduced with permission from Royal Society of Chemistry.
Altering 2-hydroxyethyl to 2-hydroxymethyl, i.e., o-/m-/p-methylol-substituted benzoxazines found to accelerate the rate of polymerization as compared to PH-a. Baqar et al. [403] studied the effect of methylol group at o-, pand m-position of phenolic ring on polymerization as shown in Figure 67b,c. The heat of polymerization and T p for the methylol substituted monomers is lower than the control, PH-a. This suggests the co-occurrence of ROP and the release of water as a byproduct from the polymerization. This also posits the electronic and intramolecular H-bonding interactions between methylol and oxygen in the oxazine ring and thus activating the ring to open and polymerize at low temperature. The effect is more pronounced in o-methylol, which is attributed to the resonance of the benzoxazine ring being affected by the methylol to form the intramolecular 6-membered hydrogen bonding, as proposed in Figure 67b. Methylol monomer exhibits lower E a compared to the unfunctionalized monomer [407].
Similarly, existence of phenolic-OH group in pyrogallol based benzoxazines PG-fa and PG-a and naphthoxazine revealed interesting H-bonding interactions, Figure 68. Low monomer loss due to evaporation is observed as ensured by stable intramolecular H-bonds with nitrogen atoms in napthoxazine. The -OH interacts with the N in the pyrrolidine ring and oxazine ring through stable intramolecular hydrogen bonds instead of presenting free -OH at room temperature, leading to the enhanced shelf life of the monomer. The free phenolic -OH initiates and catalyzes the polymerization. A latent catalytic effect is observed in 2-NP-3-apd [333]. Later temperature dependent effect of H-bonds on ROP was studied with the help of interaction of free phenolic hydroxyl between two oxazine rings attached to the same benzene ring as in pyrogallol. Interestingly, the unprotected hydroxyl group accelerates the cleavage of oxazine ring, thereby promoting ROP reaction. The intermolecular hydrogen bonding -OH· · · N (of another benzoxazine molecule R1) changed preferentially to the -OH· · · π intramolecular hydrogen bonding OH . . . .π-electron of the benzene ring as shown in Figure 68b. As a result of these interactions, it may be anticipated that PG based benzoxazine monomer may show a lower T p and E a than 2-NP-3-apd [408].

Background of Intramolecular H-bonding in Benzoxazines
The structure of inter-and intra-molecular H-bonding occurring in benzoxazine dimers, trimers and tetramers was studied by high-resolution solid-state 1 H NMR. The 2D single quantum-double quantum spectroscopic results provided evidence for local helical formation trend in polybenzoxazine chains despite the polymer being overall amorphous [409]. The persistence of intramolecular hydrogen bonding does exist even in the molten state [125]. It was proposed that benzoxazine with free o-position in phenol or two free hydroxyl groups in an open benzoxazine ring reveals co-occurrence of both inter-and intra-molecular H-bond between -OH-N-, depending on the pK a value of the involved species. This led to the formation of asymmetric product due to preoccupancy of such van der Waals forces. Therefore the p-substituted phenol-based monomers undergo self-terminated ROP as soon as dimer forms instead of giving linear oligomer or polymer, with varied reaction conditions as supported by TLC, HPLC, FTIR, 1 H-NMR and elemental analysis [80,132]. This feature is illustrated in Figure 69.  Hypothesis of the molecular mechanism for self-termination of a p-substituted phenol-based benzoxazine [132]. Intramolecular hydrogen bonds are the basis for ring-shape and helical conformations of trimeric and tetrameric units of Bz. Hydrogen bonds strongly influence the adopted structural conformation. Both trimers and tetramers contained stable intramolecular OH-N and usual OH-O hydrogen bonds giving them a closed-ring like geometry [409].
The -OH-N intramolecular hydrogen bonding forms a stable six-membered structure, resulting in a methylene proton deshielding effect in methylene protons. The amine functional group in the Mannich bridge is greatly responsible for the distribution of hydrogen bonding species. The strength of hydrogen bonding is dependent on the electronegativity of the side group or the basicity of amine functional group which is attached to the nitrogen atom [265,410]. Therefore, BA-m mainly consists of -OH-N intramolecular hydrogen bonding while BA-a has a large amount of intermolecular hydrogen bonding and relatively weak hydrogen bonding groups in the polymer network structure. The various proposed cyclic structures of N,N-bis(3,5-dimethyl-2-hydroxybenzyl)methylamine dimers showed different types of H-bonding interactions to various extents by FTIR analysis as tabulated in Table 5 [411], which are consistent with XRD structures of methyl-dimer [125]. The extent and nature of hydrogen bonding network is closely related to the basicity of the amine constituent [410]. A weaker amine, aniline (a) based poly(BA-a) showed great OH...N intermolecular hydrogen bonding while the remainder was intramolecular hydrogen bonding as shown in Figure 70. On the contrary, a monomer based on a stronger amine, methylamine (ma), poly(BA-ma) revealed a dominance of intramolecular hydrogen bonding interactions [265]. Besides basicity of amine, an interplay of the proton-transfer equilibrium between drogen bonding species. The strength of hydrogen bonding is dependent on the electronegativity of the side group or the basicity of amine functional group which is attached to the nitrogen atom [265,410]. Therefore, BA-m mainly consists of -OH---N intramolecular hydrogen bonding while BA-a has a large amount of intermolecular hydrogen bonding and relatively weak hydrogen bonding groups in the polymer network structure. The various proposed cyclic structures of N,N-bis (3,5-dimethyl-2-hydroxybenzyl)methylamine dimers showed different types of H-bonding interactions to various extents by FTIR analysis as tabulated in Table 5 [411], which are consistent with XRD structures of methyldimer [125]. The extent and nature of hydrogen bonding network is closely related to the basicity of the amine constituent [410]. A weaker amine, aniline (a) based poly(BA-a) showed great OH...N intermolecular hydrogen bonding while the remainder was intramolecular hydrogen bonding as shown in Figure 70. On the contrary, a monomer based on a stronger amine, methylamine (ma), poly(BA-ma) revealed a dominance of intramolecular hydrogen bonding interactions [265]. Besides basicity of amine, an interplay of the proton-transfer equilibrium between HO····N ⟷ O − ····H⁺N in the Mannich bridge (as >NMe or >NPh) is also accounted to the variable distribution of hydrogen bonding networks. As a result in the Mannich bridge (as >NMe or >NPh) is also accounted to the variable distribution of hydrogen bonding networks. As a result of above interactions, the polarizability of the proton is shifted depending upon the nature of amine; it is found more towards the HO····N in case of aniline-based model compounds.

Smart Benzoxazines
In general, external addition of initiators/catalysts suffer from thermal instability, limited shelf life and time-dependent leaching out of the polymer matrix. Furthermore, certain niche applications demand absence of such aids. Such initiators and proton donors can be incorporated into either the monomer or polymeric structures. This covalent tethering of initiator functionalities overcomes the issues of high volatility and migration rates often associated with low-molecular weight initiators. The covalent bond between initiator and monomers acts as "equivalent initiator monomers" [11,292,392,412] and inherent functionalities which mediates ring-opening reactions inter-molecularly [379,380,413] and intra-molecularly [189,414]. Figure 71a compares the DSC thermograms of mono-oxazine benzoxazine with and without the intramolecular five-membered ring H-bonding, showing dramatic influence on the polymerization exotherm temperature, supporting catalyzing effect of intramolecular H-bonding interactions [243]. The existence of intermolecular vs intramolecular fivemembered-ring hydrogen bonding interactions between the NH (amide group) and the oxygen (oxazine ring) in pHBA-a vs. oHBA-a was supported by concentration independent FTIR and NMR experiments Figure 71b,c. A comparison of T p amongst all known mono-oxazine structures with o-amide containing benzoxazines revealed an outstanding tendency to polymerize at much lower temperatures without the use of either initiator or catalyst [193,195]. As illustrated in Figure 72, Froimowicz et al. [415] demonstrated the existence of a five-membered ring intramolecular hydrogen bonding in o-amide isomer (oHBA-a, HBA-hydroxybenzoic acid) vs. intermolecular H-bonding in p-amide (pHBA-a) benzoxazine isomer influencing T p to vary, as 187 and 241 • C, respectively. Interestingly, the most favored reacting site for extending the polymerization is the 7-position (m-to phenolic-OH), unlike other conventional benzoxazines as presented in Figure 72.

Conclusions
The current review is designed and written in order to understand the importance of reagent choice in designing Bz monomers and their associated structure-property relationship, notably, polymerization characteristics. As such, the structure of Bz monomers has a strong influence on the formation of polymers and the related applications. The field is widely explored utilizing both petrobased and biobased/agrowaste origin feedstocks to form Bz monomers. Nevertheless, on one side, the utility of natural and waste origin chemicals as feedstocks for the manufacture of polybenzoxazines is steadily increasing, while on the other side, petrobased raw materials are used to structurally design new monomer structures to affect polymerization conditions and resultant properties. Advancement in lowering the polymerization temperature either by molecular tailoring at the structure level or by adding external aids and/or copolymerization with other polymer structures is still progressing on different frontiers. This progress is heavily dependent on the processability and end-use applications. Unlocking new frontiers using inherent functionalities thoughtfully may help in developing new domains of robust applications. While it is interesting and easier to exploit structure variation of phenol and amine to form the Bz structure, demand for new areas of exploration is high. Consequently, the extension of bonding characteristics, such as hydrogen bonding, in situ structural transformations, interactions other than the usual PBz linkages, etc., hold significant potential. An intense focus on expanding the scope of PBzs with high thermal stability, flexibility in the polymer backbone, low polymerization and processing temperature is needed to take research to next level.
These intermolecular specific interactions influence the chain structure of main polmer backbone and affect microstructure morphology leading to variation in thermal and echanical properties. A controlled nanoscale microphase separation is observed in a coolymer PBz and PCL. As shift in Tm value of PCL in blend to higher temperature sugested development of physical crosslinks between the two, which hinders the transfer of eat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single Tg which upports miscibility of the two in the melt state as shown in Figure 57a       BA-a/MWCNT (1:1 wt%) Nanocomposites            The H-bonding between the hydroxyl groups of polybenzoxazine influences physical crosslinks due to extension of intermolecular H-bonding with the polar functionalities (carbonyl, ether, amine, hydroxyl) present in other polymers such as poly(ɛ-caprolactone) (PCL) [354][355][356], poly(ethylene oxide), [357,358] chitosan (CS) [359][360][361][362], amino-cellulose [363] and polyurethane [364][365][366][367]. Although, the effect of OH groups on the polymerization of -OH or -NH2 containing benzoxazine monomers, non-benzoxazine monomers and polymers is not explicitly stated. However, this intermolecular H-bonding between polar groups of polymers and oxazine ring catalyzes the ring-opening kinetics and is expected to typically reduce the polymerization exotherm temperature in DSC thermograms.
These intermolecular specific interactions influence the chain structure of main polymer backbone and affect microstructure morphology leading to variation in thermal and mechanical properties. A controlled nanoscale microphase separation is observed in a copolymer PBz and PCL. As shift in Tm value of PCL in blend to higher temperature suggested development of physical crosslinks between the two, which hinders the transfer of heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single Tg which supports miscibility of the two in the melt state as shown in Figure 57a [356,368]. Figure  57b shows a segregation of PCL spherulitic morphologies and an effect on its growth rate is observed which confirms a reduction in their chain mobility and dilution of PCL domains due to the interpenetrating PBz framework [369]. The polymer blends appeared to be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scale as supported by 13 C CP/MAS NMR spectroscopic analyses [370]. Instead of physical blend, naphthoxazine functional PCL macromonomers were synthesized using NP-ea as the coinitiator for the stannous-2-ethylhexanoate catalyzed living ring-opening polymerization of ɛ-caprolactone [371]. The flame resistance of poly(benzoxazine-co-ε-caprolactam) nanocomposites was improved by incorporation of cyclotriphosphazene fiber [372]. It is possible that H-bonding interactions between the produced hydroxyl groups of the open-ring Mannich base of the propagating species and poly(ε-caprolactone) or poly(ε-caprolactam) chains at molecular level may influence the fundamental structural changes of the polybenzoxazine crosslinked networks [354]. The H-bonding between the hydroxyl groups of polybenzoxazine influences physical crosslinks due to extension of intermolecular H-bonding with the polar functionalities (carbonyl, ether, amine, hydroxyl) present in other polymers such as poly(ɛ-caprolactone) (PCL) [354][355][356], poly(ethylene oxide), [357,358] chitosan (CS) [359][360][361][362], amino-cellulose [363] and polyurethane [364][365][366][367]. Although, the effect of OH groups on the polymerization of -OH or -NH2 containing benzoxazine monomers, non-benzoxazine monomers and polymers is not explicitly stated. However, this intermolecular H-bonding between polar groups of polymers and oxazine ring catalyzes the ring-opening kinetics and is expected to typically reduce the polymerization exotherm temperature in DSC thermograms.
These intermolecular specific interactions influence the chain structure of main polymer backbone and affect microstructure morphology leading to variation in thermal and mechanical properties. A controlled nanoscale microphase separation is observed in a copolymer PBz and PCL. As shift in Tm value of PCL in blend to higher temperature suggested development of physical crosslinks between the two, which hinders the transfer of heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single Tg which supports miscibility of the two in the melt state as shown in Figure 57a [356,368]. Figure  57b shows a segregation of PCL spherulitic morphologies and an effect on its growth rate is observed which confirms a reduction in their chain mobility and dilution of PCL domains due to the interpenetrating PBz framework [369]. The polymer blends appeared to be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scale as supported by 13 C CP/MAS NMR spectroscopic analyses [370]. Instead of physical blend, naphthoxazine functional PCL macromonomers were synthesized using NP-ea as the coinitiator for the stannous-2-ethylhexanoate catalyzed living ring-opening polymerization of ɛ-caprolactone [371]. The flame resistance of poly(benzoxazine-co-ε-caprolactam) nanocomposites was improved by incorporation of cyclotriphosphazene fiber [372]. It is possible that H-bonding interactions between the produced hydroxyl groups of the open-ring Mannich base of the propagating species and poly(ε-caprolactone) or poly(ε-caprolactam) chains at molecular level may influence the fundamental structural changes of the polybenzoxazine crosslinked networks [354]. The H-bonding between the hydroxyl groups of polybenzoxazine influences physical crosslinks due to extension of intermolecular H-bonding with the polar functionalities (carbonyl, ether, amine, hydroxyl) present in other polymers such as poly(ɛ-caprolactone) (PCL) [354][355][356], poly(ethylene oxide), [357,358] chitosan (CS) [359][360][361][362], amino-cellulose [363] and polyurethane [364][365][366][367]. Although, the effect of OH groups on the polymerization of -OH or -NH2 containing benzoxazine monomers, non-benzoxazine monomers and polymers is not explicitly stated. However, this intermolecular H-bonding between polar groups of polymers and oxazine ring catalyzes the ring-opening kinetics and is expected to typically reduce the polymerization exotherm temperature in DSC thermograms.
These intermolecular specific interactions influence the chain structure of main polymer backbone and affect microstructure morphology leading to variation in thermal and mechanical properties. A controlled nanoscale microphase separation is observed in a copolymer PBz and PCL. As shift in Tm value of PCL in blend to higher temperature suggested development of physical crosslinks between the two, which hinders the transfer of heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single Tg which supports miscibility of the two in the melt state as shown in Figure 57a [356,368]. Figure  57b shows a segregation of PCL spherulitic morphologies and an effect on its growth rate is observed which confirms a reduction in their chain mobility and dilution of PCL domains due to the interpenetrating PBz framework [369]. The polymer blends appeared to be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scale as supported by 13 C CP/MAS NMR spectroscopic analyses [370]. Instead of physical blend, naphthoxazine functional PCL macromonomers were synthesized using NP-ea as the coinitiator for the stannous-2-ethylhexanoate catalyzed living ring-opening polymerization of ɛ-caprolactone [371]. The flame resistance of poly(benzoxazine-co-ε-caprolactam) nanocomposites was improved by incorporation of cyclotriphosphazene fiber [372]. It is possible that H-bonding interactions between the produced hydroxyl groups of the open-ring Mannich base of the propagating species and poly(ε-caprolactone) or poly(ε-caprolactam) chains at molecular level may influence the fundamental structural changes of the polybenzoxazine crosslinked networks [354]. between the hydroxyl groups of polybenzoxazine influences physical tension of intermolecular H-bonding with the polar functionalities ine, hydroxyl) present in other polymers such as poly(ɛ-caprolactone) ly(ethylene oxide), [357,358] chitosan (CS) [359][360][361][362], amino-cellulose ane [364][365][366][367]. Although, the effect of OH groups on the polymerizacontaining benzoxazine monomers, non-benzoxazine monomers and licitly stated. However, this intermolecular H-bonding between polar and oxazine ring catalyzes the ring-opening kinetics and is expected he polymerization exotherm temperature in DSC thermograms. ecular specific interactions influence the chain structure of main polaffect microstructure morphology leading to variation in thermal and es. A controlled nanoscale microphase separation is observed in a co-CL. As shift in Tm value of PCL in blend to higher temperature sugof physical crosslinks between the two, which hinders the transfer of ne region of PCL [368]. PCL/PBz blends revealed a single Tg which of the two in the melt state as shown in Figure 57a [80]. Copyright 2001. Reproduced with permission from American Chemical Society. (b) Self-termination of ring opening reaction of p-substituted phenolbased Bz [132].
These intermolecular specific interactions influence the chain structure of main polymer backbone and affect microstructure morphology leading to variation in thermal and mechanical properties. A controlled nanoscale microphase separation is observed in a copolymer PBz and PCL. As shift in Tm value of PCL in blend to higher temperature suggested development of physical crosslinks between the two, which hinders the transfer of heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single Tg which supports miscibility of the two in the melt state as shown in Figure 57a [356,368]. Figure  57b shows a segregation of PCL spherulitic morphologies and an effect on its growth rate is observed which confirms a reduction in their chain mobility and dilution of PCL domains due to the interpenetrating PBz framework [369]. The polymer blends appeared to be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scale as supported by 13 C CP/MAS NMR spectroscopic analyses [370]. Instead of physical blend, naphthoxazine functional PCL macromonomers were synthesized using NP-ea as the coinitiator for the stannous-2-ethylhexanoate catalyzed living ring-opening polymerization of ɛ-caprolactone [371]. The flame resistance of poly(benzoxazine-co-ε-caprolactam) nanocomposites was improved by incorporation of cyclotriphosphazene fiber [372]. It is possible that H-bonding interactions between the produced hydroxyl groups of the open-ring Mannich base of the propagating species and poly(ε-caprolactone) or poly(ε-caprolactam) chains at molecular level may influence the fundamental structural changes of the polybenzoxazine crosslinked networks [354].  [80]. Copyright 2001. Reproduced with permission from American Chemical Society. (b) Self-termination of ring opening reaction of p-substituted phenolbased Bz [132].
These intermolecular specific interactions influence the chain structure of main polymer backbone and affect microstructure morphology leading to variation in thermal and mechanical properties. A controlled nanoscale microphase separation is observed in a copolymer PBz and PCL. As shift in Tm value of PCL in blend to higher temperature suggested development of physical crosslinks between the two, which hinders the transfer of heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single Tg which supports miscibility of the two in the melt state as shown in Figure 57a [356,368]. Figure  57b shows a segregation of PCL spherulitic morphologies and an effect on its growth rate is observed which confirms a reduction in their chain mobility and dilution of PCL domains due to the interpenetrating PBz framework [369]. The polymer blends appeared to be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scale as supported by 13 C CP/MAS NMR spectroscopic analyses [370]. Instead of physical blend, naphthoxazine functional PCL macromonomers were synthesized using NP-ea as the coinitiator for the stannous-2-ethylhexanoate catalyzed living ring-opening polymerization of ɛ-caprolactone [371]. The flame resistance of poly(benzoxazine-co-ε-caprolactam) nanocomposites was improved by incorporation of cyclotriphosphazene fiber [372]. It is possible that H-bonding interactions between the produced hydroxyl groups of the open-ring Mannich base of the propagating species and poly(ε-caprolactone) or poly(ε-caprolactam) chains at molecular level may influence the fundamental structural changes of the polybenzoxazine crosslinked networks [354].  [80]. Copyright 2001. Reproduced with permission from American Chemical Society. (b) Self-termination of ring opening reaction of p-substituted phenolbased Bz [132].
These intermolecular specific interactions influence the chain structure of main polymer backbone and affect microstructure morphology leading to variation in thermal and mechanical properties. A controlled nanoscale microphase separation is observed in a copolymer PBz and PCL. As shift in Tm value of PCL in blend to higher temperature suggested development of physical crosslinks between the two, which hinders the transfer of heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a single Tg which supports miscibility of the two in the melt state as shown in Figure 57a [356,368]. Figure  57b shows a segregation of PCL spherulitic morphologies and an effect on its growth rate is observed which confirms a reduction in their chain mobility and dilution of PCL domains due to the interpenetrating PBz framework [369]. The polymer blends appeared to be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scale as supported by 13 C CP/MAS NMR spectroscopic analyses [370]. Instead of physical blend, naphthoxazine functional PCL macromonomers were synthesized using NP-ea as the coinitiator for the stannous-2-ethylhexanoate catalyzed living ring-opening polymerization of ɛ-caprolactone [371]. The flame resistance of poly(benzoxazine-co-ε-caprolactam) nanocomposites was improved by incorporation of cyclotriphosphazene fiber [372]. It is possible that H-bonding interactions between the produced hydroxyl groups of the open-ring Mannich base of the propagating species and poly(ε-caprolactone) or poly(ε-caprolactam) chains at molecular level may influence the fundamental structural changes of the polybenzoxazine crosslinked networks [354].  [80]. Copyright 2001. Reproduced with pe American Chemical Society. (b) Self-termination of ring opening reaction of p-subs based Bz [132].
The H-bonding between the hydroxyl groups of polybenzoxazine influ crosslinks due to extension of intermolecular H-bonding with the polar (carbonyl, ether, amine, hydroxyl) present in other polymers such as poly(ɛ (PCL) [354][355][356], poly(ethylene oxide), [357,358] chitosan (CS) [359][360][361][362], am [363] and polyurethane [364][365][366][367]. Although, the effect of OH groups on th tion of -OH or -NH2 containing benzoxazine monomers, non-benzoxazine m polymers is not explicitly stated. However, this intermolecular H-bonding groups of polymers and oxazine ring catalyzes the ring-opening kinetics a to typically reduce the polymerization exotherm temperature in DSC therm These intermolecular specific interactions influence the chain structur ymer backbone and affect microstructure morphology leading to variation i mechanical properties. A controlled nanoscale microphase separation is ob polymer PBz and PCL. As shift in Tm value of PCL in blend to higher tem gested development of physical crosslinks between the two, which hinders heat to the crystalline region of PCL [368]. PCL/PBz blends revealed a si supports miscibility of the two in the melt state as shown in Figure 57a [35 57b shows a segregation of PCL spherulitic morphologies and an effect on is observed which confirms a reduction in their chain mobility and diluti mains due to the interpenetrating PBz framework [369]. The polymer blend be homogeneous at the 40-70 nm scale but heterogeneous at the 2-4 nm scal by 13 C CP/MAS NMR spectroscopic analyses [370]. Instead of physical blen zine functional PCL macromonomers were synthesized using NP-ea as the the stannous-2-ethylhexanoate catalyzed living ring-opening polymerizati lactone [371]. The flame resistance of poly(benzoxazine-co-ε-caprolactam sites was improved by incorporation of cyclotriphosphazene fiber [372]. It i H-bonding interactions between the produced hydroxyl groups of the open base of the propagating species and poly(ε-caprolactone) or poly(ε-caprolac molecular level may influence the fundamental structural changes of the po crosslinked networks [354].