Alginate/Banana Waste Beads Supported Metal Nanoparticles for Efficient Water Remediation

Water pollution is considered a perilous issue that requires an immediate solution. This is largely because of the strong correlation between the global population increase and the amount of waste produced (most notably food waste). This project prompts the conversion of food waste into useful materials that can be used with sodium alginate as a catalytic support for metal nanoparticles. Sodium alginate/banana peel (Alg/BP) beads were prepared simply using an eco-friendly method. The prepared materials were modified using nanostructured materials to enhance their characteristics. Alg/BP beads were employed as adsorbents for metals that were then treated with sodium borohydride to produce MNPs@Alg/BP. Different MNPs@Alg/BP (MNPs = Ag, Ni, Co, Fe, and Cu) were used as catalysts for reducing 4-nitrophenol (4-NP) by NaBH4 to evaluate each catalyst performance in a model reaction. The results exhibited that Cu@Alg/BP was most efficient toward complete transformation of 4-NP. Therefore, Cu@Alg/BP was also used as a catalyst for the reduction of potassium ferricyanide, congo red, methyl orange (MO), and methylene blue. It was found that Cu@Alg/BP beads catalytically reduced up to 95–99% of above pollutants within a few minutes. Cu@Alg/BP beads were more selective in reducing MO among the pollutants. The catalytic activity of Cu@Alg/BP was examined by evaluating the impact of numerous parameters on MO reduction. The results are expected to provide a new strategy for the removal of inorganic and organic water contaminants based on efficient and low-cost catalysts.


Introduction
For last few decades, drinking water has been in high demand because of the rapid increase in population growth. Due to the recent expansion of civilization, several industrial products are widely used, such as plastics and phenolic products, which decompose into toxic chemical compounds that pollute the environment to a great extent. Moreover, human life and health, aquatic habitats, and plant species are significantly impacted. The existing source of pristine water is continuously contaminated by these industries and their toxic products. For example, groundwater is considered as a primary source of potable water for many countries; however, its quality is constantly deteriorating owing to the use of dyes, heavy metals from industries and fertilizers and pesticides from agricultural processes. Most rivers and ponds worldwide are remarkably polluted by the continuous discharge of various industrial effluents resulting in a remarkable negative influence on human health and the natural ecosystem. It has been reported that some highly toxic chemical species have been found in drinking water at alarming levels. Their effects are obvious through the presence of certain diseases that noticeably spread across the world such as liver disorder, kidney failure, and cancer. Therefore, environmentally friendly and cheaper adsorbent materials are urgently needed to improve the quality of water by eliminating chemical toxicants from potable water [1,2]. as large surface area to volume ratios and high reactivity. Notably, many different metal nanoparticles (MNPs) can be efficiently used for environmental pollutants removal [1,2]; however, the fact that NPs usually agglomerate in a reaction mixture is a significant issue. As a solution for this issue, MNPs could be applied on the surface of solids as a catalytic support. Today, many synthetic and natural polymers can be utilized as effective catalytic supports for different kinds of heterogeneous catalysts owing to their special surfaces and good mechanical characteristics, which lead to their long-term use [1]. According to the literature, many MNPs-based polymers have been widely used for environmental applications due to their valuable advantages such as high porosity and surface area, chemical stability as well as their uniform and interconnected structures [2].
Sodium alginate is a kind of polysaccharide that is plentifully available in marine brown algae. It is naturally soluble in hot water forming a viscous solution. It is an electrostatically interactive and eco-friendly degradable compound since it contains hydroxyl (-OH) and carboxylate (-COO−) functional groups in its chemical structure [21,22]. Most importantly, various metal cations can be bound to it forming a spherical structure. However, the ionically-cross-linked hydrogel of pure alginate displays some unfavorable structural characteristics such as a weak mechanical strength and structural instability causing some limitations in its application in the field of catalysis. In order to overcome these issues, the mechanical strength could be enhanced by integrating interactable polymers or nanomaterials [23,24].
In this current study, a composite of alginate polymer with banana peels (Alg/BP) as a catalytic support for different metal nanoparticles (Cu, Ag, Ni, Co, and Fe) was successfully prepared and utilized as catalysts for the reduction reaction of some environmental pollutants, 4-NP, K 3 [Fe(CN) 6 ] and three organic dyes (MO, MB, and CR), in the presence of a reducing agent (NaBH 4 ).

Materials and Method
Sodium borohydride (NaBH 4 , 97%) and Na-Alginate were purchased from BDH chemicals, UK. Organic dyes (congo red (CR), methyl orange (MO) and methylene blue (MB)), 4-nitrophenol (4-NP), and potassium hexacyanoferrate (III) were purchased from Sigma-Aldrich, USA. All other reagents were of spectral and analytical purity grade. Distilled water was used for all preparations of solutions.

Preparation of Alg/BP and MNPs@Alg/BP
Alg/BP nanocatalyst was prepared by dispersing BP in Alg solution. Briefly, banana peels were dried in open air and then ground into a fine powder. Then, 1.0 g of BP was blended with 50 mL of Alg and, after complete mixing, a viscous suspension was formed and poured into a syringe. AlCl 3 (2.0 M) solution was prepared in water and used as a cross linker for preparing the hydrogel beads. The viscous Alg was kept in the syringe with mixed BP solution and added dropwise to AlCl 3 solution. Each drop was turned into a round bead in AlCl 3 solution due to the AlCl 3 crosslinked Alg chains. Alg/BP beads were kept overnight in AlCl 3 solution and then washed carefully with distilled water. The washing continued until complete removal of surplus and unreacted Al 3+ from the Alg/BP beads. Afterwards, the Alg/BP beads were dried in open air at room temperature. The carboxyl groups of Alg cross-linked physically with cations such as Al 3+ in the aqueous solutions. After adding the solution of Alg with BP dropwise to AlCl 3 solution, sphereshaped gel formed abruptly due to electrostatic interaction amongst the carboxyl groups of Alg (negative charge) and Al 3+ cations (positive charge). As a result, the carboxyl group of sodium alginate and Al 3+ cations made it possible to cross-link with one another and convert the BP dispersed Alg solution into a gel that settled in AlCl 3 aqueous solution in the form of beads.
A total of 0. the metal ions. Beads acquired the color of the concerned salt solution after 24 h, which indicates the adsorption of the metal salt on the surface and interlayer of beads. The beads were removed from the salt solution and washed several times to eliminate the un-adsorbed metal. The metal adsorbed beads were further dipped in NaBH 4 aqueous solution, and they turned black because NaBH 4 reduced the adsorbed metal ions (Ag + , Ni 2+ , Co 2+ , Fe 3+ , and Cu 2+ ) to the corresponding MNPs (AgNPs, NiNPs, CoNPs, FeNPs, and CuNPs). The preparation and applications of the developed catalysts are graphically shown in Scheme 1.
convert the BP dispersed Alg solution into a gel that settled in AlCl3 aqueous solution in the form of beads.
A total of 0.2 g of Alg/BP beads were added to the metal salt solution (AgNO3, NiSO4·7H2O, Co(NO3)2·6H2O, FeCl3, CuSO4·5H2O) and kept overnight for adsorption of the metal ions. Beads acquired the color of the concerned salt solution after 24 h, which indicates the adsorption of the metal salt on the surface and interlayer of beads. The beads were removed from the salt solution and washed several times to eliminate the un-adsorbed metal. The metal adsorbed beads were further dipped in NaBH4 aqueous solution, and they turned black because NaBH4 reduced the adsorbed metal ions (Ag + , Ni 2+ , Co 2+ , Fe 3+ , and Cu 2+ ) to the corresponding MNPs (AgNPs, NiNPs, CoNPs, FeNPs, and CuNPs). The preparation and applications of the developed catalysts are graphically shown in Scheme 1.

Scheme 1.
Graphical presentation of the preparation and application of the developed nanocatalysts.

Instrumental Analysis
The morphology and the structure of MNPs@Alg/BP nanocatalysts were investigated using different analytical techniques. Scanning electron microscopy (FESEM from JEOL, JSM-7600F, Tokyo, Japan) was employed to study the morphology of MNPs@Alg/BP nanocatalysts. Energy dispersive X-ray spectroscopy (EDS) connected with FESEM was employed to analyze the composition of MNPs@Alg/BP nanocatalysts. X-ray diffraction (XRD) using a PANalytical diffractometer applying a Kα radiation (λ = 0.154 nm) source was employed to study the crystallinity of the sample. The functional groups of the MNPs@Alg/BP nanocatalysts were characterized by employing a Fourier transform infrared (ATR-FTIR) spectrometer (NicoletTM iS50 FTIR Spectrometer-Thermo Fisher Scientific, Waltham, MA, USA). ATR-FTIR was employed to record the spectrum in the range of 400 to 4000 cm −1 . A UV-vis spectrophotometer was applied to examine the catalytic reduction of inorganic and organic contaminants in the presence of MNPs@Alg/BP nanocatalysts.

Catalytic Studies
MNPs@Alg/BP nanocatalysts were used to assess the catalytic reaction of inorganic and organic contaminants.

Instrumental Analysis
The morphology and the structure of MNPs@Alg/BP nanocatalysts were investigated using different analytical techniques. Scanning electron microscopy (FESEM from JEOL, JSM-7600F, Tokyo, Japan) was employed to study the morphology of MNPs@Alg/BP nanocatalysts. Energy dispersive X-ray spectroscopy (EDS) connected with FESEM was employed to analyze the composition of MNPs@Alg/BP nanocatalysts. X-ray diffraction (XRD) using a PANalytical diffractometer applying a Kα radiation (λ = 0.154 nm) source was employed to study the crystallinity of the sample. The functional groups of the MNPs@Alg/BP nanocatalysts were characterized by employing a Fourier transform infrared (ATR-FTIR) spectrometer (NicoletTM iS50 FTIR Spectrometer-Thermo Fisher Scientific, Waltham, MA, USA). ATR-FTIR was employed to record the spectrum in the range of 400 to 4000 cm −1 . A UV-vis spectrophotometer was applied to examine the catalytic reduction of inorganic and organic contaminants in the presence of MNPs@Alg/BP nanocatalysts.

Catalytic Studies
MNPs@Alg/BP nanocatalysts were used to assess the catalytic reaction of inorganic and organic contaminants. The catalytic performance of MNPs@Alg/BP nanocatalysts was evaluated toward an inorganic pollutant K 3 [Fe(CN) 6 ], a positively charged dye (MB), two negatively charged dyes (CR and MO) and 4-NP. Equation (1) was applied to calculate the removal (%): where C o = initial concentration and C f = final concentration of contaminants.

Characterization
As previously mentioned, in order to overcome the agglomeration of Cu nanoparticles in the reaction mixture, they were applied to the surface of Alg@BP as a catalytic support, which effectively enhanced the performance of the nanocatalysts. Consequently, it is very important to characterize the structure of the prepared Cu@Alg/BP since the nature and structure of adsorbents play an essential role in catalytic reduction reactions of water-based pollutants for better aquatic purification. Accordingly, FESEM was employed to study the surface morphology and EDS was applied for elemental analysis of Cu@Alg/BP for further confirmation.
In FESEM, the surface morphology was analyzed and the observed morphology of Cu@Alg/BP is shown in Figure 1. High-magnification FESEM shows a sphere shape bead of Alg/BP in the size range of 1.5-2.5 mm. As can be obviously seen in the low magnification FESEM image (Figure 1), spherical shaped particles were developed on the surface of the Alg/BP. Additionally, the surface of Alg/BP was coated with sufficiently separated metal nanoparticles. Obviously, the grooves seen on the surface were caused by the elimination of water, which resulted in shrinkage of the polymer matrix. The highly magnified image (Figure 1a) reveals the roughness of the surface with good dispersion indicating that Cu nanoparticles had been embedded in and on the surface of Alg/BP. lysts was added and UV-vis spectrum was continuously measured after every 1.0 min monitor the catalytic reduction of the contaminant and the catalytic activity MNPs@Alg/BP nanocatalysts. The reduction reactions were monitored by a decrease λmax of K3[Fe(CN)6] (415 nm), 4-NP (4-nitrophenolate ion = 415 nm), MO (460 nm), CR (4 nm), and MB (658 nm).
Equation (1) was applied to calculate the removal (%): where Co = initial concentration and Cf = final concentration of contaminants.

Characterization
As previously mentioned, in order to overcome the agglomeration of Cu nanopar cles in the reaction mixture, they were applied to the surface of Alg@BP as a catalytic su port, which effectively enhanced the performance of the nanocatalysts. Consequently, is very important to characterize the structure of the prepared Cu@Alg/BP since the natu and structure of adsorbents play an essential role in catalytic reduction reactions of wate based pollutants for better aquatic purification. Accordingly, FESEM was employed study the surface morphology and EDS was applied for elemental analysis of Cu@Alg/B for further confirmation.
In FESEM, the surface morphology was analyzed and the observed morphology Cu@Alg/BP is shown in Figure 1. High-magnification FESEM shows a sphere shape be of Alg/BP in the size range of 1.5-2.5 mm. As can be obviously seen in the low magnific tion FESEM image (Figure 1), spherical shaped particles were developed on the surface the Alg/BP. Additionally, the surface of Alg/BP was coated with sufficiently separat metal nanoparticles. Obviously, the grooves seen on the surface were caused by the elim ination of water, which resulted in shrinkage of the polymer matrix. The highly magnifi image ( Figure 1a) reveals the roughness of the surface with good dispersion indicati that Cu nanoparticles had been embedded in and on the surface of Alg/BP. EDS investigations also verified the successful preparation of Cu@Alg/BP. It show peaks for carbon and oxygen as the main elements having 36.87 and 51.50 wt%, respe tively, as shown in Figure 2. As previously indicated, banana peels contain organic com pounds that are rich in carbon such as pectin substances, hemicellulose, and cellulose. EDS investigations also verified the successful preparation of Cu@Alg/BP. It showed peaks for carbon and oxygen as the main elements having 36.87 and 51.50 wt%, respectively, as shown in Figure 2. As previously indicated, banana peels contain organic compounds that are rich in carbon such as pectin substances, hemicellulose, and cellulose. It is also because of the several functional groups in the sodium alginate beads. Moreover, EDS spectra demonstrate a signal for Cu (10.45 wt%) suggesting the successful formation of is also because of the several functional groups in the sodium alginate beads. Moreov EDS spectra demonstrate a signal for Cu (10.45 wt%) suggesting the successful formati of such nanocomposites. The slight presence of Al (1.18 wt%) resulted from the crosslink present in the sample.

Catalytic Properties
In order to evaluate the catalytic activity of MNPs@Alg/BP the catalytic reducti reactions of K 3 [Fe(CN) 6 ], 4-NP, CR, MB, and MO were studied. Additionally, the MO duction reaction was chosen for further investigation as it showed better results than oth pollutants in terms of removal % and the reaction rate constant.
3.2.1. Catalytic Reduction of 4-NP Using MNPs@Alg/BP 4-Aminophenol, which is formed from the reduction of 4-NP is commonly used synthesize antipyretic and analgesic medicines such as paracetamol, phenacetin, and etanilide. On the downside, 4-NP is naturally toxic and pollutes the biosphere when dustries produce it. Therefore, its reduction is significantly needed by changing it to a other nontoxic compound in the attempt to minimize its harmfulness. The reduction of NP by NaBH4 using five different MNPs@Alg/BPs was investigated to evaluate the ca lytic performance of the catalyst. Ag, Ni, Co, Fe, and Cu nanoparticles were incorporat with Alg/BP (1 bead).
Noticeably, an absorption band at 400 nm appeared after the peak at 317 nm cor sponding to 4-NP disappeared confirming that a nitrophenolate ion was formed, shown in Figure 3. This shift to 400 nm can be attributed to the deprotonation of the -O group existing in 4-NP. Visually, the only noticeable change during the reduction of 4-N was the change of color from bright yellow to darker shade. Basically, this reaction is on thermodynamically feasible in an aqueous solution of BH4 -. However, this reaction ha slow rate as a result of the large kinetic barrier caused by the large potential differen between the strong reducing agent (NaBH4) and 4-NP. As a result, a catalyst is requir for 4-NP reduction because the energy barrier can be reached more quickly to compl the reaction at room temperature.

Catalytic Properties
In order to evaluate the catalytic activity of MNPs@Alg/BP the catalytic reduction reactions of K 3 [Fe(CN) 6 ], 4-NP, CR, MB, and MO were studied. Additionally, the MO reduction reaction was chosen for further investigation as it showed better results than other pollutants in terms of removal % and the reaction rate constant.

Catalytic Reduction of 4-NP Using MNPs@Alg/BP
4-Aminophenol, which is formed from the reduction of 4-NP is commonly used to synthesize antipyretic and analgesic medicines such as paracetamol, phenacetin, and acetanilide. On the downside, 4-NP is naturally toxic and pollutes the biosphere when industries produce it. Therefore, its reduction is significantly needed by changing it to another nontoxic compound in the attempt to minimize its harmfulness. The reduction of 4-NP by NaBH 4 using five different MNPs@Alg/BPs was investigated to evaluate the catalytic performance of the catalyst. Ag, Ni, Co, Fe, and Cu nanoparticles were incorporated with Alg/BP (1 bead).
Noticeably, an absorption band at 400 nm appeared after the peak at 317 nm corresponding to 4-NP disappeared confirming that a nitrophenolate ion was formed, as shown in Figure 3. This shift to 400 nm can be attributed to the deprotonation of the -OH group existing in 4-NP. Visually, the only noticeable change during the reduction of 4-NP was the change of color from bright yellow to darker shade. Basically, this reaction is only thermodynamically feasible in an aqueous solution of BH 4 -. However, this reaction has a slow rate as a result of the large kinetic barrier caused by the large potential difference between the strong reducing agent (NaBH 4 ) and 4-NP. As a result, a catalyst is required for 4-NP reduction because the energy barrier can be reached more quickly to complete the reaction at room temperature.
After addition of 10 mg of catalyst, the reduction process of 4-NP by the reducing agent was constantly evaluated using UV-visible spectroscopy where the changes in 4-NP concentration against time was recorded. A darker yellow color was observed when NaBH 4 was added to the reduction reaction of 4-NP, which is naturally bright yellow, catalyzed by the MNPs@Alg/BP. A colorless solution was finally obtained within 20.0, 18.0 and 17.0 min, when Ag, Ni, and Co nanoparticles@Alg/BP (1 bead) were added, respectively. The complete reaction took only 15.0 min when Fe and Cu nanoparticles@Alg/BP were used. A shorter period of time (12.0 min) was achieved for competence of this catalytic reduction using Cu@Alg/BP (2 beads), as revealed in Figure 3f. A steady decrease was observed in the absorption peak at 400 nm. Meanwhile, an absorption peak at 300 nm was observed confirming the formation of the amino group of 4-AP for which the increase in absorption indicated that the reduction reaction was complete. The nanocatalyst (MNPs@Alg/BP) accelerated the transfer of electrons from BH 4 -(the reducing agent) to 4-NP. The removal % of 4-NP by the five different MNPs@Alg/BPs (1 bead) can be calculated using Equation (1). Values of 85.89%, 91.93%, 61.79%, 58.36% and 95.86% were obtained for the removal of 4-NP by converting it to 4-AP using Ag, Ni, Co, Fe, and Cu nanoparti-cles@Alg/BP, respectively, as shown in Figure 3g. The highest removal % (97.09%) was achieved by using Cu@Alg/BP (2 beads). Consequently, Cu@Alg/BP (2 beads) was further used for the other kind of pollutants owing to its efficiency in catalysis. The adsorption of 4-NP on the catalysts' surfaces significantly influenced the step rate of the electron transference. 4-Nitrophenolate ions diffuse onto the nanocatalysts' surfaces to react with the active proton species, which come from the adsorption of hydride ion (BH 4 − ) on the nanocatalyst surface. The adsorbed nitro group reacts with BH 4 − where the electrons are released from it to 4-NP resulting in the reduction of 4-NP to 4-AP.
The kinetics of MNPs@Alg/BP toward 4-NP reduction by NaBH 4 follow a pseudo first-order rate [24], as shown in Equation (2): where C t and C o are the concentrations of the pollutant and A t and A o are UV-Vis absorbances at designated time and t = 0, respectively. K (min −1 ) is the rate constant of the reduction reaction. Based on Equation (2), the slope of the plot of ln C t /C o versus reduction time (t) gives the value of K app , as presented in Figure 3h. It was found that the values of K app for the catalytic reduction of 4-NP by NaBH 4 using 1 bead of Ag@Alg/BP, Ni@Alg/BP, Co@Alg/BP, Fe@Alg/BP, and Cu@Alg/BP were 0.0930 min −1 , 0.1043 min −1 , 0.0564 min −1 , 0.0517 min −1 , and 0.2112 min −1 , respectively. It was also revealed that the use of 2 beads of Cu@Alg/BP increased the rate constant to 0.2702 min −1 .

Reduction of K 3 [Fe(CN) 6 ]
The catalytic reduction reaction of K 3 [Fe(CN) 6 ] as an inorganic pollutant was also studied using the prepared nanocatalysts (MNPs@Alg/BP). UV-vis absorption spectroscopy was effectively applied to monitor the kinetic reduction of this inorganic pollutant. First of all, a mixture of K 3 [Fe(CN) 6 ] and NaBH 4 was treated with 10 mg of Cu@Alg/BP (2 beads). The absorbance band at 415 nm gradually disappeared in 11.0 min due to the reduction of [Fe(CN) 6 ] 3− to [Fe(CN) 6 ] 4− (Fe 3+ was reduced to Fe 2+ ), as illustrated in Figure 4d. The catalytic reduction of this inorganic pollutant mainly relies on the process of the electron transfer. The reduction efficiency of Fe 3+ to Fe 2+ was evaluated by applying Equation (1). The results showed that 95.99% of the pollutant was removed whereas the K app reached to 0.2472 min −1 (Figure 4e,f). This means that a successful conversion of K 3 [Fe(CN) 6 ] was achieved by utilizing Cu@Alg/BP as an effective catalyst in presence of NaBH 4 .
According to the literature, this catalytic reduction process occurs in two steps. The polarization of the nanocomposite beads is involved in the first rapid step using NaBH 4 (the reducing agent). In the following step, the excess surface electrons are transported to the contaminant of interest leading to formation of [Fe(CN) 6 ] 4− . Consequently, the reduction reaction is an electron-transfer process, as shown in the equation below:

Catalytic Reduction of Organic Dyes Discoloration of CR Dye
Congo red dye is a benzidine-based anionic azo dye, known as [1-naphthalenesulfonic acid, 3,30-(4,40-biphenylenebi-s(azo)) bis(4-amino-) disodium salt], containing two azo groups in its chemical structure. This organic environmental toxicant is a carcinogenic dye that harmfully affects ecosystems. According to the literature, this dye is commonly applied to study the catalytic performance of several catalysts due to their dissociation in the presence of both catalyst and reducing agent. Similar to K 3 [Fe(CN) 6 ], UV-vis spectroscopy was used to monitor the catalytic reduction of CR (0.065 mM) utilizing Cu@Alg/BP (2 beads) in the presence of NaBH 4 in order to evaluate the effectiveness of the prepared nanocatalysts. After addition of 10 mg of catalyst, the reduction process of 4-NP by the reducing agent was constantly evaluated using UV-visible spectroscopy where the changes in 4-NP concentration against time was recorded. A darker yellow color was observed when NaBH4 was added to the reduction reaction of 4-NP, which is naturally bright yellow,  According to the literature, this catalytic reduction process occurs in two steps. The polarization of the nanocomposite beads is involved in the first rapid step using NaBH4 (the reducing agent). In the following step, the excess surface electrons are transported to the contaminant of interest leading to formation of [Fe(CN) 6 ] 4− . Consequently, the reduction reaction is an electron-transfer process, as shown in the equation below:  As the results revealed, the catalytic reduction of CR occurred in 12.0 min. The absorption band of this dye at 490 nm progressively disappeared. Meanwhile, a new absorbance peak at 290 nm appeared due to the complete catalytic reduction of CR by Cu@Alg/BP in the presence of the reducing agent. It has been reported that the azo (-N=N-) group in CR is reduced when the electrons from the reducing agent (BH 4 -) are moved to the nanocomposite beads before they are transferred to the dye (CR). In fact, the azo (-N=N-) double bond is catalytically reduced to a (-N-N-) single bond causing the disappearance of CR's color. As previously mentioned, the conversion (%) was evaluated by applying Equation (1). The result showed that 97.61% of CR was reduced in 12.0 min by adding Cu@Alg/BP in presence of NaBH 4 as revealed in Figure 4a,e. Based on Equation (2), the rate constant for CR reduction using Cu@Alg/BP (2 beads) was found to be 0.3184 min −1 (Figure 4f).

Discoloration of MO Dye
Similar to CR, MO is an organic pollutant that causes harmful impacts on aquatic life. The catalytic activity of Cu@Alg/BP (2 beads) in presence of NaBH 4 was evaluated for a MO reduction using UV-vis spectroscopy. A new absorption peak at 250 nm appeared in 11.0 min while the first band at 460 nm gradually disappeared with the MO color confirming the completion of the catalyzed reduction of MO, as shown in Figure 4b. Similar to the CR reduction mechanism, the azo group (-N=N-) in MO is reduced to (-N-N-) when the electrons are transferred from the donor (BH 4 -) to the acceptor (MO) after their transmission to the catalyst (nanocomposite beads).
The conversion (%) and rate constant of MO reduction reaction by the nanocatalysts were also evaluated by applying Equations (1) and (2), respectively. The results showed that 98.48% of MO was reduced in 11.0 min by adding Cu@Alg/BP in presence of NaBH 4 , while the rate constant was 0.3975 min −1 , as shown in Figure 4b-f.

Discoloration of MB Dye
Similar to other previous dyes, the same experiment was carried out to study the catalyzed reduction of MB by adding Cu@Alg/BP (2 beads) in the presence of NaBH 4 . As previously discussed, UV-vis spectroscopy was used to investigate the reduction reaction of MB in terms of the rate of reduction reaction and the effectiveness of the catalyst. The results proved that the completion of the reaction occurred in 10.0 min when the absorption band of MB at 658 nm completely disappeared. On the other hand, a new band at 240 nm appeared because of the reduction of MB, as clearly seen in Figure 4c. By applying Equations (1) and (2), the conversion % of MB was 96.58% in a shorter period of time and it had a high reaction rate up to 0.3574 min −1 , as displayed in Figure 4e,f.

Possible Mechanism of Dyes Reduction
As previously discussed, the mechanism of the catalytic reduction of azo dyes (MO, CR, and MB) is based primarily on nanocomposite beads. At the beginning, the reducing agent (NaBH 4 ) decomposes into an aqueous solution forming BH 4 -, which is considered a proton source. In the next step, the hydrogen produced from BH 4 attacks the dye's molecules. Dye molecules then bind with MNPs@Alg/BP causing activation of azo bonds in dyes by the electrons carried by the nanocomposite beads. As a result of the bond conjugation, the azo bonds become weaker and then are broken down [25]. Double bond (-N=N-) is initially changed to single bond (-HN-NH-) which is then broken to form aromatic amines. Accordingly, the color of dyes disappear indicating the completion of the catalytic reduction. In other words, the catalyst works as an electron transferring material since it transfers the electron to the dye molecules (acceptor) from BH 4 -(donor) resulting in an acceleration of the reduction reaction.

Catalytic Reduction of MO
As previously described, MO was chosen as a model for further investigations because its catalytic reduction took place in a shorter time (11.0 min) and showed the highest removal % (98.48%) by adding Cu@Alg/BP (2 beads) in the presence of NaBH 4 . Accordingly, the impact of various parameters on the catalytic reduction reaction of pollutants by MNPs@Alg/BP with the reducing agent (NaBH 4 ) was further studied. The performance of the prepared Cu@Alg/BP was also compared with other catalysts reported in the literature for catalyzed reduction of MO in the presence of NaBH 4 , as revealed in Table 1 [25][26][27][28][29][30].

Effect of Different MNPs@Alg/BP on MO Reduction
In order to examine the influence of using different metal nanoparticles with Alg/BP (2 beads) on the catalytic reduction of MO by NaBH 4 , Co@Alg/BP and Fe@Alg/BP were selected to be added to the reaction. As previously discussed, Co and Fe showed relatively poor removal % (61.79% and 58.36%), respectively, when they were incorporated in the catalyst for the reduction of 4-NP, as illustrated in Figure 3c,d. Similarly, the reduction of MO in terms of the rate of reduction reaction and the effectiveness of the catalyst were investigated by employing UV-vis spectroscopy. The findings confirmed that the completion of MO reduction occurred in 12.0 min for both with different removal %. By applying Equation (1), the conversion % of MO by adding Fe@Alg/BP was 64.15% in 12.0 min whereas only 5.16% was achieved for the same duration of time when Co@Alg/BP was used, as shown in Figure 5a,b. On the other hand, superior removal % (98.48%) was achieved in 11.0 min when Cu@Alg/BP was added to the MO reduction reaction, as mentioned above and is shown in Figure 5c,d. To summarize, it was confirmed by the results that Cu@Alg/BP is the most effective nanocatalyst in terms of proficiency and the reaction rate of MO reduction.

Effect of Catalyst Amount on MO Reduction
In order to examine the impact of quantity of Cu@Alg/BP on MO reduction, three amounts of catalyst (1, 2 and 3 beads) were used. The other parameters were kept unchanged to investigate only the effect of the catalyst dosage on the reaction. Similarly, the

Effect of Catalyst Amount on MO Reduction
In order to examine the impact of quantity of Cu@Alg/BP on MO reduction, three amounts of catalyst (1, 2 and 3 beads) were used. The other parameters were kept unchanged to investigate only the effect of the catalyst dosage on the reaction. Similarly, the reduction of MO was examined using UV-vis spectroscopy in terms of the rate of reduction reaction and the effectiveness of the catalyst. The results demonstrated that removal % of MO remained unchanged by altering the catalyst dosage. In contrast, the reaction rate of MO reduction was slightly influenced. There is inverse proportion between the reaction rate and the catalyst amount. The reduction of MO took place in 13.0 min when the smallest amount of catalyst (1 bead) was used with the reducing agent, as shown in Figure 6a. On the other hand, it needed 9.0 min to reach the completion when the greatest quantity of catalyst (3 beads) was added, as illustrated in Figure 6c. As previously mentioned, the reduction finished in 11.0 min if 2 beads of catalyst were used, as seen in Figure 6b. In parallel to the above results, 4-NP was also reduced by NaBH 4 in the presence of 1 bead and 2 beads of Cu@Alg/BP and similar results were obtained for reaction rate and time duration. The reaction took a shorter time (12.0 min) in the presence of 1 bead of catalyst and a longer time (15.0 min) with 2 beads. In conclusion, the rate of catalytic reaction of dye is inversely proportional with the amount of catalyst used to accelerate it in the presence of NaBH 4 , as clearly illustrated in Figure 6d.

Effect of MO Concentration on Reduction Reaction Rate
Two different MO concentrations (0.108 and 0.093 mM) were used to study the impact of MO concentration on the duration of time the reduction reaction takes to finish in the presence of NaBH 4 and Cu@Alg/BP (3 beads). The amount of catalyst was selected to be 3 beads since it previously gave the shortest time for reaction completion as mentioned above. The other reaction parameters were kept unchanged in order to study the effect of MO concentration on the rate of its reduction. Similarly, UV-vis spectroscopy was used to monitor the reduction of the two MO concentrations. It was confirmed by obtained data that the rate of the reduction reaction was noticeably increased by approximately 33% with a lower concentration (0.093 mM), as shown in Figure 7a,b. The reduction finished in 9.0 min when 0.108 mM of MO was added in presence of NaBH 4 and the nanocatalyst, while it took only 3.0 min with a more diluted MO (0.093 mM) under the same reaction conditions. On contrary, the removal % of MO was approximately the same in both cases; however, the dye was reduced slightly more when a greater concentration of MO was used, as shown in Figure 7c. In conclusion, the concentration of MO is directly proportional to the duration of time it takes the catalytic reduction reaction to finish and has a slight positive impact on the conversion %.

Effect of NaBH 4 Concentration on MO Reduction
Similarly, different concentrations of reducing agent (NaBH 4 ) (0.5, 1.0, and 1.5 mL) were used to study the impact of the concentration of NaBH 4 on the reduction of MO by adding 3 beads of Cu@Alg/BP. The amount was selected to be 3 beads since it increased the reduction rate as previously confirmed. The other reaction parameters were kept unchanged in order to study the influence of NaBH 4 amount on the catalyzed reduction of MO. Similar to previous experiments, UV-Vis spectroscopy was used to monitor the reduction of MO by adding 3 different concentrations of NaBH 4 . The results showed that the removal % of MO was unaffected by changing the concentration of the reducing agent, as obviously noted in Figure 8d. In contrast, the reduction rate was remarkably influenced by altering the concentration. The reduction of the dye was faster by increasing the concentration of NaBH 4 , as shown in Figure 8a-c. In other words, the amount of reducing agent positively influences the catalytic reduction of MO. The reduction occurred in only 3.0 min when 1.5 mL of reducing agent was added. Smaller quantities (0.5 and 1.0 mL) of NaBH 4 influenced the duration of the time the reduction takes to 9 and 5.0 min, respectively. Accordingly, the reduction rate of MO is directly proportional with the concentration of the reducing agent. As mentioned earlier, the electrons are transferred from the donor (reducing agent) to the acceptor (dye) through the nanocatalyst. Therefore, when the concentration of a species that is rich in electrons is increased, it rapidly circulates in the reaction media resulting in fast electron transference to the dye by the nanocatalyst. Recyclability of Cu@Alg/BP Sufficient recovery and stability of any catalyst are vital due to its cost-value and eco-friendliness. Hence, the recyclability of Cu@Alg/BP (3 beads) used for MO catalytic reduction was investigated. The recovery of Cu@Alg/BP nanocatalyst was tested four times consecutively. After each test, the nanocatalyst beads were simply removed from the product and washed then with distilled water. The results proved the stability of the catalyst since it could be recycled several times with no impact on its catalytic performance. The time that MO catalytic reduction took in each cycle using Cu@Alg/BP nanocatalyst was evaluated, as shown in Figure 9. The results demonstrated that Cu@Alg/BP nanocatalyst could reduce MO in 12.0 min until the 5th cycle confirming its stability and recyclability. These findings suggest that Cu@Alg/BP nanocatalysts can be used for several cycles with no significant impact on catalytic activity.

Application to Real Samples
After optimization of the catalytic reduction process, three real samples were used, seawater, well water, and agricultural wastewater (FBR), to study the conversion % of the pollutant (MO) by adding Cu@Alg/BP (3 beads) with the use of NaBH 4 . Similar to the experiments described above, the catalytic reduction of MO was investigated using a UV-Vis spectrophotometer. All real sample solutions were prepared by adding 2 mL of MO solution to 1 mL of real sample. A total of 0.5 mL of NaBH 4 was then added to the solution in the UV cuvettes. Three beads of the nanocatalyst were added to each sample to accelerate the reduction of MO. In order to examine the removal % of MO in all water samples, the absorbance of the solution containing only MO with the water sample was measured. NaBH 4 was then added to the solution and the absorbance was measured again. Finally, Cu@Alg/BP (3 beads) was added to the previous solution in order to accelerate the reduction of MO. The contact time was set to 8.0 min for all water samples. The results showed that the % reduction of MO was significantly different in case of FBR sample compared with the other two samples. It was 59.81% in FBR which is much lower than the other two samples, which achieved more than 90%, as illustrated in Figure 10. Indeed, MO was effectively removed by 96.77% and 93.62% in well water and seawater samples, respectively, as shown in Figure 10b,c. In other words, the pollutant (MO) in the sample of well water was mostly converted to a safer product causing the disappearance of its absorption peak at 460 nm. Noticeably, this excellent result, achieved in 8.0 min, is in agreement with the result obtained previously (9.0 min) for MO reduction when 0.5 mL of NaBH 4 and 3 beads of Cu@Alg/BP were added, as shown above in Figure 8a. In contrast, MO was partially removed from the FBR water sample and its absorbance band at 460 nm did not disappear completely, as revealed in Figure 10a. The seawater sample showed excellent removal of MO; however, it is slightly lower than the well water sample, which has less interferences. Overall, the catalytic reduction of MO in well-and seawater samples by adding Cu@Alg/BP is a successful, robust, and feasible technique that can be used to remove pollutant (MO).

Recyclability of Cu@Alg/BP
Sufficient recovery and stability of any catalyst are vital due to its cost-val friendliness. Hence, the recyclability of Cu@Alg/BP (3 beads) used for MO cata tion was investigated. The recovery of Cu@Alg/BP nanocatalyst was tested fou secutively. After each test, the nanocatalyst beads were simply removed from t and washed then with distilled water. The results proved the stability of the ca it could be recycled several times with no impact on its catalytic performanc that MO catalytic reduction took in each cycle using Cu@Alg/BP nanocatalyst ated, as shown in Figure 9. The results demonstrated that Cu@Alg/BP nanocat

Application to Real Samples
After optimization of the catalytic reduction process, three real samples we seawater, well water, and agricultural wastewater (FBR), to study the conversion pollutant (MO) by adding Cu@Alg/BP (3 beads) with the use of NaBH4. Simila removal of MO; however, it is slightly lower than the well water sample, which has less interferences. Overall, the catalytic reduction of MO in well-and seawater samples by adding Cu@Alg/BP is a successful, robust, and feasible technique that can be used to remove pollutant (MO).

Conclusions
This study depicted the catalytic reduction of many different environmental pollutants, K 3 [Fe(CN) 6 ], 4-NP and three different dyes (MO, CR and MB), based on MNPs@Alg/BP catalysts in presence of NaBH4. This effective alginate/banana waste-based composite was successfully prepared using a robust and feasible eco-friendly method. Banana peels were efficiently converted into a useful material that could be later employed for remedying water from organic and inorganic pollutants. It was found that among many different nanocatalysts, Cu@Alg/BP was the most effective catalyst in terms of efficiency, reduction rate, and removal % of the pollutants (4-NP and MO). As data revealed, the rate of catalytic reduction (MO) is inversely proportional with the amount of catalyst

Conclusions
This study depicted the catalytic reduction of many different environmental pollutants, K 3 [Fe(CN) 6 ], 4-NP and three different dyes (MO, CR and MB), based on MNPs@Alg/BP catalysts in presence of NaBH 4 . This effective alginate/banana waste-based composite was successfully prepared using a robust and feasible eco-friendly method. Banana peels were efficiently converted into a useful material that could be later employed for remedying water from organic and inorganic pollutants. It was found that among many different nanocatalysts, Cu@Alg/BP was the most effective catalyst in terms of efficiency, reduction rate, and removal % of the pollutants (4-NP and MO). As data revealed, the rate of catalytic reduction (MO) is inversely proportional with the amount of catalyst used for enhancement and no impact of this catalyst dosage on removal % of pollutant (MO). It was also confirmed that the concentration of the toxicant (MO) is directly proportional to the time duration the catalytic reduction takes to finish and has a slight positive influence on the conversion % of pollutant. In addition, the results proved that the removal % of toxicant (MO) is unaffected by changing the concentration of the reducing agent whereas the reduction rate is directly proportional with NaBH4 concentration. Real sample analyses confirmed the efficacy of MNPs@Alg/BP for the removal of water contaminants. It can be concluded that a new effective strategy for the removal of inorganic and organic water contaminants was successfully created to be used as an alternative to high-cost commercial catalysts.