Amphiphilic Nucleobase-Containing Polypeptide Copolymers—Synthesis and Self-Assembly

Nucleobase-containing polymers are an emerging class of building blocks for the self-assembly of nanoobjects with promising applications in nanomedicine and biology. Here we present a macromolecular engineering approach to design nucleobase-containing polypeptide polymers incorporating thymine that further self-assemble in nanomaterials. Diblock and triblock copolypeptide polymers were prepared using sequential ring-opening polymerization of γ-Benzyl-l-glutamate N-carboxyanhydride (BLG-NCA) and γ-Propargyl-l-glutamate N-carboxyanhydride (PLG-NCA), followed by an efficient copper(I)-catalyzed azide alkyne cycloaddition (CuAAc) functionalization with thymidine monophosphate. Resulting amphiphilic copolymers were able to spontaneously form nanoobjects in aqueous solutions avoiding a pre-solubilization step with an organic solvent. Upon self-assembly, light scattering measurements and transmission electron microscopy (TEM) revealed the impact of the architecture (diblock versus triblock) on the morphology of the resulted nanoassemblies. Interestingly, the nucleobase-containing nanoobjects displayed free thymine units in the shell that were found available for further DNA-binding.


Introduction
Amphiphilic block copolymers are known to self-assemble in aqueous solutions into a wide range of nanostructures including worm-like or spherical micelles and vesicles [1][2][3]. In this field, polypeptide-based copolymers show considerable promise as building blocks to design bioinspired nanomaterials interfacing living systems [4,5]. Compared to other synthetic copolymers, those made of amino acids may offer several attractive features, including (1) adoption of ordered secondary conformations (α-helices, β-sheets . . . ) as in natural proteins; (2) improvement of chemical and enzymatic degradability in a biological medium; and (3) providing tailorable and metabolizable building units/blocks [6,7]. In addition, the supramolecular organization of polypeptide offers a unique opportunity to produce multivalent structures and can also be used to promote selective interactions with biological targets [8][9][10].
Varying the secondary structure of polypeptides is a unique chemical leverage in polymer science [6,11]. When secondary structure is included in amphiphilic macromolecular design, the polypeptide segment often provides rigidity and promotes the formation of lamellar structures [12]. For instance, amphiphilic polypeptides with α-helical "rod" hydrophobic block have been extensively used to prepare vesicles [13,14]. In this direction, poly(γ-benzyl-l-glutamate) (PBLG) has a strong The reported chemical shifts are relative to CDCl 3 , DMF-d 7 or D 2 O. Infrared spectroscopy was monitored on a Bruker Tensor 27 spectrometer using the attenuated total reflection (ATR) method. Polymer molar masses were determined by size-exclusion chromatography (SEC) using DMF/LiBr (1 g/L) as the eluent at 55 • C. Measurements were performed on an Ultimate 3000 system from ThermoScientific equipped with diode array detector (DAD). The system also includes a multi-angles light scattering detector MALS and differential refractive index detector dRI from Wyatt technology. Polymers (5 mg/mL) were separated on three Shodex Asahipack gel columns [GF-1G 7B (7.5 × 8 mm), GF 310 (7.5 × 300 mm), GF510 (7.5 × 300), exclusion limits from 500-300,000 Da] at a flowrate of 0.5 mL/min. Easivial kit of Polystyrene from Agilent was used as a standard (M n from 162 to 364,000 Da). Transmission Electron Microscopy (TEM) images were recorded on a JEOL USA Transmission Electron Microscopes working at 100 kV. Samples were prepared by spraying a 1 g/L solution of the block copolymer onto a copper grid (200 mesh coated with carbon) using a homemade spray tool and negatively stained with 1.2% uranyl acetate aqueous solution.
Light Scattering measurements were performed using an ALV/CGS-3 compact goniometer system, equipped with an ALV-7004 multiple tau digital correlator and a vertically-polarized He-Ne laser of 22 mW output power operating at wavelength λ = 632.8 nm at 20 • C. Scattered light was detected at scattering angles 20 • ≤ θ ≤ 150 • corresponding to scattering vector regime 0.00459 nm −1 ≤ q ≤ 0.00255 nm −1 . Z-average hydrodynamic radius (R H ) was calculated using the Stokes-Einstein equation (Equation (1)), where D 0 is the coefficient diffusion of the nanoobjects determined from the slope of the q 2 dependence of relaxation rate (<Γ> = Dq 2 ), k B is the Boltzmann constant, T is the absolute temperature and η s is the viscosity of the solvent (water). The Kc/R θ ratio was recorded in order to determine the radius of gyration (R g ) using the Guinier approximation (Equation (2)), where R θ is the average scattered intensity measured at angle θ, K is an optical constant, c is the concentration of the nanoobject dispersion and M W,NPs is the weight-average molar mass of the nanoobjects [23]. The R g is obtained from the slope of the straight line of the plot ln ( Kc R θ )vs q2 (where qR g < 1).

1)
Synthesis of γ-propargyl l-glutamate. l-glutamic acid (10 g, 68 mmol), propargyl alcohol (370 mL) and chlorotrimethylsilane (19 mL, 150 mmol) were stirred together at 0 • C (dropwise addition of the silane) for 1 h and then left stirring at room temperature (RT) for two days. Upon filtration, precipitation into diethyl ether twice to yield 9.98 g of a white solid (66%). 1  2) Synthesis of N-carboxyanhydride of γ-propargyl l-glutamate. γ-propargyl l-glutamate hydrochloride (5 g, 22.56 mmol) was stirred in THF at room temperature (RT). Careful addition of diphosgene (highly toxic, 3.11 g, 15.74 mmol) was performed and the reaction was left stirring for 2 h. The solvent was then fully removed and the solid residue washed many times with pentane. The NCA was ultimately dissolved in a minimal amount of dry CH 2 Cl 2 and passed through a column of dry silica gel [24] to afford a yellowish powder (4.7 g, 99%). 1  Synthesis of amphiphilic diblock nucleopolypeptides.
The N-carboxyanhydride (NCA) monomer of γ-benzyl-l-glutamate (2 g, 7.6 mmol) was dissolved in 10 mL of dry DMF in a Schlenk tube. A solution of hexylamine (50 µL, 0.38 mmol) in 2 mL dry DMF was added and the reaction was left to stir in a cold bath at 0 • C for 4 days under argon. After BLG-NCA had been completely consumed as monitored by FTIR (disappearance of the peaks at 1787 cm −1 and 1854 cm −1, see Figure S1) and NMR, an aliquot of the macroinitiator was taken (0.79 mL, 90 mg after Et 2 O precipitation) under argon, the left solution was used for synthesis of the diblock as described below. 1  2) Polymerization of γ-propargyl-l-glutamate from PBLG macroinitiator-Synthesis of poly(γ-benzyl-lglutamate-b-γ-propargyl-l-glutamate), PBLG-b-PPLG. A solution of PLG-NCA (1.83 g, 8.68 mmol) in DMF (3.9 mL) was added to the residual solution of PBLG macroinitiator and the reaction mixture was left stirring at RT for overnight. After full conversion (as monitored by FTIR following the disappearance of the peak at 1787 cm −1 , see Figure S1), the reaction mixture was precipitated into an excess of cold Et 2 O and recovered after centrifugation as a white solid (2.34 g, 79% yield). 1  . SEC then provided a number-average molecular weight M n of 5900 g/mol (calibration with polystyrene standards) and a low dispersity (Ð = 1.13).

1)
Synthesis of poly(γ-benzyl-l-glutamate), PBLG-ED-PBLG, difunctional macroinitiator initiated by ethylenediamine. The NCA monomer of γ-benzyl-l-glutamate (2 g, 7.6 mmol) was dissolved in 10 mL dry DMF in a Schlenk tube. A solution of ethylenediamine (12.7 µL, 0.19 mmol) in 2 mL dry DMF was added and the reaction was left to stir in a cold bath at 0 • C for 4 days under inert atmosphere. After BLG-NCA had been completely consumed as monitored by FTIR (disappearance of the peaks at 1787 cm −1 and 1854 cm −1 , see Figure S1) and NMR, an aliquot of the macroinitiator was taken (0.79 mL, 0.11 g after Et 2 O precipitation). 3 aliquots of 70 µL were used to follow the polymerization reaction by FTIR. The solution was used for synthesis of the triblock (cf. below). 1  . SEC then provided a number-average molecular weight Mn of 5000 g/mol (calibration with polystyrene standards) and a low dispersity (Ð = 1.08).
2) Polymerization of γ-propargyl-l-glutamate from PBLG-ED-PBLG macroinitiator-Synthesis of A solution of PLG-NCA (1.84 g, 8.7 mmol) in DMF (3.91 mL) was added to the residual solution of PBLG-ED-PBLG macroinitiator and the reaction mixture was left stirring at RT for another day. After full conversion (as monitored by FTIR following the disappearance of the peak at 1787 cm −1 , see Figure S1), the reaction mixture was precipitated into an excess of cold diethylether and recovered after centrifugation as a white solid (2.62 g, 88% yield). 1  3) Functionalization of PPLG-b-PBLG-b-PPLG with zidovudine using CuAAC reaction-Synthesis of amphiphilic triblock nucleopolypeptide.

Self-assembly of copolypeptides
Diblock and triblock copolypeptides were dispersed in water at 2.5 mg/mL to form nanoobjects using a direct dispersion method. Self-assembly was further probed by dynamic light scattering and uranyl acetate stained TEM. Overall, amphiphilic structures allowed the preparation of nano-assemblies having rather low size dispersity considering the direct hydration process and the use of polymeric materials.

DNA binding experiment
Upon self-assembly, the interaction of oligoDNA with nucleopolypeptide was evidenced by DNA binding experiments. (AAAAA) 4 oligoDNA (15 µM) was incubated with aqueous solutions of the amphiphilic copolymers (50 µg/mL) in milliQ water at RT. The solution was passed through a VIVASPIN centrifugal concentrator cartridge (MW cut-off 30 KDa) (from Fisher Scientific) until 5 times the volume was filtered out. The Oligo DNA retained was evaluated from UV analyses performed at 260 nm (UV absorbance of Adenine).

Results and Discussion
As simplified analogues of natural proteins, synthetic polypeptide polymers constitute important building blocks to develop highly functional materials. [25] Water-soluble polypeptides that adopt stable secondary structures are attractive because they pave the way to biomimetic structures that reproduce crucial features of natural peptides [22,26]. We recently developed thymidine-based nucleopolypeptides presenting stable β-sheets conformation in aqueous solution and exhibiting selective DNA-binding with simple sequences displaying adenine [21,22]. Herein, pursuing a macromolecular engineering design, we contemplated an introduction of such thymidine nucleobases onto multiblock polymeric backbone incorporating one clickable poly(γ-propargyl-l-glutamate) segment (Scheme 1).

Self-assembly of copolypeptides
Diblock and triblock copolypeptides were dispersed in water at 2.5 mg/mL to form nanoobjects using a direct dispersion method. Self-assembly was further probed by dynamic light scattering and uranyl acetate stained TEM. Overall, amphiphilic structures allowed the preparation of nano-assemblies having rather low size dispersity considering the direct hydration process and the use of polymeric materials.

DNA binding experiment
Upon self-assembly, the interaction of oligoDNA with nucleopolypeptide was evidenced by DNA binding experiments. (AAAAA)4 oligoDNA (15 µM) was incubated with aqueous solutions of the amphiphilic copolymers (50 µg/mL) in milliQ water at RT. The solution was passed through a VIVASPIN centrifugal concentrator cartridge (MW cut-off 30 KDa) (from Fisher Scientific) until 5 times the volume was filtered out. The Oligo DNA retained was evaluated from UV analyses performed at 260 nm (UV absorbance of Adenine).

Results and Discussion
As simplified analogues of natural proteins, synthetic polypeptide polymers constitute important building blocks to develop highly functional materials. [25] Water-soluble polypeptides that adopt stable secondary structures are attractive because they pave the way to biomimetic structures that reproduce crucial features of natural peptides. [22,26] We recently developed thymidine-based nucleopolypeptides presenting stable β-sheets conformation in aqueous solution and exhibiting selective DNA-binding with simple sequences displaying adenine. [21,22] Herein, pursuing a macromolecular engineering design, we contemplated an introduction of such thymidine nucleobases onto multiblock polymeric backbone incorporating one clickable poly(γ-propargyl-L-glutamate) segment (Scheme 1). The first step of our nucleopolypeptide design involved the synthesis of the polypeptide backbone [27,28]. Two copolymers with different architectures, diblock and triblock, were prepared in order to investigate the influence of the architecture on the morphology of nanoobjects formed by self-assembly in water. Both diblock and triblock copolymers, PBLG-b-PPLG and PPLG-b-PBLG-b-PPLG respectively, were achieved using a two-step ring-opening polymerization approach. First, macroinitiators were obtained by initiating the ring-opening polymerization of BLG-NCA in DMF at 0 °C, as a means to achieved controlled ROP with either hexylamine (PBLG) or The first step of our nucleopolypeptide design involved the synthesis of the polypeptide backbone [27,28]. Two copolymers with different architectures, diblock and triblock, were prepared in order to investigate the influence of the architecture on the morphology of nanoobjects formed by self-assembly in water. Both diblock and triblock copolymers, PBLG-b-PPLG and PPLG-b-PBLG-b-PPLG respectively, were achieved using a two-step ring-opening polymerization approach. First, macroinitiators were obtained by initiating the ring-opening polymerization of BLG-NCA in DMF at 0 • C, as a means to achieved controlled ROP with either hexylamine (PBLG) or ethylene diamine (PBLG-ED-PBLG) [29]. The polymerization reactions were monitored by FTIR following the disappearance of the BLG-NCA peaks (see Figure S1). As shown in Figure 1, upon purification, further analysis of these macroinitiators by 1 H NMR analysis allowed to deduce number-average degrees of polymerization (X n ) of 19 and 39 for PBLG and PBLG-ED-PBLG respectively.
Polymers 2020, 12, 1357 7 of 13 ethylene diamine (PBLG-ED-PBLG) [29]. The polymerization reactions were monitored by FTIR following the disappearance of the BLG-NCA peaks (see Figure S1). As shown in Figure 1, upon purification, further analysis of these macroinitiators by 1 H NMR analysis allowed to deduce number-average degrees of polymerization ( ) of 19 and 39 for PBLG and PBLG-ED-PBLG respectively. Multiblock copolymers were further obtained by ring-opening polymerization of γ-propargyl-L-glutamate NCA (PLG-NCA) from macroinitiators PBLG and PBLG-ED-PBLG using a PLG-NCA/macroinitiator ratio of 25:1 in DMF and at RT. It should be noted that, the synthesis of the monomer PLG-NCA was achieved according to our previous report. [21] The polymerizations were monitored by FTIR following the disappearance of the PLG NCA peaks. Upon purification, analysis of the block copolymers was analyzed by size exclusion chromatography in DMF and 1 H-NMR spectroscopy (Figures 2 and S2), to check the good agreement between the polymer compositions Multiblock copolymers were further obtained by ring-opening polymerization of γ-propargyl-l-glutamate NCA (PLG-NCA) from macroinitiators PBLG and PBLG-ED-PBLG using Polymers 2020, 12, 1357 8 of 13 a PLG-NCA/macroinitiator ratio of 25:1 in DMF and at RT. It should be noted that, the synthesis of the monomer PLG-NCA was achieved according to our previous report [21]. The polymerizations were monitored by FTIR following the disappearance of the PLG NCA peaks. Upon purification, analysis of the block copolymers was analyzed by size exclusion chromatography in DMF and 1 H-NMR spectroscopy (Figure 2 and Figure S2), to check the good agreement between the polymer compositions with the monomers feed ratio. As summarized in Table 1, PBLG-b-PPLG diblock and PPLG-b-PBLG-b-PPLG triblock copolypeptides exhibit low dispersities (Ð < 1.2) and weight average molar masses (Mn) of 5900 g/mol and 13,400 g/mol, respectively, close to those estimated from NMR analyses.
Polymers 2020, 12, 1357 8 of 13 with the monomers feed ratio. As summarized in Table 1, PBLG-b-PPLG diblock and PPLG-b-PBLG-b-PPLG triblock copolypeptides exhibit low dispersities (Ð < 1.2) and weight average molar masses ( ) of 5900 g/mol and 13,400 g/mol, respectively, close to those estimated from NMR analyses.  Table 1. Characteristics of the polypeptides obtained upon ROP (see Figure S2).    Figure S2). Functionalization of diblock and triblock copolypeptides with thymidine was achieved through CuAAC reaction in anhydrous and deoxygenated DMF using CuBr/PMDETA as catalytic system. Upon extensive purification by dialysis, the presence of the nucleobase in the final polymer structure was verified by 1 H NMR and 31 P NMR. As depicted in Figure 3, integration of the 1 H NMR signals indicated a quantitative coupling (integration of the signal a compared to the signal i). This was further confirmed by the complete disappearance of the 31 P NMR signal of the AZTP (Figure 3, right spectra) and of the N 3 stretching on IR analyses ( Figures S3 and S4). Functionalization of diblock and triblock copolypeptides with thymidine was achieved through CuAAC reaction in anhydrous and deoxygenated DMF using CuBr/PMDETA as catalytic system. Upon extensive purification by dialysis, the presence of the nucleobase in the final polymer structure was verified by 1 H NMR and 31 P NMR. As depicted in Figure 3, integration of the 1 H NMR signals indicated a quantitative coupling (integration of the signal a compared to the signal i). This was further confirmed by the complete disappearance of the 31 P NMR signal of the AZTP (Figure 3, right spectra) and of the N3 stretching on IR analyses ( Figures S3 and S4). Interestingly, both amphiphilic copolymers were spontaneously able to fully disperse in water, forming opalescent solutions, a qualitative indication for spontaneous self-assembly into nanoobjects. Indeed, thymidine-containing homopolypeptide have been showed to stabilize β-sheet structuring while keeping at the same time water solubility [22]. On another hand, it is well documented that poly(γ-benzyl-L-glutamate) block forms strong α-helices in aqueous solutions, a rod-like feature that was previously used to tune self-assembly in water with tree-like glycopolypeptides [16]. The presence of the secondary structures was confirmed by FTIR analyses ( Figure S3).

Polymer [M]/[I]
To better understand this self-assembly, diblock (PBLG-b-PPLGNu) and triblock Interestingly, both amphiphilic copolymers were spontaneously able to fully disperse in water, forming opalescent solutions, a qualitative indication for spontaneous self-assembly into nanoobjects. Indeed, thymidine-containing homopolypeptide have been showed to stabilize β-sheet structuring while keeping at the same time water solubility [22]. On another hand, it is well documented that poly(γ-benzyl-l-glutamate) block forms strong α-helices in aqueous solutions, a rod-like feature that was previously used to tune self-assembly in water with tree-like glycopolypeptides [16]. The presence of the secondary structures was confirmed by FTIR analyses (Figure S3).
To better understand this self-assembly, diblock (PBLG-b-PPLGNu) and triblock (PPLGNu-b-PBLG-b-PPLGNu) copolypeptides were directly solubilized in milliQ water at 2.5 mg/mL. The resulting nanoobject obtained were characterized by light scattering (LS) and transmission electron microscopy (TEM) without further purification. As shown in Figure 4, diblock copolypeptide self-assembled into nanoparticles with Z-average hydrodynamic radius (R H ) equal to 14 nm, which is characteristic for spherical micelles [30]. This observation was consistent with TEM analysis (Figure 4A), where very small spherical micelles were observed. In marked contrast to previous similar design involving PBLG for which vesicles were formed [15], this first result indicated that the rod-induced packing of the hydrophobic segment was strongly counterbalanced by the highly charged thymidinylated segments that introduced strong electrostatic repulsion of the corona and consequently an increase of the interfacial curvature. In the case of triblock copolypeptides, dynamic light scattering (DLS) analysis revealed the formation of larger nanoobjects with an averaged R H = 108 nm (see Figure 4B and Figure  S5). A Z-average radius of gyration (R g ) equal to 111 nm was determined by analyzing the static light scattering data using the Guinier plot method. A so-called ρ-ratio (ρ = R g /R H ), which is an important indication of the morphology of scattering nanoparticles, close to 1 (ρ = 1.02) was obtained, suggesting the formation of vesicular morphology with the triblock [15,31]. These findings agreed well with the TEM image, where spherical hollow nanoobjects were clearly observed ( Figure 4B and Figure S5). As compared to the diblock, the formation of vesicular structures with the triblock was assigned to the longer PBLG segments which was able to better stabilize a flat interface necessary for vesicle formation due to stronger rod-rod interaction between α-helices, that counter-balanced the electronic repulsion from the thymidinylated block. However, it is important to consider that the triblock could hypothetically be bent at the ethylene diamine further (1) inducing hydrophobic interaction between the two PBLG blocks, also (2) resulting in the possible formation of polymeric micelles with the cores of the bent PBLG blocks. This fact can partly explain the dispersity observed in Malvern analyses ( Figure 4) and multiangle analyses confirmed the presence of smaller spherical objects ( Figure S5). Overall, these results suggested a contradictory reciprocity between two phenomena-the alignment of the PBLG macrodipoles (the hydrophobic rod packing) and the negative charges repulsion of the ionic polypeptides. These two phenomena, in equilibrium, undoubtedly induced a form of dynamism in water that could explained the self-assembly observed upon direct solubilization in this solvent.
In a final step, to verify that the nucleobases present at the surface of the nanomaterials were available to mediate an efficient interaction with DNA, DNA binding assays with short single stranded oligoA DNA (20 mers) were performed. These assays involved mixing of the DNA solution (15 µM) with the two different self-assembled nanostructures (50 µg/mL) and check upon ultra-filtration the oligoA DNA retained (UV absorbance of adenine at 260 nm). As depicted on Figure 5, upon ultrafiltration using a MWCO of 30kDa, oligoA DNA was found retained with both nanomaterials. After centrifugation the eluted solution did not show any absorbance at 260 nm absorbance revealing that the oligoDNA stayed sequestered onto the microfilter upon association with the nanoassemblies (columns with (AAAAA) 4 and NP in Figure 5). The control containing oligoDNA alone, when passed through the same cartridge under the same conditions, was not retained by the cartridge (left column, Figure 5). Overall, these results demonstrated that the thymidine in the shell of the nanomaterials were available to mediate an efficient interaction with a short oligo A sequence. In previous work, no T m value was observed from hybridization experiments involving thymidinylated homopolypeptides [22]. Indeed, even if this interaction was previously found coarser than in regular base pairing occurring between two double stranded DNA, observing this same coarse interaction on the surface of nanoobjects opens up prospects for interesting surface functionalization or therapeutic targeting. resulting in the possible formation of polymeric micelles with the cores of the bent PBLG blocks. This fact can partly explain the dispersity observed in Malvern analyses ( Figure 4) and multiangle analyses confirmed the presence of smaller spherical objects ( Figure S5). Overall, these results suggested a contradictory reciprocity between two phenomena-the alignment of the PBLG macrodipoles (the hydrophobic rod packing) and the negative charges repulsion of the ionic polypeptides. These two phenomena, in equilibrium, undoubtedly induced a form of dynamism in water that could explained the self-assembly observed upon direct solubilization in this solvent.  In a final step, to verify that the nucleobases present at the surface of the nanomaterials were available to mediate an efficient interaction with DNA, DNA binding assays with short single stranded oligoA DNA (20 mers) were performed. These assays involved mixing of the DNA solution (15 µM) with the two different self-assembled nanostructures (50 µg/mL) and check upon ultra-filtration the oligoA DNA retained (UV absorbance of adenine at 260 nm). As depicted on Figure 5, upon ultrafiltration using a MWCO of 30kDa, oligoA DNA was found retained with both nanomaterials. After centrifugation the eluted solution did not show any absorbance at 260 nm absorbance revealing that the oligoDNA stayed sequestered onto the microfilter upon association with the nanoassemblies (columns with (AAAAA)4 and NP in Figure 5). The control containing oligoDNA alone, when passed through the same cartridge under the same conditions, was not retained by the cartridge (left column, Figure 5). Overall, these results demonstrated that the thymidine in the shell of the nanomaterials were available to mediate an efficient interaction with a short oligo A sequence. In previous work, no Tm value was observed from hybridization experiments involving thymidinylated homopolypeptides. [22] Indeed, even if this interaction was previously found coarser than in regular base pairing occurring between two double stranded DNA, observing this same coarse interaction on the surface of nanoobjects opens up prospects for interesting surface functionalization or therapeutic targeting.

Conclusions
In summary, we have presented a simple macromolecular design to prepare amphiphilic nucleobase-containing polypeptides fully based on amino acid and nucleotide building blocks. Using sequential and controlled NCA polymerization and efficient click thymidinylation afforded unconventional amphiphilic architecture in which hydrophilic blocks structured in β-sheets are associated to a hydrophobic block structured in alpha helix. By varying the macromolecular engineering (diblock versus triblock), the morphology of the corresponding nanostructures was changed and afforded nanomaterials able to efficiently interact with oligo DNA sequences. From a

Conclusions
In summary, we have presented a simple macromolecular design to prepare amphiphilic nucleobase-containing polypeptides fully based on amino acid and nucleotide building blocks.
Using sequential and controlled NCA polymerization and efficient click thymidinylation afforded unconventional amphiphilic architecture in which hydrophilic blocks structured in β-sheets are associated to a hydrophobic block structured in alpha helix. By varying the macromolecular engineering (diblock versus triblock), the morphology of the corresponding nanostructures was changed and afforded nanomaterials able to efficiently interact with oligo DNA sequences. From a materials perspective, the excellent control both in structure and in function drawn by our polymeric design hold promises to develop nanosized drug carriers for drug delivery systems targeting oligoA DNA sequences.
Supplementary Materials: Supplementary Materials (ESI) are available online at http://www.mdpi.com/2073-4360/ 12/6/1357/s1, Figure S1: The ring-opening polymerizations were monitored by FTIR following the disappearance of the NCA peaks in DMF (ON: overnight), Figure S2: Characterizations of the polypeptides backbones before click by SEC analysis in DMF (1% LiBr). RI detection (flow marker: toluene), Figure S3: FTIR spectra of PBLG-b-PPLGNu (powder). Comparing this spectrum to FTIR spectroscopy analysis of AZTP clearly indicates that azide peak disappeared, Figure S4: FTIR spectra of PPLGNu-b-PBLG-b-PPLGNu (powder). Comparing this spectrum to FTIR spectroscopy analysis of AZTP clearly indicates that azide peak disappeared, Figure S5: Vesicles based on PPLGNu-b-PBLG-b-PPLGNu triblock copolypeptide: left) Multi-angle light scattering experiments performed to calculate the ρ-ratio. At high angles, another population of small spherical objects are observed; right) Different TEM imaging evidencing the hollow structure of the nanoobjects.