Design of pH Responsive Textile as a Sensor Material for Acid Rain

The chemical composition of rainwater can serve as an indicator of the excess of acidifying air pollutants. The pH value of rainwater in the presence of sulphur dioxide and nitrogen oxides, the precursors of acid rain, falls below pH 5.6, which is the limit value for acid rain. In this research, the tailoring of halochromic textile was examined for the design of a functional textile that can serve as a sensor and inform the wearer about the presence of pollutants in the air by means of an immediate colour change. For this purpose, a polyamide 6 fabric was dyed with the pH-sensitive Bromocresol green dye, which causes a colour change below pH 3.6 (yellow) and above pH 5.4 (blue). In addition, the dyed polyamide 6 fabric was treated with a water and oil repellent finish. Colour and colour change before and after immersion of unfinished and finished dyed samples in buffer solutions with different pH values were evaluated spectrophotometrically using the CIELAB colour space. The colour fastness to rubbing, washing, and light, and the water and oil repellency of the dyed fabrics were determined according to valid SIST EN ISO standards. The results showed that the unfinished dyed polyamide 6 fabric undergoes a reversible colour change faster and more clearly than the finished dyed polyamide 6 fabric. The dyed polyamide 6 fabric had good colour fastness to rubbing and domestic and commercial laundering, while the colour fastness to light was poor. In addition, the dyed polyamide 6 fabric was pH-sensitive, despite dye degradation under xenon light, regardless of whether it was finished.


Introduction
During the second half of the previous century, gradual but major changes in rainwater and groundwater quality occurred as a result of an excess of environmentally harmful atmospheric emissions associated with rainwater acidification. After extensive and comprehensive studies to gain a substantial understanding of how acid deposition alters ecosystems, it was found that air pollution is closely related to rainwater quality. The pH of rainwater drops and becomes more acidic due to atmospheric emissions of air pollutants, almost exclusively caused by destructive human activities, in particular the burning of fossil fuels, industrial and agricultural activities, and car exhaust fumes. The phenomenon of wet deposition with high concentrations of sulphur dioxide and nitrogen oxides has been defined as acid rain [1][2][3]. Rain is categorised as acid rain when its pH is 5.6 or below. The acid rain phenomenon remains topical, despite extensive research and continuous monitoring of acid deposition and air pollution being carried out for at least half a century, following several cross-border agreements, protocols, and policies [1]. Although emissions have decreased significantly in Western European countries, North America, and some others, Southwest China and Southeast Asia countries are among the worst affected areas [2].

Dye
BCG dye, as a pH-sensitive triphenylmethane dye with molecular weight of 698.01 g/mol (Honeywell Fluka, Charlotte, NC, USA), was used in the research. The molecular formula of the dye is presented in Figure 1.

Dye
BCG dye, as a pH-sensitive triphenylmethane dye with molecular weight of 698.01 g/mol (Honeywell Fluka, Charlotte, NC, USA), was used in the research. The molecular formula of the dye is presented in Figure 1.

Auxiliaries
Levelling agent Sarabid C14 (CHT, Montlingen, Switzerland), a synergistic mixture of anionic and non-ionic components, and Meropan EF 150 (CHT, Montlingen, Switzerland), an ester of carboxylic acid which ensures optimal pH condition of the dyebath during the dyeing process, were used for dyeing.

Finishing Agent
Water-and oil-repellency of PA6 fabric was obtained using Dynasylan F 8815 (Evonik Resource Efficiency, Bitterfeld-Wolfen, Germany), which is a fluoroalkyl-functional water-borne oligosiloxane that acts as a surface modification agent on fibre substrates.

Dyeing
Before the dyeing procedure, the PA6 fabric was washed in distilled water at 40 °C for 30 min. Dyeing of PA6 fabric mass of 5 g and 50:1 liquor-to-goods ratio was performed in a Starlet 2 (Daelim Starlet, Shiheung, Korea) apparatus using the conventional exhaust dyeing method according to the diagram shown in Figure 2.

Auxiliaries
Levelling agent Sarabid C14 (CHT, Montlingen, Switzerland), a synergistic mixture of anionic and non-ionic components, and Meropan EF 150 (CHT, Montlingen, Switzerland), an ester of carboxylic acid which ensures optimal pH condition of the dyebath during the dyeing process, were used for dyeing.

Finishing Agent
Water-and oil-repellency of PA6 fabric was obtained using Dynasylan F 8815 (Evonik Resource Efficiency, Bitterfeld-Wolfen, Germany), which is a fluoroalkyl-functional water-borne oligosiloxane that acts as a surface modification agent on fibre substrates.

Dyeing
Before the dyeing procedure, the PA6 fabric was washed in distilled water at 40 • C for 30 min. Dyeing of PA6 fabric mass of 5 g and 50:1 liquor-to-goods ratio was performed in a Starlet 2 (Daelim Starlet, Shiheung, Korea) apparatus using the conventional exhaust dyeing method according to the diagram shown in Figure 2.

Dye
BCG dye, as a pH-sensitive triphenylmethane dye with molecular weight of 698.01 g/mol (Honeywell Fluka, Charlotte, NC, USA), was used in the research. The molecular formula of the dye is presented in Figure 1.

Auxiliaries
Levelling agent Sarabid C14 (CHT, Montlingen, Switzerland), a synergistic mixture of anionic and non-ionic components, and Meropan EF 150 (CHT, Montlingen, Switzerland), an ester of carboxylic acid which ensures optimal pH condition of the dyebath during the dyeing process, were used for dyeing.

Finishing Agent
Water-and oil-repellency of PA6 fabric was obtained using Dynasylan F 8815 (Evonik Resource Efficiency, Bitterfeld-Wolfen, Germany), which is a fluoroalkyl-functional water-borne oligosiloxane that acts as a surface modification agent on fibre substrates.

Dyeing
Before the dyeing procedure, the PA6 fabric was washed in distilled water at 40 °C for 30 min. Dyeing of PA6 fabric mass of 5 g and 50:1 liquor-to-goods ratio was performed in a Starlet 2 (Daelim Starlet, Shiheung, Korea) apparatus using the conventional exhaust dyeing method according to the diagram shown in Figure 2. Three different concentrations of dye, namely 0.1, 0.2, and 0.5% on mass fabric (o.m.f.) were used. Since the dye is very poorly soluble in water, 96% solution of ethanol was used for dissolving the dye prior dyeing. A quantity of 1% of levelling agent Sarabid C14 (CHT, Montlingen, Switzerland) and 0.5 mL/L of buffer system Meropan EF 150 (CHT Montlingen, Switzerland) held constant, irrespective of the dye concentration used in the dyebath. After dyeing, the dyed PA6 samples were rinsed twice in distilled water at a temperature of 25 • C. After rinsing, samples were left to dry in open air at a room temperature of 23 • C.

Finishing
The water and oil repellent finishing of the polyamide fabric was performed with a pad-dry-cure process. Dyed PA6 fabric was immersed in a padding bath containing 10% solution of Dynasylan F 8815 (Evonik Resource Efficiency, Bitterfeld-Wolfen, Germany) for 5 min in order to obtain good wetting. The pH value of the padding bath was adjusted to pH 4.5 with CH 3 COOH 30%. Then, padding samples were dried for 2 min at 100 • C and cured for 4 min at 150 • C.

Spectrophotometric Measurements
The colour of undyed, unfinished, and finished dyed samples was analysed using a Datacolor SF 600 PLUS-CT spectrophotometer (Lawrenceville, NJ, USA). CIELAB values and reflectance (R) were measured whilst K/S values were calculated. All measurements were performed using four layers of fabric with a 9 mm aperture, with specular reflectance included, under D65 illumination and with a 10 • standard observer. An average of ten measurements was taken for each sample. Additionally, the levelness of dyed samples was calculated by measuring K/S values of 20 random points on dyed fabric at the maximum absorption wavelength of the dye on dyed fabric (λ max = 630 nm) according to Equations (1) and (2) [24]: where σ(λ) is the standard deviation of each K/S value of random points with (K/S) λ , λ is the wavelength of dye maximum absorption, n is the number of random points tested, and (K/S) i , λ is the K/S value of each random point. The levelness increased with the decrease of the σ(λ) value.

Colour Fastness to Rubbing
The testing of the colour fastness of both unfinished and finished dyed samples to rubbing was performed on a Crockmeter M23888 (SDL ATLAS, Rock Hill, SC, USA) using the SIST EN ISO 105-X12:2002 standard. Colour fastness to rubbing was visually assessed using the grey scale.

Colour Fastness to Domestic and Commercial Laundering
The testing of the colour fastness of both unfinished and finished dyed samples to domestic and commercial laundering was performed in a GyroWash apparatus (James Heal, Halifax, UK) using the SIST EN ISO 105-C06:2012 standard. Two different test methods, A1S and A1M, were used. European Colourfastness Establishment (ECE) detergent without a fluorescent whitening agent was used as a washing agent. According to the standard, the results of one multiple (M) test may in some cases be approximated by the results of up to five domestic or commercial laundering cycles at a temperature not exceeding 70 • C. Thus, the A1M method was preformed twice, corresponding to 10 domestic

Colour Fastness to Light
The testing of the colour fastness of both untreated and treated dyed samples to xenon light was performed in a Xenotest alpha apparatus (Atlas, Rancho Cucamonga, CA, USA). Samples were prepared according to the SIST EN ISO 105-B02:2014 standard and subjected to testing.
Due to very weak fastness properties of the studied BCG dye to light, both unfinished and finished dyed samples were exposed to xenon light for 2, 4, 6, and 8 h in the Xenotest apparatus to study if the degradation of dye could influence the pH responsiveness of the dye. Therefore, the spectrophotometric measurements were performed before and after immersion of samples into buffer solutions of different pH values.

Determination of pH Responsiveness of Unfinished and Finished Dyed Fabric
To determine the pH responsiveness of unfinished and finished dyed fabric by change of colour, which was visually and spectrophotometrically detected, the unfinished dyed samples with dye concentrations of 0.1%, 0.2%, and 0.5% o.m.f., and the finished dyed sample, dyed with a dye concentration of 0.2% o.m.f., were immersed for 1 h in buffer solutions of different pH values ranging from pH 3 to 11 (pH 3, 4, 5, 6, 7, 9, and 11). After immersion, the samples were dried for 1 h at room temperature (23 • C) and spectrophotometric measurements were then taken. Additionally, the response time and spectral shifts of BCG dye in buffer solutions of different pH values was also determined. The absorption spectra of BCG in buffer solutions were recorded using UV-vis spectrophotometer Cary 1E (Varian, Australia), using a 1 cm quartz cell. Spectra were taken in the wavelength range from 400 to 700 nm.

Water and Oil Repellency
Concerning the surface wetting of the unfinished and finished dyed samples, the SIST EN ISO 4920:2012 standard was used to determine the water repellency. To examine the oil repellency of the unfinished and finished dyed samples, the SIST EN ISO 14419:2010 standard was used. The result of the oil repellency test was the highest number of a liquid hydrocarbon at which the wetting of tested fabric had not occurred within 30 s.

Spectrophotometric Measurements
From the CIELAB values, gathered in Table 1, the PA6 fabric become darker, greener, and bluer after dyeing. As expected, the dye concentration of 0.5% o.m.f., the sample became even less blue than the sample dyed with a dye concentration of 0.1% o.m.f., which was in contrast with our expectations. Finishing of the dyed sample with a waterand oil-repellent finish did not essentially change the colour of the sample. The dyed sample became slightly darker (CIE L* decrease), and the difference in CIE a* and CIE b* values of unfinished and finished dyed samples were in the area of experimental error. After immersion of dyed samples in different buffer solutions, the CIELAB values drastically changed at pH values of 3 and 4, while at pH values ranging from pH 5 to pH 11 only negligible changes in CIELAB values were noticed. This is expected because at pH 3 and 4 the change of colour occurs due to protonation of BCG. The dye transfers into monoanionic form (structure B in Figure 3) and the colour of the dye is yellow. Moreover, at higher pH (higher than pH 5) the dianionic form of dye (structure C, Figure 3) appears which is stabilised with resonance. The colour of the dye is blue. The mechanism is presented in Figure 3 [11].
Polymers 2020, 12, x FOR PEER REVIEW 7 of 16 and the colour of the dye is yellow. Moreover, at higher pH (higher than pH 5) the dianionic form of dye (structure C, Figure 3) appears which is stabilised with resonance. The colour of the dye is blue. The mechanism is presented in Figure 3 [11]. It can be seen from Table 1 that at pH 3 all of the samples, regardless of the dye concentration used, became drastically lighter (values of CIE L * are higher), less green (values of CIE a * increased and became positive), and more yellow (values of CIE b* increased and became positive). For the PA_DF sample, only a slight increase in the value of CIE L * was noticed. The sample became greener and less blue (both CIE values a* and b* were negative), which indicates that the finishing agent influences the pH responsiveness of the studied BCG dye on PA6 fabric. At pH 4 dyed samples became darker, greener, and less yellow as evident in the decrease of all CIELAB values, compared to samples before immersion into buffer solution. At pH 4 the PA_DF sample became lighter, greener, and less blue. At pH 5 the decrease of CIE L* was noticed for all dyed samples, irrespective of the dye concentration used in the research. Values of CIE a* were negative and increased, and values of CIE b* were negative and decreased. This means that at pH 5 samples became darker, less green, and bluer in contrast to samples at pH 4. Across the range between pH 6 to pH 11, as evident from the CIELAB values, the unfinished and finished dyed samples did not exhibit any notable colour change, compared to CIELAB values of dyed samples before immersion into buffer solution. The latter suggests that at a pH higher than 5 no change of colour occurred. Unfinished and finished dyed samples were green blue.
The levelness of dyeing was determined only for samples dyed with a dye concentration of 0.2%, where 20 random measurements of K/S values were taken, and the standard deviation (s) was determined. The K/S value was 10.93 and s was 0.65. From the obtained values it can be seen that the sample is not equally dyed. The reason for higher s values could lie in the creases that appeared during the dyeing process on the PA6 fabric. This can be noted in Figure 4. It can be seen from Table 1 that at pH 3 all of the samples, regardless of the dye concentration used, became drastically lighter (values of CIE L* are higher), less green (values of CIE a* increased and became positive), and more yellow (values of CIE b* increased and became positive). For the PA_DF sample, only a slight increase in the value of CIE L* was noticed. The sample became greener and less blue (both CIE values a* and b* were negative), which indicates that the finishing agent influences the pH responsiveness of the studied BCG dye on PA6 fabric. At pH 4 dyed samples became darker, greener, and less yellow as evident in the decrease of all CIELAB values, compared to samples before immersion into buffer solution. At pH 4 the PA_DF sample became lighter, greener, and less blue. At pH 5 the decrease of CIE L* was noticed for all dyed samples, irrespective of the dye concentration used in the research. Values of CIE a* were negative and increased, and values of CIE b* were negative and decreased. This means that at pH 5 samples became darker, less green, and bluer in contrast to samples at pH 4. Across the range between pH 6 to pH 11, as evident from the CIELAB values, the unfinished and finished dyed samples did not exhibit any notable colour change, compared to CIELAB values of dyed samples before immersion into buffer solution. The latter suggests that at a pH higher than 5 no change of colour occurred. Unfinished and finished dyed samples were green blue.
The levelness of dyeing was determined only for samples dyed with a dye concentration of 0.2%, where 20 random measurements of K/S values were taken, and the standard deviation (s) was determined. The K/S value was 10.93 and s was 0.65. From the obtained values it can be seen that the sample is not equally dyed. The reason for higher s values could lie in the creases that appeared during the dyeing process on the PA6 fabric. This can be noted in Figure 4.  Curves of K/S vs. λ in the studied wavelength range from 400 to 700 nm are presented in Figure 5, which shows that the colour strength (K/S) of dyed samples increased with the increase of the dye concentration. Curves of K/S vs. λ in the studied wavelength range from 400 to 700 nm are presented in Figure 5, which shows that the colour strength (K/S) of dyed samples increased with the increase of the dye concentration. Curves of K/S vs. λ in the studied wavelength range from 400 to 700 nm are presented in Figure 5, which shows that the colour strength (K/S) of dyed samples increased with the increase of the dye concentration.  (Figures 6 and 7). However, a greater decrease of K/S values was obtained for unfinished dyed samples in comparison to the finished dyed samples. These results suggest that the finishing influenced the ability of the PA6 fabric to respond to the change of pH. At pH 5 and above, values of K/S did not exhibit significant differences, meaning that the values of K/S of dyed samples were almost the same as before immersion in buffer solutions of pH 6, 7, 9, and 11.  (Figures 6 and 7). However, a greater decrease of K/S values was obtained for unfinished dyed samples in comparison to the finished dyed samples. These results suggest that the finishing influenced the ability of the PA6 fabric to respond to the change of pH. At pH 5 and above, values of K/S did not exhibit significant differences, meaning that the values of K/S of dyed samples were almost the same as before immersion in buffer solutions of pH 6, 7, 9, and 11.  The absorption spectra of BCG on PA6 fabric (Figure 6a) expressed as K/S values vs. λ, showed a significant hypsochromic shift of λmax from 630 to 440 nm when the fabric was immersed in buffer solutions of pH 3 and 4, while at other pH values no changes of spectra were noticed comparing to the dyed sample before immersion. For those spectra (pH 5-11) only a slight hyperchromic effect was noticed along the whole studied range of wavelengths in comparison with the dyed sample before immersion. In contrast to the unfinished dyed sample, the finished dyed sample showed only a hypochromic effect of λmax at 680 nm after immersion in buffer solutions of pH 3 and 4 (Figure 6b), meaning that the sample is less pH responsive and the change of colour is less obvious compared to the case of the unfinished dyed sample (Figure 6a). With the increase of dye concentration on PA6 fabric (Figure 6a and Figure 7a,b) the hyperchromic effect of λmax at 680 nm was noticed, which was expected due to higher adsorption of BCG dye. Moreover, at pH 3 and 4 a significant hypochromic effect occurred at λmax = 680 nm and, at the same time, the appearance of a new absorption peak at 440 nm was noticed. This suggests halochromic behaviour of BCG on PA6 fabric and change of colour from blue to yellow-green at pH 3 and 4. With the increase of dye concentration on PA6 fabric, the The absorption spectra of BCG on PA6 fabric (Figure 6a) expressed as K/S values vs. λ, showed a significant hypsochromic shift of λ max from 630 to 440 nm when the fabric was immersed in buffer solutions of pH 3 and 4, while at other pH values no changes of spectra were noticed comparing to the dyed sample before immersion. For those spectra (pH 5-11) only a slight hyperchromic effect was noticed along the whole studied range of wavelengths in comparison with the dyed sample before immersion. In contrast to the unfinished dyed sample, the finished dyed sample showed only a hypochromic effect of λ max at 680 nm after immersion in buffer solutions of pH 3 and 4 (Figure 6b), meaning that the sample is less pH responsive and the change of colour is less obvious compared to the case of the unfinished dyed sample (Figure 6a). With the increase of dye concentration on PA6 fabric (Figures 6a and 7a,b) the hyperchromic effect of λ max at 680 nm was noticed, which was expected due to higher adsorption of BCG dye. Moreover, at pH 3 and 4 a significant hypochromic effect occurred at λ max = 680 nm and, at the same time, the appearance of a new absorption peak at 440 nm was noticed. This suggests halochromic behaviour of BCG on PA6 fabric and change of colour from blue to yellow-green at pH 3 and 4. With the increase of dye concentration on PA6 fabric, the hyperchromic effect of λ max at 440 nm was more clearly noticed at both pH values 3 and 4 (Figures 6a and 7a,b), which was expected. Comparison of the absorption spectra of BCG in buffer solutions ( Figure 8) with absorption spectra of BCG on PA6 fabric (Figure 6a), immersed in buffered solutions of different pH values, expressed as K/S vs. λ, suggests that halochromic behaviour of BCG in buffer solution is slightly different to that of BCG applied to PA6 fabric and then immersed into buffer solutions. Furthermore, it should be stressed that a bathochromic shift of the absorption maximum of BCG was noticed from 618 nm (in solution) to 630 nm (in fibre) at pH 3. Moreover, the absorption spectrum of BCG in buffer solution of pH 3 showed only one absorption maximum at 445 nm, compared to BCG in buffer solution of pH 4, in which two absorption peaks appeared: The first at 445 nm and the second at 618 nm. This suggests that BCG became yellow in buffer solution of pH 3 and yellow-blue in buffer solution of pH 4. In contrast to BCG in buffer solution, the BCG on PA6 fabric immersed in buffers of pH 3 and 4 showed halochromic behaviour but to a lesser extent, because at both pH 3 and 4 two absorption peaks were noticed at 430 and 630 nm. The fabric changed colour from blue to yellow-blue. This suggests that the transformation of BCG bonded on PA 6 fabric into monoanionic form (yellow) was not as complete at pH 3 as in the case of BCG in buffer solution of pH 3, where only an absorption maximum at 445 was noticed. Moreover, the BCG showed a smaller halochromic behaviour when it was on fibre then when it was in solution. When BCG is yellow then it is in single anionic form B (see Figure 3), but when it is yellow-blue it indicates that the transformation of BCG from double anionic form C (blue), due to protonation, into single anionic form B (yellow) is not complete. The cause of this could be ascribed to both the textile matrix and the strength of dye-fibre interactions which hinder the interaction between dye and H + from buffer, and reflected in lower pH responsiveness of dyed PA6 fabric.
colour from blue to yellow-blue. This suggests that the transformation of BCG bonded on PA 6 fabric into monoanionic form (yellow) was not as complete at pH 3 as in the case of BCG in buffer solution of pH 3, where only an absorption maximum at 445 was noticed. Moreover, the BCG showed a smaller halochromic behaviour when it was on fibre then when it was in solution. When BCG is yellow then it is in single anionic form B (see Figure 3), but when it is yellow-blue it indicates that the transformation of BCG from double anionic form C (blue), due to protonation, into single anionic form B (yellow) is not complete. The cause of this could be ascribed to both the textile matrix and the strength of dye-fibre interactions which hinder the interaction between dye and H + from buffer, and reflected in lower pH responsiveness of dyed PA6 fabric.

Colour Fastness to Rubbing
From the results, presented in Table 2, it can be seen that both unfinished and finished dyed samples exhibited excellent colour fastness properties to rubbing. There was no staining visually detected on the dry or the wet cotton fabrics. Table 2. Visual assessment of colour fastness of tested samples to dry and wet rubbing.

Sample
Visual

Colour Fastness to Rubbing
From the results, presented in Table 2, it can be seen that both unfinished and finished dyed samples exhibited excellent colour fastness properties to rubbing. There was no staining visually detected on the dry or the wet cotton fabrics. Table 2. Visual assessment of colour fastness of tested samples to dry and wet rubbing.

Sample
Visual Assessment Using Grey Scale

Colour Fastness to Domestic and Commercial Laundering
The results, presented in Table 3, showed that the finished dyed PA6 samples exhibited excellent (grade 5) to good (grade 4/5) colour fastness to washing comparing to unfinished dyed samples, which exhibited good (grade 4/5) colour fastness to washing, irrespective of the washing cycles used. Staining was not evident on the cotton (grade 5 to 4/5), and very little on the PA6 fabric (grade 4/5 to 4). According to the obtained results it can be concluded that the unfinished and finished dyed PA6 fabrics had very good to excellent colour fastness to domestic and commercial laundering. The number of washing cycles (w) influenced the colour fastness to washing only for the finished dyed sample, as seen in a decrease of fastness for half the grade.

Colour Fastness to Light
The results of colour fastness to light visually assessed using blue scale were grade 1 for both PA_D and PA_DF samples, indicated that the studied dye had very poor fastness to light and thus cannot be used for textile products which could be exposed to daily light during use for extended periods. Additionally, the fading of dyed samples was measured after 2, 4, 6, and 8 h of illumination in a Xenotest apparatus, because complete degradation of dye was noticed after 10 h. The latter was also visually detected by the change of colour of dyed fabric from blue-green to almost white.
To prove that the faded dyed sample was still pH sensitive, the illuminated dyed samples were immersed in buffer solutions of different pH values (pH 3, 4, 5, and 6) and the change of colour was spectrophotometrically determined (Figures 9 and 10) after drying of samples. The curves of K/S vs. λ of unexposed and exposed unfinished and finished dyed samples for a specific time to xenon light, presented in Figures 9 and 10, showed that the K/S values decreased by the increase of exposure time. Nonetheless, the duration of the exposure time, whether it was 2, 4, 6, or 8 h, did not influence the pH responsiveness of dyed samples, even though dye degradation occurred. By degradation of BCG dye, the pH sensitivity was less perceived after 8 h then after 2 h of exposure, as expected.
On average, the UV index in the city of Ljubljana is 8 in June and July, 7 in May and August, 5 in April and September, 3 in March and October, 2 in February, and 1 in November, December and January [25]. Due to the poor light fastness of BCG dye on PA6 fabric, the treated fabric could only be used in winter when the UV index is lowest and air pollution is highest. In addition, the treated dyed fabric could be used as fabric for umbrellas where the light fastness properties are not as important as for functional fabrics. At this point it should be stressed that in cities such as Ljubljana the usage time for umbrellas is at least 30 min per rainy day. According to the available data, the highest number of rainy days in Ljubljana in 2019 was achieved in April, May and November [26]. Since the fabric is designed to respond to acid rain with a change of colour, the use of such an umbrella is more appropriate in winter, when the air pollution is higher than in the rainy spring  The curves of K/S vs. λ of unexposed and exposed unfinished and finished dyed samples for a specific time to xenon light, presented in Figures 9 and 10, showed that the K/S values decreased by the increase of exposure time. Nonetheless, the duration of the exposure time, whether it was 2, 4, 6, or 8 h, did not influence the pH responsiveness of dyed samples, even though dye degradation occurred. By degradation of BCG dye, the pH sensitivity was less perceived after 8 h then after 2 h of exposure, as expected.
On average, the UV index in the city of Ljubljana is 8 in June and July, 7 in May and August, 5 in April and September, 3 in March and October, 2 in February, and 1 in November, December and January [25]. Due to the poor light fastness of BCG dye on PA6 fabric, the treated fabric could only be used in winter when the UV index is lowest and air pollution is highest. In addition, the treated dyed fabric could be used as fabric for umbrellas where the light fastness properties are not as important as for functional fabrics. At this point it should be stressed that in cities such as Ljubljana the usage time for umbrellas is at least 30 min per rainy day. According to the available data, the highest number of rainy days in Ljubljana in 2019 was achieved in April, May and November [26]. Since the fabric is designed to respond to acid rain with a change of colour, the use of such an umbrella is more appropriate in winter, when the air pollution is higher than in the rainy spring season, when air Polymers 2020, 12, 2251 13 of 15 pollution is lower. Such a conscious decision could prolong the lifetime of the umbrella, as the UV index in winter is 1, and the dye would therefore not degrade as quickly.

Response Time and Reversibility Results
The unfinished and finished dyed PA6 samples changed colour after being immersed in buffer solutions of different pH values. The colour change did not occur immediately as in the case of BCG dye in buffer solution. The colour change of polyamide 6 was gradual, and the fabric required more time for the colour change to be visually noticeable. The possible explanation for such behaviour of the BCG dye on PA6 fabric could be ascribed to both the strength of dye-fibre interaction which influences the interaction between BCG dye and H + in buffer solution and the slower wetting process of the fabric with buffer solution. The same observation was noted by De. Clerk and Van der Schueren [14]. The finished dyed PA6 samples required even more time to undergo the colour change. On average the response time was 30 min for unfinished and 45 min for finished dyed samples.
All unfinished dyed samples, regardless of the dye concentration (0.1, 0.2, or 0.5 o.m.f.), reverted to their original colour. Furthermore, the samples that were previously immersed in buffer solution of pH 3 reverted to their initial colour much faster than the samples that were previously immersed in buffer solution of pH 4. The treated dyed samples with dye concentration of 0.2% o.m.f. needed a longer time to revert to their initial colour.

Water and Oil Repellency
Standard spray test ratings were ISO 1 for PA_D sample and ISO 5 for PA_DF sample. The ratings show that unfinished dyed samples had no resistance to surface wetting. As expected, the sample finished with Dynasylan F 8815 showed no wetting and no adherence of small drops of water on the sprayed surface.

Conclusions
PA6 fabric was successfully dyed with pH-sensitive BCG dye using a conventional exhaust dyeing process. The dyed PA6 fabric changed colour in the pH range between 3 and 5, indicating that the selected dye applied to the PA6 fabric could serve as an indicator of a change in the pH of rainwater. Levelness of the PA6 fabric dyed with BCG dye was not obtained due to the occurrence of creases during the dyeing process. The pH sensitivity of the dyed PA6 fabric was not affected by the dye concentration.
The PA6 fabric was also successfully treated with a water-and oil-repellent finish. The unfinished and finished PA6 showed good colour fastness to rubbing and domestic and commercial laundering. The lightfastness properties of the BCG dye applied to the PA6 fabric were not particularly good, as the dye degraded under the influence of xenon light. Nonetheless, the treatment extended the response time for the change of colour. However, the exposure time did not affect the pH sensitivity of the unfinished and finished dyed samples.