Degradation of Plastics under Anaerobic Conditions: A Short Review

Plastic waste is an issue of global concern because of the environmental impact of its accumulation in waste management systems and ecosystems. Biodegradability was proposed as a solution to overcome this problem; however, most biodegradable plastics were designed to degrade under aerobic conditions, ideally fulfilled in a composting plant. These new plastics could arrive to anaerobic environments, purposely or frequently, because of their mismanagement at the end of their useful life. This review analyzes the behavior of biodegradable and conventional plastics under anaerobic conditions, specifically in anaerobic digestion systems and landfills. A review was performed in order to identify: (a) the environmental conditions found in anaerobic digestion processes and landfills, as well as the mechanisms for degradation in those environments; (b) the experimental methods used for the assessment of biodegradation in anaerobic conditions; and (c) the extent of the biodegradation process for different plastics. Results show a remarkable variability of the biodegradation rate depending on the type of plastic and experimental conditions, with clearly better performance in anaerobic digestion systems, where temperature, water content, and inoculum are strictly controlled. The majority of the studied plastics showed that thermophilic conditions increase degradation. It should not be assumed that plastics designed to be degraded aerobically will biodegrade under anaerobic conditions, and an exact match must be done between the specific plastics and the end of life options that they will face.

The majority of biodegradable plastics have been designed to degrade in the aerobic environment of an industrial composting plant [47]. However, in developing countries, they can be disposed in landfills due to deficient management practices, misinformation, and lack of infrastructure. Also, they could be incorporated in anaerobic digestion systems in places where this technology is used to treat organic waste. While anaerobic digestion systems are specifically designed to promote the biodegradation process through the control of operational variables, the main objective in landfills is the safe confinement of waste, even if in some of them the produced biogas is collected and used [48]. Anaerobic digestion processes are usually applied to organic waste with a low content of inorganics that is processed in a defined time-frame in a closed reactor [49,50]. The process can be carried on at mesophilic or thermophilic temperatures, and inoculum is added in order to increase the rate and extent of biodegradation; optimization of solid content, carbon/nitrogen ratio and food/inoculum ratio is carried on to increase methane production [51]. In landfills, on the other hand, a complex and heterogeneous mixture of waste is buried, and the degradation process occurs as a result of the activity of bacteria present naturally in the waste. The inherent heterogeneity of waste, as well as the different environmental and operational conditions, will produce an extensive range of biodegradation processes that usually will extend through decades. In landfills, the rate of biodegradation increases as leachate is recirculated [52][53][54]. However, they are slower than in anaerobic digestion systems.
In this context, this review aims to offer an assessment of the behavior of different biodegradable plastics under anaerobic conditions that would take place in anaerobic digestion systems and landfills.
The inclusion of these new plastics in engineered anaerobic systems could contribute to methane production. In this context, this review includes a description of the anaerobic biodegradation of plastics that takes place in anaerobic digestion processes and landfills, in order to explain the mechanisms that take place in the environments mentioned above. An analysis of the different experimental conditions used in the assessment of this kind of systems is presented in order to identify common features. Following this, a summary and analysis of the results obtained for different biodegradable and conventional plastics are shown. Natural anaerobic environments are not included in this research, as they must not be considered as viable waste management options.

Methods
The search for research articles and book chapters was done in the first semester of 2019, in the scientific finders Scopus ® , Access DL ® , Oxford Academy ® , Springer link ®, and Science Direct ® . The initial keywords used were plastics plus anaerobic, degradation, polymers, and landfill. A total of 1207 abstracts were read to identify papers focused on the degradation of plastics under anaerobic conditions. This process allowed us to obtain 70 articles from 34 different peer-reviewed journals (see reference material for the complete list of articles). References were downloaded in format bibTex in the free software Mendeley ® .
The scientific articles and chapters were analyzed in order to identify information related to the following topics: (a) scenarios and mechanisms for anaerobic degradation of plastics, (b) methods for the assessment of the anaerobic degradation of plastics, and (c) degradation of plastics under anaerobic digestion and landfill conditions.

Results
The different research papers used in this review, as well as their characteristics and main results are presented in the Supplementary Materials.

Biodegradable Plastics Assessed under Anaerobic Conditions
Biodegradable plastics include polylactic acid (PLA), polycaprolactone (PCL), polybutylene succinate (PBS), poly(butyleneadipate-coterephtalazte) (PBAT), poly(hydroxybutyrate) (PHB) and poly(hydroxybutyrate)-co-poly(hydroxyvalerate) (PHBV). Except for PBAT, they are aliphatic polyesters. They can be produced from biomass or fossil fuels. Table 1 shows the monomers of the most commonly biodegradable plastics assessed under anaerobic conditions. The different research papers used in this review, as well as their characteristics and main results are presented in the supplementary materials.

Anaerobic Processes in Digestion Systems and Landfills
Anaerobic degradation is a biological process that transforms organic matter in an oxygen-free environment. It can follow two routes: anaerobic fermentation, where organic matter can act as an electron donor or receptor; or anaerobic respiration, which requires acceptors such as CO2, SO4 2− , NO3 − . The process is developed in four stages: hydrolysis, acidogenesis, acetogenesis, and methanogenesis, which lead to the production of a mixture of CH4 and CO2, known as biogas. Two thirds of CH4 produced in an anaerobic process is because of the fermentation and one third by respiration [59]. The efficiency of the anaerobic biodegradation is affected by the presence of volatile fatty acids, sulfate, ammonia, and heavy metals [60], and for factors such as pH, temperature [59], redox potential, and hydrogen [55] Polycaprolactone PCL The different research papers used in this review, as well as their characteristics and main results are presented in the supplementary materials.

Anaerobic Processes in Digestion Systems and Landfills
Anaerobic degradation is a biological process that transforms organic matter in an oxygen-free environment. It can follow two routes: anaerobic fermentation, where organic matter can act as an electron donor or receptor; or anaerobic respiration, which requires acceptors such as CO2, SO4 2− , NO3 − . The process is developed in four stages: hydrolysis, acidogenesis, acetogenesis, and methanogenesis, which lead to the production of a mixture of CH4 and CO2, known as biogas. Two thirds of CH4 produced in an anaerobic process is because of the fermentation and one third by respiration [59]. The efficiency of the anaerobic biodegradation is affected by the presence of volatile fatty acids, sulfate, ammonia, and heavy metals [60], and for factors such as pH, temperature [59], redox potential, and hydrogen [55] Polybutylene succinate PBS The different research papers used in this review, as well as their characteristics and main results are presented in the supplementary materials.

Anaerobic Processes in Digestion Systems and Landfills
Anaerobic degradation is a biological process that transforms organic matter in an oxygen-free environment. It can follow two routes: anaerobic fermentation, where organic matter can act as an electron donor or receptor; or anaerobic respiration, which requires acceptors such as CO2, SO4 2− , NO3 − . The process is developed in four stages: hydrolysis, acidogenesis, acetogenesis, and methanogenesis, which lead to the production of a mixture of CH4 and CO2, known as biogas. Two thirds of CH4 produced in an anaerobic process is because of the fermentation and one third by respiration [59]. The efficiency of the anaerobic biodegradation is affected by the presence of volatile fatty acids, sulfate, ammonia, and heavy metals [60], and for factors such as pH, temperature [59], redox potential, and hydrogen [56] Poly(butyleneadipateco-terephthalate) PBAT The different research papers used in this review, as well as their characteristics and main results are presented in the supplementary materials.

Anaerobic Processes in Digestion Systems and Landfills
Anaerobic degradation is a biological process that transforms organic matter in an oxygen-free environment. It can follow two routes: anaerobic fermentation, where organic matter can act as an electron donor or receptor; or anaerobic respiration, which requires acceptors such as CO2, SO4 2− , NO3 − . The process is developed in four stages: hydrolysis, acidogenesis, acetogenesis, and methanogenesis, which lead to the production of a mixture of CH4 and CO2, known as biogas. Two thirds of CH4 produced in an anaerobic process is because of the fermentation and one third by respiration [59]. The efficiency of the anaerobic biodegradation is affected by the presence of volatile fatty acids, sulfate, ammonia, and heavy metals [60], and for factors such as pH, temperature [59], redox potential, and hydrogen The different research papers used in this review, as well as their characteristics and main results are presented in the supplementary materials.

Anaerobic Processes in Digestion Systems and Landfills
Anaerobic degradation is a biological process that transforms organic matter in an oxygen-free environment. It can follow two routes: anaerobic fermentation, where organic matter can act as an electron donor or receptor; or anaerobic respiration, which requires acceptors such as CO2, SO4 2− , NO3 − . The process is developed in four stages: hydrolysis, acidogenesis, acetogenesis, and methanogenesis, which lead to the production of a mixture of CH4 and CO2, known as biogas. Two thirds of CH4 produced in an anaerobic process is because of the fermentation and one third by respiration [59]. The efficiency of the anaerobic biodegradation is affected by the presence of volatile fatty acids, sulfate, ammonia, and heavy metals [60], and for factors such as pH, temperature [59], redox potential, and hydrogen [55] Polyhydroxybutyrateco-polyhydroxyvalerate PHBV The different research papers used in this review, as well as their characteristics and main results are presented in the supplementary materials.

Anaerobic Processes in Digestion Systems and Landfills
Anaerobic degradation is a biological process that transforms organic matter in an oxygen-free environment. It can follow two routes: anaerobic fermentation, where organic matter can act as an electron donor or receptor; or anaerobic respiration, which requires acceptors such as CO2, SO4 2− , NO3 − . The process is developed in four stages: hydrolysis, acidogenesis, acetogenesis, and methanogenesis, which lead to the production of a mixture of CH4 and CO2, known as biogas. Two thirds of CH4 produced in an anaerobic process is because of the fermentation and one third by respiration [59]. The efficiency of the anaerobic biodegradation is affected by the presence of volatile fatty acids, sulfate, ammonia, and heavy metals [60], and for factors such as pH, temperature [59], redox potential, and hydrogen [55] 3.1.

Anaerobic Processes in Digestion Systems and Landfills
Anaerobic degradation is a biological process that transforms organic matter in an oxygen-free environment. It can follow two routes: Anaerobic fermentation, where organic matter can act as an electron donor or receptor; or anaerobic respiration, which requires acceptors such as CO 2 , SO 4 2− , NO 3 − .
The process is developed in four stages: Hydrolysis, acidogenesis, acetogenesis, and methanogenesis, which lead to the production of a mixture of CH 4 and CO 2 , known as biogas. Two thirds of CH 4 produced in an anaerobic process is because of the fermentation and one third by respiration [58]. The efficiency of the anaerobic biodegradation is affected by the presence of volatile fatty acids, sulfate, ammonia, and heavy metals [59], and for factors such as pH, temperature [58], redox potential, and hydrogen concentration [58,60]. It will also be dependent on the concentration and type of microorganisms present in the media [61,62], presence of nutrients [58], and the characteristics of the substrate [63][64][65].
In landfills, the inherent heterogeneity of waste increases the complexity of the biodegradation process [66]. Anaerobic biodegradation in these sites is developed in five stages [67]. In the first one hydrolysis takes place, producing a decrease in pH, an increase in the chemical oxygen demand and concentration of volatile fatty acids, ammonia and sulfates. In the second stage, acidogenesis produces H 2 . In the third stage, acetogenic fermentation leads acetic acid, hydrogen, and CO 2 being formed. In the fourth stage, methanogenesis leads to biogas production. In the last stage, stabilization shows a continuous decrease in the generation of biogas, increasing the concentration of N 2 . The biodegradation process is affected by temperature, oxygen, moisture content, alkalinity, presence of nutrients, and inhibitors [68]. Although it is not feasible to control all these parameters in a landfill, it has been proved that the treatment and recirculation of leachate can increase the biodegradation rates, promoting the functioning of the landfill as a bioreactor [68].

Degradation Mechanisms
The degradation of plastics is usually a concurrent phenomenon involving the interaction of physical, chemical, and biological factors. The resulting mechanism will depend on the nature of the material and the environmental conditions [69]. The factors that produce different degradation processes have been described previously [69][70][71]; they include UV radiation, temperature, mechanical stress, oxidative, hydrolysis, and biodegradation processes. Oxidation by oxygen and ozone will not be relevant in the case of anaerobic degradation of plastics, and the effect of photo-oxidation will be limited, as anaerobic systems are commonly carried on in closed vessels or confined spaces [72][73][74].
For plastics whose structure includes a carbon backbone, such as polyolefins and polystyrene [75,76], mechanisms based in the formation of free radicals that promote consecutive cleavages of the polymeric chain have been proposed; reactions begin in tertiary carbons. For polyethylene (PE), it has been proposed a mechanism for UV-promoted radiation, which produces CH 4 and H 2 as a result of the formation of free radicals [75].
On the other hand, polymers containing elements different from carbon in their main chain can undergo hydrolysis processes. The first step is the diffusion of water through the material, especially in amorphous regions that present lesser resistance. The water promotes hydrolytic rupture of the steric bonds, which causes a decrease in molecular weight and formation of water-soluble byproducts. These reactions decrease the stability of the crystalline zones of the plastic because of an autocatalytic process promoted by the degradation of acid products that increase the presence of carboxylic acids in the extremes of the polymers [77]. This type of mechanism has been proposed for the degradation of polycaprolactone (PCL) and polylactic acid (PLA). The rate of degradation increases as the reaction proceeds, and it is affected by temperature and extreme pH values [77].
The mechanisms proposed for the biodegradation of plastics such as PHBV begin with the colonization of the material surface, followed by hydrolysis, erosion of the exposed areas, and saturation that leads to fragmentation [78]. A similar sequence has been described for copolymers of polyethylene and starch, where the microorganisms attack the amorphous starch zones in the surface, allowing their entrance to internal pores [79]. However, once the starch has been consumed, the degradation of the polyethylene matrix can be obtained by chemical factors.

Assessment of the Biodegradation Process under Anaerobic Conditions
The study of the anaerobic degradation of biodegradable plastics has focused on PLA, PCL, PHBV, and copolymers that include two different biodegradable plastics, or a conventional plastic mixed with a biodegradable one. Conventional plastics (PE, PETE, PP, PS, PVC) have also been tested in order to measure their degradation, their possible adverse effects in the biodegradation processes, or in the case of polyethylene, as negative controls for the experiments. The distribution of tested plastics for anaerobic digestion and landfill conditions is shown in Figure 1. While 76% of the reviewed studies have tested degradation under anaerobic digestion conditions, 17% have tried to simulate landfill conditions and 7% tested both scenarios.
Polymers 2019, 11, x 6 of 18 of polyethylene, as negative controls for the experiments. The distribution of tested plastics for anaerobic digestion and landfill conditions is shown in Figure 1. While 76% of the reviewed studies have tested degradation under anaerobic digestion conditions, 17% have tried to simulate landfill conditions and 7% tested both scenarios.

Experimental Setup
The assessment of the anaerobic biodegradation of plastics is usually done at lab scale, because of economic and logistic reasons that prevent the development of field studies; only nine studies tested fullscale conditions, exposing the plastics in landfill cells. In laboratory experiments, the volume of the used bioreactors varies from 0.05 L to 5.0 L, as shown in Figure 2. While 28% of the experiments were performed in small reactors (0.1-0.2 L), 31% were developed in medium-size reactors (1.0-2.0 L) and only 8% were done in reactors bigger than 2.0 L. There is no a discernible pattern for the volume of reactors in the assessment of anaerobic digestion and sanitary landfill; small and big reactors were used to simulate both conditions. Very likely, the selection of the reactor's size was related to the availability of resources, and not to specific goals or designs.

Experimental Setup
The assessment of the anaerobic biodegradation of plastics is usually done at lab scale, because of economic and logistic reasons that prevent the development of field studies; only nine studies tested full-scale conditions, exposing the plastics in landfill cells. In laboratory experiments, the volume of the used bioreactors varies from 0.05 L to 5.0 L, as shown in Figure 2. While 28% of the experiments were performed in small reactors (0.1-0.2 L), 31% were developed in medium-size reactors (1.0-2.0 L) and only 8% were done in reactors bigger than 2.0 L. There is no a discernible pattern for the volume of reactors in the assessment of anaerobic digestion and sanitary landfill; small and big reactors were used to simulate both conditions. Very likely, the selection of the reactor's size was related to the availability of resources, and not to specific goals or designs. The length of the experiments is related mainly to the type of scenario that is being evaluated. Anaerobic digestion is a relatively fast process, which usually lasts 15 to 45 days. This condition is easily replicated in the laboratory, and is commonly used to test the inherent anaerobic biodegradability of new materials. Fifty-two percent of the reviewed papers focused on anaerobic digestion that lasted from 7 days to three months. On the other hand, the biodegradation process taking place in a landfill will extend The length of the experiments is related mainly to the type of scenario that is being evaluated. Anaerobic digestion is a relatively fast process, which usually lasts 15 to 45 days. This condition is easily replicated in the laboratory, and is commonly used to test the inherent anaerobic biodegradability of new materials. Fifty-two percent of the reviewed papers focused on anaerobic digestion that lasted from 7 days to three months. On the other hand, the biodegradation process taking place in a landfill will extend for a much longer timeframe, which can take up to 20 years. To simulate those conditions, some of the experiments extended up to six years; in fact, the four longest studies (2-6 years) are simulations of landfill conditions. In order to increase the biodegradation rates of reactors simulating landfills, leachate can be recirculated, as has been done in different studies [80][81][82].
The presence of a mixture of microorganisms capable of degrading waste is a necessary condition in order to achieve an efficient process. To guarantee this condition, the microbial population can be increased by the introduction of an inoculum [65]. To increase the quality and production of biogas, it is convenient to pre-incubate the microorganisms until 60% of CH 4 is reached [83]. This enrichment is commonly done in anaerobic digestion tests [61][62][63][83][84][85][86][87].

Analytical Techniques Used to Assess Plastic Degradation and Biodegradation
Different analytical techniques have been used in order to identify or measure the degradation of plastics in anaerobic environments. The main quantitative method is respirometry, which measures the cumulative biogas or methane production in reactors containing the assessed polymer, comparing it with controls that do not contain the tested material [87]. Respirometric tests allow the quantification of biodegradation, which is expressed as a percentage. Usually, the CH 4 or biogas produced is corrected subtracting the amount produced in a blank and then is compared to the theoretical production, based on the carbon content in the sample [84,[88][89][90][91][92][93][94]. Variations of this method include the measurement of CO 2 , and the inclusion of liquid and gas phases [87,95]. Modified Gompertz equations, which considers a latency factor, were used [50,60,61] to model the biodegradation process.
The international associations ASTM International and ISO have defined standards for the assessment of biodegradation of plastics under anaerobic conditions, based on respirometric measurements [96][97][98][99][100][101] (Table 2). Table 2. Standards for the assessment of biodegradation of plastics in anaerobic environments. Respirometric systems rely on the use of closed reactors, which allow the collection of all the gases produced; such conditions are difficult to obtain in big size reactors or field trials. In those cases, the assessment of the process is usually done by the direct analysis of the physical or chemical properties of the polymers [102]. The analyzed properties include loss of mass, loss of mechanical properties, changes in the thermal behavior of the materials, microbial colonization of the surface observed by scanning electron microscopy, presence of specific functional groups measured by infrared spectroscopy, or decrease in molecular weight, assessed by gel permeation or exclusion chromatography, among others [86,87,91,[103][104][105][106][107]. While these techniques can give evidence of degradation, they do not allow for the obtaining od a quantitative measurement of degradation or to distinguish between degradation caused by microorganisms and other types of degradation processes. The frequency of use of these techniques is shown in Figure 3. electron microscopy, presence of specific functional groups measured by infrared spectroscopy, or decrease in molecular weight, assessed by gel permeation or exclusion chromatography, among others [87,88,92,[104][105][106][107][108]. While these techniques can give evidence of degradation, they do not allow for the obtaining od a quantitative measurement of degradation or to distinguish between degradation caused by microorganisms and other types of degradation processes. The frequency of use of these techniques is shown in Figure 3.

Anaerobic Digestion
Biodegradable plastics have shown different biodegradation rates, depending on experimental conditions, as shown in Table 3. Studies comparing different polyhidroxialcaonates reported a 62% conversion to biogas [108,109], and an enhancement in biogas production when this plastic was present. In the specific case of PHB, it degraded 90% in 14 days at 55 • C, with a rate similar to cellulose [86]. However, it only reached 23% in 10 weeks when degrading with anaerobic sludge [89]. For PCL, reported biodegradation ranged from 80% in 50 days at 55 • C [86] to neglectable values [89,110], in some cases showing only changes in color [105]; the degradation increased when eggshell was used to produce a biocomposite [110]. Similar behavior was shown by PBS, whose degradation reached values from 25.8% under thermophilic conditions [83] and 32.5% [88], but did not show mineralization in experiments carried on at 55 • C [86]. Reported biodegradation for PLA varies from total mineralization [111], 75% in 75 days in thermophilic conditions [86], as well as 60% [88] and complete lack of biodegradation in 100 days of experimentation [112]. PBAT degraded 9.3% in 75 days [88]. Biodegradation rates of different plastics have been affected by the size of the plastic samples [103], the use of cosubstrates, and alkalinity [111]. One of the main factors to promote the process was temperature, showing higher rates for thermophilic rather than mesophylic conditions [108,113]. It was proposed that biodegradation increases when the vitrea transition temperature of the plastics was reached in the system [114].
Conventional plastics, such as cellulose acetate [115], have shown negligible biodegradation, as well as PETE [107]. The feasibility of biodegradation of PVC was obtained only if the plastic was subjected previously to a Fenton oxidation process [93]. In fact, inhibition of biogas production was reported due to the presence of HDPE, PP, and PS [116]. The addition of additives that promote abiotic oxidation to transform them into oxodegradable plastics did not promote biodegradation of PE and PETE [106]. On the other hand, PETE-PLA copolymers reached 34-69% mineralization, depending on the starting aromatic to aliphatic ratio [107]. Similarly, the use of starch in composites with PE only promoted biodegradation of the bio-based polymer [102].
In recent years there was increasing interest in the composites containing bio-based dispersed phases, known as biocomposites. Inclusion of bio-based phases was expected to decrease the environmental impact of conventional plastics because of their renewable origin and in some cases, biodegradability [117]. Starch was selected for many biocomposites, given its low cost, good permeability properties, and inherent biodegradability by microorganisms into harmless products [118]. However, evidence shows that these composites are not inherently biodegradable; for composites based in polyolefins, biodegradation occurs only for starch [119]. It was found that the starch in these composites biodegrades only partially, as it is limited if a discontinuous matrix of starch is present [120]. For composites based in a biodegradable matrix, different biodegradation rates ranging from 10.2% to 53% were reported [121][122][123]. Table 3 summarizes the results for biodegradation under anaerobic digestion conditions, showing only those where respirometric tests were used to assess the process. It can be observed that PHB, PHBV, and their copolymers achieved high levels (>80%) of mineralization, while PCL and PLA results varied widely without showing a discernable pattern related to temperature or length of the experiments. On the other hand, PBS, conventional non-degradable plastics, and their combination with pro-oxidant additives did not achieve significant biodegradation.

Landfill
PLA did not biodegrade in simulated landfill conditions, with different recirculation rates [68], due to the anaerobic conditions that decrease the rate of the initial hydrolysis step. However, a 90% mass loss was reported when thermophilic conditions were reached [59]. Degradation in landfill conditions was influenced by the presence of oxygen in the media; while PHBV degraded almost 100% in simulated conditions with forced aeration, under strictly anaerobic conditions degradation was negligible [42]. The effect can be related to the higher concentration of microorganisms found in the higher layers of waste cells, as shown in the study of Menmee et al. [129].
Conventional, not biodegradable plastics, have shown meager degradation rates in simulated and real landfill conditions. This was found for PU [135], cellulose acetate [65], PP [136], and PVC [137]. Polyolefinic plastics (HDPE, LDPE, PP) and PS degraded between 4.96% and 15% in lysimeters that simulated landfill conditions [129]. PE and PETE with biodegradation-promoting additives showed no biodegradation under soil burial [106] when the presence of oxygen was similar to the one that can be found in a landfill.

Conclusions
Biodegradable plastics were presented as a solution to the accumulation of these materials in landfills and natural ecosystems. While most of them were designed to degrade in aerobic composting systems, two scenarios could lead to their presence in anaerobic processes. The first being the interest in degrading them in digestion systems used to degrade organic waste and produce biogas. The second being that their presence in landfills and dumpsites due to mismanagement or lack of infrastructure. This latter situation is very likely to happen in developing countries, where segregation and separate treatment of different fractions of waste is scarce.
As expected, biodegradation of plastics is higher in digestion systems than in simulated landfill conditions because of the control of temperature, agitation, mixing, solids concentration, and presence of microorganisms, among other factors that can be regulated in digestion. Biodegradable plastics showed higher mineralization than conventional ones in digestion and landfill experiments. However, this research showed clearly that experimental conditions could lead to different and even opposite results, varying parameters such as time of residence, recirculation of leachate, and aeration. Besides, the use of biocomposites or copolymers increases the variability of results.
Even if standard ISO and ASTM methods are defined for the assessment of these materials, there are not current specifications that define mineralization rates that a plastic should reach in order to be labeled as "biodegradable in anaerobic digestion" or "biodegradable in landfill". This situation makes a comparison between materials difficult and prevents a complete understanding of how they will react in real waste management conditions. While in developed countries, standards and ecolabels are used to asses and explain the expected behavior of materials in different waste management options, many countries do not have these essential tools. In this context, it is common for different materials to be announced as "biodegradable" without information regarding the fate that these new plastics will have in the specific waste management conditions that they will face. In developing countries, the most likely end of life scenario will be a landfill or dumpsite, where the biodegradation rate of biodegradable plastics will be slow. Even if mineralization occurs, it could lead to greenhouse emissions if not suitable systems for biogas recovery are in place.
To increase the contribution of biodegradable plastics to the solution of the waste accumulation, further research is needed in order to increase understanding of their behavior in waste management systems. This knowledge has to be shared with consumers, decision-makers, and waste management operators to promote proper management of these new materials.