A 1 , 6-Diphenylpyrene-Based , Photoluminescent Cyclophane Showing a Nematic Liquid-Crystalline Phase at Room Temperature

Photoluminescent nematic liquid crystals have been an attractive research target for decades, because of their potential applications in optoelectrical devices. Integration of luminescent motifs into cyclic structures is a promising approach to induce low-ordered liquid-crystalline phases, even though relatively large and rigid luminophores are used as emitters. Here, we demonstrate a 1,6-diphenylpyrene-based, unsymmetric cyclophane showing a stable nematic phase at room temperature and exhibiting strong photoluminescence from the condensed state. The observed sky-blue photoluminescence was dominated by the emission species ascribed to assembled luminophores rather than monomers.


Introduction
Photoluminescent liquid crystals have attracted much attention because of their potential applications in displays, polarized light-emitting materials, and stimuli-responsive luminescent materials [1][2][3][4][5][6].Nematic liquid-crystalline (LC) phases are preferable for such purposes, because the homogeneous/homeotropic alignment of molecules can be easily achieved [7,8].In nematic phases, molecules have long-range orientational order and have no positional order [7,8].However, it is still challenging to modify the molecular structure of π-extended luminophores so that they show nematic LC phases at room temperature (r.t.).Relatively large and rigid π-conjugated moieties lead to strong intermolecular interactions, like the π-π interaction, resulting in a strong tendency to form more ordered LC phases, such as smectic, columnar, and cubic phases [2,[9][10][11][12].
Since a series of cyclic main-chain oligomers were found to show nematic LC behavior in 1992 [13], the LC properties of various cyclic compounds have been investigated.For example, Percec and co-workers demonstrated that cyclic oligomers exhibit LC phases over a wider temperature range compared with the linear analogues [14][15][16][17].Tschierske's and Hegmann's groups have reported LC behavior of low-molecular-weight cyclophanes [18][19][20][21].Though various mesogens were used in the cyclic LC compounds, highly luminescent π-conjugated groups have not been used as mesogens so far.
The course of our previous studies on luminescent cyclophanes [22][23][24][25][26][27][28][29] suggested that the introduction of a cyclic structure into luminophores is a promising way to achieve mechanoresponsive luminescent materials [3,4,[30][31][32][33][34][35][36].Luminescent cyclophanes having longer spacers have been found to show nematic LC properties.Especially, unsymmetric cyclophanes, which have only one luminophore exhibiting photoluminescence in the visible wavelength region in the cyclic structure, show a nematic phase in a lower temperature range in comparison with the symmetric analogues containing Crystals 2019, 9, 92 2 of 10 two luminophores in an individual cycle [23][24][25].Furthermore, the unsymmetric cyclophanes exhibit kinetically trapped LC phases with nematic molecular order after rapid cooling from the nematic state.As the phases with nematic order are thermodynamically metastable, moderate thermal treatment easily induces phase transitions to stable crystalline phases.The transitions are concomitant with photoluminescence color changes.However, highly luminescent cyclophanes showing thermodynamically stable nematic phases at r.t.have not been prepared yet.
Here, we report a 1,6-diphenylpyrene-based, unsymmetric cyclophane that exhibits a stable nematic LC phase at r.t.The cyclic compound shows strong blue and sky-blue photoluminescence in solution and LC phases, respectively.

General Method
All reagents and solvents were purchased from Fujifilm Wako and Tokyo Kasei.Unless otherwise noted, all reactions were carried out under a nitrogen atmosphere.Flash silica gel column chromatography was carried out with a Biotage Isolera flash system using Biotage Flash Cartridges or SHOKO-scientific Purif-Pack-EX cartridges.Silica gel from Kanto Chemicals (silica gel 60 N, spherical, 63-210 µm) was used when flash silica gel column chromatography was conducted in a conventional manner.Recycling preparative gel permeation chromatography (GPC) was performed with a Japan Analytical Industry LaboACE. 1 H NMR spectra were recorded on a JEOL JNM-ECX 400 spectrometer, and all chemical shifts are quoted on the δ-scale in ppm relative to the signal of tetramethylsilane (at 0.00) as an internal standard. 13C NMR spectra were recorded on a JEOL JNM-ECX 400 spectrometer, and all chemical shifts (δ) are reported in ppm using residual solvents as the internal standard (CDCl 3 at 77.16, DMSO-d 6 at 39.52).Coupling constants (J) are reported in Hz and relative intensities are also shown.Matrix-assisted laser desorption ionization time-of-flight (MALDI-TOF) mass spectra were obtained on an AB SCIEX TOF/TOF 5800.The differential scanning calorimetry (DSC) measurements were conducted using Hitachi DSC7020 with a heating/cooling rate of 5 • C/min under a nitrogen atmosphere.XRD measurements were carried out with a Rigaku SmartLab.UV-vis absorption spectra were measured with a JASCO V-550.Steady-state fluorescence spectra were recorded on a JASCO FP-6500.Time-resolved fluorescence measurements were carried out with a Hamamatsu Photonics Quantaurus-Tau.Quantum efficiencies were measured with a Hamamatsu Photonics Quantaurus-QY.Polarized optical microscopic observations were conducted with an Olympus BX-60 optical microscope equipped with a Shimadzu Moticam 1080.

Synthesis
The synthetic routes used to prepare cyclophane 1 and compound 2 are shown in Scheme 1; Scheme 2, respectively.

Compound 5.
A mixture of 4 (940 mg, 1.69 mmol), 10% aq.HCl (5 mL) solution, and chloroform (200 mL) was heated to reflux for 3 h and subsequently cooled to room temperature.Water (20 mL) was added, most of the chloroform was evaporated, and the solid product was filtered off.The solid was washed with water (2 × 20 mL) and methanol (2 × 5 mL).The product was dried in vacuo to afford compound 5 (577 mg, 1.49 mmol) as a yellow solid with a yield of 88%. 1  Ethyl acetate (100 mL) was added and the organic layer was washed with saturated aq.NH4Cl solution (3 × 300 mL) and saturated aq.NaCl solution (100 mL).The organic layer was dried over MgSO4 and filtered, and the solvent was evaporated.The crude product thus isolated was purified by flash column chromatography on silica gel (eluent: dichloromethane/acetone = 85:15) and recycling GPC (eluent: chloroform) to afford cyclophane 1 (280 mg, 0.269 mmol) as a pale yellow   A mixture of 4 (940 mg, 1.69 mmol), 10% aq.HCl (5 mL) solution, and chloroform (200 mL) was heated to reflux for 3 h and subsequently cooled to room temperature.Water (20 mL) was added, most of the chloroform was evaporated, and the solid product was filtered off.The solid was washed with water (2 × 20 mL) and methanol (2 × 5 mL).The product was dried in vacuo to afford compound 5 (577 mg, 1.49 mmol) as a yellow solid with a yield of 88%. 1  Compound 4. A mixture of 1,6-dibromopyrene (500 mg, 1.39 mmol), 4-tetrahydro-2H -pyran-2-yloxy)phenylboronic acid (615 mg, 2.77 mmol), Pd(PPh 3 ) 4 (80.0 mg, 6.92 × 10 −2 mmol), and K 2 CO 3 (763 mg, 5.52 mmol) in toluene (40 mL) and H 2 O (5 mL) was degassed and heated to reflux for 15 h.After cooling to r.t., the reaction suspension was poured into chloroform (200 mL).The organic layer was washed with saturated aq.NaCl solution (2 × 100 mL), dried over MgSO 4 , and filtered, after which the solvent was evaporated.The crude product was purified by flash column chromatography on silica gel (eluent: hexane/chloroform = 1:5) and subsequently precipitated from a mixture of chloroform and hexane to afford compound 4 (635 mg, 1.14 mmol) as yellow solid with a yield of 82%. 1  Compound 5. A mixture of 4 (940 mg, 1.69 mmol), 10% aq.HCl (5 mL) solution, and chloroform (200 mL) was heated to reflux for 3 h and subsequently cooled to room temperature.Water (20 mL) was added, most of the chloroform was evaporated, and the solid product was filtered off.The solid was washed with water (2 × 20 mL) and methanol (2 × 5 mL).The product was dried in vacuo to afford compound 5 (577 mg, 1.49 mmol) as a yellow solid with a yield of 88%. 1   C, the solvent was evaporated.Ethyl acetate (100 mL) was added and the organic layer was washed with saturated aq.NH 4 Cl solution (3 × 300 mL) and saturated aq.NaCl solution (100 mL).The organic layer was dried over MgSO 4 and filtered, and the solvent was evaporated.The crude product thus isolated was purified by flash column chromatography on silica gel (eluent: dichloromethane/acetone = 85:15) and recycling GPC (eluent: chloroform) to afford cyclophane 1 (280 mg, 0.269 mmol) as a pale yellow viscous liquid with a yield of 35%. 1   C.After cooling to room temperature, the solvent was evaporated.Chloroform was added, and the organic layer was washed with saturated aq.NH 4 Cl solution (3 × 300 mL) and saturated aq.NaCl solution (100 mL).The organic layer was dried over MgSO 4 and filtered, and the solvent was evaporated.The crude product thus isolated was purified by flash column chromatography on silica gel (eluent: dichloromethane/acetone = 20:1 to dichloromethane/acetone = 10:1) to afford compound 2 (85.0 mg, 0.125 mmol) as a pale yellow solid with a yield of 32%. 1

Molecular Designs
1,6-Diphenylpyrene-based, unsymmetric cyclophane 1 and the linear analogue 2 are shown in Schemes 1 and 2. 1,6-Disubstituted pyrene derivatives are known to show emissions with high quantum yields [25,[38][39][40].Cyclophane 3 (Figure 1) was previously investigated in the course of our studies on luminescent cyclophanes [25].The thermodynamically stable state of 3 at r.t. is a crystalline phase, though kinetic trapping can induce a supercooled nematic phase at r.t.Relatively large, planar 1,6-bis(phenylethynyl)pyrene moiety permits cyclophane 3 to form a closed-packed molecular arrangement.Therefore, 1,6-diphenylpyrene was used as the luminescent core of 1, because steric hindrance between protons of the pyrene group and adjacent phenyl groups would disturb the closed-packed arrangement of the luminescent groups.As in the case of 3, 1,5-disubstituted naphthalene featuring hexaethylene glycol chains was introduced to achieve the cyclic structure of 1.
phase, though kinetic trapping can induce a supercooled nematic phase at r.t.. Relatively large, planar 1,6-bis(phenylethynyl)pyrene moiety permits cyclophane 3 to form a closed-packed molecular arrangement.Therefore, 1,6-diphenylpyrene was used as the luminescent core of 1, because steric hindrance between protons of the pyrene group and adjacent phenyl groups would disturb the closed-packed arrangement of the luminescent groups.As in the case of 3, 1,5-disubstituted naphthalene featuring hexaethylene glycol chains was introduced to achieve the cyclic structure of 1.

LC Properties
As expected, cyclophane 1 shows a nematic LC phase at r.t. and exhibits sky-blue photoluminescence under excitation light of 365 nm.The characteristic schlieren texture of a nematic phase appears on the polarized optical microscopic observation at r.t.(Figure 2).DSC measurements clarified the phase transition behavior of cyclophane 1 (Figure 3).A phase transition from isotropic

LC Properties
As expected, cyclophane 1 shows a nematic LC phase at r.t. and exhibits sky-blue photoluminescence under excitation light of 365 nm.The characteristic schlieren texture of a nematic phase appears on the polarized optical microscopic observation at r.t.(Figure 2).DSC measurements clarified the phase transition behavior of cyclophane 1 (Figure 3).A phase transition from isotropic to nematic was observed at 57.6 • C on cooling, and further cooling results in a glass transition at −15.1 • C. In contrast with unsymmetric cyclophanes investigated in our previous studies [23][24][25], no transitions to crystalline phases appear on the heating DSC traces.As shown in Figure 4, no clear peaks were observed in the X-ray diffraction pattern obtained from cyclophane 1 at r.t., which coincides with the fact that cyclophane 1 exhibits the nematic LC phase at r.t.In contrast to 1 with a cyclic structure, acyclic compound 2 shows a transition to a crystalline phase at 80 • C, and no LC phases appear on cooling (Figure S1, in the Supplementary Materials).In the case of compound 3, the nematic-crystalline phase transition was observed at 67.4 • C on the cooling DSC trace [25].These results unambiguously indicated that the unsymmetric cyclic structure is vital for inducing low-ordered liquid crystallinity.Furthermore, the non-planar character of the luminophore of 1 that results from steric hindrance between protons of the pyrene and phenyl groups would prevent crystallization.In contrast with unsymmetric cyclophanes investigated in our previous studies [23][24][25], no transitions to crystalline phases appear on the heating DSC traces.As shown in Figure 4, no clear peaks were observed in the X-ray diffraction pattern obtained from cyclophane 1 at r.t., which coincides with the fact that cyclophane 1 exhibits the nematic LC phase at r.t..In contrast to 1 with a cyclic structure, acyclic compound 2 shows a transition to a crystalline phase at 80 C, and no LC phases appear on cooling (Figure S1, in the Supplementary Materials).In the case of compound 3, the nematic-crystalline phase transition was observed at 67.4 C on the cooling DSC trace [25].These results unambiguously indicated that the unsymmetric cyclic structure is vital for inducing lowordered liquid crystallinity.Furthermore, the non-planar character of the luminophore of 1 that results from steric hindrance between protons of the pyrene and phenyl groups would prevent crystallization.

Absorption and Photoluminescence Properties
Absorption and photoluminescence spectroscopic measurements were performed to obtain photophysical properties of compounds 1 and 2 in solution (Figure 5).The linear compound 2

Absorption and Photoluminescence Properties
Absorption and photoluminescence spectroscopic measurements were performed to obtain photophysical properties of compounds 1 and 2 in solution (Figure 5).The linear compound 2

Absorption and Photoluminescence Properties
Absorption and photoluminescence spectroscopic measurements were performed to obtain photophysical properties of compounds 1 and 2 in solution (Figure 5).The linear compound 2 displays the absorption band corresponding to a 1,6-diphenylpyrene group between 300 and 400 nm, with a molar extinction coefficient of 3.8 × 10 4 L mol −1 cm −1 at 360 nm (Figure 5a, black line).The absorption band of 1 in chloroform shows a slight red-shift in comparison with that of the chloroform solution of 2, suggesting that feeble ground state electronic interactions between the pyrene and naphthalene moieties occur in solution (Figure 5a, blue line).The increase in the absorption between 280 and 330 nm is attributed to the naphthalene group of 1. Compound 2 in chloroform displays the emission spectrum with a peak at 409 nm and shoulders around 430 and 470 nm (Figure 5b, black line).The emission spectrum recorded for the chloroform solution of 1 is almost identical to that of the chloroform solution of 2, implying that the photoluminescence from cyclophane 1 is a monomer emission.This is supported by the emission lifetime measurements for chloroform solutions of 1 and 2. As shown in Figure 6, the emission decay profile of 1 in chloroform is identical to that of the chloroform solution of 2. Both profiles can be fitted with a single exponential decay function, and the calculated emission lifetimes of 1 and 2 in chloroform are 1.9 and 1.8 ns, respectively.The fluorescence quantum yield of 1 in chloroform (Φ = 0.68) is also similar to that of compound 2 in the same solvent (Φ = 0.67).
emission.This is supported by the emission lifetime measurements for chloroform solutions of 1 and 2. As shown in Figure 6, the emission decay profile of 1 in chloroform is identical to that of the chloroform solution of 2. Both profiles can be fitted with a single exponential decay function, and the calculated emission lifetimes of 1 and 2 in chloroform are 1.9 and 1.8 ns, respectively.The fluorescence quantum yield of 1 in chloroform (Φ = 0.68) is also similar to that of compound 2 in the same solvent (Φ = 0.67).

Photoluminescence Properties of 1 in the Nematic Phase
Photoluminescence properties of 1 in the nematic phase were also investigated.The emission spectrum presents peaks at 452 and 469 nm and has a shoulder around 500 nm (Figure 7).The emission spectral feature is significantly different from that of the chloroform solution of 1 (Figure 5b), indicating that emission species other than a monomer dominate the former emission character.This is supported by the fact that the emission decay profile recorded for the nematic phase could be fitted with a multi-exponential decay function (Figure 8).A longer emission lifetime of 23 ns, as well as shorter ones (1.0, 3.1, and 8.0 ns) were obtained.The newly observed emission lifetimes would be ascribed to assembled luminophores, because the luminophore of cyclophane 1 can form various emission.This is supported by the emission lifetime measurements for chloroform solutions of 1 and 2. As shown in Figure 6, the emission decay profile of 1 in chloroform is identical to that of the chloroform solution of 2. Both profiles can be fitted with a single exponential decay function, and the calculated emission lifetimes of 1 and 2 in chloroform are 1.9 and 1.8 ns, respectively.The fluorescence quantum yield of 1 in chloroform (Φ = 0.68) is also similar to that of compound 2 in the same solvent (Φ = 0.67).

Photoluminescence Properties of 1 in the Nematic Phase
Photoluminescence properties of 1 in the nematic phase were also investigated.The emission spectrum presents peaks at 452 and 469 nm and has a shoulder around 500 nm (Figure 7).The emission spectral feature is significantly different from that of the chloroform solution of 1 (Figure 5b), indicating that emission species other than a monomer dominate the former emission character.This is supported by the fact that the emission decay profile recorded for the nematic phase could be fitted with a multi-exponential decay function (Figure 8).A longer emission lifetime of 23 ns, as well as shorter ones (1.0, 3.1, and 8.0 ns) were obtained.The newly observed emission lifetimes would be ascribed to assembled luminophores, because the luminophore of cyclophane 1 can form various

Photoluminescence Properties of 1 in the Nematic Phase
Photoluminescence properties of 1 in the nematic phase were also investigated.The emission spectrum presents peaks at 452 and 469 nm and has a shoulder around 500 nm (Figure 7).The emission spectral feature is significantly different from that of the chloroform solution of 1 (Figure 5b), indicating that emission species other than a monomer dominate the former emission character.This is supported by the fact that the emission decay profile recorded for the nematic phase could be fitted with a multi-exponential decay function (Figure 8).A longer emission lifetime of 23 ns, as well as shorter ones (1.0, 3.1, and 8.0 ns) were obtained.The newly observed emission lifetimes would be ascribed to assembled luminophores, because the luminophore of cyclophane 1 can form various arrangements in the nematic phase, reflecting low-ordered LC properties.Indeed, the absorption band between 350 and 400 nm of cyclophane 1 in the nematic phase was red-shifted and broadened compared with that of the chloroform solution of 1 (Figure S2).This result indicated that ground state electronic interactions occur between adjacent luminophores in the condensed states.It is noteworthy that cyclophane 1 shows a relatively high emission quantum yield of 0.51 in the nematic phase at r.t.arrangements in the nematic phase, reflecting low-ordered LC properties.Indeed, the absorption band between 350 and 400 nm of cyclophane 1 in the nematic phase was red-shifted and broadened compared with that of the chloroform solution of 1 (Figure S2).This result indicated that ground state electronic interactions occur between adjacent luminophores in the condensed states.It is noteworthy that cyclophane 1 shows a relatively high emission quantum yield of 0.51 in the nematic phase at r.t..

Conclusions
In summary, a new unsymmetric cyclophane having a 1,6-diphenylpyrene group was found to show a nematic phase at r.t.. Cyclophane 1 shows strong blue photoluminescence ascribed to the monomer emission in chloroform, whereas the emissions from the nematic phase are composed of various emission species that result from luminophore assemblies.The present result indicated that the introduction of a cyclic structure into luminophores that are known to exhibit high photoluminescence quantum yields is a reliable way to achieve a nematic LC phase at r.t..Because nematic liquid crystals with high emission quantum efficiencies have potential applications in sophisticated optoelectronic devices, development of other luminophores with a cyclic structure is ongoing in our group.

Conclusions
In summary, a new unsymmetric cyclophane having a 1,6-diphenylpyrene group was found to show a nematic phase at r.t.Cyclophane 1 shows strong blue photoluminescence ascribed to the monomer emission in chloroform, whereas the emissions from the nematic phase are composed of various emission species that result from luminophore assemblies.The present result indicated that the introduction of a cyclic structure into luminophores that are known to exhibit high photoluminescence quantum yields is a reliable way to achieve a nematic LC phase at r.t.Because nematic liquid crystals with high emission quantum efficiencies have potential applications in sophisticated optoelectronic devices, development of other luminophores with a cyclic structure is ongoing in our group.Funding: This research was funded by the Japan Society for the Promotion of Science, Kakenhi grant number JP18H02024.
observed at 57.6 C on cooling, and further cooling results in a glass transition at −15.1 C.

Figure 2 .
Figure 2. Polarized optical microscopic image of pyrene-based cyclophane 1 at r.t. in the absence of a coverslip.Scale bar: 20 m.

Figure 3 .
Figure 3. DSC traces of cyclophane 1 on heating and cooling.Tpeak: transition temperature taken at the top point of the transition peaks; Tg: grass transition temperature; H: transition enthalpy.G: glassy; N: nematic; Iso: isotropic.Scanning rate was 5 C min -1 .

Figure 2 .
Figure 2. Polarized optical microscopic image of pyrene-based cyclophane 1 at r.t. in the absence of a coverslip.Scale bar: 20 µm.

Figure 2 .
Figure 2. Polarized optical microscopic image of pyrene-based cyclophane 1 at r.t. in the absence of a coverslip.Scale bar: 20 m.

Figure 3 .
Figure 3. DSC traces of cyclophane 1 on heating and cooling.Tpeak: transition temperature taken at the top point of the transition peaks; Tg: grass transition temperature; H: transition enthalpy.G: glassy; N: nematic; Iso: isotropic.Scanning rate was 5 C min -1 .

Figure 3 .
Figure 3. DSC traces of cyclophane 1 on heating and cooling.T peak : transition temperature taken at the top point of the transition peaks; T g : grass transition temperature; ∆H: transition enthalpy.G: glassy; N: nematic; Iso: isotropic.Scanning rate was 5 • C min -1 .

Figure 2 .
Figure 2. Polarized optical microscopic image of pyrene-based cyclophane 1 at r.t. in the absence of a coverslip.Scale bar: 20 m.

Figure 3 .
Figure 3. DSC traces of cyclophane 1 on heating and cooling.Tpeak: transition temperature taken at the top point of the transition peaks; Tg: grass transition temperature; H: transition enthalpy.G: glassy; N: nematic; Iso: isotropic.Scanning rate was 5 C min -1 .

Figure 8 .
Figure 8. Emission decay profile of 1 in the nematic phase at r.t.The profile was monitored at 450 nm (λ ex = 365 nm).