A One-Dimensional Coordination Polymer Containing Cyclic [ Ag 4 ] Clusters Supported by a Hybrid Pyridine and Thioether Functionalized 1 , 2 , 3-Triazole

A pyridine and thioether co-supported triazole ligand L (L = 2-((4-(3-(cyclopentylthio)propyl) -1H-1,2,3-triazol-1-yl)methyl)pyridine) has been synthesized using the CuAAC click reaction. This ligand supports the formation of a thermally stable, one-dimensional coordination polymer [L2Ag4]n·4n(BF4) (1) possessing a cationic polymeric structure with [Ag4] metallomacrocycles, in which the ligand L displays chelate/bridging coordination modes using all four potential donors of nitrogen (N) and thioether (S). The dominant direction of the prism crystals of 1 aligns with the propagation of the chain in the lattice.


Introduction
Coordination polymers are well-defined molecular materials consisting of metal centers and organic ligands, and have received considerable attention because of their fascinating crystalline structures and wide range of applications, including as luminescent sensors, catalysts, and porous and electrochemical materials [1][2][3][4][5].The formation and dimensionality of coordination polymers are governed by the coordination number and geometry of the metal centers and the nature and arrangement of donor atoms on the ligand.Reaction conditions-such as temperature, solvent, metal-to-ligand ratio, and counter ions-also influence coordination diversity [6,7].Many synthetic chemists have dedicated themselves to the construction of new organic ligands and coordination polymers, from which to discover the principles of controlled self-assembly.Significant effort has been devoted to the complementarity of metal precursor and rationally designed organic ligands [8][9][10][11][12].Ag(I) with d 10 electronic configuration, multiple coordination geometries and luminescence resulting from Ag• • • Ag interactions is especially attractive to crystal engineers [13][14][15][16][17]. Ag(I) is a soft metal and so favored to N, O, and S donor ligands [18][19][20][21].N-heterocyclic pyridine, pyrazole, imidazole, triazole, and multidentate ligands have been employed to support Ag(I) ions and clusters.We have a particular interest in hybrid ligands with different chemical donors that demonstrate hemilability for the design of new functional materials [22,23].Schiff-base-, pyrazole-, and thioether-functionalized pyridines have been used to construct magnetic and luminescent coordination polymers of Mn II , Ni II , Cu II/I , and Zn II [24][25][26][27][28][29][30].The copper-catalyzed azide-alkyne cycloaddition (CuAAC) reactions provide access to versatile, multidirectional 1,2,3-triazole ligands and we have used these ligands to make copper-iodide cluster-based coordination compounds and study the relationship between lattice weak interactions and crystal growth [31,32].Different substituents on the ligands can be used to tune the possible coordination modes and these weak lattice interactions.The distance between two coordination sites (e.g., thioether (S) and pyridine-triazole NN groups) is also appropriate for stabilizing different sized copper-iodide clusters.As a continuation of this work, we herein report a new pyridine and thioether supported 1,2,3-triazole ligand L synthesized using the click reaction.This neutral ligand employs pyridine-triazole chelate-bridging and thioether bridging modes to stabilize Ag(I) centers and form a polymeric, cationic chain with cyclic [Ag 4 ] clusters.

Materials and Methods
All reagents were used as received.Infrared spectra were obtained on a PerkinElmer Spectrum 2000 FT-IR spectrometer from a sample in KBr disc.Elemental analyses were performed on a thermo electron corporation flash EA 1112 series analyzer.Electrospray ionization mass spectrometry (ESI-MS) was recorded in positive ion mode using a Shimadzu LCMS-IT-TOF mass spectrometer.UV-vis absorption spectrum was recorded on a Shimadzu UV-2501PC UV-vis recording spectrophotometer.Photoluminescence spectrum was measured on a Shimadzu RF-5301 PC spectrofluorophotometer. Powder X-ray diffraction data was collected on a Bruker D8 Advance X-ray diffractometer with Cu-Kα radiation (λ = 1.54056Å).Thermogravimetric analysis (TGA) was carried out in an air stream using a TA Instruments TGA Q500 analyzer with a heating rate of 20 • C per min.

Synthesis
Sodium azide is potentially explosive.Only micro-scaled reactions should be performed.The alkyne precursor (4-pentyn-1-ylthio)-cyclopentane was prepared following literature procedures for thioether formation [28,32].The crude alkyne was placed in a round bottom flask containing 2-(chloromethyl)pyridine hydrochloride (328 mg, 2 mmol), Na 2 CO 3 (210 mg, 2 mmol), NaN 3 (156 mg, 2.5 mmol), CuI (23 mg, 0.12 mmol), and CH 3 OH/H 2 O (1:1 v:v, 6 mL) (Scheme 1).The reaction was stirred at 50 • C for 24 h.The residue was extracted with ethyl acetate (150 mL) and the organic layer was washed with water (3 × 20 mL), dried (with anhydrous Mg 2 SO 4 ) and concentrated by rotary evaporator at 60 • C under vacuum.Column chromatography on silica gel with hexane/ethyl acetate (2:1 v:v) as eluent produced a band at R f = 0.1 that was collected and the solvent removed by rotary evaporator at 40 • C under vacuum.The product (L) was a pale yellow oil.Yield: 330 mg, 55%.Complex 1 was prepared by mixing a methanol solution (5 mL) of ligand L (151 mg, 0.5 mmol) and a methanol solution (5 mL) of AgBF4 (195 mg, 1 mmol).Single crystals were obtained by slow evaporation of the solvent over one week at room temperature (Scheme 2).The product was collected by filtration, washed with methanol and diethyl ether, and dried in vacuum oven for overnight at 60 °C.Yield: 270 mg, 78%.The powder sample of complex 1 is grey and no obvious solid-state luminescence was observed.Single crystals of 1 are prisms with a relative long axis.Anal

UV-Vis and Photoluminescent Spectra of Ligand L
An ethanol solution of ligand L absorbed UV-vis light at 203 nm and between 240-280 nm with a maximum at about 260 nm (Figure 1a) and exhibited a broad emission between 400-500 nm with a maximum at 442 nm upon excitation at 358 nm.Neat liquid gave a blue emission under UV 365 nm light.(Figure 1b, insert) Coordination polymer 1 was synthesized by the reaction of L and AgBF4 in methanol at room temperature (Scheme 2).IR spectroscopy indicated characteristic absorption by the BF4 − anion.The polymeric structure may be disassociated into small fragments (e.g., [LAg] + and [L2Ag] + ) in solution which were detected by ESI-MS.Complex 1 was prepared by mixing a methanol solution (5 mL) of ligand L (151 mg, 0.5 mmol) and a methanol solution (5 mL) of AgBF 4 (195 mg, 1 mmol).Single crystals were obtained by slow evaporation of the solvent over one week at room temperature (Scheme 2).The product was collected by filtration, washed with methanol and diethyl ether, and dried in vacuum oven for overnight at 60 Complex 1 was prepared by mixing a methanol solution (5 mL) of ligand L (151 mg, 0.5 mmol) and a methanol solution (5 mL) of AgBF4 (195 mg, 1 mmol).Single crystals were obtained by slow evaporation of the solvent over one week at room temperature (Scheme 2).The product was collected by filtration, washed with methanol and diethyl ether, and dried in vacuum oven for overnight at 60 °C.Yield: 270 mg, 78%.The powder sample of complex 1 is grey and no obvious solid-state luminescence was observed.Single crystals of 1 are prisms with a relative long axis.Anal.Calcd.for C32H44Ag4B4F16N8S2 (1383.

UV-Vis and Photoluminescent Spectra of Ligand L
An ethanol solution of ligand L absorbed UV-vis light at 203 nm and between 240-280 nm with a maximum at about 260 nm (Figure 1a) and exhibited a broad emission between 400-500 nm with a maximum at 442 nm upon excitation at 358 nm.Neat liquid gave a blue emission under UV 365 nm light.(Figure 1b, insert) Coordination polymer 1 was synthesized by the reaction of L and AgBF4 in methanol at room temperature (Scheme 2).IR spectroscopy indicated characteristic absorption by the BF4 − anion.The polymeric structure may be disassociated into small fragments (e.g., [LAg] + and [L2Ag] + ) in solution which were detected by ESI-MS.

UV-Vis and Photoluminescent Spectra of Ligand L
An ethanol solution of ligand L absorbed UV-vis light at 203 nm and between 240-280 nm with a maximum at about 260 nm (Figure 1a) and exhibited a broad emission between 400-500 nm with a maximum at 442 nm upon excitation at 358 nm.Neat liquid gave a blue emission under UV 365 nm light.(Figure 1b a maximum at about 260 nm (Figure 1a) and exhibited a broad emission between 400-500 nm with a maximum at 442 nm upon excitation at 358 nm.Neat liquid gave a blue emission under UV nm light.(Figure 1b, insert) Coordination polymer 1 was synthesized by the reaction of L and AgBF4 in methanol at room temperature (Scheme 2).IR spectroscopy indicated characteristic absorption by the BF4 − anion.The polymeric structure may be disassociated into small fragments (e.g., [LAg] + and [L2Ag] + ) in solution which were detected by ESI-MS.

Molecular Structure of Complex 1
Coordination polymer 1 crystallized in a monoclinic crystal system with space group P 2 1 /c.There is one neutral ligand L, two cationic Ag(I) centers and two lattice BF

Powder XRD and TGA
The experimental powder X-ray diffraction pattern for complex 1 showed good agreement with its simulated pattern determined from the single-crystal XRD experiment, supporting its phase purity (Figure 3).Thermogravimetric analysis (TGA) of 1 was conducted from room temperature to 900 °C under an air flow with a heating rate of 20 °C per min (Figure 4).Complex 1 is stable to about 230 °C.Crystals 2018, 8, 16 5 of 8

Powder XRD and TGA
The experimental powder X-ray diffraction pattern for complex 1 showed good agreement with its simulated pattern determined from the single-crystal XRD experiment, supporting its phase purity (Figure 3).Thermogravimetric analysis (TGA) of 1 was conducted from room temperature to 900 • C under an air flow with a heating rate of 20 • C per min (Figure 4).

Conclusions
In summary, a pyridine and thioether functionalized 1,2,3-triazole ligand with a relatively long methylene bridge ((CH2)3) between NN and S donors was synthesized using the CuAAC click reaction.The reaction of ligand L and AgBF4 afforded a novel, thermally stable polymeric chain structure with [Ag4] metallomacrocyclics.The propagation of these chains in the lattice aligns with the dominant growth direction of the prism crystals.The observation of two types of Ag(I) coordination geometries (linear and trigonal planar) further emphasizes the diversity of Ag(I) coordination chemistry.

Conclusions
In summary, a pyridine and thioether functionalized 1,2,3-triazole ligand with a relatively long methylene bridge ((CH2)3) between NN and S donors was synthesized using the CuAAC click reaction.The reaction of ligand L and AgBF4 afforded a novel, thermally stable polymeric chain structure with [Ag4] metallomacrocyclics.The propagation of these chains in the lattice aligns with the dominant growth direction of the prism crystals.The observation of two types of Ag(I) coordination geometries (linear and trigonal planar) further emphasizes the diversity of Ag(I)

Conclusions
In summary, a pyridine and thioether functionalized 1,2,3-triazole ligand with a relatively long methylene bridge ((CH 2 ) 3 ) between NN and S donors was synthesized using the CuAAC click reaction.The reaction of ligand L and AgBF 4 afforded a novel, thermally stable polymeric chain structure with [Ag 4 ] metallomacrocyclics.The propagation of these chains in the lattice aligns with the dominant growth direction of the prism crystals.The observation of two types of Ag(I) coordination geometries (linear and trigonal planar) further emphasizes the diversity of Ag(I) coordination chemistry.

Figure 1 .
Figure 1.UV-vis (a) and excitation (dotted line) and emission (solid line) (b) spectra of ligand L in ethanol (0.1 M).(The inset images are ligand L in a quartz cuvette under normal and 365 nm lights, respectively).

Figure 1 .
Figure 1.UV-vis (a) and excitation (dotted line) and emission (solid line) (b) spectra of ligand L in ethanol (0.1 M).(The inset images are ligand L in a quartz cuvette under normal and 365 nm lights, respectively).
, insert) Coordination polymer 1 was synthesized by the reaction of L and AgBF 4 in methanol at room temperature (Scheme 2).IR spectroscopy indicated characteristic absorption by the BF 4 − anion.The polymeric structure may be disassociated into small fragments (e.g., [LAg] + and [L 2 Ag] + ) in solution which were detected by ESI-MS.

Figure 1 .
Figure 1.UV-vis (a) and excitation (dotted line) and emission (solid line) (b) spectra of ligand L in ethanol (0.1 M).(The inset images are ligand L in a quartz cuvette under normal and 365 nm lights, respectively).

Figure 1 .
Figure 1.UV-vis (a) and excitation (dotted line) and emission (solid line) (b) spectra of ligand L in ethanol (0.1 M).(The inset images are ligand L in a quartz cuvette under normal and 365 nm lights, respectively).

4 − 7 3. 3 .
anions in the crystallographic asymmetric unit.(Figure 2a) Ag1 and Ag2 possess three-coordinated trigonal planer and two-coordinated linear geometries, respectively.Ag1 is surrounded by two chelating N donors from pyridine and triazole of ligand L and one bridging S donor from another ligand L. Ag2 is coordinated by one 3 -N triazole of ligand L and one bridging S donor from another ligand L. These two S donors also bridge neighboring Ag1-Ag2 centers to form a [Ag 4 ] metallomacrocycle.The cyclic [Ag 4 ] units are further linked by double ligands and extend along the short b axis, which aligns with the dominant direction of the prism-shaped single crystals.(Figure 2c,d) The polymeric chains are parallel to each other in the lattice (Figure 2b).The counterions BF 4 − occupy the cavities created by the cationic polymeric chains.The Ag1• • • Ag2 distances are 4.28 and 4.04 Å in the [Ag 4 ] metallomacrocycle.The shortest Ag• • • Ag distance of neighboring [Ag 4 ] units is 6.06 Å.The shortest Ag• • • Ag distance of neighboring chains is 7.60 Å. Crystals 2018, 8, 16 4 of Molecular Structure of Complex 1 Coordination polymer 1 crystallized in a monoclinic crystal system with space group P 21/c.There is one neutral ligand L, two cationic Ag(I) centers and two lattice BF4 − anions in the crystallographic asymmetric unit.(Figure 2a) Ag1 and Ag2 possess three-coordinated trigonal planer and two-coordinated linear geometries, respectively.Ag1 is surrounded by two chelating N donors from pyridine and triazole of ligand L and one bridging S donor from another ligand L. Ag2 is coordinated by one 3′-Ntriazole of ligand L and one bridging S donor from another ligand L. These two S donors also bridge neighboring Ag1-Ag2 centers to form a [Ag4] metallomacrocycle.The cyclic [Ag4] units are further linked by double ligands and extend along the short b axis, which aligns with the dominant direction of the prism-shaped single crystals.(Figure 2c,d) The polymeric chains are parallel to each other in the lattice (Figure 2b).The counterions BF4 − occupy the cavities created by the cationic polymeric chains.The Ag1⋯Ag2 distances are 4.28 and 4.04 Å in the [Ag4] metallomacrocycle.The shortest Ag⋯Ag distance of neighboring [Ag4] units is 6.06 Å.The shortest Ag⋯Ag distance of neighboring chains is 7.60 Å.

Figure 2 .
Figure 2. (a) Cationic and polymeric chain structure in 1.(b) Packing structure in 1. (BF4 − anions are removed for clarity) (c,d) Single crystal indexes in different orientations of 1.

Figure 2 .
Figure 2. (a) Cationic and polymeric chain structure in 1.(b) Packing structure in 1. (BF 4 − anions are removed for clarity) (c,d) Single crystal indexes in different orientations of 1.

of 7 Figure 3 .
Figure 3. Powder XRD patterns of 1. (T = theoretical profile referenced to the experimentally determined single-crystal XRD pattern; E = experimental data).

Figure 3 .
Figure 3. Powder XRD patterns of 1. (T = theoretical profile referenced to the experimentally determined single-crystal XRD pattern; E = experimental data).