Synthesis, Characterization and Catalytic Performance of Well-Ordered Crystalline Heteroatom Mesoporous MCM-41

Mesoporous heteroatom molecular sieve MCM-41 bulk crystals with the crystalline phase were synthesized via a one-step hydrothermal method using an ionic complex as template. The ionic complex template was formed by interaction between cetyltrimethylammonium ions and metal complex ion [M(EDTA)]2− (M = Co or Ni)]. The materials were characterized by X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy, N2 adsorption-desorption isotherms, and X-ray absorption fine structure spectroscopy. The results showed that the materials possess a highly-ordered mesoporous structure with a crystalline phase and possess highly uniform ordered arrangement channels. The structure is in the vertical cross directions with a crystalline size of about 12 μm and high specific surface areas. The metal atoms were incorporated into the zeolite frameworks in the form of octahedral coordinate and have a uniform distribution in the materials. The amount of metal complexes formed by metal ion and EDTA is an essential factor for the formation of the vertical cross structure. Compared to Si-MCM-41, the samples exhibited better conversion and higher selectivity for cumene cracking.


Introduction
By virtue of their high thermal and hydrothermal stability, microporous zeolites are widely used in industries as heterogeneous catalysts, particularly as solid acid catalysts in the fields of oil refining and petrochemistry [1].Although the micropores of zeolites have often been described as having excellent potential for chemical functions, their pore size often limits the reaction rate and thus have an adverse effect on practical chemical processes [2][3][4].In 1992, in an attempt to overcome this problem, Mobil Oil Corporation synthesized a family of mesoporous solids named M41s [5] which possess an ordered arrangement of larger pores with diameters of 2-10 nm.However, the use of these materials as catalysts is hampered by their relatively low thermal stability and weak acid strength [6,7].Therefore, it would be of great interest to synthesize a new type of material combining the advantages of both mesoporous molecular sieves and zeolites [8,9].Only a few studies have been published to date; for example, Karlsson et al. prepared MFI/MCM-41 composites using two templates (C 6 H 13 (CH 3 ) 3 NBr and C 14 H 29 (CH 3 ) 3 NBr), and optimized the template concentrations and reaction temperature [10].In previous studies, we have reported the synthesis and characterization of composite molecular sieves Crystals 2017, 7, 89 2 of 11 M 1 -MFI/M 2 -MCM-41 (M 1 , M 2 = Ni, Co) and their catalytic properties for the hydrocracking of residual oil [11] and the preparation of micro-mesoporous FeCo-MFI/MCM-41 composites which gave a clear improvement in the hydrocracking of residual oil [12].However, the resulting materials are composites of zeolite crystallites embedded in a disordered mesoporous matrix.Kaliaguine et al. described a general method for the production of a new type of material with semi-crystalline zeolite mesopore walls [13].Other attempts to crystallize the mesopore walls of mesostructure materials have resulted in the formation of materials with increased thermal stability and catalytic activity.For example, ITQ zeolites having a partially crystalline bimodal pore system with a combination of micropores and mesopores have been synthesized by delaminating the layered zeolite precursors MCM-22 and ferrierite [14].However, none of these techniques yields a regular distribution of mesopores, let alone an ideal channel system of mesopores structurally connected with the regular micropores of the zeolite.Jiang et al. reported the synthesis of zeolite ITQ-43, which features a structurally hierarchical system of connected mesopores and micropores.Although high-resolution transmission electron microscopy (HRTEM) did not show the mesopore features, evidence for the presence of mesopores was provided by automated electron diffraction tomography [15].W. Chaikittisilp recently demonstrated a new approach for the construction of hierarchically organized zeolites by sequential intergrowth; for the first time, a complex and unusual morphology was observed for MFI zeolites [16].
In this paper, M-MCM-41 bulk crystal heteroatom molecular sieves with crystalline phase have been synthesized using a direct hydrothermal method.The materials possess a crystalline phase and highly uniform ordered arrangement channels.This is a new type of crystalline mesoporous molecular sieve.Three-dimensional crystal mesoporous MCM-41 was obtained in typical synthesis conditions.

Results
The samples were labeled as Cry-Ni and Cry-Co, and the metal heteroatom contents of the samples measured by inductively coupled plasma (ICP) are listed in Table 1.Low angle XRD patterns of the samples are presented in Figure 1.All samples show an intense broad diffraction peak at very low 2θ angle of 0.7 • -1.7 • , with an overlapping broader feature at 2 • -7 • , which can be respectively attributed to the (1 0 0) diffraction peak and the overlapping pair of (1 1 0) and (2 0 0) diffraction peaks, indicating that the samples have good structural order and the obvious mesoporous structure of MCM-41 [17].
The particle size and shape of the samples were investigated using SEM, and the images are shown in Figure 2a,b.The results show that the samples have well-defined morphologies with a crystal structure (corresponding to the XRD results), and the crystalline sizes are about 12 µm with a uniform distribution.It can be seen from the images that the two samples have good dispersion.In addition, the materials possess a structure in the vertical cross direction.This is determined presumably by the structure of the metal complex.The SEM-mappings of the samples are also shown in Figure 2a*,b*, which display the composition and distribution of elements in the samples.It is clear that all samples (Cry-Ni and Cry-Co) have uniform distribution of elements, and the metal atoms (Ni and Co) were highly dispersed in the materials.It can be seen from Figure 2e,f that the two samples have good dispersion.After grinding with a ball mill, the samples were tested by HRTEM, and the results are shown in Figure 2c,d.The images indicate that the materials exhibit a uniform pore size with a highly-ordered pore structure and the characteristic long-range ordered symmetry of a mesophase.The ordered mesopores of the crystals can be easily observed in the HRTEM images.
with a highly-ordered pore structure and the characteristic long-range ordered symmetry of a mesophase.The ordered mesopores of the crystals can be easily observed in the HRTEM images.The handbook of X-ray photoelectron spectroscopy (XPS) showed the binding energy of NiO and CoO.The binding energy peak of NiO was between 854 eV and 855 eV.The peak of CoO and Co3O4 centered at 780 eV. Figure 3 shows the XPS spectra of Cry-Ni and Cry-Co samples, and the insets are the de-convoluted Ni 2p3/2 and Co 2p3/2 spectra.As shown in Figure 3a, there is a predominant peak centered at 855.95 eV [18], indicating the strong interaction between nickel atom and the silica base, suggesting the nickel atoms incorporating into the silica framework [19], which corroborates the previous results; a peak centered at 781.55 eV in the Figure 3b is the characteristic peak of Co 2p2/3 [20], indicating that cobalt atoms were also incorporating into the silica framework.Figure 4 illustrates the X-ray absorption near-edge structure (XANES) spectra of Cry-Ms.The corresponding spectra for metal oxides are given for comparison.The XANES pre-edge peak is attributed to the 1s-3d dipolar forbidden transition [21].Principally, this 1s-3d forbidden transition gains additional intensity when the metal center is in a non-centrally symmetric environment through mixing of 3d and 4p orbitals caused by the breakdown of inversion symmetry due to the structure distortion.Figure 4a illustrates the XANES spectra of NiO and Cry-Ni.The nickel atoms in The handbook of X-ray photoelectron spectroscopy (XPS) showed the binding energy of NiO and CoO.The binding energy peak of NiO was between 854 eV and 855 eV.The peak of CoO and Co 3 O 4 centered at 780 eV. Figure 3 shows the XPS spectra of Cry-Ni and Cry-Co samples, and the insets are the de-convoluted Ni 2p3/2 and Co 2p3/2 spectra.As shown in Figure 3a, there is a predominant peak centered at 855.95 eV [18], indicating the strong interaction between nickel atom and the silica base, suggesting the nickel atoms incorporating into the silica framework [19], which corroborates the previous results; a peak centered at 781.55 eV in the Figure 3b is the characteristic peak of Co 2p2/3 [20], indicating that cobalt atoms were also incorporating into the silica framework.The handbook of X-ray photoelectron spectroscopy (XPS) showed the binding energy of NiO and CoO.The binding energy peak of NiO was between 854 eV and 855 eV.The peak of CoO and Co3O4 centered at 780 eV. Figure 3 shows the XPS spectra of Cry-Ni and Cry-Co samples, and the insets are the de-convoluted Ni 2p3/2 and Co 2p3/2 spectra.As shown in Figure 3a, there is a predominant peak centered at 855.95 eV [18], indicating the strong interaction between nickel atom and the silica base, suggesting the nickel atoms incorporating into the silica framework [19], which corroborates the previous results; a peak centered at 781.55 eV in the Figure 3b is the characteristic peak of Co 2p2/3 [20], indicating that cobalt atoms were also incorporating into the silica framework.Figure 4 illustrates the X-ray absorption near-edge structure (XANES) spectra of Cry-Ms.The corresponding spectra for metal oxides are given for comparison.The XANES pre-edge peak is attributed to the 1s-3d dipolar forbidden transition [21].Principally, this 1s-3d forbidden transition gains additional intensity when the metal center is in a non-centrally symmetric environment through mixing of 3d and 4p orbitals caused by the breakdown of inversion symmetry due to the structure distortion.Figure 4a illustrates the XANES spectra of NiO and Cry-Ni.The nickel atoms in  The corresponding spectra for metal oxides are given for comparison.The XANES pre-edge peak is attributed to the 1s-3d dipolar forbidden transition [21].Principally, this 1s-3d forbidden transition gains additional intensity when the metal center is in a non-centrally symmetric environment through mixing of 3d and 4p orbitals caused by the breakdown of inversion symmetry due to the structure distortion.Figure 4a  Extended X-ray absorption fine structure (EXAFS) spectroscopy [22] is one of the most powerful structural characterization methods, especially for interface-confined effects, due to its sensitivity to the three-dimensional short-range order (typically 0-8 Å) and chemical state, including near-neighbor species, distance (R), coordination number (N), and disorder in bond distance (σ 2 ). Figure 4a 2.
The XAFS results indicated that each metal center has a coordination number six with an octahedral coordination with the surrounding atoms.The bonds of M-O-Si present in the Cry-Ms samples, and this suggests that the metal atoms are incorporated in the silica framework rather than existing as a separate oxide phase.Extended X-ray absorption fine structure (EXAFS) spectroscopy [22] is one of the most powerful structural characterization methods, especially for interface-confined effects, due to its sensitivity to the three-dimensional short-range order (typically 0-8 Å) and chemical state, including nearneighbor species, distance (R), coordination number (N), and disorder in bond distance (σ 2 ).  2.
The XAFS results indicated that each metal center has a coordination number six with an octahedral coordination with the surrounding atoms.The bonds of M-O-Si present in the Cry-Ms samples, and this suggests that the metal atoms are incorporated in the silica framework rather than existing as a separate oxide phase.The N 2 adsorption-desorption isotherm method was employed to investigate the pore structure of materials.The isotherms of the samples obtained at −196 • C are illustrated in Figure 5.It shows that the isotherms of the samples are type IV [23] and possess type H1 hysteresis loops.It is indicated that the samples are typical mesoporous materials, exhibiting a sharp characteristic of capillary condensation at intermediate partial pressures (0.3 < P/P 0 < 0.5).In the relative pressure range 0.90-0.99,all samples show another sharp with the increase of the nitrogen adsorption volume, resulting from filling the macropores formed by interparticle spaces and untransformed amorphous silica.The textural properties of samples are listed in Table 1.The pore diameters of the two samples have little difference from each other, due to the different micelle diameter of [(C 4 H 9 ) 4 N][M(EDTA)] caused by the difference radius of heteroatoms Ni 2+ and Co 2+ , which also influences the specific surface area, pore volume, and the pore diameter.The N2 adsorption-desorption isotherm method was employed to investigate the pore structur materials.The isotherms of the samples obtained at −196 °C are illustrated in Figure 5.It show t the isotherms of the samples are type IV [23] and possess type H1 hysteresis loops.It is indicate t the samples are typical mesoporous materials, exhibiting a sharp characteristic of capillar ndensation at intermediate partial pressures (0.3 < P/P0 < 0.5).In the relative pressure range 0.90 9, all samples show another sharp with the increase of the nitrogen adsorption volume, resultin m filling the macropores formed by interparticle spaces and untransformed amorphous silica.Th tural properties of samples are listed in Table 1   The 0.5 g samples of Cry-Ni and Cry-Co were placed in 50 mL 1 mol/L NaOH solution, stirring at room temperature for 2 h, then samples were filtered and dried.The morphological changes of the samples were observed under electron microscope, and the morphology of the samples is shown in Figure 6.The crystal structure of the samples treated by sodium hydroxide solution is shown.The samples covering the surface of the oxide dissolved by the lye treatment, and the crystal exhibits relatively complete form.Mesoporous molecular sieve material by traditional alkali treatment, hole wall collapse phenomenon will appear.In contrast, the crystal structure of metal atoms in the crystalline molecular sieve improves the alkali resistance of the molecular sieve.According to the above results, a possible mechanism was proposed that is revealed as Schem There are two nitrogen atoms and four carboxyl oxygen atoms (marked as A, B, C, D, respectivel the EDTA molecule which can coordinate with the metal ion to form the complex ion [M(EDAT)] ith an octahedral structure.In the chelate ion, the carboxyl oxygen atoms A, B, and two nitroge oms are at a flat surface, and the other two carboxyl oxygen atoms C and D are in the vertic rection but not at a flat surface with the two nitrogen atoms.As the complex solution was adde to the cetyltrimethyl ammonium bromide (CTAB) solution, the ionic associate [M(EDAT)] 2− (CTA + d the special structure micelle would be formed 1).As the micelle suspension was mixe ith the solution of SiO4 4− formed by SiO2 and plenty of sodium hydroxide, SiO4 4− ions would rapid drolyze and polymerize around the micelle which possessed a structure in the vertical cro rection.Additionally, the crystalline mesoporous zeolite precursors would grow along the vertic oss direction in the following hydrothermal process.Because the structure of the [M(EDAT)] mplex is not the same in the vertical cross direction, the micelle structure would not be the same e two directions; this is the main factor causing the sample to have different structures in th fferent directions (Figure 2).A certain amount of the complexes formed by metal ion and EDT as essential in the formation of the structure.Enough [M(EDTA)] 2− could ensure the formation gle structural micelles with the vertical cross structure, which is the prerequisite of the formatio the crystalline zeolite precursors.According to the above results, a possible mechanism was proposed that is revealed as Scheme 1.There are two nitrogen atoms and four carboxyl oxygen atoms (marked as A, B, C, D, respectively) in the EDTA molecule which can coordinate with the metal ion to form the complex ion [M(EDAT)] 2− with an octahedral structure.In the chelate ion, the carboxyl oxygen atoms A, B, and two nitrogen atoms are at a flat surface, and the other two carboxyl oxygen atoms C and D are in the vertical direction but not at a flat surface with the two nitrogen atoms.As the complex solution was added into the cetyltrimethyl ammonium bromide (CTAB) solution, the ionic associate [M(EDAT)] 2− (CTA + ) 2 and the special structure micelle would be formed (Scheme 1).As the micelle suspension was mixed with the solution of SiO According to the above results, a possible mechanism was proposed that is revealed as Scheme 1.There are two nitrogen atoms and four carboxyl oxygen atoms (marked as A, B, C, D, respectively) in the EDTA molecule which can coordinate with the metal ion to form the complex ion [M(EDAT)] 2− with an octahedral structure.In the chelate ion, the carboxyl oxygen atoms A, B, and two nitrogen atoms are at a flat surface, and the other two carboxyl oxygen atoms C and D are in the vertical direction but not at a flat surface with the two nitrogen atoms.As the complex solution was added into the cetyltrimethyl ammonium bromide (CTAB) solution, the ionic associate [M(EDAT)] 2− (CTA + )2 and the special structure micelle would be formed (Scheme 1).As the micelle suspension was mixed with the solution of SiO4 4− formed by SiO2 and plenty of sodium hydroxide, SiO4 4− ions would rapidly hydrolyze and polymerize around the micelle which possessed a structure in the vertical cross direction.Additionally, the crystalline mesoporous zeolite precursors would grow along the vertical cross direction in the following hydrothermal process.Because the structure of the [M(EDAT)] 2− complex is not the same in the vertical cross direction, the micelle structure would not be the same in the two directions; this is the main factor causing the sample to have different structures in the different directions (Figure 2).A certain amount of the complexes formed by metal ion and EDTA was essential in the formation of the structure.Enough [M(EDTA)] 2− could ensure the formation of single structural micelles with the vertical cross structure, which is the prerequisite of the formation of the crystalline zeolite precursors.The catalytic performance of the crystalline molecular sieves for cumene cracking was investigated.The device diagram is shown in Figure 7. Before the reaction, the samples were activated at 300 °C and nitrogen atmosphere for one hour.Reaction conditions were as follows: temperature, 30 °C; nitrogen atmosphere; mass ratio of raw material/catalyst, 100.After a certain reaction time, the The catalytic performance of the crystalline molecular sieves for cumene cracking was investigated.The device diagram is shown in Figure 7. Before the reaction, the samples were activated at 300 • C and nitrogen atmosphere for one hour.Reaction conditions were as follows: temperature, 30 • C; nitrogen atmosphere; mass ratio of raw material/catalyst, 100.After a certain reaction time, the results are shown in Figure 8.The first peak is the cumene peak, the second peak is for small molecule hydrocarbon, the third peak is attributed to benzene homologues.It can be seen from the figure that metal atoms in the crystalline molecular sieves have a catalytic effect on the of cumene.Figure 8a*,b* for the catalytic conversion curves, the catalytic efficiency of Cry-Ni and Cry-Co samples were not significantly decreased after 20 times, indicating that the samples' recycling rates are higher, and the highest conversion rate of 54.5% and 44.03% was reached.The cumene cracking reaction is a typical acid catalytic reaction.The pure silicon Si-MCM-41 molecular sieves have almost no acid, so there is no catalytic function of the reaction.Comparing to Si-MCM-41, the samples exhibited better conversion and higher selectivity for cumene cracking.The better catalytic performance is attributed to the samples possessing uniform channels, appropriate pore diameter, and active sites caused by the introduction of Ni and Co atoms into the framework of molecular sieves.tals 2017, 7, 89 8 of 1 ples were not significantly decreased after 20 times, indicating that the samples' recycling rate higher, and the highest conversion rate of 54.5% and 44.03% was reached.The cumene cracking ction is a typical acid catalytic reaction.The pure silicon Si-MCM-41 molecular sieves have almos acid, so there is no catalytic function of the reaction.Comparing to Si-MCM-41, the sample ibited better conversion and higher selectivity for cumene cracking.The better catalyti formance is attributed to the samples possessing uniform channels, appropriate pore diameter, and ve sites caused by the introduction of Ni and Co atoms into the framework of molecular sieves.samples were not significantly decreased after 20 times, indicating that the samples' recycling rates are higher, and the highest conversion rate of 54.5% and 44.03% was reached.The cumene cracking reaction is a typical acid catalytic reaction.The pure silicon Si-MCM-41 molecular sieves have almost no acid, so there is no catalytic function of the reaction.Comparing to Si-MCM-41, the samples exhibited better conversion and higher selectivity for cumene cracking.The better catalytic performance is attributed to the samples possessing uniform channels, appropriate pore diameter, and active sites caused by the introduction of Ni and Co atoms into the framework of molecular sieves.

Conclusion
Mesoporous heteroatom molecular sieves MCM-41s with crystalline phase were synthesized via a one-step hydrothermal method.The resulting materials possessed a structure in the vertical cross direction with a crystalline size of about 12 µm and high specific surface areas, and possess a highlyordered mesoporous structure and ordered arrangement channels.The elements in the samples have a uniform distribution and are highly dispersed in the materials.A certain amount of metal complexes formed by metal ion and EDTA is an essential factor for the formation of the vertical cross

Conclusion
Mesoporous heteroatom molecular sieves MCM-41s with crystalline phase were synthesized via a one-step hydrothermal method.The resulting materials possessed a structure in the vertical cross direction with a crystalline size of about 12 µm and high specific surface areas, and possess a highly-ordered mesoporous structure and ordered arrangement channels.The elements in the samples have a uniform distribution and are highly dispersed in the materials.A certain amount of metal complexes formed by metal ion and EDTA is an essential factor for the formation of the vertical cross structure.At the same time, the crystalline mesoporous heteroatom samples improve the alkali resistance of the molecular sieves.Compared to Si-MCM-41, the samples exhibited better conversion and higher selectivity for cumene cracking.

Figure 4
Figure4illustrates the X-ray absorption near-edge structure (XANES) spectra of Cry-Ms.The corresponding spectra for metal oxides are given for comparison.The XANES pre-edge peak is attributed to the 1s-3d dipolar forbidden transition[21].Principally, this 1s-3d forbidden transition gains additional intensity when the metal center is in a non-centrally symmetric environment through mixing of 3d and 4p orbitals caused by the breakdown of inversion symmetry due to the structure distortion.Figure4aillustrates the XANES spectra of NiO and Cry-Ni.The nickel atoms in Cry-Ni have similar pre-edge features to that of NiO, which indicates nickel exists as mainly Ni 2+ in the Figure4illustrates the X-ray absorption near-edge structure (XANES) spectra of Cry-Ms.The corresponding spectra for metal oxides are given for comparison.The XANES pre-edge peak is attributed to the 1s-3d dipolar forbidden transition[21].Principally, this 1s-3d forbidden transition gains additional intensity when the metal center is in a non-centrally symmetric environment through mixing of 3d and 4p orbitals caused by the breakdown of inversion symmetry due to the structure distortion.Figure4aillustrates the XANES spectra of NiO and Cry-Ni.The nickel atoms in Cry-Ni have similar pre-edge features to that of NiO, which indicates nickel exists as mainly Ni 2+ in the * shows the K 3 -weighted spectra of Cry-Ni and NiO, which are the Fourier transformed spectra of Ni K-edge EXAFS spectra in the range of k = 2-6 Å.The peaks correspond to the distance between a Ni atom and its neighboring atoms.In the curve of NiO (a standard reference material), there are five peaks ( 1 -5 ) that can be ascribed to Ni-O, Ni-Ni 2 , Ni-O 3 , Ni-Ni Ni-Ni-O, Ni-O-Ni-O, Ni-O 4 , and Ni-Ni 5 scattering paths, respectively.It is clear that the curve of Cry-Ni is different from the curve of NiO, although the two peaks 1 and 2 of Cry-Ni are similar to the peaks 1 and 2 of NiO; a new peak between peaks 1 and 2 of Cry-Ni presents, which is originated in the silicon atoms.The shape and intensity of peaks 3 , 4 , and 5 are also different from that of NiO.The results show that the structure forms of Ni atoms in Cry-Ni are different from in NiO.Similar results were obtained in the Cry-Co sample.Figure 4b* presents the Fourier transforms of k 3 -weighted Co K-edge EXAFS spectra of Cry-Co, CoO, and Co 3 O 4 (standard reference materials).The curve of Cry-Co also presents two peaks 1 and 2 , which are similar with the peaks 1 and 2 of the curve of CoO, but are much different from the curve of Co 3 O 4 .The small peak between peaks 1 and 2 in the curve of Cry-Co is also induced by the silicon atoms.The results are useful for estimation of the crystallinity of the samples, and the analytic results are listed in Table have similar pre-edge features to that of NiO, which indicates nickel exists as mainly Ni 2+ in the material.Figure4bdisplays the XANES spectra of CoO, Co3O4, and Cry-Co.The cobalt atoms in Cry-Co have similar features to CoO, suggesting that Co 2+ exists in the sample.Note that the peaks are slightly shifted to a longer distance than standard samples because of the scattering phase shifts.
Figure 4a* shows the K 3 -weighted spectra of Cry-Ni and NiO, which are the Fourier transformed spectra of Ni K-edge EXAFS spectra in the range of k = 2-6 Å.The peaks correspond to the distance between a Ni atom and its neighboring atoms.In the curve of NiO (a standard reference material), there are five peaks (①-⑤) that can be ascribed to Ni-O, Ni-Ni ②, Ni-O ③, Ni-Ni Ni-Ni-O, Ni-O-Ni-O, Ni-O ④, and Ni-Ni ⑤ scattering paths, respectively.It is clear that the curve of Cry-Ni is different from the curve of NiO, although the two peaks ① and ② of Cry-Ni are similar to the peaks ① and ② of NiO; a new peak between peaks ① and ② of Cry-Ni presents, which is originated in the silicon atoms.The shape and intensity of peaks ③, ④, and ⑤ are also different from that of NiO.The results show that the structure forms of Ni atoms in Cry-Ni are different from in NiO.Similar results were obtained in the Cry-Co sample.Figure 4b* presents the Fourier transforms of k 3 -weighted Co K-edge EXAFS spectra of Cry-Co, CoO, and Co3O4 (standard reference materials).The curve of Cry-Co also presents two peaks ① and ②, which are similar with the peaks ① and ② of the curve of CoO, but are much different from the curve of Co3O4.The small peak between peaks ① and ② in the curve of Cry-Co is also induced by the silicon atoms.The results are useful for estimation of the crystallinity of the samples, and the analytic results are listed in Table
. The pore diameters of the two samples have littl ference from each other, due to the different micelle diameter of [(C4H9)4N][M(EDTA)] caused b difference radius of heteroatoms Ni 2+ and Co 2+ , which also influences the specific surface are re volume, and the pore diameter.

Scheme 1 .
Scheme 1.The supposed formation mechanism of Cry-M.

Scheme 1 .
Scheme 1.The supposed formation mechanism of Cry-M.

Figure 7 .
Figure 7. Diagram of the apparatus for cumene cracking.

Figure 7 .
Figure 7. Diagram of the apparatus for cumene cracking.

Figure 7 .
Figure 7. Diagram of the apparatus for cumene cracking.

Table 1 .
Textural properties of the samples.ICP: inductively coupled plasma.

Table 2 .
EXAFS fitting results for samples.