Control of Intrinsic Defects in Lithium Niobate Single Crystal for Optoelectronic Applications

: A single crystal of lithium niobate is an important optoelectronic material. It can be grown from direct melt only in a lithium deﬁcient non-stoichiometric form as its stoichiometric composition exhibits incongruent melting. As a result it contains a number of intrinsic point defects such as Li-vacancies, Nb antisites, oxygen vacancies, as well as different types of polarons and bipolarons. All these defects adversely inﬂuence its optical and ferroelectric properties and pose a deterrent to the effective use of this material. Hence, controlling the defects in lithium niobate has been an exciting topic of research and development over the years. In this article we discuss the different methods of controlling the intrinsic defects in lithium niobate and a comparison of the effect of these methods on the crystalline quality, stoichiometry, optical absorption in the UV-vis region

Lithium niobate in the stoichiometric composition melts incongruently whereas it melts congruently for a non-stoichiometric composition of 48.6 mol % Li 2 O and 51.4 mol % Nb 2 O 5 [7,8,21].Hence, a single crystal of LN can be grown by using conventional melt growth methods like the Czochralski (Cz) technique only from a melt with the aforesaid lithium deficient non-stoichiometric Crystals 2017, 7, 23 2 of 20 composition, unless a special growth procedure is adopted.Because of congruent melting at this non-stoichiometric composition (congruent LN; CLN) homogeneous and high optical quality CLN single crystals can be grown efficiently with a high conversion percentage of the initial melt (typically ~80%) without any composition variations along the length of the grown crystal [7,9].Due to Li deficient composition and incongruent vaporization of Li 2 O, CLN crystals contain a high concentration of Li-vacancies (V Li − ) that favors the incorporation of unavoidable impurities, particularly transition metals that limits the performance or usability of devices fabricated from it [1,22].
Along with the Li-vacancies the excess Nb 5+ ions present in CLN occupy vacant Li sites and form Nb-antisite defects (Nb Li 5+ ) [21].Around 20% of the Li sites are partly occupied by Nb 5+ .
Consequently to ensure charge neutrality a high concentration of Li vacancies is created in the lattice [21].The presence of these defects and impurities adversely influence the nonlinear optical and ferroelectric properties of .So, the performance of the devices made out of these crystals becomes limited.Therefore, controlling the defect structure is necessary to improve the properties and the efficacy of LN crystals.
There are several ways to control the defect in LN.One approach is to introduce impurities like Mg, Zn, and Zr into the lattice within a threshold concentration limit [9,10,[26][27][28][29].However, it should be noted that addition of these impurities (external defects) in the melt may give rise to additional growth problems such as composition inhomogeneities, introduction of sub-grain structures and boundaries, striation etc. in the crystals.The other methods to suppress the intrinsic defects are through direct growth of LN in near-stoichiometric composition by high temperature solution growth technique [9,[30][31][32][33] or by converting a CLN wafer to near-stoichiometric form by the vapor transport equilibration (VTE) technique in a Li-rich ambience [34][35][36][37].Although initially much of the attention was paid to growing CLN crystals from Li-deficient congruent melts, during the last two decades significant innovations in growth techniques have directed the research and development towards the growth of homogeneous near-stoichiometric LN (SLN) crystals.In this article the defect control in LN by different techniques and the effect of these preparation methods on the crystalline quality, stoichiometry, optical absorption, band-gap, and refractive index have been compared.

Point Defects in LiNbO 3 Crystals
As mentioned in the introduction, along with the inherent thermodynamically generated vacant sites, non-stoichiometry related Frankel defects i.e., Li vacancies V Li −1 and Nb-antisites (Nb Li 5+ ) are the main defects in congruent LiNbO 3 crystals [9,21,22,38].Li vacancies are the result of Li deficiency in the composition.The Nb-antisite is generated as the excess Nb of the CLN composition occupies the Li sites.Non-stoichiometry in LiNbO 3 arises due to the characteristic difference in its constitutional chemical bonds, i.e., Li-O and Nb-O bonds.The covalent Nb-O bonds are considerably stronger than the ionic Li-O bond [39,40].Due to the dissimilar bond strength and nearly equal ionic radii of the Li and Nb ions, there is a natural tendency of the available extra Nb ions to occupy the Li sites creating an antisite defect.Consequently, due to the charge difference in the Li + and Nb 5+ ions, additional Li vacancies appear in the LiNbO 3 lattice in order to maintain the charge neutrality [21].
Along with Li vacancies and Nb-antisites, there also exist oxygen vacancies (V O 2+ ) and protons (H + ) in the form of OH and OD complexes [7][8][9].Being a transitional metal ion, Nb ions give rise to other defects such as free polaron (Nb Nb 4+ ), bound polaron (Nb Li 4+ ), and bi-polarons (Nb Li 4+ -Nb Li 4+ ) by trapping electrons [41].Similarly, Li-vacancies also form hole-polarons by trapping holes [41].So, the departure from stoichiometry leads to a high degree of structural disorder and point defects in LN crystals [9,20].
In the literature there are three different models based on Li vacancies [38], Nb vacancies [42], and oxygen vacancies [43] explaining the defect structure of LN.However, the most accepted model, explaining most of the properties of LN, is represented by the Li-site vacancy (V) model: proposed by Larner et al. [38].According to this model the structure remains stable up to x = ~0.02and the congruent melting is for x = 0.018.Figure 1 shows a representative model for the defect structure of CLN [20].[38].According to this model the structure remains stable up to x = ~0.02and the congruent melting is for x = 0.018.Figure 1 shows a representative model for the defect structure of CLN [20].
Further the intrinsic defects influence the dielectric and ferroelectric properties of CLN [24,25,54,55].The NbLi 5+ antisite defects in CLN act as pinning centers that inhibit the movement of the ferroelectric domain wall in the crystal [9].Hence, CLN crystals exhibit a high ferroelectric switching field ~21 kV/mm (Table 1) that limits its use for domain engineered devices [49,56].As the defect concentration is reduced in nSLN the coercive field becomes less than 4 kV/mm [52,53].Even a coercive field as low as 200 V/mm has been reported for nSLN crystal grown from K2O flux [49].SLN crystals, therefore, offer favorable properties for the realization of periodically poled devices (PPLN) [54] and domain engineering [52,53] where an electric field has to be applied for poling the material.

Effect of Intrinsic Defect on Properties
It is well known that optical properties of a material are sensitive to the intrinsic defects and impurities.The Nb Li 5+/4+ defects act as electron trap sites and form polaron (Nb Li 4+ ) and bipolaron (Nb Li 4+ -Nb Li 4+ ) states which are responsible for the photorefractive damage [1,44].The presence of these defects and impurities leads to light-induced changes in the refractive index that results in the optical distortion [1], phase modulation [22], Bragg scattering [23], and green induced infrared absorption (GIIRA) [45], and consequently decreases the efficiency of nonlinear interactions when the crystal is subjected to an intense visible radiation [22,23].Because of these defects the value of the optical properties such as non-linear optical coefficient, linear electo-optic coefficient etc. (Table 1) is low in defect rich CLN crystal.However, these light induced optical effects in CLN can be minimized to a significant extent by operating the device at higher temperature (~180 • C) or by using defect controlled stoichiometric LN having lesser intrinsic defects and impurities [23].When grown in the near-stoichiometric form (nSLN, Li/Nb ~1) the optical properties improve significantly (Table 1) as a result of the decrease in the defect concentration [30,[46][47][48][49][50][51][52].So nSLN is a better choice for nonlinear frequency conversion, as well as photo-refractive and holographic data storage applications [53,54] in comparison to CLN.
Further the intrinsic defects influence the dielectric and ferroelectric properties of CLN [24,25,54,55].The Nb Li 5+ antisite defects in CLN act as pinning centers that inhibit the movement of the ferroelectric domain wall in the crystal [9].Hence, CLN crystals exhibit a high ferroelectric switching field ~21 kV/mm (Table 1) that limits its use for domain engineered devices [49,56].
As the defect concentration is reduced in nSLN the coercive field becomes less than 4 kV/mm [52,53].
Even a coercive field as low as 200 V/mm has been reported for nSLN crystal grown from K 2 O flux [49].SLN crystals, therefore, offer favorable properties for the realization of periodically poled devices (PPLN) [54] and domain engineering [52,53] where an electric field has to be applied for poling the material.Being a ferroelectric material lithium niobate [57] undergoes a structural phase transition from a ferroelectric phase (R3c) to a paraelectric phase (R3c) at around 1140 • C. The ferroelectric-to-paraelectric phase transition temperature of LN occurs at different temperatures depending upon the Li/Nb ratio in the crystal [58,59].It varies from 1140-1200 • C for Li deficient LN to near stoichiometric LN.A strong correlation between the composition and the Curie temperature is established by the O'Bryan equation [60].

Defect Control through Doping
The incorporation of divalent impurities like Mg 2+ , Zn 2+ etc. into the lattice within a threshold concentration limit reduces the intrinsic defects of the CLN crystals and consequently the damage threshold increases [9,10,[26][27][28][29]52,[61][62][63].At the same time, some optical properties such as refractive index, electro-optic coefficients, nonlinear optical coefficients, and phase-matching conditions for various configurations of second-harmonic generation (SHG) are influenced by these dopants [18,19].In the present article Mg has been taken as an example in this context.
In CLN, because of the excess Nb 5+ present at Li 1+ sites (i.e., Nb Li 5+ ) four additional Li vacancies (V Li −1 ) are created for charge compensation.Up to a threshold concentration, the Mg 2+ ions preferentially replace the excess Nb at Li sites.As Mg 2+ has a lower valence state than Nb 5+ ion, the number of Li-vacancies created due to charge compensation reduces [52,61,62].In the case of CLN the threshold concentration of Mg is ~4.5 to 5 mol %, beyond which it starts substituting the regular Li site leading to a decrease in the Li/Nb ratio [61].Zhong et al. [27] showed that the resistance to photo-refractive (optical) damage improves a hundred-fold on doping CLN with 4.6 mol % Mg.Undoped and Mg doped CLN single crystals were grown from congruent melt using the Czochralski (Cz) technique.The starting material was prepared from 99.998% Li 2 CO 3 and 99.999% Nb 2 O 5 taken in the congruent ratio.A multi-step synthesis route was adopted as described in ref. [70].An indigenously developed automatic diameter controlling software was used to grow crystals with uniform diameter.Seeding was done using a (00.1) oriented seed as per the procedure describe in ref. [71].The rotation rate was kept at 25 rpm during seeding, and then gradually reduced to 15 rpm during the growth of the constant diameter body part to obtain good quality crystals.The crystals were pulled at a rate of 2-4 mm/h.Following this methodology high quality single crystals of undoped CLN (for comparison), and 2.0 and 4.0 mol % Mg doped CLN were grown.However, the growth of crystals with 6 mol % Mg using the same growth conditions resulted in cracking due to excess strain because of the higher concentration of Mg.However, a low pulling rate of 1 mm/h and slow post-growth cooling of 50 • C/h led to crack-free 6 mol % Mg-doped crystals [70].The typical sizes of the grown crystals were ~25 mm in diameter and 30-40 mm in length (Figure 2).crystals.The crystals were pulled at a rate of 2-4 mm/h.Following this methodology high quality single crystals of undoped CLN (for comparison), and 2.0 and 4.0 mol % Mg doped CLN were grown.However, the growth of crystals with 6 mol % Mg using the same growth conditions resulted in cracking due to excess strain because of the higher concentration of Mg.However, a low pulling rate of 1 mm/h and slow post-growth cooling of 50 °C/h led to crack-free 6 mol % Mg-doped crystals [70].The typical sizes of the grown crystals were ~25 mm in diameter and 30-40 mm in length (Figure 2)..16-0.17, molar ratio) [28].The chemical was synthesized as per the procedure reported in ref. [70].The axial temperature gradient of the furnace used was ~10 • C/cm.In order to quickly establish the saturation temperature with minimum loss of seed during the seeding procedure the growth was initiated with a c-oriented seed using a seeding technique described in ref. [71].The large difference in the composition of the Li-rich melt and the growing crystal (nSLN_L) posed problems [9,30,47] such as striation, faceting, and core formation which were avoided by optimizing the growth parameters and by improving the temperature stability of the growth furnace.The pulling and rotation rate were adjusted during the growth to avoid core and inclusions in the grown crystals.The optimized growth parameters for the growth of nearly flat interfaced, inclusion-and crack-free single crystals are: 0.2-0.5 mm/h pulling, 2-20 rpm rotation and 0.04-0.1 • C/h cooling rate for the thermal gradient as mentioned above.Figure 3a shows crystals grown from Li-rich melt (nSLN_L).The sizes of the grown crystals were up to 15-20 mm in diameter and 30-50 mm in length.To avoid composition variation which arises due to a gradual increase in the Li content in the remaining melt during the growth process, crystals with weight less than 5% of the total starting melt were pulled.A nearly flat solid-liquid interface was ensured in order to have a high quality crystal [72] as a non-flat interface leads to highly strained regions near the core of the crystal and results in the generation of extended defects like dislocations, low-angle grain boundaries, cracks etc. in the crystal [72].

Defect Control by Growing Near Stoichiometric LN Crystal
Near stoichiometric LN (nSLN) crystals were grown from high temperature solution by the top seeded solution growth (TSSG) technique from two different solutions, namely (a) Li-rich solution (58.0 mol % of Li2O and 42.0 mol % of Nb2O5) [2] and (b) SLN with K2O solvent (K2O/LiNbO3 ~0.16-0.17,molar ratio) [28].The chemical was synthesized as per the procedure reported in ref. [70].The axial temperature gradient of the furnace used was ~10 °C/cm.In order to quickly establish the saturation temperature with minimum loss of seed during the seeding procedure the growth was initiated with a c-oriented seed using a seeding technique described in ref. [71].The large difference in the composition of the Li-rich melt and the growing crystal (nSLN_L) posed problems [9,30,47] such as striation, faceting, and core formation which were avoided by optimizing the growth parameters and by improving the temperature stability of the growth furnace.The pulling and rotation rate were adjusted during the growth to avoid core and inclusions in the grown crystals.The optimized growth parameters for the growth of nearly flat interfaced, inclusion-and crack-free single crystals are: 0.2-0.5 mm/h pulling, 2-20 rpm rotation and 0.04-0.1 °C/h cooling rate for the thermal gradient as mentioned above.Figure 3a shows crystals grown from Li-rich melt (nSLN_L).The sizes of the grown crystals were up to 15-20 mm in diameter and 30-50 mm in length.To avoid composition variation which arises due to a gradual increase in the Li content in the remaining melt during the growth process, crystals with weight less than 5% of the total starting melt were pulled.A nearly flat solid-liquid interface was ensured in order to have a high quality crystal [72] as a non-flat interface leads to highly strained regions near the core of the crystal and results in the generation of extended defects like dislocations, low-angle grain boundaries, cracks etc. in the crystal [72].Similarly, nSLN crystals (nSLN_K) were also grown using K2O as solvent with similar growth conditions and parameters except for the rotation rates, which were marginally higher (20-5 rpm) in this case (Figure 3b).

Preparation of Near Stoichiometric Sample by VTE
For enriching the Li content in the grown CLN crystal the vapor transport equilibration (VTE) process was employed.In this method a c-oriented CLN wafer of thickness ~1 mm was hung inside a platinum crucible containing 300 g mixture of pre-reacted lithium-rich Li3NbO4 and LiNbO3 powder [73,74].The crucible was tightly covered with a platinum foil and heated at 1100 °C for 100 h.

Test of Optical Homogeneity
Optical homogeneity of the samples was investigated by concoscopy and orthoscopic Similarly, nSLN crystals (nSLN_K) were also grown using K 2 O as solvent with similar growth conditions and parameters except for the rotation rates, which were marginally higher (20-5 rpm) in this case (Figure 3b).

Preparation of Near Stoichiometric Sample by VTE
For enriching the Li content in the grown CLN crystal the vapor transport equilibration (VTE) process was employed.In this method a c-oriented CLN wafer of thickness ~1 mm was hung Crystals 2017, 7, 23 6 of 20 inside a platinum crucible containing 300 g mixture of pre-reacted lithium-rich Li 3 NbO 4 and LiNbO 3 powder [73,74].The crucible was tightly covered with a platinum foil and heated at 1100 • C for 100 h.

Test of Optical Homogeneity
Optical homogeneity of the samples was investigated by concoscopy and orthoscopic birefringence interferometry [75].The conoscopy patterns of c-plates observed under a polarized light optical microscope (Olympus BX60, Olympus Corporation, Tokyo, Japan) consisted of well-shaped circular rings for all the samples confirming the homogeneity of the samples along the radial direction.Further, the orthoscopy of y-cut samples was carried out to check the homogeneity of the samples along the growth (axial) direction.The setup is comprised of a He-Ne laser, beam expander, polarizers, and a CCD camera.The collimated parallel beam travels through birefringent crystal (y-cut, dimension: 10 × 10 × 1 mm 3 ) placed between cross polarizers with one polarizer placed at 45 • with respect to the z-axis of the sample.The phase delay between the ordinary and extraordinary components of the light passes through the sample and polarizers resulting in the formation of interference fringes revealing the birefringence map of the sample.The corresponding phase delay is: where λ is the wavelength of the laser, d is the sample thickness, and ∆n = n e − n o is the birefringence.The birefringence fringe pattern is characterized by nearly straight-line fringes corresponding to contour maps of equal birefringence for all the samples.The nearly straight line fringes and their nearly equal spacing signify the good optical homogeneity of the grown crystals along the growth direction.The order of optical homogeneity was estimated by calculating the per fringe variation in δ(∆n), which is given as: The estimated optical homogeneity of the all the samples was better than 10 −5 /mm. Figure 4 shows representative conoscopy and birefringence fringe patterns for a Mg:CLN crystal.
Crystals 2017, 7, 23 6 of 19 at 45° with respect to the z-axis of the sample.The phase delay between the ordinary and extraordinary components of the light passes through the sample and polarizers resulting in the formation of interference fringes revealing the birefringence map of the sample.The corresponding phase delay is: where λ is the wavelength of the laser, d is the sample thickness, and Δn = ne − no is the birefringence.
The birefringence fringe pattern is characterized by nearly straight-line fringes corresponding to contour maps of equal birefringence for all the samples.The nearly straight line fringes and their nearly equal spacing signify the good optical homogeneity of the grown crystals along the growth direction.The order of optical homogeneity was estimated by calculating the per fringe variation in δ(Δn), which is given as: The estimated optical homogeneity of the all the samples was better than 10 −5 /mm. Figure 4 shows representative conoscopy and birefringence fringe patterns for a Mg:CLN crystal.

Effect of Defect Control Processes on Crystalline Quality
The effect of the defect control on the structural defects and disorder of samples prepared from the crystals grown by Mg doping (Mg:CLN), nSLNs, and VTE treated CLN was analyzed by high resolution X-ray diffraction (HRXRD) measurements for (00.6) diffracting plane in symmetrical Bragg geometry with Mo-Kα1 radiation.Figure 5a-d shows the diffraction curves (DC) of undoped CLN (for comparison) and Mg-doped (2.0, 4.0, and 6.0 mol %) LN crystals.Figure 6a-c shows DCs for nSLN_L and nSLN_K crystals prepared by HTSG, and nSLN_V prepared by the VTE method.

Effect of Defect Control Processes on Crystalline Quality
The effect of the defect control on the structural defects and disorder of samples prepared from the crystals grown by Mg doping (Mg:CLN), nSLNs, and VTE treated CLN was analyzed by high resolution X-ray diffraction (HRXRD) measurements for (00.6) diffracting plane in symmetrical Bragg geometry with Mo-Kα 1 radiation.Figure 5a-d shows the diffraction curves (DC) of undoped CLN (for comparison) and Mg-doped (2.0, 4.0, and 6.0 mol %) LN crystals.Figure 6a-c shows DCs for nSLN_L and nSLN_K crystals prepared by HTSG, and nSLN_V prepared by the VTE method.
The effect of the defect control on the structural defects and disorder of samples prepared from the crystals grown by Mg doping (Mg:CLN), nSLNs, and VTE treated CLN was analyzed by high resolution X-ray diffraction (HRXRD) measurements for (00.6) diffracting plane in symmetrical Bragg geometry with Mo-Kα1 radiation.Figure 5a-d shows the diffraction curves (DC) of undoped CLN (for comparison) and Mg-doped (2.0, 4.0, and 6.0 mol %) LN crystals.Figure 6a-c shows DCs for nSLN_L and nSLN_K crystals prepared by HTSG, and nSLN_V prepared by the VTE method.The DCs of the Mg-doped LN (Figure 5b-d) crystals contain a single diffraction peak.The full-width at half-maximum (FWHM) of the DCs estimated using curve fitting are 76, 112, and 65 arc-sec for 2.0, 4.0, and 6.0 mol % Mg doped samples respectively.Overall the FWHMs of Mg:CLN are higher than the CLN sample signifying the presence of relatively more point defects in Mg doped samples.In comparison to CLN, although it has lower Li vacancy and anti-site defect, the divalent Mg ions create a distortion in the lattice around themselves as the ionic radii of Mg 2+ (86 pm in octahedral coordination) is more than Nb 5+ (78 pm in octahedral coordination).As a result the FWHM in the DC is more than that of CLN.
Further, the FWHM increases as the Mg doping was increased in the 2 and 4 mol % samples (2Mg:CLN and 4Mg:CLN) due to an increase in the lattice distortion with the increase in Mg concentration.However, the lower FWHM (Table 2) in the 6 mol % doped crystal is due to the lower pulling rate, employed to grow this composition without cracks, as pulling rate influences the crystalline perfection.In fact the cracking of the 6 mol % Mg doped crystal (6Mg:CLN) when grown with the pulling rate the same as that used for other compositions (2Mg:CLN and 4Mg:CLN) implies the presence of a relatively higher strain in that particular sample.
The DCs of CLN (Figure 5a) and nSLN_L (Figure 6a) consist of a single diffraction peak that signifies that these crystals are free from any internal sub-grain boundary [76][77][78], which is otherwise usually observed because of the strain generated during the post-growth cooling due to The DCs of the Mg-doped LN (Figure 5b-d) crystals contain a single diffraction peak.The full-width at half-maximum (FWHM) of the DCs estimated using curve fitting are 76, 112, and 65 arc-sec for 2.0, 4.0, and 6.0 mol % Mg doped samples respectively.Overall the FWHMs of Mg:CLN are higher than the CLN sample signifying the presence of relatively more point defects in Mg doped samples.In comparison to CLN, although it has lower Li vacancy and anti-site defect, the divalent Mg ions create a distortion in the lattice around themselves as the ionic radii of Mg 2+ (86 pm in octahedral coordination) is more than Nb 5+ (78 pm in octahedral coordination).As a result the FWHM in the DC is more than that of CLN.
Further, the FWHM increases as the Mg doping was increased in the 2 and 4 mol % samples (2Mg:CLN and 4Mg:CLN) due to an increase in the lattice distortion with the increase in Mg concentration.However, the lower FWHM (Table 2) in the 6 mol % doped crystal is due to the lower pulling rate, employed to grow this composition without cracks, as pulling rate influences the crystalline perfection.In fact the cracking of the 6 mol % Mg doped crystal (6Mg:CLN) when grown with the pulling rate the same as that used for other compositions (2Mg:CLN and 4Mg:CLN) implies the presence of a relatively higher strain in that particular sample.The DCs of CLN (Figure 5a) and nSLN_L (Figure 6a) consist of a single diffraction peak that signifies that these crystals are free from any internal sub-grain boundary [76][77][78], which is otherwise usually observed because of the strain generated during the post-growth cooling due to structural phase transformation at ~1140 • C (paraelectric to ferroelectric), growth imperfections, and instabilities.The FWHM of the DCs was evaluated by Lorentz fitting as tabulated in Table 2.Although the samples are devoid of any grain boundary, on close examination an asymmetry in the right wing of the DCs was observed in nSLN_L which may be attributed to the presence of point defects and their agglomerates in the sample causing strain in the lattice around the defect core that leads to defuse scattering.
On the other hand, the DCs for nSLN_V (Figure 6b) and nSLN_K (Figure 6c) are characterized by superimposition of a number of peaks signifying the presence of point defects as well as low angle grain boundaries.The peak fitting revealed that the DC of nSLN_V consists of three additional peaks.The two well separated peaks on the right of the main peak correspond to low angle grain boundaries formed due to the employed thermal treatment.The FWHM of the main peak is ~45 arc-sec.
The DC for SLN_K (Figure 6c) is the widest and consists of several satellite peaks along with the main peak as seen in curve fitting.The fitting shows the presence of low angle grain boundaries with a tilt angle in the range of 57-196 arc-sec.The broad and multi-peak DC of the nSLN_K sample depicts a relatively poor crystalline perfection with respect to other nSLN samples [79].
From the observations of the HRXRD measurements one can conclude that the structural quality of CLN is relatively better than all the three nSLN and the Mg:CLN samples.This may be due to the fact that although nSLN samples are better than CLN in terms of stoichiometry (as seen from the optical measurements described below) with lesser point defects, the higher dimensional defects like dislocation loops and low angle grain boundaries are more in the nSLN samples.It is noteworthy that nSLN crystals grown from K 2 O solution (nSLN_K) or Li-rich solution (nSLN_L) may contain several growth imperfections that arise during the growth process as the occurrence of constitutional super-cooling is common in such growth methods having additional or excess ions [80].Further, the temperature fluctuation at the solid-liquid interface during the growth influences the growth rate which subsequently deteriorates the structural quality of the growing crystal.Also, nSLN_L and nSLN_K have similar or more FWHM in comparison to Mg:CLN because of the growth issues related to them.The vapor transport equilibration treated CLN sample, i.e., SLN_V, has similar FWHM to pristine CLN with an asymmetry in the right wing of the DC but lesser FWHM than the nSLN_L and nSLN_K.This suggests that the overall crystalline quality is almost unaffected in VTE though a few low angle grain boundaries appeared due to the involved thermal treatment and the diffusion process.

Effect of Defect Control Processes on the Optical Absorption
The optical band-gap and the defect related absorption was investigated by optical transmission measurements carried out using a Jasco V670 spectrophotometer (JASCO International Co., Ltd., Tokyo, Japan).The absorption coefficient (α) was calculated from the transmittance spectra using the relation [81]: where T is transmittance, R is reflectivity, and d is the sample thickness.Further, there is a strong correlation between the AE and the Li/Nb ratio in the grown crystal [83] which was used to estimate the Li content in the grown crystals.A shift in AE towards the lower wavelength in comparison to the CLN was observed for all the nSLN samples (Figure 7).This confirms a decrease in the intrinsic defects and an increase in stoichiometry (i.e., Li/Nb) samples which was estimated using the following empirical relation [83]: where E (eV) is the photon energy corresponding to the AE and cLi is the Li2O content in the sample in mol %.The values of the AE and the corresponding Li/Nb ratio for all the nSLN crystals are summarized in grown from K/Nb~0.32 is 305.5 nm.On comparison with the values available in the literature it was found to be in close agreement with the reported values of 305.5 nm [86] and 306 nm [87,88].
Although, there is a report of AE ~303.2 nm for nSLN_K grown from K/Nb ≥ 0.38 and Li/Nb = 1 [86], but this composition leads to a growth of inhomogeneous crystals [84].According to Peter et al. [84], growth from a K/Nb ratio more than 0.36 and Li/Nb = 1 results in crystals with a bottom portion having multi-phase.
The AE was found to be ~304.6nm for the sample prepared by the VTE technique (nSLN_V).Further, there is a strong correlation between the AE and the Li/Nb ratio in the grown crystal [83] which was used to estimate the Li content in the grown crystals.A shift in AE towards the lower wavelength in comparison to the CLN was observed for all the nSLN samples (Figure 7).This confirms a decrease in the intrinsic defects and an increase in stoichiometry (i.e., Li/Nb) samples which was estimated using the following empirical relation [83]: where E (eV) is the photon energy corresponding to the AE and c Li is the Li K/Nb~0.32 is 305.5 nm.On comparison with the values available in the literature it was found to be in close agreement with the reported values of 305.5 nm [86] and 306 nm [87,88].Although, there is a report of AE ~303.2 nm for nSLN_K grown from K/Nb ≥ 0.38 and Li/Nb = 1 [86], but this composition leads to a growth of inhomogeneous crystals [84].According to Peter et al. [84], growth from a K/Nb ratio more than 0.36 and Li/Nb = 1 results in crystals with a bottom portion having multi-phase.The AE was found to be ~304.6nm for the sample prepared by the VTE technique (nSLN_V).This value is slightly blue shifted compared to the AE ~305 nm reported by Chen et al. [89] for VTE treated sample.Comparison of the AEs of the samples prepared in the present investigation revealed that the AE is the lowest for nSLN prepared by VTE (nSLN_V).This implies that the VTE technique is the most effective technique for preparing nSLN (particularly for a sample in the form of a thin wafer) in comparison to the other methods.The CLN crystal used for VTE in general contains ~4% Li vacancy and 1% Nb antisites [90].Annealing of this wafer in Li-rich ambient reduces the Li-vacancies to a great extent by replacing Nb-antisites with regular Li ions via solid-state diffusion at elevated temperature and brings the composition close to the phase boundary limit i.e., 49.9 mol % Li 2 O [91].
Further, the measured AEs for the Mg:CLN samples are 317.1 nm (2 mol %), 314.2 nm (4 mol %), and 311.6 nm (6 mol %) in comparison to the AE ~320.6 nm for undoped CLN.The observed blue shift in the UV absorption edge is in agreement with the reported literature [85][86][87].The gradual blue shift confirmed the reduction of the lithium vacancy (V Li ) in the grown crystals with the concentration of Mg in the lattice as discussed earlier.However, in comparison to the other processes employed in this investigation the effect of Mg doping on the improvement of stoichiometry is the least (Table 2).
The effect of Mg doping can be represented by Larner's Li-site defect model [38]: The reduction in the number of Nb antisites on Mg doping leads to a reduction in the number of localized excitons or other band-tail states that consequently results in a blue shift in the AE.
The influence of the preparation methods on the electronic band-gap of LN was investigated from the absorption spectra using the Tauc relation [81]: where, A is a constant, hν is photon energy, E g is the allowed energy gap, and n is an exponent determined by the nature of the electron transition during the absorption process.The value of n is 1   2   for the allowed direct transition and 2 for the allowed indirect transition.As LN is an indirect band gap material [92,93], the optical band gap characterized by phonon mediated allowed indirect transitions near the fundamental AE in the absorption spectra is estimated using the relation [81]: where, E ind g is the indirect bandgap energy and hΩ is the energy of the absorbed (+) or emitted (−) phonons needed to conserve the momentum.For estimation of the indirect band-gap energy values of (α) 1/2 vs. hν are plotted in Figure 8a,b for all the nSLN and Mg:CLN samples (undoped CLN is included for comparison).The two adjoining linear segments near the band edge describe the phonon assisted fundamental photon absorption process corresponding to the absorption or emission of phonons.The linear fits of the absorption data and their respective intercept values E − and E + with the energy axis at α = 0 were used to estimate the indirect band-gap and the associated phonon energy using Equation (6).The estimated values are summarized in Table 2.The optical absorption spectra in the visible region were further analyzed to obtain information of the defects in the samples.As shown in Figure 7 (inset), a weak broad absorption band around The energy of phonons involved in the inter-band transition is in the range of 30-40 meV (241-322 cm −1 ), which is associated with the E(TO2)-E(TO6) or A1(TO1)-A1(TO2) modes of Li/O and Nb/O vibrations as per the Raman spectra reported in reference [94].Moreover, it is clear from the table that the indirect band-gap energy of Mg:CLN and the solution grown/VTE prepared nSLN has increased significantly in comparison to CLN.This certainly indicates a decrease in the concentration of intrinsic defects and trace impurities at the Li sites resulting in a decrease in the band tailing or band narrowing phenomena in the crystals grown by the respective growth methods.The observed increase in band gap energy for Mg doped and nSLN samples confirms a decrease in structural and lattice defects (Li vacancies and Nb Li 5+ defects).This leads to an increase in the photoconductivity and a decrease in the light induced space charge field that results in an enhancement in the optical damage resistance of the Mg:CLN and nSLN crystals.Further, the direct band-gap energy can also be estimated from the direct allowed transition using the Tauc relation (Equation ( 5)).For estimation, α 2 vs. energy (hν) is plotted for all the samples as shown in Figure 9.The steep rise of absorption and its linear fit at higher photon energy depict the direct allowed interband transition [93].The intercept of the straight line at the energy axis (α 2 = 0) yields the direct optical band-gap (E g ) energies which are listed in Table 2.The values show a trend similar to that for the indirect band-gap.The observed direct band-gap energy, for nSLN_V (4.11 eV) is closer to the theoretically estimated value which is 4.7 eV [95].The observed difference between the theoretically calculated and experimentally measured value is attributed to the excitonic (quasi-particle) effects included in the theoretical model.Referring to the trend in Table 2 it appears that the experimental value will be further closer to the theoretical value [95] if the Li/Nb ratio of the sample approaches unity.The optical absorption spectra in the visible region were further analyzed to obtain information of the defects in the samples.As shown in Figure 7 (inset), a weak broad absorption band around The optical absorption spectra in the visible region were further analyzed to obtain information of the defects in the samples.As shown in Figure 7 (inset), a weak broad absorption band around 2.55 eV (485 nm) was observed.This is in good agreement with the occurrence of a similar band reported in reduced CLN crystals [96].Hence, the origin of this absorption may be attributed to oxygen vacancies present in the sample.Evidently such absorption is prominent in the nSLN_V sample where the probability of formation of an oxygen vacancy is more as the sample was kept at high temperature for long time.The mechanism of the loss of oxygen (reduction) can be represented as: where V O − is the oxygen vacancy carrying two positive charges.The electrons released from the oxygen site are trapped at the Nb Li 5+ defect sites.Depending upon the number of trapped electrons electronic defects such as bound polaron [Nb Li 4+ ] (at 1.6 eV), free polaron Nb Nb 4+ (at 0.94 eV), bi-polarons [Nb Li 4+ -Nb Nb 4+ ] (at 2.5 eV) and Q-polarons (interaction of two bipolarons) (at 3.6 eV) [41,96,97] are formed in the lattice.So, comparing the energy values it appears that the observed absorption at 2.55 eV in the present study is due to the bi-polaron.In Mg:CLN (inset of Figure 7) there are weak peaks near 2.5 eV as well.
The optical absorption just above (in the wavelength plot) the fundamental AE is due to the structural defects and disorders present in the lattice.These defects give rise to an exponential tail, known as the Urbach tail, in the absorption plot (Figure 7) as their density of states falls sharply away from the conduction and valance band [98][99][100].This is governed by the Urbach rule [98]: where, α o is a characteristic crystal parameter, hν is the incident photon energy, and E U is the Urbach energy that corresponds to the width of the defect tail states [93,98,99].
Figure 10 shows the logarithm of absorption coefficient (lnα) vs. incident photo energy plot.As per Equation ( 8) the linear region shown in the figure near the band absorption edge corresponds to the Urbach tail.The Urbach energy E U was estimated from the inverse of the slope of the linear fit (Table 2).The Urbach energy for CLN (74 meV) is in good agreement with the value (74 meV) estimated by Castillo-Torres [82].It is to be noted that although there is a decrease in the concentration fo Li vacancies and antisites defects in nSLN samples, the Urbach energy for nSLN crystals (~74 meV) was found to be slightly higher with respect to CLN (65 meV) (Table 2).This is consistent with the observation in HRXRD measurement indicating the fact that the structural defects are more in nSLN samples compared to CLN.Further, the Urbach energy of Mg:CLN is 77, 84, and 76 meV for 2, 4, and 6 mol % Mg doped samples respectively.This is also consistent with the observation in the HRXRD measurements.
known as the Urbach tail, in the absorption plot (Figure 7) as their density of states falls sharply away from the conduction and valance band [98][99][100].This is governed by the Urbach rule [98]: where, αo is a characteristic crystal parameter, hν is the incident photon energy, and EU is the Urbach energy that corresponds to the width of the defect tail states [93,98,99].
Figure 10 shows the logarithm of absorption coefficient (lnα) vs. incident photo energy plot.As per Equation ( 8) the linear region shown in the figure near the band absorption edge corresponds to the Urbach tail.The Urbach energy EU was estimated from the inverse of the slope of the linear fit (Table 2).The Urbach energy for CLN (74 meV) is in good agreement with the value (74 meV) estimated by Castillo-Torres [82].It is to be noted that although there is a decrease in the concentration fo Li vacancies and antisites defects in nSLN samples, the Urbach energy for nSLN crystals (~74 meV) was found to be slightly higher with respect to CLN (65 meV) (Table 2).This is consistent with the observation in HRXRD measurement indicating the fact that the structural defects are more in nSLN samples compared to CLN.Further, the Urbach energy of Mg:CLN is 77, 84, and 76 meV for 2, 4, and 6 mol % Mg doped samples respectively.This is also consistent with the observation in the HRXRD measurements.

Effect of Defect Control Processes on the Refractive Index
The refractive index of the samples was measured using the Prism coupling technique (Metricon 2010/M) as described in ref. [101].Measurements were carried out for 532 and 1064 nm at room temperature.Figure 11 shows the variation of the ordinary (n o ) and extraordinary (n e ) refractive indices for CLN along with all the three nSLN samples.It is evident from the plot that the value of n o is almost unaffected by the method of the preparation of the samples, whereas the value of n e shows a decreasing trend with an increase in the Li content in the crystal (CLN > nSLN_L > nSLN_K > nSLN_V) for both 532 and 1064 nm.This correlates with the Li/Nb ratio: as the Li/Nb ratio increases the n e decreases.Figure 11 also shows the variation of both the n o and n e for Mg:CLN in comparison to that of undoped CLN.A gradual decrease of n o and n e with the increase in the Mg doping concentration was noticed, which is attributed to the decrease in the concentration of intrinsic defects of Nb Li 5+ in CLN due to Mg doping [70].It shows that Mg ions influence the microscopic polarizability and dielectric susceptibility of CLN for both the polarizations.The refractive index is correlated to the band gap energy (E g ) by an empirical relation [102]: where c is a material dependent constant.The decrease in the refractive index in nSLN samples as well as for the Mg doped samples is in agreement with the trend in the shift of AE discussed earlier (Table 2).The variation in the refractive index is explained on the basis of the nature of constitutional chemical bonds determining the polarizability of the lattice [103].According to Pauling [103], the ionic character of a bond depends on the relative electro-negativity of the constituent ions.As the electro-negativity of Li, Nb, and O ions are 1.0, 1.2, and 3.5 respectively, the Li-O bond is more ionic than the Nb-O bond.As a result the electrons in the Li-O bonds are more tightly bound to the oxygen atom, and therefore are less polarizable compared to the Nb-O bond [104].So, the presence of relatively more Nb-O bonds in a lattice results in higher polarizability, hence higher refractive index.Accordingly the refractive index is influenced by the Li/Nb ratio of the sample.It is evident from Figure 11 that the refractive index (especially n e ) gradually decreases along with the lowering of the AE listed in Table 2 (i.e., improvement in the Li/Nb ratio) for all seven samples.Further, Figure 12 shows the variation of the birefringence (∆n = n o − n e ) in nSLN and the Mg:CLN samples for 532 and 1064 nm.The birefringence of the samples increases with the decrease in AE as a result of the decrease in the value of the n e .The VTE treated sample exhibits the highest birefringence among the samples prepared by all the methods.
where c is a material dependent constant.The decrease in the refractive index in nSLN samples as well as for the Mg doped samples is in agreement with the trend in the shift of AE discussed earlier (Table 2).
The variation in the refractive index is explained on the basis of the nature of constitutional chemical bonds determining the polarizability of the lattice [103].According to Pauling [103], the ionic character of a bond depends on the relative electro-negativity of the constituent ions.As the electro-negativity of Li, Nb, and O ions are 1.0, 1.2, and 3.5 respectively, the Li-O bond is more ionic than the Nb-O bond.As a result the electrons in the Li-O bonds are more tightly bound to the oxygen atom, and therefore are less polarizable compared to the Nb-O bond [104].So, the presence of relatively more Nb-O bonds in a lattice results in higher polarizability, hence higher refractive index.Accordingly the refractive index is influenced by the Li/Nb ratio of the sample.It is evident from Figure 11 that the refractive index (especially ne) gradually decreases along with the lowering of the AE listed in Table 2 (i.e., improvement in the Li/Nb ratio) for all seven samples.Further, Figure 12 shows the variation of the birefringence (Δn = no − ne) in nSLN and the Mg:CLN samples for 532 and 1064 nm.The birefringence of the samples increases with the decrease in AE as a result of the decrease in the value of the ne.The VTE treated sample exhibits the highest birefringence among the samples prepared by all the methods.

Conclusions
Defects in the lattice adversely influence several important properties of congruent lithium niobate.There are several ways to control these defects: (a) by introduction of impurities such as Mg into the lattice within a threshold concentration limit, (b) by direct growth of LN in near-stoichiometric composition using a Li-rich melt or K2O solvent by high temperature solution growth and (c) by converting a CLN wafer into near-stoichiometric form by vapor transport equilibration in Li-rich ambience.The study shows that the best stoichiometry (Li/Nb ratio) can be achieved by growth from solution using K2O flux.However, HRXRD measurement revealed that in these crystals the crystalline quality is an issue as it contains low angle grain boundaries.The crystalline quality is the best in the VTE treated nSLN sample with an excellent Li/Nb ratio of ~0.998.However, this method is suitable only for thin wafers.For preparation of bulk crystal, nSLN grown from Li-rich melt is good in crystalline quality (FWHM ~108 arc-sec) with Li/Nb ratio of ~0.985.For optical-damage-resistant Mg doped CLN samples the crystalline quality degrades as the Mg content increases in the crystal.However, it can be minimized by employing slower pulling during the growth of the crystal.The estimation of the Urbach energy, associated with the disorder in the crystal, also supports the observations in the HRXRD measurements for all the samples.The refractive index, especially the extraordinary component (ne), was observed to decrease with an

Conclusions
Defects in the lattice adversely influence several important properties of congruent lithium niobate.There are several ways to control these defects: (a) by introduction of impurities such as Mg into the lattice within a threshold concentration limit, (b) by direct growth of LN in near-stoichiometric composition using a Li-rich melt or K 2 O solvent by high temperature solution growth and (c) by converting a CLN wafer into near-stoichiometric form by vapor transport equilibration in Li-rich ambience.The study shows that the best stoichiometry (Li/Nb ratio) can be achieved by growth from solution using K 2 O flux.However, HRXRD measurement revealed that in these crystals the crystalline quality is an issue as it contains low angle grain boundaries.The crystalline quality is the best in the VTE treated nSLN sample with an excellent Li/Nb ratio of ~0.998.However, this method is suitable only for thin wafers.For preparation of bulk crystal, nSLN grown from Li-rich melt is good in crystalline quality (FWHM ~108 arc-sec) with Li/Nb ratio of ~0.985.For optical-damage-resistant Mg doped CLN samples the crystalline quality degrades as the Mg content increases in the crystal.However, it can be minimized by employing slower pulling during the growth of the crystal.The estimation of the Urbach energy, associated with the disorder in the crystal, also supports the observations in the HRXRD measurements for all the samples.The refractive index, especially the extraordinary component (n e ), was observed to decrease with an increase in the Li/Nb ratio or decrease in intrinsic defects in the case of nSLN.Whereas both the n o and n e were found to decrease with an increase in the Mg content in the Mg:CLN crystals.With the absorption edge showing a blue shift, the corresponding trend in the value of the refractive index is CLN > Mg:CLNs > nSLN grown from Li-rich melt > nSLN grown using K 2 O solvent > VTE treated CLN.This is due to the relative decrease in the number of easily polarizable Nb-O bonds with the increase in the Li/Nb ratio.The birefringence of the samples shows a reverse trend.

3. 2 .
Defect Control by Growing Near Stoichiometric LN Crystal Near stoichiometric LN (nSLN) crystals were grown from high temperature solution by the top seeded solution growth (TSSG) technique from two different solutions, namely (a) Li-rich solution (58.0 mol % of Li 2 O and 42.0 mol % of Nb 2 O 5 ) [2] and (b) SLN with K 2 O solvent (K 2 O/LiNbO 3 ~0

Figure 7
shows the absorption spectra of nSLN crystals prepared by different techniques, i.e., nSLN_L, nSLN_K, nSLN_V and the Mg (2, 4, and 6 mol %):CLN crystals along with the spectrum of undoped CLN included for comparison.The absorption spectra are characterized by the fundamental absorption edge (AE) which in LN arises due to the inter-band electronic transition between the 2p orbitals of the O 2− (valance band) and the 4d orbitals of the Nb 5+ (conduction band)[82].The AE was estimated as the wavelength at which the absorption coefficient is 20 cm −1[83] and summarized in Table2.A blue shift in the fundamental absorption edge of nSLN and Mg doped samples with respect to CLN sample is evident from the plot.The blue shift indicates the influence of intrinsic defects on the fundamental absorption processes and signifies an improvement in the optical band structure and the lattice of LN due to a decrease in intrinsic defects (Nb Li +5 and V Li −1 ) and defect-induced band tailing states that give rise to band narrowing[84].The disorder in the Nb sub-lattice due to the presence of Nb Li 5+ antisite defects leads to the distortion in the oxygen octahedron and influences the fundamental AE.Crystals 2017, 7, 23 9 of 19

Figure 7 .
Figure 7. Absorption spectra of CLN, Mg doped CLN and nSLN crystals.Inset shows absorption band due to bi-polaron absorption at around 2.55 eV.

Figure 7 .
Figure 7. Absorption spectra of CLN, Mg doped CLN and nSLN crystals.Inset shows absorption band due to bi-polaron absorption at around 2.55 eV.

Figure 10 .
Figure 10.The dependence of lnα with incident photon energy.Figure 10.The dependence of lnα with incident photon energy.

Figure 10 .
Figure 10.The dependence of lnα with incident photon energy.Figure 10.The dependence of lnα with incident photon energy.

Figure 11 .
Figure 11.Refractive index (n o and n e ) of different (a) Mg:CLN; and (b) nSLN crystals at 532 and 1064 nm wavelength.

Figure 12 .
Figure 12.Birefringence at 532 and 1064 nm of differently prepared lithium niobate crystals.

Figure 12 .
Figure 12.Birefringence at 532 and 1064 nm of differently prepared lithium niobate crystals.

Table 2 .
High resolution X-ray diffraction (HRXRD) and optical parameters of the LiNbO 3 crystals prepared by different methods.

Table 2
. The AE for nSLN_L (310.2 nm) is better than the value reported by Wang et al. i.e., 311 nm for the nSLN_L sample [85].Further the observed AE for nSLN_K (305.5 nm)