Surface Quality Experimental Study on Rotary Ultrasonic Machining of Honeycomb Composites with a Circular Knife Cutting Tool

: Honeycomb composites (HCs) are diversely employed in aerospace, national defense and other ﬁelds owing to their remarkable spatial geometry and excellent mechanical properties. Their complex hexagonal cell structure and heterogeneous material properties cause major problems when implementing high-quality processing. Surface defects generated by processing will reduce the capability and service lifespan of the honeycomb sandwich structure. Therefore, the high quality of HCs is a topic of close attention for researchers. In this paper, the consequences of different cutting parameters of rotary ultrasonic machining (RUM) on surface quality with an ultrasonic circular knife (UCK) were studied through multiple groups of single-factor and orthogonal experiments with two-factors/four-levels and one-factor/three-levels. The single factor experiment was used to explain the effect that the degree of cutting parameters has on surface quality, and the orthogonal experiments were applied to explain the interaction between the processing parameters and the inﬂuence law of each factor on surface quality. Therefore, the reasonable cutting parameters of HCs were determined through experimental results to provide guidance for the realization of the precise and efﬁcient machining of HCs. This study can provide a basis for the subsequent comprehensive consideration of various factors to achieve high-quality machining of HCs.


Introduction
Compared with other structures of the same material, the honeycomb sandwich structure has excellent spatial geometry and mechanical properties [1]. The honeycomb core sandwich structure is a sandwich composite material formed by connecting the honeycomb core and the upper and lower panels with adhesive and curing. It has high stiffness along the axial direction of the cell, therefore, it can bear an impact force on the sandwich structure [2]. However, honeycomb is a typical thin-walled porous structure. The particularity of its structure leads to low in-plane rigidity of the honeycomb core, which is prone to various defects during processing and reduces the performance and service life [3][4][5][6][7][8][9]. The mechanical properties largely rely on honeycomb composite core density, quality and the bonding strength between the core and the panel [1,10]. Therefore, the influence of machining defects on the honeycomb core and its mechanical properties is a key factor to be considered. Consequently, it is significant to research the morphology features of the honeycomb composite (HCs) core and the effect of cutting parameters on HCs core surface quality.
Due to the merits of high processing efficiency and convenient manufacturing of processing equipment, conventional high-speed CNC milling was widely used in honeycomb core material processing. However, traditional processing methods cause the following problems, such as poor processing quality, harsh processing environment, tool wear and so on [11,12]. Thence, rotary ultrasonic machining technology (RUM) was applied to solve the shortcomings of traditional technologies for HC core machining. As a rapidly developing processing technology, RUM technology has been more and more widely employed in the processing of various materials such as composites [13][14][15][16], crystal [17], ceramics [18,19], titanium alloys [20,21], glass and aluminum alloys [22][23][24][25]. In the past, most scholars have carried out research on RUM technology, mainly including the design of the ultrasonic system and ultrasonic cutting tools, the degree of effect of the independent variable cutting parameters on the surface quality of the dependent variable, etc. Xiang et al. [26] proposed that the ultrasonic longitudinal-torsional composite vibration machining method has excellent performance and better surface morphology compared with the transonic longitudinal vibration machining method by analyzing the kinematics of the two processing methods. Xia et al. [27] optimized the structure of ultrasonic cutting tools and explored the influence of distinct tool structure parameters on the machining efficiency of the Nomex honeycomb composite core. Sun et al. [28] concluded that the introduction of RUM technology can significantly reduce the cutting generation of tool cutting forces during machining, thereby reducing the deformation of aluminum honeycomb core walls, resulting in high-quality workpieces. Ahmad et al. [29] conducted a comprehensive review on machining technologies for Nomex HC and Ahmad et al. [30] discussed the influence of different structural parameters of the UCK cutting tool used in machining on ultrasonic amplitude as well as the resonant frequency. Ahmad et al. [31] also researched RUM characteristics of Nomex HCs by a series of UCK cutting tools through a series of controlled variable experiments and orthogonal experimental methods. Asmael et al. [32] reported a review on carbon-fiberreinforced plastic composites by ultrasonic machining. Hu et al. [33] proposed a cutting force model of a triangular blade on honeycomb composites by ultrasonic machining. Cao et al. [34] constructed a three-dimensional finite element model through ABAQUS to analyze the ultrasonic vibration-assisted tool of the Nomex honeycomb core.
In this paper, a group of single-factor experiments and orthogonal experiments of RUM technology with a circular ultrasonic knife for HC core in terms of the aluminum honeycomb core and the Nomex honeycomb core workpiece were conducted to discuss the effect of different processing parameters, i.e., tool feed rate, tool cutting width, ultrasonic spindle speed on surface quality. Then, we further analyzed the significance of different cutting parameters on surface quality through orthogonal experiments developed in this study. Therefore, the framework of this paper is arranged as follows. The experimental synopsis is introduced in Section 2. Section 3 shows the experimental program. The phenomenon and discussion are presented in Section 4. The next section, namely, Section 5, summarizes this paper.

Experimental Synopsis
Most RUM systems are mainly composed of the following parts: ultrasonic power supply, ultrasonic converters, amplitude modifier (booster) and ultrasonic cutting tool. Ultrasonic power supply (ultrasonic generator) outputs high-frequency AC oscillating electrical signals. The ultrasonic transducer converts the high-frequency AC oscillating electrical signal output by the ultrasonic generator into a mechanical vibration signal with the same frequency, the ultrasonic transducer used in this paper is a piezoelectric ceramic sensor. The ultrasonic horn amplifies the amplitude of the weak mechanical vibration signal from the ultrasonic transducer to achieve the amplitude required for the actual cutting process, and at the same time, it can ensure that the entire acoustic system is always in a resonance state. The ultrasonic circular knife was used for processing the HC core. A schematic diagram of the RUM system for HC core workpiece machining was displayed in Figure 1. In this paper, the experimental devices for RUM of Aluminum honeycomb composites (ALHCs) core workpiece and Nomex honeycomb composites (NHCs) core workpiece were illustrated in Figures 2 and 3, respectively. Surface quality experiments for RUM of the HC core workpiece by UCK were executed on the ultrasonic machine tool (NO: IT5X111) produced by INNOTECH company. Ultrasonic equipment was installed on the machine tool, then ultrasonic cutting experiment was carried out by switching the power of the ultrasonic generator and air cooling was adopted for the cooling system in the machine tool, as shown in Figures 1-3. Ultrasonic generator (Model: GT2010-GT2015), ultrasonic converters, amplitude modifier and ultrasonic cutting tool were developed by SONIMAT (EUROPE TECHNOLOGIES) in France. The major parameters of the RUM system are ultrasonic frequency (20 KHz), ultrasonic power (Max 1500 w), power supply:230 V mono 50/60 Hz, ultrasonic spline speed (Max 1000 rpm) and vibration amplitude (Max 0.08 mm). ∅63 mm disc cutting tool was used in the experiment, as shown in Figure 4.

Materials Used in Experiment
In this experiment, the Nomex honeycomb composite core workpiece (Type Designation: ACCH-2I-1/8-3.0) was produced by AVIC Composite Materials Co., Ltd. The aluminum honeycomb composite core workpiece (Type Designation: HexWeb ® CR-PAA-5052-3/16-3.1-Non-p) was produced by HEXCEL company. NHCs core workpieces with dimensions of ribbon (L), a direction perpendicular to the ribbon (W) and cell depth (T) as 100 mm × 50 mm × 100 mm and ALHCs core workpieces with dimensions of ribbon (L), a direction perpendicular to the ribbon (W) and cell depth (T) as 100 mm × 50 mm × 80 mm were used in this experiment, as shown in Figure 5. Key parameters for the hexagonal cellular structure of the workpiece are cell size, single wall thickness, double wall thickness and cell edges, as shown in Figure 5 and specimen attributes of ALHCs core workpiece and NHCs core workpiece were demonstrated in Tables 1 and 2, respectively.
Double-sided adhesive tape and synthetic resin adhesive were used to fix ALHCs core and NHCs core workpiece (a group of four workpieces) on the machining table of the machine tool instead of fixing them on a special fixture due to the small dimensions of the workpiece. The fixing system of the specimen is shown in Figure 6.

Measurement Methods for Surface Characteristics
To observe the machining results, a high-definition video detector (CHECKER145Linear-M, STILL, Guangdong China) was used to measure the surface morphology of ALHCs core and NHCs core workpieces after RUM, then, to observe processing defects of the workpiece under different cutting parameters and the effect on surface quality. The concrete analysis is reflected in Section 4. Experimental setup for surface morphology of ALHCs core and NHCs core workpieces are displayed in Figure 7.

Processing Conditions in the Experiment
High quality has always been the core goal of processing. Compared with traditional technology, rotary ultrasonic machining reduces surface defects and improves efficiency. Therefore, the reasonable selection of processing parameters has become the core issue to improve efficiency and workpiece surface quality. Thus, in this research, a group of single-factor experiments and orthogonal experiments with two-factors/four-levels and one-factor/three-levels were used to discuss the effect of cutting parameters such as cutting tool feed rate, tool cutting depth and ultrasonic spindle speed on surface quality. In experiments for ALHC core workpieces, the cutting depth remained at 0.8 mm for each experiment due to material property and great cutting effects. In the experiments for NHC core workpieces, cutting depth remained at 2 mm for each experiment. Vibration amplitude was kept fixed at 0.08 mm according to the manufacturer. According to the parameters of the ultrasonic equipment itself and the performance parameters of the machine tool with ultrasonic equipment, the single-factor experiments designed are illustrated in Table 3. Through single-factor controlled variable method experiments, the effect of each parameter on the surface quality can be obtained. However, the interaction between different machining parameters cannot be illustrated in single-factor controlled variable method experiments. Therefore, two-factors/four-levels and one-factor/three-levels orthogonal experimental methods were designed to discuss the influence of distinct processing variables in this paper. Meanwhile, orthogonal experimental technology was used to obtain the optimal association of cutting parameters for rotatory ultrasonic machining of ALHC core workpieces and Nomex honeycomb core workpieces with a UCK cutting tool according to the orthogonal experiments. The parameter factors and levels in the orthogonal experiments of the RUM are displayed in Table 4. The two-factors/four-levels and onefactor/three-levels L 12 3 × 4 2 orthogonal experimental conditions of ALHC core and NHC core specimens are shown in Table 5.

Results and Discussion
The honeycomb sandwich structure consists of a high-strength adhesive bonding a relatively thin skin panel to a comparatively thick lightweight honeycomb core, and the overall structure is like a honeycomb structure. As the key component of a sandwich structure, a honeycomb core can greatly increase stiffness and strength on the premise of slightly increasing the overall quality of the sandwich structure, and is lightweight. Therefore, processing quality directly affects the performance and service life. RUM technology is used in composite material machining to greatly reduce defects and improve surface quality. Therefore, it is worthwhile to further study the processing characteristics of RUM with UCK and the influence of different cutting parameters on the workpiece surface quality. However, the ultrasonic cutting tool used in this experiment was newly fabricated, so tool tear was ignored and dust, delamination and collapse of cells did not exist in this study due to the RUM technology. In these experiments, the processing principle of the RUM technology and the disc cutting tool ultrasonic vibration trajectory are displayed in Figure 8. In this figure, A represents ultrasonic amplitude, f represents ultrasonic frequency, n represents disc tool rotary velocity and P represents any point on the disc cutting tool. When the disc cutting tool is without ultrasonic vibration, the tangential velocity V t was much greater than feed velocity V f , therefore, tool rotational motion was the main motion, and V t can be expressed as: where D represents disc cutting tool diameter. When the disc cutting tool used ultrasonic vibration, the cutting tool produced displacement S with periodic changes in magnitude and direction along the tool axis. S can be expressed as: where t represents the cutting time, θ represents the vibration initial phase angle. Differently to Equation 2, vibration cutting velocity along the tool axis (Z direction) can be obtained as: In the RUM technology, the vibration cutting velocity V s was much greater than the tangential velocity V t and feed velocity V f , therefore, tool vibration motion along the tool axis became the main motion in processing. The magnitude and the direction of V s changed periodically over time.
Then, the authors observed the effect of different processing parameters on the workpiece surface with a disc ultrasonic cutting tool. The surface morphology of the ALHC core and the NHC core workpieces under different processing parameters was analyzed in detail below. The effect degree of the ultrasonic spindle speed on the workpiece surface morphology was studied by rotatory ultrasonic machining tests on the ALHC core workpiece with a UCK cutting tool on the machine tool. The parameters of the cutting tool feed rate, tool cutting width, and tool cutting depth were fixed, and the spindle speed was gradually increased. The average length of tears L was used as the evaluation parameter to measure the surface quality due to tears that seriously affected the service life of the part. The processed surface was divided into three equal observation areas, two honeycomb cells can be observed in each observation area. The average tearing length was measured by the experiment setup in Figure 7, as shown in Figure 9. The surface quality experimental results of the RUM with the UCK cutting tool are shown in Figure 10. As shown in Figures 9 and 10, the feed rate is fixed at 500 mm/min, the cutting width is fixed at 8 mm and the cutting depth is fixed at 0.8 mm. The range of spindle speeds is 500~800 rpm. The defect mainly included tearing, burr and crush fold on the surface morphology with the machined workpiece. The amount and the average length of tearing decreased with increased spindle speed during the ultrasonic machining experiment of the ALHC core workpieces with an ultrasonic circular knife cutting tool. The shearing effect on the material increased with an increased spindle speed, therefore, the shearing length decreased in this experiment at different spindle speeds from 500~800 rpm. Burr changed the same as tearing.

Results of Tool Feed Rate on Surface Morphology
The effect of the degree of tool feed rate on surface morphology was studied by rotatory ultrasonic machining tests on the ALHC core workpiece with a UCK cutting tool on the machine tool. The parameters of spindle speed, cutting width, and cutting depth were fixed, and the feed rate was gradually increased. The average tearing length was measured with the experimental setup in Figure 7, as shown in Figure 11. The surface quality experimental results of the RUM with a UCK cutting tool are shown in Figure 12.  Figures 11 and 12, spindle speed is fixed at 800 rpm and cutting width is fixed at 8 mm. Both the number and length of tears decreased as the feed rate increased. The reason for this phenomenon was due to the increased feed rate speeding up the cutting process, shortening the touching time between the tool and the workpiece, thus improving the surface morphology to a certain extent, although the cutting force in the processing increased with an increased cutting tool feed rate.

Result of Tool Cutting Width on Surface Morphology
The effect of the degree of cutting width on surface morphology was researched by rotatory ultrasonic machining experiments on the ALHC core workpiece with a UCK cutting tool on the machine tool at different cutting widths from 4 µm to 10 µm. The parameters of the ultrasonic spindle speed, tool feed rate, tool cutting depth were fixed. The average tearing length was measured by the experimental setup in Figure 7, as shown in Figure 13. The surface quality experimental results of the RUM with a UCK cutting tool are shown in Figure 14.   As shown in Figures 13 and 14, the feed rate was fixed at 2000 mm/min and the spindle speed was fixed at 800 rpm. During the RUM experiments of the NCH core workpieces, tearing length decreased to a certain extent with an increased tool cutting width, but the effect was small. The authors found that the crush fold phenomenon was largely affected by the cutting width. The stiffness of the cell single wall was lower, therefore, the AL honeycomb cell single wall underwent plastic deformation due to the cutting force. The increase in tool cutting width increased the touching area between the cutting tool and the aluminum honeycomb, therefore, the material volume increased in the cutting process. The larger the cutting width, the more prone the aluminum honeycomb wall was to plastic deformation, which can lead to a crush fold defect.

Results of Cutting Parameters on Surface Morphology by Two-Factors/Four-Levels and One-Factor/Three-Factors L 12 3 × 4 2 Orthogonal Experiments
The influence of a single variable on the surface morphology of the ALHC core workpiece can be obtained through a group of single-factor experiments. However, the effect of a different combination of multiple variables on surface morphology cannot be determined. Therefore, according to the performance of the machine tool and ultrasonic device, two-factors/four-levels and one-factor/three-factors orthogonal experiments technology was proposed to study the effect of different cutting parameters on surface morphology. In this paper, the influence of various parameters, namely ultrasonic spindle speed, cutting tool feed rate and cutting width under the constant value of vibration amplitude 0.08 mm and cutting depth 2 mm were obtained by rotatory ultrasonic machining on an ALHC core specimen with an ultrasonic circular knife cutting tool. The authors only showed surface experimental results in area one to save space, as shown in Figure 15. In order to further analyze the significance of machining variables, the results of the orthogonal experiments were quantified by the evaluation parameter, namely L, of surface macro-topography proposed above. The orthogonal experimental significance analysis results in the average length L of tearing, as shown in Table 6.  In conclusion from Table 6, the range variance of tearing average L among the three processing variables including ultrasonic spindle speed, tool feed rate and tool cutting width under the constant cutting depth and ultrasonic vibration amplitude during ultrasonic machining experiments of the Nomex honeycomb core workpiece by disc was: R f eed rate > R spindle speed > R cutting width (4) It can be seen from Equation (1) that feed rate has the maximum effect on the tearing average length L and the cutting width has the minimum influence on the tearing average L.

Results of Ultrasonic Spindle Speed on Surface Morphology
The influence of the degree of ultrasonic spindle speed on surface quality was studied by rotatory ultrasonic machining experiments on a Nomex HC core workpiece with a disc cutting tool on the machine tool. The parameters of tool feed rate, tool cutting width, and cutting depth were fixed, and the spindle speed was gradually increased. The number of tears N (length more than 1 mm) and the average length of tears L were used as evaluation parameters to measure the surface quality as a surface with tears will seriously affect the service life of the part. The processed surface was divided into three equal observation areas, five honeycomb cells can be observed in each observation area, and the total number of tears and the average length of the three observation areas are counted. The surface quality experimental results of the RUM with a UCK cutting tool are shown in Figure 16. The average tearing length and amount were measured by the experimental setup in Figure 7, as shown in Figure 17.   Figures 16 and 17, area one, area two, and area three represent the observation areas, respectively. The feed rate was fixed at 500 mm/min, the cutting depth was fixed at 2 mm and the cutting width was fixed at 8 mm. The average length of tears L decreased when increasing the ultrasonic spindle speed and the total number of tears changes less during the experiments on the Nomex HC core specimen with a disc cutting tool.

As shown in
The reason for this conclusion is that the high-frequency vibration of the cutting tool makes the vibration speed far greater than the tangential speed of the disc cutter during RUM, and the main cutting motion is the ultrasonic vibration of the tool. The main force for fracture separation of the honeycomb wall is not the shear force, but the high-frequency impact force of the disc cutter on the chip and the machined surface. Therefore, the change of spindle speed has little effect on the extrusion and the friction force of the cutting tool on the material along the feeding direction, and the amount of tearing does not change significantly. However, the increase in spindle speed can increase the shearing effect on the material to a certain extent, therefore, the shearing length decreases with an increase in cutting tool speed. The cutting force in processing decreases with ultrasonic spindle speed which increases in rotatory ultrasonic machining experiments of the NHC core specimens, therefore, the number of burrs decreases.

Results of Tool Feed Rate on Surface Morphology
The effect of the degree of tool feed rate on surface quality was studied with rotatory ultrasonic machining experiments on a Nomex HCs core workpiece with a disc cutting tool on the machine tool. The parameters of spindle speed, cutting width, and cutting depth were fixed, and the feed rate was gradually increased. The average tearing length and amount of tears were measured by the experimental setup in Figure 7, as shown in Figure 18. The surface quality experimental results of the RUM by disc cutting tool are displayed in Figure 19.  Figures 18 and 19, the spindle speed is fixed at 800 rpm and the cutting width is fixed at 8 mm. Both the number and length of tears increase as the feed rate increases. In ultrasonic cutting, the extrusion force of the cutting tool on the material decreases with a feed rate decrease. Therefore, the tearing defect generated by the cutting tool due to the compressive deformation of the honeycomb core wall increases when increasing the tool feed rate. However, RUM technology has a greater effect on reducing the extrusion force, therefore, the effect of feed rate on tearing tends to be gentle.

Results of Tool Cutting Width on Surface Morphology
The effect of the degree of tool cutting width on surface quality was studied by rotatory ultrasonic machining tests on a Nomex HC core workpiece with a disc cutting tool on the machine tool at different cutting widths from 4 µm to 10 µm. The parameters of the ultrasonic spindle speed, tool feed rate, and cutting depth were fixed. The average tearing length and amount of tears were measured by the experimental setup in Figure 7, as shown in Figure 20. The surface quality experimental results of RUM with the disc cutting tool are illustrated in Figure 21.   As shown in Figures 20 and 21, the feed rate was fixed at 2000 mm/min and the spindle speed was fixed at 800 rpm.
Both the number and length of tears increase as the cutting width increases with the disc cutting tool during the RUM tests of the NCH core workpieces. The reason for this conclusion is that the touching area between the disc tool and the workpiece corresponding to the different cutting widths was also different, and the contact area was proportional to the cutting width, resulting in the larger the cutting width, the greater the friction between the tool and the workpiece in the cutting process. Burr changed the same as tearing.

Results of Cutting Parameters on Surface by Two-Factors/Four-Levels and
One-Factor/Three-Factors L 12 3 × 4 2 Orthogonal Experiments The influence degree of a single variable on the surface morphology of the Nomex HC core workpiece can be obtained through a group of single-factor experiments. However, the influence of a different combination of multiple variables on surface morphology cannot be determined. Therefore, according to the performance of the machine tool and the ultrasonic device, two-factors/four-levels and one-factor/three-factors orthogonal experiments technology were proposed to study the effect of different cutting parameters on surface morphology. In this study, the effect of cutting parameters on surface quality was investigated by establishing orthogonal experiments with different variable combinations. The authors only showed surface experiments in the results area one to save space, as shown in Figure 22. To further discuss the significance of cutting parameters, the results of orthogonal experiments were quantified by evaluation parameters, namely N, L, of the surface macro-topography, as proposed above. The orthogonal experimental significance analysis results of the total amount N and average length L of tearing were measured by the experimental device in Figure 7, as shown in Tables 7 and 8 separately.   In conclusion from Table 7, the range in the variance of tearing amount N among the three processing variables including ultrasonic spindle speed, tool feed rate and tool cutting width under the same depth and ultrasonic vibration amplitude of ultrasonic machining for the Nomex HC core workpiece with a disc cutting tool was: From Equation (2) it can be observed that the cutting width has the maximum effect on the tearing amount N and the spindle speed has the least influence on the tearing amount N.
In conclusion from Table 8, the range in the variance of average tearing length L among the three processing variables including ultrasonic spindle speed, tool feed rate and tool cutting width under an identical depth and ultrasonic vibration amplitude of ultrasonic machining for the Nomex HC core workpiece with a disc cutting tool was: From Equation (3) it can be seen that the cutting width has the maximum effect on the average tearing length L and the feed rate has the least influence on the tearing average L.

Conclusions
In this paper, the surface quality experiment for rotatory ultrasonic machining (RUM) of a honeycomb composite core (aluminum honeycomb and Nomex honeycomb) by ultrasonic circular knife (UCK) was developed to research the influence of different cutting variables on surface morphology for the aluminum honeycomb composite (ALHCs) core workpiece and the Nomex honeycomb composite (NHCs) core workpiece through a serious of single-factor experiments. Then, the optimal processing parameters of ultrasonic machining were received through orthogonal experimental technology. The results can be concluded as follows.
For the ALHC core workpiece, processing defects mainly include burr, tearing and crush fold of RUM with an ultrasonic disc cutting tool. Burr and tearing decrease with increasing ultrasonic spindle speeds and disc tool feed rates due to the increase in spindle speed increasing the shearing effect on the material to a certain extent and the increasing disc tool feed rate can speed up the cutting process, shortening the touching time between the disc cutting tool and the workpiece. Crush folds were largely affected by the cutting width through a group of single-factor experiments and these defects increase with the increase in cutting width due to the aluminum honeycomb being more prone to plastic deformation when there is a larger contact area between the cutting tool and the aluminum honeycomb. Feed rate has the greatest effect on the tearing average of surface morphology and cutting width has the smallest influence during the RUM experiment with a UCK cutting tool through significance analysis of two-factors/four-levels and one-factor/threelevels (L 12 3 × 4 2 ) orthogonal experimental results.
For the NHC core workpiece, burr, tearing and uncut fiber defects existed on the surface morphology of the RUM with a UCK cutting tool. Burr and tearing decrease when improving the ultrasonic spindle speed owing to the high-frequency impact force of the disc cutter on the chip and the machined surface. However, tearing increases with the improvement in disc tool feed rate because of an increase in extrusion force of the cutting tool on the material and the increase in material removal volume by the single-factor experiments. Therefore, burr and tearing increase when increasing the disc tool cutting width due to the increase in the touching area between the disc tool and the workpiece, resulting in an improvement in tool cutting force. Cutting width has the greatest effect on the tearing average and the number of tears to the surface morphology. Spindle speed has the smallest influence on the number of tears and the feed rate has the least effect on the tearing average during this experimental study by significance analysis of two-factors/fourlevels and one-factor/three-levels (L 12 3 × 4 2 ) orthogonal experimental results.
The research in this paper can provide a basis for the subsequent comprehensive consideration of various factors to achieve high-quality processing of HC and it should be noted that the conditions of all single-factor experiments and orthogonal experiments in this paper were designed according to the actual performance of ultrasonic CNC machine tools in a factory, therefore, the results of this paper are generally applicable to most factories involved in the high surface quality processing of honeycomb composites.

Institutional Review Board Statement: Not applicable.
Informed Consent Statement: Not applicable.

Data Availability Statement:
The datasets generated and analyzed during the current study are available from the corresponding author on reasonable request.